KR100697596B1 - Fomentation device made by stone - Google Patents
Fomentation device made by stone Download PDFInfo
- Publication number
- KR100697596B1 KR100697596B1 KR1020050055566A KR20050055566A KR100697596B1 KR 100697596 B1 KR100697596 B1 KR 100697596B1 KR 1020050055566 A KR1020050055566 A KR 1020050055566A KR 20050055566 A KR20050055566 A KR 20050055566A KR 100697596 B1 KR100697596 B1 KR 100697596B1
- Authority
- KR
- South Korea
- Prior art keywords
- latent heat
- sodium
- phase change
- temperature
- weight
- Prior art date
Abstract
본 발명은 상호 합체되는 1쌍의 맥반석으로 된 찜질체로 이루어지고, 그 내부에는 잠열재가 충전 수용된 찜질체와, 이 찜질체를 수용할 수 있으며 내주벽에는 외측이 단열재로 피복된 면상 발열체가 수용되고, 외부 한쪽에 상기 면상 발열체로 전원을 인가하기 위한 터미널이 부착된 수납가방으로 구성되어, 상기 찜질체를 수납가방에 수용하여 놓고, 면상 발열체를 가동시켜 가온 되게 하는 구성으로 된 맥반석 찜질기이며, 상기 잠열재는 가온에 의해 축열된 후 외부 에너지의 공급이 없이도 장시간 찜질체의 온도를 50℃ 이상으로 유지시켜 찜질 효과를 배가시키게 되어 있는 맥반석 찜질기이다.The present invention is composed of a pair of agglomerates consisting of a pair of ganban stones, the inside of which is filled with a latent heat filled with a culprit, and can accommodate this culprit, the inner circumferential wall is coated with a heating element coated with a heat insulating material on the outside The outer bag is configured as an accommodating bag having a terminal for applying power to the planar heating element, the accommodating body is housed in the accommodating bag, and is configured to be warmed by operating the planar heating element. The latent heat material is an elbow steamer that is doubled by the heating by maintaining the temperature of the cuddle body for more than 50 ° C. for a long time without supplying external energy.
찜질기, 맥반석 찜질, Poultry machine, ganban stone poultice,
Description
도 1은 본 발명의 주요 구성을 나타내는 사시도.1 is a perspective view showing a main configuration of the present invention.
도 2는 도 1에 도시한 찜질체의 단면도.2 is a cross-sectional view of the poultice body shown in FIG.
도 3은 도 1에 도시한 수납가방의 소재 단층도.3 is a material tomographic view of the storage bag shown in FIG.
도 4는 도 3에 도시한 면상 발열체의 단면도.4 is a cross-sectional view of the planar heating element shown in FIG. 3.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
2: 찜질체 4: 수납가방2: poultice body 4: storage bag
6: 잠열재 8: 자석6: latent material 8: magnet
10: 덮개 12a, 12b: 벨크로 화스너10:
14: 내부공간 16: 전원 플럭14: Internal space 16: Power plug
18: 터미널 소켓 20: 내피18: terminal socket 20: inner shell
22: 면상 발열체 24: 단열재22: planar heating element 24: heat insulating material
26: 외피 28: 섬유사26: jacket 28: fiber yarn
30: 흑연 함유수지30: graphite-containing resin
본 발명은 찜질기에 관한 것으로서, 특히 맥반석을 주재료로 한 맥반석 찜질기에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a steaming machine, and more particularly, to an elbow steamer having elvan as the main material.
찜질기는 손발의 혈행 장애, 울혈 해소, 근육 긴장완화 등을 목적으로 환부에 열을 가하는 장치로서, 종래부터 여러 가지 구조의 것이 실용화되고 있으나, 본 발명은 맥반석의 우수한 원적외선 방사 효능으로 찜질 효과를 거두려 하는 것이다.Poultry is a device for applying heat to the affected area for the purpose of blood circulation disorders, relieve congestion, muscle tension relief, etc., the conventional structure has been practically used, but the present invention has a poultice effect due to the excellent far-infrared radiation effect of elvan I'm afraid.
맥반석의 원적외선 방사 효능을 이용한 찜질기는 주로 맥반석 분을 수용한 포대 내부에 가열 원을 배치한 구조로 됨이 통상이다.The steaming machine using the far-infrared radiation efficacy of elvan has a structure in which a heating source is arranged inside the bag containing the elvan.
