KR100466270B1 - Adhesive pad for sports shoes and sports shoes attached with the same - Google Patents
Adhesive pad for sports shoes and sports shoes attached with the same Download PDFInfo
- Publication number
- KR100466270B1 KR100466270B1 KR10-2001-0065932A KR20010065932A KR100466270B1 KR 100466270 B1 KR100466270 B1 KR 100466270B1 KR 20010065932 A KR20010065932 A KR 20010065932A KR 100466270 B1 KR100466270 B1 KR 100466270B1
- Authority
- KR
- South Korea
- Prior art keywords
- ball
- latex
- layer
- weight
- parts
- Prior art date
Abstract
본 발명은 축구화 또는 럭비화의 공과의 마찰력을 크게 함으로써 공의 회전을 증가시켜 공의 방향성과 거리감을 용이하게 조절할 수 있도록 운동화에 부착 가능한 점착형 패드 및 이를 부착시킨 운동화에 관한 것으로, 이형지 위에 점착제층이 형성되고, 상기 점착제층 위에, 라텍스 100 중량부에 대하여 계면활성제 0.001∼0.1 중량부, 충전제 1∼100 중량부, 및 안료를 혼합하여 형성된 라텍스층에 입도 2000∼16 메쉬의 연마재가 15∼1000 g/㎡의 양으로 부착된 층이 형성된 것을 특징으로 하는 본 발명의 운동화용 점착형 패드는, 공을 찼을 때 공의 회전율을 크게 증가시키므로 공의 방향성과 거리감을 사용자가 조절하기 쉽게 만들어주는데, 접착 테이프와 같은 롤 형상으로 제조되므로, 필요에 따라 사용자 임의로 칼이나 가위를 사용해서 적절한 형상 및 크기로 재단해서 운동화 외면의 공과 접촉하는 부분에만 접착하여 편리하게 사용할 수 있으며, 장시간 사용하여도 쉽게 마모 및 박리되지 않는다는 효과가 있다.The present invention relates to a pressure-sensitive adhesive pad and a sneaker attached to the sneaker so as to increase the rotation of the ball by increasing the friction force with the ball of soccer shoes or rugby shoes and to easily adjust the sense of direction and distance of the ball, the adhesive on the release paper A layer was formed, and the abrasive having a particle size of 2000 to 16 mesh was formed in the latex layer formed by mixing 0.001 to 0.1 parts by weight of surfactant, 1 to 100 parts by weight of filler, and pigment to 100 parts by weight of latex on the pressure sensitive adhesive layer. Adhesive pad for sneakers of the present invention, characterized in that the layer formed in an amount of 1000 g / ㎡ is attached, the ball rotation rate of the ball is greatly increased when the ball is filled, making the direction and distance of the ball easier to control the user Since it is manufactured in roll shape like adhesive tape, user can use knife or scissors arbitrarily Can conveniently by only bonding ball and the contact portions of the shoes to be cut into the outer surface, and the effect is not easily peeled off by wear and prolonged use.
Description
본 발명은 축구화 또는 럭비화의 공과의 마찰력을 크게 함으로써 공의 회전을 증가시켜 공의 방향성과 거리감을 용이하게 조절할 수 있도록 운동화에 부착 가능한 점착형 패드 및 이를 부착시킨 운동화에 관한 것이다.The present invention relates to a pressure-sensitive adhesive pad attachable to sneakers and sneakers attached thereto so as to increase the rotation of the ball by increasing the friction force with the ball of soccer shoes or rugby shoes to easily adjust the direction and distance of the ball.
축구나 럭비와 같이 발을 사용하여 공을 제어하는 운동 종목에서 운동화의 역할은 특히 중요하다고 할 수 있다. 종래의 축구화는 외피의 재질이나 표지의 재봉선, 발의 회전 각도 등에 의하여 공의 움직임을 미세하게 조절하게 되어 있는데, 공과 축구화의 밀착이 제대로 이루어지지 않으면 목적하는 대로 공의 방향과 거리를 조절하기가 쉽지 않게 된다. 특히 우천시 또는 다른 영향으로 축구화가 물에 젖을 경우에는 공과의 마찰력이 더욱 낮아지기 때문에, 공이 미끄러진다거나 공이 움직이는 방향이나 거리 등을 조절하지 못하는 일이 속출하게 된다.The role of sneakers is particularly important in sports that control the ball using the feet, such as football or rugby. Conventional soccer shoes finely control the movement of the ball by the material of the jacket, the seam of the cover, the angle of rotation of the foot, etc., if the contact between the ball and soccer shoes is not properly made, it is easy to adjust the direction and distance of the ball as desired Will not. In particular, when the soccer shoes are wet with water due to rain or other effects, the frictional force between the ball is further lowered, so that the ball slips or fails to control the direction or distance the ball moves.
