KR100579652B1 - Hydrophilic inorganic paint Complex - Google Patents
Hydrophilic inorganic paint Complex Download PDFInfo
- Publication number
- KR100579652B1 KR100579652B1 KR1020040037754A KR20040037754A KR100579652B1 KR 100579652 B1 KR100579652 B1 KR 100579652B1 KR 1020040037754 A KR1020040037754 A KR 1020040037754A KR 20040037754 A KR20040037754 A KR 20040037754A KR 100579652 B1 KR100579652 B1 KR 100579652B1
- Authority
- KR
- South Korea
- Prior art keywords
- oxide
- hydrophilic inorganic
- coating composition
- present
- phosphate
- Prior art date
Abstract
본 발명은 무기도료 조성물에 관한 것으로서, 보다 상세하게는 물을 용제로 사용할 수 있으며, 모재에 코팅시 물과의 결합력이 우수한 친수성 표면이 형성되고, 모재와의 밀착도가 우수한 친수성 무기도료 조성물에 관한 것이다. The present invention relates to an inorganic coating composition, and more particularly, water may be used as a solvent, and a hydrophilic surface having excellent bonding strength with water when coating on a base material is formed, and a hydrophilic inorganic coating composition having excellent adhesion to the base material. will be.
본 발명은, 경화제, 베이스, 촉매제로 이루어지되, 상기 경화제는 알칼리 금속 산화물(alkali metal oxide)과 알칼리 실리케이트(alkali silicate)로 이루어지며, 상기 베이스는 금속 산화물(metal oxide)과 금속 인산화물(metal phosphate) 및 알칼리 실리케이트로 이루어지는 것을 특징으로 하는 친수성 무기도료 조성물을 제공한다.The present invention comprises a curing agent, a base, and a catalyst, wherein the curing agent is composed of an alkali metal oxide and an alkali silicate, and the base is a metal oxide and a metal phosphate. It provides a hydrophilic inorganic coating composition comprising a phosphate) and an alkali silicate.
도료, 무기도료, 친수성, 코팅Paint, Inorganic Paint, Hydrophilic, Coating
Description
도 1은 본 발명의 실시예에 따른 친수성 무기도료 조성물을 사용하여 형성되는 도막의 구조를 나타내는 단면도이다. 1 is a cross-sectional view showing the structure of a coating film formed using a hydrophilic inorganic coating composition according to an embodiment of the present invention.
도 2는 본 발명의 실시예에 따른 친수성 무기도료 조성물을 사용하여 형성되는 도막 표면 및 내부 구조를 나타내는 단면도이다. 2 is a cross-sectional view showing the surface and the internal structure of the coating film formed using a hydrophilic inorganic coating composition according to an embodiment of the present invention.
도 3은 본 발명의 실시예에 따른 친수성 무기도료 조성물을 사용하여 형성되는 도막의 분자 구조를 입체적으로 나타내는 도면이다. 3 is a view showing in three dimensions the molecular structure of the coating film formed using a hydrophilic inorganic coating composition according to an embodiment of the present invention.
도 4는 본 발명의 실시예에 따른 친수성 무기도료 조성물을 사용하여 형성되는 도막 표면에 유기물질이 오염된 경우의 모습을 나타내는 도면이다. 4 is a view showing a state in which an organic material is contaminated on the surface of the coating film formed using a hydrophilic inorganic coating composition according to an embodiment of the present invention.
< 도면의 주요부분에 대한 부호의 설명 ><Description of Symbols for Major Parts of Drawings>
10 : 도막10: coating film
20 : 모재20: base material
30 : 인산 피막30: phosphate coating
40 : 유기물질40: organic matter
본 발명은 무기도료 조성물에 관한 것으로서, 보다 상세하게는 물을 용제로 사용할 수 있으며, 모재에 코팅시 물과의 결합력이 우수한 친수성 표면이 형성되고, 모재와의 밀착도가 우수한 친수성 무기도료 조성물에 관한 것이다. The present invention relates to an inorganic coating composition, and more particularly, water may be used as a solvent, and a hydrophilic surface having excellent bonding strength with water when coating on a base material is formed, and a hydrophilic inorganic coating composition having excellent adhesion to the base material. will be.
