KR100638110B1 - A manufacturing method of building materials using scrapped wood - Google Patents

A manufacturing method of building materials using scrapped wood Download PDF

Info

Publication number
KR100638110B1
KR100638110B1 KR1020040028043A KR20040028043A KR100638110B1 KR 100638110 B1 KR100638110 B1 KR 100638110B1 KR 1020040028043 A KR1020040028043 A KR 1020040028043A KR 20040028043 A KR20040028043 A KR 20040028043A KR 100638110 B1 KR100638110 B1 KR 100638110B1
Authority
KR
South Korea
Prior art keywords
wood
knots
defects
multilayer board
adhesive
Prior art date
Application number
KR1020040028043A
Other languages
Korean (ko)
Other versions
KR20050071321A (en
Inventor
홍기호
Original Assignee
홍기호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 홍기호 filed Critical 홍기호
Priority to KR1020040028043A priority Critical patent/KR100638110B1/en
Publication of KR20050071321A publication Critical patent/KR20050071321A/en
Application granted granted Critical
Publication of KR100638110B1 publication Critical patent/KR100638110B1/en

Abstract

본 발명은 폐목재를 적용하여 건축자재를 제조하는 방법에 관한 것으로, 상세하게는 슬라이스된 목재의 옹이 및 하자 부위를 분리하여 옹이 및 하자 부위 조각면을 형성하고, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면을 접착제 재질의 봉합사로 봉합하여 일정한 크기의 목재 단판을 형성하고, 상기 목재 단판을 같은 결로 적층으로 접착하고 일정한 온도와 압력으로 압착하여 목재 다층 보드를 형성하고, 상기 목재 다층 보드의 표면에 기판을 접착하는 과정으로 형성되어 폐목재인 옹이 및 하자 부위를 활용하여 고부가가치의 건축자재를 제조하도록 구성되는 폐목재를 이용한 건축자재의 제조 방법에 관한 것이다.The present invention relates to a method for manufacturing building materials by applying waste wood, and in detail, the knots and the defects of the sliced wood are separated to form the knots and the defects, and the fragments of the knots and the defects. The knots and flaws are sealed with a suture made of an adhesive material to form a wood veneer of a constant size, and the wood veneers are bonded by the same condensation lamination and pressed at a constant temperature and pressure to form a wood multilayer board, and the wood multilayer The present invention relates to a method of manufacturing building materials using waste wood, which is formed by adhering a substrate to a surface of a board and is configured to manufacture high value-added building materials by using knots and defects of waste wood.

폐목재, 건축자재, 옹이 부위, 하자 부위, 목재 다층 보드Waste wood, building materials, knots, defects, wood multilayer board

Description

폐목재를 이용한 건축자재의 제조 방법{A manufacturing method of building materials using scrapped wood}A manufacturing method of building materials using scrapped wood}

도 1은 목재 단판의 구성도1 is a block diagram of a wooden veneer

도 2는 목재 다층 보드의 구성도2 is a block diagram of a wood multilayer board

도 3은 건축자재의 구성도
도 4는 조각면의 결합도3 is a block diagram of building materials
4 is a coupling of the engraving surface

