KR100729493B1 - Headtie or damask cloth and manufacturing method of thats - Google Patents

Headtie or damask cloth and manufacturing method of thats Download PDF

Info

Publication number
KR100729493B1
KR100729493B1 KR1020060112942A KR20060112942A KR100729493B1 KR 100729493 B1 KR100729493 B1 KR 100729493B1 KR 1020060112942 A KR1020060112942 A KR 1020060112942A KR 20060112942 A KR20060112942 A KR 20060112942A KR 100729493 B1 KR100729493 B1 KR 100729493B1
Authority
KR
South Korea
Prior art keywords
yarn
weft
warp
fabric
damask
Prior art date
Application number
KR1020060112942A
Other languages
Korean (ko)
Inventor
동영상
Original Assignee
동영상
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 동영상 filed Critical 동영상
Priority to KR1020060112942A priority Critical patent/KR100729493B1/en
Application granted granted Critical
Publication of KR100729493B1 publication Critical patent/KR100729493B1/en

Abstract

The headtie or damask cloth and a manufacturing method thereof are provided to express clearly the pattern of a metallic yarn on the headtie or damask cloth and to reduce the waste of resources. A weft(100) comprises a weft a(110) and a weft b(120) formed by a chemical fiber. A warp a(210) comprising a gold yarn(211) and a silver yarn(212) is crossly weaved on an upper beam and a warp b(220) comprising a chemical fiber is weaved on a lower beam so that a warp(200) is formed by the double beam. The warp a is crossly weaved between the wefts a and the warp b is crossly weaved between the wefts b. The warp a is exposed on the outside surface of the cloth and forms a pattern so that the headtie or damask cloth is manufactured.

Description

헤드타이 또는 다마스크원단 및 그 제조방법{headtie or damask cloth and manufacturing method of thats}Headtie or damask cloth and manufacturing method of thats

도 1은 본 발명 헤드타이 또는 다마스크원단의 실시사진.1 is a photograph of an embodiment of the present invention the head tie or damask fabric.

도 2는 본 발명 헤드타이 또는 다마스크원단의 구성을 나타낸 단면도,Figure 2 is a cross-sectional view showing the configuration of the head tie or damask fabric of the present invention,

도 3은 이중빔을 도시한 개략도,3 is a schematic diagram illustrating a double beam;

도 4는 이중빔의 실시사진.4 is an implementation photograph of a double beam;

<도면의 주요 부분에 대한 부호의 설명><Explanation of symbols for the main parts of the drawings>

10 : 헤드타이 또는 다마스크원단 20 : 교차점10: head tie or damask fabric 20: intersection

30 : 이중빔 31 : 상빔30: double beam 31: upper beam

32 : 하빔 100 : 위사 32: Harbim 100: Weft

110 : 위사a 120 : 위사b 110: weft a 120: weft b

200 : 경사 210 : 경사a 200: slope 210: slope a

211 : 금사 212 : 은사 211: gold yarn 212: silver

220 : 경사b220: slope b

본 발명은 헤드타이 또는 다마스크원단 및 그 제조방법에 관한 것으로, 화섬사와 화섬사, 은사와 금사를 위사 사이로 교차하도록 제직하되, 상빔에 금속사 또는화섬사를 정경하고, 하빔에 금속사 또는 화섬사를 정경한 이중빔을 이용하여 제직하고, 상기 두 가지의 직물을 교호하여 무늬가 형성토록 한 헤드타이 또는 다마스크원단 및 그 제조방법에 관한 것이다.The present invention relates to a head tie or a damask fabric and a method of manufacturing the same, but weaving so as to cross the weaving yarn and chemical fiber yarns, silver and gold yarns between the weft yarn, and to respect the metal yarn or flower thread yarn in the upper beam, the metal yarn or flower thread yarn in the bottom beam The present invention relates to a head tie or a damask fabric which is woven by using a double beam, and wherein the two fabrics are alternately formed so that a pattern is formed.

다마스크는 옷감과 무늬가 안팎으로 반대인 조직의 원단을 말하고, 바탕은 수자직이며, 무늬를 바탕과 안팎이 반대되는 같은 색의 수자조직으로 나타낸 것을 포함하여 이것과 유사한 직물을 의미하고, 조직은 보통 5매주자 조직인데, 때로는 8매 또는 10매주자 조직인 경우도 있으며, 조직적인 면에서 볼 때 린스의 조직과 같으나, 린스는 생견직물인 데 대하여 다마스크는 연견직물인 점이 다르다.Damask refers to fabrics of tissues that are opposite in and out of cloth and pattern, and the base is vertical, and means fabrics similar to this, including those represented by the same colored number of tissues opposite to the inside and the outside. It is usually a 5 weekly organization, sometimes an 8 or 10 weekly organization, and in terms of organization, it is the same as the condition of rinse, but the rinse is a raw fabric.

