KR100912636B1 - Keeping cloth for prevention of permeation of mosquitoes bitting, suits and manufacturing method of it's - Google Patents
Keeping cloth for prevention of permeation of mosquitoes bitting, suits and manufacturing method of it's Download PDFInfo
- Publication number
- KR100912636B1 KR100912636B1 KR1020090039322A KR20090039322A KR100912636B1 KR 100912636 B1 KR100912636 B1 KR 100912636B1 KR 1020090039322 A KR1020090039322 A KR 1020090039322A KR 20090039322 A KR20090039322 A KR 20090039322A KR 100912636 B1 KR100912636 B1 KR 100912636B1
- Authority
- KR
- South Korea
- Prior art keywords
- yarn
- fabric
- weaving
- mosquito
- polyester
- Prior art date
Abstract
Description
본 발명은 모기 물림 방지용 원단 및 의복과 그 제조방법에 관한 것으로, 보다 구체적으로는 통기성이 양호하면서 모기의 침이 뚫지 못하는 원단과 그 원단으로 제조된 의복 및 그 원단의 제조방법에 관한 것이다.The present invention relates to a fabric and clothes for preventing mosquito bites, and more particularly, to a fabric that is breathable and not penetrated by mosquitoes, and to a garment made of the fabric and a method of manufacturing the fabric.
모기는 학명으로 쿨리시대(Culicidae)이며, 파리목 모기과의 곤충으로 전 세계에 약 3,500종이 살고 있고, 우리나라에도 9속에 56종이 살고 있는 것으로 알려져 있으며, 알-유충-번데기-성충의 생활환을 갖는 완전변태 곤충이다. The mosquito is the scientific name Culicidae , an insect of the fly mosquito family, and 3,500 species live in the world, and 56 species live in 9 genera in Korea. It is a metamorphosis insect.
암컷 모기는 일생동안 단 한번만 교미하며 그 후로는 수컷 모기를 피하고, 알을 낳기 위해서는 많은 영양분(동물성 단백질)을 필요로 하며 이러한 영양분은 동물의 피에서 섭취하는 것으로, 무더운 여름철 모기에 물리면 가렵고 귀찮은 정신적 스트레스뿐만 아니라 인간에게 치명적인 질병을 옮길 수 있는 해로운 곤충이다. Female mosquitoes mate only once in their life, after which they avoid male mosquitoes, and require a lot of nutrients (animal protein) to lay eggs. These nutrients are taken from the blood of animals. It is a harmful insect that can transmit not only stress, but also fatal diseases to humans.
모기로 인한 전염병은 말라리아, 일본뇌염, 상피병(사상충증), 뎅기열 등이 있는데, 말라리아의 경우 우리나라에서도 매년 지속적으로 감염자 수가 증가하는 추세에 있으며, 뇌염 바이러스도 15세 이하의 어린이들에게는 치명적인 질병이며, 상피병이나 뎅기열과 같은 질병도 모기로부터 전염되는 질병인 것이다. Infections caused by mosquitoes include malaria, Japanese encephalitis, epithelial disease (denomyosis), and dengue fever. Malaria continues to increase in number of infections every year in Korea, and encephalitis virus is also fatal for children under 15 years of age. Diseases such as epithelial disease and dengue fever are also transmitted from mosquitoes.
상기한 바와 같은 모기로 인한 질병으로 고통 받고 있는 모든 나라에서는 모기에 물리지 않고, 모기를 퇴치하기 위한 많은 연구가 이루어지고 있지만 아직까지 모기를 완전히 퇴치하거나 모기에 물리지 않는 제품은 발견되지 않고 있다. In all countries suffering from diseases caused by mosquitoes as described above, a lot of research has been made to combat mosquitoes without mosquito bite, but there are no products that have yet been completely mosquitoed or mosquito bites.
상기한 바와 같은 모기 퇴치를 위해서는 가장 많이 이용되는 것이 모기가 싫어하는 향을 발산하여 모기를 퇴치하는 방법이 있다. In order to combat mosquitoes as described above, there is a method of combating mosquitoes by releasing scents that mosquitoes do not like most.
즉, 인진쑥을 다려 그 물을 스프레이 하는 방법, 허브 향을 발산하는 방법, 쑥을 태워 연기를 발산하는 방법이 있으나, 이는 일시적으로는 효과가 있지만 일정시간이 지나면 다시 모기가 날아오기 때문에 수시로 향을 발산하여야 하는 문제점이 있다. In other words, there are ways to spray the water by spraying Injin mugwort, to give off herb aroma, and to burn smoke from mugwort, but this works temporarily, but after a certain time, the mosquitoes fly again. There is a problem that must be divergent.