* 도면의 주요 부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

1 : 옹이 및 하자 부위 조각면1: engraving of the knots and defects

2 : 목재 단판2: wood veneer

3 : 목재 다층 보드3: wood multilayer board

4 : 기판4: substrate

5 : 봉합사5: suture

본 발명은 목재를 0.5 ∼ 1 ㎜의 두께로 슬라이스하고 그 옹이 및 하자 부위를 분리하여 옹이 및 하자 부위 조각면을 형성하는 과정과, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면을 접착제 재질의 봉합사로 봉합하여 상호간에 연결하여 일정한 크기의 목재 단판을 형성하는 과정과, 상기 목재 단판 다수매를 접착제로 접착하여 같은 결로 적층하고 일정한 온도와 압력으로 압착하여 목재 다층 보드를 형성하는 과정과, 상기 목재 다층 보드의 일 표면에 일정한 두께의 기판을 접착제로 접착하는 과정으로 구성되어 폐목재인 옹이 및 하자 부위를 활용하여 바닥재, 벽재, 천정재 등과 같은 고부가가치의 건축자재를 제조하므로서 목재 활용 비율을 크게 증가시키는 폐목재를 이용한 건축자재의 제조 방법에 관한 것이다.The present invention is a process of slicing wood to a thickness of 0.5 to 1 mm and separating the knots and defects to form the knots and defects engraving surface, and the knots and defects engraving surface and the knots and defects engraving surface adhesive Suture with a suture made of a material to connect to each other to form a wood veneer of a certain size, the process of adhering a plurality of the wood veneer with an adhesive and laminated in the same condensation and pressing at a constant temperature and pressure to form a wood multilayer board and In addition, the process of bonding a substrate of a certain thickness to one surface of the wood multilayer board with an adhesive, utilizing the knots and defects of the waste wood to manufacture high value-added building materials such as flooring, wall materials, ceiling materials, etc. It relates to a method of manufacturing building materials using waste wood to greatly increase the.

벌목된 원목에는 옹이 부위 뿐만 아니라 나무진, 변색, 부패, 훼손, 공동 등의 각종 하자 부위가 많이 존재한다.Logged wood has many defects such as knots, discoloration, decay, damage, and cavities.

따라서, 종래에는 목재 가공 공정에서 목재를 일정한 두께로 슬라이스하고 상기 슬라이스된 목재로부터 옹이 및 하자 부위를 제거하고 남은 부분만을 활용하여 베니어, 합판, 기타 목조 건축자재를 제조하며, 상기 목재 가공 과정에서 제거된 옹이 및 하자 부위는 폐기되거나 땔감으로 활용되기 때문에 원목에 대한 목재의 활용 비율이 평균 35 %에 불과하여 대량의 목재가 낭비되며, 이것은 결국 과다한 목재 소비로 연결된다는 문제점이 있다.Therefore, conventionally, in the wood processing process, the wood is sliced to a certain thickness, the knots and flaws are removed from the sliced wood, and only the remaining parts are used to manufacture veneers, plywood, and other wooden building materials, and the wood processing is removed. Since the knots and defects that have been used are discarded or used as firewood, the use ratio of wood to timber is only 35% on average, which causes a large amount of wood to be wasted, which leads to excessive wood consumption.

본 발명의 목적은 목재를 0.5 ∼ 1 ㎜ 두께로 슬라이스하고 그 옹이 및 하자 부위를 분리하여 옹이 및 하자 부위 조각면을 형성하고, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면을 접착제 재질의 봉합사로 봉합하여 일정한 크기의 목재 단판을 형성하고, 상기 목재 단판을 같은 결로 적층으로 접착하고 일정한 온도와 압력으로 압착하여 목재 다층 보드를 형성하고, 상기 목재 다층 보드의 일 표면에 일정한 두께의 기판을 접착하는 과정으로 구성되어 폐목재인 옹이 및 하자 부위를 활용하여 건축자재를 형성하는 폐목재를 이용한 건축자재의 제조 방법을 제공하는데 있다.An object of the present invention is to slice the wood into 0.5 ~ 1 mm thick and to separate the knots and defects to form the knots and defects engraving surface, and the knots and defects engraving surface and the knots and defects engraving surface adhesive material Suture with a suture to form a wood veneer of a constant size, the wood veneer is bonded with the same condensation lamination and pressed at a constant temperature and pressure to form a wood multilayer board, a substrate of a constant thickness on one surface of the wood multilayer board It is to provide a method of manufacturing a building material using the waste wood consisting of the process of gluing the wood to form the building material by using the knotty and defect parts of the waste wood.

