KR100866047B1 - Method of inkjet printing using resinless ink - Google Patents

Method of inkjet printing using resinless ink Download PDF

Info

Publication number
KR100866047B1
KR100866047B1 KR1020070064082A KR20070064082A KR100866047B1 KR 100866047 B1 KR100866047 B1 KR 100866047B1 KR 1020070064082 A KR1020070064082 A KR 1020070064082A KR 20070064082 A KR20070064082 A KR 20070064082A KR 100866047 B1 KR100866047 B1 KR 100866047B1
Authority
KR
South Korea
Prior art keywords
ink
printing
laser beam
synthetic resin
inkjet
Prior art date
Application number
KR1020070064082A
Other languages
Korean (ko)
Inventor
김태원
Original Assignee
백진상
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 백진상 filed Critical 백진상
Priority to KR1020070064082A priority Critical patent/KR100866047B1/en
Application granted granted Critical
Publication of KR100866047B1 publication Critical patent/KR100866047B1/en

Abstract

An inkjet printing method using resinless ink is provided to print character, symbol, and pattern very clearly. A character, a symbol, and a pattern are printed on a synthetic resin printed object by using an ink-jet printer. Laser beam is irradiated on the character, symbol, and pattern and heats them. While moving above the printed object, the printer head prints the predetermined character, symbol, and pattern. Anhydrous paper printing ink emitted from the ink-jet nozzle of the printer head is sublimated and deposited inside the surface of the printed object.

Description

무수지잉크를 이용한 합성수지재 상의 잉크젯 프린팅 방법{Method of inkjet printing using resinless ink}Inkjet printing method on synthetic resin material using anhydrous ink {Method of inkjet printing using resinless ink}

도 1은 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 잉크젯 프린팅 장치의 첫 번째 실시예의 구성도이다.1 is a block diagram of a first embodiment of a synthetic resin surface inkjet printing apparatus using an anhydrous ink according to the present invention.

도 2는 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 잉크젯 프린팅 장치의 두 번째 실시예의 구성도이다.2 is a block diagram of a second embodiment of a synthetic resin surface inkjet printing apparatus using an anhydrous ink according to the present invention.

도 3은 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 잉크젯 프린팅 장치의 세 번째 실시예의 구성도이다.Figure 3 is a block diagram of a third embodiment of a synthetic resin surface inkjet printing apparatus using an anhydrous ink according to the present invention.

도 4는 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 고해상도 잉크젯 프린팅을 위해 인쇄잉크를 분사하고 이때 낙점된 인쇄잉크를 레이저빔에 의하여 고열로 순간 가열하여 컴퓨터 프로그램상에서 설정,지시한 인쇄 데이터 값에 따라 가.감 없이 정밀 하게 피인쇄물의 표피 내측에 승화 침착시키기 위한 레이저빔 조절장치의 첫 번째 실시예의 구성도이다. Figure 4 is sprayed printing ink for high-resolution inkjet printing of a synthetic resin surface using an anhydrous ink according to the present invention, and the print data values set and instructed on a computer program by instantaneously heating the dropped printing ink to a high temperature by a laser beam Fig. 1 is a schematic diagram of a first embodiment of a laser beam control device for sublimation deposition on the inside of the skin of an object with precision without feeling.

도 5는 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 고해상도 잉크젯 프린팅을 위해 인쇄잉크를 분사하고 이때 낙점된 인쇄잉크를 고열로 순간 가열하여 컴퓨터 프로그램상에서 설정,지시한 인쇄 데이터 값에 따라 가.감 없이 정밀하게 피인쇄물의 표피 내측에 승화 침착시키기 위한 레이저빔 조절장치의 두 번째 실시예의 구성도이다.5 is sprayed the printing ink for high-resolution inkjet printing on the surface of the synthetic resin using anhydrous ink according to the present invention, the instantaneous heating of the dropped printing ink at a high temperature in accordance with the print data values set and indicated on the computer program. This is a schematic diagram of a second embodiment of the laser beam control device for sublimation deposition on the inside of the skin of a printed object with precision.

도 6은 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 고해상도 잉크젯 프린팅 공정도이다.Figure 6 is a high-resolution inkjet printing process of the surface of the synthetic resin material using the resin ink according to the present invention.

