KR100837850B1 - Soil ceramics and process for the preparation thereof - Google Patents
Soil ceramics and process for the preparation thereof Download PDFInfo
- Publication number
- KR100837850B1 KR100837850B1 KR20070057158A KR20070057158A KR100837850B1 KR 100837850 B1 KR100837850 B1 KR 100837850B1 KR 20070057158 A KR20070057158 A KR 20070057158A KR 20070057158 A KR20070057158 A KR 20070057158A KR 100837850 B1 KR100837850 B1 KR 100837850B1
- Authority
- KR
- South Korea
- Prior art keywords
- tile
- duck
- weight
- group
- soil
- Prior art date
Abstract
Description
도 1은 본 발명의 토양 타일에서 소지층과 표면처리층을 나타낸 예시도이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is an illustration showing an underlayer and a surface treatment layer in a soil tile of the present invention. FIG.
도 2는 본 발명에 따른 타일의 제조방법 중 건식 성형 방식의 공정도이다.Fig. 2 is a process diagram of the dry forming method among the tile manufacturing methods according to the present invention.
본 발명은 토양 타일 및 이의 제조방법에 관한 것으로서 보다 상세하게는 수산화칼슘(Ca(OH)2)과, 황토와, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분과, 실리카(SiO2)와, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분으로 이루어지고, 표면에 염료, 항균제를 포함하는 토양 타일 및 이의 제조방법에 관한 것이다.The present invention relates particularly to calcium hydroxide (Ca (OH) 2) and, and ocher and, quartz porphyry, illite, any one or more components selected from tourmaline, silica (SiO 2) than relates to a process for producing soil tile and thereof, Fly ash, diatomaceous earth, and volcanic ash, and a soil tile including a dye and an antimicrobial agent on the surface thereof, and a method for producing the same.
본 발명은 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분으로 인한 미세 다공에 의한 경량성 및 조습 효과, 맥반석 및 천연황토에 의한 원적외선 복사효과, 천연염료 도포를 통한 은은한 색상의 재현과 함께 인체에 유용한 효과와 표면의 항균제 코팅에 의한 항균, 항곰팡이 효과 등을 가진 토양 타일 및 이를 제조하는 방법에 관한 것이다. The present invention relates to a lightweight and humidity-proof effect due to micropores caused by at least one component selected from fly ash, diatomaceous earth, and volcanic ash, a far-infrared radiative effect caused by a quartz stone and natural loess, To a soil tile having useful effects and antimicrobial and antifungal effects by coating the surface with an antimicrobial agent, and a method for producing the same.
타일(tile)은 건축물의 바닥, 벽 등의 표면을 피복하기 위하여 만든 평판상(平板狀)의 점토질 소성제품으로, 설치되는 위치나 특성 등에 따라 내장(內裝)타일, 외장타일, 모자이크타일, 내산타일, 바닥타일, 염전타일, 쿼리타일 등이 있다. A tile is a flat plate-like clay-fired product made to cover the surface of the floor or wall of a building. Depending on the installed location and characteristics, the tile may be an internal tile, an exterior tile, a mosaic tile, Acid tiles, floor tiles, salt tiles, and query tiles.
타일은 여러 가지 성능을 가지고 있으며 비교적 시공도 간단할 뿐 아니라 시공후에 균열을 일으키거나 변색하는 일이 거의 없고 특히 내구성이 있으므로 구조물의 표면을 피복 보호하는데 가장 좋은 재료이다. 따라서 타일은 건축물에 있어서 위생적인 점이 요구되는 주방, 화장실, 목욕탕, 세면장 등에 주로 사용되고 있다. Tiles have various performances, they are relatively easy to install, they do not cause cracking or discoloration after construction, and they are the best material to protect the surface of the structure because of its durability. Therefore, tiles are mainly used in kitchens, toilets, bathrooms and restrooms where hygiene is required in buildings.
종래의 일반적인 실내 바닥 타일은 점토, 고령토, 장석, 도석등의 무기질 원료를 볼밀에서 미분쇄 및 분말 제조 후 가압 성형한 다음 성형품을 건조 및 시유하여 1,170℃ 정도에서 소성하여 제품을 만드는 것으로 표면이 유리질화 되어 있고, 소지도 소결되어 있어 천연 토양의 질감 및 기능이 없이 일반 장식용의 단순한 건축 내장재에 해당된다. Conventional indoor floor tiles are produced by milling inorganic raw materials such as clay, kaolinite, feldspar, and stones from a ball mill and then pressing and molding them, and then drying and sintering the products to form products by heating at about 1,170 ° C. It is nitrided and sintered so that it does not have the texture and function of natural soil and it is a simple building interior material for ordinary decoration.
한편, 본 발명과 관련된 선행기술로서 소석회, 점토, 황토, 규석, 실리카 등을 혼합 분쇄하여 성형한 후 수열합성반응을 통해 타일을 제조하는 방법이 있다. 상기에 기재된 방법은 구성 원료가 결정성질로 이루어져 반응성이 떨어짐으로 인한 강도 발현상의 문제점 및 진비중이 커 무거운 중량을 가지며, 점토에 함유된 유기물에 의해 타일 자체 색상의 변색이 발생될 수 있는 가능성이 크다. 또한, 제품의 표면에 오염물질 부착시 흡수를 통한 미관 훼손이 발생될 수 있는 단점이 있다.Meanwhile, as a prior art related to the present invention, there is a method of preparing a tile by mixing and pulverizing slaked lime, clay, loess, silica, silica and the like, followed by hydrothermal synthesis. The above-described method has a problem in that the constituent raw materials are made of crystalline materials and the reactivity thereof is poor. Thus, there is a possibility that the color of the tile itself may be discolored due to the organic matter contained in the clay Big. In addition, there is a disadvantage in that when a contaminant is adhered to the surface of a product, aesthetic damage may occur due to absorption.