이러한 구조의 찜질기는 약간의 유연성이 있어서 환부에 접촉시키기 좋은 이점이 있으나, 맥반석에서 방출되는 원적외선이 환부로 쬐게 되는 양이 적어 찜질 효과가 낮은 단점이 있다. This structure has a slight flexibility has a good advantage in contact with the affected area, but the amount of far-infrared rays emitted from elvan is less exposed to the affected area has a disadvantage of low poultry effect.
그리고 종래의 찜질기는 찜질 효능에만 그치고 있어서 그 쓰임새가 좋지 않다.And the conventional poultry machine is only good poultry efficacy, its use is not good.
본 발명자는 국내 실용신안등록 출원 20-2005-0004683호를 통하여, 맥반석 특유의 원적외선 방사 효능이 직접 환부에 작용할 수 있는 구조로 된 찜질기로서, 족온 기능, 목침 대용 기능, 복부 다이어트 기능을 갖춘 맥반석 찜질기를 제안한 바 있다.The present inventors through the Korean Utility Model Registration Application No. 20-2005-0004683, as a steaming machine having a structure capable of directly acting on the affected part of far-infrared radiation effect unique to the elvan, the elvan stone steamer with foot temperature function, substitute needle function, abdominal diet function Has been proposed.
그런데 제안한 맥반석 찜질기는 찜질체 내부에 전열수단을 배치한 구조로서, 이 전열수단이 단선 또는 단락되면 수리가 용이하지 않은 결점이 있고, 또한 가온은 내부에서 발원하여 외부로 전도되기 때문에 가온 시간이 길어지는 단점이 있다.However, the proposed Elvan steamer has a heat dissipation means arranged inside the steaming body, and if the heat dissipation means is disconnected or short-circuited, there is a drawback that is not easy to repair, and the warming time is long since the heat is sourced from the inside and conducted to the outside. There are disadvantages to losing.
또, 잠열재로서 운모석분, 산화알미늄분, 구리분 등을 채용한 현열(sensible heat) 방식의 잠열재를 사용하고 있는 관계로, 가열 직후는 대단히 뜨거워 수건 등으로 싸서 사용할 정도이지만 얼마 지나지 않아 식어 버려 항온성이 좋지 않은 단점이 있다.The latent heat of the sensible heat method using mica stone powder, aluminum oxide powder, copper powder, etc. is used as the latent heat material, so it is very hot right after heating and wrapped around with a towel. There is a drawback of poor temperature stability.
잠열재로서, 난방분야에서는 상변화물질(PCM: phase change material)이 사용되고 있다. 상변화물질이란 물리적, 화학적 조건 변화에 따라 상 전이되는 성질을 가진 물질을 뜻하며, 상전이의 예로는 융해, 고화, 기화, 응결 따위를 들 수 있다.As a latent heat material, a phase change material (PCM) is used in the heating field. Phase change material refers to a material having a property of phase transition according to changes in physical and chemical conditions. Examples of phase transitions include melting, solidification, vaporization, and condensation.
상전이를 일으키는 상변화물질은 수없이 많은 종류가 알려져 있고, 각 물질의 용융온도는 천차만별로 나타나기 때문에 축열의 용도에 맞게 혼합 사용함이 일반적이다.There are many kinds of phase change materials that cause phase transitions, and since the melting temperature of each material varies only for each type, it is common to use a mixture according to the purpose of heat storage.
상변화물질을 이용한 잠열에서 나타나는 문제점은, 물질이 상전이를 반복할 때에 차츰 침전물로 변천되어 잠열 효과가 저하되는 상분리 현상, 용융점 이하로 온도가 내려가도 액체에서 고체로 상변화가 일어나지 않아 잠열 방출이 정지되는 과냉각현상, 화학적 결합 또는 시간이 지남에 따라 물성이 변화되는 부식 현상이 알려져 있고, 이들 문제점은 상변화물질의 각 특성을 잘 조합하여 해소하거나, 따로 핵 생성제(nucleating agent), 증점제(thickening agent)를 준비하여 첨가함으로써 해소하고 있다.The problem with latent heat using phase change materials is that phase change occurs when the material is gradually transformed into sediment when the phase transition is repeated, and latent heat release occurs because the phase change does not occur from liquid to solid even when the temperature falls below the melting point. Stationary subcooling, chemical bonding or corrosion that changes physical properties over time is known, and these problems can be solved by combining the characteristics of phase change materials, or nucleating agent, thickener ( The solution is prepared by adding a thickening agent.