*도면의 주요부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *

10,15 : 레이저빔발생장치 11,12,13,22,23 : 미러10,15 laser beam generator 11,12,13,22,23 mirror

20 : 프린터헤드 21 : 잉크젯노즐20: printhead 21: inkjet nozzle

24 : 렌즈 30 : 캐리지레일24 lens 30 carriage rail

40 : 받침대 41 : 피인쇄물40: pedestal 41: the print

본 발명은 열가소성수지 또는 열경화성수지 표면에 수지성분을 포함하지 않는 잉크를 이용하여 문자, 기호, 문양 등을 고해상도로 잉크젯 프린트할 수 있으며 합성수지재의 표면상에 인쇄층의 높이를 가지지 않는 무수지잉크를 이용한 합성수지재 상의 잉크젯 프린팅 방법에 관한 것이다.The present invention can inkjet print letters, symbols, patterns, etc. in high resolution using an ink that does not contain a resin component on the surface of a thermoplastic or thermosetting resin, and an anhydrous ink that does not have a height of a printing layer on the surface of a synthetic resin material. It relates to an inkjet printing method on a synthetic resin material used.

잘 알려진 바와 같이, 잉크젯 프린팅 방식은 피에조소자를 이용하는 압전 잉크젯 방식과 저항소자의 가열에 의한 가열식 잉크젯 방식으로 대별된다.As is well known, the inkjet printing method is roughly classified into a piezoelectric inkjet method using a piezo element and a heated inkjet method by heating the resistance element.

여기서 압전식 잉크젯 프린팅 방식은 프린터의 잉크 카트리지에 인쇄명령의 전기적신호가 가해지면 프린터 헤드부의 피에조장치가 작동하여 잉크 카트리지 내의 잉크가 노즐을 통해 피인쇄물 표면에 방출되도록 한 것이고, 가열식 잉크젯 방 식은 잉크 탱크내의 레지스터를 통해 잉크를 가열하여 기포를 생성시키고 이렇게 생성된 기포는 내부의 압력증가에 의해 노즐을 통해 피인쇄물 표면으로 방출되게 한 것이다.Here, the piezoelectric inkjet printing method is a piezoelectric device of the print head when an electrical signal of a print command is applied to the ink cartridge of the printer so that the ink in the ink cartridge is discharged to the surface of the to-be-printed object through the nozzle. The ink is heated through a resistor in the tank to create bubbles, which are then released through the nozzle to the surface of the substrate by increasing pressure therein.

이러한 잉크젯 프린터를 이용하여 피인쇄물의 표면에 문자, 기호, 도형 등을 인쇄할 때, 피인쇄물의 재질이 지물류 또는 직물류에서는 프린터의 성능에 따라 사용자가 원하는 정도의 인쇄품질을 얻는 것이 가능하였다.When printing letters, symbols, figures, and the like on the surface of a to-be-printed object using such an inkjet printer, it is possible to obtain print quality of a degree desired by a user according to the performance of the printer in the material of paper or textiles.

그러나 열가소성수지나 열경화성수지와 같은 합성수지재의 표면에 특정 문양이나 기호, 문자 등을 인쇄할 경우 표면이 매끄럽게 잘 연마된 피인쇄물에서는 잉크와 피인쇄물 표면 사이에서 일어나는 표면 장력 증가 등으로 인한 잉크의 응집(말림), 잉크의 퍼짐,현상으로 인하여 원하는 고해상도의 인쇄품질을 얻을 수 없다.However, in the case of prints on which the surface of the synthetic resin material such as thermoplastic resin or thermosetting resin is smoothly polished when printing certain patterns, symbols, or characters, ink agglomeration due to the increase in surface tension between the ink and the surface of the print material ( Curling), ink spreading and development may not achieve the desired high resolution print quality.

또한 합성수지재의 표면에 잉크젯 방식의 프린팅을 위해서는 인쇄잉크에 수지성분을 포함시켜야 하는데, 이는 잉크의 점도 증가에 따른 잉크젯 인쇄속도의 저하문제와 인쇄잉크를 고착시키기 위한 열처리시간의 증가를 초래한다.In addition, in order to print the inkjet method on the surface of the synthetic resin material, a resin component should be included in the printing ink, which causes a decrease in inkjet printing speed due to an increase in viscosity of the ink and an increase in heat treatment time for fixing the printing ink.

