KR100886792B1 - Oil-resistant sole with air-permeability, waterproofness and water-repellency

Info

Publication number: KR100886792B1
Application number: KR1020080073881A
Authority: KR
Inventors: 조덕용; 김미진
Original assignee: (주)조은제화; 김미진; 조덕용
Priority date: 2008-07-29
Filing date: 2008-07-29
Publication date: 2009-03-04

Abstract

An oil-resistant shoe sole is provided, which prevents the contaminant of the oil etc from being flowed in the shoe from the outside. An oil-resistant shoe sole comprises: an oil resistant outsole(10) equipped with a ventilation section in which ventilation holes are repeatedly arranged; an oil resistant and waterproof paper(20) formed in the top of the ventilation section of the outsole; and a functional waterproof paper adhered to the upper side of the midsole(30) positioned at the top of the outsole. The oil resistant outsole is formed by mixing acrylonitrile-butadiene rubber(NBR) and fluorine-silicon rubber(FVMQ) and adding sulfur of 1~3 weight% and 2,4 dichloro benzoyl peroxide in the mixture 97~99 weight%.

Description

Oil-resistant sole with air permeability, water repellency {Oil-resistant sole with air-permeability, waterproofness and water-repellency}

본 발명은 신발의 바닥창에 있어서, 특히 내유성 물질이 혼합된 상태로 성형된 통기성 아웃솔과, 상기 아웃솔의 상측에 위치하는 내유성 방발수지 및 통기성 스펀지가 내장된 미드솔의 형성하며, 상기 미드솔의 상부면에는 기능성 방발수지를 각각 형성함으로써, 신발 내부의 습기나 냄새 등을 효과적으로 제거하면서도, 외부로부터의 물기의 유입은 방지되게 하는 것이며, 특히 기름 등의 오염원으로부터 장시간 노출되더라도 변형이나 물성 변화없이 안전하게 사용할 수 있게 한 것이다.The present invention relates to a shoe sole, in particular a breathable outsole molded with a mixture of oil-resistant materials, and a midsole with oil-resistant anti-fog resin and a breathable sponge positioned on an upper side of the outsole, the upper surface of the midsole By forming functional anti-repellent resin each, it effectively removes moisture and odor inside the shoe, and prevents water from flowing in from the outside. In particular, it can be safely used without deformation or change in physical properties even if it is exposed for a long time from a pollutant such as oil. It was made.

일반적으로 남성 및 여성의 정장화 또는 운동화나 레저화 및 등산화 등의 신발은 일상에서 반드시 착용되는 필수품목인 것으로서, 사용자의 취향이나 목적에 따라 다양한 디자인 및 기능을 갖고 있다.In general, men's and women's formal shoes or sneakers or leisure shoes and hiking shoes, etc. are essential items that are necessarily worn in everyday life, and have various designs and functions according to a user's taste or purpose.

이와 같은 신발은 착용감이 우수하여야 하면서도 발의 피로감을 덜어주어야 하는 것이며, 장시간 착용하더라도 체중의 효과적인 분산을 통해 압박감을 최소화 하여야 하는 기술적 특성을 갖고 있는 것이다.Such shoes should be excellent in wearing comfort, but also to reduce the fatigue of the foot, even if worn for a long time has the technical characteristics to minimize the pressure through the effective dispersion of weight.

도 1은 일반적인 신발의 구조를 단면 도시한 것으로, 통상적으로 경질의 고무재로 된 아웃솔(Outsole)(100)의 상부에는 미드솔(Midsole)(101)을 부착 형성하는 것인데, 상기한 아웃솔(100)과 미드솔(101)은 사용자의 체중을 분산시키면서도 충격을 흡수하는 역할을 하게 된다.1 is a cross-sectional view showing a structure of a general shoe, which is to form a midsole 101 attached to the upper portion of the outsole 100, which is typically made of a hard rubber material, the outsole 100 And midsole 101 serves to absorb the shock while dispersing the user's weight.

이때, 전기한 미드솔(101)은 통상적으로 폴리우레탄(Poly Urethane)이나 에바(EVA) 등의 재질로 이루어지는 것으로서, 대부분 비교적 내구성이 우수한 폴리우레탄 계열의 재질로 된 미드솔을 널리 채택하고 있다.At this time, the aforementioned midsole 101 is generally made of a material such as polyurethane (Poly Urethane), EVA (EVA), etc., and mostly adopts a midsole made of a polyurethane-based material having a relatively high durability.

