KR100870936B1 - Hemp cloth shroud coated gold dust and artificial gold and its manufacturing process - Google Patents

Hemp cloth shroud coated gold dust and artificial gold and its manufacturing process Download PDF

Info

Publication number
KR100870936B1
KR100870936B1 KR1020060116819A KR20060116819A KR100870936B1 KR 100870936 B1 KR100870936 B1 KR 100870936B1 KR 1020060116819 A KR1020060116819 A KR 1020060116819A KR 20060116819 A KR20060116819 A KR 20060116819A KR 100870936 B1 KR100870936 B1 KR 100870936B1
Authority
KR
South Korea
Prior art keywords
gold
coating layer
binder
weight
simulated
Prior art date
Application number
KR1020060116819A
Other languages
Korean (ko)
Other versions
KR20080047006A (en
Inventor
유병필
나영주
Original Assignee
유병필
나영주
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 유병필, 나영주 filed Critical 유병필
Priority to KR1020060116819A priority Critical patent/KR100870936B1/en
Publication of KR20080047006A publication Critical patent/KR20080047006A/en
Application granted granted Critical
Publication of KR100870936B1 publication Critical patent/KR100870936B1/en

Abstract

본 발명은 모의 금 및 금분이 코팅된 삼베수의에 관한 것으로, 삼베로 직조된 직물(20); 직물(20)의 표면에 형성되며, 모의 금(32) 및 희석된 바인더(34)가 혼합된 성분으로 이루어진 제1코팅층(30); 제1코팅층(30)의 특정 부위에 형성되며, 금분(42) 및 희석된 바인더(44)가 혼합된 성분으로 이루어진 제2코팅층(40)을 포함하여 구성된다. 이에 따라, 고급스러우면서도 가격이 상대적으로 저렴한 수의를 대중적으로 보급시킬 수 있다.The present invention relates to sham gold and gold powder coated hemp veterinary, hemp woven fabric 20; A first coating layer 30 formed on the surface of the fabric 20 and composed of a component in which the simulated gold 32 and the diluted binder 34 are mixed; It is formed on a specific portion of the first coating layer 30, and comprises a second coating layer 40 made of a mixture of the gold powder 42 and the diluted binder 44. Accordingly, luxury and relatively low price can be popularly distributed.

직물, 모의 금, 금분, 바인더, 코팅층Fabric, Mock Gold, Gold Powder, Binder, Coating Layer

Description

모의 금 및 금분이 코팅된 삼베수의 및 그 제조방법 {HEMP CLOTH SHROUD COATED GOLD DUST AND ARTIFICIAL GOLD AND ITS MANUFACTURING PROCESS}Simulated gold and gold powder coated hemp and its manufacturing method {HEMP CLOTH SHROUD COATED GOLD DUST AND ARTIFICIAL GOLD AND ITS MANUFACTURING PROCESS}

도 1은 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의를 도시한 사시도,1 is a perspective view showing the sham gold and gold powder coated burlap according to the present invention,

도 2는 도 1의 A-A′선에 따른 단면도,2 is a cross-sectional view taken along line AA ′ of FIG. 1;

도 3은 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의의 제1코팅층을 확대 도시한 단면도,3 is an enlarged cross-sectional view of a first coating layer of hemp gold and gold powder coated according to the present invention;

도 4는 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의의 제2코팅층을 확대 도시한 단면도,4 is an enlarged cross-sectional view of a second coating layer of hemp gold and gold powder coated with simulated gold according to the present invention;

도 5는 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의의 제조방법을 도시한 흐름도이다.Figure 5 is a flow chart showing a method of manufacturing simulated gold and gold powder coated hemp according to the present invention.

