KR100913438B1 - Sectional flooring, and method for manufacturing the same - Google Patents
Sectional flooring, and method for manufacturing the same Download PDFInfo
- Publication number
- KR100913438B1 KR100913438B1 KR1020070111601A KR20070111601A KR100913438B1 KR 100913438 B1 KR100913438 B1 KR 100913438B1 KR 1020070111601 A KR1020070111601 A KR 1020070111601A KR 20070111601 A KR20070111601 A KR 20070111601A KR 100913438 B1 KR100913438 B1 KR 100913438B1
- Authority
- KR
- South Korea
- Prior art keywords
- acrylate
- monomer
- flooring
- coating layer
- butadiene
- Prior art date
Abstract
본 발명은 상부면과 하부면, 및 4개의 측면을 포함하는 바닥재에 있어서, 상기 4개의 측면 중 적어도 한 면은 아크릴레이트계 중합체 코팅층을 포함하는 것인 바닥재를 제공한다.The present invention provides a flooring material comprising an upper surface and a lower surface, and four side surfaces, wherein at least one of the four side surfaces includes an acrylate polymer coating layer.
상기 바닥재는 내수성, 및 내습성이 우수하고, 수명 특성이 우수하여 장기간 사용에 따른 외관 변화가 적고, 시공 후 결합 부위에서 접착이 이루어져 바닥재 간의 연결 부위에서 발생하는 소음이 감소되고, 난방시의 건조나 스팀 청소기 등에 대한 내구성이 우수하다.The flooring material is excellent in water resistance, moisture resistance, excellent life characteristics, less change in appearance with long-term use, adhesion is made at the bonding site after construction, noise generated at the connection site between the flooring is reduced, drying during heating Excellent durability for steam cleaners and the like.
바닥재, 라텍스, 코팅층, 고밀도섬유판, 모양지, 아크릴레이트계 중합체, 스틸렌-부타디엔-아크릴레이트공중합체 Flooring material, latex, coating layer, high density fiberboard, paper, acrylate polymer, styrene-butadiene-acrylate copolymer
Description
본 발명은 조립식 바닥재, 및 이의 제조 방법에 관한 것으로서, 더욱 상세하게는 바닥재는 내수성, 내습성, 및 수명 특성이 우수하고, 시공 후 결합 부위에서 접착이 이루어져 소음이 적으며, 내구성이 우수한 조립식 바닥재, 및 이의 제조 방법에 관한 것이다.The present invention relates to a prefabricated flooring material, and a method for manufacturing the same, and more particularly, the flooring material has excellent water resistance, moisture resistance, and lifespan characteristics, and has low noise due to adhesion at a bonding site after construction. And a method for producing the same.
소비자의 삶의 질 향상과 의식수준 개선으로 주거 바닥재 시장이 변화하고 있다. 즉, 상대적으로 저가이면서도 시공 및 사용이 편리한 PVC의 재질 바닥재에서 친환경적인 자재인 목재를 이용한 원목, 합판, 강화마루, 강마루 등의 바닥재로 변화 확대되고 있다. The residential flooring market is changing due to the improvement of consumer's quality of life and improved consciousness. In other words, it is expanding from PVC material flooring materials, which are relatively inexpensive and easy to construct and use, to flooring materials such as solid wood, plywood, reinforced floor, and steel floor using eco-friendly materials.
상기 목재를 이용한 모든 바닥재는 수분 및 습기에 취약하다는 단점이 있다. 사계절이 뚜렷한 우리나라의 경우, 특히 장마철이나 비가 많이 내리는 여름철에 수분이나 습기에 노출되어 바닥재의 가공 부위가 부풀어 외형이 변화하거나, 바닥재가 변질되는 문제점이 있다.All the flooring using the wood has the disadvantage that it is vulnerable to moisture and moisture. In Korea, where the four seasons are distinct, there is a problem in that the processed part of the flooring is swollen due to exposure to moisture or moisture, especially during the rainy season or in the summer when it rains a lot, or the flooring changes.
특히, 강화마루는 원목 질감이 나도록 라미네이트 처리한 모양지의 두께가 0.2mm 이내의 얇은 층으로 구성되어 있어, 원목마루와 같이 판재 상부의 엣지(edge) 부위를 경사각으로 면취하여 'V' 컷팅을 할 수 없다는 단점이 있다. 상기, 강화마루를 'V' 컷팅하는 경우 상기 모양지의 접합 부분이 드러나게 되어 수분에 더욱 취약하게 된다.In particular, the reinforced floor consists of a thin layer within 0.2mm of the thickness of the laminated paper processed to give a solid wood texture, so that the 'V' cutting can be done by chamfering the edge of the upper part of the plate like a wooden floor at an inclined angle. The disadvantage is that it can't be. When cutting the reinforced floor 'V', the joint part of the paper is exposed, which makes it more vulnerable to moisture.
또한, 상기 강화마루는 상기 라미네이트 처리한 모양지를 포함하고 있어, 각 층간의 재질이 서로 다르기 때문에 경사각으로 면취하였을 경우, 원목의 질감을 가질 수 없게 된다는 미감상의 문제도 있다. 미적 처리를 한다고 하더라도 완전한 방습성을 이루지 못하면 습기가 침투되어 엣지 커팅 부위가 부풀어 오르거나, 건조되어 수축되면서, 바닥재의 변형을 가속화시키게 된다.In addition, the reinforcement floor includes the laminated patterned paper, and there is also a problem of aesthetic feeling that, when chamfered at an inclination angle, the texture of the wood cannot be obtained because the materials between the layers are different from each other. Even if aesthetic treatment does not achieve full moisture resistance, moisture may penetrate and swell the edge cutting area, or dry and shrink, thereby accelerating the deformation of the flooring.
상기 강화마루가 갖는 결점을 보완하기 위하여, 바닥재의 가공 부위를 발수제, 방수제, 또는 왁스 등의 물질을 도포한 예가 있다. 국내 실용신안 등록 제20-0362163호에 따르면, 강화마루의 가공 부위에 도료를 도포 및 건조하고, 다시 이 도료층 상부에 왁스를 코팅하여, 바닥재가 물을 흡수하여 팽창하거나 건조 수축하는 문제를 해소한 선 등록 고안이 알려져 있다.In order to compensate for the drawbacks of the reinforced floor, there is an example in which a material such as a water repellent, a waterproofing agent, or a wax is applied to the processing part of the flooring material. According to Korean Utility Model Registration No. 20-0362163, paint is applied to the processed part of the reinforced floor and dried, and the wax is coated on top of the paint layer again to solve the problem of flooring absorbing water and expanding or shrinking. One line registration scheme is known.
