KR100499279B1 - A composition for elimination of red tide and a method using the same - Google Patents
A composition for elimination of red tide and a method using the same Download PDFInfo
- Publication number
- KR100499279B1 KR100499279B1 KR10-2003-0057507A KR20030057507A KR100499279B1 KR 100499279 B1 KR100499279 B1 KR 100499279B1 KR 20030057507 A KR20030057507 A KR 20030057507A KR 100499279 B1 KR100499279 B1 KR 100499279B1
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- particles
- red tide
- weight
- parts
- Prior art date
Abstract
본 발명은 천연 암석을 주성분으로 하는 적조 생물 방제용 조성물 및 이러한 조성물을 이용하여 적조 생물을 방제하는 방법에 관한 것으로서, 구체적으로는 주성분으로서 견운모 입자, 점질도석 입자, 형석 입자 및 암면, 질석 및 페라이트로 이루어진 군으로부터 선택된 하나 이상을 포함하는 수경재배석 입자로 이루어진 군으로부터 선택된 하나 이상의 천연 암석 및 부성분으로서 수산화 알루미늄을 더 포함하는 것을 특징으로 하는 조성물 및 이를 이용한 적조 생물 방제 방법에 관한 것이다.The present invention relates to a composition for the control of red tide organisms based on natural rocks and to a method for controlling red tide organisms using such a composition, specifically, mica particles, viscous pottery particles, fluorite particles and rock wool, vermiculite and ferrite as main components. It relates to a composition and a red tide biological control method using the same, characterized in that it further comprises aluminum hydroxide as one or more natural rock and subcomponent selected from the group consisting of hydroponic cultivation particles comprising one or more selected from the group consisting of.
본 발명에 따른 조성물은 비교적 소량을 살포하더라도 적조 방제 효과가 탁월하고, 황토 살포와 같이 그 사용방법이 매우 간편하며, 경제적이면서도, 천연 암석을 주성분으로 사용함으로써 2차 환경파괴를 최소화할 수 있다.The composition according to the present invention is excellent in red tide control effect even when spraying a relatively small amount, very easy to use, such as loess spray, economical, it is possible to minimize the secondary environmental destruction by using natural rock as the main component.
Description
본 발명은 천연 암석을 주성분으로 하는 적조 생물 방제용 조성물 및 이러한 조성물을 이용하여 적조 생물을 방제하는 방법에 관한 것으로서, 구체적으로는 주성분으로서 점질도석 (kaolinite, Al4Si4O10(OH)8) 입자, 견운모 (sericite) 입자, 형석 (fluorite, CaF2) 입자 및 수경재배석 (hydroponics) 입자로 이루어진 군으로부터 선택된 하나 이상의 천연 암석 및 부성분으로서 수산화 알루미늄 (Al(OH)3)을 더 포함하는 것을 특징으로 하는 조성물 및 이를 이용한 적조 생물 방제 방법에 관한 것이다.The present invention relates to a composition for the control of red tide organisms based on natural rock and a method for controlling red tide organisms using such a composition, specifically, kaolinite (Al 4 Si 4 O 10 (OH)) 8 as a main component ) One or more natural rocks and subcomponents selected from the group consisting of particles, sericite particles, fluorite (CaF 2 ) particles and hydroponics particles, further comprising aluminum hydroxide (Al (OH) 3 ). It relates to a composition and a method of controlling red tide organisms using the same.
일반적으로 red tide, red water, brown water 등의 영문 명칭으로 표기되는 적조 현상이라 함은, '특정 종의 플랑크톤이 급격히 증식하여 물의 색을 변화시키는 것'으로 정의된다. 이러한 적조 현상은 우리나라 뿐만 아니라, 일본 연안 해역, 미국 캘리포니아 연안, 동남 아시아 연안 및 북해 연안 등에서 빈번히 발생되고 있으며, 어패류의 패사나 유해성을 유발한다는 점 이외에도 수역 이용 가치를 저하시키고, 더 나아가 경제적인 가치를 초월하여 생태계 전체적으로도 커다란 환경 문제를 야기한다.In general, the red tide phenomenon represented by the English names red tide, red water and brown water is defined as 'changing the color of water by the rapid proliferation of plankton of a specific species'. Such red tide occurs frequently not only in Korea, but also in Japan, the US, California, Southeast Asia, and the North Sea, and in addition to causing the loss or harmfulness of fish and shellfish, it deteriorates the value of water use and further economic value. Beyond this, the entire ecosystem causes great environmental problems.