헤드타이는 스카프나 천으로 머리를 감싸 목 뒤에서 묶어 고정시키거나, 머리에 맞게 모자 모양으로 만든 원단을 의미하고, 아프리카 여성 또는 남성들이 중요한 행사시에 그 행사를 빛내고 아름답게 보이기 위하여 머리에 감아 사용하여 온 전통의상용 소품이다.A head tie is a fabric made of a scarf or cloth wrapped around the head and tied to the back of the neck, or made into a hat shaped to fit the head, and used by African women or men to wrap the head to shine and beautify the occasion when it is important. This is a traditional costume accessory.

기존의 다마스크나 헤드타이는 천연사, 합성사와 같은 화섬사로 이루어진 경사와 금사, 은사와 같은 금속사로 이루어진 위사로 구성되고, 상기 경사 사이를 위사가 교차하여 금색 도는 은색의 금속사를 이용하여 무늬를 형성하여 제직되는 것이 일반적이었다.Conventional damask or head ties consist of warp yarns made of natural yarns, synthetic yarns such as synthetic yarns, and weft yarns made of metal yarns such as gold yarns and silver yarns. It was common to form and weave.

그러나 상기와 같은 통상의 다마스크나 헤드타이는 원단의 구성이 매우 얇아 무늬가 선명하게 나타나지 아니하고, 고급스럽지 못하며, 선염이 불가능하여 제직 후 염색을 시행하여야 했고, 또한, 원단의 평활도가 매우 낮아 외관상 미려하지 못할 뿐더러 터치감이 좋지 못하였으며, 제직 후 테투리부위에 메탈릭사가 잉여되어 잘라내야 하는 번거로움과 자원의 낭비가 발생하게 되는 문제점이 있었다. However, the normal damask or head ties as described above have a very thin fabric, so that the pattern does not appear vividly, does not appear classy, and the dyeing is impossible, so we have to perform dyeing after weaving. In addition, the smoothness of the fabric is very low in appearance. Not only did not have a good touch, there was a problem that the hassle and waste of resources to be cut off due to excess excess of metallic yarn on the rim part after weaving.

따라서, 원단에 메탈릭사의 무늬가 선명하게 나타나고, 고급스러우며, 선염이 가능하여 제직 후 염색을 시행하지 않도록 하며, 또한, 원단의 평활도가 높아 외관상 미려할 뿐만 아니라 터치감이 좋으며, 제직 후 테투리부위에 메탈릭사가 잉여되지 않아 잘라내야 하는 번거로움과 자원의 낭비가 발생하지 않는 다마스크나 헤드타이원단의 제공이 시급히 요구되고 있다.Therefore, the pattern of metallic yarn appears clearly on the fabric, and it is luxurious and ombre-dyed, so that it is not dyed after weaving. In addition, the smoothness of the fabric is not only beautiful in appearance but also good in touch, and it is applied to the rim part after weaving. There is an urgent need for the provision of damask or head-tie fabrication that does not cause any waste of resources and waste of resources due to the excess of metallic yarn.

본 발명의 목적은 원단에 메탈릭사의 무늬가 선명하게 나타나고, 고급스러우며, 선염이 가능하여 제직 후 염색을 시행하지 않도록 하며, 또한, 원단의 평활도가 높아 외관상 미려할 뿐만 아니라 터치감이 좋으며, 제직 후 테투리부위에 메탈릭사가 잉여되지 않아 잘라내야 하는 번거로움과 자원의 낭비가 발생하지 않는 헤드타이 또는 다마스크원단 및 그 제조방법을 제공하는 데 있다. The object of the present invention is that the pattern of metallic yarn appears clearly on the fabric, luxurious, and ombre-dyed, so as not to perform dyeing after weaving, and also the smoothness of the fabric is not only beautiful in appearance but also good in touch, after weaving It is to provide a head tie or damask fabric and a method of manufacturing the same, which does not cause any waste of resources and waste of cutting due to the excess of metallic yarn in the rim part.