본 발명은 비중이 낮은 원료의 구성 즉 구상입자를 사용하여 소재를 경량화 하고 또한 비정질상을 갖는 원료를 사용하여 수산화칼슘과의 반응성을 증대시켜 에트링가이트(Ettringite)상의 생성에 의한 강도 증진을 유도함과 동시에 유기물이 다량 함유되어 있는 점토를 사용하지 않음으로써 색상 변색을 방지하고 또한 항균제가 첨가시켜 세균서식 및 오염물질의 부착을 방지할 수 있고, 또한 원적외선 복사 및 온열, 조습효과, 항균, 항곰팡이 효과 및 천연염료 사용에 의한 은은한 색상 재현 등 인체에 유익하고 다기능의 환경 친화적인 토양 타일 및 이의 제조방법을 제공을 목적으로 한다.The present invention relates to a process for producing a material having a low specific gravity, that is, using spherical particles to lighten the material and increase the reactivity with calcium hydroxide by using a raw material having an amorphous phase to induce the strength enhancement by the formation of the ettringite phase It is possible to prevent the discoloration of the color by not using the clay containing a large amount of the organic matter and to prevent the attachment of the bacterial culture and the contaminants by adding the antibacterial agent and also to the effect of the far infrared radiation and the heat, The present invention provides an environmentally friendly soil tile which is beneficial to the human body and has versatility, such as a soft color reproduction by using natural dyes, and a manufacturing method thereof.
본 발명은 수산화칼슘과, 황토와, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분과, 실리카와, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분으로 이루어지고, 표면에 염료, 항균제를 포함하는 토양 타일을 나타낸다.The present invention relates to a process for the production of an aqueous solution containing at least one component selected from calcium hydroxide, at least one component selected from the group consisting of loess, elvan, ilite and tourmaline, silica, fly ash, diatomaceous earth and volcanic ash, Represents a soil tile.
본 발명에서 타일은 수산화칼슘 100중량부에 대하여 황토 10∼20중량부, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분 10∼20중량부, 실 리카 10∼20중량부, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분 40∼100중량부로 이루어지고, 상기 타일 표면의 염료, 항균제가 첨가된 표면 경화제는 상기 타일 1m2에 대해 각각 5∼125g, 타일 전면의 발수제는 상기 타일 1m2에 대해 20∼500g 도포되는 토양 타일을 나타낸다.In the present invention, the tile is composed of 10 to 20 parts by weight of loess, 10 to 20 parts by weight of at least one component selected from elvan, ilite and tourmaline, 10 to 20 parts by weight of silica, , And the surface hardener to which the dyestuff and the antimicrobial agent are added is 5 to 125 g per 1 m 2 of the tile and 20 to 20 g per 1 m 2 of the tile, ~ 500g represents soil tiles to be applied.
본 발명의 토양 타일 성분중에서 수산화칼슘(Ca(OH)2)은 고온, 고압 증기하에서 하기 반응식(1)과 같이 비정질 실리카와 수화반응으로 성형체 내부에 C-S-H계 침상 수화물을 생성하는 역할을 한다.Among the soil tile components of the present invention, calcium hydroxide (Ca (OH) 2 ) plays a role of generating CSH-based acylhydrate in the interior of the formed body by reaction with amorphous silica under high temperature and high pressure steam as shown in the following reaction formula (1).
Ca(OH)2 + SiO2 + H2O => C-S-H겔상 [C-S-H계 수화물]... 반응식(1)Ca (OH) 2 + SiO 2 + H 2 O => CSH gel phase [CSH-based hydrate]
상기 반응식(1)은 토양 타일 성형체 내부에서 일어나는 수화반응으로, 초기에는 수분에 용해된 Ca2 + 이온이 실리카 입자주위를 둘러싸서 C-S-H계 겔막을 형성하고, 이 C-S-H겔막이 침상의 수화물로 전환된다. 결국 고온, 고압 하에서 수화반응으로 인해 실리카 입자사이에 수화물 C-S-H계 겔상이나 침상을 형성함으로써 성형체의 강도를 발현하는 주요인이 되며, 이러한 수화물 생성은 분말의 입도, 원료의 비정질상, 수산화칼슘(Ca(OH)2)의 혼합상태 및 성형체의 치밀도 등의 요인에 따라 달라질 수 있다.The reaction formula (1) is a hydration reaction occurring inside the soil tile formed body. In the beginning, Ca 2 + ions dissolved in water surround the silica particles to form a CSH gel membrane, and this CSH gel membrane is converted into acicular hydrate . As a result, hydration reaction under high temperature and high pressure results in the formation of hydrated CSH-based gel phase or needle-like phase between the silica particles, which leads to the development of the strength of the formed body. Such hydrate formation is caused by the particle size, amorphous phase of the raw material, 2 ) and the compactness of the formed body.
본 발명의 토양 타일 성분의 하나로 사용할 수 있는 플라이애쉬는 주 화학성분이 SiO2, Al2O3 이며, 주결정상이 쿼츠(SiO2), 멀라이트(3Al2O3ㆍ2SiO2)로 이루어져 있다. 결정구조는 구형입자의 세노스피어(Cenosphere)와 그의 응집체 형태로 존재 하는데, 이는 속이 비어 있으며, 입경의 크기는 수㎛~수백㎛ 정도이다. 이러한 구상의 미립자는 소재를 미세 다공형태로 만들어주어 가볍고, 습기를 흡수하거나 방출하는 역할을 하게 된다. The fly ash which can be used as one of the soil tile components of the present invention is composed of SiO 2 and Al 2 O 3 as main chemical components and is composed of quartz (SiO 2 ) and mullite (3Al 2 O 3 .2SiO 2 ) . The crystal structure exists in the form of a spherical particle of Cenosphere and its aggregate, which is hollow and has a particle size of several μm to several hundreds of micrometers. These spherical fine particles make the material into a microporous form, so that they are light and absorb moisture or emit moisture.
본 발명의 토양 타일 성분의 하나로 사용할 수 있는 규조토는 순수한 것은 화학조성이 SiO2 96% 이상으로 되어 있고, 그 특성이 직경이 약 3∼10㎛ 크기의 매우 많은 기공을 가진 비정질상의 다공질(Porous)체로 존재하므로 조습기능, 탈취기능을 제공하게 된다.The diatomaceous earth which can be used as one of the soil tile components of the present invention is a pure diatomaceous earth having a chemical composition of 96% or more of SiO 2 and a characteristic of porous of amorphous phase having a very large number of pores having a diameter of about 3 to 10 μm. So it provides humidity control function and deodorization function.
본 발명의 토양 타일 성분의 하나로 사용할 수 있는 화산재는 주요 구성성분이 알로펜으로 상기 알로펜은 비정질상의 미세한 구형 입자를 갖는 규산 알루미늄광물로써, 포름알데히드,톨루엔 등의 독성물질을 저감시킬 뿐 아니라 공기정화,습도조절,악취제거 등의 효과가 있다.As the volcanic ash which can be used as one of the soil tile components of the present invention, allopen is a main constituent component. Allopen is an aluminum silicate mineral having fine spherical particles in an amorphous phase, and not only reduces toxic substances such as formaldehyde and toluene, Purification, humidity control, odor removal and so on.
