KR100663261B1 - Coationg in minerals which improves the interior air quality - Google Patents

Coationg in minerals which improves the interior air quality Download PDF

Info

Publication number
KR100663261B1
KR100663261B1 KR1020060076994A KR20060076994A KR100663261B1 KR 100663261 B1 KR100663261 B1 KR 100663261B1 KR 1020060076994 A KR1020060076994 A KR 1020060076994A KR 20060076994 A KR20060076994 A KR 20060076994A KR 100663261 B1 KR100663261 B1 KR 100663261B1
Authority
KR
South Korea
Prior art keywords
oxygen
natural mineral
mineral powder
weight
blood
Prior art date
Application number
KR1020060076994A
Other languages
Korean (ko)
Inventor
기상인
Original Assignee
이온하우징 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이온하우징 주식회사 filed Critical 이온하우징 주식회사
Priority to KR1020060076994A priority Critical patent/KR100663261B1/en
Application granted granted Critical
Publication of KR100663261B1 publication Critical patent/KR100663261B1/en

Abstract

Finishing material comprising natural mineral and binder is provided to represent forest aromatic bath effect with oxygen concentration of 20.5 to 21.5% and to smoothly supply oxygen by comprising silicon dioxide, aluminum oxide, potassium oxide, iron oxide, titanium or germanium as well as binder. The natural mineral finishing material comprises 35-40wt.% of natural mineral powder including: 73-78wt.% of silicon dioxide;, 8-10wt.% of aluminum oxide; 4-6wt.% of potassium oxide; 9-11wt.% of iron oxide and 0.4-0.6wt.% of titanium dioxide, as well as 60-65wt.% of a binder. The natural mineral powder includes 1ppm of germanium based on the mineral powder. As a result of assaying radionuclide for the natural mineral powder, it has 0.5 to 1Bq. The finishing material(2) is applied to a concrete wall body(1) in thickness of 1 to 2mm before attaching a wall paper(3) thereon.

Description

삼림욕 효과를 갖는 천연광물질 미장재.{Coationg in minerals which improves the interior air quality}Natural mineral plaster with forest bath effect. {Coationg in minerals which improves the interior air quality}

도 1은 본 발명의 일실시예로서 미장재를 시공한 상태의 벽면의 분해사시도.1 is an exploded perspective view of the wall surface of the plastering state as an embodiment of the present invention.

도 2는 본 발명의 일실시예로서 미장재를 시공한 상태의 벽면의 단면도.Figure 2 is a cross-sectional view of the wall surface of the plastering state as an embodiment of the present invention.

*도면의 주요 부호에 대한 설명** Description of Major Symbols in Drawings *

1: 벽체 2: 미장재 3: 벽지1: wall 2: plastering 3: wallpaper

본 발명은 삼림욕 효과를 갖는 천연광물질 미장재에 관한 것으로, 더욱 상세하게는 이산화규소, 산화알루미늄, 산화칼륨, 산화철, 이산화티탄, 게르마늄 등으로 되는 천연광물질에 바인더를 혼합하여 벽면에 시공함으로써, 실내 공기 중의 산소농도를 자연 휴양림 수준인 20.5∼21.5% 수준으로 향상시킬 수 있도록 한 것이다.The present invention relates to a natural mineral plaster having a forest bath effect, and more particularly, by mixing a binder with natural minerals made of silicon dioxide, aluminum oxide, potassium oxide, iron oxide, titanium dioxide, germanium, etc. The oxygen concentration in the air can be improved to 20.5 ~ 21.5%, the level of natural recreation forest.

일반적으로 자갈, 모래, 시멘트 및 물로 되는 레미콘이나 모래와 시멘트 및 물로만 되는 모르타르는, 그것들로 건축물을 시공했을 때 시공시의 작업자들에게나 시공 후 그 건물에 입주하여 그 건물을 이용하는 사람들에게는, 그 조성물에 섞여 있는 각종 중금속, 세균 등 유해 물질들에 의해서 인체에 해를 입고 있으나, 사람들은 그것을 모르고 위해(危害)를 입은 채 지나치고 있는 실정이다.In general, concrete or gravel made of gravel, sand, cement and water, or mortar made only of sand and cement and water, are used by workers during construction and by those who move into and use the building after construction. The human body is harmed by harmful substances such as various heavy metals and bacteria mixed in the composition, but people do not know it and are overly harmed.

이러한 위해를 좀더 예방하기 위한 기술이 실용신안등록 제20-0341079호인 집열 및 집진기능을 갖는 공기정화 통합시스템과, 실용신안등록 제20-0341903호인 음이온 발생장치 및 실용신안등록 제20-0339856호인 이온변환증폭기를 갖는 음이온 발생장치에 소개되었다..The technology for further preventing such hazards is an integrated air purifying system having the function of collecting and collecting dust, utility model registration No. 20-0341079, anion generator and utility model registration No. 20-0339856, utility model registration No. 20-0341903. An anion generator with a conversion amplifier was introduced.