또한, 상기한 미드솔(101)의 상부에는 사용자의 발바닥 및 발의 측부와 밀착되게 한 인솔(Insole)(102)을 접착 형성하거나 끼워 넣게 되는데, 필요에 따라 아웃솔(100)과 미드솔(101)의 사이에 부직포(105)를 삽입하거나 제거하여 제작할 수도 있는 것이다.In addition, the upper portion of the midsole 101 is adhesively formed or sandwiched insole (102) in close contact with the sole of the user's foot and the side of the foot, if necessary, between the outsole 100 and the midsole 101. It is also possible to manufacture by inserting or removing the nonwoven fabric 105 in.

또한, 상기한 인솔(102)의 경우 천연가죽이나 인조가죽 등으로 제작되며, 인솔(102)은 신발 내부 전체에 형성되거나 신발의 내측부에 한정적으로 사용되기도 하는 것으로서, 신발을 착용하는 경우 부드러운 착용감을 제공하면서도 소정의 쿠션을 부여하므로 착용감을 향상시키기 위한 목적으로 사용되는 것이다.In addition, in the case of the insole 102 is made of natural leather or artificial leather, etc., the insole 102 is formed on the entire inside of the shoe or used as limited to the inner side of the shoe, when wearing shoes, a soft fit While providing a predetermined cushion while providing, it is used for the purpose of improving the fit.

이와 같은 바닥층을 이루는 신발은 상기한 아웃솔(100)과 미드솔(101)의 가장자리 사이에 외피(103)의 하단을 끼워넣은 상태에서 이들을 서로 접착 형성함으로써 신발이 완성되는 것이다.The shoe forming the bottom layer is completed by adhering the shoes to each other in a state in which the lower end of the outer shell 103 is inserted between the edges of the outsole 100 and the midsole 101.

이때, 상기와 같은 일반적은 신발은 사용자의 발에서 배출되는 땀이나 온기 등을 원활하게 배출하지 못하므로 냄새나 무좀의 원인균이 증식하는 문제점이 있어 근자에 들어서는 상기한 아웃솔(100)과 미드솔(101) 및 인솔(102)에 미세한 통기공(104)(104')(104")을 무수히 많게 형성하여 이들 통기공(104)(104')(104")을 통해 신발 내부에서 발생하는 땀이나 습기 등이 신발 외부로 배출되게 하면서도, 신발 외부로부터 유입되려 하는 물기는 차단함으로써 항상 쾌적한 신발 상태를 유지하도록 하고 있는 것이다.At this time, the general shoe as described above does not smoothly discharge sweat or warmth discharged from the user's foot, so there is a problem that the causative agent of odor or athlete's foot is proliferating, the above-mentioned outsole 100 and midsole (101) Sweat and moisture generated inside the shoe through the vent holes 104, 104 'and 104 " by forming a myriad of fine vent holes 104, 104' and 104 " While the back is discharged to the outside of the shoe, by blocking the moisture to be introduced from the outside of the shoe to maintain a comfortable shoe state at all times.

그러나, 방수 및 발수 기능을 갖는 상기의 기능성 신발은 인솔과 미드솔 및 아웃솔을 경유하여 통기와 투습 작용을 하게 되므로 수분이나 공기가 소통되는 경로가 길고 복잡하므로 통기성이 뛰어나지 못한 것이 사실이며, 원활한 투습성을 위해 미세한 타공의 크기를 확장하는 경우에는 방수 및 발수 기능이 현저히 저하되므로 방수 및 발수와 동시에 우수한 투습성을 실현하는데 상당한 문제점을 드러내고 있는 것이다.However, since the functional shoes having waterproof and water repellent functions to perform ventilation and moisture permeation through insoles, midsoles, and outsoles, it is true that the moisture and air communication paths are long and complicated, and thus the breathability is not excellent. In the case of expanding the size of the fine perforations, the waterproof and water repellent function is significantly lowered, thereby revealing a significant problem in achieving excellent waterproof and water repellency at the same time.

더구나, 상기와 같이 인솔 및 미드솔과 아웃솔에 걸쳐 형성된 미세한 타공으로 된 통기공은 전기한 바와 같이 소통의 경로가 복잡하고 길어 일정 시간 사용 후에는 신발 내부에서 발생한 미세한 분진 등이 이들 통기공을 막아버리게 되므로 투습성을 거의 상실하게 되므로 실질적인 기능성 신발의 효과를 거의 볼 수 없게 되는 폐단이 있는 것이며, 아웃솔의 상부 표면에 부착되는 미드솔이나 부직포의 경우 접착제를 사용하여 부착되므로 접착제로 인해 상기한 통기공이 완전히 막히게 되므로 실질적인 통기성의 확보가 어려운 문제점은 물론 화학성분으로 된 접착제는 인 체에 유익하지 못한 문제점을 갖고 있는 것이다.In addition, as described above, the perforated pores formed through the insole and the midsole and the outsole have a complicated and long communication path as described above, so that after a certain period of time, fine dust generated inside the shoe blocks these vents. As a result, almost no moisture permeability, there is a closed end that almost no effect of the functional shoes can be seen. As it becomes clogged, it is difficult to secure practical breathability, as well as adhesives made of chemicals, which are not beneficial to the human body.

