KR100902907B1 - Apparatus and method for mechanical test of optical disk surface - Google Patents
Apparatus and method for mechanical test of optical disk surface Download PDFInfo
- Publication number
- KR100902907B1 KR100902907B1 KR1020080024420A KR20080024420A KR100902907B1 KR 100902907 B1 KR100902907 B1 KR 100902907B1 KR 1020080024420 A KR1020080024420 A KR 1020080024420A KR 20080024420 A KR20080024420 A KR 20080024420A KR 100902907 B1 KR100902907 B1 KR 100902907B1
- Authority
- KR
- South Korea
- Prior art keywords
- optical disk
- polishing wheel
- scratch
- rotating
- optical
- Prior art date
Abstract
본 발명은 광디스크 표면의 기계적 특성을 향상하기 위해 기계적 내구성의 특성을 정량화하기 위한 최적의 평가 장치 및 방법을 제공하기 위한 것으로서, 스크래치를 낼 광디스크를 올려놓고 회전운동을 통해 상기 광디스크를 회전시키는 회전판과, 상기 회전판과 수직하는 위치에 형성되고 상기 광디스크에 접촉되어 상기 광디스크 표면에 기 설정된 하중으로 5회 이하의 상기 회전판의 회전을 통해 스크래치를 발생시키는 하나 이상의 연마 휠(abrasion wheel)을 포함하여 구성되는데 있다.The present invention is to provide an optimum evaluation apparatus and method for quantifying the mechanical durability characteristics to improve the mechanical properties of the optical disk surface, and a rotating plate for placing the optical disk to scratch and rotating the optical disk through a rotational movement; And at least one abrasive wheel formed at a position perpendicular to the rotating plate and contacting the optical disc to generate scratches by rotating the rotating plate five times or less with a predetermined load on the surface of the optical disc. have.
내구성 평가, 광디스크, 스틸 울, 보호막 Durability rating, optical disc, steel wool, protective film
Description
본 발명은 광디스크의 품질 검사에 관한 것으로, 특히 광디스크 표면의 기계적 내구성을 검사하는 장치 및 방법에 관한 것이다.The present invention relates to quality inspection of optical discs, and more particularly, to an apparatus and method for inspecting the mechanical durability of an optical disc surface.
지금까지 기록매체로는 자기 기록방식의 테이프와, 광디스크로서의 LD(Laser Disc) 또는 CD(Compact Disc) 및 최근 대용량의 정보 저장능력을 갖고 탄생된 DVD(Digital Video Disc)등을 들 수 있다.Until now, the recording medium includes a magnetic recording tape, an LD (Laser Disc) or CD (Compact Disc) as an optical disc, and a DVD (Digital Video Disc), which has been recently produced with a large capacity for storing information.
이러한 기록매체 중에서 광디스크는 기존에 사용하였던 자기 기록 방식의 테이프와 기록 방식이 다른 디지털 기록방식을 사용하고 있고, 매우 작은 부피 및 무게를 갖기 때문에 보관 및 이동에 매우 효율적이라는 것에 의하여 소비자들에게 그 호응도가 매우 높은 편이다.Among these recording media, optical discs use digital recording methods different from the conventional magnetic recording tapes, and because they have very small volume and weight, they are very efficient for storage and movement. Is very high.
그러나 어떠한 제품에 있어서든지 제조된 제품이 아무런 하자 없이 사용이 가능해야 하고, 만약 제품의 품질에 문제가 발생되었을 경우에는 제품을 생산한 생산자의 신뢰를 떨어뜨리는 일이 될 것이다.However, in any product, the manufactured product should be able to be used without any defects, and if problems with the quality of the product occur, it will reduce the trust of the producer who produced the product.
이와 같은 부분은 광디스크에서도 마찬가지이다. 특히, 매우 미세한 신호 특 성을 갖는 광디스크는 스크래치, 성형불량, 지문 및 제조과정 중에 이물질 부착 등으로 인해 품질이 양호하지 못하다는 결과를 가져오기도 하였다.The same holds true for optical discs. In particular, optical discs with very fine signal characteristics have resulted in poor quality due to scratches, molding defects, fingerprints, and adhesion of foreign matters during the manufacturing process.
그래서 제조가 완료된 광디스크는 그 다음 공정으로써 품질검사를 행하게 되고, 그 다음에 광디스크 시장으로 출하되고 있다.Thus, the completed optical disc is subjected to quality inspection as a next step, which is then shipped to the optical disc market.
종래 광디스크의 품질 검사는 일반적으로 4개의 측정 드라이브에 의해서 검사하도록 하고 있다.Quality inspection of conventional optical discs is generally carried out by four measuring drives.
우선, 동일장치로부터 제조된 광디스크들의 특성이 같다는 가정하에서 생산자는 제조된 모든 광디스크 중에서 임의의 광디스크를 선택하여 측정 시스템에 장착한다. First, on the assumption that the optical disks manufactured from the same device have the same characteristics, the producer selects an arbitrary optical disk from all the optical disks manufactured and mounts it in the measurement system.
첫 번째 측정 드라이브에서는 광디스크로부터 재생되는 신호에 의하여 고주파신호 및 지터를 측정한다.In the first measurement drive, high frequency signals and jitter are measured by signals reproduced from the optical disc.
두 번째 측정 드라이브에서는 광디스크로부터 재생되는 신호에 기초해서 서보 신호(포커싱 에러신호 및 트랙킹 에러신호)를 측정한다.The second measurement drive measures servo signals (focusing error signal and tracking error signal) based on the signal reproduced from the optical disc.
세 번째 측정 드라이브에서는 품질 검사 수행중인 광디스크의 기계적 특성을 측정한다.The third measuring drive measures the mechanical properties of the optical disc under quality inspection.