본 발명의 토양 타일 성분 중에서 황토는 결정구조가 2:1 층상 구조를 가지는 3층 구조로서 테트라헤드랄 시트(Tetrahedral sheet : 4면체)와 옥타헤드랄 시트(Octahedral sheet : 8면체)가 반복적으로 겹쳐져 한개의 층을 구성하는 2:1형 구조이다. 이와 같은 구조적 특성의 황토는 사면체 내에 Si+4 이온 대신 Al+3 이온과 팔면체내에 Al+3, Fe+3 이온 대신 Mg+2, Fe+2 등의 동형 치환에 의하여 황토로부터 음전하가 발생할 경우 이 음전하를 중화시키기 위해 Na+, Ca+2 및 H+ 이온이 상기 사면체에 약하게 부착되어 있어 원적외선이 복사되는 효과가 있다.Among the soil tile components of the present invention, the loess is a three-layered structure having a 2: 1 layer structure of the crystal structure, and a tetrahedral sheet (tetrahedron) and an octahedral sheet (octahedron) are repeatedly overlapped It is a 2: 1 structure that constitutes one layer. In the same structural characteristics of yellow soil is, if a negative result from ocher by the isomorphic substitution, such as Al +3, Fe +3 ions instead of Mg +2, Fe +2 in the Si +4 ions instead of Al +3 ions in the tetrahedron and octahedron Na + , Ca +2 and H + ions are weakly attached to the tetrahedron in order to neutralize the negative charge, so that far-infrared rays are copied.
본 발명의 토양 타일 성분 중에서 실리카는 실리카 함유량이 60~70% 내외인 황토나 플라이애쉬 등에 미분의 실리카를 첨가함으로써 무기결합제인 수산화칼슘(Ca(OH)2) 과의 수화반응을 통해 더욱 치밀한 침상 수화물을 생성시켜 강도를 증가시킬 수 있다. 이때 본 발명의 토양 타일 성분으로서 실리카는 실리카 분말을 사용하는 것이 좋다.Among the soil tile components of the present invention, silica is prepared by adding hydrated silica such as yellow soil or fly ash having a silica content of about 60 to 70% to hydration reaction with an inorganic binder such as calcium hydroxide (Ca (OH) 2 ) Can be generated to increase the strength. At this time, silica powder is preferably used as the soil tile component of the present invention.
본 발명의 토양 타일 성분의 하나로 사용할 수 있는 맥반석은 원적외선이 복사되는 대표적인 세라믹 원료로 주성분은 Al2O3와 SiO2이고, 소량의 산화제2철이 함유되어 있다. 1㎤당 3∼15만 개의 구멍으로 이루어져 있어 흡착성이 강하고, 약 2만 5000천종의 무기염류를 함유하고 있다. 중금속과 이온을 교환하는 작용을 하여 인체에 유해한 유해금속 제거제로도 사용하며, 열을 가하면 열전자방사(이온화방사)에 의한 알파(α)선이 방출됨과 동시에 8㎛∼10㎛(마이크론)의 원적외선을 90%이상 방사하며, 탈취율이 우수하고, 축열기능 효과가 있다.The elvan, which can be used as one of the soil tile components of the present invention, is a typical ceramic raw material in which far-infrared rays are radiated. Its main components are Al 2 O 3 and SiO 2 , and contains a small amount of ferric oxide. It consists of 3 to 150 thousand holes per cm 3, and is strong in adsorption and contains about 25 thousand inorganic salts. It is also used as a harmful metal removing agent harmful to the human body by the action of exchanging ions with heavy metals. When heat is applied, alpha (alpha) radiation by thermoelectron emission (ionizing radiation) is released and at the same time, far- Of 90% or more, excellent deodorization rate, and has an effect of heat storage function.
상기의 토양 타일 구성성분으로서 맥반석은 맥반석 대신에 일라이트, 토르말린 중에서 선택된 어느 하나 이상을 사용할 수 있거나 또는 맥반석 이외에 일라이트, 토르말린 중에서 선택된 어느 하나 이상을 추가로 더 사용할 수 있다.As the soil tile component, at least one selected from the group consisting of ilite and tourmaline can be used instead of elvanite, or alternatively at least one selected from ilite and tourmaline can be used in addition to elvanite.
본 발명의 토양 타일은 수산화칼슘과, 황토와, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분과, 실리카와, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분으로 이루어지고, 그 표면에 염료, 항균제를 포함하도록 하여 염료 사용에 의한 은은한 색상 재현, 항균, 항곰팡이 효과 등의 인체에 유익하고 다기능의 환경 친화적인 토양 타일을 얻을 수 있다(도 1 참조).The soil tile of the present invention is composed of at least one component selected from calcium hydroxide, at least one component selected from yellow loam, elvan, ilite and tourmaline, silica, fly ash, diatomaceous earth and volcanic ash, It is possible to obtain a multifunctional environmentally friendly soil tile which is beneficial to the human body such as a soft color reproduction by using a dye, an antibacterial effect and an antifungal effect (see FIG. 1).