상기한 기술 등은 일반적으로 유기물질(VOC) 제거를 주제로 하여, 공기 정화기 등 공기의 순환 및 여과를 통하여 실내 공기의 청정도를 유지하여 왔으나, 소모성 부품의 교체 및 고장 등의 이유로 지속적인 성능발현에 문제점이 있는 것으로 알려져 있다. 아울러 에너지의 소모 및 소음의 발생 등 부가 2차 오염요소가 내재된 방안인 것일 뿐만 아니라, 전기 장치가 여러 곳에 설치되어 산소발생 효과보다는 전자파로 인한 피해를 주는 문제점이 있는 것이었다.The above-described technologies have generally maintained the cleanliness of indoor air through the circulation and filtration of air, such as air purifiers, with the theme of removing organic substances (VOC). It is known to have a problem. In addition, not only the secondary secondary contaminants such as energy consumption and noise generation are inherent, but also electrical devices are installed in various places, which causes damage due to electromagnetic waves rather than oxygen generation effects.

한편, 산소가 인체에 미치는 영향에 대해 설명하면 다음과 같다.On the other hand, when the effect of oxygen on the human body is described as follows.

우리 몸을 지배하는 중추신경계의 하나인 뇌는 약 145억 개의 뇌세포로 이루어져 있으며, 휴식을 취하고 있을지라도 많은 양의 산소를 필요로 한다. 또한, 뇌로의 산소 유입은 혈액에 의하여 이루어지는데, 하루 평균 약 2,000리터의 혈액이 뇌로 유입되어 산소를 공급하는 것이다. 이는 인체의 총 혈액양의 400배에 달하는 값으로 뇌에 산소를 공급하기 위해서 이렇게 막대한 양의 혈액 순환이 이루어지는 것이다.The brain, one of the central nervous systems that dominates our bodies, is made up of about 14.5 billion brain cells and needs a lot of oxygen, even at rest. In addition, the inflow of oxygen into the brain is made by the blood, and an average of about 2,000 liters of blood flows into the brain to supply oxygen. This is about 400 times the total amount of blood in the human body, so that a tremendous amount of blood circulation takes place to supply oxygen to the brain.

따라서, 혈액순환이 막히거나 혈액 내 산소부족으로 뇌의 산소공급이 원활하지 않는 경우에 뇌의 기능에 중대한 장애를 일으키게 된다. 졸도를 할 때 쓰러지는 이유는 뇌로의 혈액공급을 원활히 하기 위함이며, 흔히 중풍이라 부르는 뇌졸증의 흔한 원인도 뇌의 혈액순환 장애에 의한 산소공급 부족으로 뇌세포의 파괴를 가져온 것이다.Therefore, when the blood circulation is blocked or the oxygen supply of the brain is not smooth due to the lack of oxygen in the blood, it causes a serious obstacle to the function of the brain. The reason for the fall of fainting is to facilitate the blood supply to the brain, and the common cause of stroke, commonly called stroke, is the destruction of brain cells due to the lack of oxygen supply due to the brain's blood circulation disorder.

또한, 생물의 에너지 생성방법 중 하나가 호흡인 데, 에너지 생성에 필요한 산소를 들이마시고 반응 경과물인 탄산가스를 내보내는 기관이 폐이다. 이때, 혈액속의 산소는 각각의 세포 소기관에서 우리가 먹은 음식과 결합하여 에너지를 생성하는 데 쓰이고, 에너지 생성 결과 나타난 탄산가스는 우리 몸에 해롭기 때문에 혈액을 통해 폐로 가서 몸 밖으로 배출되는 것이다. In addition, one of the energy generating methods of living organisms is the respiration. The lungs inhale oxygen necessary for energy generation and emit carbon dioxide gas, which is a reaction product. At this time, the oxygen in the blood is used to produce energy by combining with the food we ate in each organelle, and carbon dioxide gas produced as a result of the energy is harmful to our body and goes through the blood to the lungs and is discharged out of the body.

따라서, 폐의 이상으로 인한 호흡 곤란이 치명적인 이유는 우리 몸에 필요한 산소가 부족하고 해로운 탄산가스가 축적되기 때문이다. 그리고 혈액 중에 산소가 증가한다는 것은 산소를 운반하는 적혈구의 수가 늘어나는 것을 말하며, 혈액양이 증가해 다량의 혈액이 혈관 안을 흐르게 되는 것이다. 이때, 혈액은 혈관 내벽에 부착된 콜레스테롤 등의 불순물을 씻어버리고 정화하여 우리 몸을 정상적으로 만드는 것이다.Therefore, the difficulty in breathing due to abnormal lungs is fatal because the body lacks necessary oxygen and harmful carbon dioxide accumulates. In addition, the increase in oxygen in the blood refers to the increase in the number of red blood cells that carry oxygen, the amount of blood is increased and a large amount of blood flows through the blood vessels. At this time, the blood washes and cleanses impurities such as cholesterol attached to the inner wall of blood vessels to make our body normal.