상기의 목적을 달성하기 위한 본 발명은 헤드타이 또는 다마스크원단을 제직함에 있어서, 화섬사로 형성된 위사a와, 화섬사로 형성된 위사b로 구비되는 위사, 금사와 은사로 구비되는 경사a를 상빔에 교차로 정경하고, 화섬사로 구비되는 경사b를 하빔에 정경한 이중빔을 사용하여 구비되는 경사;로 구성되고, 상기 경사a는 위사a 사이로 교차하고, 경사b는 위사b 사이로 교차하여 제직되고, 무늬 형성시 경사b는 표면에 노출되도록 제직되어 이루어지는 헤드타이 또는 다마스크원단 및 그 제조방법을 제공한다.The present invention for achieving the above object in the weaving of the head tie or damask fabric, the weft a formed of a weft yarn and a weft yarn formed of a weft b formed of a weft yarn, a warp a provided with a gold yarn and a silver cross in the upper beam intersection A warp provided by using a double beam inclined to the lower beam by the warp b provided to the yarn, and the warp a crosses between the weft a, and the warp b crosses between the weft b, and is woven to form a pattern. The time inclination b provides a head tie or damask fabric which is woven so as to be exposed to the surface, and a manufacturing method thereof.

또한, 헤드타이 또는 다마스크원단에 있어서, 화섬사로 형성된 위사a와, 화섬사로 형성된 위사b로 구비되는 위사, 금사와 은사로 구비되는 경사a를 상빔에 교차로 정경하고, 화섬사로 구비되는 경사b를 하빔에 정경한 이중빔을 사용하여 구비되는 경사로 구성되고, 상기 경사a는 위사a 사이로 교차하고, 경사b는 위사b 사이로 교차하여 제직되고, 무늬 형성시 경사b는 표면에 노출되도록 제직되어 구성되는 헤드타이 또는 다마스크원단을 제공한다.Further, in the head tie or damask fabric, the weft a formed of the weaving yarn and the weft yarn formed of the weft yarn b are made of weft yarns, and the warp a provided with the gold yarn and the silver yarn are cross-cut to the upper beam, and the warp b provided as the weft yarn is It is composed of a warp provided by using a double beam inclined to the lower beam, the warp a crosses between the weft a, the warp b is interwoven between the weft b, weaving, the warp b is formed to be woven so as to expose the surface when forming a pattern Provide headtie or damask fabric.

이하, 도시된 첨부 도면을 참조하여 본 발명에 따른 헤드타이 또는 다마스크원단 및 그 제조방법의 특징적인 구성과 작용효과를 상세히 설명하면 다음과 같다. Hereinafter, with reference to the accompanying drawings shown in detail the characteristic configuration and the effect of the head tie or damask fabric and a manufacturing method according to the present invention.

도 1은 본 발명 헤드타이 또는 다마스크원단의 실시사진이고, 도 2는 본 발명 헤드타이 또는 다마스크원단의 구성을 나타낸 단면도이고, 도 3은 이중빔을 도시한 측면도이며, 도 4는 이중빔의 실시사진이다.1 is a photograph of an embodiment of the head tie or damask fabric of the present invention, Figure 2 is a cross-sectional view showing the configuration of the head tie or damask fabric of the present invention, Figure 3 is a side view showing a double beam, Figure 4 is a double beam Is an implementation photograph.

본 발명 헤드타이 또는 다마스크원단(10)의 제조방법은 상기의 목적을 달성하기 위한 본 발명은 헤드타이 또는 다마스크원단(10)을 제직함에 있어서, 화섬사로 형성된 위사a(110)와, 화섬사로 형성된 위사b(120)로 구비되는 위사(100), 금사(211)와 은사(212)로 구비되는 경사a(210)를 상빔(31)에 교차로 정경하고, 화섬사로 구비되는 경사b(220)를 하빔(32)에 정경한 이중빔(30)을 사용하여 구비되는 경사(200)로 구성되고, 상기 경사a(210)는 위사a(110) 사이로 교차하고, 경사b(220)는 위사b(120) 사이로 교차하여 제직되고, 무늬 형성시 경사b(220)는 표면에 노출되도록 제직되어 이루어지는 구성이다.The present invention is a method of manufacturing the head tie or damask fabric 10 is the present invention for weaving the head tie or damask fabric 10, in the weaving head tie or damask fabric 10, weft a (110) formed of a fiber thread, and a fiber thread yarn The weft yarn 100, which is provided with the weft yarn b (120) formed by the warp yarns (211) provided with the gold yarn 211 and the silver yarn 212, cross-viewed to the upper beam 31, the warp yarn b (220) ) Is composed of an inclined 200 is provided using a double beam 30 to the lower beam 32, the inclination a (210) intersects between the weft a (110), the inclination b (220) weft Cross weaves between the b (120), the inclination b (220) is formed to be woven so as to expose the surface when forming a pattern.