일반적으로 도료는 철도 차량, 선박, 도로시설, 전자, 전기 등의 각종 산업분야는 물론 주방, 거실 등의 일반 가정에서도 사용될 수 있어서 매우 광범위한 용도를 가진다. In general, the paint can be used in a variety of industries such as rail vehicles, ships, road facilities, electronics, electricity, as well as general households such as kitchens, living rooms, etc., has a very wide range of uses.
그러나 종래의 도료는 알콜 등 유기 용제를 사용하므로 환경오염의 문제가 있다. 또한 종래의 도료는 그 표면에 유기 물질(예들 들어 각종 기름, 락카 스프레이, 유성 매직 등)이 묻어서 오염되는 경우 그 유기 물질을 물로 제거하는 것이 용이하지 않은 문제점이 있다. 이는 종래의 도료 표면이 유기 물질과 잘 결합할 수 있는 소수성을 가지기 때문이다. However, conventional paints use an organic solvent such as alcohol, so there is a problem of environmental pollution. In addition, the conventional paint has a problem that it is not easy to remove the organic material with water when it is contaminated by the organic material (for example, various oils, lacquer spray, oil magic, etc.) on the surface. This is because the conventional paint surface has a hydrophobic property that can bind well with organic materials.
또한 종래의 도료는 모재에 코팅하기 위해 모재의 표면을 센딩 처리 하는 등의 부수적인 공정이 요구되는 문제점이 있다. 이는 종래의 도료가 모재에 대한 접착성이 낮기 때문이다. 따라서 모재에 밀착도가 높은 물질을 먼저 코팅해주고 도료를 코팅하는 등 코팅 공정이 복잡해지고, 비용이 높아지는 문제점이 있다. In addition, the conventional paint has a problem that an additional process, such as for example the send treatment of the surface of the base material in order to coat the base material. This is because the conventional coating material is low in adhesion to the base material. Therefore, there is a problem in that the coating process is complicated, such as coating a material having a high adhesion to the base material first and coating a coating material, thereby increasing the cost.
본 발명의 목적은 물을 용제로 사용할 수 있으며, 코팅에 의하여 형성되는 도막 표면에 친수성 단분자막이 형성되며, 모재와의 밀착도가 우수한 친수성 무기도료 조성물을 제공함에 있다. An object of the present invention is to provide a hydrophilic inorganic coating composition can be used as a solvent, a hydrophilic monomolecular film is formed on the surface of the coating film formed by the coating, excellent adhesion to the base material.
전술한 목적을 달성하기 위하여 본 발명은, 경화제, 베이스, 촉매제로 이루어지되, 상기 경화제는 알칼리 금속 산화물(alkali metal oxide)과 알칼리 실리케이트(alkali silicate)로 이루어지며, 상기 베이스는 금속 산화물(metal oxide)과 금속 인산화물(metal phosphate) 및 알칼리 실리케이트로 이루어지는 것을 특징으로 하는 친수성 무기도료 조성물을 제공한다.In order to achieve the above object, the present invention consists of a curing agent, a base, a catalyst, the curing agent is composed of an alkali metal oxide (alkali metal oxide) and alkali silicate (alkali silicate), the base is a metal oxide (metal oxide) The present invention provides a hydrophilic inorganic coating composition comprising a metal phosphate and an alkali silicate.
또한 본 발명은, 경화제 30 ~ 70 중량 %, 베이스 30 ~ 70 중량 %의 비율로 경화제와 베이스를 혼합하되, 경화제와 베이스 중량의 합이 100 중량%이며, 상기 경화제와 베이스를 합한 중량의 2 ~ 25 중량 %가 되도록 상기 촉매제를 더 첨가하여 친수성 무기도료 조성물을 형성시킴으로써, 코팅작업시 반응이 신속하게 일어나며, 모재와의 밀착도가 우수하게 한다. In the present invention, the curing agent and the base is mixed at a ratio of 30 to 70% by weight of the curing agent, 30 to 70% by weight of the base, the sum of the weight of the curing agent and the base is 100% by weight, the amount of 2 ~ By further adding the catalyst to 25% by weight to form a hydrophilic inorganic coating composition, the reaction occurs quickly during the coating operation, and excellent adhesion to the base material.