상기 선 등록 고안의 기술에 따르면 일시적인 효과는 있으나, 상기 바닥재가 장시간 물에 노출되었을 경우 바닥재의 가공부위가 부풀어 외관 형상이 변질되거나, 또는 난방에 의하여 건조되는 경우, 틈새 및 소음이 발생하는 등 여러 문제점이 발생한다.According to the technology of the pre-registration design, there is a temporary effect, but when the flooring is exposed to water for a long time, the processing part of the flooring is swollen, deteriorating its appearance, or when dried by heating, gaps and noises are generated. A problem occurs.
본 발명의 목적은 내수성, 및 내습성이 우수하고, 수명 특성이 우수하여 장기간 사용에 따른 외관 변화가 적고, 시공 후 결합 부위에서 접착이 이루어져 바닥재 간의 연결 부위에서 발생하는 소음이 감소되고, 난방시의 건조나 스팀 청소기 등에 대한 내구성이 우수한 바닥재를 제공하고자 하는 것이다.An object of the present invention is excellent in water resistance and moisture resistance, excellent life characteristics, less change in appearance with long-term use, adhesion is made at the bonding site after construction, noise generated at the connection site between flooring is reduced, when heating To provide a durable flooring for drying or steam cleaners.
본 발명의 다른 목적은 상기 바닥재를 제조하는 제조 방법을 제공하는 것이다.Another object of the present invention is to provide a manufacturing method for producing the flooring.
본 발명의 일 구현예에 따르면, 상부면과 하부면, 및 4개의 측면을 포함하는 바닥재에 있어서, 상기 4개의 측면 중 적어도 한 면은 아크릴레이트계 중합체 코팅층을 포함하는 것인 바닥재를 제공한다.According to one embodiment of the present invention, a flooring material comprising an upper surface and a lower surface, and four sides, at least one of the four sides provides a flooring material comprising an acrylate-based polymer coating layer.
상기 아크릴레이트계 중합체 코팅층은 아크릴로 니트릴, 메틸메타크릴레이트, 에틸헥실아크릴레이트, 메틸아크릴레이트, 에틸아크릴레이트, 2-하이드록시에틸아크릴레이트, 2-하이드록시에틸메틸아크릴레이트, N-메틸올아크릴레이트, 글리시딜메틸아크릴레이트, 부틸아크릴레이트, 아크릴 아마이드, n-프로필아크릴레이트 n-부틸아크릴레이트, 헥실메타크릴레이트 2-에틸헥실메타아크릴레이트, 및 이들의 조합으로 이루어진 군에서 선택되는 아크릴레이트계 단량체를 포함하는 아크릴레이트계 중합체를 포함하는 것이 바람직하다.The acrylate polymer coating layer may be acrylonitrile, methyl methacrylate, ethylhexyl acrylate, methyl acrylate, ethyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxyethyl methyl acrylate, N-methylol Acrylate, glycidylmethyl acrylate, butyl acrylate, acrylamide, n-propyl acrylate n-butyl acrylate, hexyl methacrylate 2-ethylhexyl methacrylate, and combinations thereof It is preferable to include the acrylate polymer containing an acrylate monomer.
상기 아크릴레이트계 중합체는 아크릴산, 메타크릴산, 이타콘산, 푸마르산, 말레인산, 말레인산 무수물, 및 이들의 조합으로 이루어진 군에서 선택되는 α,β-불포화카르복실산 단량체를 더 포함하는 것이 바람직하다.The acrylate-based polymer preferably further includes an α, β-unsaturated carboxylic acid monomer selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, fumaric acid, maleic acid, maleic anhydride, and combinations thereof.
상기 아크릴레이트계 중합체는 상기 아크릴레이트계 단량체를 1 내지 20 중량부, 및 상기 α,β-불포화카르복실산 단량체를 1 내지 10 중량부로 포함하는 것이 바람직하다.The acrylate polymer preferably contains 1 to 20 parts by weight of the acrylate monomer, and 1 to 10 parts by weight of the α, β-unsaturated carboxylic acid monomer.
상기 아크릴레이트계 중합체는 유화제, 중합 개시제, 연쇄 이동제, 및 이들의 조합으로 이루어진 군에서 선택되는 첨가제를 상기 아크릴레이트계 단량체와 혼합한 후, 상기 아크릴레이트계 단량체를 중합시켜 제조되는 것이 바람직하다.The acrylate polymer is preferably prepared by mixing an additive selected from the group consisting of an emulsifier, a polymerization initiator, a chain transfer agent, and a combination thereof with the acrylate monomer, and then polymerizing the acrylate monomer.
상기 아크릴레이트계 중합체 코팅층은 스틸렌-부타디엔-아크릴레이트 공중합체 코팅층인 것이 바람직하다.The acrylate polymer coating layer is preferably a styrene-butadiene-acrylate copolymer coating layer.
상기 스틸렌-부타디엔-아크릴레이트 공중합체는 아크릴레이트계 단량체, 및 스틸렌 단량체와 부타디엔 단량체를 공중합시켜 제조할 수 있다.The styrene-butadiene-acrylate copolymer may be prepared by copolymerizing an acrylate monomer and a styrene monomer and a butadiene monomer.
상기 스틸렌-부타디엔-아크릴레이트 공중합체는 상기 아크릴레이트계 단량체를 1 내지 70 중량부, 및 상기 스틸렌 단량체와 부타디엔 단량체를 1 내지 70 중량부로 포함하는 것이 바람직하다.The styrene-butadiene-acrylate copolymer preferably contains 1 to 70 parts by weight of the acrylate monomer, and 1 to 70 parts by weight of the styrene monomer and butadiene monomer.
상기 스틸렌-부타디엔-아크릴레이트 공중합체에서 상기 스틸렌 단량체와 부타디엔 단량체의 중량비는 4 : 6 내지 6 : 4인 것이 바람직하다.In the styrene-butadiene-acrylate copolymer, the weight ratio of the styrene monomer and the butadiene monomer is preferably 4: 6 to 6: 4.