< 도면의 주요 부분에 대한 부호의 설명 >              <Description of Symbols for Main Parts of Drawings>

10 : 삼베수의 20 : 직물              10: 20 of the hemp

30 : 제1코팅층 32 : 모의 금              30: first coating layer 32: simulated gold

34,44 : 바인더 40 : 제2코팅층              34,44: binder 40: second coating layer

42 : 금분              42: gold powder

본 발명은 삼베수의에 관한 것으로서, 보다 상세하게는 고급스러움을 강조하기 위하여 그 표면에 모의 금 및 금분이 코팅된 삼베수의 및 그 제조방법에 관한 것이다.The present invention relates to burlap veterinary ware, and more particularly, to mock gold and gold powder coated on its surface in order to emphasize luxury, and a manufacturing method thereof.

일반적으로, 수의(壽衣)는 염습할 때에 송장에 입히는 옷을 일컫는 말로서, 수의용 직물로는 삼베와 아마 또는 모시 등으로 직조된 천연섬유가 주로 사용된다.In general, veterinary refers to clothes worn on invoices when wet, and veterinary fabrics mainly use natural fibers woven from burlap and flax or ramie.

특히, 삼베는 수분의 흡수력 및 배출력이 상대적으로 우수할 뿐 아니라 항균 기능 및 자외선 차단 기능을 동시에 가짐으로써 수의용 직물로 가장 적합하다.In particular, burlap is most suitable as a veterinary fabric by having a relatively good absorption and discharge of water as well as having an antibacterial function and a UV protection function at the same time.

최근에 들어 외관적 고급스러움을 강조한 금분이 함유된 최고급 수의가 선보이고 있다.Recently, the highest quality veterinary containing gold powder, which emphasizes the appearance of luxury, has been introduced.

그 일 예로서, 삼베를 기지로 하는 직물지에 귀금속분이 함유된 부착제를 분사 도포하여 이루어지는 수의가 있으며, 이는 실용신안등록번호 제20-0255821호에 개시되어 있다.As an example, there is a veterinary product by spraying and applying an adhesive containing precious metal powder to textile paper based on burlap, which is disclosed in Utility Model Registration No. 20-0255821.

또한, 공개특허공보 제2002-0033117호에는 폴리우레탄계의 수용성 접착제와 금분 및 식물성 효료를 일체로 혼합시켜 하나의 섬유 바인더인 코팅제로 형성한 다음, 이를 삼베로 직조된 직물지의 표면에 도포하여 건조시킨 수의가 개시되어 있다.In addition, Korean Patent Laid-Open Publication No. 2002-0033117 discloses a polyurethane-based water-soluble adhesive, gold powder, and vegetable chemicals, which are integrally mixed to form a coating agent, which is a fiber binder, and then coated on a surface of fabric paper woven with burlap. Veterinary is disclosed.

이 외에도 금 성분을 이용한 다양한 형태의 수의가 시중에 공지되어 있다.In addition, various forms of veterinary using the gold component are known on the market.

그러나 상기와 같은 수의는 삼베로 직조된 직물에 순도 약 100%의 금분이 혼합된 혼합물이 전체적으로 코팅됨으로써 외관상 고급스러움을 강조할 수 있다는 장점은 있으나, 상당한 양의 금분이 소요되어 수의의 단가가 높다는 문제점이 있다.However, the above-mentioned veterinary merchandise has the advantage of being able to emphasize the luxury in appearance by coating the mixture of gold powder of about 100% purity on the woven fabric of burlap, but it takes a considerable amount of gold powder and the cost of veterinary is high. There is a problem.

이에 따라, 일부 부유층들 외에는 상기와 같은 수의를 구입하기에는 현실적 어려움이 있다.Accordingly, there is a practical difficulty to purchase such a veterinarian except for some rich people.

이는, 사회계층 간의 위화감을 조성함은 물론이고 수의용 직물을 고급스럽게 하기를 원하는 대부분의 망자 유족들을 이용한 지나친 상술에 불과하다는 지적이 있다.It is pointed out that this is merely an excessive detail using most of the deceased families who want to create a sense of discomfort among the social class as well as veterinary fabrics.