또한, 모기에 물리지 않기 위하여 방충망이나 모기장을 치고 생활하는 경우가 있으나, 사람이 언제나 방충망이나 모기장 안에만 있을 수 없어 모기에 물리지 않을 수 없으며, 특히 전방에서 경계근무를 서는 군인, 야간에 낚시를 하는 어부나 낚시꾼, 가축을 돌보는 축산업 종사자 및 야간에 활동하는 많은 사람들에게는 아무런 도움을 주지 못하였다. Also, in order to avoid mosquito bites, people may live with insect screens or mosquito nets, but people cannot stay inside the nets or mosquito nets at all times, so they are forced to stay mosquitoes. No help was given to fishermen, anglers, livestock care workers, and many at night.
따라서, 상기한 바와 같이 야간활동을 하는 동안에도 모기에 물리지 않기 위해서 대한민국 실용신안등록 제 20-0167680호에 모자가 부착된 상의와 벨크로 파스너로 조임하는 하의를 구성함에 있어서, 상의와 하의를 두 겹의 내외 망지로 구성하여, 내 망지는 구멍이 비교적 크게 뚫린 망지로 구성하고 외 망지는 모기가 침투할 수 없을 정도의 구멍이 뚫린 통풍이 원활한 망지로 구성하되 내외 망지의 사이에 적정 간격을 두고 탄성이 우수한 고무 스프링을 설치하여서 되는 곤충 침투 예방 옷이 기재되어 있다. Therefore, in order to avoid mosquito bites during night activities as described above, in the Korean Utility Model Registration No. 20-0167680, in forming a top with a cap and a bottom fastening with velcro fasteners, the top and bottom are doubled. It consists of inner and outer ledges, and the inner ledge is composed of ledges with relatively large holes, and the outer ledges are composed of ventilated ledges with perforated holes that mosquitoes can't penetrate. Insect penetration prevention clothing described by installing this excellent rubber spring is described.
그러나, 상기한 곤충 침투 예방 옷은 두 겹의 내외 망지로 구성하고 내외 망지의 사이에 적정 간격을 두고 탄성이 우수한 고무 스프링을 설치하는 기술이 극히 어려울 뿐만 아니라, 고무 스프링이 파손되면 모기가 침투하지는 못하여도 모기의 침이 옷을 뚫고 피를 빨 수 있어 모기 물림을 방지하기 어려운 문제가 있다. However, the insect penetration prevention clothes described above are composed of two layers of internal and external nets, and it is extremely difficult to install a rubber spring having excellent elasticity at appropriate intervals between the internal and external nets. Even if the mosquito can not penetrate through the clothes to suck the blood is difficult to prevent mosquito bites.
또한, 모기 퇴치용 의복으로는 직물 원단에 모기가 싫어하는 향료를 코팅하여 사용하는 경우도 있으나, 그 향료가 세탁이나 마찰에 의하여 향을 발산하지 못하여 그 기능을 상실하는 경우, 의복을 믿다가 오히려 모기에 물리는 경우가 발생한다.In addition, mosquito-repelling clothing may be used to coat the fabric fabric with a mosquito-like fragrance, but if the perfume loses its function due to washing or friction, the mosquito is believed Bite occurs.
본 발명은 상기와 같은 종래의 제반 문제점을 해결하기 위한 것으로, 본 발명의 목적은 통기성이 좋으면서도 모기의 침이 뚫지 못하는 원단을 제공하고, 그 원단을 이용하여 의복을 제조하여 입으면 의복이 헤어져 구멍이 나지 않는 이상 모기로부터의 물림을 방지할 수 있는 모기 물림 방지 복을 제공하는데 있다.The present invention is to solve the conventional problems as described above, the object of the present invention is to provide a fabric that is breathable but not penetrates the mosquitoes, the fabric is manufactured by using the fabric to wear clothes break up holes The present invention provides a mosquito bite prevention suit that can prevent bites from mosquitoes.
또한, 본 발명은 모기 물림 방지용 원단과 그의 제조방법을 제공함으로써 여름철에 야간활동을 하는 사람들의 건강을 도모하는데 제2의 목적이 있다.In addition, the present invention has a second object to promote the health of people doing night activities in the summer by providing a fabric for preventing mosquito bites.