그리고 마지막 네 번째 측정 드라이브에서는 광디스크의 광학 특성을 측정한다.And the last fourth measurement drive measures the optical characteristics of the optical disc.
이와 같이 종래의 광디스크 품질 검사는 정보 기록의 정확성과, 광디스크의 기계적 특성 및 광학 특성 등을 검사하게 된다.As described above, the conventional optical disc quality inspection checks the accuracy of information recording, the mechanical characteristics and optical characteristics of the optical disc.
이중, 고밀도 광디스크의 사용중 정보기록/재생용 레이저빔의 입사 표면에 발생할 수 있는 기계적 손상, 즉 스크래치 등은 광디스크의 신호의 열화뿐만 아니라 데이터의 손실, 심한 경우에는 광디스크에 정보를 기록하거나 재생하는 것이 가능하지 않게 되는 상황까지도 발생할 수 있게 되어 광디스크 품질 검사 중 가장 큰 비중을 차지하는 부분이다.Of these, mechanical damage that may occur on the incident surface of the information recording / reproducing laser beam during use of a high density optical disk, ie, scratches, is not only a signal degradation of the optical disk, but also a loss of data and, in severe cases, recording or reproducing information on the optical disk. Even the situation that is not possible can occur, which is the largest part of the optical disc quality inspection.
따라서, 이를 방지하기 위해서 디스크 표면에 기계적 강도나 경도를 향상시키기 위한 보호막(protective coating)을 형성하는 경우가 있다.Therefore, in order to prevent this, a protective coating may be formed on the surface of the disk to improve mechanical strength or hardness.
그러나 이런 기능을 목적으로 디스크 표면에 보호막을 형성한 후 그 보호막의 기계적 특성이 정량화되어야 한다. 즉, 디스크 사용중에 발생할 수 있는 스크래치에 어느 정도 견디는가에 대한 정량화가 필요하다. However, for this purpose, after forming a protective film on the surface of the disk, the mechanical properties of the protective film must be quantified. In other words, it is necessary to quantify how much to withstand scratches that may occur during use of the disc.
이중, 고밀도 광디스크의 표면 내 스크래치를 정량화 하기 위한 평가 방법으로는 펜슬 경도 검사(pencil hardness test) 방법과 테이버 연마 검사(taber abrasion test) 방법 등이 사용되고 있다.Among these, as an evaluation method for quantifying scratches on the surface of a high density optical disk, a pencil hardness test method and a taper abrasion test method are used.
상기 펜슬 경도 검사는 서로 다른 강도를 갖는 펜슬을 직선운동을 통해 디스크에 접촉시켜서 스크래치(scratch)가 발생하는 순간의 펜슬 경도에 대응되는 경도값으로 평가를 하는 방법이다.The pencil hardness test is a method in which pencils having different strengths are contacted with a disk through a linear motion to evaluate the hardness value corresponding to the pencil hardness at the time of scratching.
그러나 상기 펜슬 경도 검사는 펜슬을 통해 사람이 디스크 표면에 접촉을 시켜서 스크래치를 발생시키는 방법으로, 동일한 하중을 계속해서 유지하기 어려울 뿐만 아니라 스크래치의 개수 또한 원하는 만큼 발생하지 않기 때문에 정량적으로 스크래치를 낼 수 없는 문제점이 있다.However, the pencil hardness test is a method in which a person contacts the surface of a disc through a pencil to generate scratches, and it is difficult to keep the same load continuously, and the number of scratches does not occur as much as desired, so that scratches can be quantitatively scratched. There is no problem.
상기 테이버 연마 검사는 일종의 연마 휠 종류로 미국 표준 검사 규격인 ASTM(American Society for Testing and Materials) 기준의 D1004 방법으로 소정의 하중을 주면서 균일하게 표면을 마모시켜 그 견디는 정도 등으로 판단하는 방법이다.The taper polishing test is a kind of polishing wheel, and it is a method of judging the surface by uniformly wearing the surface by applying a predetermined load by the D1004 method of ASTM (American Society for Testing and Materials), which is an American standard inspection standard. .
종래의 테이버 연마 검사 장치는 스크래치를 낼 광디스크를 올려놓고 회전운동을 통해 상기 광디스크를 회전시키고, 상기 회전되는 광디스크와 수직하는 위치에서 일정한 하중을 갖는 다수개의 연마 휠(abrasion wheel)이 상기 광디스크에 접촉되어 상기 광디스크 표면에 일정한 하중으로 최하 10회 이상의 광디스크의 회전을 통해 스크래치를 발생시키게 된다.Conventional taper inspection apparatus is to place the optical disk to scratch, rotate the optical disk through a rotational movement, a plurality of abrasion wheel (abrasion wheel) having a constant load in the position perpendicular to the rotating optical disk on the optical disk In contact with the surface of the optical disc, scratches are generated through rotation of the optical disc at least 10 times at a constant load.
이때, 상기 연마 휠에서 발생되는 하중은 미국 표준 검사 규격인 ASTM(American Society for Testing and Materials) 기준에 1000 gf 이하로 정의되어 있으며, 그 종류로는 CS-10F, CS-10, CS-17를 사용한다.At this time, the load generated from the abrasive wheel is defined as less than 1000 gf in the American Society for Testing and Materials (ASTM) standard, which is the American standard inspection standard, the type is CS-10F, CS-10, CS-17 use.
이와 같이 구성되는 테이버 연마 검사 장치는 그 사용목적이 광디스크에 스크래치를 하여 광디스크 표면의 기계적 내구성을 검사하기 위한 목적으로 설계된 장비가 아니라, 일반 플라스틱 제품의 스크래치 정도를 검사하기 위해 설계된 장비이다.The taper polishing inspection device configured as described above is not designed for the purpose of inspecting the mechanical durability of the optical disk surface by scratching the optical disk, but is designed to inspect the degree of scratching of general plastic products.