상기 위사a(110)와 위사b(120), 경사b(220)는 통상의 화섬사로 이루어지며, 화섬사는 원료를 가열 처리하여 가늘고 긴 화섬사를 제조하는 공지의 화섬사의 제조방법에 있어서, 합성수지 97중량% ∼ 99.9중량%와 나노실버 0.1중량% ∼ 3중량%를 혼합 교반하여 혼합물을 형성하고, 상기 혼합물을 원료로 사용하는 것을 포함하여 이루어지는 화섬사와 같이 공지된 다양한 종류의 화섬사를 사용하는 것이 바람직 하다.The weft a (110), weft b (120), the inclined b (220) is made of a conventional chemical fiber yarns, chemical fiber yarns in the manufacturing method of a known chemical fiber yarns for producing a long, fine yarns by heat treatment raw material, synthetic resin 97 It is preferable to use a variety of known fiber yarns, such as a fiber yarn comprising mixing and stirring the weight% to 99.9% by weight and 0.1% to 3% by weight of the nanosilver, and using the mixture as a raw material. Do.

위사(100)는 피륙을 짤 때 가로 방향으로 놓인 실을 의미하는 것으로, 횡사(橫絲)라고도 하며, 경사(200)는 피륙을 짤 때 세로 방향으로 놓인 실을 의미하고, 종사(縱絲)라고도 한다.The weft yarn 100 refers to a thread placed in the horizontal direction when weaving the skin, also called a cross (橫 絲), the inclination 200 refers to a thread placed in the vertical direction when weaving the skin, engaged (종사) Also called.

위사a(110)는 화섬사로 구성되고, 색상 및 재질은 다양하게 구비될 수 있음을 밝혀둔다.Weft a (110) is composed of a fiber thread, it turns out that the color and material can be provided in various ways.

경사a(210)는 금사(211)와 은사(212)로 구비되는 것으로 상빔(31)에 상기 금사(211)와 은사(212)가 번갈아 가면서 반복적으로 감겨져 있는 형태이다.The inclination a 210 is provided as the gold yarn 211 and the silver yarn 212, and the gold yarn 211 and the silver yarn 212 are alternately wound on the upper beam 31 alternately.

상빔(31)은 이중빔(30)에서 상단에 구성된 일종의 실타래를 의미하고, 금사(211)와 은사(212)가 번갈아 가면서 반복적으로 감겨져 있다.The upper beam 31 refers to a kind of thread formed at the upper end of the double beam 30, and the gold yarn 211 and the silver yarn 212 are alternately wound up alternately.

상기 금사(211)와 은사(212)는 상빔(31)에 번갈아가며 감겨져 있고, 기계적인 작동에 의해 상하로 교차함과 동시에 매번 교차가 진행될 때, 위사a(110)를 금사(211)와 은사(212) 사이에 끼우면서 제직하게 된다.The gold yarn 211 and the silver yarn 212 are alternately wound on the upper beam 31, and when we cross up and down at the same time every time the cross proceeds at the same time by a mechanical operation, the weft a (110) and the gold yarn 211 and silver yarn (212) is sandwiched between the weaving.

위사b(120)는 화섬사로 구성되고, 색상 및 재질은 다양하게 구비될 수 있음 을 밝혀둔다.Weft b (120) is composed of a fiber thread, it turns out that the color and material can be provided in various ways.

경사b(220)는 화섬사로 구비되는 것으로 하빔(32)에 다수의 화섬사가 반복적으로 번갈아 가면서 감겨져 잇고, 한쌍의 화섬사가 상하로 교차함과 동시에 상기 화섬사 사이로 위사b(120)를 끼워가면서 제직하게 된다.The inclined b 220 is provided as a fiber thread, and a plurality of fiber threads are repeatedly wound alternately on the lower beam 32, and a pair of fiber threads cross up and down and weft b 120 is interposed between the fiber threads. do.

하빔(32)은 이중빔(30)에서 하단에 구성된 일종의 실타래를 의미하는 것으로, 다수개의 화섬사가 반복적으로 감겨져 있다.The lower beam 32 refers to a kind of thread formed at the lower end of the double beam 30, and a plurality of fiber threads are repeatedly wound.