상기 바닥재는 합판, 원목, 강마루, 및 강화마루로 이루어진 군에서 선택되는 것이 바람직하다.The flooring material is preferably selected from the group consisting of plywood, solid wood, steel floor, and reinforced floor.
상기 강화마루는 고밀도 섬유판(high density fiber board), 및 중밀도 섬유 판(medium density fiber board)로 이루어진 군에서 선택되는 섬유판을 포함하는 것이 바람직하다.The reinforcement floor preferably includes a fiber board selected from the group consisting of a high density fiber board and a medium density fiber board.
상기 섬유판의 상부면에 모양지가 라미네이트된 것이 바람직하다.It is preferable that the pattern paper is laminated on the upper surface of the fibreboard.
상기 바닥재는 일 측면에 돌출부를 포함하는 제1 체결 구조를 구비하고, 다른 일 측면에 오목부를 포함하는 제2 체결 구조를 구비하며, 상기 제1 체결 구조가 구비된 일 측면, 상기 제2 체결 구조가 구비된 다른 일 측면, 및 이들의 조합으로 이루어진 군에서 선택되는 측면은 아크릴레이트계 중합체 코팅층을 포함하는 것이 바람직하다.The flooring material has a first fastening structure including a protrusion on one side, a second fastening structure including a recess on the other side, and one side with the first fastening structure, the second fastening structure Another side provided with, and the side selected from the group consisting of a combination thereof preferably includes an acrylate-based polymer coating layer.
상기 바닥재의 상부면과 일 측면을 연결하는 연결면을 더 포함하고, 상기 연결면은 아크릴레이트계 중합체 코팅층을 포함하는 것이 바람직하다.It further comprises a connection surface for connecting one side and the top surface of the flooring, the connection surface preferably comprises an acrylate-based polymer coating layer.
본 발명의 다른 일 구현예에 따르면, 상부면과 하부면, 및 4개의 측면을 포함하는 바닥재의 상기 4개의 측면 중 적어도 한 면에 아크릴레이트계 중합체 라텍스를 도포하여 아크릴레이트계 중합체 코팅층을 형성하는 단계를 포함하는 바닥재의 제조 방법을 제공한다.According to another embodiment of the present invention, to form an acrylate-based polymer coating layer by applying an acrylate-based polymer latex to at least one side of the four sides of the flooring including a top and bottom, and four sides It provides a method for producing a flooring comprising the step.
상기 아크릴레이트계 중합체 라텍스는 스틸렌-부타디엔-아크릴레이트 공중합체 라텍스인 것이 바람직하다.The acrylate-based polymer latex is preferably a styrene-butadiene-acrylate copolymer latex.
상기 아크릴레이트계 중합체 라텍스는 아크릴레이트계 중합체가 물, 유화제, 유동성 개량제, 및 이들의 조합으로 이루어진 군에서 선택되는 용매에 분산된 것이 바람직하다.The acrylate-based polymer latex is preferably the acrylate-based polymer is dispersed in a solvent selected from the group consisting of water, emulsifiers, fluidity improving agents, and combinations thereof.
상기 아크릴레이트계 중합체 라텍스는 아크릴레이트계 중합체를 40 내지 60 중량부, 및 상기 용매를 40 내지 60 중량부로 포함하는 것이 바람직하다.The acrylate polymer latex preferably contains 40 to 60 parts by weight of the acrylate polymer, and 40 to 60 parts by weight of the solvent.
상기 아크릴레이트계 중합체 라텍스의 도포는 스프레이 방법, 및 롤러 방법으로 이루어진 군에서 선택되는 방법을 이용하여 실시하는 것이 바람직하다.Application of the acrylate-based polymer latex is preferably carried out using a method selected from the group consisting of a spray method and a roller method.
상기 아크릴레이트계 중합체 코팅층을 형성한 후, 상기 아크릴레이트계 중합체 코팅층을 건조하는 단계를 더 포함하는 것이 바람직하다.After forming the acrylate-based polymer coating layer, it is preferable to further include the step of drying the acrylate-based polymer coating layer.
상기 건조는 자외선 램프 건조, 및 열풍 건조로 이루어진 군에서 선택되는 방법을 이용하는 것이 바람직하다.The drying is preferably used a method selected from the group consisting of ultraviolet lamp drying, hot air drying.
본 발명의 일 구현예에 따른 바닥재는 내수성, 및 내습성이 우수하고, 수명 특성이 우수하여 장기간 사용에 따른 외관 변화가 적고, 시공 후 결합부위에서 접착이 이루어져 바닥재 간의 연결 부위에서 발생하는 소음이 감소되고, 난방시의 건조나 스팀 청소기 등에 대한 내구성이 우수하다.Flooring according to an embodiment of the present invention is excellent in water resistance and moisture resistance, excellent in life characteristics, less appearance changes with long-term use, and the noise generated at the connection between the flooring material is made at the bonding site after construction It is reduced, and excellent durability against drying at the time of heating or a steam cleaner.
이하, 첨부한 도면을 참조하여 본 발명의 일 구현예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 일 구현예에 한정되지 않는다.DETAILED DESCRIPTION Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art may easily implement the present invention. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of the present invention.
도 1, 및 도 2는 각각 본 발명의 일 구현예에 따른 바닥재의 사시도, 및 평면도이다.1 and 2 are respectively a perspective view and a plan view of a flooring according to an embodiment of the present invention.
도 1, 및 도 2를 참조하면, 본 발명의 일 구현예에 따른 바닥재(100)는 상부 면(110)과 상기 상부면(110)에 대향하는 하부면(120), 및 상기 상부면(110)과 하부면(120)을 둘러싸는 4개의 측면(131, 132, 133, 및 134)을 포함한다. 상기 4개의 측면(131, 132, 133, 및 134) 중 적어도 한 면은 아크릴레이트계 중합체 코팅층(140)을 포함한다.1 and 2, the
도 1, 및 도 2에서는 상기 아크릴레이트계 중합체 코팅층(140)이 양 측면(131, 132)에 형성되는 구조에 대하여 도시하고 있으나, 본 발명은 이에 한정되는 것이 아니고, 상기 아크릴레이트계 중합체 코팅층(140)은 다른 두 측면(133, 134)들에도 형성될 수 있다.1 and 2 illustrate the structure in which the acrylate
상기 아크릴레이트계 중합체 코팅층(140)은 바닥재(100)의 내수성, 및 내습성을 향상시키고, 이에 따라 바닥재(100)의 수분 흡수에 의한 외관 변형을 저지하여 바닥재(100)의 수명을 연장시킨다. 또한, 상기 아크릴레이트계 중합체 코팅층(140)은 상기 바닥재(100)가 장시간 물에 노출되거나, 또는 난방에 의하여 건조되는 경우에도 바닥재(100)의 외관 형상이 변질되는 것을 방지한다.The acrylate-based
상기 아크릴레이트계 중합체 코팅층은 아크릴레이트계 중합체를 포함한다. The acrylate polymer coating layer comprises an acrylate polymer.