따라서, 상기 테이버 연마 검사 장치에서 발생되는 스크래치는 광디스크가 실생활에서 실제 사용중에 발생하는 스크래치와는 큰 차이를 갖게 된다.Therefore, the scratches generated in the taper polishing inspection apparatus have a great difference from the scratches generated during the actual use of the optical disc in real life.
즉, 상기 테이버 연마 검사 장치는 광디스크 표면을 마모시켜 그 견디는 정도 등으로 판단하는 방법으로, 이는 실제 발생하는 스크래치가 그 광디스크를 동작하는 구동체(예를 들어 광디스크 드라이브)에서 반응하여 작동되는 상황과 큰 차이 를 나타내고 있다.That is, the taper polishing inspection apparatus is a method of judging the surface of the optical disk by abrasion and the like, and this is a situation in which a scratch actually occurs in response to a drive body (for example, an optical disk drive) operating the optical disk. And shows a big difference.
따라서, 상기 테이버 연마 장치 검사를 통해 광디스크의 불량 또는 양품으로 분류하는 경우는 현실성 있는 절대 기준값에 따른 정량화된 분류가 아닌 오랜 노하우를 갖는 제조업자의 상대적인 평가에 의한 분류이기 때문에 많은 오류를 범하게 된다. 또한 실생활에서 광디스크에 실제 발생되는 스크래치와 상기 테이버 연마 검사 장치에서 발생된 스크래치의 형태가 크게 다르기 때문에 절대 기준값이 없는 노하우만으로 불량과 양품을 구분해 내기란 더욱 많은 오류를 범하게 될 것이다.Therefore, the classification of defective or good optical discs through the inspection of the tape polishing apparatus causes a lot of errors because the classification is based on a relative evaluation of a manufacturer having long know-how, not a quantitative classification based on a realistic absolute reference value. . In addition, since the scratches that are actually generated on the optical disk and the scratches generated by the tape polishing inspection device in the real life are greatly different, it is more likely to make more errors to distinguish between defective and good products only with know-how without absolute reference values.
이와 같이, 광디스크의 품질에 큰 영향을 미치면서도 현재까지 광디스크 표면의 기계적 내구성을 검사하기 위한 스크래치의 발생정도를 정량화하는 방법이 특별히 없는바, 이에 대한 정량화 방법의 개발이 시급한 실정이다. As described above, there is no particular method for quantifying the degree of occurrence of scratches for inspecting the mechanical durability of the surface of the optical disc while having a great influence on the quality of the optical disc. Therefore, it is urgent to develop a quantification method for this.
따라서 본 발명은 상기와 같은 문제점을 해결하기 위해 안출한 것으로서, 광디스크 표면의 기계적 특성을 향상하기 위해 기계적 내구성의 특성을 정량화하기 위한 최적의 평가 장치 및 방법을 제공하는데 그 목적이 있다.Accordingly, an object of the present invention is to provide an optimum evaluation apparatus and method for quantifying the mechanical durability characteristics in order to improve the mechanical characteristics of the optical disk surface.
본 발명의 다른 목적은 신뢰성을 높이면서 검사 비용을 절감할 수 있는 광디스크 표면의 기계적 내구성 검사 장치 및 방법을 제공하는데 있다.It is another object of the present invention to provide an apparatus and method for testing the mechanical durability of an optical disk surface which can reduce the inspection cost while increasing the reliability.
본 발명의 또 다른 목적은 현실성 있는 절대 기준치를 설정하여 불량 또는 양품의 분류를 신속하고 정확하게 분류하는 장치 및 방법을 제공하는데 있다.It is still another object of the present invention to provide an apparatus and method for quickly and accurately classifying a defective or good product by setting a realistic absolute reference value.
본 발명의 또 다른 목적은 실생활에서 발생될 수 있는 스크래치와 가장 가까운 형태의 스크래치를 유발하여 광디스크 표면의 기계적 내구성 검사의 신뢰도를 높이는데 있다.Another object of the present invention is to increase the reliability of the mechanical durability inspection of the surface of the optical disk by causing the scratches closest to the scratches that can occur in real life.
본 발명은 광디스크를 회전시키기 위한 회전판과, 상기 광디스크에 접촉하여 스크래치를 발생시키며, 제 1 방향으로 회전하는 연마 휠(abrasion wheel)과 제 2 방향으로 회전하는 연마 휠(abrasion wheel)으로 구성된 복수개의 연마 휠을 포함하되, 상기 스크래치는 상기 연마 휠들이 상기 회전되는 광디스크에 기설정된 하중을 가하는 동안 상기 광디스크가 5회까지 회전하는 동안 발생하며, 상기 광디스크 표면에 발생한 스크래치로부터 결과값과 기 설정된 기준값을 비교하여 상기 광 디스크가 내구성을 갖고 있는지를 결정하는 것을 특징으로 하는 광디스크 표면의 스 크래치 내구성 검사 장치를 제공한다.The present invention provides a plurality of rotating plates for rotating an optical disk, a polishing wheel that generates scratches in contact with the optical disk, and an abrasion wheel that rotates in a first direction and an abrasion wheel that rotates in a second direction. And a polishing wheel, wherein the scratch is generated while the optical disk rotates up to five times while the polishing wheels apply a predetermined load to the rotating optical disk, and the resultant value and the predetermined reference value are determined from scratches on the surface of the optical disk. And a scratch durability inspection apparatus for the surface of the optical disk, characterized in that it is determined whether the optical disk has durability.
상기 연마휠들에 의해서 상기 광디스크에 가해지는 하중은 0.5N(50gf)에서 16.2(1650gf)인 것을 특징으로 한다.The load applied to the optical disk by the polishing wheels is characterized in that from 0.5N (50gf) to 16.2 (1650gf).