또한, 알콜과 산소 역시 매우 밀접한 관계를 가지고 있는 바, 술의 알콜은 아세트알데히드로 분해되고 이것은 다시 탄산과 물로 재분해된다. 즉, 술을 많이 마실수록 산소도 더 필요하게 되는 것이다. 음주 후에 산소가 불충분하면 아세트알데히드는 분해되지 않은 채로 남아 있게 되어 두통을 유발하게 되고, 졸음이 오거나 숙취 등의 현상이 나타나게 되는 데, 이러한 현상들은 일종의 산소부족현상이라고 볼 수 있다. 실제로, 일본의 한 박사는 20명의 학생들에게 30분동안 180cc의 위스키를 마시게 한 후 혈액 속의 산소량을 측정하는 테스트를 통해 음주 후에 혈액 산소량이 낮음을 발견하였다. 또한, 음주 후 20분이 지나 산소를 공급하고 다시 혈중 산소량을 측정하니 음주 직후보다 혈중 산소량이 증가한 것이다. 뇌파도 측정해 보았는데 산소가 알콜에 의한 뇌기능 감소를 회복시켜준다는 결과를 얻게 되었다.In addition, alcohol and oxygen also have a very close relationship: alcohol of alcohol is decomposed into acetaldehyde, which is re-decomposed into carbonic acid and water. In other words, the more you drink, the more oxygen you need. Insufficient oxygen after drinking alcohol causes acetaldehyde to remain intact, causing headaches, resulting in drowsiness or hangovers, which can be seen as a type of oxygen deficiency. Indeed, a Japanese doctor found that 20 students drank 180 cc of whiskey for 30 minutes and then tested for blood oxygen levels to find that the blood oxygen level was low after drinking. In addition, 20 minutes after drinking the oxygen supply and the blood oxygen again measured the oxygen content of the blood than immediately after drinking. EEG was also measured, and oxygen was found to restore alcohol-induced brain function decline.

그리고, 배기가스에 의한 중독은 산소를 마심으로서 회복될 수 있다는 것이 밝혀져, 순수한 산소를 마시는 것이 유독가스에 의한 치료책으로 여겨질 수 있게 되었다. 배기가스를 마신 사람들은 술에 취했을 때의 파형과 비슷한 의식 상실 상태의 뇌파에 가까워지는 것으로 확인되었다. 이들에게 산소를 5∼10분간 흡입시키고 다시 뇌파를 측정하여 신체가 정상화되고 작업능력이 또한 향상됨이 밝혀졌다.In addition, it has been found that poisoning by exhaust gas can be recovered by drinking oxygen, so that drinking pure oxygen can be considered as a cure by toxic gas. Those who drank the exhaust gas were found to be close to an unconscious brainwave, similar to the waveform of drunkenness. They inhaled oxygen for 5 to 10 minutes and measured the brain waves again to find that the body was normalized and workability was also improved.

또한, 담배 연기 중에는 각종 유해 물질이 포함되어 있으며, 특히 일산화탄소는 자동차의 배기가스에 달하는 농도가 포함되어 있다. 일산화탄소는 헤모글로빈 과의 결합력이 산소보다 200배나 높아 결과적으로 산소가 헤모글로빈과 결합하는 것을 방해하여 산소 수송 능력이 저하시킨다. 더욱이, 일산화탄소와 결합한 헤모글로빈은 산이 각 조직에 도달해 산소를 분리할 때에 산소와 결합한 헤모글로빈을 방해하는 역할을 하는 것이다. 운동량이 활발한 20∼30세의 경우라도 애연가라면 담배로부터 일산화탄소를 흡수함으로서 산소공급이 2∼3배 줄어들게 된다.In addition, various types of harmful substances are contained in cigarette smoke, and carbon monoxide, in particular, contains concentrations that reach exhaust gases of automobiles. Carbon monoxide has a binding force with hemoglobin 200 times higher than that of oxygen, and as a result, oxygen is prevented from binding to hemoglobin, resulting in decreased oxygen transport capacity. Moreover, hemoglobin combined with carbon monoxide plays a role in interfering with oxygen bound hemoglobin when acid reaches each tissue to separate oxygen. Even if you are 20 to 30 years of active momentum, if you are a smoker, your oxygen supply will be reduced 2-3 times by absorbing carbon monoxide from your cigarettes.