상기 위사a(110)와 경사a(210), 위사b(120)와 경사b(220)에 의해 이중직물이 제직되고, 직물지의 표면에 금사(211)나 은사(212)가 노출되어 화려한 무늬를 형성하고자 할 때에는 경사a(210)가 경사b(220)의 상부에 위치하게 되고, 경사b(220)는 하단에 위치하며, 이에 따라 경사b(220)와 위사b(120)는 바탕직물로 구비되고, 경사b(220)와 교차하여 교차점(20)을 형성하며 표면에 노출된 경사a(210)는 꽃이나 기타 기하학적인 무늬로 제직되어 헤드타이 또는 다마스크원단(10)에 화려한 장식이 형성될 수 있도록 제직된다.The double fabric is woven by the weft a (110) and warp a (210), weft b (120) and warp b (220), the gold yarn 211 or silver yarn 212 is exposed on the surface of the fabric paper colorful pattern When forming the inclined a (210) is located at the top of the inclined b (220), the inclined b (220) is located at the bottom, accordingly, the inclined b (220) and weft b (120) is a base fabric And a cross point 20 formed to intersect with the inclined b 220, and the inclined a 210 exposed on the surface is woven into a flower or other geometric pattern to form a colorful decoration on the head tie or damask fabric 10. It is woven so that it can be formed.

따라서, 금사(211), 은사(212)와 같은 금속사를 정경한 상빔(31)과, 화섬사를 정경한 하빔(32)의 구성으로 이중빔(30)을 사용하여 헤드타이 또는 다마스크원단(10)을 제직하게 되고, 상기 헤드타이 또는 다마스크원단(10)은 이중직으로 형성된다.Therefore, the head tie or damask fabric (using the double beam 30 in the configuration of the upper beam 31 having a view of the metallic yarns such as the gold yarn 211 and the silver yarn 212 and the lower beam 32 having the fine yarn yarn) 10) and the head tie or damask fabric 10 is formed of a double weave.

참고로, 상기 금사(211)는 금빛이 나는 실을 의미하고, 주로 장식용으로 쓰이며 '금루'라고도 하며, 저면에 금색전착도장층이 형성된 두께가 두꺼운 폴리에칠렌(PE)필름, 상면에 수지접착제를 도포하고 두께가 얇은 폴리에칠렌(PE)필름을 합 지한 다음 150℃∼400℃의 열을 가하면 팽창계수의 차이로 두께가 얇은 쪽으로 동그랗게 말리면서 형성되는 금사(211)와 같이 공지의 다양한 종류의 금사(211)를 사용할 수 있음은 물론이다.For reference, the gold yarn 211 means a golden-colored thread, mainly used for decoration, also referred to as 'geolru', a thick polyethylene film (PE) film formed with a gold electrodeposition coating layer on the bottom, a resin adhesive applied to the upper surface And a thin polyethylene film (PE) film, and then heat is applied to 150 ℃ ~ 400 ℃ and a variety of known gold yarn (211), such as gold yarn (211) is formed by curling in a thin direction by the difference in expansion coefficient Of course, you can use).

또한, 은사(212)는 은빛이 나는 실을 의미하고, 주로 장식용으로 쓰이며 '은루'라고도 하며, 두 폴리에스테르 필름에 은(AG)을 각각 증착하는 한편, 상기 폴리에스테르 필름과 두 은증착 필름에 아크릴수지와 같은 산화방지용 도료를 코팅처리한 다음, 상기 두 은증착 필름이 상호 면접되게 이들을 합지한 상태에서 세절하여 구성되는 은사(212)와 같은 공지된 다양한 종류의 은사(212)를 사용할 수 있음은 물론이다.In addition, the silver yarn 212 means a silvery thread, and is mainly used for decoration, also referred to as 'silver lu', and deposits silver (AG) on two polyester films, respectively, while the polyester film and two silver deposition films After coating an anti-oxidant paint such as acrylic resin, various kinds of known gifts 212 may be used, such as a gift 212 configured by cutting the two silver deposition films in a state where they are laminated to be mutually interviewed. Of course.