축구화의 이와 같은 문제를 해결하기 위한 기술로, 대한민국 실용신안 공개 1999-36009(1999. 11. 5)에서는 축구화의 내측과 외측에 볼과의 접촉시 반발작용을 하는 실리콘으로 된 돔 형태의 탄력적인 볼록부를 열프레스 공법으로 형성하고 있으며, 대한민국 특허 공개 10-2001-25630(2001. 4. 6)에서는 내부에 탄력체가 설치된 회전돌기를 축구화의 앞부분 내측과 외측에 설치하는 기술을 개시하고 있다. 또한, 대한민국 실용신안 공개 2000-3368(2000. 2. 15)에서는 찰고무 표면에 돌기가 형성된 덧신 형태의 보조용품을 운동화 외면에 밀착 고정하도록 하고 있다.As a technology to solve such problems of soccer shoes, Korean Utility Model Publication 1999-36009 (1999. 11. 5) is a dome-shaped elastic of silicone that reacts to the ball on the inside and outside of the soccer shoes. The convex portion is formed by the heat press method, and Korean Patent Laid-Open Publication No. 10-2001-25630 (April 6, 2001) discloses a technique for installing a rotating protrusion having an elastic body installed inside and outside the front part of a soccer shoe. In addition, the Republic of Korea Utility Model Publication 2000-3368 (February 15, 2000) is to be fixed to the outer surface of the sneakers in the form of an overshoe type with protrusions formed on the surface of the rubber rubber.
그러나, 이처럼 축구화 내측과 외측에 볼록부 또는 회전돌기를 형성하는 기술은 추가적인 공정이 필요할 뿐 아니라, 시간이 지남에 따라 돌기 등이 떨어져나가거나 마모된다는 단점이 있다. 또한, 축구화에 덧신 형태로 부착한 보조용품도 격렬한 동작에 의해 표면이 마모되거나 떨어지기 쉽고, 한 번 떨어지면 다시 부착하기 어려울 뿐 아니라, 무엇보다도 공과의 마찰력을 충분히 크게 하지 못한다는 것이 문제가 된다.However, such a technique of forming convex portions or rotating protrusions on the inside and outside of the soccer shoe not only requires an additional process, but also has the disadvantage that the protrusions fall or wear out over time. In addition, the auxiliary article attached to the shoe in the form of an oversized shoe is a problem that the surface is easily worn or dropped by the violent motion, it is difficult to reattach once dropped, and above all, the friction force of the ball is not large enough.
본 발명의 목적은 종래의 축구화가 갖는 이러한 문제점을 해결하기 위한 것으로, 축구화 또는 럭비화의 표면에 부착하여 공과의 마찰력을 증가시키기 위한 운동화용 점착형 패드로서, 사용자 임의로 필요한 부위에 적절한 크기로 용이하게 탈부착할 수 있으며 장시간 사용하여도 마모 및 박리되지 않으면서, 공과의 접촉시공의 회전을 증가시켜 공의 방향성과 거리감을 조절하기에 충분한 마찰력을 부여할 수 있도록 된 운동화에 부착하기 위한 점착형 패드 및 이를 부착시킨 운동화를 제공하는 것을 목적으로 한다.An object of the present invention is to solve this problem of the conventional soccer shoes, the adhesive pad for sneakers to increase the frictional force with the ball by attaching to the surface of the soccer shoes or rugby shoes, easy to the appropriate size to the user's arbitrarily necessary site Adhesive pad for attaching to sneakers that can be attached and detached, and can be given sufficient friction to adjust the direction and distance of the ball by increasing the rotation of contact construction with the ball without wear and peeling even after long use And to provide a sneaker attached thereto.
도 1은 본 발명에 따른 운동화용 점착형 패드의 제조 방법을 공정별로 도시한 것,Figure 1 shows the manufacturing method of the pressure-sensitive adhesive pad for sneakers according to the present invention,
도 2는 본 발명의 운동화용 점착형 패드를 부착시킨 운동화를 제조하는 과정을 공정별로 도시한 것.Figure 2 shows the process for producing a sneaker attached to the adhesive pad for sneakers of the present invention by process.