상기와 같은 목적을 달성하기 위한 본 발명의 원단은 섬도가 50~200데니어이고, 꼬임수가 1000~3000TPM인 강연 폴리에스터 원사 95~99중량%와, 정전기 방지용 은사(銀絲) 또는 동사(銅絲)가 혼방된 80~150데니어의 금속 혼방사 1~5중량%로 되고 상기한 강연 폴리에스터 원사와 금속 혼방사를 경위사로 사용하며 경위사 각각 250~320본/인치의 밀도로 제직하되, 금속 혼방사는 상기한 폴리에스터 원사 20~40본 당 1본으로 배열하여 제직하는 것을 특징으로 한다.Fabric of the present invention for achieving the above object is 95 ~ 99% by weight of a polyester polyester yarn with a fineness of 50 to 200 denier, twist number of 1000 ~ 3000TPM, antistatic silver (銀絲) or verb (銅絲) ) Is a blended 80 ~ 150 denier metal blend yarn 1 ~ 5% by weight, using the above-mentioned lecture polyester yarn and metal blend yarn as the weft yarn, weaving weaving at a density of 250 ~ 320 bone / inch, respectively, Characterized by weaving arranged in one sheet per 20 to 40 polyester yarns described above.
또한, 본 발명은 상기한 원단을 제직하기 위한 방법은 먼저 섬도가 50~200데니어이고, 꼬임수가 1000~3000TPM인 강연 폴리에스터 원사 및 80~150데니어의 금속 혼방사를 준비하는 단계;In addition, the present invention is a method for weaving the fabric, the first step is to prepare a polyester polyester yarn with a fineness of 50 ~ 200 denier, twist number 1000 ~ 3000TPM and metal blend yarn of 80 ~ 150 denier;
준비된 폴리에스터 원사와 금속 혼방사를 원하는 배열로 통경하는 제직 준비 단계; 및 A weaving preparation step of passing the prepared polyester yarn and the metal blend yarn into a desired arrangement; And
제직 준비된 직기에서 경사와 같은 비율로 위사를 공급하여 제직하는 단계로 이루어지는 것을 특징으로 한다. Characterized in that the step of weaving by supplying the weft yarn at the same ratio as the warp in the weaving ready loom.
상기에서, 폴리에스터 원가의 섬도가 50데니어 미만인 경우에는 조밀하게 제직하는 경우 통기성이 저하되어 여름철에 상쾌한 기분을 잃게 되고, 200데니어를 초과하는 경우에는 직물의 공극이 커지므로 모기의 침이 뚫을 수 있는 문제가 발생할 수도 있고, 원단의 무게가 무거워 의복이 무겁게 되는 문제가 발생한다. In the above, if the fineness of the polyester cost is less than 50 denier, breathability is lowered when weaving densely, and the freshness is lost in the summer, and if it exceeds 200 denier, the air gap of the fabric becomes larger, so that the mosquito stings can penetrate. There may be a problem, or the weight of the fabric is heavy, causing a problem of heavy clothing.
또한, 은사 또는 동사와 같은 금속 혼방사를 일정간격으로 배열함으로써 원단에서 발생하기 쉬운 정전기를 방지할 수 있는 것이며, 금속 혼방사가 1중량% 미만인 경우에는 정전기 방지 효과가 저하되며, 5중량%를 초과하면 직물의 질이 저하되면서 단가를 올리는 문제가 발생한다.In addition, it is possible to prevent the static electricity easily generated in the fabric by arranging the metal blend yarn, such as silver or verb at regular intervals, when the metal blend yarn is less than 1% by weight, the antistatic effect is lowered, if it exceeds 5% by weight As the quality of the fabric is degraded, there is a problem of raising the unit price.
또한, 폴리에스터 원사의 꼬임수가 1000TPM 미만이면 직물의 공극이 일정하게 되므로 모기의 침에 의하여 쉽게 뚫릴 수 있으며, 3000TPM을 초과하면 직물원단의 촉감이 저하되는 문제가 있다. In addition, if the number of twists of the polyester yarn is less than 1000TPM, the voids of the fabric is constant, so that it can be easily pierced by the needle of the mosquitoes, if more than 3000TPM there is a problem that the touch of the fabric fabric is lowered.
