KR100947866B1 - Lamp cover manufacturing method - Google Patents

Lamp cover manufacturing method Download PDF

Info

Publication number
KR100947866B1
KR100947866B1 KR1020090081463A KR20090081463A KR100947866B1 KR 100947866 B1 KR100947866 B1 KR 100947866B1 KR 1020090081463 A KR1020090081463 A KR 1020090081463A KR 20090081463 A KR20090081463 A KR 20090081463A KR 100947866 B1 KR100947866 B1 KR 100947866B1
Authority
KR
South Korea
Prior art keywords
glass
milky
mold
finished product
transparent
Prior art date
Application number
KR1020090081463A
Other languages
Korean (ko)
Inventor
한상일
Original Assignee
한상일
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한상일 filed Critical 한상일
Priority to KR1020090081463A priority Critical patent/KR100947866B1/en
Application granted granted Critical
Publication of KR100947866B1 publication Critical patent/KR100947866B1/en

Abstract

PURPOSE: A method for manufacturing a glass lampshade is provided to implement two-tone colors by forming a transparent glass on the surface of milky glass. CONSTITUTION: A mold is prepared(S110). A milky glass is formed by coating a milky glass melted solution on the inner surface of the mold(S120). A half-finished product is manufactured by forming transparent glass on the inner surface of the milky glass(S130). The half-finished product is separated from the mold(S140). A protrusion is cut from the surface of the half-finished product(S150). The half-finished product is heated at a temperature between 900 and 1000 °C(S160). A transparent thin layer is coated on the surface of the half-finished product(S170).

Description

유리 조명 갓 제조방법{LAMP COVER MANUFACTURING METHOD}Glass lamp shade manufacturing method {LAMP COVER MANUFACTURING METHOD}

본 발명은 유리 조명 갓 제조방법에 관한 것으로, 좀더 상세하게는 유백색 유리 표면에 투명 유리가 형성되어 투 톤의 색상이 고급스럽게 어울어지는 유리 조명 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a glass lampshade, and more particularly, to a glass lighting manufacturing method in which transparent glass is formed on a milky-white glass surface so that a two-tone color is matched with luxury.

일반적으로 조명 갓은 조명등을 보호하고, 간접조명을 형성할 뿐만 아니라, 인테리어 효과를 높이기 위해 사용된다.Generally, lamp shades are used to protect lighting, form indirect lighting, and enhance interior effects.

최근에는 다양한 소재와 형상으로 조명 갓이 제작됨에 따라, 다양한 실내 분위기를 연출할 수 있다. 이러한 조명 갓의 재료로는 유리, 종이, 직물 등 다양한 소재가 사용되며, 이 중 유리는 불에 강하고 소재가 흔하다는 점에서 많이 사용되어 왔다.Recently, as the lampshade is manufactured with various materials and shapes, various indoor atmospheres can be produced. As a material of such a lampshade, various materials such as glass, paper, and fabrics are used. Among them, glass has been used in view of fire resistance and common materials.

종래 유리 조명 갓은 단일 유리 재로 성형되는 것이 대부분이어서 기능은 물론 디자인이 단순하고 단조로워 다양한 제품을 원하는 소비자의 요구에 부응하지 못하고 있는 실정에 있다.Conventional glass lampshade is mostly molded from a single glass material, so the function as well as the design is simple and monotonous does not meet the needs of consumers who want a variety of products.

본 발명은 전술한 문제점을 해결하기 위한 것으로, 유백색 유리 표면에 투명 유리가 형성되어 투 톤의 색상이 고급스럽게 형성됨으로써 제품 경쟁력을 갖는 유리 조명 갓 제조방법을 제공함에 그 목적이 있다.The present invention is to solve the above-mentioned problems, and the object of the present invention is to provide a glass lampshade manufacturing method having a product competitiveness by forming a transparent glass on the milky-white glass surface to form a two-tone color luxuriously.