상기 광 디스크가 기 설정된 내구성을 갖고 있는 경우, 상기 광 디스크의 표면에 발생한 스크래치의 깊이는 0~2μm인 것을 특징으로 한다.When the optical disk has a predetermined durability, the scratch depth generated on the surface of the optical disk is characterized in that 0 ~ 2μm.
상기 연마휠은 CS-10F, CS-10, CS-17 중의 하나인 것을 특징으로 한다.The polishing wheel is characterized in that one of CS-10F, CS-10, CS-17.
상기 복수개의 휠은, 시계 방향으로 회전하는 제 1 연마휠과, 반시계 방향으로 회전하는 제 2 연마휠을 더 포함하는 것을 특징으로 한다.The plurality of wheels may further include a first polishing wheel that rotates in a clockwise direction and a second polishing wheel that rotates in a counterclockwise direction.
상기 연마휠의 타입은 CS-10F이고, 상기 각 연마휠의 기설정된 하중은 2.5N인 것을 특징으로 한다.The polishing wheel is of type CS-10F, and the predetermined load of each polishing wheel is 2.5N.
또한, 본 발명은 제 1 방향으로 회전하는 적어도 하나의 연마휠과, 제 1 방향과 반대 방향인 제 2 방향으로 회전하는 적어도 하나의 연마휠을 포함하는, 기설정된 하중을 갖는 연마휠을 광디스크의 표면에 접촉시키는 단계; 상기 광디스크의 표면에 스크래치를 발생시키기 위해, 상기 광 디스크가 5회 까지 회전하는 동안 상기 광디스크의 표면과 상기 연마휠의 표면의 접촉을 유지하는 단계; 상기 광 디스크 표면으로부터 발생한 스크래치로부터의 결과값과 기 설정된 기준값을 비교하여 상기 광 디스크가 내구성을 갖고 있는지 여부를 결정하는 단계를 포함하는 것을 특징으로 하는 광디스크 표면의 스크래치 내구성 검사방법을 제공한다.The present invention also provides a polishing wheel having a predetermined load, comprising at least one polishing wheel that rotates in a first direction and at least one polishing wheel that rotates in a second direction opposite to the first direction. Contacting the surface; Maintaining contact between the surface of the optical disk and the surface of the polishing wheel while the optical disk is rotated up to five times to cause scratches on the surface of the optical disk; And comparing a result value from scratches generated from the surface of the optical disk with a predetermined reference value to determine whether the optical disk has durability.
상기 스크래치를 발생시키는 동안 상기 연마휠에 의해서 상기 광디스크에 가해지는 힘은 0.5N(50gf)이상 16.2N(1650gf)이하인 것을 특징으로 한다.The force applied to the optical disk by the polishing wheel while generating the scratch is characterized in that less than 0.5N (50gf) 16.2N (1650gf) or less.
상기 연마휠은 CS-10F, CS-10, CS-17 중의 하나인 것을 특징으로 한다.The polishing wheel is characterized in that one of CS-10F, CS-10, CS-17.
상기 결정하는 단계에서, 상기 스크래치의 깊이가 0~2μm일 때에, 상기 광 디스크는 양품인 것으로 판단하며, 상기 스크래치의 깊이 2μm 이상이면, 상기 광디스크를 불량품인 것으로 판단하는 것을 특징으로 한다.In the determining step, when the scratch depth is 0 ~ 2μm, it is determined that the optical disc is good, and if the scratch depth is 2μm or more, the optical disc is determined to be defective.
또한, 본 발명은 광 디스크의 표면에 스크래치를 발생시키기 위해, 기설정된 하중을 갖는, 제 1 방향으로 회전하는 적어도 하나의 연마휠과, 제 2 방향과 반대방향으로 회전하는 적어도 하나의 연마휠을 상기 광 디스크의 표면에 접촉시키는 단계; 상기 광 디스크의 표면에 발생한 스크래치로부터 결과값을 기 설정된 기준값과 비교하는 단계; 상기 비교하는 단계의 결과에 기초하여 상기 광 디스크가 내구성을 갖고 있는지 평가하는 단계를 포함하는 광 디스크 표면의 스크래치 내구성 검사방법을 제공한다.In addition, the present invention provides at least one polishing wheel that rotates in a first direction and at least one polishing wheel that rotates in a direction opposite to the second direction, to have a predetermined load on the surface of the optical disk. Contacting a surface of the optical disk; Comparing a result value with a predetermined reference value from scratches generated on the surface of the optical disk; A method for inspecting scratch durability of the surface of an optical disk, the method comprising evaluating whether the optical disk has durability based on the result of the comparing step.
상기 스크래치는, 상기 광 디스크가 5회까지 회전하는 동안, 상기 광디스크의 표면과 상기 연마휠의 접촉에 의해서 발생하는 것을 특징으로 한다.The scratch is characterized in that it occurs by contact of the surface of the optical disk with the polishing wheel while the optical disk is rotated up to five times.
상기 스크래치는 상기 광 디스크가 1회 내지 5회 회전하는 동안, 상기 광디스크의 표면과 상기 연마휠의 접촉에 의해서 발생하는 것을 특징으로 한다.The scratch may be caused by contact of the surface of the optical disk with the polishing wheel while the optical disk is rotated one to five times.
상기 복수개의 휠은 2개이고, 상기 각 휠의 타입은 CS-10F인 것을 특징으로 한다.The plurality of wheels are two, each type of wheel is characterized in that the CS-10F.
상기 각 CS-10F의 하중은 2.5N인 것을 특징으로 한다.Each CS-10F is characterized in that the load is 2.5N.