특히, 일반적은 신발은 대부분 가벼운 재질 및 구조적 개선을 통해 가능한 최소의 중량만을 갖도록 제작하여 가볍게 제작함에 따라 착용감을 증대시키고자 하고 있으나, 상기의 기능성 신발을 포함한 종래의 모든 신발은 아웃솔과 미드솔 및 인솔에 의한 고중량을 갖고 있으므로 가볍고 편안한 신발의 제작이 불가능한 문제점을 갖고 있는 것이다.In particular, in general, most shoes are manufactured to have only the minimum weight possible through light materials and structural improvements, and to increase the wearing comfort, but all conventional shoes including the above functional shoes have outsoles, midsoles, and insoles. Since it has a high weight by having a problem that is impossible to produce light and comfortable shoes.

또한, 일반적인 신발은 기름에 의한 오염이 발생하게 되면 점성을 갖고 있으면서도 밀도가 높은 기름은 발수가 쉽게 되지 않고 점착되어 압력이 발생하게 되면 신발 내측으로 밀려 유입되는 현상이 발생하게 되고, 상기와 같은 기름에 장시간 아웃솔 및 미드솔 등이 노출되는 경우에는 물성이 변하거나 경화되는 등 신발의 내구성에 치명적인 악영향을 끼치게 되는 것인데, 상기와 같은 일반적인 신발 및 기능성 신발은 모두 기름 등에 취약한 문제점을 갖고 있는 것이다.In addition, in general, when shoes are contaminated by oil, the oil having a high viscosity and high density is not easily water-repellent and adhered to the shoe when the pressure is generated. If the outsole and the midsole is exposed to for a long time, such as a physical property change or hardening will have a fatal adverse effect on the durability of the shoe, such general shoes and functional shoes are all vulnerable to oil and the like.

본 발명은 전기한 바와 같은 문제점을 개선한 것으로서, 내유성 물질이 혼합된 상태의 원료를 성형하여 제작한 아웃솔을 구비하고, 상기 아웃솔에는 비교적 크기가 큰 통기공을 형성하며, 아웃솔의 상부에는 내유성 방발수지와 미드솔 및 기능성 방발수지를 순차적으로 적층 형성하되, 상기 미드솔에는 통기성 스펀지를 관통 삽입 형성함으로써,The present invention is to solve the problems as described above, having an outsole manufactured by molding a raw material in a state in which oil-resistant materials are mixed, the outsole to form a relatively large ventilation hole, the oil-resistant explosion-proof on the top of the outsole Resin, a midsole and a functional anti-repellent resin is sequentially laminated, but by forming a breathable sponge through the midsole,

내유성 방발수지와 기능성 방발수지에 의한 통기성 및 방수성을 확보하면서도, 내유성 아웃솔과 내유성 방발수지에 의해 기름으로부터 안전한 사용이 가능하도록 한 것이며, 통기성 스펀지는 신발 전체의 중량을 가볍게 하면서도 부드러운 착용감을 제공하면서도 우수한 통기성을 연출하는 특징의 내유성 신발창을 제공함에 본 발명의 목적이 있는 것이다.While ensuring breathability and water resistance by oil-resistant and functional oil-resistant resins, oil-resistant outsoles and oil-resistant oil-resistant resins enable safe use from oil, and breathable sponges provide a soft fit while reducing the weight of the entire shoe. It is an object of the present invention to provide an oil-resistant sole of the characteristics that produce breathability.