또한, 본 발명에서 원단의 밀도가 250본/인치 미만이면 원단의 공극이 커지므로 모기의 침이 쉽게 뚫을 수 있으며, 320본/인치를 초과하면 제직하기가 어렵고, 제직 후에도 통기성이 저하되는 문제가 발생한다. In addition, in the present invention, if the density of the fabric is less than 250 / inch, the air gap of the fabric becomes large, so that the mosquito's saliva can be easily penetrated. Occurs.
일반적으로 사용하는 원사의 섬도가 가늘면 제직 밀도를 높이고, 섬도가 굵으 면 제직 밀도를 낮추는 것은 상식적인 것이다. It is common sense to increase the weaving density when the fineness of the yarn used is thin, and to reduce the weaving density when the fineness is thick.
상기와 같은 본 발명의 직물 원단은 강연사를 사용하여 조밀하게 제직하였기 때문에 통기성이 양호하여 옷을 만들어 착용하면 상쾌한 느낌을 주지만, 원단의 공극이 지그재그로 형성되므로 모기의 침이 휘어지지 않는 한 침투할 수 없는 것이다. As the fabric fabric of the present invention as described above is densely woven using a twisted yarn, the breathability is good, making the clothes feel refreshing when worn, but the pores of the fabric is formed in a zigzag, so the mosquito's saliva does not penetrate. I can't.
한편, 본 발명의 모기 물림 방지 원단에 이미 알려져 있는 모기가 싫어하는 향을 발산하는 향료를 스프레이 하거나 코팅하여 사용하면 모기가 일시적으로는 접근하지 않으므로 모기소리가 들리지 않아 심리적으로 안정된 효과를 얻을 수는 있지만 모기에 물리지 않는 효과가 증진되는 것은 아니다.On the other hand, when spraying or coating the fragrance that emits the smell of mosquitoes that are already known to the mosquito bite prevention fabric of the present invention, because the mosquitoes do not approach temporarily, you can not hear the sound of mosquitoes to obtain a psychologically stable effect. Mosquito bites do not improve.
본 발명에 의하면 통기성이 좋으면서도 모기의 침이 뚫지 못하는 원단을 제공하고, 그 원단을 이용하여 의복을 제조하여 입으면 의복이 헤어져 구멍이 나지 않는 이상 장기적으로 사용이 가능하여 언제나 쾌적함을 유지하여 여름철에 야간활동을 하는 사람들이 모기에 물리지 않아 모기를 매개체로 하는 질병을 예방함으로 인류의 건강을 도모하는데 효과가 있다. According to the present invention provides a fabric that is breathable but not mosquito penetrates, and manufactures a garment using the fabric, long-term use can be used as long as the clothing does not break up and punctures to maintain comfort all the time in summer It is effective in promoting the health of mankind by preventing the mosquito-borne disease because people who do night activities are not bitten by mosquitoes.
또한, 본 발명의 모기 물림 방지 원단으로 제조한 옷을 입고 있으면 다른 바르는 약이나 분사식 모기약 또는 모기향을 사용하지 않아도 되기 때문에 별도의 준비물이 없어도 간편하게 모기에 물리지 않게 되는 효과가 있다. In addition, if the clothes made of the anti-mosquito bite fabric of the present invention, there is no need to use any other medicine or spray mosquitoes or mosquitoes because there is an effect that the mosquitoes simply do not need to prepare.
이하 본 발명의 모기 물림 방지용 원단 및 의복과 그 제조방법에 대하여 구체적으로 설명한다.Hereinafter, the mosquito bite prevention fabric and clothing of the present invention and a manufacturing method thereof will be described in detail.
본 발명의 모기 물림 방지용 원단은 섬도가 50~200데니어이고, 꼬임수가 1000~3000TPM인 강연 폴리에스터 원사 95~99중량%와, 정전기 방지용 은사(銀絲) 또는 동사(銅絲)가 혼방된 80~150데니어의 금속 혼방사 1~5중량%로 되고 상기한 강연 폴리에스터 원사와 금속 혼방사를 경위사로 사용하며 경위사 각각 250~320본/인치의 밀도로 제직하되, 금속 혼방사는 상기한 폴리에스터 원사 20~40본 당 1본으로 배열하여 제직하는 것을 특징으로 한다.Mosquito bite prevention fabric of the present invention is 50 ~ 200 denier fineness, twisted yarn 1000 ~ 3000TPM 95 ~ 99% by weight of the yarn, and anti-static silver or verb (80) mixed 1 to 5% by weight of the metal blended yarn of ~ 150 denier, using the above-described gyre polyester yarn and metal blended yarn as theodolite and weaved at a density of 250-320 yarns / inch, respectively, the metal blended yarn It is characterized by weaving arranged in 1 book per 20-40 copies.