또한, 본 발명 헤드타이 또는 다마스크원단(10)은 헤드타이 또는 다마스크원단(10)에 있어서, 화섬사로 형성된 위사a(110)와, 화섬사로 형성된 위사b(120)로 구비되는 위사(100), 금사(211)와 은사(212)로 구비되는 경사a(210)를 상빔(31)에 교차로 정경하고, 화섬사로 구비되는 경사b(220)를 하빔(32)에 정경한 이중빔(30)을 사용하여 구비되는 경사(200)로 구성되고, 상기 경사a(210)는 위사a(110) 사이로 교차하고, 경사b(220)는 위사b(120) 사이로 교차하여 제직되고, 무늬 형성시 경사b(220)는 표면에 노출되도록 제직되어 이루어지는 구성이다.In addition, the head tie or damask fabric 10 of the present invention in the head tie or damask fabric 10, the weft yarn 100 is provided with a weft a (110) formed of a fiber thread, and a weft b (120) formed of a fiber thread. ), A double beam 30 having a warp a 210 provided with a gold yarn 211 and a silver yarn 212 at an intersection with the upper beam 31 and a warp b 220 provided with a filament yarn with a lower beam 32. ), The inclination a (210) is provided using, the inclination a (210) intersects between the weft a (110), the inclination b (220) is interwoven between the weft b (120), weaving, when forming a pattern The inclined b 220 is configured to be woven to expose the surface.

상기 위사a(110)와 위사b(120), 경사b(220)는 통상의 화섬사로 이루어지며, 화섬사는 원료를 가열 처리하여 가늘고 긴 화섬사를 제조하는 공지의 화섬사의 제조방법에 있어서, 합성수지 97중량% ∼ 99.9중량%와 나노실버 0.1중량% ∼ 3중량%를 혼합 교반하여 혼합물을 형성하고, 상기 혼합물을 원료로 사용하는 것을 포함하 여 이루어지는 화섬사와 같이 공지된 다양한 종류의 화섬사를 사용하는 것이 바람직 하다.The weft a (110), weft b (120), the inclined b (220) is made of a conventional chemical fiber yarns, chemical fiber yarns in the manufacturing method of a known chemical fiber yarns for producing a long, fine yarns by heat treatment raw material, synthetic resin 97 It is preferable to use a variety of known types of fiber thread, such as a fiber thread comprising mixing and stirring the weight% to 99.9% by weight and 0.1% to 3% by weight of the nanosilver, and using the mixture as a raw material. desirable.

위사(100)는 피륙을 짤 때 가로 방향으로 놓인 실을 의미하는 것으로, 횡사(橫絲)라고도 하며, 경사(200)는 피륙을 짤 때 세로 방향으로 놓인 실을 의미하고, 종사(縱絲)라고도 한다.The weft yarn 100 refers to a thread placed in the horizontal direction when weaving the skin, also called a cross (橫 絲), the inclination 200 refers to a thread placed in the vertical direction when weaving the skin, engaged (종사) Also called.

위사a(110)는 화섬사로 구성되고, 색상 및 재질은 다양하게 구비될 수 있음을 밝혀둔다.Weft a (110) is composed of a fiber thread, it turns out that the color and material can be provided in various ways.

경사a(210)는 금사(211)와 은사(212)로 구비되는 것으로 상빔(31)에 상기 금사(211)와 은사(212)가 번갈아 가면서 반복적으로 감겨져 있는 형태이다.The inclination a 210 is provided as the gold yarn 211 and the silver yarn 212, and the gold yarn 211 and the silver yarn 212 are alternately wound on the upper beam 31 alternately.

상빔(31)은 이중빔(30)에서 상단에 구성된 일종의 실타래를 의미하고, 금사(211)와 은사(212)가 번갈아 가면서 반복적으로 감겨져 있다.The upper beam 31 refers to a kind of thread formed at the upper end of the double beam 30, and the gold yarn 211 and the silver yarn 212 are alternately wound up alternately.

상기 금사(211)와 은사(212)는 상빔(31)에 번갈아가며 감겨져 있고, 기계적인 작동에 의해 상하로 교차함과 동시에 매번 교차가 진행될 때, 위사a(110)를 금사(211)와 은사(212) 사이에 끼우면서 제직하게 된다.The gold yarn 211 and the silver yarn 212 are alternately wound on the upper beam 31, and when we cross up and down at the same time every time the cross proceeds at the same time by a mechanical operation, the weft a (110) and the gold yarn 211 and silver yarn (212) is sandwiched between the weaving.

위사b(120)는 화섬사로 구성되고, 색상 및 재질은 다양하게 구비될 수 있음을 밝혀둔다.Weft b (120) is composed of a fiber thread, it turns out that the color and material can be provided in various ways.

경사b(220)는 화섬사로 구비되는 것으로 하빔(32)에 다수의 화섬사가 반복적으로 번갈아 가면서 감겨져 잇고, 한쌍의 화섬사가 상하로 교차함과 동시에 상기 화섬사 사이로 위사b(120)를 끼워가면서 제직하게 된다.The inclined b 220 is provided as a fiber thread, and a plurality of fiber threads are repeatedly wound alternately on the lower beam 32, and a pair of fiber threads cross up and down and weft b 120 is interposed between the fiber threads. do.