상기 아크릴레이트계 중합체는 아크릴로 니트릴, 메틸메타크릴레이트, 에틸헥실아크릴레이트, 메틸아크릴레이트, 에틸아크릴레이트, 2-하이드록시에틸아크릴레이트, 2-하이드록시에틸메틸아크릴레이트, N-메틸올아크릴레이트, 글리시딜메틸아크릴레이트, 부틸아크릴레이트, 아크릴 아마이드, n-프로필아크릴레이트 n-부틸아크릴레이트, 헥실메타크릴레이트 2-에틸헥실메타아크릴레이트, 및 이들의 조합으로 이루어진 군에서 선택되는 아크릴레이트계 단량체가 중합되어 형성되는 것이 바 람직하다. The acrylate polymer is acrylonitrile, methyl methacrylate, ethylhexyl acrylate, methyl acrylate, ethyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxyethyl methyl acrylate, N-methylol acryl Acrylate, glycidylmethyl acrylate, butyl acrylate, acrylamide, n-propyl acrylate n-butyl acrylate, hexyl methacrylate 2-ethylhexyl methacrylate, and combinations thereof Preferably, the rate monomer is polymerized and formed.
상기 아크릴레이트계 중합체는 아크릴산, 메타크릴산, 이타콘산, 푸마르산, 말레인산, 말레인산 무수물, 및 이들의 조합으로 이루어진 군에서 선택되는 α,β-불포화카르복실산 단량체를 더 포함하는 것이 바람직하다. 상기 아크릴레이트계 중합체가 상기 α,β-불포화카르복실산 단량체를 더 포함하는 경우, 상기 아크릴레이트계 중합체의 열안정성, 화학적 안정성, 기계적 안정성, 및 내수성이 증가한다는 점에서 바람직하다.The acrylate-based polymer preferably further includes an α, β-unsaturated carboxylic acid monomer selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, fumaric acid, maleic acid, maleic anhydride, and combinations thereof. When the acrylate polymer further includes the α, β-unsaturated carboxylic acid monomer, it is preferable in that the thermal stability, chemical stability, mechanical stability, and water resistance of the acrylate polymer are increased.
상기 아크릴레이트계 중합체는 상기 아크릴레이트계 단량체를 10 내지 70 중량부, 및 상기 α,β-불포화카르복실산 단량체를 1 내지 10 중량부로 포함하는 것이 바람직하다. 상기 아크릴레이트계 중합체가 상기 α,β-불포화카르복실산 단량체를 상기 범위 내로 포함하는 경우, 열안정성, 화학적 안정성, 기계적 안정성, 및 내수성이 증가한다는 점에서 바람직하다.The acrylate polymer preferably contains 10 to 70 parts by weight of the acrylate monomer, and 1 to 10 parts by weight of the α, β-unsaturated carboxylic acid monomer. When the acrylate polymer includes the α, β-unsaturated carboxylic acid monomer in the above range, it is preferable in that thermal stability, chemical stability, mechanical stability, and water resistance increase.
상기 아크릴레이트계 중합체 코팅층은 스틸렌-부타디엔-아크릴레이트 공중합체 코팅층인 것이 바람직하다.The acrylate polymer coating layer is preferably a styrene-butadiene-acrylate copolymer coating layer.
또한, 상기 스틸렌-부타디엔-아크릴레이트 공중합체 코팅층은 아크릴레이트계 단량체, 및 스틸렌 단량체와 부타디엔 단량체를 중합시켜 제조할 수 있다. 상기 아크릴레이트계 중합체가 상기 스틸렌 단량체와 부타디엔 단량체를 더 포함하는 경우, 접착력이 증가되고, 점탄 성격에 의한 소음 저감 효과가 증대된다는 점에서 바람직하다.In addition, the styrene-butadiene-acrylate copolymer coating layer may be prepared by polymerizing an acrylate monomer and a styrene monomer and a butadiene monomer. When the acrylate polymer further comprises the styrene monomer and the butadiene monomer, it is preferable in that the adhesive force is increased and the noise reduction effect due to the viscoelastic character is increased.
상기 아크릴레이트계 중합체는 상기 아크릴레이트계 단량체를 1 내지 70 중 량부, 및 상기 스틸렌 단량체와 부타디엔 단량체를 1 내지 70 중량부로 포함하는 것이 바람직하고, 상기 아크릴레이트계 단량체를 5 내지 40 중량부, 및 상기 스틸렌 단량체와 부타디엔 단량체를 10 내지 55 중량부로 포함하는 것이 바람직하다. The acrylate polymer is preferably 1 to 70 parts by weight of the acrylate monomer, and 1 to 70 parts by weight of the styrene monomer and butadiene monomer, 5 to 40 parts by weight of the acrylate monomer, and It is preferable to include the styrene monomer and butadiene monomer 10 to 55 parts by weight.
상기 아크릴레이트계 단량체, 및 상기 스틸렌 단량체와 부타디엔 단량체의 함량이 상기 범위 내인 경우, 스틸렌-부타디엔-아크릴레이트 공중합체 코팅층의 내수성이 향상되고, 접착력 및 소음 방지 효과가 크게 증대되어 바람직하다. 상기 함량이 상기 범위를 벗어나면 과도한 접착력에 의한 마루판 재시공 작업이 불가하고, 내수성 및 열안정성의 하락으로 마루판 들뜸 현상이 발생될 수 있다. When the content of the acrylate-based monomer, and the styrene monomer and the butadiene monomer is in the above range, the water resistance of the styrene-butadiene-acrylate copolymer coating layer is improved, the adhesion and noise prevention effect is greatly increased is preferable. When the content is out of the above range, floorboard reconstruction work is not possible due to excessive adhesive force, and floorboard lifting may occur due to a decrease in water resistance and thermal stability.