상기한 바와 같은 목적을 달성하기 위한 본 발명은, 비교적 내경이 큰 통기공이 반복 배열된 통기부가 형성된 내유성 아웃솔을 구비하고, 상기 아웃솔의 통기부 상측에는 내유성 방발수지를 형성하며, 상기 아웃솔의 상측에 위치하는 미드솔에는 상기 아웃솔의 통기부과 대응하는 절개부를 형성하고, 상기 절개부에는 통기성 스펀지를 삽입하되, 상기 통기성 스펀지의 하측 테두리에는 절개부 보다 큰 플랜지부를 형성하여 상기 통기성 스펀지가 미드솔의 하측으로부터 절개부의 내측으 로 상향 삽입되게 하고, 상기 미드솔의 상부면에는 기능성 방발수지를 부착 형성하여 구성하여 이루어진 것이다.The present invention for achieving the object as described above, has an oil-resistant outsole is formed with a ventilation portion is arranged a plurality of ventilation holes with a relatively large inner diameter, forming an oil-resistant oil-resistant resin on the upper side of the vent of the outsole, the upper side of the outsole The midsole is located in the cutout corresponding to the venting portion of the outsole, the breathable sponge is inserted into the cutout, the lower edge of the breathable sponge is formed a flange portion larger than the cutout so that the breathable sponge is the lower side of the midsole It is made to be inserted upward from the incision from the incision, and formed by forming a functional anti-repellent resin attached to the upper surface of the midsole.

본 발명은, 내유성 아웃솔과 내유성 방발수지에 의해 신발 외부로부터 기름 등의 오염물이 유입되는 것을 방지하면서도 아웃솔에 점착되는 기름에 의한 물성 변화 등에 의해 사용 수명이 단축되는 것을 예방하는 것이며, 내측의 내유성 방발수지와 기능성 방발수지는 통기성을 확보하는 한편 신발 외부로부터의 물기 유입은 차단하는 역할을 하는 것이며, 중창에 관통하여 삽입된 통기성 스펀지는 더욱 우수한 통기성의 확보는 물론 신발의 경량화를 꾀하는 것이며, 신발의 착용시 발가락에 해당하는 절곡부가 더욱 부드럽게 접혀지거나 구부러질 수 있게 하여 우수한 착용감을 제공하는 효과를 갖는 것이다.The present invention is intended to prevent the service life from being shortened due to changes in physical properties due to oil adhering to the outsole while preventing the inflow of contaminants such as oil from the outside of the shoe by the oil resistant outsole and the oil resistant oil repellent resin. Resin and functional anti-fog resin ensures breathability while blocking the inflow of water from the outside of the shoe, and the breathable sponge inserted through the midsole ensures better breathability and lighter shoes. When worn, the bent portion corresponding to the toe can be folded or bent more smoothly, thereby providing an excellent fit.

본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms or words used in this specification and claims are not to be construed as being limited to the common or dictionary meanings, and the inventors can appropriately define the concept of terms in order to explain their invention in the best way. Based on the principle, it should be interpreted as meaning and concept corresponding to the technical idea of the present invention.

이하 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명하기 로 한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 2는 본 발명에 따른 신발창의 분리 사시도이고, 도 3은 본 발명에 따른 신발창의 분리 단면도이며, 도 4는 본 발명에 따른 신발창의 결합 단면도이다.Figure 2 is an exploded perspective view of the sole according to the present invention, Figure 3 is an exploded cross-sectional view of the sole according to the present invention, Figure 4 is a combined cross-sectional view of the sole according to the present invention.

도시와 같이 본 발명에 따른 신발창은 일반적인 형태의 아웃솔(10)과 상기 아웃솔(10)의 상부면에 위치하는 내유성 방발수지(20) 및 미드솔(30)과 통기성 스펀지(40), 기능성 방발수지(50)의 구성으로 이루어져 있는 것이다.As shown, the sole according to the present invention is a general type of outsole 10 and the oil-resistant oil-resistant resin 20 and the midsole 30 and the breathable sponge 40, which is located on the upper surface of the outsole 10, functional anti-fog resin ( It consists of 50).

여기서, 상기의 아웃솔(10)은 아크릴로니트릴-부타디엔 고무(NBR)와 불소-실리콘 고무(FVMQ)의 혼합 비율은 중량비 4:6 내지 6:4의 범위로 해줄 수 있는데, 이 범위 내에서 블렌딩된 합성고무는 개개의 합성고무보다 우수한 물성을 발휘한다.Here, in the outsole 10, the mixing ratio of acrylonitrile-butadiene rubber (NBR) and fluorine-silicone rubber (FVMQ) may be in the range of weight ratio 4: 6 to 6: 4, and blending within this range Synthetic rubber exhibited better physical properties than individual synthetic rubbers.

즉, 각 소재의 물성이 상호 보완적인 역할을 하여 니트릴 고무에서 문제되는 내유성 및 내열특성과, 불소-실리콘 고무에서 문제되는 작업성 불량이 상호 보완되는 것이다.That is, the physical properties of each material play a complementary role, and oil resistance and heat resistance problems of nitrile rubber and workability defects of fluorine-silicon rubber are complemented with each other.