상기 목적을 달성하기 위하여 본 발명에서는,In the present invention to achieve the above object,
이형지 위에 점착제층이 형성되고,An adhesive layer is formed on the release paper,
상기 점착제층 위에, 라텍스 100 중량부에 대하여 계면활성제 0.001∼0.1 중량부, 충전제 1∼100 중량부, 및 안료를 혼합하여 형성된 라텍스층에 입도 2000∼16 메쉬의 연마재가 15∼1000 g/㎡의 양으로 부착된 층이 형성된 것을 특징으로 하는, 운동화에 부착시켜 공과의 마찰력을 증가시키기 위한 점착형 패드를 제공한다.In the latex layer formed by mixing 0.001 to 0.1 parts by weight of surfactant, 1 to 100 parts by weight of filler, and pigment to 100 parts by weight of latex on the pressure sensitive adhesive layer, the abrasive having a particle size of 2000 to 16 mesh was 15 to 1000 g / m 2. A positively attached layer is provided, which provides a sticky pad for attaching to sneakers to increase friction with the ball.
이상과 같은 운동화에 부착시켜 공과의 마찰력을 증가시키기 위한 점착형 패드의 제조방법은,Method of producing a pressure-sensitive adhesive pad for adhering to the sneakers as described above to increase friction with the ball,
라텍스 100 중량부에 대하여 계면활성제 0.001∼0.1 중량부, 충전제 1∼100 중량부, 및 안료를 첨가하여 혼합하고,0.001 to 0.1 parts by weight of surfactant, 1 to 100 parts by weight of filler, and pigment are added to 100 parts by weight of latex and mixed,
상기 혼합물을 이형지에 도포한 후 건조하여 라텍스층을 형성하고,After applying the mixture on a release paper and dried to form a latex layer,
고전압을 사용하여 상기 라텍스층에 입도 2000∼16 메쉬의 연마재를 15∼1000 g/㎡의 양으로 부착시키고, 건조하여 경화시킨 후, 이형지를 분리하여 연마재가 부착된 라텍스층을 형성하고,After attaching the abrasive having a particle size of 2000 to 16 mesh in an amount of 15 to 1000 g / m 2 to the latex layer using a high voltage, drying and curing, the release paper was separated to form a latex layer with the abrasive,
별도의 이형지에 점착제를 도포한 후 예열하여 점착제층을 형성하고,After applying the pressure-sensitive adhesive on a separate release paper to form a pressure-sensitive adhesive layer,
상기 점착제층 위에 상기 연마재가 부착된 라텍스층을 부착시키는 단계를 포함하는 것을 특징으로 한다.And attaching the latex layer to which the abrasive is attached onto the pressure-sensitive adhesive layer.
또한, 본 발명에서는 상기와 같이 제조된 점착형 패드를 부착하여 제조된 운동화를 제공한다.In addition, the present invention provides a sneaker prepared by attaching the adhesive pad prepared as described above.
본 발명의 운동화용 점착형 패드 제조시 사용되는 라텍스는 천연고무 라텍스와 합성고무 라텍스를 공중합하여 얻은 고유연성, 고내열성, 고내수성의 라텍스로서, 예를 들어 LN470 계열(Bayer 사 제조) 등을 사용할 수 있다. 또한, 라텍스층에 부착되는 연마재는 가죽 연마를 위한 제품 제조시 사용되는 원재료 중 하나인 천연 또는 합성 연마재로서 입도 2000∼16 메쉬의 것이 바람직하며, 예를 들어, 에머리(Emery), 규사와 같은 천연 연마제나, 산화알루미늄, 실리콘 카바이드, 지르코늄 등의 합성 연마제를 사용할 수 있다. 그리고, 이러한 연마재가 부착된 라텍스층을 운동화에 부착시키는 점착제층을 형성하기 위한 점착제로는 고내열성, 고방수성을 점착제로서, 예를 들어, 폴리비닐롤 수지, 폴리에스테르 수지, 폴리에틸렌 수지, 폴리비닐아세테이트 수지 등이나 이들을 베이스로 한 점착제 등을 사용할 수 있다.The latex used in manufacturing the pressure-sensitive adhesive pad for sneakers of the present invention is a high-flexibility, high heat resistance, high water resistance latex obtained by copolymerizing natural rubber latex and synthetic rubber latex, and for example, LN470 series (manufactured by Bayer) can be used. Can be. In addition, the abrasive attached to the latex layer is a natural or synthetic abrasive, which is one of the raw materials used in the manufacture of products for leather polishing, preferably of a particle size of 2000 to 16 mesh, for example, natural such as Emery, silica An abrasive | polishing agent and synthetic abrasives, such as aluminum oxide, a silicon carbide, zirconium, can be used. In addition, the pressure-sensitive adhesive for forming the pressure-sensitive adhesive layer for attaching the latex layer with the abrasive to the sneakers is a high heat resistance and high water resistance as the pressure-sensitive adhesive, for example, polyvinyl roll resin, polyester resin, polyethylene resin, polyvinyl Acetate resins and the like and adhesives based thereon.