그리고, 혈압이 높은 사람의 1/2은 신경질적이며 호흡이 빠르고 리듬도 불규칙함으로 호흡은 혈압과 어느 정도 관계가 있는 것이다. 헤모글로빈의 산소 결합능력은 혈중 pH값이 떨어지면 헤모글로빈은 산소를 쉽게 분리하여 조직으로 산소를 공급하게 된다. 산소를 마시는 것이 혈압을 안정시킨다는 것은 과학적으로 충분히 해명된 메카니즘은 아니다. 하지만 산소를 들이마심으로서 혈압을 조절하는 중추 신경계에 좋은 영향을 주며, 자율신경의 활발한 움직임으로 혈관이 확장되고 헤모글로빈의 움직임을 보다 활발하게 한다는 추측은 성립된다.In addition, half of people with high blood pressure are nervous, and breathing is fast and rhythm is irregular, so breathing is somewhat related to blood pressure. The oxygen binding capacity of hemoglobin is when the pH of the blood drops, hemoglobin easily separates oxygen and supplies oxygen to tissues. Drinking oxygen to stabilize blood pressure is not a scientifically well understood mechanism. However, inhaling oxygen has a good effect on the central nervous system, which regulates blood pressure, and speculation is made that the vigorous movement of autonomic nerves expands blood vessels and makes hemoglobin more active.

당뇨병 환자에게 필요한 운동은 유산소 운동이다. 대화를 나눌 수 있을 정도로 가벼운 운동을 일정시간 계속하면 혈액 중의 당과 중성지방 값이 내려가는데, 이는 유산소 운동 시 에너지 원천으로 당과 중성지방이 이용되기 때문이다. 반면 산소의 공급이 없어도 이루어지는 운동인 무산소 운동은 오히려 혈당값을 올리게 되는데 100m 단거리 달리기 같은 운동이 이에 속한다. 이러한 운동의 경우 근육 속의 글리코겐이 에너지의 원천으로 이용되기 때문이다.Exercise needed for diabetics is aerobic exercise. If you continue to exercise light enough to talk for a certain period of time, the sugar and triglycerides in the blood will be lowered because the use of sugar and triglycerides as an energy source during aerobic exercise. On the other hand, the anaerobic exercise, which is an exercise without oxygen supply, raises the blood sugar value, such as a 100m short run. This is because glycogen in the muscle is used as a source of energy.

그리고, 피부의 표면에 있는 땀샘과 표피 지방선으로부터 계속해서 수분과 기름성분이 신체 밖으로 배출되고 체내에 불필요한 노폐물을 외부로 분비하는 데 탄산가스도 피부호흡을 통하여 끊임없이 외부로 배출된다. 신선한 산소를 공급하는 것은 구석구석의 세포에 대사활동을 활발하게 하여 체내의 일산화탄소, 이산화탄소, 기타 불순물의 배설을 촉진하고 모든 기능의 조절을 하는 것이다. 이 때문에 충분한 산소의 공급은 자연스럽게 피부의 혈액순환을 원활하게 하여 건강하고 탄력있는 피부가 만들어지게 된다. 한방에서 피부의 트러블을 신진대사의 불순으로 설명하는 것도 이 때문이다. 또한 최근에는 피부에 직접적인 산소공급을 통해 피부주름을 없애는 기술도 개발되었다.In addition, water and oil components continue to be discharged from the body from sweat glands and epidermal fatty glands on the surface of the skin and secrete unnecessary wastes into the body to the outside. Carbon dioxide is also continuously discharged to the outside through skin respiration. The supply of fresh oxygen promotes the metabolism of cells in every corner of the cell, promoting the excretion of carbon monoxide, carbon dioxide and other impurities in the body and regulating all functions. For this reason, the supply of sufficient oxygen naturally facilitates the blood circulation of the skin, making the skin healthy and elastic. This is why it is because of the metabolic impurity of skin trouble in one shot. Recently, a technology for removing skin wrinkles by directly supplying oxygen to the skin has also been developed.

