KR100848044B1 - Dyed veneer and method of manufacturing thereof - Google Patents

Dyed veneer and method of manufacturing thereof Download PDF

Info

Publication number
KR100848044B1
KR100848044B1 KR1020080015291A KR20080015291A KR100848044B1 KR 100848044 B1 KR100848044 B1 KR 100848044B1 KR 1020080015291 A KR1020080015291 A KR 1020080015291A KR 20080015291 A KR20080015291 A KR 20080015291A KR 100848044 B1 KR100848044 B1 KR 100848044B1
Authority
KR
South Korea
Prior art keywords
veneer
natural
dyed
natural veneer
dyeing
Prior art date
Application number
KR1020080015291A
Other languages
Korean (ko)
Inventor
신호열
Original Assignee
(주) 혜성무늬목
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주) 혜성무늬목 filed Critical (주) 혜성무늬목
Priority to KR1020080015291A priority Critical patent/KR100848044B1/en
Application granted granted Critical
Publication of KR100848044B1 publication Critical patent/KR100848044B1/en

Abstract

A dyed natural veneer manufacturing method and a dyed veneer produced by the same are provided to unify the tones of the dyed veneer made of the same species of trees, at low cost through a simple process and to use the veneer with the unified tone and the veneer with the natural tone selectively. A dyed natural veneer manufacturing method comprises the steps of: dispersing oil dyes having the single color, in an oil solvent and applying the mixture to a thin film(101); laminating the film on the veneer of 0.1~0.5mm which is not decolorized(102); and making tones of the front and rear surfaces of the veneer different by gradually dyeing the veneer with dyes in the thickness of 10~70% of the veneer while keeping temperature of 160~190°C and pressure of 5~30Kg/cm^3 by a heat press(103).

Description

염색 천연 무늬목 제조 방법 및 그 제조 방법으로 제조된 염색 천연 무늬목{DYED VENEER AND METHOD OF MANUFACTURING THEREOF}DYED VENEER AND METHOD OF MANUFACTURING THEREOF

본 발명은 염색에 의하여 색조(tone:색깔이 짙거나 옅은 정도)를 변경한 염색 천연 무늬목 및 그 제조 방법에 관한 것으로, 더 상세하게는 동일 수종이면서도 색조의 차이를 나타내는 천연 무늬목의 일면에 염료를 일정 두께로 침염하여 표면의 색조는 통일시키고 이면의 색조는 천연 색조가 그대로 유지되게 함으로써 천연 무늬목의 활용도를 높인 염색 천연 무늬목 및 그 제조 방법에 관한 것이다.The present invention relates to a dyed natural veneer and a method of manufacturing the same by changing the color tone (dark or light color) by dyeing, and more particularly, the dye on one side of the natural veneer showing the difference in color between the same species Dyeing natural veneer and a method for producing the same by increasing the utilization of natural veneer by dyeing the surface to a uniform thickness and uniformity of the color tone of the surface and maintaining the natural color tone.

천연 무늬목은 자연스러운 무늬, 색감 및 질감으로 인하여 바닥표면재, 벽장식재, 가구용 문짝 등 특히 자연스러운 미감이 요구되는 인테리어 표면재나 가구의 표면재로 널리 사용되고 있다. 일반적으로 동일한 장소의 바닥표면재, 벽장식재 또는 동일한 셋트의 가구 등에는 동일 수종의 천연 무늬목이 사용된다. 그러나, 천연 무늬목은 동일 수종 및 동일 무늬인 경우에도 나무의 생육환경, 연령 등에 따라 그 색조(色調)에 차이가 있다. 이것이 소위 천연 무늬목의 이색(異色) 문제이다. 천연 무늬목을 인테리어나 가구 소재로 사용하는 경우 색조가 일치하지 않은 천연 무늬목을 그대로 사용하여 자연스러운 미감을 얻기도 하지만, 동일 수종 및 동일 무늬 뿐만 아니라 동일 색조를 갖는 천연 무늬목을 이용하여 고급스러운 미감을 얻기도 한다.Natural veneer is widely used as interior surface material or surface material of furniture, which requires natural aesthetics such as floor surface material, wall decoration material, furniture door, etc. due to natural pattern, color and texture. Generally, the same species of natural veneer is used for floor coverings, wall coverings or furniture of the same set in the same place. However, natural veneer differs in the color tone of the same species and the same pattern depending on the growth environment and age of the tree. This is the so-called bicolor problem of natural veneer. If natural veneer is used as interior or furniture material, natural veneers with different color tones can be used as they are, but a natural aesthetic can be obtained. Also

당업계에서는 천연 무늬목의 이색 문제를 다음의 2가지 방법으로 해결해 왔다.The art has solved the bicolor problem of natural veneer in the following two ways.