본 발명의 폐목재를 이용한 건축자재의 제조 방법은 목재를 0.5 ∼ 1 ㎜의 두께로 슬라이스하고 그 옹이 및 하자 부위를 분리하여 옹이 및 하자 부위 조각면(1)을 형성하는 과정과, 상기 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)을 접착제 재질의 봉합사(5)로 봉합하여 상호간에 연결하여 일정한 크기의 목재 단판(2)을 형성하는 과정과, 상기 목재 단판(2) 다수매를 적층으로 접착하고 일정한 온도와 압력으로 압착하여 목재 다층 보드(3)를 형성하는 과정과, 상기 목재 다층 보드(3)의 일 표면에 일정한 두께의 기판(4)을 접착제로 접착하는 과정으로 구성되는 특징이 있다.The method for manufacturing building materials using the waste wood of the present invention comprises the steps of slicing the wood to a thickness of 0.5 to 1 mm and separating the knots and the flaws to form the knots and flaws of the engraving part (1), the knots and A process of forming a wooden end plate (2) of a constant size by stitching the flaw surface engraving surface (1) and the knots and flaw surface engraving surface (1) with an suture (5) made of an adhesive material and connecting them to each other; 2) adhering a plurality of sheets in a stack and pressing them at a constant temperature and pressure to form a wood multilayer board 3, and adhering a substrate 4 of a constant thickness to one surface of the wood multilayer board 3 with an adhesive. It is characterized by the process of doing.

또한, 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)의 변을 접착제로 접합하여 상호간에 연결하여 일정한 크기의 목재 단판(2)을 구성한다.In addition, the sides of the knot and defect portion engraving surface (1) and the knot and defect portion engraving surface (1) are bonded to each other by connecting to each other to form a wooden end plate 2 of a constant size.

또한, 서로 다른 수종의 목재 단판(2) 다수매를 접착제로 접착하여 적층하고 일정한 온도와 압력으로 압착하여 목재 다층 보드(3)를 구성한다.In addition, a plurality of different types of wood veneer (2) is bonded by laminating with an adhesive and pressed to a certain temperature and pressure to constitute a wood multilayer board (3).

도 1은 목재 단판의 구성을 도시한 것이고 도 2는 목재 다층 보드의 구성을 도시한 것이고 도 3은 완성된 건축자재의 구성을 도시한 것이고 도 4는 옹이 및 하자 부위 조각면의 결합 구조의 실시예를 도시한 것이다.Figure 1 shows the configuration of the wood veneer, Figure 2 shows the configuration of the wood multilayer board, Figure 3 shows the configuration of the finished building material and Figure 4 shows the implementation of the combined structure of the knots and defects engraving An example is shown.

원목을 1차 가공한 목재를 0.5 ∼ 1 ㎜의 두께로 슬라이스하고, 상기와 같이 슬라이스된 목재로부터 옹이 및 각종 하자가 존재하는 부위를 분리하여 다양한 크 기와 형상의 옹이 및 하자 부위 조각면(1)을 형성한다. 목재를 0.5 ㎜ 미만의 두께로 슬라이스하면 슬라이스된 목재 또는 옹이 및 하자 부위 조각면(1)이 훼손되기 쉽고, 1 ㎜를 초과하는 두께로 슬라이스하면 옹이 및 하자 부위 조각면(1)을 접착제 재질의 봉합사로 봉합하는 작업이 곤란해진다.Sliced wood with primary processing of wood to a thickness of 0.5 to 1 mm, and separating knots and various defects from the sliced wood as described above, and cutting pieces of knots and defects of various sizes and shapes (1) To form. If the wood is sliced to a thickness of less than 0.5 mm, the sliced wood or knot and flaw face pieces 1 are easily damaged. If the slice is more than 1 mm thick, the knot and flaw face pieces 1 are made of adhesive material. The work of suturing with a suture becomes difficult.

상기와 같이 형성된 다양한 크기와 형상의 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)을 봉합사(5)로 봉합하여 상호간에 연결하고, 이러한 과정을 반복하여 일정한 크기의 목재 단판(2)을 형성한다. 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)을 봉합하여 연결하는 봉합사(5)는 접착제 재질로 구성되며, 옹이 및 하자 부위 조각면(1)을 봉합하여 연결하는 접착제 재질의 봉합사(5)는 같은 결로 적층된 목재 단판(2)을 일정 온도와 압력으로 압착하는 과정에서 용융되어 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1) 사이로 침투하여 경화되므로 상기 접착제 재질의 봉합사(5)의 이음 표시가 노출되지 않으며 적층된 목재 다층 보드(3)의 강도가 배가된다.The knots and defects of the various sizes and shapes formed as described above (1) and the knots and defects of the engraving (1) by suture (5) and connected to each other, and repeating this process wood of constant size The end plate 2 is formed. The suture 5 which sutures and connects the knots and the flap part 1 to the knot and the flaw part 1 is made of an adhesive material, and the adhesive to suture and connect the knots and the flaw part 1 to the flaw part. Suture (5) of the material is melted in the process of pressing the laminated wood veneer (2) with the same condensation at a constant temperature and pressure to penetrate between the knot and defect portion engraving surface (1) and the knot and defect portion engraving surface (1) Since it hardens, the joint mark of the suture 5 of the said adhesive material is not exposed, and the strength of the laminated wood multilayer board 3 is doubled.