상기 스틸렌-부타디엔-아크릴레이트 공중합체 코팅층에서 상기 스틸렌 단량체와 부타디엔 단량체의 중량비는 4 : 6 내지 6 : 4인 것이 바람직하다. 상기 스틸렌 단량체와 부타디엔 단량체의 중량비가 상기 범위 내인 경우, 상기 코팅층의 내수성 및 접착력이 우수하고, 탄성 복원력이 우수하여 소음방지 효과가 높아진다는 점에서 바람직하다.In the styrene-butadiene-acrylate copolymer coating layer, the weight ratio of the styrene monomer and the butadiene monomer is preferably 4: 6 to 6: 4. When the weight ratio of the styrene monomer and the butadiene monomer is within the above range, it is preferable in that the water resistance and adhesion of the coating layer are excellent, and the elastic restoring force is excellent, thereby preventing noise.
상기 아크릴레이트계 중합체는 유화제, 중합 개시제, 연쇄 이동제, 및 이들의 조합으로 이루어진 군에서 선택되는 첨가제와 상기 아크릴레이트계 단량체를 혼합한 후, 상기 아크릴레이트계 단량체를 중합시켜 제조할 수 있다.The acrylate polymer may be prepared by mixing an acrylate monomer with an additive selected from the group consisting of an emulsifier, a polymerization initiator, a chain transfer agent, and a combination thereof, and then polymerizing the acrylate monomer.
상기 유화제로는 음이온성, 양이온성, 또는 비이온성 유화제를 사용할 수 있다. 상기 음이온성 유화제로는 비누, 알킬벤젠설폰산염 바람직하게는 직쇄알킬설폰산염(LAS), 소듐도데실벤젠설폰산염(SDBS), 라우릴설페이트염(SLS), 라우릴에테르설페이트염(SLES), 디옥실설포석시네이트염(DOS), 알킬프로필 설포석시네이트염, 또는 지방산 알코올류 등을 바람직하게 사용할 수 있다.Anionic, cationic or nonionic emulsifiers may be used as the emulsifier. As the anionic emulsifier, soap, alkylbenzene sulfonate, preferably linear alkyl sulfonate (LAS), sodium dodecylbenzene sulfonate (SDBS), lauryl sulfate salt (SLS), lauryl ether sulfate salt (SLES), Dioxyl sulfosuccinate salt (DOS), alkylpropyl sulfosuccinate salt, fatty acid alcohol, etc. can be used preferably.
상기 양이온성 유화제로는 스테아릴트리케닐 암모늄염, 벤잘코니움 등을 바람직하게 사용할 수 있다. 상기 비이온성 유화제로는 노닐페놀(NP) 또는 라우릴 알코올의 에틸렌옥사이드(EO) 부가물 등을 바람직하게 사용할 수 있다.As said cationic emulsifier, stearyl trikenyl ammonium salt, benzalconium, etc. can be used preferably. As the nonionic emulsifier, nonylphenol (NP) or ethylene oxide (EO) adduct of lauryl alcohol can be preferably used.
상기 유화제는 단량체 혼합물의 반응 특성에 따라 단일 또는 혼합물 형태로 사용할 수 있다. The emulsifier may be used in the form of a single or a mixture depending on the reaction characteristics of the monomer mixture.
상기 개시제로는 소듐 퍼설페이트, 포타슘 퍼설페이트, 또는 암모늄 퍼설페이트를 사용할 수 있다. 상기 연쇄 이동제(chain-transfer agent)로는 알킬머캅탄류를 바람직하게 사용할 수 있다.Sodium persulfate, potassium persulfate, or ammonium persulfate may be used as the initiator. Alkyl mercaptans can be preferably used as the chain-transfer agent.
상기 아크릴레이트계 중합체 코팅층(140)의 두께는 바닥재 측면의 표면에 코팅층을 형성할 수 있을 정도이면 되고, 특별히 한정되는 것은 아니다.The thickness of the acrylate-based
상기 제1 체결 구조(153)가 구비된 일 측면(132), 상기 제2 체결 구조(154)가 구비된 다른 일 측면(131), 및 이들의 조합으로 이루어진 군에서 선택되는 측면은 아크릴레이트계 중합체 코팅층(140)을 포함하는 것이 바람직하다. 도 1은 상기 양 측면(131, 132)에 체결 구조가 형성된 것을 도시하고 있으나, 본 발명은 이에 한정되지 않으며, 상기 양 측면(131, 132) 이외의 두 측면(133, 134)에도 체결 구조가 형성될 수 있음은 물론이다. The side selected from the group consisting of one
상기 체결 구조(153, 154)가 형성된 측면(131, 132)에 구비된 아크릴레이트계 중합체 코팅층 (140)은 상기 체결 구조(153, 154)를 통하여 습기가 바닥재(100)로 침투하는 것을 방지하여, 바닥재(100)의 내습성, 및 내수성을 향상시킨다. 또 한, 상기 아크릴레이트계 중합체 코팅층(140)은 점성이 있어 바닥재와 바닥재 사이의 체결 구조에 의하여 발생하는 소음을 줄여 준다. 또한, 상기 아크릴레이트계 중합체 코팅층(140)은 수명 특성이 우수하여 장기간 사용으로 인하여 파괴되지 않는다. The acrylate
반면, 종래와 같이 왁스를 이용하여 상기 체결 구조에 코팅층을 형성하는 경우, 상기 왁스는 자체의 점성이 없어 바닥재와 바닥재 사이의 체결 구조에 의해 발생하는 소음을 줄여주지 못하며, 상기 왁스는 장기간 사용시 섬유판 내부로 흡수되어 피막의 형성이 깨어져 버리는 문제점도 있다.On the other hand, in the case of forming a coating layer on the fastening structure using a wax as in the prior art, the wax does not reduce the noise caused by the fastening structure between the flooring material and the flooring material because it is not viscous itself, the wax is a fiber board for a long time use There is also a problem in that the formation of the coating is broken due to absorption into the interior.