상기의 토양 타일의 표면에의 염료는 쪽풀, 계장초, 붓꽃, 갈매나무, 감귤, 붓꽃, 단풍나무, 개옷나무, 쑥, 괴화, 황백, 매자나무, 졸참나무, 꼭두서니, 홍화, 생강나무, 소방목, 산행목, 소목, 괴화, 오배자, 주목, 자작나무, 갈참나무, 소목, 동백, 포도, 감, 붓나무, 자초, 치자, 노목, 회화나무, 양파, 황벽, 황련, 정향나무, 자소, 울금, 오리나무, 개오동나무, 밤나무, 상수리나무, 소나무, 양매, 석류, 계수나무, 붉나무, 연자각, 진피, 석류나무, 단풍나무, 졸참나무, 단풍나무소, 방목 중에서 선택된 어느 하나 이상으로부터 추출한 천연염료를 포함할 수 있다.The dyestuffs on the surface of the soil tiles are selected from the group consisting of aphids, hedgehogs, irises, fir trees, citrus fruits, irises, maple trees, wormwood, Climbing trees, bamboo shoots, bamboo shoots, obsidian, attention, birch, goose, joan, camellia, grape, persimmon, brushwood, Natural dyes extracted from one or more selected from among at least one selected from the group consisting of a duck, a promontory, a chestnut, an oak, a pine, a pine, a pomegranate, a cassia, a rhododendron, a rhizome, a dermis, a pomegranate, a maple, . ≪ / RTI >
상기의 천연염료는 쪽풀, 계장초, 붓꽃, 갈매나무, 감귤, 붓꽃, 단풍나무, 개옷나무, 쑥, 괴화, 황백, 매자나무, 졸참나무, 꼭두서니, 홍화, 생강나무, 소방목, 산행목, 소목, 괴화, 오배자, 주목, 자작나무, 갈참나무, 소목, 동백, 포도, 감, 붓나무, 자초, 치자, 노목, 회화나무, 양파, 황벽, 황련, 정향나무, 자소, 울금, 오리나무, 개오동나무, 밤나무, 상수리나무, 소나무, 양매, 석류, 계수나무, 붉나무, 연자각, 진피, 석류나무, 단풍나무, 졸참나무, 단풍나무소, 방목 중에서 선택된 어느 하나 이상 염료 재료의 잎, 줄기, 뿌리, 수피 중에서 선택된 어느 하나 이상으로부터 추출한 것이나 또는 시중에서 상품으로 판매되고 있는 천연염료를 사용할 수 있다.The above-mentioned natural dyestuffs can be used in a variety of fields such as aphids, hedgehogs, iridescent trees, tangerines, irises, maple trees, dogwoods, wormwood, Onion, Echinopsis, Chrysanthemum, Cloves, Scallop, Scutellaria, Duckwood, Leafwood, Fruit tree, Fruit tree, Fruit tree Leaves, stem, roots, leaves of any one or more selected from chestnut, oak, pine, pine, pomegranate, cassia, rhododendron, kite, dermis, pomegranate, maple, Or natural dyes sold as commercial products on the market can be used.
상기의 토양 타일의 표면에 항균제는 은 또는 구리가 담지된 티탄졸 항균제, 나노실버 항균제 중에서 선택된 어느 하나 이상을 사용할 수 있다.The surface of the soil tile may be coated with at least one selected from the group consisting of a titanium-zirconium antimicrobial agent and a nano-silver antimicrobial agent on which silver or copper is supported.
상기 토양 타일의 표면에 존재하는 항균제는 항균제와 표면 경화제의 혼합물 을 토양 타일의 표면에 도포할 수 있다.The antimicrobial agent present on the surface of the soil tile may be applied to the surface of the soil tile with a mixture of the antimicrobial agent and the surface hardener.
상기에서 표면 경화제는 폴리우레탄, 비닐계 합성수지 중에서 선택된 어느 하나 이상을 사용할 수 있다.The surface hardener may be at least one selected from polyurethane and vinyl-based synthetic resin.
상기에서 항균제와 표면 경화제의 혼합물은 항균제 1∼10중량%, 표면 경화제 90∼99중량%으로 이루어진 것을 사용할 수 있다.In the above, the mixture of the antimicrobial agent and the surface hardening agent may be composed of 1 to 10% by weight of the antimicrobial agent and 90 to 99% by weight of the surface hardening agent.
상기에서 항균제와 표면경화제가 처리된 토양 타일의 전면에 발수제를 도포시킬 수 있다.The water repellent agent may be applied to the entire surface of the soil tile having been treated with the antimicrobial agent and the surface hardener.
상기에서 발수제는 불소 및 실리콘 발수제 중 선택된 어느 하나 이상을 사용할 수 있다.The water repellent agent may be selected from fluorine and silicone water repellent agents.
상기에서 염료와 항균제 및/또는 표면 경화제, 발수제를 스프레이(spray)로 분무하거나 또는 코팅기를 이용하여 토양 타일 표면에 염료와 항균제 및/또는 표면 경화제, 토양 타일 전면에 발수제를 도포할 수 있다.In the above, the dye, the antimicrobial agent and / or the surface hardener and the water repellent agent may be applied to the surface of the soil tile by spraying the dye with the antimicrobial agent and / or the surface hardener and the water repellent agent by spray or by using the coating machine.
본 발명의 토양 타일은 수산화칼슘과, 황토와, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분과, 실리카와, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분의 분말을 혼합시 광석입자를 추가로 더 첨가하여 혼합할 수 있다.The soil tile of the present invention is obtained by adding ore particles when mixing powders of at least one selected from calcium hydroxide, at least one component selected from yellow loam, elvan, ilite and tourmaline, silica, fly ash, diatomaceous earth and volcanic ash Can be added and mixed.
상기 광석입자는 도석, 장석, 납석, 활석, 맥반석 중에서 선택된 어느 하나 이상을 사용할 수 있다.The ore particles may be at least one selected from the group consisting of stones, feldspar, pyroxene, talc, and quartz.
상기 광석입자는 수산화칼슘 100중량부에 대하여 0.1∼5.0중량부 사용할 수 있다.The ore particles may be used in an amount of 0.1 to 5.0 parts by weight based on 100 parts by weight of calcium hydroxide.
본 발명은 토양 타일의 제조방법을 포함한다.The present invention includes a method for producing a soil tile.
본 발명의 토양 타일의 제조방법은 (1)수산화칼슘과, 황토와, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분과, 실리카와, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분의 분말을 혼합 및 압축하여 그린 타일로 성형하는 건식성형단계,The method for producing a soil tile according to the present invention comprises the steps of (1) preparing a powder of at least one component selected from calcium hydroxide, at least one component selected from yellow loam, elvan, ilite and tourmaline, silica, fly ash, diatomaceous earth, A dry-forming step of molding into a green tile by mixing and compressing,
(2)상기 건식성형된 그린 타일을 수열합성하는 양생단계,(2) a curing step of hydrothermally synthesizing the dry-formed green tile,
(3)상기 양생단계에서 수열합성된 타일의 표면에 천연염료와 항균제가 첨가된 표면 경화제 도포와 타일의 전면에 발수제를 도포하는 코팅 단계, 및 (3) a coating step of applying a surface hardener to the surface of the tile hydrothermally synthesized in the curing step to which a natural dye and an antimicrobial agent are added, and a water repellent agent on the entire surface of the tile, and
(4)상기 천연염료와 항균제가 첨가된 표면 경화제가 타일의 표면에 도포되고, 발수제가 전면에 도포된 타일을 건조하는 건조단계를 포함한다.(4) a drying step in which the surface hardener to which the natural dye and the antimicrobial agent are added is applied to the surface of the tile, and the tile coated with the water repellent agent is dried.