또한 본 발명에서는 상기 알칼리 금속 산화물을, 산화 칼륨(K2O), 산화 나트륨(Na2O), 산화 리튬(Li2O) 등으로 이루어지는 군에서 선택되는 어느 하나 또는 둘 이상을 선택하고 혼합하여 이루어지도록 한다. In the present invention, the alkali metal oxide is selected and mixed with any one or two or more selected from the group consisting of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 O) and the like. To be done.
또한 본 발명에서는, 상기 금속 산화물을, 산화 아연(ZnO), 산화 알루미늄(Al2O3), 산화 칼슘(CaO), 산화 마그네슘(MgO) 등으로 이루어지는 군에서 선택되는 어느 한 또는 둘 이상을 선택하고 혼합하여 이루어지도록 한다. In the present invention, the metal oxide is selected from one or more selected from the group consisting of zinc oxide (ZnO), aluminum oxide (Al 2 O 3 ), calcium oxide (CaO), magnesium oxide (MgO) and the like. And mix.
또한 본 발명에서는, 상기 금속 인산화물을, 알루미늄 인산화물 또는 아연 인산화물 등으로 이루어지는 군 중 어느 하나이거나, 그 혼합물이 되도록 한다. In the present invention, the metal phosphate is any one of a group consisting of aluminum phosphate, zinc phosphate, or the like, or a mixture thereof.
또한 본 발명에서는 친수성 무기도료 조성물에 촉매제 및 안료가 더 포함되도록 하여 다양한 색상의 도막 색상이 나타나도록 한다. In addition, in the present invention, a catalyst and a pigment are further included in the hydrophilic inorganic coating composition so that various colors of the coating film appear.
이하에서는 첨부된 도면을 참조하여 본 발명의 구체적인 실시예를 상세하게 설명한다. Hereinafter, with reference to the accompanying drawings will be described in detail a specific embodiment of the present invention.
본 실시예에 따른 친수성 무기도료 조성물을 사용하여 모재에 코팅 작업을 실시하면 도 1에 도시된 바와 같은, 도막(10)이 형성된다. 즉, 모재(20)와 도막(10) 사이에 강력한 밀착도를 가지는 인산 피막(30)이 형성되며, 도 2에 도시된 바와 같이, 도막(10) 표면에는 OH 기가 노출되어 있어서, 친수성을 가진 OH 단분자막이 형성된다. When the coating operation is performed on the base material using the hydrophilic inorganic coating composition according to the present embodiment, a
코팅시에 전술한 구조를 가지는 본 실시예에 따른 친수성 무기도료 조성물은 경화제, 베이스, 촉매제로 이루어진다. The hydrophilic inorganic coating composition according to the present embodiment having the structure described above at the time of coating is composed of a curing agent, a base, and a catalyst.
이때 경화제는, 도막의 경화를 촉진하는 역할을 하며, 도막의 주 구성 물질이 된다. 즉, 경화제는 본 실시예에 따른 친수성 무기도료 조성물을 사용하여 코팅 하는 경우 도막을 형성하는 물질인 알칼리 실리케이트(소성식 : M20·nSiO2·mH2
O, M은 알칼리 금속임.)를 형성한다. At this time, a hardening | curing agent serves to accelerate hardening of a coating film, and becomes a main component material of a coating film. That is, the curing agent is an alkali silicate (calcination formula:
여기에서 도막의 구조는 도 3에 도시된 바와 같다. 즉, 알칼리 실리케이트는, 정사면체 구조 내부에 알칼리 금속이 봉해지는 입체구조를 가지는 것이다. Here, the structure of the coating film is as shown in FIG. That is, the alkali silicate has a three-dimensional structure in which an alkali metal is sealed inside the tetrahedron structure.