또는, 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)의 변을 접착제로 접합하여 상호간에 연결하므로서 일정한 크기의 목재 단판(2)을 구성할 수 있다.Alternatively, by joining the knots and the defect portion engraving surface 1 and the sides of the knots and the defect portion engraving surface 1 with an adhesive, it is possible to configure a wooden end plate 2 of a constant size.

상기와 같이 일정한 크기로 봉합된 목재 단판(2) 다수매를 적층으로 접착하고, 적층된 목재 단판(2)을 즉시 일정한 온도와 압력으로 압착하여 목재 다층 보드(3)를 형성한다.A plurality of wood end plates (2) sealed to a predetermined size as described above are bonded in a stack, and the laminated wood end plates (2) are immediately pressed to a constant temperature and pressure to form a wood multilayer board (3).

구체적으로, 목재 단판(2)의 표면에 접착제를 일정한 두께로 도포하고 다른 목재 단판(2)을 접착하고, 이러한 과정을 반복하여 다수매의 목재 단판(2)을 같은 결로 차례로 적층하며, 적층된 목재 단판(2)을 롤러 사이로 통과시켜서 일정한 압력으로 압착하여 목재 다층 보드(3)를 형성한다. 목재 단판(2)의 표면에 도포된 접착제는 같은 결로 적층된 목재 단판(2)을 일정 온도와 압력으로 압착하는 과정에서 용융되어 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)의 변 사이로 침투하여 경화된다.Specifically, by applying an adhesive to the surface of the wood veneer (2) to a certain thickness and bonding the other wood veneer (2), and repeating this process to stack a plurality of wood veneer (2) in the same condensation, laminated The wood end plate 2 is passed through the rollers and compressed at a constant pressure to form a wood multilayer board 3. The adhesive applied to the surface of the wood veneer (2) is melted in the process of pressing the laminated wood veneer (2) at the same temperature and pressure at a constant temperature and pressure, so that the knot and flaw engraving surface (1) and the knot and flaw engraving surface ( It penetrates between the sides of 1) and hardens.

목재 다층 보드(3)으로 적층되는 목재 단판(2)의 수효가 3 매 미만이면 목재 다층 보드(3)의 강도와 내구성의 부족으로 인하여 건축자재로서의 적용이 불가하며, 적층되는 목재 단판(2)의 수효가 11 매를 초과하면 필요 이상의 적층 공정이 발생하여 목재 다층 보드(3)의 제조원가가 상승하여 경제성이 저하된다.If the number of wood veneers 2 laminated by the wood multilayer board 3 is less than three sheets, it cannot be applied as a building material due to the lack of strength and durability of the wood multilayer board 3, and the laminated wood veneer 2 When the number of sheets exceeds 11 sheets, more than necessary lamination processes will occur, resulting in an increase in the manufacturing cost of the wood multilayer board 3, resulting in lower economic efficiency.

선택적으로, 서로 다른 수종의 목재 단판(2) 다수매를 접착제로 접착하여 적층하고 적층된 목재 단판(2)을 일정한 온도와 압력으로 압착하여 목재 다층 보드(3)를 구성할 수 있다. 예를 들면, 참나무의 목재 단판(2)과 박달나무의 목재 단판(2)과 나왕의 목재 단판(2)을 교대로 접착하여 적층하고 일정한 온도와 압력으로 압착하여 서로 다른 수종으로 이루어지는 목재 다층 보드(3)를 구성한다.Optionally, a plurality of different kinds of wood veneers 2 may be adhered and laminated with an adhesive, and the laminated wood veneers 2 may be pressed at a constant temperature and pressure to form a wood multilayer board 3. For example, a wood multi-layer board made of different species by bonding and stacking wood veneer (2) of oak, wood veneer (2) of birch and wood veneer (2) of Nawang, alternately bonded and pressed at a constant temperature and pressure. (3) is constituted.