우선, 비교적 고가 원목을 슬라이싱(slicing)하여 얻은 얇은 천연 무늬목을 정련->표백->수세->중화처리 등의 단계를 거쳐 탈색하고, 드라이어에 의하여 건조한 후 열프레스에 의하여 곧게 펼쳐 염료통에 딥핑(dipping)함으로써, 무늬목 전체를 동일한 색조로 염색 처리하는 방법이 사용되고 있다. 다음, 비교적 저가 원목을 스라이싱(slicing)하여 얻은 얇은 천연 무늬목을 위와 같은 과정을 거쳐 염색 처리한 후 이들을 블럭(각재)으로 집성하여 다시 슬라이싱함으로써 얇은 염색 무늬목을 얻는 방법도 사용되고 있다. 그러나, 이 방법들은 정련 설비, 표백 설비, 수세 설비, 중화 설비, 건조설비, 열프레스 등의 많은 설비를 요구할 뿐만 아니라, 염색 시간이 많이 소요되어 지나치게 고가이다. 또한, 자연스러운 천연 무늬목의 질감이나 무늬를 얻을 수 없고, 이면과 표면이 전체적으로 동일한 색상으로 염색이 되어 후술하는 바와 같이 사용자가 염색된 색상과 천연 색상을 필요에 따라 선택하여 사용할 수 없는 단점이 있다.First, the thin natural veneer obtained by slicing relatively expensive solid wood is decolorized through steps such as refining-> bleaching-> washing-> neutralization, dried by a dryer and straightened by a heat press to dip into a dye container. By dipping, the method of dyeing the whole veneer with the same color tone is used. Next, a method of obtaining a thin dyed veneer by slicing the thin natural veneer obtained by slicing relatively inexpensive solid wood through the same process and then slicing them into blocks (squares) is also used. However, these methods not only require a lot of equipment such as refining equipment, bleaching equipment, washing equipment, neutralization equipment, drying equipment, heat press, etc., but also require excessive dyeing time and are too expensive. In addition, the natural natural veneer texture or pattern can not be obtained, the back and the surface is dyed in the same color as a whole, there is a disadvantage that the user can not select and use the dyed color and natural color as needed as will be described later.

상술한 종래 천연 무늬목이 갖는 이색 문제를 해결하고자 안출된 본 발명은 표면과 이면의 무늬가 동일하면서도 표면은 통일된 색조를 갖고 이면은 천연 무늬목의 색상을 그대로 갖는 염색 천연 무늬목을 제공하는 데 그 목적이 있다. The present invention devised to solve the bi-color problem of the conventional natural veneer described above is to provide a dyed natural veneer having the same pattern on the surface and the back surface, but the surface has a uniform color tone and the same color as the natural veneer. There is this.

본 발명이 다른 목적은 매우 간단한 공정 및 저렴한 비용으로 동종 수종의 천연 무늬목이 갖는 색조를 통일시킬 수 있는 염색 천연 무늬목 제조 방법을 제공하는 데 있다. Another object of the present invention is to provide a method for producing dyed natural veneer that can unify the color tone of the same species of natural veneer in a very simple process and at a low cost.

본 발명의 또 다른 목적은 사용자가 통일된 색조와 천연 색조를 선택적으로 사용할 수 있는 염색 천연 무늬목 및 그 제조 방법을 제공하는 데 있다.Still another object of the present invention is to provide a dyed natural veneer and a method of manufacturing the same, in which a user can selectively use a unified color tone and a natural color tone.

상술한 목적을 달성하고자 하는 본 발명에 따른 염색 천연 무늬목은 탈색되지 않은 0.1mm 내지 0.5mm 두께의 얇은 천연 무늬목에, 단일 색상으로 배합된 유성 염료를 천연무늬목 두께의 10% ~ 70%의 두께까지 침염(浸染)시켜, 천연 무늬목의 전면과 후면의 색조(色調)가 다르게 한 것을 특징으로 한다. Dyeing natural veneer according to the present invention to achieve the above object is a thin natural veneer of 0.1mm to 0.5mm thickness not discolored, the oil-based dye blended in a single color up to 10% to 70% of the thickness of the natural veneer thickness It is characterized by differentiation of the color of the front and back of natural veneer.