이러한 경화제는 알칼리 금속 산화물(alkali metal oxide)과 알칼리 실리케이트로 이루어지는 것이 바람직하다. 이때 상기 알칼리 금속 산화물은, 산화 칼륨(K2O), 산화 나트륨(Na2O), 산화 리튬(Li2O) 등으로 이루어지는 군에서 선택되는 어느 하나 또는 둘 이상을 선택하고 혼합하여 형성되는 것이 바람직하다. Such a curing agent is preferably composed of alkali metal oxides and alkali silicates. In this case, the alkali metal oxide is formed by selecting and mixing any one or two or more selected from the group consisting of potassium oxide (K 2 O), sodium oxide (Na 2 O), lithium oxide (Li 2 O), and the like. desirable.
다음으로 베이스는 도 1에 도시된 도막 구조에서 모재(20)와 도막(10) 사이에 형성되는 인산 피막(30)을 형성시키는 역할을 한다. Next, the base serves to form a
이때 인산 피막이 형성되는 과정은 다음과 같다. At this time, the process of forming the phosphate film is as follows.
H3PO4 + Al(OH)3 -> Al(H2PO4), Al2(HPO 4)3, AlPO4 H 3 PO 4 + Al (OH) 3- > Al (H 2 PO 4 ), Al 2 (HPO 4 ) 3 , AlPO 4
Al(H2PO4) + MO -> AlPO4 + M(H2PO4)2 Al (H 2 PO 4 ) + MO-> AlPO 4 + M (H 2 PO 4 ) 2
M(H2PO4)2 -> MHPO4·3H2OM (H 2 PO 4 ) 2- > MHPO 4 , 3H 2 O
본 실시예에 따른 친수성 무기도료에 있어서, 인산 피막(30)은 도막(10)과 모재(20)를 강력하게 밀착시키는 역할을 한다. 즉, 본 실시예에 따른 친수성 무기 도료 조성물에서는 별도의 접착제를 모재에 코팅하지 않아도 조성물 자체의 구성성분의 반응에 의하여 인산 피막이 생성되므로 단 한번의 코팅으로 강력한 밀착도를 가진 도막을 형성시킬 수 있는 장점이 있는 것이다. In the hydrophilic inorganic coating according to the present embodiment, the
이러한 베이스는 금속 산화물(metal oxide)과 금속 인산화물(metal phosphate) 및 알칼리 실리케이트 등으로 이루어지는 것이 바람직하다. 이때, 상기 금속 산화물은, 산화 아연(ZnO), 산화 알루미늄(Al2O3), 산화 칼슘(CaO), 산화 마그네슘(MgO) 등으로 이루어지는 군에서 선택되는 어느 하나로 이루어지거나 또는 둘 이상을 선택하고 혼합하여 형성되는 것이 바람직하다. 그리고 상기 금속 인산화물은, 알루미늄 인산화물 또는 아연 인산화물 중 어느 하나이거나, 그 혼합물로 형성되는 것이 바람직하다. The base is preferably made of metal oxide (metal oxide), metal phosphate (metal phosphate), alkali silicate and the like. At this time, the metal oxide is made of one selected from the group consisting of zinc oxide (ZnO), aluminum oxide (Al 2 O 3 ), calcium oxide (CaO), magnesium oxide (MgO), or two or more selected. It is preferable to form by mixing. The metal phosphate is preferably any one of aluminum phosphate and zinc phosphate or a mixture thereof.
그리고 본 실시예에 따른 친수성 무기 도료 조성물은, 경화제 30 ~ 70 중량 %, 베이스 30 ~ 70 중량 %의 비율이 되도록, 경화제와 베이스를 혼합하여 형성되는 것이 바람직하다. 이때 상기 경화제와 베이스를 합한 중량의 2 ~ 25 중량 %가 되도록 상기 촉매제를 더 첨가하여 마련되는 것이 반응 속도의 향상을 위하여 더욱 바람직하다. 이때 상기 촉매제는 산화 티타늄(TiO2)인 것이 바람직하다. And it is preferable that the hydrophilic inorganic coating composition which concerns on a present Example is formed by mixing a hardening | curing agent and a base so that it may become a ratio of 30 to 70 weight% of a hardening | curing agent and 30 to 70 weight% of a base. At this time, it is more preferable that the catalyst is further added so as to be 2 to 25% by weight of the total weight of the curing agent and the base to improve the reaction rate. In this case, the catalyst is preferably titanium oxide (TiO 2 ).