상기와 같이 적층 형성된 목재 다층 보드(3)의 일 표면에 일정한 두께의 기판(4)을 접착제로 접착하여 건축자재를 구성하며, 선택적으로 상기 목재 다층 보드(3)의 반대 표면에 장식지 또는 장식 쉬트 또는 무늬목판 등을 접착제로 접착하여 미려한 외관의 건축자재를 구성한다. 상기와 같이 구성된 건축자재는 바닥재, 벽재, 천정재 등과 같이 주로 건축물의 내장재 용도로 사용 가능하다. 이러한 건축자재의 사용 목적과 설치 장소 등에 따라서 목재 다층 보드(3)의 표면에 접착되는 일정한 두께의 기판(4)은 목재, 철, 동, 합금, 합성수지 재질로 다양하게 선택되며, 상기와 같은 재질로 구성된 기판(4)이 목재 다층 보드(3)를 지지한다.As described above, a substrate 4 having a predetermined thickness is bonded to one surface of the laminated multilayer wood board 3 with an adhesive to construct a building material, and optionally, a decorative paper or a decorative sheet on an opposite surface of the wood multilayer board 3. Alternatively, the wooden board is glued to form a building material with a beautiful appearance. The building materials configured as described above can be used mainly for interior materials of buildings, such as flooring, walling, and ceiling materials. According to the purpose of use of the building materials and the installation location, the substrate 4 having a predetermined thickness bonded to the surface of the wood multilayer board 3 is variously selected from wood, iron, copper, alloy, synthetic resin, and the like. The board | substrate 4 which consists of these supports the wooden multilayer board 3.

실시예를 참조하여 본 발명을 상세하게 설명하면,The present invention will be described in detail with reference to Examples.

원목을 1차 가공한 목재를 양 방향으로 왕복시키면서 깍아내어 0.5 ㎜의 두께로 슬라이스하고, 상기 슬라이스된 목재로부터 옹이 및 각종 하자가 존재하는 부위를 식별하고, 식별된 옹이 및 하자 부위를 절단기로 분리하여 다양한 크기와 형상의 옹이 및 하자 부위 조각면(1)을 형성한다.The wood is first chopped and chopped wood in both directions, sliced to a thickness of 0.5 mm, and the areas where knots and various defects exist from the sliced wood are identified, and the identified knots and defects are separated by a cutter. To form knots and defects engraving surfaces 1 of various sizes and shapes.

상기 다양한 크기와 형상의 옹이 및 하자 부위 조각면(1)을 적절하게 배열하고, 봉합기를 사용하여 접착제 재질의 봉합사(5)로 봉합하여 상기 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1) 사이를 연결하고, 이러한 봉합 과정을 반복하여 0.5 ㎜ 두께인 사각형의 목재 단판(2)을 형성한다.The knots and defect portion engraving surfaces 1 of various sizes and shapes are appropriately arranged, and sutured with the sutures 5 of an adhesive material using a suture, and the knots and defect portions of the knots and defect portions engraving surface 1 The connection between the pieces 1 is repeated and this suture process is repeated to form a square wood veneer 2 of 0.5 mm thickness.

상기 목재 단판(2)의 표면에 목재 가공용 친환경적 멜라민 접착제를 0.2 ㎜의 두께로 도포하고 도포된 접착제층에 다른 목재 단판(2)을 대면하여 접착하고, 이러한 과정을 반복하여 9 매의 목재 단판(2)을 같은 결로 차례로 적층하며, 적층된 목재 단판(2)을 130 ℃의 온도로 가온된 2 개의 롤러 사이로 통과시켜서 압착하여 9 층의 목재 다층 보드(3)를 형성한다. 선택적으로, 상기 목재 다층 보드(3)를 절단기로 절단하여 일정한 크기와 형태로 분할한다.Applying the eco-friendly melamine adhesive for wood processing to the surface of the wood veneer (2) to a thickness of 0.2 mm and bonding the other wood veneer (2) to face the adhesive layer applied, and repeating this process, nine wood veneers ( 2) are laminated in sequence with the same condensation, and the laminated wood end plates 2 are passed through two rollers warmed to a temperature of 130 ° C to be compressed to form a nine-layer wood multilayer board 3. Optionally, the wood multilayer board 3 is cut with a cutter and divided into a predetermined size and shape.