또한, 본 고무 혼합공정에서는 양 고무성분이 혼합, 반죽됨에 따라 각 고무중의 겔 조직이 깨뜨려져 가소성으로 되어 혼화성이 증대되고, 첨가되는 가황제 혹은 경화제로 하여금 균일하게 잘 분산되도록 해 준다.In addition, in the present rubber mixing process, as both rubber components are mixed and kneaded, the gel structure in each rubber is broken and plasticized, thereby increasing the miscibility and allowing the added vulcanizing agent or curing agent to be uniformly well dispersed.

상기의 첨가제는 고무 혼합물에 황 및 2,4 디클로로 벤조일 퍼록사이드 등의 첨가제를 첨가하여 성형하면 되는 것인데, 여기서 상기 첨가제 중 황은 혼합물에 대해 0.5-1.5중량%를, 2,4 디클로로벤조일 퍼록사이드는 혼합물에 대해 0.5-1.5중량%를 배합해 주는 것이 바람직하다.The additive may be formed by adding an additive such as sulfur and 2,4 dichloro benzoyl peroxide to the rubber mixture, wherein sulfur in the additive is 0.5-1.5 wt% based on the mixture, and 2,4 dichlorobenzoyl peroxide is added to the rubber mixture. It is preferable to mix 0.5-1.5 weight% with respect to the mixture.

이들 첨가제는 상기 고무혼합공정에서 제조된 고무 혼합물이 가소성으로 되 어 있으므로 균일하게 분산이 잘 이루어지게 되며, 이렇게 분산된 각 첨가제는 고무혼합공정에서 일정 정도 파괴된 고무성분을 다시 경화시켜 고무의 기본적인 물성을 유지해 주게 된다.These additives are uniformly dispersed because the rubber mixture produced in the rubber mixing process is plastic, and each of the additives thus dispersed hardens the rubber component that is destroyed to some extent in the rubber mixing process. It will keep the physical properties.

여기서, 상기 고무 재질의 내유성이 문제가 되는 이유는 소위 말해 스웰링(Swelling)이라는 현상 때문인데, 스웰링(Swelling)이라는 현상은 거대분자인 고분자 물질구조에 작은 분자물질이 침투하여 고분자 물질의 분자들 간의 거리를 늘려 결과적으로 고분자로 만들어진 물체가 제 형상을 유지하지 못하고 부풀어 오르는 현상을 발생시키는 것을 말한다.Here, the oil resistance of the rubber material is a problem because of a phenomenon called swelling. Swelling is a phenomenon in which a small molecular material penetrates into a macromolecular polymer structure, and thus the molecule of the polymer material. Increasing the distance between them results in a swelling phenomenon in which the object made of polymer does not maintain its shape.

이러한 현상에 따라 고분자 물체의 강도도 약해지는 결과를 낳게 되는 것이며, 일반적으로 고무는 탄소와 수소들로 이루어진 하이드로 카본계의 물질인데, 기름 역시 하이드로 카본계 혼합물이므로 친화성이 좋기 때문에 특히 고무 내로 잘 침투하므로 고무의 내유성이 중요시 되는 것이다.As a result of this phenomenon, the strength of the polymer object is also weakened. In general, rubber is a hydrocarbon-based material composed of carbon and hydrogen. Since oil is also a hydrocarbon-based mixture, the affinity is good, so it is particularly well incorporated into rubber. Since it penetrates, the oil resistance of rubber becomes important.

이런 현상이 잘 관찰할 수 있는 경우는 고무신발 밑창으로 기름이 많은 곳을 다니면 밑창이 녹아내리는 경우 같은 예일 것이다.A good example of this can be observed when the sole of the shoe is melted when the oily shoe goes around a lot of oil.

이에 따라 상기의 아크릴로니트릴-부타디엔 고무(NBR)와 불소-실리콘 고무(FVMQ)의 혼합물에 의해 종래의 고무가 갖는 신축 탄력성을 그대로 유지하면서도, 불소-실리콘 고무에 의해 우수한 내유성을 확보할 수 있게 되는 것이다.Accordingly, the mixture of acrylonitrile-butadiene rubber (NBR) and fluorine-silicone rubber (FVMQ) maintains the elasticity of elasticity of conventional rubber while maintaining excellent oil resistance by fluorine-silicone rubber. Will be.