특히, 합성수지재 표면에의 잉크젯 인쇄시 나타나는 여러 문제점들 중에서도 인쇄품질에 가장 영향을 미치는 것은 인쇄잉크가 피인쇄물의 표면에 돌출된다는 점이다. 이것은 합성수지재의 표면에 특정 문자자 문양 등을 잉크젯 프린팅하기 위해서는 잉크에 수지성분을 포함시키고 있기 때문이며, 잉크성분 모두 승화하고 나더라도 잉크에 포함되었던 수지성분이 피인쇄물인 합성수지재의 표면 위에 또 다른 인쇄층을 형성하기 때문이다.In particular, the most influential print quality among the various problems encountered in inkjet printing on the surface of the synthetic resin material is that the printing ink protrudes from the surface of the object to be printed. This is because in order to inkjet print certain character patterns and the like on the surface of the synthetic resin material, a resin component is included in the ink, and even after all the ink components are sublimated, another printing layer is placed on the surface of the synthetic resin material whose resin component is contained in the ink. Because it forms.

이러한 합성수지재 표면 상의 인쇄층은 사용감 과 질감을 떨어뜨리므로 고품위용 제품 케이스로서 합성수지재를 사용하는데 제한이 따르게 된다.Since the printing layer on the surface of the synthetic resin degrades the feel and texture, there is a restriction in using the synthetic resin as a high-quality product case.

본 발명은 상기와 같은 종래 잉크젯 프린팅 기술의 문제점을 해결하기 위한 것으로, 본 발명의 목적은 열가소성수지 또는 열경화성수지 표면에 수지성분을 포함하지 않는 잉크를 이용하여 소정의 문자, 기호, 문양 등을 인쇄한 후 즉시 레이저빔에 의한 가열을 통해 프로그램상에서 설정,지시한 데이터 값을 가.감 없이 정밀 수행하여 인쇄잉크를 피인쇄물의 내부에 승화 침착시킴으로서 인쇄층의 높이가 없는 고해상도의 인쇄품질을 얻을 수 있는 무수지잉크를 이용한 합성수지재 상의 잉크젯 프린팅 방법을 제공하는데 있다.The present invention is to solve the problems of the conventional inkjet printing technology as described above, an object of the present invention is to print a predetermined letter, symbol, pattern, etc. using an ink that does not contain a resin component on the surface of the thermoplastic resin or thermosetting resin Immediately afterwards, the laser beam can be precisely set and instructed through the heating of the laser beam to precisely execute the print ink without sublimation. To provide an inkjet printing method on a synthetic resin material using an anhydrous ink.

상기 목적을 달성하기 위한 본 발명의 무수지잉크를 이용한 합성수지재 상의 잉크젯 프린팅 방법은 프린터헤드가 합성수지재인 피인쇄물 위를 이동하면서 소정의 문자, 기호, 문양을 잉크젯 인쇄하게 하되, 상기 프린터헤드의 잉크젯노즐에서 피인쇄물로 분사되는 무수지인쇄잉크가 피인쇄물 표면에 낙점되는 즉시 레이저빔에 의해 순간 가열되어 컴퓨터 프로그램상에서 설정,지시한 데이터 값을 가.감 없이 정밀 수행하여 피인쇄물 표피층 내부로 승화 침착되게 하는 것을 특징으로 한다.The inkjet printing method on a synthetic resin material using the anhydrous ink of the present invention for achieving the above object is to allow inkjet printing of predetermined characters, symbols, and patterns while the printhead moves on a to-be-printed material, the inkjet of the printer head As soon as the ink-free printing ink sprayed from the nozzle is dropped onto the surface of the substrate, it is instantaneously heated by the laser beam and sublimed to the inside of the substrate layer by precisely performing the data values set and indicated in the computer program. It is characterized in that.

첨부한 도면을 참고로 하여 본 발명을 설명하면 다음과 같다.Hereinafter, the present invention will be described with reference to the accompanying drawings.

도 1은 본 발명에 따른 무수지잉크를 이용한 합성수지재 상의 잉크젯 프린팅 장치의 첫 번째 실시예의 구성도이다.1 is a block diagram of a first embodiment of an inkjet printing apparatus on a synthetic resin material using an anhydrous ink according to the present invention.