그러나 상변화물질로서 공지된 것은, 대부분 난방에 적용하기 위한 것이므로 본 발명에 관련된 찜질기에서 요구되는 잠열 효과에는 부합되지 않는다.However, what is known as a phase change material, for most applications for heating does not meet the latent heat effect required in the steaming machine according to the present invention.
본 발명의 목적은 맥반석 특유의 원적외선 방사 효능이 직접 환부에 작용할 수 있는 구조로 된 찜질기로서, 족온 기능, 목침 대용 기능, 복부 다이어트 기능 등을 갖춤과 동시에, 전열수단의 고장 수리가 용이하고 단시간에 가온 될 수 있는 구성을 갖춘 맥반석 찜질기를 제공함에 있다.An object of the present invention is a steaming machine having a structure capable of directly acting on the affected part of far-infrared radiation effect unique to elvan, having a foot temperature function, a needle replacement function, an abdominal diet function, etc. It is to provide an elvan steamer with a configuration that can be warmed.
본 발명의 다른 목적은 찜질에 적합한 온도 범위로 장시간 유지될 수 있는 잠열재를 갖추게 하여, 지속적인 외부 열원의 공급이 없이도 수시간 동안 찜질을 행할 수 있는 맥반석 찜질기를 제공함에 있다.Another object of the present invention is to provide a latent heat material that can be maintained for a long time in a suitable temperature range for steaming, to provide a ganchorite steamer that can steam for several hours without a continuous supply of external heat source.
상술한 목적을 구현하는 본 발명은, 맥반석으로 되고 상호 접합 되는 1쌍으로 이루어지며 내부에는 잠열재가 충전되는 찜질체로 된다.The present invention for realizing the above-mentioned object is made of a pair of ganban rock and mutually bonded to the inside is made of a poultice filled with latent heat.
그리고 이 찜질체를 수용할 수 있고 외측이 단열재로 피복된 면상 발열체를 내주면에 구비하는 수납가방이 더 구비될 수 있다.And it may be further provided with a storage bag for accommodating the poultice and having a planar heating element on the inner circumferential surface is coated with a heat insulating material on the outside.
또한, 상기 찜질체의 내부에 충전된 잠열재 속으로는 혈행 촉진을 위한 자석이 배열될 수도 있다.In addition, a magnet for promoting blood circulation may be arranged in the latent heat material filled in the poultice.
본 발명의 찜질기에 수용되는 잠열재는, 피로인산나트륨 10수화물(Na4P2O7ㆍ10H2O)과 도코산(C22H46)을 혼합한 상변화물질 69 ~ 87 중량%에, 핵 생성제로서 염화나트륨(NaCL) 10 ~ 15 중량%, 증점제로서 아크릴산 1 ~ 3 중량%, 잠열 온도조절제로서 붕사비료 2 ~ 13 중량%를 첨가하고 교반 혼합한 것이 사용된다.The latent heat material accommodated in the steamer of the present invention is nucleated in 69 to 87% by weight of a phase change material in which sodium pyrophosphate decahydrate (Na 4 P 2 O 7 10H 2 O) and docoic acid (C 22 H46) are mixed. 10 to 15% by weight of sodium chloride (NaCL), 1 to 3% by weight of acrylic acid as a thickener, and 2 to 13% by weight of borax fertilizer as a latent thermostat are used and stirred and mixed.
또, 상기 상변화물질은 염화칼슘 6수화물(Cacl2ㆍ6H2O), 티오황산나트륨 5수화물(Na2S2O3ㆍ5H2O), 탄산나트륨 10수화물(Na2CO3ㆍ10H2O), 인산수소나트륨 12수화물(NaHPO4ㆍ12H2O), 아세트산 나트륨 3수화물(CH3COONaㆍ3H2O), 황산나트륨 10수화물(Na2SO4ㆍ10H2O) 중에서 선택한 1종을 도코산(C22H46)과 교반 혼합하여 사용할 수도 있다.Further, the phase change material is calcium chloride hexahydrate (Cacl 2 and 6H 2 O), sodium thiosulfate pentahydrate (Na 2 S 2 O 3 and 5H 2 O), sodium carbonate decahydrate (Na 2 CO 3 and 10H 2 O), Sodium hydrogen phosphate 12-hydrate (NaHPO 4 12H 2 O), sodium acetate trihydrate (CH 3 COONa, 3H 2 O), sodium sulfate decahydrate (Na 2 SO 4 10H 2 O) is selected from docoic acid (C 22 H46) may be used by stirring and mixing.