또한, 내유성 방발수지(20)는 폴리에스테르 또는 나이론 등의 원사(21)를 직조하여 물방울은 통과되지 못하고 공기와 수분은 통과되도록 직조하여 이루어진 것 인데, 상기의 원사(21) 표면에는 액상의 실리콘을 코팅하여 된 내유성 코팅층(22)을 형성하여 직조되므로 상기의 내유성 코팅층(22)에 의해 우수한 내유성을 확보하게 되는 것이다.In addition, the oil-resistant anti-fog resin 20 is made by weaving a yarn 21, such as polyester or nylon, so that water droplets do not pass, but air and water pass, but the surface of the yarn 21 is liquid silicone Since the oil-resistant coating layer 22 formed by coating the woven fabric is to ensure excellent oil resistance by the oil-resistant coating layer 22.

따라서, 상기의 아웃솔(10)에 형성된 통기부(12)의 통기공(11)(11')을 통해 외부로부터 물이나 기름 등이 신발 내부로 유입되더라도 상기의 내유성 방발수지(20)에 의해 일차적으로 기름과 물의 차단이 이루어지게 된다.Therefore, even though water or oil is introduced into the shoe from the outside through the air vents 11 and 11 ′ of the vent 12 formed in the outsole 10, the oil-resistant anti-fog resin 20 is primarily used. This will block oil and water.

또한, 상기의 미드솔(30)은 일반적인 형태와 재질로 된 이루어진 것인데, 상기의 미드솔(30)에는 아웃솔(10)의 통기부(12)과 대응하는 위치와 형태를 갖는 관통의 절개부(31)가 형성되어 있고, 상기의 절개부(31)에는 별도의 통기성 스펀지(40)가 삽입되어 있는 것으로, 상기의 스펀지(40)는 신발창의 전체적인 중량을 크게 줄여주는 역할을 하면서도 신발 내부에서 더욱 우수한 통기 부재로의 역할을 겸하게 되는 것이며, 신발을 착용하고 보행하거나 작업을 하는 경우 신발의 앞부분이 보다 부드럽게 절곡되거나 구부러지게 하는 역할을 하므로 뛰어난 착용감을 제공하면서도, 고탄력의 스펀지는 신축 탄력성이 우수하므로 사용자의 체중에 의한 발바닥의 충격이나 압력을 분산 및 완화시켜 주게 된다.In addition, the midsole 30 is made of a general shape and material, the midsole 30 is a cut through portion 31 having a position and shape corresponding to the vent 12 of the outsole 10. Is formed, and the incision portion 31 is a separate breathable sponge 40 is inserted, the sponge 40 serves to significantly reduce the overall weight of the shoe sole, but more excellent ventilation inside the shoe It also serves as a member, and when the user walks or wears shoes, the front part of the shoe is bent or bent more smoothly, providing a superior fit, while the high elastic sponge has excellent elasticity and elasticity. This will disperse and relieve the impact or pressure of the soles caused by weight.

특히, 상기의 통기성 스펀지(40) 하부에는 외향 돌출된 플랜지부(41)가 형성되어 있어 상기의 통기성 스펀지(40)가 미드솔(30)로부터 신발 내측으로 분리되는 것을 방지하게 되는데, 상기의 통기성 스펀지(40)는 미드솔(30)의 절개부(31) 하측으로부터 상향 삽입하여 신발창 및 이를 이용한 신발을 완성하는 경우 상기의 통기성 스펀지(40)는 더욱 견고한 고정력을 얻게 되는 것이며, 미드솔(30)의 절개부(31)와 통기성 스펀지(40)의 틈새 사이로 누적되거나 퇴적되는 분진이나 이물질 등에 의해 내유성 방발수지(20)의 통기성 간극을 메우거나 아웃솔(10)의 통기공(11)(11')을 메우는 등의 폐단을 방지하는 차단부의 역할도 겸하게 되는 것이다.Particularly, the outwardly protruding flange portion 41 is formed under the breathable sponge 40 to prevent the breathable sponge 40 from being separated from the midsole 30 to the inside of the shoe. 40 is inserted from the bottom of the cut portion 31 of the midsole 30 to complete the sole and shoes using the same breathable sponge 40 is to obtain a more firm fixing force, the incision of the midsole 30 Filling the air gap between the oil-resistant anti-fog resin 20 or the air vent 11 and 11 ′ of the outsole 10 by dust or foreign matter accumulated or accumulated between the gap between the part 31 and the air-permeable sponge 40. It will also serve as a blocker to prevent the back of the lungs.