현재까지 적조 현상의 원인이 명확하게 밝혀지지는 않았으나, 일사량 증가로 인한 특정 식물성 플랑크톤의 과다 광합성, 해수 교환의 부족으로 인한 영양염 증가 및 해수 온도 상승 등이 원인이 되는 것으로 알려져 있다.To date, the cause of the red tide is not clear, but it is known that excessive photosynthesis of certain phytoplankton due to increased solar radiation, increased nutrients due to lack of seawater exchange, and increased seawater temperature.
종래에 이러한 적조 현상을 제거 내지는 완화시키기 위해서는 제초제, 황산 제1철 (FeSO4), 차아염소산 (HOCl) 또는 차아염소산 이온류 (OCl-) 및 계면활성제 등을 이용하여 적조 생물을 파괴 또는 치사시키는 화학적 방법, 천적 생물 등을 살포하는 생물학적 방법, 및 초음파 또는 오존 활성법, 원심분리법 및 전기분해법 등과 같은 물리적 방법이 존재 하였으나, 이러한 방법들은 양식 중인 어패류 및 해초류를 폐사시킬 위험성이 크고, 그 효과 또한 충분히 입증되지 않은 상태였다.Conventionally, in order to remove or alleviate the red tide phenomenon, it is necessary to destroy or kill red tide organisms by using herbicide, ferrous sulfate (FeSO 4 ), hypochlorous acid (HOCl) or hypochlorite ions (OCl − ), and a surfactant. There have been chemical methods, biological methods of spraying natural organisms, and physical methods such as ultrasonic or ozone activation methods, centrifugation methods and electrolysis methods, but these methods have a high risk of killing shellfish and seaweeds. It was not proven enough.
따라서, 현재는 적조 방제 방법으로서, 황토 또는 고분자 응집제를 살포하여 적조 생물을 흡착 또는 응집시켜 침강시키거나 회수하는 방법이 가장 널리 사용되고 있다. 그러나, 이러한 방법은 콜로이드성 입자가 응집되고 흡착되는 과정에 의해서 그 방제 효율이 Al, Fe 등의 금속 이온 함량에 비례하는 양상을 띄지만, 흡착된 황토 또는 고분자 응집제가 해수 저면에 하강 후 일정 시간이 경과하면 다시 복원되는 관계로, 적조를 일시적으로 제거하는 방법이 될 뿐이며, 그 살포량이 막대하여 재차 생태계를 파괴한다는 단점이 존재한다.Therefore, at present, as a method for controlling red tide, a method of spraying ocher or polymer flocculant to adsorb or aggregate red tide organisms to settle or recover them is most widely used. However, this method shows the fact that the control efficiency is proportional to the content of metal ions such as Al and Fe due to the aggregation and adsorption of colloidal particles, but the adsorbed ocher or polymer flocculant is lowered to the bottom of the seawater for a certain time. After this, it is restored again, and it is only a method of temporarily removing the red tide, and there is a disadvantage that the amount of spraying is huge and destroys the ecosystem again.
따라서, 본 발명은 비교적 소량을 살포하더라도 적조 방제 효과가 탁월하고, 황토 살포와 같이 그 사용방법이 매우 간편하며, 경제적이면서도, 천연 암석을 주성분으로 사용함으로써 2차 환경파괴를 최소화할 수 있는 적조 생물 방제용 조성물을 제공하고자 한다.Therefore, the present invention is excellent in red tide control effect, even when spraying a relatively small amount, very easy to use, such as loess spray, economical, red tide organisms that can minimize secondary environmental destruction by using natural rock as the main component It is to provide a composition for controlling.