상기 목재 다층 보드(3)의 일 표면에 접착제를 도포하고 동 재질의 기판(4) 을 접착하여 바닥재인 건축자재를 완성한다.An adhesive is applied to one surface of the wood multilayer board 3 and the substrate 4 of the same material is adhered to complete the building material as a flooring material.

상기 완성된 바닥재를 건축물의 실내 바닥에 차례로 배설하여 시공하며, 이 때 상기 건축 자재의 기판(4)을 바닥에 대면하도록 접착하여 지하의 수맥파가 차단되는 마루 바닥을 완공한다.The completed flooring materials are sequentially disposed on the indoor floor of the building, and at this time, the substrate 4 of the building material is bonded to face the floor, thereby completing the flooring of the basement where water waves in the basement are blocked.

상기와 같이 실시예를 참조하여 본 발명의 폐목재를 이용한 건축자재의 제조 방법을 상세하게 설명하였으나, 본 발명의 구성 및 기술사상은 상기한 실시예에 의해 한정되지 않으며, 옹이 및 하자 부위 조각면(1)의 두께, 목재 단판(2)으로 봉합되는 옹이 및 하자 부위 조각면(1)의 배치, 적층되는 목재 단판(2)의 수효, 압착 과정에서 적용되는 온도 및 압력 등과 같은 본 발명의 구체적인 실시 과정은 당업자에 의해 특허청구범위에 기재된 내용이나 기술사상을 벗어나지 않는 범위 내에서 다양하게 수정하거나 변경시킬 수 있다.Although the manufacturing method of the building material using the waste wood of the present invention has been described in detail with reference to the embodiment as described above, the configuration and technical spirit of the present invention are not limited by the above-described embodiment, the knots and flaw surface engraving Specific thickness of the present invention, such as the thickness of (1), the knots and flaw sections (1) to be sewn with the wood veneer (2), the number of the laminated wood veneer (2), the temperature and pressure applied in the pressing process, etc. The implementation process may be variously modified or changed by those skilled in the art without departing from the contents or technical spirit described in the claims.

본 발명에서는 일정한 두께로 슬라이스된 목재로부터 옹이가 존재하는 부위를 분리하여 형성되는 옹이 및 하자 부위 조각면(1)을 적용하여 고부가가치의 건축자재를 구성하므로 종래에 폐기되거나 땔감으로 사용되던 목재의 옹이 및 하자 부위를 활용할 수 있기 때문에 원목에 대한 목재의 활용 비율이 종래의 평균 35 %에서 70 %로 크게 증가된다.In the present invention, by applying the knot and flaw part (1) formed by separating the presence of knots from the wood sliced to a certain thickness to constitute a high value-added building material of the wood that was conventionally discarded or used as firewood The availability of knots and defects greatly increases the utilization of wood to timber from 70% to 35% on average.

또한, 목재 단판(2)이 적층되어 목재 다층 보드(3)를 구성하므로 설치된 건축자재의 표면, 즉 목재 다층 보드(3)의 최상층이 훼손되는 경우에는 상기 훼손된 최상층의 목재 단판(2)을 그라인더로 용이하게 깍아내고 그 하부층의 목재 단판(2)을 노출시키므로서 상기 건축자재를 연속적으로 활용하기 때문에 건축자재의 수명을 건축물의 수명과 동일하게 연장시킬 수 있으며, 특히 목재 다층 보드(3)가 서로 다른 수종의 목재 단판(2)으로 접착 구성되는 경우에는 최상층의 목재 단판(2)을 깍아내면 다른 수종의 목재 단판(2)이 노출되어 새로운 무늬와 분위기의 건축자재를 연출할 수 있다.In addition, when the wood veneer (2) is laminated to constitute a wood multilayer board (3), when the surface of the installed building material, that is, the top layer of the wood multilayer board (3) is damaged, the damaged wood veneer (2) of the top layer is ground. It is possible to extend the life of the building material to the same as the life of the building because the building material is continuously utilized by easily cutting off the wood and exposing the wooden veneer 2 of the lower layer. When the adhesive is composed of different kinds of wood veneer (2), by cutting off the wood veneer (2) of the uppermost layer, the other wood veneer (2) can be exposed to create a new pattern and building materials.