여기에서 잉크젯 프린터 장치는 컴퓨터(도시생략)로부터 인쇄 데이터신호나 사전에 프로그램된 인쇄 데이터신호를 받아 프린터 몸체 양쪽의 측벽(31,32)사이에 배치되는 캐리지레일(30)을 이동하면서 받침대(40)상의 피인쇄물(41) 표면에 소정의 문자, 기호, 문양을 인쇄하는 프린터헤드(20)를 포함한다.Here, the inkjet printer apparatus receives a print data signal or a pre-programmed print data signal from a computer (not shown) and moves the carriage rail 30 disposed between the side walls 31 and 32 on both sides of the printer body, thereby supporting the base 40. It includes a printhead 20 for printing a predetermined letter, symbol, pattern on the surface of the to-be-printed 41.

상기 프린터헤드(20)는 잉크젯노즐(21)을 열가소성수지 도는 열경화성 수지 등의 합성수지재 표면에 잉크를 분사하여 인쇄하도록 배치한다.The print head 20 arranges the ink jet nozzle 21 to print by spraying ink onto a surface of a synthetic resin such as a thermoplastic resin or a thermosetting resin.

상기 프린터헤드(20)의 잉크젯노즐(21)로부터 피인쇄물의 표면에 분사 안착된 인쇄잉크를 고열승화시켜 합성수지재인 피인쇄물의 표피층 내부로 침착시키기 위한 레이저빔을 발생하는 레이저빔 발생장치(10)를 잉크젯 프린터의 소정의 위치에 배치한다.A laser beam generator (10) for generating a laser beam for high thermal sublimation of the print ink jetted and seated on the surface of the to-be-printed object from the inkjet nozzle (21) of the printer head (20) to be deposited into the skin layer of the to-be-printed material (synthetic resin material). Is placed in a predetermined position of the inkjet printer.

상기 레이저빔발생장치(10)로부터 출력되는 레이저빔은 프린터헤드가 장착될 캐리지레일(30)과 평행한 방향으로 반사되도록 레이저빔 발생장치의 반대쪽 측벽에 제1미러(11)를 배치한다. 여기서 제1미러는 레이저빔의 반사각을 조절 가능한 상태로 배치한다.The first mirror 11 is disposed on the side wall opposite to the laser beam generator so that the laser beam output from the laser beam generator 10 is reflected in a direction parallel to the carriage rail 30 on which the print head is to be mounted. Here, the first mirror is arranged in a state in which the reflection angle of the laser beam is adjustable.

상기 제1미러(11)에서 반사되어 캐리지레일(30)과 평행한 방향으로 조사되는 레이저빔은 프린터헤드(20)에 장착된 제2미러(22)를 통해서 잉크젯노즐에 의한 인쇄 직후의 지점으로 조사되게 제2미러(22)를 배치한다.The laser beam reflected from the first mirror 11 and irradiated in a direction parallel to the carriage rail 30 passes to the point immediately after printing by the inkjet nozzle through the second mirror 22 mounted on the printer head 20. Position the second mirror 22 to be irradiated.

이와 같이 구성된 본 발명 장치의 첫 번째 실시예의 작용을 설명하면 다음 과 같다.Referring to the operation of the first embodiment of the device of the present invention configured as described above is as follows.

레이저발생장치(10)에서 출력되는 레이저빔은 제1미러(11)와 제2미러(22)를 통하여 프린터헤드(20)의 잉크젯노즐(21)에 의한 직전의 인쇄지점에 조사된다. 따라서 프린터헤드(20)가 캐리지레일(30)을 따라 이동하면서 인쇄동작을 수행하게 되면 레이저빔도 동일하게 잉크젯 인쇄부위를 따라가면서 분사된 잉크를 고열로 가열하여 해당 인쇄잉크가 표면 장력에 영향을 받지않고 컴퓨터 프로그램상에서 설정,지시한 데이터 값을 가.감 없정밀 인쇄되어 피인쇄물 표피층 내부에 승화 침작된다.The laser beam output from the laser generating apparatus 10 is irradiated to the printing position just before the inkjet nozzle 21 of the print head 20 through the first mirror 11 and the second mirror 22. Therefore, when the print head 20 moves along the carriage rail 30 and performs a printing operation, the laser beam also follows the inkjet printing portion and heats the ejected ink at high temperature, thereby affecting the surface tension. The data are set and instructed on the computer program without being received, and then printed precisely without subtraction.