이와 같이 아웃솔(10)과 미드솔(30)의 사이에 내유성 방발수지(20)를 삽입한 상태에서 상기의 미드솔(30) 상부면에는 역시 상기 아웃솔(10)의 통기부(12)와 대응하는 위치에 별도의 기능성 방발수지(50)를 부착 형성하여 완성되는 것인데,In such a state that the oil-resistant anti-fog resin 20 is inserted between the outsole 10 and the midsole 30, the upper surface of the midsole 30 also corresponds to the vent 12 of the outsole 10. It is completed by attaching to form a separate functional explosion-proof resin (50),

상기의 기능성 방발수지(50)는, 기능성 코팅층(52)을 갖는 원사(51)를 이용하여 물방울은 통과되지 못하고 공기와 수분은 통과되도록 직조하여 구성된 것으로서, 상기의 기능성 코팅층(52)은 접착제 60~70중량%와 기능성 분말 30~40중량%를 혼합한 후, 이를 원사(51)에 도포 또는 원사(51)를 코팅액에 함침하여 완성하는 것이다.The functional anti-fog resin 50 is configured by weaving water and water through the yarn 51 having a functional coating layer 52 so as not to pass through, the functional coating layer 52 is adhesive 60 After mixing ~ 70% by weight and 30 to 40% by weight of the functional powder, it is applied to the yarn 51 or finished by impregnating the yarn 51 in the coating liquid.

특히, 상기의 기능성 분말은 숫 분말 또는 나노은, 또는 토르말린 분말, 세라믹 분말, 자수정 분말, 옥 분말 중 어느 하나 이상의 것을 혼합하여 되는 것으로, 상기의 예로부터 다양한 조합이나 선택적 사용이 가능할 뿐만 아니라, 인체에 이롭거나 항균 또는 악취 제거의 특성을 갖고 있는 물질이면 어떠한 것이든지 적용이 가능할 것이다.In particular, the functional powder is a mixture of any one or more of male powder or nano silver, tourmaline powder, ceramic powder, amethyst powder, jade powder, not only various combinations or selective use from the above examples, but also to the human body Any material that is beneficial or has antimicrobial or odor removal properties may be applied.

이에 따라, 상기와 같은 조합에 의해 완성된 신발창은 도 5의 도시와 같이 수분과 공기의 수통은 자유로워 쾌적한 신발 내부를 형성할 수 있는 것이며, 기능성 방발수지(50)는 신발 내부에서 발생하는 악취를 효과적으로 제거하는 것이며, 세균이나 무좀균의 발생이나 증식을 억제하는 효과를 갖게 된다.Accordingly, the shoe sole completed by the combination as described above is to be able to form a comfortable shoe interior of the water and air cans as shown in Figure 5, the functional repellent resin 50 is the odor generated inside the shoe It is effective to remove, and has the effect of suppressing the occurrence or proliferation of bacteria and athlete's foot.

또한, 물이나 기름의 차단이 이중으로 이루어져 일반적인 평상화는 물론 레져화 또는 특수작업화에 매우 효과적인 것으로서, 사용 및 적용 범위가 제한되지 아니하므로 더욱 합리적이고 경제적인 특징을 갖는다.In addition, since water or oil is doubled, it is very effective for general leveling as well as leisure or special work shoes, and has a more reasonable and economical feature because the use and application range are not limited.

이와 같은 본 발명 신발창은 도 6의 도시와 같이 상기의 아웃솔(10)에 요홈부(13)를 형성하여 더욱 합리적인 형태의 신발창을 완성할 수 있는 것인데, 상기한 요홈부(13)에는 통기공(11)(11')을 갖는 통기부(12)가 형성되고, 상기 요홈부(13)의 내측으로는 전기한 내유성 방발수지(20)가 안치되는 것이며, 그 내유성 방발수지(20)의 상측에는 통기성 스펀지(40)의 하부 플랜지부(41)가 삽입되는 것으로, 상기의 요홈부(13)의 깊이는 내유성 방발수지(20)와 플랜지부(41)의 두께를 합한 것과 일치되도록 형성하면 되는 것이다.Such a shoe sole of the present invention is to form a recess 13 in the outsole 10 as shown in Figure 6 to complete the shoe sole of a more rational form, the groove 13 is a ventilation hole ( 11) (11 ') is provided with a vent 12, the oil-resistant oil-resistant resin 20 is placed inside the groove portion 13, the upper side of the oil-resistant oil-resistant resin 20 The lower flange portion 41 of the breathable sponge 40 is inserted, and the depth of the groove portion 13 may be formed to match the sum of the thicknesses of the oil-resistant anti-fog resin 20 and the flange portion 41. .