본 발명은 상기 기술적 과제를 달성하기 위해서,The present invention to achieve the above technical problem,
천연 암석을 주성분으로 하는 적조 생물 방제용 조성물에 관한 것으로서, 점질도석 입자 100 중량부에 대하여 견운모 입자 40 내지 60 중량부, 형석 입자 3 내지 20 중량부 및 암면, 질석 및 페라이트로 이루어진 군으로부터 선택된 하나 이상을 포함하는 수경재배석 입자 3 내지 20 중량부를 포함하는 것을 특징으로 하는 조성물을 제공한다.The present invention relates to a composition for controlling red tide organisms based on natural rocks, wherein the composition is selected from the group consisting of 40 to 60 parts by weight of mica particles, 3 to 20 parts by weight of fluorite particles, and rock wool, vermiculite and ferrite, based on 100 parts by weight of viscous stone particles. It provides a composition comprising 3 to 20 parts by weight of hydroponic cultivation particles containing the above.
바람직하게는, 상기 조성물은 상기 견운모 입자 100 중량부에 대하여 수산화 알루미늄 5 내지 10 중량부를 더 포함한다.Preferably, the composition further comprises 5 to 10 parts by weight of aluminum hydroxide based on 100 parts by weight of the mica particles.
바람직하게는, 상기 점질도석 입자, 견운모 입자, 형석 입자 및 수경재배석 입자의 평균 입경은 각각 60 ㎛ 이하이다.Preferably, the average particle diameters of the viscous pottery particles, biotite particles, fluorite particles and hydroponic cultivation particles are 60 µm or less, respectively.
바람직하게는, 상기 적조 생물은 코클로디니움 (Cochlodinium) 속, 스켈레토네마 (Skeletonema) 속, 카에토세로스 (Chaetoceros) 속, 니츠쉬아 (Nitzschia) 속, 짐노디니움 (Gymnodinium) 속, 지로디니움 (Gyrodinium) 속, 프로로센트룸 (Prorocentrum) 속, 헤테로시그마 (Heterosigma) 속, 노티쿨라 (Noticula) 속 및 고니아울락스 (Gonyaulax) 속으로 이루어진 군으로부터 선택된 하나 이상의 적조 생물이다.Preferably, the red tide organisms are of the genus Cochlodinium, Skeletonema, Chaetoceros, Nitzschia, Gymnodinium, or Girdinium. One or more red tide creatures selected from the group consisting of the genus Gyrodinium, Prorocentrum, Heterosigma, Noticula and Gonyaulax.
또한, 본 발명은 상기 적조 생물 방제용 조성물을 해수 중에 살포함으로써 적조 생물을 방제하는 방법에 관한 것으로서, 상기 조성물의 해수 중 살포시 농도가 1 m2 당 2 내지 8 g이 되도록 살포하는 것을 특징으로 하는 적조 생물 방제 방법을 제공한다.The present invention also relates to a method of controlling red tide organisms by spraying the composition for controlling red tide organisms in seawater, wherein the composition is sprayed so that the concentration is 2 to 8 g per 1 m 2 when the composition is sprayed in seawater. Provides a method of controlling red tide creatures.
이하, 본 발명을 첨부 도면 및 실시예를 참조하여 더욱 상세히 설명하기로 한다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings and examples.
도 1은 본 발명에 따른 조성물을 현미경으로 확대하여 촬영한 사진이다.1 is a photograph taken by enlarging a composition according to the present invention under a microscope.
본 발명의 적조 생물 방제용 조성물은 4종의 입자상 천연 암석을 주성분으로서 포함하고, 수산화 알루미늄을 선택적으로 포함할 수 있다. 사용된 천연 암석 입자는 점질도석 입자, 견운모 입자, 형석 입자 및 수경재배석 입자이다.The composition for controlling red tide organisms of the present invention contains four kinds of particulate natural rock as a main component, and may optionally include aluminum hydroxide. Natural rock particles used are viscous stone particles, biotite particles, fluorite particles and hydroponic particles.