본 발명에 따른 운동화용 점착형 패드는 연마재가 부착된 라텍스층을 이형지 상에 형성된 점착제층 위에 부착시켜 접착 테이프와 같은 롤 형상으로 제조되는 것으로, 필요에 따라 사용자 임의로 칼이나 가위를 사용해서 적절한 형상 및 크기로 재단하여 운동화 외면의 공과 접촉하는 부분에만 부착하여 사용할 수 있다.The adhesive pad for sneakers according to the present invention is manufactured in a roll shape such as an adhesive tape by attaching a latex layer with an abrasive on an adhesive layer formed on a release paper. And cut to size and can be used only attached to the contact with the ball on the outer surface of the sneakers.
즉, 운동화 외면의 공과 접촉하는 면에 부착되는 점착형 패드를 라텍스에 연마재를 부착하고 경화시켜 형성함으로써, 장시간 사용하여도 마모 및 박리되지 않으면서, 공과의 마찰력을 크게 증대시켜 공의 회전을 증가시키므로 공의 방향성과 거리감을 쉽게 조절할 수 있도록 해준다.That is, the adhesive pad attached to the surface in contact with the ball on the outer surface of the sneaker is formed by attaching and curing the abrasive to the latex, thereby greatly increasing the friction force of the ball and increasing the rotation of the ball without abrasion and peeling even after long use. This makes it easy to adjust the direction and distance of the ball.
이하, 도면을 참조하여 본 발명에 따른 운동화용 점착형 패드 및 이를 부착한 운동화의 제조 방법을 구체적으로 설명한다.Hereinafter, with reference to the drawings will be described in detail a pressure-sensitive adhesive pad for sneakers and a method of manufacturing the sneakers attached thereto.
도 1은 본 발명에 따른 운동화용 점착형 패드의 제조 방법을 공정별로 도시한 것이다.Figure 1 shows the manufacturing method of the pressure-sensitive adhesive pad for sneakers according to the present invention.
먼저, 라텍스 100 중량부에 대하여 계면활성제 0.001∼0.1 중량부, 충전제 1∼100 중량부, 및 내수성 안료 0.01∼10 중량부를 혼합, 교반하여 라텍스 혼합물을 제조한다.First, 0.001 to 0.1 parts by weight of surfactant, 1 to 100 parts by weight of filler, and 0.01 to 10 parts by weight of water-resistant pigment are mixed and stirred with respect to 100 parts by weight of latex to prepare a latex mixture.
라텍스 혼합물을 정밀한 롤러를 사용하여 이형지(1)에 0.3∼8 ㎜의 두꼐로 도포한 후, 40∼60 ℃에서 30∼150 초 동안 가건조하여 라텍스층(2)을 형성한다(도 1a 및 1b).The latex mixture is applied to the release paper 1 with a thickness of 0.3 to 8 mm using a precision roller, and then dried at 40 to 60 ° C. for 30 to 150 seconds to form the latex layer 2 (FIGS. 1A and 1B). ).
고전압을 사용하여 가건조된 라텍스층(2)에 입도 2000∼16 메쉬의 천연 또는 합성 연마재를 15∼1000 g/㎡의 양으로 부착시키고, 연마재가 라텍스층 내부로 완전히 침투될 때까지 80∼130 ℃의 저온에서 건조시킨 후, 연마제의 침투 상태를 확인하여 100∼150 ℃에서 완전히 경화시킨다(도 1c).A natural or synthetic abrasive having a particle size of 2000 to 16 mesh is attached to the latex layer 2 temporarily dried using high voltage in an amount of 15 to 1000 g / m 2, and 80 to 130 until the abrasive fully penetrates into the latex layer. After drying at low temperature, the penetration state of the abrasive was checked and completely cured at 100 to 150 ° C (FIG. 1C).