그리고 직물지에 금분을 도포하는 방법상의 문제점으로 인해, 금분이 직물지에 제대로 코팅되지 않거나 또는 금속 질감의 발현성이 상대적으로 저하되는 단점이 있다.In addition, due to a problem in the method of applying gold powder to the textile paper, the gold powder is not properly coated on the textile paper or there is a disadvantage that the expression of the metal texture is relatively reduced.

본 발명은 상기와 같은 문제점을 해결하기 위하여 창출된 것으로, 외관이 고급스러우면서도 가격이 저렴한 모의 금 및 금분이 코팅된 삼베수의 및 그 제조방법을 제공하고자 하는 데 그 목적이 있다.The present invention has been made to solve the above problems, and an object of the present invention is to provide a mock gold and gold powder coated and a manufacturing method of the mock gold and gold powder with a high appearance and low cost.

상기와 같은 목적을 달성하기 위하여 본 발명은, 삼베로 직조된 직물; 상기 직물의 표면에 형성되며, 모의 금 및 희석된 바인더가 혼합된 성분으로 이루어진 제1코팅층; 상기 제1코팅층의 소매 및 고름 부위에 형성되며, 금분 및 희석된 바인더가 혼합된 성분으로 이루어진 제2코팅층을 포함하여 구성되는 데 그 기술적 특징이 있다.In order to achieve the above object, the present invention, the woven fabric burlap; A first coating layer formed on the surface of the fabric and composed of a component in which mock gold and a diluted binder are mixed; It is formed on the sleeve and pus portion of the first coating layer, and comprises a second coating layer made of a mixture of gold powder and diluted binder has a technical feature.

상기 제1코팅층은 모의 금 10∼20 중량%, 바인더 50∼70 중량% 및 희석액 20∼30중량%로 이루어지는 것이 바람직하다.The first coating layer is preferably made of 10 to 20% by weight of simulated gold, 50 to 70% by weight of the binder and 20 to 30% by weight of the diluent.

상기 모의금은 운모와 산화규소의 혼합물 45.1∼67.0 중량%, 산화티타늄 19.0∼29.0 중량% 및 산화철 14.0∼25.0 중량%로 이루어지는 것이 바람직하다.It is preferable that the said sum consists of 45.1-67.0 weight% of a mixture of mica and silicon oxide, 19.0-29.0 weight% of titanium oxide, and 14.0-25.0 weight% of iron oxide.

상기 바인더로는 아크릴 바인더, 상기 희석액으로는 물이 사용되는 것이 바람직하다.It is preferable that an acrylic binder is used as said binder and water is used as said diluent.

상기 운모, 상기 산화규소, 상기 산화티타늄 및 상기 산화철은 그 입자의 크기가 10∼60㎛인 것이 바람직하다.The mica, silicon oxide, titanium oxide and iron oxide preferably have a particle size of 10 to 60 µm.

그리고 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의의 제조방법은, 운모, 산화규소, 산화티타늄 및 산화철로 이루어진 모의 금 10∼20 중량%, 바인더 50∼70 중량% 및 희석액 20∼30중량%를 혼합하여 제1코팅재를 제조하는 단계; 제1코팅재를 삼베로 직조된 직물에 공기압을 이용한 스프레이 방식으로 분사하여 제1코팅층을 형성하는 단계; 제1코팅층을 건조하는 단계; 금분 및 희석된 바인더를 혼합하여 제2코팅재를 제조하는 단계; 제2코팅재를 제1코팅층의 소매 및 고름 부위에 공기압을 이용한 스프레이 방식으로 분사하여 제2코팅층을 형성하는 단계; 제2코팅층을 건조하는 단계를 포함하여 구성되는 데 그 기술적 특징이 있다.And the method of manufacturing simulated gold and gold powder coated hemp according to the present invention, 10 to 20% by weight of simulated gold consisting of mica, silicon oxide, titanium oxide and iron oxide, 50 to 70% by weight binder and 20 to 30% by weight of diluent Mixing the% to prepare a first coating material; Forming a first coating layer by spraying the first coating material on a fabric woven with burlap by a spray method using air pressure; Drying the first coating layer; Preparing a second coating material by mixing the gold powder and the diluted binder; Forming a second coating layer by spraying the second coating material on the sleeve and the pus part of the first coating layer by a spray method using air pressure; There is a technical feature that comprises a step of drying the second coating layer.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예를 설명하면 다음과 같다.Hereinafter, exemplary embodiments of the present invention will be described with reference to the accompanying drawings.