전술한 목적을 달성하기 위하여 본 발명에 따른 유리 조명 갓 제조방법은 내주 면에 무늬 장 홈이 형성된 금형을 준비하는 단계; 상기 금형 안에 유백색 유리용융액을 주입하고 상기 유백색 유리용융액 안에 공기를 주입하여 상기 유백색 유리용융액을 상기 금형 내주 면에 도포하고 응고시켜서 유백색 유리를 제조하는 단계; 상기 금형 안에 투명 유리용융액을 주입하고 상기 투명 유리용융액 안에 공기를 주입하여 상기 투명 유리용융액을 상기 유백색 유리 내주 면에 도포 후 응고시킴으로써 외 측에 유백색 유리가 위치하고 내 측에 투명 유리가 위치하는 반제품을 제조하는 단계; 상기 반제품을 상기 금형으로부터 분리하는 단계; 상기 무늬 장 홈에 의해서 상기 반제품 표면으로 돌출된 부분을 커팅하여 상기 투명 유리를 노출시키는 단계; 상기 커팅된 반제품을 900-1000℃로 가열하는 단계; 및 상기 가열된 반제품을 코팅용 투명유리 용융액 탱크 안에 함침(含浸)시켜 회전시키면서 상기 반제품 표면에 투명 박막을 코팅하여 완제품을 완성하는 단계;를 포함한다.Glass lighting shade manufacturing method according to the present invention in order to achieve the above object comprises the steps of preparing a mold having a patterned groove is formed on the inner peripheral surface; Preparing a milky glass by injecting a milky glass melt into the mold and injecting air into the milky glass melt to apply the milky glass melt to the inner surface of the mold and to solidify the milky glass; Inject the transparent glass melt into the mold and inject air into the transparent glass melt to apply the transparent glass melt to the inner surface of the milky glass and then solidify it so that the milky glass is located on the outside and the transparent glass is located on the inside. Manufacturing; Separating the semifinished product from the mold; Cutting the protruding portion of the semi-finished surface by the patterned groove to expose the transparent glass; Heating the cut semifinished product to 900-1000 ° C .; And coating a transparent thin film on the surface of the semifinished product while rotating the impregnated heated semifinished product in a transparent glass melt tank for coating to complete the finished product.

본 발명에 따른 유리 조명 갓은 상기 방법에 의해 제조되며, 유백색 유리 표면에 투명 유리가 형성되어 투 톤의 색상이 형성된다.The glass lampshade according to the present invention is manufactured by the above method, and transparent glass is formed on the milky-white glass surface to form a two-tone color.

이상에서 설명한 바와 같이, 본 발명은 금형 안에 유백색 유리용융액을 주입하고 상기 유백색 유리용융액 안에 공기를 주입하여 상기 유백색 유리용융액을 상기 금형 내주 면에 도포 응고시키고, 연이어 동일한 방법으로 투명 유리용융액을 상기 유백색 유리 내주 면에 도포 후 응고시킴으로써 외 측에 유백색 유리가 위치하고 내 측에 투명 유리가 위치하는 반제품을 제조한 후 상기 반제품 표면으로 돌출된 부분을 커팅하고 상기 커팅된 반제품을 900-1000℃로 가열하며 상기 가열된 반제품의 표면을 코팅하여 완제품을 완성함으로써 투 톤의 색상이 고급스럽게 형성되어 제품 경쟁력을 갖는 효과가 있다.As described above, the present invention injects a milky-white glass melt into a mold and injects air into the milky-white glass melt to apply and solidify the milky glass melt on the inner surface of the mold, and subsequently the transparent glass melt is the milky white. After coating on the inner surface of the glass to solidify it to produce a semi-finished product with the milky white glass on the outside and the transparent glass on the inside, cut the protruding part to the surface of the semi-finished product and heat the cut semi-finished product to 900-1000 ℃ By coating the surface of the heated semi-finished product to complete the finished product is a two-tone color is luxuriously formed has the effect of having a product competitiveness.

이하, 첨부 도면을 참조하여 본 발명의 바람직한 실시 예에 따른 유리 조명 갓 제조방법에 대하여 상세하게 설명한다.Hereinafter, a method of manufacturing a glass lampshade according to a preferred embodiment of the present invention with reference to the accompanying drawings will be described in detail.

도 1 내지 도 8은 본 발명에 따른 유리 조명 갓 제조방법을 보인 구성도이고 도 9는 본 발명에 따른 유리 조명 갓 제조방법을 보인 흐름도이다.1 to 8 is a schematic view showing a glass lampshade manufacturing method according to the invention and Figure 9 is a flow chart showing a glass lampshade manufacturing method according to the present invention.