그리고 본 실시예에 따른 친수성 무기도료 조성물에는 안료가 더 첨가될 수 있다. 안료는 모재에 형성되는 도막이 다양한 색상을 나타내도록 하는 것이며, 본 실시예에서는 전체 조성물 중량의 0.01 ~ 20 중량 %의 비율로 첨가되는 것이 바람직하다. And a pigment may be further added to the hydrophilic inorganic coating composition according to the present embodiment. The pigment is such that the coating film formed on the base material exhibits various colors. In this embodiment, the pigment is preferably added at a ratio of 0.01 to 20% by weight of the total composition weight.
이하에서는 본 실시예에 따른 친수성 무기도료 조성물에 의하여 도막이 형성될때 진행되는 화학 반응을 설명한다. Hereinafter, the chemical reaction proceeds when the coating film is formed by the hydrophilic inorganic coating composition according to the present embodiment.
< 화학식 1 ><Formula 1>
즉, 경화제, 베이스, 촉매제, 안료를 물에 혼합하고 용해 시킨다. That is, the curing agent, base, catalyst and pigment are mixed and dissolved in water.
< 화학식 2 ><Formula 2>
이렇게 되면 알칼리 실리케이트 안에 알칼리 금속(K+)가 분리되고, 동시에 탈수축합반응이 시작된다. This causes the alkali metal (K + ) to separate in the alkali silicate, and at the same time the dehydration condensation reaction starts.
< 화학식 3 > <Formula 3>
탈수 축합반응과 동시에 칼륨의 겔화가 시작되고 3차원 구조가 형성된다. Simultaneously with the dehydration condensation reaction, the gelation of potassium begins and a three-dimensional structure is formed.
< 화학식 4 > <Formula 4>
( M : K, Mn, Ca, Zn, Mg 등)(M: K, Mn, Ca, Zn, Mg, etc.)
겔화된 칼륨산(K+)은 소성에 의해 실리카의 정사면체 입체구조를 형성하고, 알칼리 및 다른 금속 이온은 입체구조 바구니안에 봉해져서 도막이 형성된다. 이과정에서 도막 표면으로는 OH 기가 노출된다. Gelled potassium acid (K + ) forms a tetrahedral conformation of silica by firing, and alkalis and other metal ions are sealed in the conformation basket to form a coating film. In this process, OH groups are exposed on the surface of the coating film.
이러한 실리카 입체구조의 완전성형에는 건조온도의 제어와 동시에 경화제의 촉매활성을 높이는 것이 중요하다. In the complete shaping of the three-dimensional silica structure, it is important to increase the catalytic activity of the curing agent while controlling the drying temperature.
이하에서는 본 발명에 따른 친수성 무기도료 조성물의 제조방법을 보다 구체적으로 설명한다. Hereinafter will be described in more detail the manufacturing method of the hydrophilic inorganic coating composition according to the present invention.
본 실시예에 따른 코팅용 무기 조성물은, 경화제; 베이스; 촉매제; 안료;를 혼합 교반하여 제조된다. 혼합시에 경화제와 베이스는 액상이며, 촉매제와 안료는 분말 상태인 것이 바람직하다. Inorganic composition for coating according to the present embodiment, a curing agent; Base; Catalysts; Pigment; prepared by mixing and stirring. It is preferable that a hardening | curing agent and a base are liquid at the time of mixing, and a catalyst and a pigment are in powder form.
이때 경화제는 산화 칼륨(K2O), 산화 나트륨(Na2O), 알칼리 실리케이트로 구성되는 것이 바람직하다. 필요에 따라서는 산화 나트륨(Li2O)를 더 첨가할 수도 있다. At this time, the curing agent is preferably composed of potassium oxide (K 2 O), sodium oxide (Na 2 O), alkali silicates. If necessary, sodium oxide (Li 2 O) may be further added.