도 1 내지 도 4에 도시된 바와 같이, 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의(10)는 삼베로 직조된 직물(20); 직물(20)의 표면에 형성되는 제1코팅층(30); 제1코팅층(30)의 특정 부위에 형성되는 제2코팅층(40)을 포함하여 구성된다.As shown in Figures 1 to 4, simulated gold and gold powder coated burlap 10 according to the present invention is a burlap woven fabric 20; A first coating layer 30 formed on the surface of the fabric 20; It is configured to include a second coating layer 40 formed on a specific portion of the first coating layer 30.

직물(20)의 원재료로 사용되는 삼베는 수분의 흡수력 및 배출력이 상대적으로 우수할 뿐 아니라 항균 기능 및 자외선 차단 기능을 가지는 등 여러 장점이 있다. Burlap used as a raw material of the fabric 20 has a number of advantages, such as having a relatively good absorption and discharge of moisture, as well as having an antibacterial function and UV protection.

한편, 삼베의 재질적 특성은 공지된 기술의 일부이므로 그 자세한 설명은 생략하기로 한다.On the other hand, since the material characteristics of the burlap is a part of the known technology, a detailed description thereof will be omitted.

제1코팅층(30)은 직물(20)의 외부면 전체에 형성되며, 제1코팅층(30)은 도 3에서와 같이 모의 금(32) 및 희석된 바인더(binder)(34)가 혼합된 성분으로 이루어진다. The first coating layer 30 is formed on the entire outer surface of the fabric 20, the first coating layer 30 is a component in which the simulated gold 32 and the diluted binder 34 is mixed as shown in FIG. Is done.

즉, 제1코팅층(30)은 색상 및 광택 그리고 직물(20)과의 결합성 등을 고려하여 모의 금(32) 10∼20 중량%, 바인더(34) 50∼70 중량% 및 희석액 20∼30중량%로 이루어지는 것이 바람직하다.
상기와 같이 제1코팅층(30)의 성분함량을 수치한정한 이유는 모의 금의 중량비가 10 중량% 미만일 경우에는 그 광택이나 색상의 질이 저하되고, 10 중량%를 초과할 경우에는 삼베 자체의 질감이 상대적으로 저하된다는 문제점이 있기 때문입니다. 그리고 바인더 및 희석액이 한정된 중량비를 벗어날 경우에는 모의 금 및 직물과의 상호 결합력이 현저하게 저하되거나 또는 건조가 잘 되지 않으며, 건조된 후에도 코팅액이 묻어나오는 문제점이 있기 때문입니다.That is, the first coating layer 30 is 10 to 20% by weight of the simulated gold (32), 50 to 70% by weight of the binder 34 and the diluent 20 to 30 in consideration of color and gloss, and bonding to the fabric 20, etc. It is preferable to consist of weight%.
The reason for limiting the component content of the first coating layer 30 as described above is that if the weight ratio of the simulated gold is less than 10% by weight, the gloss or the quality of the color is lowered. This is because there is a problem that the texture is relatively degraded. If the binder and the diluent are out of the limited weight ratio, the mutual bonding strength between the simulated gold and the fabric will be significantly reduced or the drying will not be good, and the coating liquid will still come out after drying.

모의 금(32)은 운모(mica)와 산화규소(SiO2)의 혼합물 45.1∼67.0 중량%, 산화티타늄(TiO2) 19.0∼29.0 중량% 및 산화철(Fe2O3) 14.0∼25.0 중량%로 이루어진다.Simulated gold (32) is 45.1-67.0 wt% of mica and silicon oxide (SiO 2 ), 19.0-29.0 wt% of titanium oxide (TiO 2 ) and 14.0-25.0 wt% of iron oxide (Fe 2 O 3 ). Is done.