점질도석 (kaolinite, Al4Si4O10(OH)8)은, 경도 2 내지 2.5, 비중 2.6으로서 단사정계에 속하고, 결정은 미세한 육각형 또는 주상, 판상형이지만, 육안으로는 작은 비늘상이나 토상으로 보인다. 이는 주로 도자기 및 시멘트 공업의 원료가 된다. 점질도석은 원적외선 방사율이 0.913에 이르며, 이는 대부분 암석의 원적외선 방사율이 0.5 정도인 점을 감안할 때, 점질도석이 월등하게 우수한 원적외선 방사 물질임을 의미한다. 따라서, 본 발명의 조성물은 이렇게 우수한 원적외선 방사율을 갖는 점질도석을 포함함으로써, 부가적으로 원적외선에 의한 적조 생물의 방제 효과도 가질 수 있게 된다.Kaolinite (kaolinite, Al 4 Si 4 O 10 (OH) 8 ) is a monoclinic system with a hardness of 2 to 2.5 and specific gravity of 2.6, and the crystals are fine hexagonal, columnar, or plate-like, but with small scales or soils with the naked eye. see. It is primarily a raw material for the ceramics and cement industries. Viscous stone has far-infrared emissivity of 0.913, which means that viscous stone is superior far-infrared radiation material, considering that most of the rocks have far-infrared emissivity of about 0.5. Therefore, the composition of the present invention includes a viscous coating having such an excellent far-infrared emissivity, thereby additionally having a control effect of red tide organisms by far-infrared rays.
견운모 또는 세리사이트는, 단사정계에 속하는 광물로서, 원래는 결정편암, 특히 견운모편암의 주성분 광물을 의미하였으나, 오늘날에는 열수 작용으로 생긴 점토 모양의 미세한 백운모 (muscovite, KAl2AlSi3O10(OH,F)2 )를 가리킨다. 견운모의 화학성분은 백운모와 거의 같으나, 칼륨이 백운모보다 적고 수분이 다소 많다. 견운모는 도자기나 내화벽돌의 혼입재로 쓰이며, 그 밖에 도료, 전기절연체, 활마재 (滑摩材), 피부 점착력을 향상시키기 위한 화장품 재료 등 매우 다양한 용도로 활용된다. 본 발명의 조성물 중 견운모 성분은 적조 생물에 대하여 살균력을 나타내는 형석 및 수경재배석과 같은 성분들이 적조 생물에 점착되는 것을 보다 용이하게 하기 위해서 사용되었다.Cicada or sericite is a mineral belonging to the monoclinic system, originally meaning crystalline schist rock, especially the main component mineral of chondrial schist rock, but today it is a clay-like fine dolomite (muscovite, KAl 2 AlSi 3 O 10 (OH) , F) 2 ). The chemical composition of the mica is almost the same as that of the mica, but the potassium is less than that of the mica and somewhat more moisture. Cicada is used as a mixing material in ceramics or firebrick, and is also used in a wide variety of applications such as paints, electrical insulators, active materials, and cosmetic materials to improve skin adhesion. The mica component in the composition of the present invention was used to make it easier for components such as fluorspar and hydroponic cultivation to exhibit red bactericidal activity to red tide organisms.
본 발명의 조성물은, 점질도석 입자 100 중량부에 대하여 견운모 입자를 40 내지 60 중량부의 함량으로 포함하며, 견운모 입자의 함량이 상기 범위에 미달되는 경우에는 본 발명에 따른 조성물 입자들의 적조 생물에의 점착력이 떨어지는 문제점이 있으며, 상기 범위를 초과하는 경우에는 최적의 방제 효율을 얻을 수 없다는 문제점이 있다.The composition of the present invention comprises the mica particles in an amount of 40 to 60 parts by weight based on 100 parts by weight of viscous pottery particles, and when the content of the mica particles falls within the above range, There is a problem that the adhesive strength is lowered, there is a problem that the optimum control efficiency can not be obtained when it exceeds the above range.