또한, 만성피로를 회복하는 길은 적당한 운동을 통해 신체의 리듬을 유지시키는 데 있고, 우리의 몸은 산소가 있는 경우와 없는 경우 다른 패턴에 의해 에너지를 생성한다. 산소가 없는 경우 생성된 에너지를 무산소에너지라 하는데, 이 힘은 강하지만 내구성이 짧아 1∼2분이 경과되면 체내에 젖산이 쌓이게 되고 에너지는 고갈된다. 이때 쌓인 젖산이 바로 피로를 유발하는 요소이다. 하지만 이 순간에 산소가 공급되면 축적되었던 젖산이 분해되어 새로운 에너지원으로 재생성되는데 이것이 유산소에너지라고 한다. 따라서, 유산소 에너지는 산소공급에 의해 스테미너가 오래 지속될 수 있다는 것을 의미한다.In addition, the way to recover from chronic fatigue is to maintain the body's rhythm through proper exercise, and our body generates energy by different patterns with and without oxygen. In the absence of oxygen, the generated energy is called anoxic energy. This strength is strong, but the durability is short, and after 1 to 2 minutes, lactic acid accumulates in the body and energy is depleted. The accumulated lactic acid is the factor that causes fatigue. However, when oxygen is supplied at this moment, the accumulated lactic acid is decomposed and regenerated as a new energy source, which is called aerobic energy. Thus, aerobic energy means that stamina can be sustained by oxygen supply.

따라서, 본 발명의 목적은 상기한 바와 같이 인체에 중요한 역할을 하는 산소의 공급을 원활히 하기 위하여, 이산화규소, 산화알루미늄, 산화칼륨, 산화철, 이산화티탄, 게르마늄 등으로 되는 천연광물질에 바인더를 혼합하여 벽면에 시공함으로써, 실내 공기 중의 산소농도를 자연 휴양림 수준인 20.5∼21.5% 수준으로 향상시킬 수 있도록 하여, 신체의 신진대사를 원활히 할 수 있도록 하고, 신체 건강유지에 도움을 줄 수 있도록 하는 삼림욕 효과를 갖는 천연광물질 미장재를 제공함에 있다.Accordingly, an object of the present invention is to mix the binder with a natural mineral material made of silicon dioxide, aluminum oxide, potassium oxide, iron oxide, titanium dioxide, germanium, etc. in order to facilitate the supply of oxygen, which plays an important role in the human body as described above. By installing it on the wall, it is possible to improve the oxygen concentration in the indoor air to 20.5 ~ 21.5%, which is the level of natural recreation forest, so that the metabolism of the body can be smoothed, and the forest bath effect can help to maintain the physical health. In providing a natural mineral plaster having a.

상기한 목적을 달성하기 위한 본 발명의 삼림욕 효과를 갖는 천연광물질 미장재는,Natural mineral plaster having a forest bath effect of the present invention for achieving the above object,

천연광물질분말 35∼40중량%에 바인더 60∼65중량%를 혼합하여 미장재를 구성하되,A plastering material is formed by mixing 60 to 65% by weight of binder with 35 to 40% by weight of natural mineral powder.

상기 천연광물질분말은 이산화규소 73∼78중량%, 산화알루미늄 8∼10중량%, 산화칼륨 4∼6중량%, 산화철 9∼11중량% 및 이산화티탄 0.4∼0.6중량%로 이루어지는 것을 특징으로 한다.The natural mineral powder is characterized by consisting of 73 to 78% by weight of silicon dioxide, 8 to 10% by weight of aluminum oxide, 4 to 6% by weight of potassium oxide, 9 to 11% by weight of iron oxide, and 0.4 to 0.6% by weight of titanium dioxide.

그리고, 상기 천연광물질분말에는 게르마늄 1ppm이 추가로 포함되는 것을 특징으로 한다.In addition, the natural mineral powder is characterized in that it further comprises germanium 1ppm.

그리고, 상기 천연광물질분말의 방사선 핵종분석 결과는 0.5∼1Bq인 것을 특징으로 한다.In addition, the radionuclide analysis result of the natural mineral powder is characterized in that 0.5 ~ 1Bq.

삭제delete

이하, 본 발명을 상세히 설명하도록 한다.Hereinafter, the present invention will be described in detail.

본 발명에 의한 산소발생을 이해하기 위해 원자의 성격과 주기율을 간단히 설명하면, 수소는 2개의 수소전자와 그 궤도를 도는 (-)전자로 구성되어 안정을 유지하는 데, 모든 원소는 3번 궤도부터 8개의 전자를 갖추어 안정된 상태를 유지하려는 성질을 갖고 있다. 예를들어 염화나트류(NaCl)을 분석해 보면 나트륨의 3번 궤도에는 전자가 1개만 존재한다. 반면, 염소의 3번 궤도에는 7개의 전자가 존재하므로 나트륨의 전자 1개를 흡수하면 안정을 찾을 수 있으므로, 나트륨과 쉽게 결합하여 안정을 유지한다. 공기 중의 질소가 산소보다 4배 많지만, 전자의 산소에 대한 친화력은 3.80인데 비해, 질소의 전자친화력은 0.04로 질소가 음이온이 되는 확률은 산소의 1/100이므로 공기 중의 음이온은 산소 음이온인 것이다.Briefly describing the nature and periodicity of atoms in order to understand the oxygen generation according to the present invention, hydrogen is composed of two hydrogen electrons and (-) electrons orbiting their orbits to maintain stability. It has 8 electrons and it has a property to maintain stable state. For example, in the analysis of sodium chloride (NaCl), only one electron exists in orbit 3 of sodium. On the other hand, since seven electrons exist in the orbit 3 of chlorine, absorption of one electron of sodium can find stability, so it is easily combined with sodium to maintain stability. Although nitrogen in the air is four times more than oxygen, the electron has affinity for oxygen of 3.80, whereas the electron affinity of nitrogen is 0.04, and the probability that nitrogen becomes an anion is 1/100 of oxygen, so the anion in the air is an oxygen anion.