모의 금(32)은 상기와 같은 성분 및 비율을 가짐으로써 순도 약 100%의 금분과 거의 유사한 광택 및 색상을 표현할 수 있을 뿐 아니라 직물(20)과의 결합력 또한 탁월하다는 장점이 있다. 즉, 부착성 및 금속질감의 발현성을 보다 향상시킬 수 있다.Simulated gold 32 has the above-described components and ratios, which can express gloss and color almost similar to gold powder having a purity of about 100%, as well as excellent bonding force with the fabric 20. That is, the adhesiveness and the expression of metal texture can be improved more.

바인더(34)로는 아크릴 바인더(acrylic binder)가 사용되며, 바인더(34)의 재질로는 아크릴을 비롯하여 공지된 다양한 재질의 것을 선택적으로 적용할 수 있음은 물론이다.Acrylic binder (acrylic binder) is used as the binder 34, the material of the binder 34 can be selectively applied to a variety of known materials, including acrylic.

희석액은 제1코팅층(30)의 코팅이 용이하도록 바인더(34)를 희석시키기 위한 것이다. 그리고 희석액으로는 물을 비롯하여 바인더(34)의 부착성 및 금펄(32)의 색 발현성 등을 향상시킬 수 있는 범위 내에서 공지된 다양한 종류의 것을 선택적으로 사용할 수 있다.The diluent is for diluting the binder 34 to facilitate coating of the first coating layer 30. In addition, as the diluent, various kinds of known materials can be selectively used within a range capable of improving the adhesion of the binder 34 and the color development of the gold pearl 32, including water.

예컨대, 물 등과 같은 희석액을 이용하여 바인더(34)를 희석시키지 않을 때에는 제1코팅층(30)의 건조가 잘 되지 않음은 물론이고 건조가 된 후에도 코팅액이 묻어 나오는 단점이 있다.For example, when the binder 34 is not diluted using a diluent such as water, the first coating layer 30 may not be dried well, and there is a disadvantage in that the coating liquid remains even after drying.

모의 금(32)의 성분인 운모, 산화규소, 산화티타늄 및 산화철은 그 입자의 크기가 10∼60㎛인 것이 바람직하다. 이렇게 모의 금(32)의 성분에 대한 입자의 크기를 제한하는 이유는 그 입자의 크기가 10㎛ 미만일 경우에는 색의 발현성이 상대적으로 떨어지며, 60㎛를 초과할 경우에는 입자가 거칠어 코팅작업이 어려울 뿐 아니라 외관상 보기가 좋지 않다는 문제점이 있기 때문입니다.Mica, silicon oxide, titanium oxide and iron oxide, which are components of the simulated gold 32, preferably have a particle size of 10 to 60 mu m. The reason for limiting the size of the particles to the components of the simulated gold 32 is that when the size of the particles is less than 10 μm, the expressability of color is relatively low, and when the size of the particle exceeds 60 μm, the coating is difficult due to the roughness of the particles. Not only is it difficult, but it doesn't look good.

한편, 모의 금(32)은 필요에 따라 진주가루로 만든 모조금분을 사용할 수도 있다.On the other hand, the simulated gold 32 may use imitation gold powder made of pearl powder as needed.

제2코팅층(40)은 삼베수의(10)의 소매 및 고름 등과 같은 특정 부위에 형성된다. The second coating layer 40 is formed on a specific portion, such as sleeve and pus of the hemp veterinary 10.

제2코팅층(40)의 형성위치는 적절하게 변경 가능하며, 필요에 따라 일정의 무늬를 형상화할 수도 있다.The position at which the second coating layer 40 is formed can be appropriately changed, and a predetermined pattern can be shaped as necessary.