연마재가 부착된 라텍스층(3)이 경화된 후 이형지(1)를 분리시킨다(도 1d).After the latex layer 3 with the abrasive is cured, the release paper 1 is separated (FIG. 1D).
별도의 이형지(11)에 고내열성, 고방수성 점착제를 0.3∼8 ㎜의 두꼐로 도포한 후, 점착 성능을 최대화 하기 위해 40∼60 ℃에서 예열하여 점착제층(4)을 형성한다(도 1e 및 1f).After applying a heat-resistant, highly water-resistant pressure-sensitive adhesive with a thickness of 0.3 to 8 mm on a separate release paper 11, and preheated at 40 to 60 ℃ to maximize the adhesive performance to form the pressure-sensitive adhesive layer (4) (Fig. 1E and 1f).
예열된 점착제층(4) 위에 상기 연마재가 부착된 라텍스층(3)을 부착한 후 적절한 압력으로 가압하여 본 발명의 점착형 패드를 형성한다(도 1g).After attaching the latex layer 3 with the abrasive on the preheated pressure-sensitive adhesive layer 4, the pressure-sensitive adhesive pad of the present invention is formed by pressing at an appropriate pressure (FIG. 1g).
본 운동화용 점착형 패드를 사용할 때는 이형지(11)를 제거하고 점착제층(4)을 운동화면에 압착하여 접착시킨다(도 1h).When using the pressure-sensitive adhesive pad for sneakers, the release paper 11 is removed, and the pressure-sensitive adhesive layer 4 is pressed and adhered to the exercise screen (FIG. 1H).
도 2는 본 발명의 운동화용 점착형 패드를 부착시킨 운동화를 제조하는 과정을 공정별로 도시한 것이다.Figure 2 shows the process for producing a sneaker attached to the adhesive pad for sneakers of the present invention by process.
운동화에 부착하기 위한 연마재가 부착된 라텍스층을 형성하는 과정은 위와 동일하다(도 1a∼1d).The process of forming a latex layer with an abrasive for attaching to sneakers is the same as above (FIGS. 1A-1D).
별도의 이형지(21)에 고내열성, 고방수성, 고접착성의 2액형 합성수지 접착제를 0.5∼8 ㎜의 두꼐로 도포한 후, 접착 성능을 최대화 하기 위해 80∼100 ℃에서 예열하여 접착제층(5)을 형성한다(도 2a 및 2b).High heat resistance, high water resistance and high adhesion two-component synthetic resin adhesive is applied to a separate release paper 21 at a thickness of 0.5 to 8 mm, and then preheated at 80 to 100 ° C. to maximize adhesive performance. To form (FIGS. 2A and 2B).
예열된 접착제층(5) 위에 상기 연마재가 부착된 라텍스층(3)을 부착한 후 적절한 압력으로 가압하여 접착제층(5) 위에 연마재가 부착된 라텍스층(3)을 형성한다(도 2c).The latex layer 3 with the abrasive is attached onto the preheated adhesive layer 5 and then pressurized at an appropriate pressure to form the latex layer 3 with the abrasive on the adhesive layer 5 (FIG. 2C).
여기에서 이형지(21)를 제거한 후 축구화 또는 럭비화를 제조하기 위한 소재에 부착하고, 접착력을 유지하기 위하여 120∼140 ℃에서 완전 경화시킨다(도 2d). 이와 같이 제조된 소재를 사용하여 축구화 또는 럭비화를 제조한다.The release paper 21 is removed here, and then attached to a material for manufacturing soccer shoes or rugby shoes, and completely cured at 120 to 140 ° C. to maintain adhesive strength (FIG. 2D). Using the material prepared as described above, soccer shoes or rugby shoes are manufactured.
이하, 실시예를 통하여 본 발명을 더욱 상세히 설명한다. 단, 이들 실시예는 본 발명의 예시일 뿐, 본 발명의 범위가 이들만으로 제한되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples. However, these Examples are only illustrative of the present invention, and the scope of the present invention is not limited thereto.