즉, 컴퓨터 또는 자체의 프로그램에 따른 인쇄 데이터신호를 프린터헤드가 받아 잉크젯노즐(21)을 통해 합성수지재의 피인쇄물(41)상에 문자, 기호, 문양 등을 인쇄하게 되면, 잉크젯노즐(21)에서 분사되어 피인쇄물에 안착된 잉크는 상기 레이저빔에 의해 즉시 가열되어 승화침착이 일어나게 되므로 받침대(40)상의 피인쇄물(41)표면에는 인쇄층의 높이를 가지지 않는 각종 문자, 기호, 문양 등이 형성된다.That is, when the printhead receives a print data signal according to a computer or a program thereof, and prints letters, symbols, patterns, etc. on the to-be-printed material 41 of the synthetic resin material through the inkjet nozzle 21, the inkjet nozzle 21 Since the ink sprayed and deposited on the to-be-printed object is immediately heated by the laser beam to cause sublimation deposition, various letters, symbols, and patterns are formed on the surface of the to-be-printed material 41 on the pedestal 40 without the height of the printed layer. do.

즉, 위와 같은 인쇄잉크의 순간 레이저 가열에 의한 승화 및 침착현상은 피인쇄물의 매끄러운 표면에서 나타나는 통상적인 표면 장력 증가 등으로 인한 잉크의 응집(말림), 잉크 의 퍼짐,현상 으로 인한 문제를 해결하므로 고해상도의 인쇄품질을 얻을 수 있게 하면서 또한 인쇄층이 피인쇄물의 표피층 내부로 참착됨에 따라 인쇄층의 두께를 가지지 않는 질감과 외관이 우수한 인쇄품질을 얻을 수 있게 한다.That is, the sublimation and deposition phenomenon by the instantaneous laser heating of the printing ink solves the problems caused by the cohesion (curing) of the ink, the spread of the ink, and the phenomenon caused by the increase of the normal surface tension appearing on the smooth surface of the printed matter. It is possible to obtain a high-quality print quality and also to obtain a print quality that is excellent in texture and appearance without the thickness of the print layer as the print layer comes into the skin layer of the to-be-printed material.

합성수지재의 표면 인쇄를 위해 상기 잉크젯 카트리지에 충입되는 잉크는 수지성분을 포함하지 않는 무수지 잉크이다.The ink filled in the inkjet cartridge for printing the surface of the synthetic resin material is an anhydrous ink containing no resin component.

본 발명에서는 잉크젯프린터의 속도와 인쇄형태 등에 따라 최상의 해상도와 고품질을 얻기 위해 통상의 레이저빔 조절장치(도시생략)로 상기 레이저빔발생장치의 출력을 조절할 수 있다.In the present invention, the output of the laser beam generator can be controlled by a conventional laser beam control device (not shown) in order to obtain the best resolution and high quality according to the speed and printing form of the inkjet printer.

도 2는 본 발명의 무수지 잉크를 이용한 합성수지 표면 잉크젯 프린팅 장치의 두 번째 실시예로서, 양방향 잉크젯 인쇄모드를 지원할 수 있는 구조를 보인 것이다.Figure 2 is a second embodiment of a synthetic resin surface inkjet printing apparatus using an anhydrous ink of the present invention, it shows a structure capable of supporting a bidirectional inkjet printing mode.

본 발명장치의 두 번째 실시예는 앞서 설명한 첫 번째 실시예의 구성에 제3-5미러(12,13,23)를 추가 설치한 구성으로, 상기 프린터헤드(20)의 제2미러(22)와 대응하는 반대쪽에 제5미러(23)를 장착하고, 제5미러(23)에는 상기 제1미러(11)와 대응하는 반대 위치에 배치된 제4미러(13)와 상기 제1미러의 상부에 배치된 제3미러(12)를 통하여 레이저빔발생장치(10)의 레이저빔이 조사되게 구성하고 있다.The second embodiment of the apparatus of the present invention is a configuration in which the third to fifth mirrors 12, 13, and 23 are additionally installed in the configuration of the first embodiment described above, and the second mirror 22 of the printer head 20 The fifth mirror 23 is mounted on the corresponding opposite side, and the fifth mirror 23 is mounted on the fourth mirror 13 and the upper portion of the first mirror disposed at the opposite position corresponding to the first mirror 11. The laser beam of the laser beam generator 10 is irradiated through the arranged third mirror 12.