이러한 경화제는 본 실시예에 따른 친수성 무기도료 조성물이 경화되면, K20·Na2O·nSiO2·mH2O 의 단일조성식을 가지는 물질로 변화된다. 이때 n 과 m 은 자연수이다. Such a curing agent is changed to a material having a single composition of K 2 O · Na 2 O · nSiO 2 · mH 2 O when the hydrophilic inorganic coating composition according to the present embodiment is cured. Where n and m are natural numbers.
또한 베이스(base)는 알루미늄 포스페이트(AlPO4), 알칼리 실리케이트, 산화 아연(ZnO)으로 구성되는 것이 바람직하다. 이러한 베이스는 본 실시예에 따른 무기 조성물이 경화되면, AlPO4·SiO2·ZnO·Al2O3·lH2O의 조성식을 가지는 물질로 변화된다. 이때 l은 자연수이다. In addition, the base is preferably composed of aluminum phosphate (AlPO 4 ), alkali silicate, zinc oxide (ZnO). This base is changed to a material having a composition formula of AlPO 4 · SiO 2 · ZnO · Al 2 O 3 · lH 2 O when the inorganic composition according to the present embodiment is cured. Where l is a natural number.
전술한 경화제와 베이스는 혼합시에 그 비율을, 산화 칼륨(K2O) 3 ~ 40 중량 %, 산화 나트륨(Na2O) 3 ~ 5 중량 %, 알칼리 실리케이트 20 ~ 45 중량 %, 알루미늄 포스페이트(AlPO4) 30 ~ 55 중량 %, 산화 아연(ZnO) 10 ~ 20 중량 %로 혼합하는 것이 바람직하다. 또한 경화제에 산화 리튬(Li2O)을 더 첨가하는 경우에는 그 비율을 3 ~ 10 중량 %로 하여 첨가하는 것이 바람직하다. The ratio of the above-mentioned curing agent and the base at the time of mixing is 3 to 40% by weight of potassium oxide (K 2 O), 3 to 5% by weight of sodium oxide (Na 2 O), 20 to 45% by weight of alkali silicate, aluminum phosphate ( AlPO 4 ) 30 to 55% by weight, it is preferable to mix with 10 to 20% by weight of zinc oxide (ZnO). In addition, further addition of lithium oxide (Li 2 O) in the curing agent is preferably added to the ratio of 3 to 10% by weight.
그리고 본 실시예에 따른 친수성 무기도료 조성물에는 탈수 축합 반응을 촉매하는 촉매제 및 안료가 더 포함되는 것이 바람직하다. 즉, 본 실시예에 따른 친수성 무기도료 조성물을 모재에 코팅하고 나서 경화시키는 과정에서 발생하는 탈수 축합 반응을 촉매하기 위한 촉매제가 더 첨가되는 것이다. 이때 촉매제는 전술한 경화제와 베이스의 중량을 100%로 하였을때, 2 ~ 25 중량 %가 되도록 첨가한다. In addition, the hydrophilic inorganic coating composition according to the present embodiment may further include a catalyst and a pigment for catalyzing the dehydration condensation reaction. That is, a catalyst for catalyzing the dehydration condensation reaction occurring in the process of coating the base material with the hydrophilic inorganic coating composition according to the present embodiment and then curing is further added. At this time, the catalyst is added so that 2 to 25% by weight when the weight of the curing agent and the base to 100%.
그리고 안료를 더 첨가할 수 있다. 안료는 코팅된 도막이 특정한 색상을 나타내도록 하기 위하여 첨가된다. 본 실시예 따른 친수성 무기도료 조성물에 안료를 첨가하지 않은 경우에는 코팅 후의 색이 흰색인데, 안료를 첨가하면 안료에 따라 다양한 색상을 얻을 수 있다. 이때 안료의 첨가 비율은, 0.01 ~ 20 중량 %로 하는 것이 바람직하다. And pigment can be added further. Pigments are added to make the coated coating exhibit a specific color. When the pigment is not added to the hydrophilic inorganic coating composition according to the present embodiment, the color after coating is white. When the pigment is added, various colors may be obtained according to the pigment. At this time, it is preferable that the addition ratio of a pigment shall be 0.01-20 weight%.