상술한 목적을 달성하고자 하는 본 발명에 따른 염색 천연 무늬목의 제조 방법은 단일 색상을 갖도록 배합한 유성 염료를 유기 용제에 분산시켜 얇은 필름에 도포한 후, 탈색되지 않은 0.1mm 내지 0.5mm 두께의 천연 무늬목 상에 적층하고, 열프레스에 의하여 160 ~ 190℃ 온도, 5 ~ 30 Kg/㎠의 압력을 유지하면서, 염료의 침염(浸染) 두께가 천연무늬목 두께의 10% ~ 70%에 이르게 하여, 천연 무늬목의 전면과 후면의 색조가 다르게 한 것을 특징으로 한다. According to the present invention, a method of manufacturing dyed natural veneer according to the present invention is to disperse an oily dye blended to have a single color in an organic solvent and apply it to a thin film. Laminated on the veneer, the dyeing thickness of the dye reaches 10% to 70% of the thickness of the natural veneer, while maintaining the pressure of 160 ~ 190 ℃ temperature, 5 ~ 30 Kg / ㎠ by heat press It is characterized by different shades of the front and back of the veneer.

상술한 구성을 갖는 본 발명에 의하면, 매우 간단한 공정 및 저렴한 비용으로 동종 수종의 천연 무늬목이 갖는 색조의 차이를 통일시킬 수 있을 뿐만 아니라, 사용자가 색조가 통일된 무늬목과 천연 색조의 무늬목을 선택적으로 사용할 수 있는 효과가 있다.According to the present invention having the above-described configuration, it is possible to unify the differences in the hue of the natural veneers of the same species in a very simple process and at a low cost, and the user can selectively select the veneers of the uniform hue and the veneer of the natural hue. There is an effect that can be used.

이하, 첨부한 도면을 참조하여 본 발명에 따른 염색 천연 무늬목 및 그 제조 방법의 바람직한 실시 예를 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment of the dyed natural veneer according to the present invention and its manufacturing method.

도 1a은 수종은 동일하나 색조가 다른 천연 무늬목을 분리하여 배치한 평면도를, 도 1b는 도 1a에 도시된 천연 무늬목을 연결한 상태를 보여 주는 평면도를, 도 2는 색조의 보정이 필요한 천연 무늬목과 염료 도포 필름을 차례로 열프레스의 베이스 상면에 적층하고, 열압착하는 방법으로 보여 주는 공정 사시도를, 도 3은 본 발명 에 따른 천연 무늬목의 염색 방법을 보여 주는 공정도를, 도 4a는 염색된 면이 상면에 오도록 도시한 본 발명에 따른 염색 천연 무늬목을, 도 4b는 염색되지 않은 면이 상면에 오도록 도시한 본 발명에 따른 염색 천연 무늬목을 각각 나타낸다.FIG. 1A is a plan view of a natural veneer separated from one another but different shades, and FIG. 1B is a plan view showing a state in which natural veneers shown in FIG. 1A are connected, and FIG. 2 is a natural veneer requiring color correction. And a dye coating film are sequentially laminated on the base upper surface of the heat press, and a process perspective view showing a method of thermocompression bonding, FIG. 3 is a process chart showing a method of dyeing natural veneer according to the present invention, and FIG. 4A is a dyed surface. The dyed natural veneer according to the present invention shown to be on this top surface, Figure 4b shows the dyed natural veneer according to the present invention shown so that the undyed side is on the top.

도 1a은 천연 무늬목이 수종이 동일하여 그 목리, 무늬 및 질감이 같은 경우에도, 색조(tone)에 있어서는 나무마다 조금씩 차이가 있음을 보여 준다. 즉 도 1a에는 부호 1a로 표시한 천연 무늬목이 부호 1b로 표시한 천연 무늬목보다 더 진한 색조를 갖는 경우를 예시적으로 도시한 것이다. 이러한 색조의 차이가 있는 천연 무늬목을 이용하여 벽장식 등의 인테리어를 할 경우, 동일 수종의 천연 무늬목 소재를 사용함에도 불구하고, 도 1b에 나타낸 바와 같이, 각 무늬목 마다 모양은 같지만 색조의 차이를 보여, 전체적인 색조의 통일감을 얻기 어렵게 된다. Figure 1a shows that even when the natural wood veneer is the same species, the tree, the pattern and the texture are the same, there is a slight difference for each tree in the tone (tone). That is, FIG. 1A exemplarily illustrates a case in which the natural veneer indicated by the reference 1a has a darker color tone than the natural veneer indicated by the reference 1b. When interiors such as wall decoration using natural veneer with such a difference in color tone are used, even though natural veneer materials of the same species are used, as shown in FIG. 1B, each veneer has the same shape but shows a difference in color tone. It becomes difficult to obtain the unity of the general hue.