일 예로, 상기 제1 체결 구조(153)는 상기 바닥재(100)의 일 측면(132)에 돌출부(151)를 포함하도록 형성되고, 상기 제2 체결 구조(154)는 다른 일 측면(131)에 오목부(152)를 포함하도록 형성될 수 있다. 상기 바닥재의 체결 구조(153, 154)는 다른 바닥재와의 조립을 가능하게 하는 것으로서, 상기 돌출부(151)와 오목부(152)의 결합 구조를 이용하여 두 바닥재를 끼워 맞춰 바닥재를 조립하게 된다. 다만, 상기 체결 구조의 형상은 다양한 형태가 가능하며, 도 1, 및 도 2에 도시된 형상에 한정되는 것은 아니다.For example, the
상기 바닥재(100)로는 종래 바닥재로 사용되는 것이면 어느 것이나 사용 가능하고, 특히 합판, 원목, 강마루, 및 강화마루로 이루어진 군에서 선택되는 것이 바람직하게 사용할 수 있다. As the
상기 강화마루는 고밀도 섬유판(high density fiber board), 및 중밀도 섬유판(medium density fiber board)로 이루어진 군에서 선택되는 섬유판을 포함하는 것이 바람직하다. The reinforcing floor preferably includes a fiber board selected from the group consisting of a high density fiber board and a medium density fiber board.
도 3은 본 발명의 다른 일 구현예에 따른 바닥재의 단면도이다.3 is a cross-sectional view of the flooring according to another embodiment of the present invention.
도 3을 참조하면, 본 발명의 일 구현예에 따른 바닥재(100)는 상기 섬유판(101) 위에 모양지(102)가 라미네이트된 것이 바람직하다. 상기 모양지(102)는 무늬가 인쇄된 종이를 멜라민 수지 등에 함침하여 제조할 수 있으나, 이에 한정되는 것은 아니다. 또한, 상기 모양지는 원목 무늬를 갖는 것이 바람직하다.Referring to FIG. 3, the
또한, 상기 모양지(102) 위에는 멜라민 수지로 함침된 오버레이(overlay)지(도시하지 않음)가 추가될 수 있으며, 상기 섬유판(101) 아래에는 후면지(도시하지 않음)가 추가될 수도 있다. 상기 오버레이지는 바닥재의 표면 강도를 강화시켜 바닥재의 내크스레치, 및 내마모성을 증대시키고, 상기 후면지는 바닥재의 방수 기능을 강화시키는 역할을 한다.In addition, an overlay paper (not shown) impregnated with melamine resin may be added on the
상기 모양지(102)를 상기 섬유판(101) 등에 라미네이트 시키는 방법, 및 상기 모양지(102)에 대한 내용은 종래에 잘 알려진 것이므로 자세한 설명은 생략한다.The method of laminating the
이 때, 상기 바닥재(100)의 양 측면(131, 132)에 형성된 아크릴레이트계 중합체 코팅층(140)은 상기 모양지(102)와 섬유판(101)의 접합 부분을 덮도록 형성되어, 상기 접합 부분의 방습성을 향상시킨다.At this time, the acrylate-based
도 4는 본 발명의 다른 일 구현예에 따른 바닥재의 단면도이고, 도 5는 도 4의 A 부분을 확대한 확대 단면도이다. 상기 도 4, 및 도 5를 참조하면, 상기 바닥재(400)는 상부면(410)과 양 측면(431, 432)을 연결하는 연결면(460)을 더 포함하 고, 상기 연결면(460)은 아크릴레이트계 중합체 코팅층(440)을 포함하는 것이 바람직하다. 상기 아크릴레이트계 중합체 코팅층(440)은 상기 연결면(460)을 덮으면서, 상기 양 측면(431, 432)도 덮도록 형성되는 것이 바람직하다. 4 is a cross-sectional view of a flooring according to another embodiment of the present invention, and FIG. 5 is an enlarged cross-sectional view of an enlarged portion A of FIG. 4. 4 and 5, the
상기 연결면(460)은 시공 높이 불균일에 따른 턱의 발생을 방지하고 조립 시공의 편의성 및 미적 기능성을 향상시키기 위하여 형성되는 것이다. 상기 연결면(460)은 상부면(410)의 에지(edge) 부분을 경사지게 면취하여 형성하는 것으로, 상기 연결면(360)에 형성된 아크릴레이트계 중합체 코팅층(370)은 상기 연결면(360)의 완전한 방습을 이루도록 하여, 습기의 침투에 의한 엣지 커팅 부위의 부품 현상 및 건조 수축 현상 등에 의한 바닥재의 변형을 막는 역할을 한다.The connecting
또한, 상기 바닥재(400)는 섬유판(401) 위에 모양지(402)가 라미네이트되어 형성된다. 이 경우, 상기 연결면을 형성함에 따라 상기 섬유판(401)과 모양지(402)의 접합면이 드러나는 미감상의 문제를 해결하기 위하여, 도료층(470)을 더 형성할 수 있다. 이 때, 상기 도료층(470)을 형성한 후, 상기 도료층(470) 위에 상기 아크릴레이트계 중합체 코팅층(440)을 형성하는 것이 바람직하다.In addition, the
본 발명의 또 다른 일 구현예에 따르면, 상부면과 하부면, 및 4개의 측면을 포함하는 바닥재의 상기 4개의 측면 중 적어도 한 면에 아크릴레이트계 중합체 라텍스를 도포하여 아크릴레이트계 중합체 코팅층을 형성하는 단계를 포함하는 바닥재의 제조 방법을 제공한다.According to another embodiment of the present invention, the acrylate-based polymer coating layer is formed by applying an acrylate-based polymer latex to at least one of the four sides of the flooring material including the upper and lower surfaces, and four sides It provides a method of manufacturing a flooring material comprising the step.
상기 아크릴레이트계 중합체 라텍스는 아크릴레이트계 중합체가 물, 유화제, 유동성 개량제, 및 이들의 조합으로 이루어진 군에서 선택되는 용매에 분산된 것이 바람직하다. 상기 아크릴레이트계 중합체 라텍스에 포함된 아크릴레이트계 중합체는 스틸렌-부타디엔-아크릴레이트 공중합체인 것이 바람직하다. The acrylate-based polymer latex is preferably the acrylate-based polymer is dispersed in a solvent selected from the group consisting of water, emulsifiers, fluidity improving agents, and combinations thereof. The acrylate polymer contained in the acrylate polymer latex is preferably a styrene-butadiene-acrylate copolymer.