또한, 본 발명은 제 1 방향으로 회전하는 연마휠과, 제 1 방향과는 반대방향인 제 2 방향으로 회전하는 연마휠을 포함하는 복수개의 휠이 기 설정된 하중을 갖 고, 상기 기록매체의 표면에 스크래치를 발생시키기 위한 접촉하는 단계와, 상기 기록매체의 표면에 발생된 결과값을 기 설정된 기준값과 비교하는 단계와, 상기 비교단계의 결과에 기초하여 상기 기록매체가 기 설정된 내구성을 갖고 있는지 여부를 평가하는 단계를 포함하는 방법을 이용하여, 스크래치에 대해서 충분한 내구성을 갖고 있는지 여부가 검사될 수 있는 기록매체를 제공한다.In addition, the present invention provides a plurality of wheels including a polishing wheel that rotates in a first direction and a polishing wheel that rotates in a second direction opposite to the first direction has a predetermined load, and the surface of the recording medium Contacting to generate scratches, comparing a result value generated on the surface of the recording medium with a preset reference value, and whether the recording medium has a predetermined durability based on the result of the comparing step. Using a method comprising the step of evaluating, it provides a recording medium that can be inspected whether or not it has sufficient durability against scratches.
상기 스크래치는, 상기 광 디스크가 5회까지 회전하는 동안, 상기 광디스크의 표면과 상기 연마휠의 접촉에 의해서 발생하는 것을 특징으로 한다.The scratch is characterized in that it occurs by contact of the surface of the optical disk with the polishing wheel while the optical disk is rotated up to five times.
상기 스크래치는 상기 광 디스크가 1회 내지 5회 회전하는 동안, 상기 광디스크의 표면과 상기 연마휠의 접촉에 의해서 발생하는 것을 특징으로 한다.The scratch may be caused by contact of the surface of the optical disk with the polishing wheel while the optical disk is rotated one to five times.
본 발명에 따른 광디스크 표면의 기계적 내구성 검사 장치 및 방법은 다음과 같은 효과가 있다.Apparatus and method for testing the mechanical durability of an optical disk surface according to the present invention have the following effects.
첫째, 스크래치의 발생 정보를 정량화하여 표면 기계 특성을 향상시킬 수 있어서 광디스크의 고밀도 구현에 따른 데이터 보존성을 더욱 증가시킬 수 있다.First, the surface mechanical characteristics can be improved by quantifying the occurrence information of the scratch, thereby further increasing data retention due to the high density implementation of the optical disk.
둘째, 손쉽고 정확하게 광디스크의 품질을 검사할 수 있으므로 신뢰성을 높이는 것이 가능하다.Second, since the quality of the optical disk can be inspected easily and accurately, it is possible to increase the reliability.
셋째, 짧은 시간에 원하는 만큼의 스크래치를 형성할 수 있게 되어 광디스크 표면의 기계적 내구성 검사에 따른 테스트 시간을 줄이면서 제조비용을 절감시킬 수 있다. Third, it is possible to form as many scratches as desired in a short time to reduce the manufacturing time while reducing the test time according to the mechanical durability inspection of the optical disk surface.
이상 설명한 내용을 통해 당업자라면 본 발명의 기술 사상을 일탈하지 아니 하는 범위에서 다양한 변경 및 수정이 가능함을 알 수 있을 것이다.Those skilled in the art will appreciate that various changes and modifications can be made without departing from the spirit of the present invention.
따라서, 본 발명의 기술적 범위는 실시예에 기재된 내용으로 한정되는 것이 아니라 특허 청구의 범위에 의하여 정해져야 한다.Therefore, the technical scope of the present invention should not be limited to the contents described in the embodiments, but should be defined by the claims.
상기와 같은 목적을 달성하기 위한 본 발명에 따른 광디스크 표면의 기계적 내구성 검사 장치의 특징은 스크래치를 낼 광디스크를 올려놓고 회전운동을 통해 상기 광디스크를 회전시키는 회전판과, 상기 회전판과 수직하는 위치에 형성되고 상기 광디스크에 접촉되어 상기 광디스크 표면에 기 설정된 하중으로 5회 이하의 상기 회전판의 회전을 통해 스크래치를 발생시키는 하나 이상의 연마 휠(abrasion wheel)을 포함하여 구성되는데 있다.Features of the mechanical durability inspection device of the surface of the optical disk according to the present invention for achieving the above object is a rotary plate for placing the optical disk to scratch and rotate the optical disk through a rotational movement, and is formed in a position perpendicular to the rotating plate And one or more abrasion wheels that come into contact with the optical disc and cause scratches by rotating the rotary plate five times or less with a predetermined load on the surface of the optical disc.
이때, 상기 연마 휠을 통해 기 설정된 하중은 스크래치 깊이가 2㎛ 깊이를 유발하는 하중 조건인 50gf 이상에서 1650gf 이하인 것이 바람직하다.At this time, the predetermined load through the polishing wheel is preferably 1650gf or less at 50gf or more load condition that the scratch depth causes a 2㎛ depth.
*그리고 상기 연마 휠은 CS-10F, CS-10, CS-17 중 어느 하나로 구성되는 것이 바람직하다.And the polishing wheel is preferably composed of any one of CS-10F, CS-10, CS-17.
상기와 같은 목적을 달성하기 위한 본 발명에 따른 광디스크 표면의 기계적 내구성 검사 방법의 특징은 회전판 위에 광디스크를 고정시킨 후, 상기 회전판과 함께 상기 광디스크를 회전시키는 단계와, 상기 회전하는 광디스크 상단에서 스크래치 검사에 따라 기 설정된 소정 하중을 상기 광디스크와 수직 방향으로 가하여 상기 광디스크와 연마 휠의 접촉 하중을 증가하는 단계와, 5회 이하로 기 설정된 광디스크의 회전수만큼 상기 광디스크와 연마 휠의 접촉 하중을 유지한 후, 상기 연마 휠의 수직운동을 통해 상기 광디스크에 접촉된 연마 휠을 이격시키는 단계와, 상기 스크래치된 광디스크를 회전판에서 분리하여 상기 광디스크 표면에 발생된 스크래치의 깊이를 기 설정된 절대 기준치와 비교하여, 불량과 양품을 구분하는 단계를 포함하여 이루어지는데 있다.Features of the mechanical durability test method of the surface of the optical disk according to the present invention for achieving the above object is the step of fixing the optical disk on the rotating plate, rotating the optical disk with the rotating plate, and scratch inspection on the rotating optical disk Increasing a contact load between the optical disc and the polishing wheel by applying a predetermined predetermined load in a direction perpendicular to the optical disc, and maintaining the contact load between the optical disc and the polishing wheel by the number of rotations of the predetermined optical disc less than five times. Thereafter, by separating the polishing wheel in contact with the optical disk through the vertical movement of the polishing wheel, separating the scratched optical disk from the rotating plate to compare the depth of the scratch generated on the surface of the optical disk with a predetermined absolute reference value, Including the step of distinguishing between defective and good To lose.