상기 제4미러(13)와 제5미러(23)사이의 레이저빔은 앞서 설명한 제1미러(11)와 제2미러(22)사이의 레이저빔과 마찬가지로 캐리지레일(30)과 동일한 평행선을 이루도록 구성한다.Like the laser beam between the first mirror 11 and the second mirror 22 described above, the laser beam between the fourth mirror 13 and the fifth mirror 23 forms the same parallel lines as the carriage rail 30. Configure.

따라서 잉크젯 프린터의 양방향 인쇄시, 프린터헤드(20)의 인쇄방향이 도면상 우측에서 좌측으로 이동하면서 인쇄할 경우 레이저빔발생장치(10)의 레이저빔은 제3,4,5미러(12,13,23)를 통하여 피인쇄물(41)의 표면에 안착된 인쇄잉크를 즉시 가열 승화침착시키고, 반대로 프린터헤드(20)의 인쇄방향이 도면상 좌측에서 우측으로 이동하면서 인쇄할 경우 레이저빔발생장치(10)의 레이저빔은 제1,2미러(11,22)를 통하여 피인쇄물(41)의 표면에 안착된 인쇄잉크를 가열 승화 침착시킨 다.Therefore, in the bidirectional printing of the inkjet printer, when the printing direction of the print head 20 is printed while moving from right to left on the drawing, the laser beams of the laser beam generator 10 are the third, fourth, and fifth mirrors 12 and 13. When the printing ink seated on the surface of the to-be-printed material 41 is immediately heated and sublimed, and on the contrary, the printing direction of the print head 20 moves from left to right on the drawing, the laser beam generator ( The laser beam of 10) heat-sublimates and deposits the printing ink seated on the surface of the to-be-printed object 41 through the first and second mirrors 11 and 22.

이것은 앞에서도 설명한 바와 같이 잘 연마된 합성수지재의 표면 인쇄시 나타날 수 있는 표면 장력 증가 등으로 인한 잉크의 응집(말림), 잉크 의 퍼짐,현상 으로 인한 인쇄품질 저하 및 해상도 저하를 방지한다.This prevents agglomeration (curing) of the ink, spreading of the ink, deterioration of print quality due to increase in surface tension, etc., which may occur when printing the surface of a well polished synthetic resin material, as described above.

위와 같은 본 발명 장치의 두 번째 실시예의 양방향 인쇄동작 모드에서는 당해 기술분야에서 통상의 지식을 가진 자가 쉽게 선택할 수 있는 레이저빔발생장치(10)의 간단하고 통상적인 틸팅제어가 요구된다.In the bidirectional printing operation mode of the second embodiment of the apparatus of the present invention as described above, a simple and conventional tilting control of the laser beam generator 10 which can be easily selected by those skilled in the art is required.

도 3은 본 발명에 따른 합성수지재 표면에의 고해상도 잉크젯 프린팅 장치의 세 번째 실시예로서, 또 다른 양방향 잉크젯 인쇄모드를 지원할 수 있는 구조를 보인 것이다.3 is a third embodiment of a high resolution inkjet printing apparatus on a surface of a synthetic resin material according to the present invention, and shows a structure capable of supporting another bidirectional inkjet printing mode.

여기서는 각각 독립적인 한 쌍의 레이저빔발생장치(10,15)와 제1,2미러(11,22) 및 제4,5미러(13,23)에 의해 합성수지재인 피인쇄물(41)의 표면에 양방향 잉크젯 프린팅을 수행할 수 있으며, 한 쌍의 레이저빔발생장치(10,15)에서 출력되는 레이저빔과 제1,2미러(11,22) 및 제4,5미러(13.23)를 이용하여 피인쇄물(41)의 표면에 안착된 인쇄잉크를 가열 승화시킴으로서 컴퓨터 프로그램상에서 설정,지시한 데이터값의 가.감 없이 정밀 수행에 이어 피인쇄물 내부에 소정의 문자나 문양 등을 침착시키게 된다.In this case, a pair of independent laser beam generators 10 and 15, first and second mirrors 11 and 22, and fourth and fifth mirrors 13 and 23 are applied to the surface of the to-be-printed material 41 which is a synthetic resin material. Two-way inkjet printing can be performed, using the laser beams output from the pair of laser beam generators 10 and 15, and the first and second mirrors 11 and 22 and the fourth and fifth mirrors 13.23. By heating and sublimating the printing ink seated on the surface of the printed matter 41, predetermined characters, patterns, etc. are deposited inside the printed matter following precision execution without the influence of data values set and indicated on a computer program.