제2코팅층(40)은 도 4에서와 같이 순도 약 100%의 금분(gold dust)(42) 및 희석된 바인더(binder)(44)가 혼합된 성분으로 이루어지며, 제2코팅층(40)은 색상 및 광택 그리고 직물(20)과의 결합성 등을 전체적으로 고려하여 금분(42) 10∼20 중량%, 바인더(44) 50∼70 중량% 및 희석액 20∼30중량%로 이루어지는 것이 바람직하다.As shown in FIG. 4, the second coating layer 40 is composed of a mixture of gold dust 42 having a purity of about 100% and a diluted binder 44, and the second coating layer 40 is In consideration of the color and gloss, and the binding to the fabric 20, it is preferable that the composition consists of 10 to 20% by weight of the gold powder 42, 50 to 70% by weight of the binder 44 and 20 to 30% by weight of the diluent.

금분(42)과 희석된 바인더(44)의 혼합비율은 필요에 따라 적절히 조절 가능하다.The mixing ratio of the gold powder 42 and the diluted binder 44 can be suitably adjusted as needed.

바인더(44)로는 제1코팅층(30)과 마찬가지로 아크릴 바인더가 사용되며, 바인더(44)를 희석시키기 위한 희석액 역시 물이 사용되는 것이 보다 바람직하다. As the binder 44, an acrylic binder is used similarly to the first coating layer 30, and more preferably water is used as the diluent for diluting the binder 44.

이상에서와 같이, 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의는 외관적인 고급스러움을 강조함과 아울러 그 제조단가를 현저하게 절감시킬 수 있도록 직물(20)의 표면에 전체적으로 모의 금(32) 및 희석액에 의해 희석된 바인더(34) 혼합물로 이루어진 제1코팅층(30)을 형성하고, 제1코팅층(30)의 특정의 영역에는 금분(42) 및 희석액에 의해 희석된 바인더(44) 혼합물로 이루어진 제2코팅층(40)을 형성한 것에 그 기술적 특징이 있다.As described above, the simulated gold and gold powder coated hemp veterinary coating according to the present invention emphasizes the appearance of luxury and significantly reduces the manufacturing cost of the simulated gold (32) And a mixture of the binder 44 diluted by the gold powder 42 and the diluent in a specific area of the first coating layer 30, and a mixture of the binder 34 diluted with the diluent. The technical feature is that the second coating layer 40 made of a.

도 5는 본 발명에 따른 모의 금 및 금분이 코팅된 삼베수의의 제조방법을 도시한 흐름도이다.Figure 5 is a flow chart showing a method of manufacturing simulated gold and gold powder coated hemp according to the present invention.

① 제1단계(S1) : 삼베로 직물을 직조하는 단계로서, 삼베수의를 만들 수 있을 정도의 크기로 삼베를 직조한다.① 1st step (S1): This is a step of weaving fabric with burlap, and weaving burlap to the size enough to make burlap.

② 제2단계(S2) : 운모, 산화규소, 산화티타늄 및 산화철로 이루어진 모의 금 및 희석된 바인더를 일정시간 동안 혼합하여 제1코팅재를 제조하는 단계.② second step (S2): a step of preparing a first coating material by mixing the simulated gold and the diluted binder consisting of mica, silicon oxide, titanium oxide and iron oxide for a predetermined time.

이 때, 제1코팅재의 코팅효율을 극대화시키기 위해서 모의 금은 10∼20 중량%를 가지며, 바인더는 50∼70 중량%를 가지며, 희석액은 20∼30중량%를 가지도록 한다. In this case, in order to maximize the coating efficiency of the first coating material, the simulated gold has 10 to 20% by weight, the binder has 50 to 70% by weight, and the diluent has 20 to 30% by weight.

③ 제3단계(S3) : 모의 금 및 희석액에 의해 희석된 바인더가 혼합된 제1코팅재를 공기압에 의한 스프레이 분사방식으로 직물의 표면에 분사하여 제1코팅층을 형성하는 단계.③ Third step (S3): forming a first coating layer by spraying the first coating material mixed with the simulated gold and the diluting liquid to the surface of the fabric by a spray spray method by air pressure.