이때, 상기 회전판 위에 검사하고자 하는 다른 광디스크를 위치시켜 상기 동작을 반복하여 불량과 양품을 구분하는 단계를 더 포함하여 이루어지는 것이 바람직하다. At this time, it is preferable to further comprise the step of positioning the other optical disk to be inspected on the rotating plate to repeat the operation to distinguish between good and bad.
그리고 상기 연마 휠을 통해 기 설정된 하중은 연마 힐 CS-10F를 사용하고, 광디스크의 회전수를 1번만 회전한 조건에서, 하중은 50~250gf로 더욱 바람직하게는 150gf로 정량화하는 것이 바람직하다.The predetermined load through the polishing wheel uses polishing heel CS-10F, and under the condition that the rotation speed of the optical disc is rotated only once, the load is preferably quantified to 50 to 250 gf, more preferably to 150 gf.
또한, 상기 연마 휠을 통해 기 설정된 하중은 연마 힐 CS-10을 사용하고, 광디스크의 회전수를 1번만 회전한 조건에서, 하중은 650~850gf로 더욱 바람직하게는 750gf로 정량화하는 것이 바람직하다.In addition, the predetermined load through the polishing wheel using the polishing heel CS-10, under the condition that the rotation speed of the optical disk only once, the load is preferably quantified to 650gf to 850gf more preferably 750gf.
그리고, 상기 연마 휠을 통해 기 설정된 하중은 연마 힐 CS-17을 사용하고, 광디스크의 회전수를 1번만 회전한 조건에서, 하중은 1200~1400gf로 더욱 바람직하게는 1350gf로 정량화하는 것이 바람직하다.In addition, the predetermined load through the polishing wheel uses polishing heel CS-17, and under conditions in which the rotation speed of the optical disc is rotated only once, the load is preferably quantified to 1200 to 1400 gf, more preferably 1350 gf.
아울러 상기 불량 및 양품을 구분하는 단계는 상기 광디스크 표면에 발생된 스크래치의 깊이가 0㎛ 이상에서 2㎛ 미만인 경우는 양품으로 구분하고, 상기 광디스크 표면에 발생된 스크래치의 깊이가 2㎛ 이상인 경우는 불량으로 구분하는 것이 바람직하다.In addition, the step of distinguishing the defect and good quality is classified as good quality when the scratch depth generated on the surface of the optical disc is less than 0㎛ more than 2㎛, if the depth of the scratch generated on the surface of the optical disc is more than 2㎛ It is preferable to divide by.
또한, 상기 기 설정된 광디스크의 회전수는 5회 이하의 회전수인 것이 바람직하다.In addition, the preset rotation speed of the optical disc is preferably 5 rotations or less.
그리고 상기 절대 기준치는 2㎛인 것이 바람직하다.And it is preferable that the said absolute reference value is 2 micrometers.
본 발명의 다른 목적, 특성 및 잇점들은 첨부한 도면을 참조한 실시예들의 상세한 설명을 통해 명백해질 것이다.Other objects, features and advantages of the present invention will become apparent from the following detailed description of embodiments taken in conjunction with the accompanying drawings.
본 발명에 따른 광디스크 표면의 기계적 내구성 검사 장치 및 방법의 바람직한 실시예에 대하여 첨부한 도면을 참조하여 설명하면 다음과 같다.A preferred embodiment of the apparatus and method for testing the mechanical durability of an optical disk surface according to the present invention will be described with reference to the accompanying drawings.
도 1 은 본 발명에 따른 테이버 연마 검사 장치를 나타낸 구성도이다.1 is a block diagram showing a taper polishing inspection apparatus according to the present invention.
도 1 과 같이 광디스크 표면의 기계적 내구성 검사 장치는 스크래치를 낼 광디스크(30)를 올려놓고 회전운동을 통해 상기 광디스크(30)를 회전시키는 회전판(20)과, 상기 회전판(20)과 수직하는 위치에 형성되고 상기 광디스크(30)에 접촉되어 상기 광디스크(30) 표면에 기 설정된 하중으로 5회 이하의 상기 회전판(20)의 회전을 통해 스크래치를 발생시키는 다수개의 연마 휠(abrasion wheel)(10)로 구성된다.As shown in FIG. 1, the apparatus for testing the mechanical durability of the surface of an optical disk includes a
이때 상기 연마 휠의 종류로는 CS-10F, CS-10, CS-17를 사용한다.In this case, CS-10F, CS-10, and CS-17 are used as the polishing wheel.
이와 같이 구성된 본 발명에 따른 광디스크 표면의 기계적 내구성 검사 방법을 첨부한 도면을 참조하여 상세히 설명하면 다음과 같다.Referring to the accompanying drawings, the mechanical durability inspection method of the optical disk surface according to the present invention configured as described in detail as follows.
도 2 는 본 발명에 따른 광디스크 표면의 기계적 내구성 검사 방법을 나타낸 흐름도이다.2 is a flowchart illustrating a mechanical durability inspection method of an optical disk surface according to the present invention.