본 발명의 특징은 천연 무늬목 표면을 단일 색조의 염료로 일정 깊이 만큼 염색하여, 표면과 이면의 무늬나 질감은 같으면서도, 표면은 통일된 색조를 갖게 하고, 이면은 천연 무늬목의 색조를 그대로 갖게 한 데 있다.A feature of the present invention is that the surface of the natural veneer is dyed to a certain depth with a single color tone, so that the surface and the back surface have the same pattern and texture, but the surface has a uniform color tone, and the back surface has the color of the natural veneer intact. There is.

도 2 및 도 3를 참조하면, 이를 위하여 본 발명에 따른 염색 천연 무늬목 제조 방법은 동종 수종의 천연 무늬목을 0.1mm 내지 0.5mm 두께로 절삭하여 얇은 천연 무늬목 시트를 얻는 단계(100)와, 청색, 적색 및 황색의 유성 분산 염료를 적절히 배합하여 단일 색상을 갖는 유성 염료를 얻고, 이를 메탄올 및 에탄올 등의 유기 용 제에 분산시켜, 얇은 필름에 도포하는 단계(101)를 포함한다. 이 때 유성 염료 및 유기 용제의 혼합 비율은 20:80 중량% 내지 40:60 중량%이다.여기에는 폴리비닐부티랄 등의 수지 확산제와 에틸렌글리콜 등의 유화제를 적량(유성 염료 및 유기 용제의 혼합물에 대한 1중량%이하) 첨가할 수 있다. 2 and 3, for this purpose, the method for producing dyed natural veneer according to the present invention comprises the steps of obtaining a thin natural veneer sheet by cutting a natural veneer of the same species to a thickness of 0.1mm to 0.5mm (100), blue, A red and yellow oily dye is suitably blended to obtain an oily dye having a single color, which is dispersed in an organic solvent such as methanol and ethanol and applied to a thin film (101). At this time, the mixing ratio of the oil dye and the organic solvent is 20: 80% by weight to 40: 60% by weight. Herein, a suitable amount of an emulsifier such as a resin diffusing agent such as polyvinyl butyral and ethylene glycol is used. Up to 1% by weight of the mixture).

본 발명에 따른 염색 천연 무늬목 제조 방법은 염색할 천연 무늬목(1a, 1b)과 염료 도포 필름(7)을 열프레스의 베이스(5)에 적층하는 단계(102) 및 염료 도포 필름(7)을 열프레스 가동부(3)로 압착하여 염료가 천연 무늬목의 표면으로 부터 천연 무늬목 두께의 10% ~ 70%에 이르기 까지 침염하게 하는 단계(103)를 더 포함한다. 열프레스에 의한 열압착 조건은 160 ~ 190℃ 온도, 5 ~ 30 Kg/㎠의 압력을 유지하면서, 약 10초 내지 70초를 유지하는 것이 바람직하나, 필요한 염료의 침염(浸染) 두께에 따라 가감할 수 있다. 본 발명에 따른 염색 천연 무늬목 제조 방법의 특징은 염료를 열압착 방법에 의하여 침염시키고, 그 침염 두께를 침염 압력 및 침염 시간에 의하여 조절하는 데 있다. Dyeing natural veneer manufacturing method according to the present invention comprises the step (102) laminating the natural veneer (1a, 1b) and the dye coating film (7) to the base 5 of the heat press to be dyed and heat the dye coating film (7) The method further comprises a step 103 of pressing the press moving part 3 to dye the dye from the surface of the natural veneer to 10% to 70% of the thickness of the natural veneer. The thermocompression conditions by heat press are preferably maintained at about 10 seconds to 70 seconds while maintaining a temperature of 160 to 190 ° C. and a pressure of 5 to 30 Kg / cm 2, but depending on the dyeing thickness of the dye required. can do. A characteristic of the method for producing dyed natural veneer according to the present invention is to dye the dye by thermocompression method, and to control the thickness of the dye by the dyeing pressure and dyeing time.