도면을 참조하면, 본 발명에 따른 유리 조명 갓 제조방법은 내주 면에 무늬 장 홈(11)이 형성된 금형(10)을 준비하는 단계(S110); 상기 금형(10) 안에 유백색 유리용융액(20)을 주입하고 상기 유백색 유리용융액(20) 안에 공기를 화살표 방향으로 주입하여 상기 유백색 유리용융액(20)을 상기 금형(10) 내주 면에 도포하고 응고시켜서 유백색 유리(20')를 제조하는 단계(S120); 상기 금형(10) 안에 투명 유리용융액(30)을 주입하고 상기 투명 유리용융액(30) 안에 공기를 화살표 방향으로 주입하여 상기 투명 유리용융액(30)을 상기 유백색 유리(20') 내주 면에 도포 후 응고시킴으로써 외 측에 유백색 유리(20')가 위치하고 내 측에 투명 유리(30')가 위치하는 반제품(100')을 제조하는 단계(S130); 상기 반제품(100')을 상기 금형(10)으로부터 분리하는 단계(S140); 상기 무늬 장 홈(11)에 의해서 상기 반제품(100') 표면으로 돌출된 부분을 커팅하여 상기 투명 유리(30')를 노출시키는 단계(S150); 상기 커팅된 반제품(100')을 900-1000℃로 가열하는 단계(S160); 및 상기 가열된 반제품(100')을 코팅용 투명유리 용융액 탱크(40) 안에 함침(含浸)시켜 회전시키면서 상기 반제품(100') 표면에 투명 박막(50)을 코팅하여 완제품(100)을 완성하는 단계(S170);를 포함한다.Referring to the drawings, the method for manufacturing a glass lampshade according to the present invention comprises the steps of preparing a mold 10 having a patterned long groove 11 formed on the inner peripheral surface (S110); Injecting the milky glass melt 20 into the mold 10 and injecting air into the milky glass melt 20 in the direction of the arrow to apply the milky glass melt 20 to the inner peripheral surface of the mold 10 and to solidify Preparing a milky glass 20 '(S120); The transparent glass melt 30 is injected into the mold 10 and air is injected into the transparent glass melt 30 in the direction of an arrow to apply the transparent glass melt 30 to the inner circumferential surface of the milky glass 20 '. Manufacturing a semi-finished product 100 'having a milky glass 20' on the outside and a transparent glass 30 'on the inside by solidifying (S130); Separating the semifinished product (100 ') from the mold (S140); Cutting the protruding portion of the semi-finished product (100 ') surface by the patterned groove (11) to expose the transparent glass (30') (S150); Heating the cut semifinished product (100 ') to 900-1000 ° C. (S160); And coating the transparent thin film 50 on the surface of the semi-finished product 100 'while impregnating and rotating the heated semi-finished product 100' in the transparent glass melt tank 40 for coating to complete the finished product 100. Step S170; includes.

본 발명에 따른 유리 조명 갓 제조방법에 있어서, 상기 단계(S110)에서는 내주 면에 무늬 장 홈(11)이 형성된 금형(10)을 준비한다. 상기 금형(10)은 2등 분할 (혹은 4등 분할)되는 구조로 형성되어 금형(10) 내부에 응고된 유리를 쉽게 꺼낼 수 있도록 하는 것이 바람직하다.In the method of manufacturing a glass lampshade according to the present invention, in step S110, a mold 10 having a patterned long groove 11 formed on an inner circumferential surface thereof is prepared. The mold 10 is preferably formed in a structure that is divided into two (or four) divided so that the glass solidified in the mold 10 can be easily taken out.

상기 금형(10)의 내주 면에 형성된 무늬 장 홈(11)은 후술하는 완제품에 무늬를 갖도록 하는 역할을 하는바, 가능한 매끄럽고 다양한 형태로 형성하는 것이 디자인 측면에서 유리하다.The patterned groove 11 formed on the inner circumferential surface of the mold 10 serves to have a pattern on the finished product to be described later, it is advantageous in terms of design to form as smooth and various forms as possible.

상기 단계(S120)에서는 상기 금형(10) 안에 유백색 유리용융액(20)을 주입하고 상기 유백색 유리용융액(20) 안에 공기를 주입하여 상기 유백색 유리용융액(20)을 상기 금형(10) 내주 면에 도포하고 응고시켜서 유백색 유리(20')를 제조한다.In step S120, the milky glass melt 20 is injected into the mold 10 and air is injected into the milky glass melt 20 to apply the milky glass melt 20 to the inner peripheral surface of the mold 10. And coagulated to produce a milky glass 20 '.