도 2와 같이, 먼저, 회전판(20) 위에 광디스크(30)를 고정시킨 후, 상기 회전판(20)과 함께 상기 광디스크(30)를 회전시킨다(S10).As shown in FIG. 2, first, the
이어, 상기 회전하는 광디스크 상단에서 연마휠(10)의 수직운동을 통해 광디스크를 접촉한다(S20).Subsequently, the optical disk contacts the optical disk through the vertical movement of the
그리고 스크래치 검사에 따라 기 설정된 소정 하중을 상기 광디스크(30)와 수직 방향으로 가하여 상기 광디스크와 연마 휠(10)의 접촉 하중을 증가시킨다(S30). In addition, the predetermined load is applied in the vertical direction to the
그리고 상기 기 설정된 광디스크(30)의 회전수만큼 상기 광디스크(30)와 연마 휠(10)의 접촉 하중을 유지한 후, 상기 연마 휠(10)의 수직운동을 통해 상기 광디스크(30)에 접촉된 연마 휠(10)을 이격시킨다(S40).And after maintaining the contact load of the
이와 같이, 상기 회전되는 광디스크(30) 표면은 소정 하중 및 기 설정된 회전수에 따라 접촉된 연마 휠(10)에 의해 도 2와 같이 광디스크에 소정의 스크래치 패턴이 생성되게 된다. As described above, a predetermined scratch pattern is generated on the optical disk as shown in FIG. 2 by the
도 3과 같이, 본 발명에 따른 테이버 연마 테스터를 이용하여 광디스크에 소정의 스크래치 패턴을 형성하고, 이 결과 나타난 스크래치 깊이(depth)를 구하게 된다.As shown in FIG. 3, a predetermined scratch pattern is formed on an optical disc using a taper polishing tester according to the present invention, and the resulting scratch depth is obtained.
도 4 는 본 발명에 따른 광디스크에 가하는 하중에 따라 발생되는 스크래치 깊이를 실험치를 통해 나타낸 도면이다. 여기서 보호막이 없는 디스크(bare disc)와 하드 코팅된 디스크(hard-coated disc)를 실험치로 사용한다.4 is a view showing the scratch depth generated according to the load applied to the optical disk according to the present invention through an experimental value. Bare discs and hard-coated discs are used as experimental values.
도 4와 같은 실험을 통해, 스크래치 깊이가 2㎛ 보다 깊은 스크래치가 발생 되는 경우 광디스크의 동특성 평가시 서보(servo) 에러를 유발하게 되는 것을 측정하게 되었다.Through the experiment as shown in FIG. 4, it was measured that if a scratch depth of more than 2 μm is generated, a servo error is caused when the dynamic characteristics of the optical disc are evaluated.
즉, 광디스크 표면의 내구성 검사시 상기 2㎛를 광디스크의 불량 및 양품을 평가하는 절대 기준치로 정의하고, 2㎛의 스크래치 깊이를 유발하는 스틸 울 테스트 조건을 찾아서, 이 조건에서 광디스크 표면의 기계적 내구성을 검사하여 스크래치의 발생정도를 정량화하게 된다.That is, when the durability test of the surface of the optical disc, the 2μm is defined as an absolute reference value for evaluating the defect and good quality of the optical disc, and the steel wool test condition that causes the scratch depth of 2 μm is found and the mechanical durability of the optical disc surface is improved under this condition. The test will quantify the occurrence of scratches.
도 5 는 본 발명에 따른 광디스크 표면의 기계적 내구성 검사 방법을 나타낸 도면으로, 연마 휠의 종류인 CS-10F, CS-10, CS-17에 각각 가해지는 하중에 따라 광디스크에 발생되는 스크래치의 깊이를 그래프로 나타내고 있다.5 is a view showing a mechanical durability test method of the surface of the optical disk according to the present invention, the depth of the scratch generated in the optical disk according to the load applied to the CS-10F, CS-10, CS-17, respectively, the kind of the grinding wheel It is shown in the graph.
도 5와 같이, 상기 연마 휠에서 발생되는 하중은 50~1650gf로 정량화하며, 이는 상기 연마 휠의 종류에 따라 서로 다르게 정량화를 설정하게 된다.As shown in Figure 5, the load generated in the polishing wheel is quantified to 50 ~ 1650gf, which is set differently depending on the type of the polishing wheel.
즉, 테이버 연마 테스트에서 연마 힐의 종류를 CS-10F를 사용하고, 광디스크의 회전수를 1번만 회전한 조건에서, 스크래치 깊이가 2㎛ 깊이를 유발하는 하중 조건은 50~250gf로 더욱 바람직하게는 150gf임을 알 수 있다.That is, in the taper polishing test, CS-10F is used as the type of polishing heel, and under the condition that the rotation speed of the optical disc is rotated only once, the load condition that the scratch depth causes the depth of 2 μm is more preferably 50 to 250 gf. It can be seen that is 150gf.
그리고 연마 휠의 종류를 CS-10을 사용하고, 광디스크의 회전수를 1번만 회전한 조건에서, 스크래치 깊이가 2㎛ 깊이를 유발하는 하중 조건은 650~850gf로 더욱 바람직하게는 750gf임을 알 수 있다.In addition, the CS-10 is used as the type of the polishing wheel, and under the condition that the rotation speed of the optical disc is rotated only once, it can be seen that the load condition that the scratch depth causes the depth of 2 μm is 650 to 850 gf, more preferably 750 gf. .
또한 연마 휠의 종류를 CS-17을 사용하고, 광디스크의 회전수를 1번만 회전한 조건에서, 스크래치 깊이가 2㎛ 깊이를 유발하는 하중 조건은 1200~1400gf로 더욱 바람직하게는 1350gf임을 알 수 있다.In addition, the CS-17 was used as the type of the polishing wheel, and under the condition that the rotation speed of the optical disc was rotated only once, it can be seen that the load condition that the scratch depth causes the depth of 2 μm is 1200 to 1400 gf, more preferably 1350 gf. .