도 4a 및 도 4b에 도시된 바와 같이, 이렇게 염색된 천연 무늬목(1a, 1b)의 표면(도 4a)은 은 통일된 색조를 가지지만, 그 이면(도 4b)은 무늬가 표면과 동일하면서도 천연의 색조를 그대로 가지게 된다. 도 4a에서 부호 A는 염색된 층을 부호 B는 염색되지 않은 층을 각각 나타낸다.As shown in Figs. 4A and 4B, the surface (Fig. 4A) of the natural veneers 1a and 1b thus dyed has a uniform silver hue, while the back side (Fig. 4B) has the same pattern as the surface but is natural. It will have a hue of. In FIG. 4A, symbol A represents a dyed layer and symbol B represents an undyed layer, respectively.

따라서, 본 발명에 의하면, 매우 간단한 공정 및 저렴한 비용으로 동종 수종의 천연 무늬목이 갖는 색조의 차이를 통일시킬 수 있을 뿐만 아니라, 사용자가 색조가 통일된 염색 무늬목과 천연 색조의 무늬목을 선택적으로 사용할 수 있게 되는 것이다.Therefore, according to the present invention, it is possible to unify the differences in the hue of the natural veneers of the same species in a very simple process and at a low cost, and the user can selectively use the dyed veneer and the natural shades of uniform shades. Will be.

도 1a은 수종은 동일하나 색조가 다른 천연 무늬목을 분리하여 배치한 평면도이다.FIG. 1A is a plan view in which natural veneers having the same species but different hue are arranged separately.

도 1b는 도 1a에 도시된 천연 무늬목을 연결한 상태를 보여 주는 평면도이다.FIG. 1B is a plan view showing a state in which the natural veneer shown in FIG. 1A is connected.

도 2는 색조의 보정이 필요한 천연 무늬목과 염료 도포 필름을 차례로 열프레스의 베이스 상면에 적층하고, 열압착하는 방법으로 보여 주는 공정 사시도이다.FIG. 2 is a process perspective view illustrating a method of laminating a natural veneer and a dye coating film on the base upper surface of a heat press which are in need of color correction, and then thermocompressing.

도 3은 본 발명에 따른 천연 무늬목의 염색 방법을 보여 주는 공정도이다. 3 is a process chart showing a method of dyeing natural veneer according to the present invention.

도 4a는 염색된 면이 상면에 오도록 도시한 본 발명에 따른 염색 천연 무늬목의 사시도이다.Figure 4a is a perspective view of a dyed natural veneer according to the invention shown so that the dyed side is on the top.

도 4b는 염색되지 않은 면이 상면에 오도록 도시한 본 발명에 따른 염색 천연 무늬목Figure 4b is dyed natural veneer according to the present invention shown so that the undyed side is on the top

* 도면의 주요 부분에 대한 부호의 설명 *                  Explanation of symbols on the main parts of the drawings

1a, 1b : 천연 무늬목 3 : 열프레스 가동부1a, 1b: Natural veneer 3: Heat press moving part

5 : 열프레스 베이스 7 : 염료 도포 필름5: heat press base 7: dye coating film

Claims (2)

단일 색상을 갖도록 배합한 유성 염료를 유기 용제에 분산시켜 얇은 필름에 도포한 후, 탈색되지 않은 0.1mm 내지 0.5mm 두께의 천연 무늬목 상에 적층하고, 열프레스에 의하여 160 ~ 190℃ 온도, 5 ~ 30 Kg/㎠의 압력을 유지하면서, 염료의 침염(浸染) 두께가 천연무늬목 두께의 10% ~ 70%에 이르게 하여, 천연 무늬목의 전면과 후면의 색조가 다르게 한 것을 특징으로 하는 염색 천연 무늬목 제조 방법.The oil-based dye blended to have a single color is dispersed in an organic solvent and applied to a thin film, and then laminated on a natural veneer having a thickness of 0.1 mm to 0.5 mm, which is not discolored. While maintaining the pressure of 30 Kg / ㎠, the dyeing dyeing thickness of the dye reaches 10% to 70% of the thickness of the natural veneer, the dyeing natural veneer, characterized in that the color tone of the front and back of the natural veneer different Way. 제 1 항에 기재된 방법에 의하여 제조된 염색 천연 무늬목.Dyed natural veneer produced by the method of claim 1.
KR1020080015291A 2008-02-20 2008-02-20 Dyed veneer and method of manufacturing thereof KR100848044B1 (en)