즉, 스테인레스 봉(2)의 끝단에 유백색 유리용융액(20)을 묻히고, 상기 스테 인레스 봉(2)을 통해서 상기 유백색 유리용융액(20) 안에 공기를 주입하여 상기 유백색 유리용융액(20)을 상기 금형(10) 내주 면에 도포하고 일정시간을 지나 응고시킨 후 유백색 유리(20')를 제조한다.That is, the milky glass melt 20 is buried at the end of the stainless steel rod 2, and the air is injected into the milky glass melt 20 through the stainless rod 2 to draw the milky glass melt 20. After the mold 10 is coated on the inner circumferential surface and solidified after a predetermined time, the milky glass 20 'is manufactured.

상기 단계(S130)에서는 상기 금형(10) 안에 투명 유리용융액(30)을 주입하고 스테인레스 봉을 통해서 상기 투명 유리용융액(30) 안에 공기를 주입하여 상기 투명 유리용융액(30)을 상기 유백색 유리(20') 내주 면에 도포 후 응고시킴으로써 외 측에 유백색 유리(20')가 위치하고 내 측에 투명 유리(30')가 위치하는 반제품(100')을 제조하는 것이다.In the step (S130), the transparent glass melt 30 is injected into the mold 10 and air is injected into the transparent glass melt 30 through a stainless rod to transfer the transparent glass melt 30 to the milky glass 20 ') The semi-finished product 100' in which the milky glass 20 'is positioned on the outer side and the transparent glass 30' is positioned on the inner side by solidifying after coating on the inner peripheral surface.

상기 단계(S140)에서는 상기 금형(10)을 2등 분할(또는 4등 분할)하고, 상기 금형(10)으로부터 상기 반제품(100')을 꺼낸다. 여기서 전술한 단계에서 무늬 장홈 안으로 유백색 유리(20')와 투명 유리(30')가 삽입된 상태로 응고되어 상기 반제품(100')은 무늬 장홈 부분이 돌출된 상태를 갖는다.In the step S140, the mold 10 is divided into second (or fourth) portions, and the semi-finished product 100 'is removed from the mold 10. Here, in the above-described step, the milky white glass 20 'and the transparent glass 30' are solidified into the pattern long groove, so that the semifinished product 100 'has a state where the pattern long groove is protruded.

상기 단계(S150)에서는 상기 무늬 장 홈(11)에 의해서 상기 반제품(100') 표면으로 돌출된 부분을 커팅하여 상기 투명 유리(30')를 노출시킨다. 커팅 면은 상기 유백색 유리(20')의 표면과 동일한 면을 갖도록 균일하게 커팅하는 것이 바람직하다.In step S150, the transparent glass 30 ′ is exposed by cutting a portion protruding from the patterned groove 11 to the surface of the semi-finished product 100 ′. The cutting surface is preferably cut uniformly to have the same surface as the surface of the milky glass 20 '.

상기 단계(S160)에서는 가열로(1) 안에서 상기 커팅된 반제품(100')을 900-1000℃로 가열한다.In step S160, the cut semifinished product 100 ′ is heated to 900-1000 ° C. in the heating furnace 1.

마지막으로 상기 단계(S170)에서는 상기 가열된 반제품(100')을 코팅용 투명유리 용융액 탱크(40) 안에 함침(含浸)시켜 회전시키면서 상기 반제품(100') 표면 에 투명 박막(50)을 코팅하여 완제품(100)을 완성한다.Finally, in the step (S170) by coating the transparent thin film 50 on the surface of the semi-finished product (100 ') while rotating by impregnating the heated semi-finished product (100') in the transparent glass melt tank 40 for coating Complete the finished product 100.

한편, 상기 방법에 의해 제조된 본 발명의 유리 조명 갓(100)은 유백색 유리 표면에 투명 유리가 형성되어 투톤의 색상이 형성된다. 다시 말해, 본 발명의 유리 조명 갓은 전체적으로 유백색의 유리를 가지면서 상기 무늬 장 홈에 의해 형성된 부분에 투명 유리가 형성됨으로써 투 톤의 색상이 어울어져 고상하고 고급스러운 디자인을 갖는다.On the other hand, the glass lampshade 100 of the present invention prepared by the method is a transparent glass is formed on the milky glass surface to form a two-tone color. In other words, the glass lampshade of the present invention has a milky-white glass as a whole, and transparent glass is formed in a portion formed by the patterned grooves, so that two-tone colors match, thereby having a noble and luxurious design.