본원 발명의 삼림욕 효능은 천연광물질분말에 바인더를 혼합하여 미장처리함으로써 이루어지는 데, 상기 천연광물질분말은 공기 중에 음이온을 공급하고 원적외선을 방사하여 삼림욕 효능을 갖도록 하는 것이며,The forest bath effect of the present invention is achieved by mixing the natural mineral powder with a binder and the plastering process, the natural mineral powder is to supply the anion in the air and radiate far infrared rays to have a forest bath effect,

바인더는, 천연광물질분말의 상호 접착을 돕고 미장재로서 벽면에 시공하였을 경우 강도와 접착력을 유지하기 위함이다.The binder is intended to help the mutual adhesion of the natural mineral powder and to maintain the strength and adhesive strength when applied to the wall as a plastering material.

상기 천연광물질분말과 바인더의 혼합비는 천연광물질분말 35∼40중량%에 바인더 60∼65중량%를 혼합하는 것이 가장 바람직한 바, 천연광물질이 40중량%를 초과하면 천연광물질이 과량이 되어 접착력이 떨어지게 되는 등의 문제점이 있고, 35중량% 미만이 되면 천연광물질을 투입하는 효과, 즉 삼림욕의 효능이 최대로 발휘되지 않기 때문이다.The mixing ratio of the natural mineral powder and the binder is most preferably mixed with 60 to 65% by weight of the binder and 35 to 40% by weight of the natural mineral powder, when the natural mineral is more than 40% by weight of the natural mineral is excessive to reduce the adhesive strength There is a problem such as, and less than 35% by weight because the effect of the input of natural minerals, that is, the efficacy of the forest bath is not exhibited to the maximum.

그리고, 상기 천연광물질분말로는 이산화규소 72∼75중량%, 산화알루미늄 8∼10중량%, 산화칼륨 4∼6중량%, 산화철 9∼11중량% 및 이산화티탄 0.4∼0.6중량%로 이루어지는 것을 사용하는 것이 바람직하며, 여기에 추가적으로 전체 천연광물질분말을 기준으로 게르마늄 1ppm이 추가로 포함되는 것을 특징으로 한다.The natural mineral powder is composed of 72 to 75% by weight of silicon dioxide, 8 to 10% by weight of aluminum oxide, 4 to 6% by weight of potassium oxide, 9 to 11% by weight of iron oxide, and 0.4 to 0.6% by weight of titanium dioxide. Preferably, it is additionally characterized in that it further comprises 1 ppm of germanium based on the entire natural mineral powder.

상기 이산화규소(SiO2)는 순수한 것은 무색 투명한 고체로, 분자량 60.09이다. 천연산은 불순물을 함유하므로 불투명, 또는 유색인 것도 있다. 규소를 4개의 산소가 둘러싼 정사면체형인 SiO4를 기본단위로 하고, 모든 산소를 규소가 공유하여 3차원적으로 연결된 거대 분자구조를 가지고 있는 것으로, 음이온 방사 능력이 탁 월한 것이다. 상기 이산화규소의 배합비가 73중량% 미만이면 이산화규소의 방사 능력이 줄어들게 되고, 78중량%를 초과하면 과량이 되어 다른 광물질의 배합비가 줄어들게 되므로, 73∼78중량%를 배합하는 것이 바람직하다.The silicon dioxide (SiO 2 ) is a pure, colorless transparent solid, having a molecular weight of 60.09. Natural acids contain impurities, so they may be opaque or colored. Silicon is a tetrahedral SiO 4, which is surrounded by four oxygens, and has a large molecular structure in which all oxygen is shared by silicon and connected three-dimensionally. When the blending ratio of silicon dioxide is less than 73% by weight, the radiation capacity of silicon dioxide is reduced, and when the blending ratio exceeds 78% by weight, the blending ratio of other minerals is reduced, so it is preferable to blend 73 to 78% by weight.