[실시예 1] 운동화용 점착형 패드의 제조Example 1 Preparation of an Adhesive Pad for Running Shoes
먼저, 라텍스 100 중량부에 대하여 계면활성제로서 EU00113, NXZ 및 SPAN 80의 혼합물 0.04 중량부, 충전제로서 침강탄산칼슘 18 중량부, 및 내수성 안료로서 산화철, 티타늄, 및 유기 염료 2.8 중량부를 혼합하고 20 분간 교반하여 라텍스 혼합물을 제조하였다.First, 0.04 parts by weight of a mixture of EU00113, NXZ, and SPAN 80 as a surfactant, 18 parts by weight of precipitated calcium carbonate as a filler, and 2.8 parts by weight of iron oxide, titanium, and an organic dye as a water-resistant pigment were mixed with respect to 100 parts by weight of latex, and mixed for 20 minutes. Stirring made a latex mixture.
라텍스 혼합물을 롤러를 사용하여 이형지에 약 4 ㎜의 두꼐로 도포한 후, 약 60 ℃에서 약 90 초 동안 가건조하여 라텍스층을 형성하였다.The latex mixture was applied to a release paper with a roller at a thickness of about 4 mm and then dried at about 60 ° C. for about 90 seconds to form a latex layer.
25,000 V의 고전압을 사용하여 가건조된 라텍스층에 입도 2000∼16 메쉬의 천연 또는 합성 연마재로서 산화알루미늄과 에머리를 약 372 g/㎡의 양으로 부착시키고, 약 80 ℃에서 건조시킨 후, 다시 130 ℃ 이상으로 건조하여 완전히 경화시켰다.Aluminum oxide and emery were adhered to an amount of about 372 g / m 2 as a natural or synthetic abrasive having a particle size of 2000 to 16 mesh to a latex layer temporarily dried using a high voltage of 25,000 V, dried at about 80 ° C., and then again 130 It dried over C and hardened completely.
연마재가 부착된 라텍스층이 경화된 후 이형지를 분리시켜, 연마재가 부착된 라텍스층을 형성하였다.After the latex layer with the abrasive was cured, the release paper was separated to form a latex layer with the abrasive.
별도의 이형지에 고내열성, 고방수성 점착제로서 폴리비닐롤 수지를 약 5 ㎜의 두께로 도포한 후, 약 60 ℃에서 예열하여 점착제층을 형성하였다.The polyvinyl roll resin was applied to a separate release paper as a high heat resistant and high waterproof adhesive to a thickness of about 5 mm, and then preheated at about 60 ° C. to form an adhesive layer.
예열된 점착제층 위에 상기 연마재가 부착된 라텍스층을 부착한 후 적절한 압력으로 가압하여 본 발명의 점착형 패드를 제조하였다.The pressure-sensitive adhesive pad of the present invention was prepared by attaching the latex layer having the abrasive attached on the preheated pressure-sensitive adhesive layer and then pressing it at an appropriate pressure.
[실시예 2] 본 발명의 점착형 패드를 부착시킨 운동화의 제조[Example 2] Preparation of sneakers to which the adhesive pad of the present invention was attached
이형지에 고내열성, 고방수성, 고접착성의 2액형 합성수지 접착제로서 에폭시수지 LER 850을 약 5 ㎜의 두꼐로 도포한 후, 약 90 ℃에서 예열하여 접착제층을형성하였다.Epoxy resin LER 850 was applied to a release paper with a thickness of about 5 mm as a high heat resistance, high water resistance, and high adhesion two-component synthetic resin adhesive, and then preheated at about 90 ° C. to form an adhesive layer.
예열된 접착제층 위에 실시예 1에서 제조한 연마재가 부착된 라텍스층을 부착한 후 적절한 압력으로 가압하여 접착제층 위에 연마재가 부착된 라텍스층을 형성하였다.The latex layer with the abrasive prepared in Example 1 was attached onto the preheated adhesive layer and then pressurized at an appropriate pressure to form a latex layer with the abrasive attached on the adhesive layer.
이형지를 제거한 후 축구화를 제조하기 위한 소재에 부착하고, 130 ℃ 이상에서 완전 경화시킨 후, 본 재료를 사용하여 축구화를 제조하였다.After removing the release paper, it was attached to a material for producing soccer shoes, and after completely cured at 130 ° C. or higher, soccer shoes were manufactured using the present material.