이 때, 직물의 표면에 형성되는 제1코팅층의 두께는 적절하게 조절 가능하다.At this time, the thickness of the first coating layer formed on the surface of the fabric can be adjusted appropriately.

④ 제4단계(S4) : 제1코팅층을 건조하는 단계.④ fourth step (S4): drying the first coating layer.

이 때, 제1코팅층은 자연 건조시키거나 또는 별도의 가열수단을 사용하여 건조시킬 수 있다.At this time, the first coating layer may be naturally dried or may be dried using a separate heating means.

⑤ 제5단계(S5) : 금분 및 희석된 바인더를 혼합하여 제2코팅재를 제조하는 단계.⑤ fifth step (S5): a step of preparing a second coating material by mixing gold powder and diluted binder.

이 때, 금분 및 희석액에 의해 희석된 바인더의 혼합비율은 광택 및 결합성을 등을 고려하여 적절하게 조절 가능하다.At this time, the mixing ratio of the binder diluted with the gold powder and the dilution liquid can be appropriately adjusted in consideration of the gloss and the bonding properties.

⑥ 제6단계(S6) : 금분 및 희석액에 의해 희석된 바인더가 혼합된 제2코팅재를 공기압에 의한 스프레이 분사방식으로 제1코팅층의 특정 부위에 분사하여 제2코팅층을 형성하는 단계.⑥ the sixth step (S6): forming a second coating layer by spraying a second coating material mixed with a gold powder and a diluent binder to a specific portion of the first coating layer by a spray spray method by air pressure.

이 때, 제1코팅층의 특정 표면에 형성되는 제2코팅층의 두께는 적절하게 조절 가능하다.At this time, the thickness of the second coating layer formed on the specific surface of the first coating layer can be appropriately adjusted.

⑦ 제7단계(S7) : 제2코팅층을 건조하는 단계.⑦ seventh step (S7): drying the second coating layer.

이 때, 제2코팅층은 자연 건조시키거나 또는 별도의 가열수단을 사용하여 건조시킬 수 있다.At this time, the second coating layer may be naturally dried or may be dried using a separate heating means.

⑧ 제8단계(S8) : 제1코팅층 및 제2코팅층이 형성된 직물을 재단하여 바지, 저고리 등과 같이 특정 형상의 수의로 만드는 단계.⑧ eighth step (S8): cutting the fabric formed with the first coating layer and the second coating layer to make a certain number of shapes, such as pants, ring.

이상에서와 같은 총 8단계를 거쳐 모의 금 및 금분이 코팅된 삼베수의의 제조과정이 완료되며, 이 과정 중 본원의 기술적 핵심은 제2단계(S2)에서 제7단계(S7)를 거치는 데 있다.The manufacturing process of the simulated gold and gold powder coated hemp is completed through a total of eight steps as described above, the technical core of the present application is from the second step (S2) to the seventh step (S7). .

한편, 제1단계(S1) 및 제2단계(S2)는 공정순서가 바뀌어도 전혀 무관하며, 제1코팅재 및 제2코팅재는 미리 제조해 놓거나 공정 중에 제조할 수 있음은 물론이다.On the other hand, the first step (S1) and the second step (S2) is completely irrelevant even if the process order is changed, the first coating material and the second coating material may be prepared in advance or can be manufactured during the process.

이상에서 설명한 바와 같이 본 발명에 따르면, 삼베수의에 모의 금 및 금분이 적절히 조화됨으로써 외관상으로는 순도 약 100%의 금분이 함유된 삼베수의와 실질적으로 동일한 효과를 기대할 수 있음은 물론이고 제품단가는 현저하게 낮출 수 있다.As described above, according to the present invention, the simulated gold and gold powder are suitably harmonized with the hemp, and the product price can be expected to be substantially the same as that of the hemp which is about 100% pure gold. Can be significantly lowered.

그로 인해, 고급스러우면서도 가격이 저렴한 수의를 대중적으로 보급시킬 수 있다.As a result, luxury and low price can be popularized.