이하 본 발명을 첨부 도면에 따른 바람직한 실시 예로 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to preferred embodiments according to the accompanying drawings.
도 1은 본 발명에 관련된 찜질기의 구성을 나타내는 사시도로서, 도면에서 상하로 배치된 1쌍의 찜질체(2)는 맥반석으로 된 것이며, 이것은 상호 접합 되는 1쌍으로 이루어진 것이다.1 is a perspective view showing the configuration of a steaming machine according to the present invention, in which the pair of
이 찜질체(2)는 수납가방(4)에 넣어져 보관, 가온, 또는 휴대할 수 있는 것이며, 도 2로 나타낸 바와 같이, 내부는 잠열재(6)가 충전될 수 있는 공간이 있고, 또 잠열재(6)와 함께 다수의 자석(8)이 배치될 수도 있는 것이다.The steaming
1쌍으로 이루어져서 상호 대향 접합 되는 찜질체(2)는, 견고한 접합을 구현하기 위하여 어느 한쪽에 돌출테를 부여하여 끼워 맞춤 형식으로 접합 되게 할 수도 있다.The
본 발명에서, 찜질체(2)의 내부로 충전되는 잠열재(6)는 상변화물질, 핵 생성제, 증점제, 잠열 온도 조절제를 혼합하여 되는 것이다.In the present invention, the
상변화물질로는 피로인산나트륨 10수화물(Na4P2O7ㆍ10H2O)과 도코산(C22H46)을 혼합한 것이 적당하다.As a phase change material, a mixture of sodium pyrophosphate decahydrate (Na 4 P 2 O 7 ㆍ 10H 2 O) and docoic acid (C 22 H46) is appropriate.
상변화물질로서 도코산을 단독으로 사용하고, 초기온도 30℃에서 온도 80℃로 가온하여 축열 시키면서 전체 상변화의 평균온도와 축열량 변화를 관찰하면, 초기 열 저장시 도코산의 온도는 서서히 증가하고 58 ~ 62℃에서 잠열 구간의 형성이 시작되고 축열량은 68.375㎉/㎏로 측정된다.When doco acid is used alone as a phase change material, and the average temperature and the amount of heat storage change of the total phase change are observed while heating and reheating from the initial temperature of 30 ° C. to 80 ° C., the temperature of the doco acid increases gradually during initial heat storage. The formation of the latent heat section starts at 58 ~ 62 ℃ and the heat storage amount is measured as 68.375 ㎉ / ㎏.
또, 피로인산 나트륨을 단독으로 채택하여 초기온도 40℃ 에서 90℃로 가온하여 축열 시키면서 전체 상변화의 평균온도와 축열량 변화를 관찰하면, 초기 열 저장시 급속히 온도가 상승하고 75 ~80℃에서 잠열 구간이 형성되며 축열량은 73.25㎉/㎏ 로 측정된다.In addition, when sodium pyrophosphate is used alone and the temperature is increased from 40 ℃ to 90 ℃, and the heat storage is observed, when the average temperature and heat storage change of the phase change are observed, the temperature rises rapidly during the initial heat storage, and the temperature is increased from 75 to 80 ℃. A latent heat zone is formed and the heat storage amount is measured as 73.25㎉ / ㎏.
그렇지만, 도코산과 피로인산 나트륨을 교반 혼합한 것을, 초기 온도 35℃에서 85℃로 가온하여 축열 시키면서 전체 상변화의 평균온도와 축열량 변화를 관찰하면, 초기 열 저장시는 용융점이 낮은 도코산의 축열량이 신속하게 증가하여 축열 종료되는 한편, 피로인산 나트륨은 그보다 높은 온도에서 축열량이 증가하기 t작하며, 이때의 축열량은 일반적으로 피로인산 나트륨이 도코산에 비해 약 6% 더 높게 나타난다.However, when the mixed mixture of docoic acid and sodium pyrophosphate was heated and regenerated by heating at an initial temperature of 35 ° C. to 85 ° C., the average temperature and heat storage change of the phase change were observed. While heat is rapidly increased and heat storage ends, sodium pyrophosphate is less likely to increase heat storage at higher temperatures, with heat storage typically showing sodium pyrophosphate about 6% higher than docoic acid.