본 발명에 의한 폐목재를 이용한 건축자재의 제조 방법은 슬라이스된 목재의 옹이 및 하자 부위를 분리하여 옹이 및 하자 부위 조각면을 형성하고, 상기 옹이 및 하자 부위 조각면과 옹이 및 하자 부위 조각면을 접착제 재질의 봉합사로 봉합하여 목재 단판을 형성하고, 상기 목재 단판을 적층하고 압착하여 목재 다층 보드를 형성하고, 상기 목재 다층 보드의 표면에 기판을 접착하는 과정으로 구성되어 종래에는 폐기되던 목재의 옹이 및 하자 부위를 활용하여 바닥재, 벽재, 천정재 등과 같은 고부가가치의 건축자재를 제조하므로서 원목에 대한 목재 활용 비율을 배가하고 원목 소비를 억제하는 효과가 있다.In the method of manufacturing building materials using waste wood according to the present invention, the knots and flaws of sliced wood are separated to form knots and flaw pieces, and the knots and flaw pieces and knots and flaw pieces Suture is made of a suture made of adhesive material to form a wood veneer, laminating and pressing the wood veneer to form a wood multi-layer board, and bonding the substrate to the surface of the wood multi-layer board knots of previously discarded wood And by using the defects to produce high value-added building materials, such as flooring, wall materials, ceiling materials, etc. There is an effect of doubling the ratio of wood to wood and suppressing the consumption of wood.

Claims (3)

목재를 0.5 ∼ 1 ㎜의 두께로 슬라이스하고 그 옹이 및 하자 부위를 분리하여 옹이 및 하자 부위 조각면(1)을 형성하는 과정과, 상기 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)을 접착제 재질의 봉합사(5)로 봉합하여 상호간에 연결하여 일정한 크기의 목재 단판(2)을 형성하는 과정과, 상기 목재 단판(2) 다수매를 적층으로 접착하고 일정한 온도와 압력으로 압착하여 목재 다층 보드(3)를 형성하는 과정과, 상기 목재 다층 보드(3)의 일 표면에 일정한 두께의 기판(4)을 접착제로 접착하는 과정으로 구성되는 것을 특징으로 하는 폐목재를 이용한 건축자재의 제조 방법.Slicing the wood to a thickness of 0.5 to 1 mm and separating the knots and the flaws to form the knots and the flaw pieces 1 and the pieces of the knots and the flaw parts 1 and the pieces of the knots and the flaws Stitching the surface (1) with an adhesive suture (5) and connecting them to each other to form a wood veneer (2) of a predetermined size; Using a wood waste, characterized in that it comprises a process of forming a wood multilayer board (3) by pressing and bonding the substrate (4) of a predetermined thickness on one surface of the wood multilayer board (3) with an adhesive Method of manufacturing construction materials. 제 1 항에 있어서, 옹이 및 하자 부위 조각면(1)과 옹이 및 하자 부위 조각면(1)의 변을 접착제로 접합하여 상호간에 연결하여 일정한 크기의 목재 단판(2)을 구성하는 것을 특징으로 하는 폐목재를 이용한 건축자재의 제조 방법.The method according to claim 1, wherein the knot and defect portion engraving surface 1 and the sides of the knot and defect portion engraving surface 1 are bonded to each other by an adhesive to form a wood veneer 2 having a constant size. Method of manufacturing building materials using waste wood. 제 1 항에 있어서, 서로 다른 수종의 목재 단판(2) 다수매를 접착제로 접착하여 적층하고 일정한 온도와 압력으로 압착하여 목재 다층 보드(3)를 구성하는 것을 특징으로 하는 폐목재를 이용한 건축자재의 제조 방법.The construction material using waste wood according to claim 1, wherein a plurality of different types of wood veneers (2) are bonded and laminated with an adhesive and compressed at a constant temperature and pressure to form a wood multilayer board (3). Method of preparation.
KR1020040028043A 2004-04-23 2004-04-23 A manufacturing method of building materials using scrapped wood KR100638110B1 (en)