이와 같이 본 발명의 권리는 상기 설명된 실시 예에 한정되지 않고, 청구범위에 기재된 바에 의해 정의되며, 본 발명의 기술분야에서 통상의 지식을 가진 자가 청구범위에 기재된 권리범위 내에서 다양한 변형을 할 수 있다는 것은 자명하다.As such, the rights of the present invention are not limited to the embodiments described above, but are defined by the claims, and those skilled in the art can make various modifications within the scope of the claims. It is self evident.

도 1 내지 도 8은 본 발명에 따른 유리 조명 갓 제조방법을 보인 구성도1 to 8 is a schematic view showing a glass lighting shade manufacturing method according to the present invention

도 9는 본 발명에 따른 유리 조명 갓 제조방법을 보인 흐름도9 is a flow chart showing a glass lamp shade manufacturing method according to the present invention

* 주요부분에 대한 도면 설명* Description of the main parts

1: 가열로1: heating furnace

2: 스테인레스 봉2: stainless rods

10: 금형10: mold

11: 무늬 장 홈11: pattern cabinet groove

20: 유백색 유리용융액20: milky glass melt

20': 유백색 유리20 ': milky glass

100: 유리 조명 갓100: glass lighting lampshade

30: 투명 유리용융액30: clear glass melt

30': 투명 유리30 ': clear glass

40: 코팅용 투명유리 용융액 탱크40: Clear Glass Melt Tank for Coating

50: 투명 박막50: transparent thin film

100': 반제품100 ': semi-finished product

100: 유리 조명 갓100: glass lighting lampshade

Claims (2)

내주 면에 무늬 장 홈(11)이 형성된 금형(10)을 준비하는 단계(S110);Preparing a mold 10 having a patterned groove 11 formed on an inner circumferential surface thereof (S110); 상기 금형(10) 안에 유백색 유리용융액(20)을 주입하고 상기 유백색 유리용융액(20) 안에 공기를 주입하여 상기 유백색 유리용융액(20)을 상기 금형(10) 내주 면에 도포하고 응고시켜서 유백색 유리(20')를 제조하는 단계(S120);The milky glass melt 20 is injected into the mold 10 and air is injected into the milky glass melt 20 to apply the milky glass melt 20 to the inner peripheral surface of the mold 10 and to solidify the milky glass ( 20 ') manufacturing step (S120); 상기 금형(10) 안에 투명 유리용융액(30)을 주입하고 상기 투명 유리용융액(30) 안에 공기를 주입하여 상기 투명 유리용융액(30)을 상기 유백색 유리(20') 내주 면에 도포 후 응고시킴으로써 외 측에 유백색 유리(20')가 위치하고 내 측에 투명 유리(30')가 위치하는 반제품(100')을 제조하는 단계(S130);The transparent glass melt 30 is injected into the mold 10 and air is injected into the transparent glass melt 30 to apply the transparent glass melt 30 to the inner circumferential surface of the milky glass 20 'and then to solidify it. Manufacturing a semi-finished product 100 'having a milky glass 20' at the side and a transparent glass 30 'at the inner side (S130); 상기 반제품(100')을 상기 금형(10)으로부터 분리하는 단계(S140);Separating the semifinished product (100 ') from the mold (S140); 상기 무늬 장 홈(11)에 의해서 상기 반제품(100') 표면으로 돌출된 부분을 커팅하여 상기 투명 유리(30')를 노출시키는 단계(S150);Cutting the protruding portion of the semi-finished product (100 ') surface by the patterned groove (11) to expose the transparent glass (30') (S150); 상기 커팅된 반제품(100')을 900-1000℃로 가열하는 단계(S160); 및Heating the cut semifinished product (100 ') to 900-1000 ° C. (S160); And 상기 가열된 반제품(100')을 코팅용 투명유리 용융액 탱크(40) 안에 함침(含浸)시켜 회전시키면서 상기 반제품(100') 표면에 투명 박막(50)을 코팅하여 완제품(100)을 완성하는 단계(S170);를 포함하는 유리 조명 갓 제조방법.Coating the transparent thin film 50 on the surface of the semi-finished product 100 'while impregnating the heated semi-finished product 100' in the transparent glass melt tank 40 for coating to complete the finished product 100 (S170); glass lighting shade manufacturing method comprising a. 삭제delete
KR1020090081463A 2009-08-31 2009-08-31 Lamp cover manufacturing method KR100947866B1 (en)