상기 아크릴레이트계 중합체 라텍스는 아크릴레이트계 중합체를 40 내지 60 중량부, 및 상기 용매를 40 내지 60 중량부로 포함하는 것이 바람직하고, 아크릴레이트계 중합체를 45 내지 55 중량부, 및 상기 용매를 45 내지 55 중량부로 포함하는 것이 더욱 바람직하다. 상기 용매의 함량이 상기 범위 내인 경우, 상기 아크릴레이트계 중합체 라텍스의 저장 안정성 및 취급 용이성과 더불어 코팅 용이성 확보되어 바람직하다. The acrylate polymer latex preferably contains 40 to 60 parts by weight of the acrylate polymer, and 40 to 60 parts by weight of the solvent, 45 to 55 parts by weight of the acrylate polymer, and 45 to 45 parts of the solvent. More preferably, it contains 55 parts by weight. When the content of the solvent is within the above range, the storage stability and ease of handling of the acrylate-based polymer latex is preferably secured and the coating is secured.
상기 아크릴레이트계 중합체는 상기 바닥재에서의 내용과 같다. 다만 상기 아크릴레이트를 구성하는 단량체를 혼합하고, 상기 단량체를 중합하여 아크릴레이트계 중합체를 제조하는 방법은 당해 기술 분야에서 잘 알려진 내용이므로 구체적인 설명은 생략한다.The acrylate polymer is the same as the content in the flooring. However, a method of preparing the acrylate polymer by mixing the monomers constituting the acrylate and polymerizing the monomer is well known in the art, so a detailed description thereof will be omitted.
상기 아크릴레이트계 중합체 라텍스의 도포는 스프레이 방법, 및 롤러 방법으로 이루어진 군에서 선택되는 방법을 이용하여 실시하는 것이 바람직하고, 스프레이 방법을 이용하는 것이 보다 바람직하다.It is preferable to perform application | coating of the said acrylate type polymer latex using the method chosen from the group which consists of a spray method and a roller method, and it is more preferable to use a spray method.
상기 아크릴레이트계 중합체 코팅층을 형성한 후, 상기 아크릴레이트계 중합체 코팅층을 건조하는 단계를 더 포함하는 것이 바람직하다. 상기 건조는 자외선 램프 건조, 및 열풍 건조로 이루어진 군에서 선택되는 방법을 이용하는 것이 바람직하다. After forming the acrylate-based polymer coating layer, it is preferable to further include the step of drying the acrylate-based polymer coating layer. The drying is preferably used a method selected from the group consisting of ultraviolet lamp drying, hot air drying.
또한, 상기 건조는 30℃ 내지 90℃에서 30초 이내로 실시하는 것이 바람직하 다. In addition, the drying is preferably carried out within 30 seconds at 30 ℃ to 90 ℃.
상기 아크릴레이트계 중합체 라텍스의 도포 및 건조는 2회 이상 실시하는 것도 가능하다. 상기 라텍스의 도포 및 건조를 2회 실시하여 적절한 두께의 코팅층이 형성되도록 할 수 있다.The application and drying of the acrylate-based polymer latex can also be carried out two or more times. The latex coating and drying may be performed twice to form a coating layer having an appropriate thickness.
이하 본 발명의 바람직한 실시예 및 비교예를 기재한다. 그러나 하기한 실시에는 본 발명의 바람직한 일 실시예일뿐 본 발명이 하기한 실시예에 한정되는 것은 아니다.Hereinafter, preferred examples and comparative examples of the present invention are described. However, the following embodiments are only preferred embodiments of the present invention, and the present invention is not limited to the following embodiments.
(바닥재의 제조)(Production of flooring material)
(( 실시예Example 1) One)
아크릴로 니트릴 10 중량부, 메틸메타크릴레이트 20 중량부, 아크릴산 2 중량부, 음이온성 유화제 0.5 중량부, 및 암모늄 퍼설페이트 1 중량부를 혼합한 후, 약 80℃에서 5시간 동안 중합하여 물 55 중량%를 함유하는 아크릴레이트계 중합체 라텍스를 제조하였다.10 parts by weight of acrylonitrile, 20 parts by weight of methyl methacrylate, 2 parts by weight of acrylic acid, 0.5 parts by weight of anionic emulsifier, and 1 part by weight of ammonium persulfate were mixed, followed by polymerization at about 80 ° C. for 5 hours to obtain 55 parts of water. An acrylate polymer latex containing% was prepared.
원목 무늬 모양지가 라미네이트된 고밀도 섬유판의 양 측면에 체결 구조를 형성하고, 상부면과 상기 체결 구조가 형성된 양 측면을 연결하는 연결면을 형성하였다.A fastening structure was formed on both sides of the high-density fiberboard laminated with the wood pattern paper, and a connection surface was formed to connect the upper surface and both sides of the fastening structure.
상기 제조한 아크릴레이트계 중합체 라텍스를 상기 고밀도 섬유판의 체결 구조가 형성된 양 측면과 상기 양 측면의 연결면에 스프레이 방법을 이용하여 1차 도포하고, 상기 아크릴레이트계 중합체 라텍스 도포층 위에 다시 아크릴레이트계 중합체 라텍스를 도포한 후, 바닥재의 표면 온도가40내지 45℃가 되도록 자외선 램프 를 조절하여 약 2초 동안 통과시켜 바닥재를 제조하였다.The prepared acrylate-based polymer latex is first applied to both sides of the fastening structure of the high-density fiber board and the connection surface of the both sides by using a spray method, and the acrylate-based polymer latex is applied again on the application layer After applying the polymer latex, the flooring material was prepared by passing the UV lamp for about 2 seconds so that the surface temperature of the flooring material was 40 to 45 ° C.
(( 실시예Example 2) 2)
부타디엔 단량체 40 중량부, 스틸렌 단량체 47 중량부, 아크릴로 니트릴 5 중량부, 메틸메타크릴레이트 5 중량부, 아크릴산 3 중량부, 2-하이드록시에틸아크릴레이트 2중량부, 음이온성 유화제 0.5 중량부, 및 암모늄 퍼설페이트 1.0 중량부를 혼합한 후, 약 80℃에서 5시간 동안 중합하여 물 55 중량%를 함유하는 스틸렌-부타디엔-아크릴레이트 공중합체 라텍스를 제조하였다. 40 parts by weight of butadiene monomer, 47 parts by weight of styrene monomer, 5 parts by weight of acrylonitrile, 5 parts by weight of methyl methacrylate, 3 parts by weight of acrylic acid, 2 parts by weight of 2-hydroxyethyl acrylate, 0.5 parts by weight of anionic emulsifier, And 1.0 parts by weight of ammonium persulfate were mixed, and then polymerized at about 80 ° C. for 5 hours to prepare a styrene-butadiene-acrylate copolymer latex containing 55% by weight of water.