이에 따라 상기의 요홈부(13)에 의해 아웃솔(10)의 자체 중량을 더욱 경감시키면서도 두께를 갖는 내유성 방발수지(20)와 통기성 스펀지(40)의 플랜지부(41)가 상기 요홈부(13) 내에 완전하게 삽입되는 형태를 갖추게 되므로 결국 아웃솔(10)의 상부면과 미드솔(30)의 저면에는 틈새나 단턱 등이 전혀 발생하지 않게 되므로 더욱 우수한 밀착도는 물론 착용감의 향상을 꾀할 수 있게 된다.Accordingly, the recess portion 13 of the oil-resistant anti-fog resin 20 and the air-permeable sponge 40 having a thickness while further reducing the weight of the outsole 10 by the recess portion 13 is the recess portion 13. Since the shape is completely inserted into the upper surface of the outsole 10 and the bottom surface of the midsole 30, no gaps or steppings are generated, and thus, more excellent adhesion and improvement of fit can be achieved.

이상과 같은 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 이들을 대체할 수 있는 다양한 균등물과 변형 예들이 있을 수 있음을 이해하여야 한다.The embodiments described in the present specification and the drawings shown in the drawings are only the most preferred embodiments of the present invention and do not represent all of the technical idea of the present invention, and various equivalents and modifications that may be substituted for them are provided. It should be understood that there may be examples.

도 1은 일반적인 신발의 전체구조를 보인 단면도1 is a cross-sectional view showing the overall structure of a typical shoe

도 2는 본 발명에 따른 신발창의 분리 사시도2 is an exploded perspective view of the sole according to the invention

도 3은 본 발명에 따른 신발창의 분리 단면도3 is an exploded cross-sectional view of the sole according to the present invention.

도 4는 본 발명에 따른 신발창의 결합 단면도4 is a cross-sectional view of the shoe sole in accordance with the present invention

도 5는 도 4의 A부에 대한 확대 단면도5 is an enlarged cross-sectional view of a portion A of FIG.

도 6은 본 발명에 따른 신발창의 다른 실시예를 보인 분리 사시도Figure 6 is an exploded perspective view showing another embodiment of a shoe sole according to the present invention

* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

10 : 아웃솔 11,11' : 통기공10: outsole 11,11 ': ventilator

12 : 통기부 13 : 요홈부12: vent 13: groove

20 : 내유성 방발수지 21 : 원사20: oil resistant resinous resin 21: yarn

22 : 내유성 코팅층22: oil resistant coating layer

30 : 미드솔 31 : 절개부30: midsole 31: incision

40 : 통기성 스펀지 41 : 플랜지부40: breathable sponge 41: flange portion

50 : 기능성 방발수지 51 : 원사50: functional waterproof resin 51: yarn

52 : 기능성 코팅층52: functional coating layer

Claims

An oil-resistant outsole 10 having a vent 12 formed by repeatedly arranging vents 11 and 11 ′ is formed, and an oil-resistant anti-oil resin 20 is formed above the vent 12 of the outsole 10. ,

The midsole 30 positioned above the outsole 10 is formed with a cutout portion 31 corresponding to the vent 12 of the outsole 10, and a breathable sponge 40 is formed at the cutout 31. Insert a, but the lower edge of the breathable sponge 40 to form a flange portion 41 larger than the cutout portion 31 so that the breathable sponge 40 from the lower side of the midsole 30 to the inside of the cutout 31 To be inserted upward,

In the upper surface of the midsole 30 in the oil-resistant sole having a breathable and water-resistant, water-repellent function formed by attaching the functional waterproofing resin 50,

The oil-resistant outsole 10 is selected from acrylonitrile-butadiene rubber (NBR) and fluorine-silicone rubber (FVMQ), respectively, within a range of weight ratio of 4: 6 to 6: 4, and then mixed with each other. Molded by mixing 99% by weight of 1-3% by weight of sulfur and additives of 2,4 Dichloro benzoyl Peroxide,

The oil-resistant anti-fog resin 20, the aeration characterized in that it is configured by weaving so that water droplets do not pass through the air and moisture through the yarn 21, the oil-resistant coating layer 22 formed of a liquid silicone on the surface Oil resistant sole with water repellent function.

delete

The method of claim 1,

The functional anti-repellent resin 50, the water droplets do not pass through the yarn 51 formed with the functional coating layer 52 applied by mixing 60 to 70% by weight of the adhesive and 30 to 40% by weight of the functional powder, air and moisture Oil-resistant sole having aeration and room, water-repellent function, characterized in that weave to pass through.

The method of claim 4, wherein

Functional powder, male powder or nano silver, tourmaline powder, ceramic powder, amethyst powder, jade powder, characterized in that the mixture of any one or more of the oil-resistant sole having a water-repellent, waterproof, water-repellent function.

delete