따라서, 연마 휠의 종류가 부드러운 CS-10F인 경우에는 광디스크 표면의 하중을 50~250gf로 더욱 바람직하게는 150gf로 정량화하고, 미들(middle)인 CS-10인 경우는 광디스크 표면의 하중을 650~850gf로 더욱 바람직하게는 750gf로 정량화하고, 그리고 단단한(hard) CS-17인 경우는 광디스크의 표면의 하중을 1200~1400gf로 더욱 바람직하게는 1350gf로 정량화한다.Therefore, when the kind of polishing wheel is soft CS-10F, the load on the surface of the optical disc is quantified to 50 to 250 gf, more preferably 150 gf, and on the case of the middle CS-10, the load on the surface of the optical disc is 650 to More preferably, 850 gf is quantified, and in the case of hard CS-17, the load on the surface of the optical disc is quantified at 1200-1400 gf, more preferably 1350 gf.
이와 같은 정량화된 조건에 따라, 광디스크의 회전수에 비례하여 상기 광디스크(30)와 연마 휠(10)의 접촉 하중을 해당 하중으로 유지하여 상기 광디스크(30)에 스크래치를 생성시킨다.According to the quantified condition, the contact load between the
이때, 광디스크의 회전수를 5회 미만으로 줄여서 연마 휠(10)에 의한 광디스크의 마모 정도를 최소한으로 줄임으로써, 실생활에서 발생될 수 있는 스크래치와 매우 가까운 형태의 스크래치를 생성하여 광디스크 표면의 기계적 내구성 검사의 신뢰도를 높일 수 있게 된다.At this time, by reducing the rotational speed of the optical disk to less than five times to reduce the wear of the optical disk by the grinding
즉, 실생활에서 광디스크에 발생될 수 있는 스크래치는 한 두번의 긁힘에서 발생되는데 반하여, 테이버 연마 테스터를 사용하여 여러 번의 광디스크 회전을 통해 발생되는 스크래치는 연마 휠(10)에 긁히는 횟수가 증가하면 할 수록, 스크래치되는 주변 광디스크의 마모로 인해 그 형태가 실생활에서 발생되는 스크래치와 큰 차이가 나게된다.That is, in real life, scratches that may occur on the optical disk are generated from one or two scratches, whereas scratches generated by rotating the optical disk several times using a taper polishing tester are required to increase the number of scratches on the
이에 따라, 스크래치에 따른 광디스크 표면의 기계적 내구성 검사의 신뢰성에 문제가 발생되는데, 이것이 종래의 광디스크 표면의 기계적 내구성 검사에서 발생되는 가장 큰 문제점이다.Accordingly, a problem arises in the reliability of the mechanical durability inspection of the optical disk surface due to scratches, which is the biggest problem that occurs in the mechanical durability inspection of the conventional optical disk surface.
이를 본 발명에서는 정량화된 절대 기준치를 통해 광디스크의 회전수를 작게는 1회에서 많게는 5회 미만으로 줄일 수 있으므로, 실생활에서 발생될 수 있는 스크래치와 가장 가까운 형태의 스크래치를 유발하여 광디스크 표면의 기계적 내구성 검사의 신뢰도를 높일 수 있게 된다.In the present invention, since the number of revolutions of the optical disk can be reduced from as little as one to as many as less than five times through the quantified absolute reference value, the mechanical durability of the surface of the optical disk can be caused by causing a scratch closest to the scratch that can occur in real life. The reliability of the test can be increased.
이와 같이, 1번의 광디스크 회전만을 통해, 스크래치 깊이가 2㎛ 깊이를 유발하는 하중 조건인 50~1650gf를 이용하여 스크래치를 발생시킨 후, 스크래치된 광디스크(30)를 회전판(20)에서 분리하여 상기 광디스크(30) 표면에 발생된 스크래치를 통해 내구성을 검사하게 된다. 그리고, 상기 광디스크(30)의 불량과 양품을 구분하게 된다(S50).As such, after only one rotation of the optical disk, the scratch is generated by using a load condition of 50 to 1650 gf, which is a scratch depth causing a depth of 2 μm, and then the scratched
이어 다음으로 검사하고자 하는 다른 광디스크를 회전판(20)에 위치시키고 상기 동작을 반복함으로써, 다수개의 광디스크의 불량과 양품을 구분할 수 있게 된다. Subsequently, by placing the other optical disk to be examined on the
도 1 은 본 발명에 따른 테이버 연마 검사 장치를 나타낸 구성도1 is a block diagram showing a taper polishing inspection apparatus according to the present invention
도 2 는 본 발명에 따른 광디스크 표면의 기계적 내구성 검사 방법을 나타낸 흐름도2 is a flow chart showing a mechanical durability inspection method of the surface of the optical disk according to the present invention.
도 3 은 본 발명에 따른 마이크로스크래치 테스터를 이용하여 광디스크에 소정의 스크래치 패턴이 형성된 도면FIG. 3 is a diagram in which a predetermined scratch pattern is formed on an optical disc using a microscratch tester according to the present invention. FIG.
도 4 는 본 발명에 따른 광디스크에 가하는 압력에 따라 발생되는 스크래치 깊이를 실험치를 통해 나타낸 도면4 is a view showing the scratch depth generated according to the pressure applied to the optical disk according to the present invention through an experimental value;
도 5 는 본 발명에 따른 광디스크 표면의 기계적 내구성 검사 방법을 나타낸 도면5 is a view showing a mechanical durability inspection method of the surface of the optical disk according to the present invention;
*도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
10 : 연마 휠 20 : 회전판10: polishing wheel 20: rotating plate
30 : 광디스크30: optical disc
Claims (18)