상기 (1)단계의 그린 타일로 성형하는 건식성형단계는 수산화칼슘 100중량부에 대하여 황토 10∼20중량부, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분 10∼20중량부, 실리카 10∼20중량부, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분 40∼100중량부로 이루어진 각각의 분말을 혼합하고, 성형압력 200∼400㎏/㎠, 바람직하게는 250∼350㎏/㎠에서 압축하여 그린 타일을 성형할 수 있다.The dry-forming step of forming the green tile in the step (1) comprises adding 10 to 20 parts by weight of loess, 10 to 20 parts by weight of at least one component selected from quartz, ilite and tourmaline, 10 to 20 parts by weight of silica, Each powder consisting of 40 to 100 parts by weight of at least one component selected from among alumina, silica, alumina, alumina, silica, alumina, The tile can be formed.
상기에서 그린 타일은 두께 10∼50㎜로 성형할 수 있다.The green tile may be formed to a thickness of 10 to 50 mm.
상기 (2)단계의 그린 타일을 수열합성하는 양생단계는 건식 성형된 그린 타 일은 수열합성하여 그린 타일의 성분 중에서 수산화칼슘(Ca(OH)2)이 비정질 실리카와 수화반응으로 성형체 내부에 C-S-H계 침상 수화물을 생성하도록 하여 실리카 입자사이에 수화물 C-S-H계 겔상이나 침상을 형성함으로써 성형체의 강도를 발현하도록 한다.In the curing step of hydrothermal synthesis of the green tile in the step (2), the dry-formed green tile is hydrothermally synthesized, and calcium hydroxide (Ca (OH) 2 ) among the components of the green tile is subjected to a hydration reaction with the amorphous silica, And hydrate CSH-based gel or needle-like particles are formed between the silica particles so as to exhibit the strength of the formed body.
상기에서 그린 타일의 수열합성은 60psi, 150℃, 8시간 이상 실시할 수 있다.In the above, the hydrothermal synthesis of the green tile can be carried out at 60 psi, 150 캜 for 8 hours or more.
상기에서 그린 타일의 수열합성은 60∼560psi, 150∼250℃, 8∼12시간 동안 실시할 수 있다. The hydrothermal synthesis of the green tile may be performed at 60 to 560 psi, 150 to 250 캜, and 8 to 12 hours.
상기 (3)단계는 수열합성된 타일의 표면에 염료와 항균제가 첨가된 표면 경화제 및 타일의 전면에 발수제를 도포하는 코팅 단계이다.The step (3) is a coating step of applying a water repellent agent to the entire surface of the tile and the surface hardener to which the dye and the antimicrobial agent are added on the surface of the hydrothermally synthesized tile.
상기에서 수열합성된 타일의 표면에 코팅하는 염료는 쪽풀, 계장초, 붓꽃, 갈매나무, 감귤, 붓꽃, 단풍나무, 개옷나무, 쑥, 괴화, 황백, 매자나무, 졸참나무, 꼭두서니, 홍화, 생강나무, 소방목, 산행목, 소목, 괴화, 오배자, 주목, 자작나무, 갈참나무, 소목, 동백, 포도, 감, 붓나무, 자초, 치자, 노목, 회화나무, 양파, 황벽, 황련, 정향나무, 자소, 울금, 오리나무, 개오동나무, 밤나무, 상수리나무, 소나무, 양매, 석류, 계수나무, 붉나무, 연자각, 진피, 석류나무, 단풍나무, 졸참나무, 단풍나무소, 방목 중에서 선택된 어느 하나 이상으로부터 추출한 천연염료를 사용할 수 있다.The dyes to be coated on the surface of the hydrothermally synthesized tiles may be at least one selected from the group consisting of aphids, hedgehogs, irises, cinnabar, citrus, iris, maple, dogwood, wormwood, spruce, , Firewood, hiking trail, joist, chrysanthemum, chimpanzee, attention, birch, goose, joan, camellia, grape, persimmon, brushwood, gardenia, From at least one selected from the group consisting of Eucalyptus, Oriental, Oriental, Chestnut, Quercus, Pine, Pine, Pomegranate, Cassia, Rhus vernicifolia, Ricinus, Dipper, Pomegranate, Maple, Quercus, Maple The extracted natural dyes can be used.
상기의 천연염료는 쪽풀, 계장초, 붓꽃, 갈매나무, 감귤, 붓꽃, 단풍나무, 개옷나무, 쑥, 괴화, 황백, 매자나무, 졸참나무, 꼭두서니, 홍화, 생강나무, 소방목, 산행목, 소목, 괴화, 오배자, 주목, 자작나무, 갈참나무, 소목, 동백, 포도, 감, 붓나무, 자초, 치자, 노목, 회화나무, 양파, 황벽, 황련, 정향나무, 자소, 울금, 오리나무, 개오동나무, 밤나무, 상수리나무, 소나무, 양매, 석류, 계수나무, 붉나무, 연자각, 진피, 석류나무, 단풍나무, 졸참나무, 단풍나무소, 방목 중에서 선택된 어느 하나 이상 염료 재료의 잎, 줄기, 뿌리, 수피 중에서 선택된 어느 하나 이상으로부터 추출한 것이나 또는 시중에서 상품으로 판매되고 있는 천연염료를 사용할 수 있다.The above-mentioned natural dyestuffs can be used in a variety of fields such as aphids, hedgehogs, iridescent trees, tangerines, irises, maple trees, dogwoods, wormwood, Onion, Echinopsis, Chrysanthemum, Cloves, Scallop, Scutellaria, Duckwood, Leafwood, Fruit tree, Fruit tree, Fruit tree Leaves, stem, roots, leaves of any one or more selected from chestnut, oak, pine, pine, pomegranate, cassia, rhododendron, kite, dermis, pomegranate, maple, Or natural dyes sold as commercial products on the market can be used.
상기에서 수열합성된 타일의 표면에 코팅하는 염료는 타일 표면 1m2에 대해 5∼125g 도포할 수 있다.The dye to be coated on the surface of the hydrothermally synthesized tile may be applied in an amount of 5 to 125 g per 1 m 2 of the surface of the tile.
상기에서 수열합성된 타일의 표면에 코팅하는 염료는 수용액 형태로 타일 표면에 도포할 수 있다.The dye to be coated on the surface of the hydrothermally synthesized tile may be applied to the surface of the tile in the form of an aqueous solution.
상기에서 염료 수용액은 정제수 100중량부에 대하여 상기 염료 10∼50중량부를 첨가하여 얻은 염료 수용액을 사용할 수 있다.The dye aqueous solution may be an aqueous dye solution obtained by adding 10 to 50 parts by weight of the dye to 100 parts by weight of purified water.