형석 (fluorite 또는 fluorospar, CaF2)은 경도 4, 비중 3.1 내지 3.2으로서 등축정계에 속하고, 육면체의 결정 또는 팔면체의 형태를 이루며, 결정질의 덩어리나 입상의 집합체를 이루기도 한다. 일반적으로 형석은 강철 또는 알루미늄의 제조, 유리의 부식, 법랑의 제조, 납의 전기분해, 광학기기 등에 사용되는 그 용도가 매우 광범위하고 폭 넓다. 또한, 형석 입자는 그 자체에 불소를 함유하고 있으며, 따라서 이온화시에 발생된 불소 이온으로 인해서 뛰어난 살균 효과를 가지는 것으로도 알려져 있다.Fluorite (fluorite or fluorospar, CaF 2 ) has a hardness of 4 and specific gravity of 3.1 to 3.2, belongs to the equiaxed crystal system, forms hexahedral crystals or octahedrons, and forms crystalline masses or granular aggregates. Fluorite is generally used in the manufacture of steel or aluminum, the corrosion of glass, the manufacture of enamel, the electrolysis of lead, optical instruments, and the like. In addition, the fluorspar particles contain fluorine in themselves, and are therefore known to have excellent sterilizing effect due to fluorine ions generated during ionization.
본 발명의 조성물은, 점질도석 입자 100 중량부에 대하여 형석 입자를 3 내지 20 중량부의 함량으로 포함하는 것이 바람직하며, 형석 입자의 함량이 3 중량부 미만인 경우에는 형석 입자에 의한 충분한 살균 효과를 얻을 수 없다는 문제점이 있다.The composition of the present invention preferably comprises fluorite particles in an amount of 3 to 20 parts by weight with respect to 100 parts by weight of viscous pottery particles, and when the content of the fluorspar particles is less than 3 parts by weight, sufficient sterilization effect is obtained by the fluorspar particles. There is a problem that can not be.
수경재배석 (hydroponics)은 식물재배지에서 종종 사용되는 암석으로서, 식물 뿌리의 해충이나 박테리아에 대해서 뛰어난 살균력을 나타내는 암석이다.Hydroponics is a rock often used in plant cultivation. It is a rock that exhibits excellent bactericidal activity against pests and bacteria in plant roots.
본 발명의 조성물은, 점질도석 입자 100 중량부에 대하여 암면, 질석 및 페라이트로 이루어진 군으로부터 선택된 하나 이상을 포함하는 수경재배석 입자를 3 내지 20 중량부의 함량으로 포함하는 것이 바람직하며, 수경재배석 입자의 함량이 3 중량부 미만인 경우에는 수경재배석 입자에 의한 충분한 살균 효과를 얻을 수 없다는 문제점이 있다.The composition of the present invention, it is preferable that the hydroponic cultivation particles containing at least one selected from the group consisting of rock wool, vermiculite and ferrite in an amount of 3 to 20 parts by weight, based on 100 parts by weight of viscous pottery particles, When the content of the particles is less than 3 parts by weight, there is a problem in that sufficient sterilization effect by hydroponic cultivation particles cannot be obtained.
또한, 본 발명의 조성물은 부성분으로서 상기 견운모 입자 100 중량부에 대하여 수산화 알루미늄 5 내지 10 중량부를 더 포함할 수도 있다. 수산화 알루미늄은 상기 견운모 입자, 점질도석 입자, 형석 입자 및 수경재배석 입자가 해수 내에 유입되었을 때, 암석 자체가 갖는 특성상 확산이 빠르지 못한 단점을 극복하여 상기 입자들의 확산을 용이하게 하고, 그 외에도 부가적인 살균 효과를 부여하기 위해서 첨가된 것이다.In addition, the composition of the present invention may further comprise 5 to 10 parts by weight of aluminum hydroxide relative to 100 parts by weight of the mica particles as a subcomponent. Aluminum hydroxide facilitates the diffusion of these particles by overcoming the disadvantage that the diffusion of the biotite particles, viscous pottery particles, fluorite particles and hydroponic cultivation particles into the seawater is not fast diffusion due to the characteristics of the rock itself, It is added to give a sterilizing effect.