또한, 제1·2코팅층의 성분비적 특성 및 특정의 코팅방법(공기압에 의한 분사방식)을 사용함으로써 색상 및 광택이 우수할 뿐 아니라 그 결합력을 향상시킬 수 있다는 장점이 있다.In addition, by using the component ratio characteristics of the first and second coating layer and a specific coating method (injection method by air pressure), there is an advantage that not only the color and gloss are excellent, but also the bonding force can be improved.

Claims (4)

수의에 있어서,In veterinary terms, 삼베로 직조된 직물;Burlap woven fabrics; 상기 직물의 표면에 형성되며, 모의 금 및 희석된 바인더가 혼합된 성분으로 이루어진 제1코팅층;A first coating layer formed on the surface of the fabric and composed of a component in which mock gold and a diluted binder are mixed; 상기 제1코팅층의 소매 및 고름 부위에 형성되며, 금분 및 희석된 바인더가 혼합된 성분으로 이루어진 제2코팅층을 포함하는 것을 특징으로 하는 모의 금 및 금분이 코팅된 삼베수의.Simulated gold and gold powder coated hemp is formed on the sleeve and pus portion of the first coating layer, comprising a second coating layer consisting of a mixture of gold powder and diluted binder. 제1항에 있어서,The method of claim 1, 상기 제1코팅층은 모의 금 10∼20 중량%, 바인더 50∼70 중량% 및 희석액 20∼30중량%로 이루어지며,The first coating layer is composed of 10 to 20% by weight of simulated gold, 50 to 70% by weight of the binder and 20 to 30% by weight of the diluent, 상기 모의 금은 운모와 산화규소의 혼합물 45.1∼67.0 중량%, 산화티타늄 19.0∼29.0 중량% 및 산화철 14.0∼25.0 중량%로 이루어지는 것을 특징으로 하는 모의 금 및 금분이 코팅된 삼베수의.The gold simulated gold and gold powder coated hemp consists of 45.1-67.0% by weight of a mixture of mica and silicon oxide, 19.0-29.0% by weight of titanium oxide and 14.0-25.0% by weight of iron oxide. 제2항에 있어서,The method of claim 2, 상기 운모, 상기 산화규소, 상기 산화티타늄 및 상기 산화철은 그 입자의 크기가 10∼60㎛인 것을 특징으로 하는 모의 금 및 금분이 코팅된 삼베수의.The mica, the silicon oxide, the titanium oxide and the iron oxide are simulated gold and gold powder coated hemp, characterized in that the particle size is 10 ~ 60㎛. 운모, 산화규소, 산화티타늄 및 산화철로 이루어진 모의 금 10∼20 중량%, 바인더 50∼70 중량% 및 희석액 20∼30중량%를 혼합하여 제1코팅재를 제조하는 단계;Preparing a first coating material by mixing 10-20 wt% of mock gold, silicon oxide, titanium oxide and iron oxide, 50-70 wt% of a binder, and 20-30 wt% of a diluent; 제1코팅재를 삼베로 직조된 직물에 스프레이 방식으로 분사하여 제1코팅층을 형성하는 단계;Spraying the first coating material onto the fabric woven with burlap to form a first coating layer; 제1코팅층을 건조하는 단계;Drying the first coating layer; 금분 및 희석된 바인더를 혼합하여 제2코팅재를 제조하는 단계;Preparing a second coating material by mixing the gold powder and the diluted binder; 제2코팅재를 제1코팅층의 소매 및 고름 부위에 스프레이 방식으로 분사하여 제2코팅층을 형성하는 단계;Forming a second coating layer by spraying a second coating material on the sleeve and the pus portion of the first coating layer by a spray method; 제2코팅층을 건조하는 단계를 포함하는 것을 특징으로 하는 모의 금 및 금분이 코팅된 삼베수의 제조방법.Method of producing a simulated gold and gold powder coated hemp comprising the step of drying the second coating layer.
KR1020060116819A 2006-11-24 2006-11-24 Hemp cloth shroud coated gold dust and artificial gold and its manufacturing process KR100870936B1 (en)