상기에서 본 발명에서 사용되는 폴리에스터 원사의 섬도는 단사 섬도를 나타내는 것이고, 섬도가 50~200데니어로 일반적으로 약간 굵은 섬도의 것을 1000~3000TPM으로 강연함으로써 제직 후에 원단의 공극이 커지면서도 그 공극이 꼬임방향으로 삐뚤어지게 되어 모기의 침이 원단을 뚫지 못하도록 하는 것이 중요하며, 섬도가 너무 가늘면 강연을 하여도 밀도가 조밀하게 제직하면 통기성이 저하되어 쾌적한 분위기를 조성할 수 없는 것이다.The fineness of the polyester yarn used in the present invention indicates a single yarn fineness, and the fineness of the fine yarn is 50 to 200 denier, which is generally a bit thick, to 1000 to 3000 TPM. It is important to prevent the mosquito's saliva from penetrating the fabric because it is twisted in the twisting direction, and if the density is too dense even if the lecture is too thin, the breathability is lowered and a pleasant atmosphere cannot be formed.
또한, 합성섬유로 된 원단은 일반적으로 정전기 발생이 심하므로 이를 완화하기 위하여 전기전도성이 좋은 은이나 동이 함유된 금속 혼방사를 일정한 간격마다 배열함으로써 정전기 발생을 예방할 수 있어 보다 쾌적한 원단을 얻을 수 있는 것이다.In addition, since fabrics made of synthetic fibers generally generate severe static electricity, in order to alleviate the static electricity, metal blend yarns containing silver or copper having good electrical conductivity can be arranged at regular intervals, thereby preventing static electricity from being generated, thereby obtaining a more comfortable fabric. .
또한, 필요에 따라 상기한 섬유 원단에 원적외선이나 음이온 발생이 풍부하다고 알려진 바이오세라믹을 폴리에스터 필라멘트의 제조에 혼합하면 상기한 원단을 의복으로 제조하여 입으면 건강에 더욱 좋은 효과가 있음을 알 수 있지만 바이오 세라믹의 함량 조절에 주의하여야 한다. 즉, 바이오세라믹의 함량이 과도하게 사용되면 원사의 강도가 현저하게 저하되며, 너무 적게 사용하면 원적외선이나 음이온 발생이 미미하여 효과를 기대할 수 없기 때문이다. In addition, if bioceramics, which are known to be rich in far-infrared rays or anions, are mixed in the manufacture of polyester filaments, the fabric may be fabricated as a garment, and it may be better for health. Care should be taken in controlling the content of ceramics. That is, if the content of the bioceramic is excessively used, the strength of the yarn is significantly lowered, and if it is used too little, far infrared rays or negative ions are generated and the effect cannot be expected.
따라서 상기 바이오 세라믹은 미세 분말로 하여 폴리에스터 방사할 때에 혼입하는 것이 좋으며 그 함량을 폴리에스터에 대하여 0.5~5중량%를 사용하는 것이 좋다. Therefore, the bio-ceramic is preferably mixed when the polyester spinning as a fine powder, the content of 0.5 to 5% by weight relative to the polyester is preferable.
또한, 본 발명의 모기 물림 방지용 의복은 상기한 모기 물림 방지용 원단을 이용하여 통상의 방법으로 제조된 의류를 포함한다. In addition, the mosquito bite preventing garment of the present invention includes a garment produced by a conventional method using the fabric for preventing mosquito bites.