하빔(32)은 이중빔(30)에서 하단에 구성된 일종의 실타래를 의미하는 것으 로, 다수개의 화섬사가 반복적으로 감겨져 있다.The lower beam 32 refers to a kind of thread formed at the lower end of the double beam 30, and a plurality of fiber threads are repeatedly wound.

상기 위사a(110)와 경사a(210), 위사b(120)와 경사b(220)에 의해 이중직물이 제직되고, 직물지의 표면에 금사(211)나 은사(212)가 노출되어 화려한 무늬를 형성하고자 할 때에는 경사a(210)가 경사b(220)의 상부에 위치하게 되고, 경사b(220)는 하단에 위치하며, 이에 따라 경사b(220)와 위사b(120)는 바탕직물로 구비되고, 경사b(220)와 교차하여 교차점(20)을 형성하며 표면에 노출된 경사a(210)는 꽃이나 기타 기하학적인 무늬로 제직되어 헤드타이 또는 다마스크원단(10)에 화려한 장식이 형성될 수 있도록 제직된다.The double fabric is woven by the weft a (110) and warp a (210), weft b (120) and warp b (220), the gold yarn 211 or silver yarn 212 is exposed on the surface of the fabric paper colorful pattern When forming the inclined a (210) is located at the top of the inclined b (220), the inclined b (220) is located at the bottom, accordingly, the inclined b (220) and weft b (120) is a base fabric And a cross point 20 formed to intersect with the inclined b 220, and the inclined a 210 exposed on the surface is woven into a flower or other geometric pattern to form a colorful decoration on the head tie or damask fabric 10. It is woven so that it can be formed.

따라서, 금사(211), 은사(212)와 같은 금속사를 정경한 상빔(31)과, 화섬사를 정경한 하빔(32)의 구성으로 이중빔(30)을 사용하여 헤드타이 또는 다마스크원단(10)을 제직하게 되고, 상기 헤드타이 또는 다마스크원단(10)은 이중직으로 형성된다.Therefore, the head tie or damask fabric (using the double beam 30 in the configuration of the upper beam 31 having a view of the metallic yarns such as the gold yarn 211 and the silver yarn 212 and the lower beam 32 having the fine yarn yarn) 10) and the head tie or damask fabric 10 is formed of a double weave.

참고로, 상기 금사(211)는 금빛이 나는 실을 의미하고, 주로 장식용으로 쓰이며 '금루'라고도 하며, 저면에 금색전착도장층이 형성된 두께가 두꺼운 폴리에칠렌(PE)필름, 상면에 수지접착제를 도포하고 두께가 얇은 폴리에칠렌(PE)필름을 합지한 다음 150℃∼400℃의 열을 가하면 팽창계수의 차이로 두께가 얇은 쪽으로 동그랗게 말리면서 형성되는 금사(211)와 같이 공지의 다양한 종류의 금사(211)를 사용할 수 있음은 물론이다.For reference, the gold yarn 211 means a golden-colored thread, mainly used for decoration, also referred to as 'geolru', a thick polyethylene film (PE) film formed with a gold electrodeposition coating layer on the bottom, a resin adhesive applied to the upper surface And a thin polyethylene film (PE) film is laminated, and then heat is applied to 150 ° C. to 400 ° C., and a variety of known gold yarns 211 are formed, such as gold yarns 211 formed by curling in a thin direction with a difference in expansion coefficient. Of course, you can use).

또한, 은사(212)는 은빛이 나는 실을 의미하고, 주로 장식용으로 쓰이며 '은루'라고도 하며, 두 폴리에스테르 필름에 은(AG)을 각각 증착하는 한편, 상기 폴리 에스테르 필름과 두 은증착 필름에 아크릴수지와 같은 산화방지용 도료를 코팅처리한 다음, 상기 두 은증착 필름이 상호 면접되게 이들을 합지한 상태에서 세절하여 구성되는 은사(212)와 같은 공지된 다양한 종류의 은사(212)를 사용할 수 있음은 물론이다.In addition, the silver yarn 212 means a silvery thread, and is mainly used for decoration, also referred to as 'silver lu', while depositing silver (AG) on two polyester films, respectively, on the polyester film and two silver deposition films. After coating an anti-oxidant paint such as acrylic resin, various kinds of known gifts 212 may be used, such as a gift 212 configured by cutting the two silver deposition films in a state where they are laminated to be mutually interviewed. Of course.