핵 생성제는 상변화물질의 결정핵 형성을 촉진하여 과냉각을 억제하게 되는 것으로서 본 발명에서는 염화나트륨(NaCL)이 사용된다.The nucleating agent promotes crystal nucleation of the phase change material to inhibit supercooling, and sodium chloride (NaCL) is used in the present invention.
또, 증점제는 상기 표의 상변화물질이 융해-응고하는 과정에서의 과냉각을 억제함과 동시에 융해-응고를 반복하여 생기는 상분리 현상도 억제하는 것으로서, 본 발명에서는 아크릴산 100 중량%, 혹은 아크릴산 99 중량%에 C핵산, 계면활성제, 수산화나트륨(NaOH) 33% 수용액, 메타놀(MeOH) 및 에폭시 812의 혼합물을 1 중량% 이내로 첨가 혼합한 것을 사용할 수 있다.In addition, the thickener inhibits supercooling during the melting-solidification process of the phase change materials in the above table, and also inhibits phase separation caused by repeated melting-solidification. In the present invention, 100% by weight of acrylic acid or 99% by weight of acrylic acid is used. A mixture of C nucleic acid, a surfactant, a 33% aqueous solution of sodium hydroxide (NaOH), a methanol (MeOH), and an epoxy 812 in an amount of 1 wt% or less can be used.
잠열 온도조절제는 특정 온도 범위를 장시간 지속시키기 위하여 투입하는 것 이며, 본 발명에서는 붕사비료를 사용한다.The latent heat temperature regulator is to be added to maintain a specific temperature range for a long time, and in the present invention, borax fertilizer is used.
상술한 상변화물질, 핵 생성제, 증점제, 잠열온도 조절제는,The above-described phase change material, nucleating agent, thickener, latent temperature control agent,
상변화물질 69 ~ 87 중량% Phase change material 69 ~ 87 wt%
핵 생성제 10 ~ 15 중량%10-15 wt% of nucleating agent
증점제 1 ~ 3 중량%Thickener 1-3 wt%
잠열 온도조절제 2 ~ 13 중량% 를 교반 혼합하면 본 발명에 적합한 잠열재(6)를 얻게 된다.Stirring and mixing 2 to 13% by weight of the latent heat regulator to obtain a
이렇게 얻어지는 잠열재(6)를 찜질체(2)에 수용할 때는 상변화물질의 용융점보다 10 ~ 20℃ 정도 높은 온도까지 가온시키면 간편하게 주입 충전할 수 있다.When accommodating the latent heat material (6) thus obtained in the poultice body (2) can be injected and charged simply by heating up to a temperature of about 10 to 20 ℃ higher than the melting point of the phase change material.
상기 잠열재(6)의 가열 온도에 따른 축열량의 변화는 다음 표 1과 같았다.The change in heat storage amount according to the heating temperature of the
상기 표에서 □는 본 발명, △은 비교 예로서의 물, 그리고 ○는 비교 예로서의 돌에 관한 축열량 변화를 나타내는 그래프이다.In the above table,? Is the present invention,? Is water as a comparative example, and? Is a graph showing a change in heat storage amount relating to stones as a comparative example.
표 1을 보아 알 수 있듯이, 본 발명에 사용되는 잠열재(6)는 온도 63℃에 이를 때까지 축열량은 최고 30Kcal/Kg으로 나타났으나, 상기 온도 63℃에 이르러서는 순식간에 85Kcal/Kg으로 급하게 증가하고, 그 이상의 온도에서는 다시 완만하게 축열량이 증가하는 특성을 보여 주고 있는바, 이는 63℃ 부근까지는 도코산의 축열이 시작되어 순식간에 종료되고, 다시 더 높은 온도에서는 피로인산 나트륨의 용융이 개시되면서 서서히 축열이 진행되는 현상으로 나타나기 때문이다.As can be seen from Table 1, the
또, 축열 후의 잠열 효과는 표 2와 같은 결과로 나타났다.Moreover, the latent heat effect after heat storage was shown by the result of Table 2.