본 발명에 따른 조성물에 포함된 상기 4가지 종류의 암석 입자들의 평균 입경은 60 ㎛이하인 것이 바람직한데, 이는 평균 입경이 60 ㎛를 초과하는 경우에는 해수 내의 부유력이 약해져서 살균 효과가 떨어지고, 살균 효과의 지속시간이 짧아지기 때문이다.The average particle diameter of the four types of rock particles included in the composition according to the present invention is preferably 60 μm or less, which means that when the average particle size exceeds 60 μm, the floating force in seawater is weakened, so that the sterilizing effect is lowered and the sterilizing effect is reduced. This is because the duration of is shortened.
본 발명에 따른 조성물은, 적조를 유발시킬 수 있는 식물성 플랑크톤 및 동물성 플랑크톤 등에 폭 넓게 적용될 수 있으며, 코클로디니움 (Cochlodinium) 속, 스켈레토네마 (Skeletonema) 속, 카에토세로스 (Chaetoceros) 속, 니츠쉬아 (Nitzschia) 속, 짐노디니움 (Gymnodinium) 속, 지로디니움 (Gyrodinium) 속, 프로로센트룸 (Prorocentrum) 속, 헤테로시그마 (Heterosigma) 속, 노티쿨라 (Noticula) 속 및 고니아울락스 (Gonyaulax) 속으로 이루어진 군으로부터 선택된 하나 이상의 적조 생물에 적용될 수 있고, 특히 코클로디니움 (Cochlodinium) 속의 적조 생물에 대한 방제 효과가 뛰어나다.The composition according to the present invention can be widely applied to phytoplankton and zooplankton, etc., which can cause red tide. Genus (Nitzschia), genus Gymnodinium, genus Gyrodinium, genus Prorocentrum, genus Heterosigma, genus Naticula and genus Goniaulax It can be applied to one or more red tide creatures selected from the group consisting of, and is particularly effective in controlling red tide organisms in the genus Cochlodinium.
본 발명은 또한 상기 적조 생물 방제용 조성물을 해수 중에 살포함으로써 적조 생물을 방제하는 방법을 제공한다. 상기 조성물의 해수 중 살포 농도는, 살포시 농도가 1 m2 당 2 내지 8 g이 되는 것이 바람직하다. 살포 농도가 상기 범위를 초과하는 경우에는 경제성이 떨어진다는 문제점이 있고, 상기 범위에 미달되는 경우에는 충분한 적조 생물 방제 효과를 낼 수 없다는 문제점이 있다.The present invention also provides a method for controlling red tide organisms by spraying the composition for controlling red tide organisms in seawater. It is preferable that the spraying concentration in the seawater of the composition is 2 to 8 g per 1 m 2 when spraying. If the spraying concentration exceeds the above range, there is a problem in that the economy is inferior, and if it is less than the above range, there is a problem in that sufficient red tide biological control effect cannot be obtained.
본 발명에 따른 조성물의 상기와 같은 살포 농도는 황토 살포의 경우보다 현저하게 낮은 것이며 (황토 살포의 경우 적정 살포 농도는 1 m2 당 100 내지 400 g임), 따라서 본 발명의 조성물은 소량 살포로도 탁월한 적조 생물 방제 효과를 얻을 수 있다는 효과가 있다.Such sparging concentrations of the compositions according to the invention are significantly lower than in the case of loess sparging (in the case of loess sparging the appropriate sparging concentration is between 100 and 400 g per m 2 ), thus the composition of the present invention There is also an effect that can obtain an excellent red tide control effect.
이하, 실시예를 참조하여 본 발명을 설명하기로 한다. 하기 실시예는 본 발명을 설명하기 위한 예시적인 것일 뿐, 본 발명을 한정하는 것은 아니다.Hereinafter, the present invention will be described with reference to Examples. The following examples are merely illustrative for the purpose of illustrating the present invention and are not intended to limit the present invention.