도 4는 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 고해상도 잉크젯 프린팅을 위해 인쇄잉크를 분사하고 이때 낙점된 인쇄잉크를 고열로 순간 가열하여 피인쇄물의 표피 내측에, 컴퓨터 프로그램상에서 설정,지시한 인쇄 데이터 값 에 따라 가.감 없이 승화 침착시키기 위한 레이저빔 조절장치의 첫 번째 실시예의 구성도이다.4 is sprayed printing ink for high-resolution inkjet printing using synthetic resin surface according to the present invention, and instantaneous heating of the dropped printing ink at a high temperature inside the skin of the to-be-printed object, which is set and indicated on a computer program. A schematic diagram of a first embodiment of a laser beam control device for sublimation deposition without depending on the print data value.

이것은 프린터헤드(20)에 장착될 제2미러(22) 또는 제5미러(23)의 표면을 레이저빔 확산용 미러로 만듬으로써 잉크젯노즐에서 분사되어 피인쇄물(41)의 표면에 낙점된 인쇄잉크를 레이저빔에 의하여 고열로 가열, 피인쇄물 의 표피층 내부로 해당 문양 등을 컴퓨터 프로그램상에서 설정,지시한 데이터값에 따라 가.감 없이 정밀 하게 승화 침착시킬 때, 고열 승화 침착범위 및 가열온도 등을 결정하는 레이저빔의 조사영역과 그 확산범위를 조절할 수 있다.This is a printing ink sprayed from the inkjet nozzle by dropping the surface of the second mirror 22 or the fifth mirror 23 to be mounted on the printhead 20 by the laser beam diffusion mirror and dropping the surface of the to-be-printed object 41. Heats with high temperature by laser beam, and sets the corresponding pattern into the inside of the skin layer of the printed matter according to the specified data value. The irradiation area of the laser beam to be determined and its diffusion range can be adjusted.

여기서 레이저빔의 확산범위(L1, L2)는 제2미러(22) 또는 제5미러(23)의 설치높이 조절 또는 이들의 반사각도 조절을 통하여 조정하는 것이 가능하다.Herein, the diffusion ranges L1 and L2 of the laser beam may be adjusted by adjusting the installation height of the second mirror 22 or the fifth mirror 23 or adjusting the reflection angle thereof.

도 5는 본 발명에 따른 유리 또는 금속 표면에의 고해상도 잉크젯 프린팅을 위한 분사잉크의 가열 승화침착 조절장치의 두 번째 실시예의 구성도이다.5 is a block diagram of a second embodiment of a heating sublimation deposition control apparatus of a jet ink for high resolution inkjet printing on a glass or metal surface according to the present invention.

여기서는 프린터헤드(20)에 장착된 제2미러(22) 또는 제5미러(23)와 피인쇄물 사이의 공간에 위치이동 가능한 렌즈(24)를 설치한다. 이것은 피인쇄물(41)의 표면에 낙점된 잉크를 레이저빔으로 고열 승화침착, 컴퓨터 프로그램상에서 설정,지시한 데이터값의 가.감 없는 정밀 수행할 때, 레이저빔의 확산 정도 및 확산범위(L1, L2)를 조절할 수 있게 한다.Here, the lens 24 which can be moved is provided in the space between the second mirror 22 or the fifth mirror 23 attached to the printer head 20 and the printed object. This results in the degree of diffusion of the laser beam and the diffusion range L1, when the ink droplets dropped on the surface of the to-be-printed object 41 are subjected to high-temperature sublimation deposition with a laser beam, and precisely performed without a sense of setting and indicating data values on a computer program. L2) can be adjusted.

도 6은 본 발명에 따른 무수지잉크를 이용한 합성수지재 표면 고해상도 잉크젯 프린팅 공정도이다.Figure 6 is a high-resolution inkjet printing process of the surface of the synthetic resin material using the resin ink according to the present invention.

여기에서 참고되는 것처럼, 합성수지재의 피인쇄물 표면에 잉크젯프린터를 이용하여 소정의 문자, 기호, 문양을 무수지 잉크로 인쇄하고(a, b), 인쇄된 소정의 문자, 기호, 문양 위에 레이저빔을 조사 가열하여(c), 합성수지재의 표면층 내부로 무수지인쇄잉크를 승화 침착시키고 있다(d).As referred to herein, an inkjet printer is used to print a predetermined letter, symbol, or pattern on the surface of a synthetic resin material using an inkjet printer (a, b), and a laser beam is placed on the printed predetermined letter, symbol, or pattern. Irradiation heating (c) causes sublimation deposition of anhydrous printing ink into the surface layer of the synthetic resin material (d).