본 발명은 상술한 특정의 실시 예에 한정되지 아니하며, 특허청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 본 발명이 속하는 해당 기술분야에서 숙련된 당업자는 다양하게 변형하여 실시할 수 있고, 그와 같은 변경은 청구범위 기재의 범위내에 있다.The present invention is not limited to the specific embodiments described above, and those skilled in the art to which the present invention pertains may be variously modified and practiced without departing from the gist of the present invention as claimed in the claims. Such changes are within the scope of the claims.

본 발명은 원단 표면에 금사와 음사가 제직되어 형성된 무늬가 선명하게 나타나고, 그 무늬가 고급스러우며, 선염이 가능하여 제직 후 염색을 시행하지 않도록 하며, 또한, 원단의 평활도가 높아 외관상 미려할 뿐만 아니라 터치감이 좋으며, 제직 후 테투리부위에 메탈릭사가 잉여되지 않아 잘라내야 하는 번거로움과 자원의 낭비가 발생하지 않는 매우 유용한 발명이다.In the present invention, the pattern formed by weaving gold yarn and umsa on the surface of the fabric appears clearly, the pattern is luxurious, and the dye is possible to prevent dyeing after weaving, and the smoothness of the fabric is not only beautiful in appearance. It has a good touch and is a very useful invention that does not cause the hassle and waste of resources to be cut off due to excess metallic yarn on the rim part after weaving.

Claims (2)

헤드타이 또는 다마스크원단(10)을 제직함에 있어서, In weaving the head tie or damask fabric 10, 화섬사로 형성된 위사a(110)와, 화섬사로 형성된 위사b(120)로 구비되는 위사(100);Weft yarn (100) provided with a weft yarn (110) formed of a fiber thread, and a weft yarn (120) formed of a fiber thread; 금사(211)와 은사(212)로 구비되는 경사a(210)를 상빔(31)에 교차로 정경하고, 화섬사로 구비되는 경사b(220)를 하빔(32)에 정경한 이중빔(30)을 사용하여 구비되는 경사(200);로 구성되고, The inclined a 210 provided with the gold yarn 211 and the silver yarn 212 is fixed to the upper beam 31 at an intersection, and the double beam 30 inclined the inclined b 220 provided with the filament yarn to the lower beam 32 is formed. Slope 200 is provided using; consisting of, 상기 경사a(210)는 위사a(110) 사이로 교차하고, 경사b(220)는 위사b(120) 사이로 교차하여 제직되고, 경사a(210)는 원단 외부 표면에 노출되어 무늬를 형성하도록 제직되는 것을 특징으로 하는 헤드타이 또는 다마스크원단(10)의 제조방법.The warp a 210 crosses between the weft a 110, the warp b 220 interweaves between the weft b 120, and the warp a 210 is exposed to the outer surface of the fabric to form a pattern. Method of manufacturing a head tie or damask fabric (10), characterized in that. 헤드타이 또는 다마스크원단(10)에 있어서, In the head tie or damask fabric 10, 화섬사로 형성된 위사a(110)와, 화섬사로 형성된 위사b(120)로 구비되는 위사(100);Weft yarn (100) provided with a weft yarn (110) formed of a fiber thread, and a weft yarn (120) formed of a fiber thread; 금사(211)와 은사(212)로 구비되는 경사a(210)를 상빔(31)에 교차로 정경하고, 화섬사로 구비되는 경사b(220)를 하빔(32)에 정경한 이중빔(30)을 사용하여 구비되는 경사(200);로 구성되고, The inclined a 210 provided with the gold yarn 211 and the silver yarn 212 is fixed to the upper beam 31 at an intersection, and the double beam 30 inclined the inclined b 220 provided with the filament yarn to the lower beam 32 is formed. Slope 200 is provided using; consisting of, 상기 경사a(210)는 위사a(110) 사이로 교차하고, 경사b(220)는 위사b(120) 사이로 교차하여 제직되고, 경사a(210)는 원단 외부 표면에 노출되어 무늬를 형성하도록 제직되는 것을 특징으로 하는 헤드타이 또는 다마스크원단(10).The warp a 210 crosses between the weft a 110, the warp b 220 interweaves between the weft b 120, and the warp a 210 is exposed to the outer surface of the fabric to form a pattern. Head tie or damask fabric, characterized in that 10.
KR1020060112942A 2006-11-15 2006-11-15 Headtie or damask cloth and manufacturing method of thats KR100729493B1 (en)