실시예 1. 본 발명에 따른 조성물의 제조Example 1 Preparation of a Composition According to the Invention
시중에서 판매되는 쇄석기를 사용하여, 점질도석, 견운모, 형석 및 수경재배석을 평균 입경 60 ㎛ 이하의 분말상으로 분쇄하였으며, 교반기를 사용하여 점질도석 입자 100 g, 견운모 입자 50 g, 형석 입자 10 g, 및 수경재배석 10 g의 중량비로 혼합한 후, 수산화 알루미늄 분말 3.5 g을 첨가하였다. 제조된 조성물은 상온의 건조한 곳에서 보관하였다.Viscous stone, biotite, fluorspar and hydroponic cultivation were pulverized into powders with an average particle diameter of 60 μm or less using a commercially available crusher, and 100 g of viscous stone particles, 50 g of mica particles, and 10 g of fluorite particles using a stirrer. After mixing at a weight ratio of 10 g of hydroponic cultivation, 3.5 g of aluminum hydroxide powder was added. The prepared composition was stored in a dry place at room temperature.
실시예 2. 적조 생물 방제 효율에 대한 실내 실험Example 2 Indoor Experiments on Red Tide Biocontrol Efficiency
방제 대상이 되는 적조 생물로서 코클로디니움 폴리크리코이데스 (Cochlodinium polykrikoides)를 사용하였으며, 상기 생물의 배양액 중 밀도는 2,000 세포/ml이었다. 실시예 1의 조성비를 가지며 분말상 (평균 입경 60 ㎛ 이하)으로 된 조성물 1 및 직경 3 mm의 입자상으로된 조성물 2을, 10 ppm의 농도로 투입하였고, 시간에 따른 방제 효율을 하기 표 1에 나타내었다.Cochlodinium polykrikoides was used as a red tide organism to be controlled, and the density of the organism was 2,000 cells / ml. Composition 1 having a composition ratio of Example 1 and a powder composition (average particle diameter of 60 μm or less) and a composition 2 having a particle size of 3 mm in diameter were added at a concentration of 10 ppm, and control efficiency with time is shown in Table 1 below. It was.
방제 효율 = 처리 후 사멸된 개체수/처리 전 개체수 ×100 (%)Control efficiency = number of dead after treatment / number of pretreatment × 100 (%)
표 1의 결과로부터 알 수 있는 바와 같이, 본 발명에 따른 조성물은 살포 후 1 시간 이내에 코클로디니움 폴리크리코이데스를 90% 이상의 방제 효율로 사멸시킬 수 있었다.As can be seen from the results in Table 1, the compositions according to the invention were able to kill Coclodinium polycricoides with at least 90% control efficiency within 1 hour after sparging.
실시예 3. 적조 생물 방제 효율에 대한 실외 실험Example 3 Outdoor Experiments on Red Tide Biocontrol Efficiency
경남 거제 및 통영 인근의 5개 양식장에서 본 발명에 따른 조성물을 적조 예방용 및 적조 구제용으로 사용한 결과, 탁월한 예방 및 구제 효과를 나타내었다.As a result of using the composition according to the present invention for red tide prevention and red tide relief in five farms near Gyeongje Geoje and Tongyeong, it showed an excellent prevention and relief effect.
본 발명에 따른 조성물은 비교적 소량을 살포하더라도 적조 방제 효과가 탁월하고, 황토 살포와 같이 그 사용방법이 매우 간편하며, 경제적이면서도, 천연 암석을 주성분으로 사용함으로써 2차 환경파괴를 최소화할 수 있다.The composition according to the present invention is excellent in red tide control effect even when spraying a relatively small amount, very easy to use, such as loess spray, economical, it is possible to minimize the secondary environmental destruction by using natural rock as the main component.
도 1은 본 발명에 따른 조성물을 현미경으로 확대하여 촬영한 사진이다.1 is a photograph taken by enlarging a composition according to the present invention under a microscope.
Claims (5)