표 2에서, 본 발명의 잠열재(6)는 온도 60℃ 이상까지는 비례적으로 식지만, 온도 60℃에서는 대략 5시간 동안 그 온도를 유지하는 잠열 구간을 형성한 다음, 그후부터는 비례적으로 식어가는 특성을 보여주고 있다. In Table 2, the
상기 잠열 구간에서는 도코산의 잠열 효과로 온도 60℃가 유지되는 한편, 피로인산 나트륨에서 발산되는 잠열로 인하여 도코산이 재차 축열 하는 작용이 반복하여 나타나 장시간 유지되는 것이다.In the latent heat section, the temperature of 60 ° C. is maintained due to the latent heat effect of docosan, and the action of regenerating docosan again due to the latent heat emitted from sodium pyrophosphate is repeated and maintained for a long time.
또 상기 잠열구간의 온도 60℃는 맥반석 찜질에 최적한 온도가 되므로 상술한 바와 같이 2종을 교반 혼합한 상변화물질은 맥반석 찜질에 가장 효과적인 잠열재가 됨을 알 수 있다.In addition, since the temperature of 60 ° C of the latent heat section is the optimum temperature for gangan rock poultice, it can be seen that the phase-change material in which the two species are stirred and mixed as described above is the most effective latent heat material for ganban stone poultice.
본 발명의 잠열재(6)는 상술한 도코산과 피로인산 나트륨의 2종 혼합으로 한정되는 것은 아니며, 이들과 균등한 특성이 있는 상변화 물질로서 염화칼슘 6수화물(Cacl2ㆍ6H2O), 티오황산나트륨 5수화물(Na2S2O3ㆍ5H2O), 탄산나트륨 10수화물(Na2CO3ㆍ10H2O), 인산수소나트륨 12수화물(NaHPO4ㆍ12H2O), 아세트산 나트륨 3수화물(CH3COONaㆍ3H2O), 황산나트륨 10수화물(Na2SO4ㆍ10H2O)을 들 수 있고, 이들 상변화물질에 상기 도코산(C22H46)을 포함시킨 군에서 2종을 선택하여 혼합한 것을 사용할 수 있다.The
다음 표 3은 상기의 상변화물질이 갖고 있는 용융점과 단위 중량당 잠열량이 측정치이다.Table 3 below shows the melting point and latent heat amount per unit weight of the phase change material.
다시 도 1을 참조하면, 수납가방(2)은 덮개(10)를 구비하고 있고, 이 덮개(10)는 벨크로 화스너(12a, 12b)에 의해 닫힌 상태를 보전할 수 있게 되어 있으며, 이 덮개(10)에 의해 수납가방(2)의 내부공간(14)은 외부로부터 격리되어 가온 시의 열손실을 줄이게 된다.Referring back to FIG. 1, the
수납가방(4)의 외부 한쪽에는 통상의 온도 조절회로를 갖춘 전원 플럭(16)이 끼워져 연결되기 위한 터미널 소켓(18)이 구비되어 있고, 이 터미널 소켓(18)을 통하여 인가되는 전원은 수납가방(4)으로 인가된다. The outer side of the
한편, 수납가방(4)의 소재는 도 3으로 도시한 바와 같이, 내피(20)에 인접하여 망상의 면상 발열체(22)가 겹쳐져 배치되고, 그 외측으로는 단열재(24)가 겹쳐진 다음, 외피(26)로 피복된 단층구조를 가진다.Meanwhile, as shown in FIG. 3, the material of the
또, 도면에는 나타나 있지 않으나 단열재(24)는 면상 발열체(22)와 접하는 면이 은박 반사면으로 되어, 상기 면상 발열체(22)로부터 발생하는 적외선을 수납가방(4)의 내측으로 반사시켜 열손실을 줄이게 되어 있다.Although not shown in the figure, the
면상 발열체(22)는 반드시 망상으로 구성해야 하는 것은 아니지만, 본 발명에서는 70℃ 이하의 낮은 온도로 가온시키기 위하여 필요한 것이다.The
또한, 망상의 면상 발열체(22)는 도 4의 도시와 같이, 섬유사(28)의 외표면에 흑연 함유 수지(30)가 코팅된 구조로 되어 있어서, 인가되는 전원은 흑연 함유 수지를 통해 흐르면서 발열하게 된다.In addition, the
상술한 구성의 본 발명은, 다만 찜질체(2)를 수납가방(4)에 넣고 덮개(10)를 닫은 후에 상기 수납가방(4)의 터미널 소켓(18)으로 전원 플럭(16)을 끼워 연결하는 간단한 조작으로 찜질체(2)를 가온시킬 수 있다.According to the present invention having the above-described configuration, the
또, 찜질체(2)는 전자레인지에 넣어져 고주파로 내부의 잠열재(6) 온도가 승온되게 함으로써 소망하는 온도 범위로 가온될 수 있으며, 이렇게 가온 되는 찜질체(2)는 맥반석으로 만들어져 있음에 따라 특유의 원적외선을 방출하게 된다.In addition, the poultice (2) is put in a microwave oven can be heated to a desired temperature range by allowing the temperature of the latent heat material (6) inside the high frequency at high temperature, the heated poultice (2) is made of elvan According to the emission of unique far infrared rays.