즉, 본 발명의 무수지잉크를 이용한 합성수지재 표면 인쇄방법은 프린터헤드가 합성수지재인 피인쇄물 위를 이동하면서 소정의 문자, 기호, 문양을 잉크젯 인쇄하게 하되, 상기 프린터헤드의 잉크젯노즐에서 피인쇄물로 분사되는 무수지인쇄잉크는 피인쇄물 표면 낙점 즉시 레이저빔에 의해 순간 가열되도록 컴퓨터 프로그램상에서 설정,지시한 데이터값을 가.감 없이 인쇄잉크를 피인쇄물의 표피층 내부에 승화 침착시킴으로서 합성수지재인 피인쇄물의 표면에 인쇄층의 돌출이 없는 고해상도의 인쇄품질을 얻을 수 있다.That is, the synthetic resin surface printing method using the anhydrous ink of the present invention allows the printhead to move on the to-be-printed material, which is inkjet printing a predetermined letter, symbol, or pattern, from the inkjet nozzle of the printhead to the to-be-printed. The sprayed anhydrous printing ink can be sublimed and deposited on the inside of the skin layer of the to-be-printed material by applying a data value set and indicated in a computer program so as to be instantly heated by the laser beam immediately after the drop of the to-be-printed surface. It is possible to obtain high resolution printing quality without protruding print layer on the surface.

이상에서 설명한 바와 같은 본 발명의 무수지잉크를 이용한 합성수지재 상의 잉크젯 프린팅 방법은 열가소성수지 또는 열경화성수지 표면에 수지성분을 포함하지 않는 잉크를 이용하여 문자, 기호, 문양 등을 인쇄하되, 잉크젯노즐에서 피인쇄물 표면으로 분사되는 인쇄잉크를 레이저빔을 조사하여 컴퓨터 프로그램상에서 설정,지시한 데이터값의 가.감 없는 피인쇄물 표면층 내부로 승화침착시킴으로서 합성수지재의 케이스 표면에 인쇄층의 높이를 가지지 않는 고품위, 고품질의 인쇄를 가능하게 하는 특유의 효과가 나타난다.As described above, the inkjet printing method on the synthetic resin material using the anhydrous ink of the present invention prints letters, symbols, and patterns on the surface of the thermoplastic resin or thermosetting resin using ink that does not contain a resin component, High quality that does not have the height of the printing layer on the surface of the case of synthetic resin material by sublimating and depositing the printing ink sprayed onto the surface of the substrate by irradiating a laser beam into the surface layer of the to-be-printed material without setting or indicating the data value. A distinctive effect is shown to enable high quality printing.

Claims (1)

잉크젯 프린터를 이용한 합성수지재 표면 인쇄방법에 있어서, 프린터헤드가 합성수지재인 피인쇄물 위를 이동하면서 소정의 문자, 기호, 문양을 잉크젯 인쇄하게 하되, 상기 프린터헤드의 잉크젯노즐에서 피인쇄물로 분사되는 무수지인쇄잉크는 피인쇄물의 표면에 낙점되는 즉시 컴퓨터 프로그램상에서 설정,지시한 데이터값의 가.감 없이 레이저빔에 의해 순간 고열로 가열되어 피인쇄물의 표피층 내부로 인쇄잉크가 승화 침착되게 하는 것을 특징으로 하는 무수지잉크를 이용한 합성수지재 상의 잉크젯 프린팅 방법.A method of printing a surface of a synthetic resin material using an inkjet printer, wherein the printhead moves on a to-be-printed material, and ink-jet prints predetermined characters, symbols, and patterns, and is sprayed onto the to-be-printed inkjet nozzle of the printhead. The printing ink is heated to instantaneous high temperature by the laser beam without any change of the data values set and indicated on the computer program as soon as it falls on the surface of the printed material, thereby subliming deposition of the printing ink into the inside of the surface of the printed material. An inkjet printing method on a synthetic resin material using an anhydrous ink.
KR1020070064082A 2007-06-28 2007-06-28 Method of inkjet printing using resinless ink KR100866047B1 (en)