상기 스틸렌-부타디렌-아크릴레이트 공중합체 라텍스를 이용한 것을 제외하고는 실시예 1과 동일하게 실시하여 바닥재를 제조하였다.Except for using the styrene-butadiene-acrylate copolymer latex was carried out in the same manner as in Example 1 to prepare a flooring.
(( 비교예Comparative example 1) One)
원목 무늬 모양이 라미네이트된 고밀도 섬유판의 양 측면에 체결 구조를 형성하고, 상부면과 상기 체결 구조가 형성된 양 측면을 연결하는 연결면을 형성하였다.A fastening structure was formed on both sides of the high-density fiber board laminated with a wood pattern, and a connection surface was formed to connect the upper surface and both sides of the fastening structure.
상기 고밀도 섬유판의 체결 구조가 형성된 양 측면과 상기 양 측면의 연결면에 스프레이 방법을 이용하여 왁스를 도포한 후, 자외선 램프를 통과시켜 바닥재를 제조하였다.After the wax was applied to both sides of the fastening structure of the high-density fiber board and the connection surface of the both sides by using a spray method, a floor lamp was manufactured by passing an ultraviolet lamp.
(제조된 바닥재의 특성)(Characteristic of manufactured flooring material)
상기 실시예 1, 실시예 2, 및 비교예 1에서 제조된 바닥재를 물이 담긴 용기에(20℃, 상대습도 65%) 침수시켜 시간의 경과에 따른 두께 팽창율(%)을 측정하였고, 그 결과를 하기 표 1에 나타내었다.The bottom ash prepared in Example 1, Example 2, and Comparative Example 1 was immersed in a container containing water (20 ℃, 65% relative humidity) to measure the thickness expansion rate (%) over time, the results It is shown in Table 1 below.
[표 1]TABLE 1
또한, 상기 실시예 1, 실시예 2, 및 비교예 1에서 제조된 바닥재를 결합한 후, 바닥재의 표면에 물을 부어 시간의 경과에 따른 두께 팽창율(%)을 측정하였고, 그 결과를 하기 표 2에 나타내었다.In addition, after combining the flooring material prepared in Example 1, Example 2, and Comparative Example 1, water was poured on the surface of the flooring material to measure the thickness expansion ratio (%) over time, and the results are shown in Table 2 below. Shown in
[표 2]TABLE 2
또한, 상기 실시예 1, 실시예 2, 및 비교예 1에서 제조된 바닥재에 히팅 맨틀(heating mantle, MS-E1040®, 350W, 220V)을 사용하여 바닥재에 스팀을 가한 후, 시간의 경과에 따른 두께 팽창율(%)을 측정하였다.In addition, after applying steam to the flooring using a heating mantle (heating mantle, MS-E1040 ® , 350W, 220V) to the flooring prepared in Example 1, Example 2, and Comparative Example 1, over time Thickness expansion rate (%) was measured.
[표 3]TABLE 3
상기 표 1 내지 표 3에서 상기 두께 팽창율은 하기 수학식 1에 의하여 계산하였다. 참고로, 실험 전 바닥재의 두께는 약 8mm였다.In Tables 1 to 3, the thickness expansion ratio was calculated by the following Equation 1. For reference, the thickness of the flooring material before the experiment was about 8mm.
[수학식 1][Equation 1]
두께 팽창율(%)=(실험 후 바닥재의 두께-실험 전 바닥재의 두께)/실험 전 바 닥재의 두께X 100Thickness Expansion Rate (%) = (Thickness of Flooring after Experiment-Thickness of Flooring Before Experiment) / Thickness of Flooring Material Before
또한, 상기 표 1 내지 표 3에서 상기 개선율은 하기 수학식 2에 의하여 계산하였다.In addition, the improvement rate in Tables 1 to 3 was calculated by the following equation.
[수학식 2][Equation 2]
개선율(%)=(비교예 1의 수치/실시예 2의 수치) X 100% Improvement = (numeric value of comparative example 1 / numeric value of Example 2)
상기 표 1 내지 표 3을 참조하면, 실시예 2의 바닥재가 비교예 1의 바닥재 보다 내수성, 및 스팀에 대한 저항력이 매우 우수한 것을 확인할 수 있다.Referring to Tables 1 to 3, it can be seen that the flooring material of Example 2 is very excellent in water resistance and steam resistance than the flooring material of Comparative Example 1.
본 발명의 단순한 변형 또는 변경은 모두 이 분야의 통상의 지식을 가진 자에 의하여 용이하게 실시될 수 있으며 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.All simple modifications or changes of the present invention can be easily carried out by those skilled in the art, and all such modifications or changes can be seen to be included in the scope of the present invention.
도 1은 본 발명의 일 구현예에 따른 바닥재의 사시도.1 is a perspective view of a flooring according to an embodiment of the present invention.
도 2는 본 발명의 일 구현예에 따른 바닥재의 측면도.Figure 2 is a side view of the flooring according to an embodiment of the present invention.
도 3은 본 발명의 일 구현예에 따른 바닥재의 단면도.3 is a cross-sectional view of the flooring according to an embodiment of the present invention.
도 4는 본 발명의 다른 일 구현예에 따른 바닥재의 단면도.4 is a cross-sectional view of the flooring according to another embodiment of the present invention.
도 5는 도 4의 A 부분을 확대한 확대 단면도.5 is an enlarged cross-sectional view illustrating an enlarged portion A of FIG. 4.
<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>
100 : 바닥재 110 : 상부면100: flooring 110: upper surface
120 : 하부면 140 : 아크릴레이트계 중합체 코팅층 120: bottom surface 140: acrylate polymer coating layer
101 : 섬유판 102 : 모양지101: fiberboard 102: shape paper
153 : 제1 체결 구조 154 : 제2 체결 구조153: first fastening structure 154: second fastening structure
Claims (28)