그러므로 사용자는 가온된 찜질체(2)의 외표면을 환부 등에 접촉시키는 간단한 방법으로 사용할 수 있다.Therefore, the user can use the simple method of bringing the outer surface of the
전자레인지 또는 수납가방(4)에서 가온된 찜질체(2)는 외부로부터의 가열원과 단절되어도 내부에 수용된 잠열재(6)를 통한 지속적인 가온 작용으로, 상당 시간 예를 들면, 최단 3 ~ 4시간, 최장 5시간 정도 가온 된 상태를 유지하게 된다.The
상술한 바와 같은 구성으로 된 본 발명의 찜질기는, 찜질체를 직접 환부에 접촉시키는 것이므로 다른 찜질기에 비하여 원적외선의 방사량이 월등히 많아 찜질 효과가 좋다.The steaming machine of the present invention having the above-described configuration has a much higher radiation rate of far-infrared rays than other steaming machines, and thus has a good steaming effect.
게다가 상기 찜질 효과는, 외부 에너지의 공급이 없어도 내부에 수용된 잠열재의 작용으로 장시간 발휘되는 것이므로 종래의 일반적 찜질기에 비해 사용하기가 편리하다.In addition, since the poultice effect is exhibited for a long time without the supply of external energy by the action of the latent heat contained therein, it is more convenient to use than the conventional general poultice machine.
또, 상호 접합 되는 1쌍으로 이루어진 찜질체는 그 표면을 어떤 형태로든 가공할 수 있는 것이므로, 도시한 원반형뿐만이 아니고, 중앙이 오목한 만곡면으로 된 목침 형태 등으로도 쉽게 만들어낼 수 있어서 간단하게 목 경부 찜질을 행할 수 있고, 그 만곡면으로 편안하게 발을 걸쳐 놓을 수도 있어 족온기로도 활용될 수 있으며, 찜질기로 사용하지 않을 때는 목침으로 사용될 수 있는 등 용도가 다양하다.In addition, the pair of cudices that are bonded to each other can be processed into any form, so that not only the disk shape shown in the figure but also the needle shape of the curved surface with a concave center can easily be formed. The cervix can be steamed, and the foot can be comfortably spread over the curved surface, which can be utilized as a foot warmer, and can be used as a needle when not used as a steamer.
또, 만곡면은 인체의 복부 곡선에도 어울리는 것이므로 이것을 복부에 얹고 복식 호흡하면, 복부의 지방층이 원적외선 효과로 쉽게 분해되어, 다이어트 효과가 좋고, 게다가 찜질기의 무게가 복부를 압박하게 되어 복부 비만을 줄이는데 탁월한 효과가 있다. In addition, the curved surface fits the abdomen curve of the human body, so if you put it on your abdomen and breathe double, the fat layer of the abdomen is easily decomposed by the far-infrared effect, and the diet effect is good, and the weight of the steamer compresses the abdomen, reducing abdominal obesity. Excellent effect
본 발명은 상기와 같은 효과 외에도, 전열수단으로 되는 면상 발열체가 수납가방의 내주면에 설치되어 있는 관계로, 고장 발생 시에는 수납가방을 교체하면 되는 것이므로 사용자에 대한 애프터 서비스를 간편하게 할 수 있는 이점과, 수납가방은 찜질체의 보관, 휴대 및 열 손실 없는 단시간의 가온 효과를 도모하게 하는 장점이 있다.The present invention, in addition to the above effects, since the heating element is provided on the inner circumferential surface of the storage bag, which is a heat transfer means, when the failure occurs because the replacement of the storage bag to the advantage that can simplify the after-sales service for the user and , The storage bag has the advantage of facilitating the short-term heating effect without storage, portability and heat loss of the poultice.
Claims (4)