상기에서 수열합성된 타일의 표면에 코팅하는 항균제는 은 또는 구리가 담지된 티탄졸 항균제, 나노실버 항균제 중에서 선택된 어느 하나 이상을 사용할 수 있다.The antimicrobial agent coated on the surface of the hydrothermally synthesized tile may be at least one selected from silver antioxidants, copper-supported titanium antimicrobial agents and nano silver antimicrobial agents.
상기에서 수열합성된 타일의 표면에 항균제 코팅시 항균제와 표면 경화제의 혼합물을 토양 타일의 표면에 도포할 수 있다.A mixture of the antimicrobial agent and the surface hardener may be applied to the surface of the soil tile when the antimicrobial agent is coated on the surface of the hydrothermally synthesized tile.
상기에서 표면 경화제는 폴리우레탄, 비닐계 합성수지 중에서 선택된 어느 하나 이상을 사용할 수 있다.The surface hardener may be at least one selected from polyurethane and vinyl-based synthetic resin.
상기에서 항균제와 표면 경화제의 혼합물은 항균제 1∼10중량%, 표면 경화제 90∼99중량%으로 이루어진 것을 사용할 수 있다.In the above, the mixture of the antimicrobial agent and the surface hardening agent may be composed of 1 to 10% by weight of the antimicrobial agent and 90 to 99% by weight of the surface hardening agent.
상기에서 수열합성된 타일의 표면에 코팅하는 항균제와 표면 경화제의 혼합물은 타일 표면 1m2에 대해 5∼125g 도포할 수 있다.The mixture of the antimicrobial agent and the surface hardening agent coated on the surface of the hydrothermally synthesized tile may be applied to 5 to 125 g per 1 m 2 of the tile surface.
상기에서 수열합성된 타일의 표면에 코팅하는 항균제와 표면 경화제의 혼합물은 수용액 형태로 타일 표면에 도포할 수 있다.The mixture of the antimicrobial agent and the surface hardening agent coated on the surface of the hydrothermally synthesized tile may be applied to the surface of the tile in the form of an aqueous solution.
상기에서 항균제와 표면 경화제의 혼합물 수용액은 정제수 100중량부에 대하여 상기 항균제와 표면 경화제의 혼합물 10∼50중량부를 첨가하여 얻은 항균제와 표면 경화제의 혼합물 수용액을 사용할 수 있다.The aqueous solution of the mixture of the antimicrobial agent and the surface hardening agent may be an aqueous solution of the mixture of the antimicrobial agent and the surface hardening agent obtained by adding 10 to 50 parts by weight of a mixture of the antimicrobial agent and the surface hardening agent to 100 parts by weight of purified water.
상기에서 항균제와 표면경화제가 도포된 토양 타일의 전면에 발수제를 도포할 수 있다.The water repellent agent may be applied to the entire surface of the soil tile to which the antimicrobial agent and the surface hardener are applied.
상기에서 발수제는 불소 및 실리콘 발수제 중에서 선택된 어느 하나 이상을 사용할 수 있다.The water repellent agent may be selected from fluorine and silicone water repellent agents.
상기에서 수열 합성된 타일의 전면에 코팅하는 발수제는 타일 표면 1m2에 대해 20∼500g 도포할 수 있다.The water repellent agent coated on the entire surface of the hydrothermally synthesized tile may be applied in an amount of 20 to 500 g per 1 m 2 of the surface of the tile.
상기에서 수열 합성된 타일의 전면에 코팅하는 발수제는 수용액 형태로 도포할 수 있다.The water repellent agent coated on the entire surface of the hydrothermally synthesized tile may be applied in the form of an aqueous solution.
상기에서 발수제 수용액은 정제수 100중량부에 대하여 상기 발수제를 10∼20중량부를 첨가하여 얻은 발수제 수용액을 사용할 수 있다. The aqueous solution of the water repellent agent may be an aqueous solution of the water repellent agent obtained by adding 10 to 20 parts by weight of the water repellent agent to 100 parts by weight of purified water.
상기에서 염료와 항균제 및/또는 표면 경화제, 발수제를 스프레이(spray)로 분무하거나 또는 코팅기를 이용하여 토양 타일 표면에 염료와 항균제 및/또는 표면 경화제, 토양 타일 전면에 발수제를 도포할 수 있다.In the above, the dye, the antimicrobial agent and / or the surface hardener and the water repellent agent may be applied to the surface of the soil tile by spraying the dye with the antimicrobial agent and / or the surface hardener and the water repellent agent by spray or by using the coating machine.
상기 (4)단계는 염료와 항균제가 첨가된 표면 경화제가 표면에 도포되고, 발수제가 전면에 도포된 타일을 건조하는 건조단계이다.The step (4) is a drying step in which a surface hardener to which a dye and an antimicrobial agent are added is applied to a surface, and a tile coated with a water repellent agent is dried.
이때 타일의 건조는 60℃ 이상의 온도에서 5분 이상 실시할 수 있다.At this time, the tile can be dried at a temperature of 60 ° C or more for 5 minutes or more.
이때 타일의 건조는 60∼120℃에서 5∼30분 동안 실시할 수 있다.At this time, the tile can be dried at 60 to 120 ° C for 5 to 30 minutes.
본 발명의 토양 타일 제조에 있어서, 수산화칼슘과, 황토와, 맥반석, 일라이트, 토르말린 중에서 선택된 어느 하나 이상의 성분과, 실리카와, 플라이애쉬, 규조토, 화산재 중에서 선택된 어느 하나 이상의 성분의 분말을 혼합시 광석입자를 추가로 더 첨가하여 혼합할 수 있다.In the production of the soil tile of the present invention, when powder of at least one component selected from calcium hydroxide, at least one component selected from yellow loam, elvan, ilite and tourmaline, silica, fly ash, diatomite, Further particles can be added and mixed.
상기 광석입자는 도석, 장석, 납석, 활석, 맥반석 중에서 선택된 어느 하나 이상을 사용할 수 있다.The ore particles may be at least one selected from the group consisting of stones, feldspar, pyroxene, talc, and quartz.
상기 광석입자는 수산화칼슘 100중량부에 대하여 0.1∼5.0중량부 사용할 수 있다.The ore particles may be used in an amount of 0.1 to 5.0 parts by weight based on 100 parts by weight of calcium hydroxide.
한편 본 발명의 토양 타일에 있어서, 다양한 성분, 함량으로 토양 타일을 제 조한바, 상기에서 언급한 조건에 의해 토양 타일 제조시 본 발명의 목적에 부합하는 토양 타일을 얻을 수 있다.Meanwhile, the soil tiles of the present invention can be obtained by preparing the soil tiles in various compositions and contents, and the soil tiles meeting the object of the present invention can be obtained in the production of the soil tiles by the above-mentioned conditions.