또한, 본 발명의 모기 물림 방지용 원단의 제조 방법은 먼저 섬도가 50~200데니어이고, 꼬임수가 1000~3000TPM인 강연 폴리에스터 원사 및 80~150데니어의 금속 혼방사를 준비하는 단계;In addition, the method of manufacturing the fabric for preventing mosquito bites of the present invention comprises the steps of first preparing a twisted polyester yarn having a fineness of 50 ~ 200 denier, 1000 ~ 3000TPM twisted yarn and a metal blend yarn of 80 ~ 150 denier;
상기에서 준비된 강연 폴리에스터 원사 20~40 본당 1본의 비율로 금속 혼방사를 통경하여 금속 혼방사가 1~5중량%가 되도록 경사를 배열하는 제직 준비 단계; 및 Weaving preparation step of arranging the inclined so that the metal blend yarn is 1 to 5% by weight through the metal blend yarn at a ratio of 20 to 40 per one yarn polyester yarn prepared above; And
상기에서 제직 준비된 직기에서 경사의 배열과 같은 비율로 위사를 공급하여 제직하는 단계로 이루어지는 것을 특징으로 한다. Characterized in that the weaving prepared by weaving by supplying the weft yarn in the same proportion as the arrangement of the warp in the weaving ready.
즉, 본 발명의 특징은 모기의 침이 뚫지 못하도록 하면서 통기성이 양호한 원단을 공급하기 위한 것으로 그 목적에 적합한 섬도와 연도(꼬임 수) 및 직물의 밀도를 얼마나 적절하게 선택하고 배열하느냐에 있는 것으로, 모기가 성행하는 무더운 여름철에 이용되는 것이므로 양호한 통기성과 삐뚤어지는 공극의 형성이 중요한 것이다.In other words, the characteristics of the present invention is to provide a good breathable fabric while preventing the mosquitoes penetrate, and how to properly select and arrange the fineness and year (twist number) and the density of the fabric suitable for the purpose, mosquito Good breathability and the formation of crooked voids are important because they are used during the hot summer months.
이하에 실시예를 통하여 본 발명을 구체적으로 설명하지만 본 발명이 실시예에 한정되는 것은 아니며 본 발명의 범주 내에서 여러 가지 변형을 기할 수도 있음은 물론이다. Hereinafter, the present invention will be described in detail with reference to Examples, but the present invention is not limited to the Examples, and various modifications may be made within the scope of the present invention.
<실시예 1> <Example 1>
섬도가 100데니어이고, 꼬임수가 1500TPM인 강연 폴리에스터 원사를 경위사로 하고 상기 경사에 120데니어의 은 혼방사를 경사 20본에 1본씩 배열하고, 역시 위사에도 같은 비율로 위입하여 경위사 밀도를 300본/인치로 제직한 후 얻어진 원단을 이용하여 의복을 제조하였다. The twisted polyester yarn with 100 denier and twisted 1500TPM is used as the weft yarn, and 120 denier silver mixed yarns are arranged on the warp yarns in 20 warp yarns, and the weft yarns are also inscribed in the same ratio. A garment was manufactured using the fabric obtained after weaving in / inch.
<실시예 2> <Example 2>
바이오 세라믹이 1중량% 함유된 단사 섬도가 150데니어, TPM이 2000인 폴리에스터 섬유를 사용하고 직물 밀도를 290본 /인치로 한 것 외에는 실시예 1과 같은 방법으로 의복을 제조하였다. A garment was manufactured in the same manner as in Example 1 except that polyester fiber having a single yarn fineness containing 1% by weight of bio ceramics and polyester fiber having a TPM of 2000 was used and the fabric density was 290 / inch.
<실시예 3> <Example 3>
금속 혼방사를 구리 혼방사를 사용하고 혼방사의 배열을 경위사 공히 폴리에스터 사 30본에 혼방사 1본으로 한 것 외에는 실시예 1과 같은 방법으로 의복을 제조하였다. A garment was manufactured in the same manner as in Example 1, except that the metal blended yarn was made of copper blended yarn and the blended yarn was arranged in 30 yarns of polyester yarn with one blended yarn.
<실시예 4> <Example 4>
원단에 모기가 싫어하는 라벤더 향을 스프레이 한 후 의복을 제조한 것 외에는 실시에 1과 같이 방법을 이용하였다. The method was used in the same manner as in Example 1 except that the garment was manufactured after spraying lavender scent that mosquitoes do not like.
상기 실시예 1, 2, 3 및 4에서 얻어진 의복은 실험결과 모두 모기의 침이 뚫지 못하는 것으로 나타났다. The clothes obtained in Examples 1, 2, 3, and 4 were found to be impenetrable to all of the mosquitoes.