전술한 조성을 가지도록 각 원료를 교반기에 투입한 후, 교반하여 골고루 혼합한다. 이때 교반기의 회전 속도는 필요에 따라 10 ~ 30 RPM, 40 ~ 100 RPM, 300 ~ 800 RPM으로 조정할 수 있다. 교반 공정이 완료되면 본 실시예에 따른 친수성 무기도료 조성물이 완성된다. Each raw material is put into a stirrer so as to have the composition described above, followed by stirring and mixing evenly. At this time, the rotation speed of the stirrer can be adjusted to 10 ~ 30 RPM, 40 ~ 100 RPM, 300 ~ 800 RPM as needed. When the stirring process is completed, the hydrophilic inorganic coating composition according to the present embodiment is completed.
그리고 교반된 본 실시예에 따른 친수성 무기도료 조성물을 모재에 코팅한다. 모재에 코팅하는 방법은 매우 다양하다. And the hydrophilic inorganic coating composition according to the present embodiment is coated on the base material. There are many ways to coat the base material.
본 발명의 친수성 무기도료 조성물을 사용하여 모재에 코팅을 실시하면, 도 1에 도시된 바와 같은 도막이 형성된다. 이 도막(10) 표면에 유기물질이 묻어서 오염이 발생하더라도, 물로 세척하여 손쉽게 유기물질을 제거할 수 있는 장점이 있다. 즉, 도 4a에 도시된 바와 같이, 도막 표면에 유기물질(40)로 된 오염이 발생하는 경우, 본 실시예에 따른 친수성 무기도료 조성물에 의하여 형성된 도막 표면에는 친수성 OH기로 이루어진 단분자막이 존재하며, 유기물질이 도막과 강하게 결합하지 못한다. When the base material is coated using the hydrophilic inorganic coating composition of the present invention, a coating film as shown in FIG. 1 is formed. Even if contamination occurs due to the organic material on the surface of the
오히려 도 4b에 도시된 바와 같이 물이 묻으면 도막(10) 표면의 OH 기와 물이 결합하여 유기 물질(40)을 띄우는 현상이 발생한다. 따라서 유기물질이 물에 의하여 손쉽게 제거될 수 있는 것이다. Rather, as shown in FIG. 4B, when the water is deposited, the OH group on the surface of the
또한 본 발명에 따른 친수성 무기도료 조성물은 모재와의 밀착도가 우수하여, 모재에 별도의 하도 공정을 하거나, 별도의 센딩 공정을 진행하지 않아도 강한 밀착이 이루어진다. 따라서 코팅 공정이 간단해지며, 모재에 변형을 주지않는 장점이 있다. In addition, the hydrophilic inorganic coating composition according to the present invention is excellent in adhesion with the base material, a strong adhesion is achieved even if a separate undercoating process to the base material or a separate sending process. Therefore, the coating process is simplified, there is an advantage that does not deform the base material.
그리고 본 발명에 따른 친수성 무기도료 조성물에 의하여 형성되는 도막에서는 금속 원자가 실리카의 정사면체 구조내에 봉인되어지므로 외부에 노출되지 않아서, 외부로부터의 변화에 강한 저항성을 가진다. 즉, 강한 내후성, 내구성, 내약품성 등의 특징을 가지는 것이다. 따라서 그 수명이 반영구적인 장점이 있다. In the coating film formed by the hydrophilic inorganic coating composition according to the present invention, since the metal atoms are sealed in the tetrahedral structure of silica, they are not exposed to the outside and thus have strong resistance to changes from the outside. That is, it has characteristics such as strong weather resistance, durability and chemical resistance. Therefore, the life is semi-permanent advantage.
또한 본 발명에 따른 친수성 무기도료 조성물은 물을 용제로 하여 사용할 수 있으므로 그 코팅 과정에서 오염물질이 발생하지 않아서 친환경적인 도료이다. In addition, since the hydrophilic inorganic coating composition according to the present invention can be used as a solvent as a solvent, no pollutants are generated during the coating process, thereby making it an environmentally friendly paint.
Claims (7)