이하 본 발명의 내용을 실시예 및 시험예를 통하여 구체적으로 설명한다. 그러나, 이들은 본 발명을 보다 상세하게 설명하기 위한 것으로 본 발명의 권리범위가 이들에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described in detail with reference to Examples and Test Examples. However, these are for the purpose of illustrating the present invention in more detail, and the scope of the present invention is not limited thereto.
<실시예><Examples>
도 2와 같은 공정을 이용하여 토양 타일을 제조하였다.Soil tiles were prepared using the process shown in FIG.
제토공정으로 수산화칼슘(Ca(OH)2) 100중량부에 대하여 플라이애쉬 100중량부, 천연황토 25중량부, 맥반석 12.5중량부, 실리카(SiO2) 12.5중량부를 평량 후, 습식 미분쇄를 위해 물과 함께 볼밀에 넣고 3시간 분쇄시켜 비중 1.6, 잔사율 3.12%(230mesh기준)로 슬립을 제조하였다. 이 슬립을 분무 건조기에서 파우더 함수분 10%, 파우더 대립입도(0.5㎜ 이상) 14.3%, 미립입도(0.08㎜ 이하) 2.7%로 하는 과립 파우더를 제조하였다.Moldboard process with calcium hydroxide (Ca (OH) 2) 100 parts by weight of fly ash 100 parts by weight of natural loess 25 parts by weight, relative to, quartz porphyry and 12.5 parts by weight of silica (SiO 2) 12.5 parts by weight After the parts of the basis weight, the water for the wet-milling And ground for 3 hours to prepare a slip having a specific gravity of 1.6 and a residual ratio of 3.12% (based on 230 mesh). The slip was prepared in a spray dryer to have a powder powder content of 10%, a powder opacity particle size (more than 0.5 mm) of 14.3%, and a fine particle size (less than 0.08 mm) of 2.7%.
상기에서 제조된 과립 파우더를 혼합(mixing)한 다음 100mmㅧ 100mmㅧ 20mm 규격의 몰드에 넣은 후 유압 프레스로 실성형압 300kg/㎠으로 건식 가압 성형하였다. The granulated powder prepared above was mixed and then put into a mold having a size of 100 mm ㅧ 100 mm ㅧ 20 mm, followed by dry pressing with a hydraulic press at a real molding pressure of 300 kg / cm 2.
상기에서 건식 가압 성형된 성형품을 밀폐압력용기(Auto Clave)에서 밀폐 압 력 10기압, 내부온도 180℃에서 10시간 유지, 수열 합성의 양생 공정으로 토양 타일 소지를 제조하였다.The dry press-molded product was held in a sealed pressure vessel (Auto Clave) at a sealing pressure of 10 atm and an internal temperature of 180 ° C for 10 hours, and a soil tile base was produced by a curing process of hydrothermal synthesis.
상기의 수열 합성된 토양 타일 소지의 표면과 전면에 염료와 항균제가 첨가된 표면 경화제 및 발수제를 도포하였다. 이때 1차 코팅과정으로 천연염료 수용액을 상기 토양 타일 소지 표면에 토양 타일 1m2당 125g 도포하고, 이후 2차 코팅과정에서 표면 경화제 97중량% 및 나노실버 항균제 3중량%으로 이루어진 혼합액을 토양 타일 소지 표면에 토양 타일 1m2당 125g 도포하였으며, 이후 3차 코팅과정에서 발수제 수용액을 토양 타일 소지 전면에 1m2당 500g 도포하였다.A surface hardener and a water repellent agent to which a dye and an antimicrobial agent were added were applied to the surface and the entire surface of the hydrothermally synthesized soil tile substrate. At this time, 125 g of the natural dye aqueous solution was applied to the surface of the soil tile at a rate of 1 m 2 per 1 m 2 of the soil tile, and then, in the secondary coating process, the mixed solution of 97 wt% of the surface hardening agent and 3 wt% 125g per 1 m 2 of soil tile was applied to the surface, and then 500g per 1 m 2 of the water repellent solution was applied on the entire surface of the soil tile in the third coating process.
상기에서 토양 타일 소지의 표면에 염료와 항균제가 첨가된 표면 경화제 및 발수제를 도포 후 80℃에서 10분간 건조하여 토양 타일 완제품을 제조하였다.In the above, the surface hardener and the water repellent agent having the dye and the antimicrobial agent added to the surface of the soil tile substrate were coated and dried at 80 ° C for 10 minutes to prepare a soil tile finished product.
상기에서 천연염료는 오배자를 사용하였고, 천연염료 수용액은 정제수 100중량부에 대하여 상기 천연염료 30중량부를 첨가하여 얻은 천연염료 수용액을 사용하였다.In the above, natural dyes were used as the natural dyes, and a natural dye aqueous solution obtained by adding 30 parts by weight of the natural dyes to 100 parts by weight of purified water was used.
상기에서 표면 경화제는 폴리우레탄을 사용하였고, 표면 경화제 및 나노실버 항균제 혼합액은 정제수 100중량부에 대하여 표면 경화제 및 나노실버 항균제 혼합물 50중량부를 첨가하여 얻은 것을 사용하였다.Polyurethane was used as the surface hardening agent, and a mixture of the surface hardening agent and the nano silver antibacterial agent mixture was prepared by adding 50 parts by weight of a surface hardener and a nano silver antibacterial agent mixture to 100 parts by weight of purified water.
상기에서 발수제는 실리콘 발수제를 사용하였고, 발수제 수용액은 정제수 100중량부에 대하여 실리콘 발수제 15중량부를 첨가하여 얻은 것을 사용하였다.A silicone water repellent agent was used as the water repellent agent and an aqueous solution of the water repellent agent was obtained by adding 15 parts by weight of silicone water repellent agent to 100 parts by weight of purified water.
<시험예 1>≪ Test Example 1 >
상기 실시예에서 제조한 토양 타일의 화학조성을 XRF 성분분석 기기를 이용하여 분석하였으며, 그 분석한 결과는 하기 표 1-1, 표 1-2에 나타내었다.The chemical composition of the soil tile prepared in the above examples was analyzed using an XRF component analyzer. The results of the analysis are shown in Tables 1-1 and 1-2 below.