특히 실시예 1, 2, 3에서는 모기가 매우 많이 날아들었지만 모기에 물리지는 않았으며, 실시예 4에서 얻어진 의복은 1회 착용 시에는 모기가 근접하지 않았으나, 세탁 후 재 착용하였을 때에는 모기의 접촉에 실시예 1, 2, 3과 차이가 없음을 알 수 있었다. In particular, in Examples 1, 2, and 3, the mosquito flew very much, but was not bitten by mosquitoes. The garment obtained in Example 4 was not close to the mosquito when worn once, but when contacted again after washing, It was found that there is no difference from Examples 1, 2, and 3.
본 발명의 의복에 대한 모기 물림 방지효과의 실험 결과는 다음 표 1 및 표2와 같다. Experimental results of the anti-mosquito bite effect on the clothing of the present invention are shown in Table 1 and Table 2.
이 실험은 국립 창원대학교 기초과학 연구소에서 온도 27±2℃, 습도 75±5% 로 유지한 상태에서 총 5회 반복하여 실시한 결과이다. 실험에 사용한 모기는 흰줄 숲모기(Aedes albopictus)로 일명 전투모기라 불리우는 종으로 군(軍)에서 전투복 및 청바지도 뚫는다는 침투력이 강한 모기 종(種)이다.The experiment was repeated five times at the National Institute of Basic Science, Changwon National University, maintained at a temperature of 27 ± 2 ℃ and a humidity of 75 ± 5%. The mosquito used in the experiment was Aedes albopictus , a so-called combat mosquito, which is a highly invasive mosquito that penetrates military uniforms and jeans.
<표 1> 시험 용역 보고서(1)<Table 1> Test Service Report (1)
※ 흡혈률 = 흡혈수/유인수×100※ Vampire Rate = Vampire Count / Attracted Factor × 100
상기 <표 1>에서 나타난 바와 같이 일반 의류와 비교해 볼 때 모기가 본 발명의 의복은 모기가 흡혈할 수 없는 것으로 나타나 절대 모기에 물리지 않는 것으로 확인되었다. As shown in Table 1, compared to the general clothing, the mosquitoes of the present invention was confirmed that the mosquitoes can not be vampire, never mosquito bite.
<표 2> 시험 용역 보고서(2)<Table 2> Test Service Report (2)
※ 흡혈률 = 흡혈수/유인수×100※ Vampire Rate = Vampire Count / Attracted Factor × 100
상기 <표 2>에서 보는 바와 같이 본 발명 모기 물림 방지복(모기퇴치복)과 사병용 전투복에 대한 모기의 흡혈률을 비교해보면 본 발명 모기물림 방지복은 흡혈률이 0%이고, 사병용 잔투복은 흡혈률이 39.73%로 조사되어 본 발명의 의복은 모기에 거의 물리지 않는 것으로 나타나고 있다. As shown in Table 2, when comparing the mosquito vampires of the present invention mosquito bite suits (mosquito repellent suit) and the combat suits for private soldiers, the mosquito bite suits of the present invention has a vampire rate of 0%, the morbid The vomiting rate was 39.73%, indicating that the clothing of the present invention was hardly bitten by mosquitoes.
본 발명의 모기물림 방지 원단은 모기가 흡혈할 수 없으므로, 이러한 원단으로 제조된 의복이 널리 보급되면 모기로부터의 원치 않는 고통을 해결하고, 보다 쾌적한 삶을 누릴 수 있게 될 것이다. Since the mosquito bite prevention fabric of the present invention can not be a blood-sucking mosquito, if the clothing made of such a fabric is widely spread will solve the unwanted pain from the mosquitoes, will be able to enjoy a more comfortable life.
본 발명의 원단에 자외선을 차단하고 음이온을 발산하여 신진대사를 활성화시킬 수 있으며 원적외선을 방출하는 바이오 세라믹을 첨가함으로써 건강 증징 의류로서의 기능을 추구할 수도 있고, 폴리에스터 필라멘트에 모기를 쫓는 성질을 가진 허브 또는 라벤더 등의 천연 향을 추가할 수도 있음은 물론이다. It can activate the metabolism by blocking ultraviolet rays and emitting negative ions to the fabric of the present invention, and can also pursue the function as a health-enhancing garment by adding a bio-ceramic that emits far infrared rays, and has a property of chasing mosquitoes in polyester filaments. Naturally, you can add natural flavors like herbs or lavender.
- 첨부 - - attachment -
시험 용역 보고서(1) : 2008. 12. 4.Test Service Report (1): December 4, 2008
시험 용역 보고서(2) : 2009. 3. 18.Test Service Report (2): March 18, 2009
Claims (4)