상기 산화알루미늄(Al2O3)은, 광물질의 효능인 삼림욕효과를 돕는 것은 물론 난연재로서의 역할 또한 하는 것으로, 산화알루미늄이 8중량% 미만이 되면 그 효과가 미미하게 되고, 10중량%를 초과하더라도 그 효과가 더 증진되지 않으므로, 그 배합비를 8∼10중량%로 하는 것이 바람직하다.The aluminum oxide (Al 2 O 3 ), as well as the role of flame retardant to help the forest bath effect of the efficacy of minerals, when the aluminum oxide is less than 8% by weight, the effect is negligible, even if it exceeds 10% by weight Since the effect is not enhanced further, it is preferable to make the compounding ratio into 8 to 10 weight%.

상기 산화칼륨(K2O)은, 음이온 방사는 물론 흡습성을 갖는 광물질로서, 물과 반응하여 KOH와 O2로 분해 되는 것이다. 상기 산화칼륨이 4중량% 미만이 되면 흡습력이 부족하게 되고 6중량%를 초과하면 과량이 되므로, 그 배합비를 4∼6중량%로 하는 것이 바람직하다.The potassium oxide (K 2 O) is a mineral having hygroscopicity as well as anion radiation, and reacts with water to decompose into KOH and O 2 . If the potassium oxide is less than 4% by weight, the hygroscopicity is insufficient. If the potassium oxide is more than 6% by weight, it is excessive. Therefore, the blending ratio is preferably 4 to 6% by weight.

그리고, 상기 산화철(Fe2O3)은 계속적으로 음이온을 방사하는 물질로, 산화철의 배합비가 9중량% 미만이 되면 산화철의 효과가 미미하게 되고 11중량%를 초과하면 과량이되므로, 그 배합비를 9∼11중량%로 하는 것이 바람직하다.In addition, the iron oxide (Fe 2 O 3 ) is a substance that continuously emits anions, the iron oxide compounding ratio is less than 9% by weight, the effect of the iron oxide is insignificant, if it exceeds 11% by weight, the compounding ratio It is preferable to set it as 9-11 weight%.

또한, 이산화티탄(TiO2)는 광촉매로서 가장 많이 사용되고 있는 물질로서, 반도체의 특성을 가지고 있는데, 반도체는 밴드 갭(band gap) 이상의 에너지를 외부에서 받으면 전자(e-), 전공(h+)쌍을 발산하고, 이산화티탄에 밴드 갭(band gap)이상의 에너지를 갖는 빛을 조사하면, 내부에 전자(e-), 전공(h+)쌍이 생성되고 이것이 광촉매 표면에 흡착된 유기물질과 반응해 산화, 환원반응을 일으켜 흡착된 물질을 분해하게 되는 것이다. 상기 산화환원작용은 이산화티탄에서 생성된 전자(e-), 전공(h+)쌍이 공기중의 산소(O2) 및 물(H2O)과 반응을 일으켜 이산화티탄 표면에 슈퍼옥사이드 음이온(O2-)와 수산라디칼(OH-)로 된 2종의 활성산소를 생성하게 되는 것으로서, 이산화티탄이 0.4중량% 미만이 되면 그 효과각 미미하게 되고 0.6중량%를 초과하면 과량이 되므로, 그 배합비를 0.4∼0.6중량%로 하는 것이 가장 바람직하다.In addition, titanium dioxide (TiO 2 ) is a material most commonly used as a photocatalyst, and has the characteristics of a semiconductor. A semiconductor has an electron (e-) and an electron (h +) pair when it receives energy above a band gap from the outside. When irradiated with light having energy above the band gap to titanium dioxide, electrons (e-) and electron (h +) pairs are formed inside, which react with the organic material adsorbed on the surface of the photocatalyst to oxidize, It causes a reduction reaction to decompose the adsorbed material. The redox action causes the electron (e-) and electron (h +) pairs produced from titanium dioxide to react with oxygen (O 2 ) and water (H 2 O) in the air, resulting in superoxide anion (O2- ) And two kinds of free radicals consisting of hydroxyl radical (OH-). When titanium dioxide is less than 0.4% by weight, the effect is insignificant, and when it exceeds 0.6% by weight, the compounding ratio is 0.4. Most preferably, it is-0.6 weight%.

또한, 상기 광물질분말 전체를 기준으로 게르마늄(Ge) 1ppm을 추가로 포함할 수도 있는 것으로, 상기 게르마늄은 음이온의 발생을 돕는 것은 물론, 항균, 항취작용을 하여 냄새제거에 탁월한 효과가 있도록 하는 것이다.In addition, germanium (Ge) may further include 1ppm of the mineral powder as a whole, the germanium is to help the generation of anions, as well as antibacterial, anti-odor action to have an excellent effect on the odor removal.