표 1-1. 토양 타일 조성물 및 각 원료의 화학 분석Table 1-1. Soil tile composition and chemical analysis of each raw material
표 1-2. 토양 타일 조성물 및 각 원료의 화학 분석Table 1-2. Soil tile composition and chemical analysis of each raw material
<시험예 2>≪ Test Example 2 &
상기 실시예에서 제조한 토양 타일에 대해 꺾임 강도, 경도, 겉보기 비중, 수축율, 흡수율 등의 물성을 측정하고 그 결과를 아래의 표 2에 나타내었다.The soil tiles prepared in the above examples were measured for physical properties such as bending strength, hardness, apparent specific gravity, shrinkage and water absorption, and the results are shown in Table 2 below.
표 2.토양 타일의 일반적인 물성Table 2. Typical properties of soil tiles
<시험예 3>≪ Test Example 3 >
상기 실시예에서 제조한 토양 타일의 원적외선 복사율, 항균, 항곰팡이, 흡방습기능 시험을 행하였으며, 그 결과는 하기 표 3 내지 표 6과 같다. The far-infrared emissivity, antibacterial, antifungal and moisture absorptive and desorptive functions of the soil tiles prepared in the above examples were tested. The results are shown in Tables 3 to 6 below.
표 3. 토양 타일의 원적외선 복사율 및 복사에너지Table 3. Far-infrared emissivity and radiant energy of soil tiles
표 3은 FT-IR Spectrometer를 이용하여 40℃에서 Black Body 대비로 측정한 결과이다. 본 발명에 따라 제조되어진 세라믹 경화체는 92.6%의 높은 평균 방사율과 3.74X10-2W/m2의 다량의 원적외선 방사에너지를 가짐을 확인 할 수 있다.Table 3 shows the results of measurement with respect to the black body at 40 ° C using an FT-IR spectrometer. It can be confirmed that the ceramic cured body produced according to the present invention has a high average emissivity of 92.6% and a large amount of far-infrared radiation energy of 3.74 × 10 -2 W / m 2 .
표 4. 토양 타일의 항균시험 결과Table 4. Antimicrobial test results of soil tiles
주)CFU = Colony Forming UnitNote) CFU = Colony Forming Unit
표 4는 대장균(Escherichia coli ATCC 25922)과 녹농균(Staphylococcus aureus ACTT 6538)에 대하여 세균 감소율을 시험한 결과로 대장균의 경우 24시간 경과 후 균수가 감소하여 99.8%의 세균 감소율을 보였으며, 녹농균 또한 24시간 후 균수가 감소하여 99.8%의 세균 감소율을 보였다.Table 4 shows that Escherichia coli ATCC 25922) and Staphylococcus aureus (ACTT 6538). As a result, the bacterial count was reduced by 99.8% after 24 hours in Escherichia coli, and the bacterial count was decreased by 99.8% % Of bacteria.
표 5. 토양 타일의 항곰팡이시험 결과Table 5. Antifungal test results of soil tiles
표 5는 ASTM G-21-2002 시험 방법에 의해 얻어진 항곰팡이 시험 결과로서 0등급을 나타내었다.Table 5 shows the results of the anti-fungal test obtained by the ASTM G-21-2002 test method, showing 0 grade.
표 6. 토양 타일의 흡방습량 시험결과 Table 6. Absorption and desorption amount test results of soil tiles
표 6은 흡습, 방습량 시험결과로서 토양타일을 온도 25℃, 50% RH의 항온항습조 안에 24시간 방치한 다음, 온도 25℃, 90% RH의 항온항습조 안에 넣고 24시간 후 흡습량(g)을 측정하고, 다시 이 시험품을 온도 25℃, 50% RH의 항온항습조 안에 넣고 24시간 후 방습량(g)을 측정한 결과 147.5gr/m2의 높은 흡,방습량을 나타내었다. Table 6 shows the results of the moisture absorption and moisture absorption test. The soil tiles were left in a constant-temperature and constant-humidity bath at 25 ° C and 50% RH for 24 hours and then placed in a constant-temperature and humidity bath at 25 ° C and 90% g) was measured, and the sample was placed in a constant-temperature and constant-humidity chamber at 25 ° C and 50% RH. After 24 hours, the moisture-proof amount (g) was measured. As a result, a high absorption and desorption amount of 147.5 gr / m 2 was exhibited.
상술한 바와 같이, 본 발명의 바람직한 실시예를 참조하여 설명하였지만 해당 기술 분야의 숙련된 당업자라면 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. It will be understood that the present invention can be changed.
본 발명의 토양 타일은 소재를 불에 굽지 않고 수열 합성에 의해 경화시킨 제품으로 흙을 밟는 감촉과 부드럽고 따뜻한 느낌의 질감을 유지시켜 줄 수 있다.The soil tile of the present invention is a product obtained by hardening the material by hydrothermal synthesis without burning it, and it can keep the feeling of stepping on the soil and the texture of soft and warm feeling.
본 발명의 토양 타일은 미세한 다공조직으로 이루어진 소재를 사용하여 뛰어난 조습기능을 가지므로 실내의 습도를 적정한 상태로 항시 유지시킴으로써 실내공간을 쾌적하고 신선하게 유지시켜 줄 수 있다. Since the soil tile of the present invention has excellent humidity control function by using a material made of a fine porous structure, the humidity of the room is maintained at an appropriate state at all times, thereby keeping the indoor space pleasant and fresh.
본 발명의 토양 타일은 타일의 표면을 항균제로 처리하여 실내에서 서식하기 쉬운 세균, 곰팡이, 진드기, 벌레 등의 생성을 억제하며, 세균에 대한 멸균효과가 있어 위생적인 공간을 유지 할 수 있다.The soil tile of the present invention treats the surface of a tile with an antimicrobial agent to inhibit the generation of bacteria, fungi, mites, insects and the like which are easily inhabited in the room, and has a sterilizing effect against bacteria, thereby maintaining a sanitary space.
본 발명은 원적외선 복사량이 우수하여 온열효과를 통해 실내 생활을 하는데 있어 인체의 혈액순환 신진대사를 촉진시켜 피로 회복은 물론, 몸의 상태를 쾌적하게 유지시켜 줄 수 있다.The present invention has an excellent far infrared ray radiation amount and can promote the blood circulation metabolism of the human body in the indoor life through the effect of the heat, so that the body condition can be maintained comfortably as well as the fatigue.
또한 본 발명의 토양 타일은 천연원료인 황토, 맥반석, 규조토, 화산재와 재활용 원료인 플라이애쉬를 사용하여 환경친화적인 제품이다.The soil tile of the present invention is an environmentally friendly product using natural raw materials such as loess, elvan, diatomaceous earth, volcanic ash and fly ash as recycled raw material.
Claims (10)