[효과시험예][Effective test example]
본 발명의 운동화용 점착형 패드를 14 ㎜×7 ㎜의 직사각형으로 절단하여 축구화 앞면 좌측과 우측에 부착한 축구화와 일반 축구화를 가지고 동일 조건 하에서 실험하였다. 즉, 공을 찼을 때 공의 회전율 증가에 따른 공의 각도를 측정하고, 공의 최초 지점으로부터 최종 정지점까지 공의 경로를 각도로 비교하였다.The adhesive pad for sports shoes of the present invention was cut into a rectangle of 14 mm x 7 mm and experimented under the same conditions with a soccer shoe and a general soccer shoe attached to the front left and right sides of the soccer shoe. That is, the angle of the ball was measured as the ball rotation rate was increased when the ball was filled, and the path of the ball from the initial point of the ball to the final stop point was compared in degrees.
먼저, 축구 경기장의 임의의 한 지점에서 공을 시축하여 공이 회전하며 진행한 최종 정지점까지의 경로를 표시하였다. 공의 최초 시작점과 최조 정지점을 직선으로 연결하고 실험자의 정면에 대하여 각도를 측정하였다.First, the ball was trialized at any one point of the football stadium to indicate the path to the final stop where the ball rotated. The initial starting point and the lowest stop of the ball were connected in a straight line and the angle was measured with respect to the front of the experimenter.
동일 조건을 유지하기 위하여 실험자가 1회 시축시마다 본 발명의 점착형 패드를 부착한 축구화와 일반 축구화를 교체 착용하였다.In order to maintain the same condition, the experimenter alternately wore a soccer shoe and a general soccer shoe attached with a sticky pad of the present invention every time.
시축 총횟수는 맑은 날씨에 40 회, 우천시에 40 회로 하였다.The total number of trials was 40 times in clear weather and 40 times in rainy weather.
다음 표 1 및 2는 위와 같이 본 발명의 운동화용 점착형 패드를 부착한 축구화와 일반 축구화를 신고 시축한 후 측정한 각도를 나타낸 것으로, 표 1은 맑은 날씨, 표 2는 우천시의 측정 결과이다.The following Tables 1 and 2 show the angles measured after wearing the soccer shoes and the general soccer shoes to which the adhesive pad for sneakers of the present invention is attached as described above, Table 1 is the clear weather, and Table 2 is the measurement result in rainy weather.
위 표에서 보듯이, 본 발명에 따른 운동화용 점착형 패드를 부착한 축구화를 신고 시축하였을 때 일반 축구화에 비하여 공의 회전 각도가 맑은 날씨에는 평균 2.5 배, 우천시에는 평균 2.45 배의 결과가 나왔다. 따라서, 본 축구화는 일반 축구화에 비하여 공의 회전율을 크게 증가시켜 공의 방향 및 거리를 사용자가 원하는 대로 쉽게 조절할 수 있게 해주는 것을 알 수 있다.As shown in the above table, when the soccer shoes attached to the sneakers adhesive pad according to the present invention was put on and tested, the average rotation angle of the ball was 2.5 times in clear weather and 2.45 times in rainy weather, compared to general soccer shoes. Therefore, the present soccer shoes can be seen that the user can easily adjust the direction and distance of the ball as desired by greatly increasing the rotation rate of the ball compared to the general soccer shoes.
이상에서 살펴 본 바와 같이, 축구화 또는 럭비화의 표면에 부착하여 공과의 마찰력을 증가시키기 위한 본 발명의 운동화용 점착형 패드는, 공을 찼을 때 공의 회전율을 크게 증가시키므로 공의 방향성과 거리감을 사용자가 조절하기 쉽게 만들어 준다.As described above, the adhesive pad for sneakers of the present invention for adhering to the surface of soccer shoes or rugby shoes to increase the frictional force with the ball, since the rotation rate of the ball is greatly increased when the ball is filled, the direction and distance of the ball Make it easy for users to adjust.
더우기, 본 발명의 운동화용 점착형 패드는 접착 테이프와 같은 롤 형상으로 제조되므로, 필요에 따라 사용자 임의로 칼이나 가위를 사용해서 적절한 형상 및 크기로 재단해서 운동화 외면의 공과 접촉하는 부분에만 접착하여 편리하게 사용할수 있으며, 장시간 사용하여도 쉽게 마모 및 박리되지 않는다는 장점도 있다.In addition, since the adhesive pad for sneakers of the present invention is manufactured in a roll shape such as an adhesive tape, it is convenient for the user to cut it into a shape and size appropriately by using a knife or scissors, and to adhere only to the part in contact with the ball of the outer surface of the sneaker as needed. It can be used easily, and it can be easily worn and peeled off even if used for a long time.
Claims (3)