그리고, 상기 천연광물질분말의 방사선 핵종분석 결과는 0.5∼1Bq인 것이 바람직한 바, 방사선 핵종분석 결과가 1Bq 을 초과하면 인체에 위험을 줄 수 있기 때문이다.In addition, the radionuclide analysis result of the natural mineral powder is preferably 0.5 to 1Bq, because if the radionuclide analysis results exceed 1Bq, it may pose a danger to the human body.

상기와 같이 구성되는 미장재는, 도 1 및 도 2에서 알 수 있는 바와 같이, 콘크리트 벽체(1) 등에 미장재(2)를 1∼2mm의 두께로 코팅하고, 그 위에 벽지(3)를 시공하는 것으로서, 상기 미장재(2)의 코팅방법은 붓, 로울러 등으로 도포하거나 스프레이를 이용하여 분사하는 방법 등을 모두 이용할 수 있는 것으로, 그 방법을 제한하지 않는다.As shown in FIG. 1 and FIG. 2, the plastering material comprised as mentioned above coats the plastering material 2 with the thickness of 1-2 mm etc. in the concrete wall 1, etc., and constructs the wallpaper 3 on it. As the coating method of the plastering material (2) can be used both by applying a brush, a roller or the like, or spraying using a spray, etc., the method is not limited.

상기 미장재(2)를, 1∼2mm의 두께로 코팅하는 이유는 미장재(2)가 1mm 미만이 되면 미장재로서의 효과가 미미하게 되고, 2mm를 초과하면 콘크리트 벽면 시멘트 견출공정의 두께인 1∼2mm를 초과하게 되기 때문인 것으로, 시멘트 견출 공정을 미장재료 대체하기 위하여 1∼2mm의 두께로 코팅하는 것이 가장 바람직하다.The reason why the plastering material 2 is coated with a thickness of 1 to 2 mm is that when the plastering material 2 is less than 1 mm, the effect as a plastering material is insignificant. It is because it exceeds -2mm, it is most preferable to coat with a thickness of 1-2mm in order to replace the cement extraction process with the plastering material.

상기와 같이 되는 본 발명의 미장재 및 그 시공방법에 따르면, 실내공기의 농도를 쾌적한 상태로 유지하여 인체 건강유지에 도움을 줄 수 있도록 하는 것이다.According to the plastering and the construction method of the present invention as described above, to maintain the concentration of indoor air in a comfortable state to help maintain human health.

상기한 설명을 통해 분명히 알 수 있는 바와 같이, 본 발명의 삼림욕 효과를 갖는 천연광물질 미장재는 이산화규소, 산화알루미늄, 산화칼륨, 산화철, 이산화티탄, 게르마늄 등으로 되는 천연광물질에 바인더를 혼합하여 벽면에 시공함으로써, 실내 공기 중의 산소농도를 자연 휴양림 수준인 20.5∼21.5% 수준으로 향상시킬 수 있도록 하여, 신체의 신진대사를 원활히 할 수 있도록 하고, 신체 건강유지에 도움을 줄 수 있도록 하는 등의 유용한 효과를 제공한다.As can be clearly seen through the above description, the natural mineral plaster having the forest bath effect of the present invention is mixed with a natural mineral material made of silicon dioxide, aluminum oxide, potassium oxide, iron oxide, titanium dioxide, germanium and the like on the wall surface By constructing, it is possible to improve the oxygen concentration in indoor air to 20.5 ~ 21.5% level, which is the level of natural recreation forest, to facilitate the metabolism of the body, and to help maintain the body health. To provide.

Claims (4)

이산화규소 73~78중량%, 산화알루미늄 8~10중량%, 산화칼륨 4~6중량%, 산화철 9~11중량% 및 이산화티탄 0.4~0.6중량%로 이루어지는 천연광물질분말 35~40중량%에 바인더 60~65중량%를 혼합하여 미장재를 구성하되,Binder to 35-40 wt% of natural mineral powder consisting of 73-78 wt% of silicon dioxide, 8-10 wt% of aluminum oxide, 4-6 wt% of potassium oxide, 9-11 wt% of iron oxide, and 0.4-0.6 wt% of titanium dioxide Make up the plastering material by mixing 60-65% by weight, 상기 천연광물질분말에는 전체 천연광물질분말을 기준으로 게르마늄 1ppm이 추가로 포함되며, 상기 천연광물질분말의 방사선 핵종분석 결과는 0.5~1Bq인 것을 특징으로 하는 삼림욕 효과를 갖는 천연광물질 미장재.The natural mineral powder further comprises 1 ppm of germanium on the basis of the total natural mineral powder, the radionuclide analysis result of the natural mineral powder natural mineral plaster having a forest bath effect, characterized in that 0.5 ~ 1Bq. 삭제delete 삭제delete 삭제delete
KR1020060076994A 2006-08-16 2006-08-16 Coationg in minerals which improves the interior air quality KR100663261B1 (en)