KR100457697B1 - Rubber Specimen and its Clamping Jig - Google Patents
Rubber Specimen and its Clamping Jig Download PDFInfo
- Publication number
- KR100457697B1 KR100457697B1 KR10-2003-0089787A KR20030089787A KR100457697B1 KR 100457697 B1 KR100457697 B1 KR 100457697B1 KR 20030089787 A KR20030089787 A KR 20030089787A KR 100457697 B1 KR100457697 B1 KR 100457697B1
- Authority
- KR
- South Korea
- Prior art keywords
- specimen
- grip
- rubber
- support plate
- fastening
- Prior art date
Abstract
본 발명은 고무시편 및 그 체결용 지그에 관한 것으로, 얇은 원판형상으로 다수개의 체결부(11)가 방사상으로 형성되되, 그 두께(T)는 1mm이고 전체 직경(D1)은 75mm이며 상기 체결부(11)의 끝단을 이루는 가상의 내원(13)의 직경(D2)은 54mm로 형성되며, 상기 체결부(11)와 인접한 체결부(11) 사이에는 홈(12)이 형성되며 그 폭(W)은 2.5mm로 이루어지는 고무시편(10)이 구비되는 한편, 평탄한 상부면을 갖는 그립하면지지판(21)이 구비되고; 상기 그립하면지지판(21)의 중앙에 동심상으로 돌출성형되며 상부면에는 상기 고무시편(10)이 안착되는 시편지지판(22)이 형성되며; 상기 시편지지판(22)의 상부면에는 가는 핀형상의 시편고정핀(23)이 다수개 설치되고; 상기 시편지지판(22)의 외곽으로 배치되되, 상기 시편지지판(22)을 중심으로 등각으로 이격배치된 다수개의 그립측면지지블록(24)이 형성되며; 상기 그립측면지지블록(24)의 외곽으로 배치되되, 상기 시편지지판(22)을 중심으로 등각으로 이격배치되는 다수개의 그립후면지지핀(25)이 형성되어 이루어진 지그(20)가 구비되어, 상기 지그(20)에 의해 상기 고무시편(10)을 체결하도록 된 그립(30)의 전·후·좌·우 및 바닥면이 확실하게 지지됨과 동시에, 고무시편(10)과의 정확한 체결위치에 고정될 수 있게 되어 인장시험의 신뢰성을 향상시킬 수 있도록 된 것이다.The present invention relates to a rubber specimen and a jig for fastening thereof, wherein a plurality of fastening portions 11 are formed radially in a thin disk shape, the thickness T of which is 1 mm, and the overall diameter D 1 is 75 mm. The diameter D 2 of the virtual inner circle 13 forming the end of the portion 11 is 54 mm, and a groove 12 is formed between the fastening portion 11 and the adjacent fastening portion 11 and the width thereof. (W) is provided with a rubber specimen (10) made of 2.5mm, while the grip plate having a flat upper surface is provided with a support plate (21); When the grip is formed in the center of the support plate 21 concentrically protruding and the upper surface is formed with a specimen support plate 22 on which the rubber specimen 10 is seated; On the upper surface of the specimen support plate 22, a plurality of fine pin-shaped specimen fixing pins 23 are installed; A plurality of grip side support blocks (24) disposed at an outer side of the specimen support plate (22) and spaced at an equidistant center around the specimen support plate (22); The grip side support block 24 is disposed on the outside of the jig 20 is provided with a plurality of grip rear support pins 25 are formed to be equidistantly spaced about the specimen support plate 22, the The jig 20 securely supports the front, rear, left, right, and bottom surfaces of the grip 30 to fasten the rubber specimen 10 and is fixed at the correct fastening position with the rubber specimen 10. It is possible to improve the reliability of the tensile test.
Description
본 발명은 고무시편 및 이 고무시편을 체결할 때 사용하는 지그(Jig)에 관한 것으로, 특히 정확한 실험결과의 도출에 알맞도록 제작된 고무시편과 이 고무시편을 방사방향으로 신장시키는 그립과의 정확한 체결을 유도하도록 다수의 가이드가 형성된 고무시편 체결용 지그에 관한 것이다.The present invention relates to rubber specimens and jigs (Jig) used when fastening the rubber specimens, and in particular, the rubber specimen and the grip that radially stretches the rubber specimens are made to be suitable for deriving accurate test results. It relates to a rubber specimen fastening jig formed with a plurality of guides to induce fastening.
일반적으로, 고무재료는 대변형 특성과 큰 변형률 범위에서 높은 탄성을 갖는 특성 때문에 다양한 산업분야에서 활용도가 증대되고 있는데, 특히 자동차, 항공기, 일반기계, 사무기계, 산업기계, 의료기계 등을 비롯하여 많은 부분에서 중요한 요소부품으로 그 사용분야가 더욱 확대되고 있다. 이에 따라 고무재료의 정확한 물성측정이 요소부품 설계의 중요한 인자인 동시에, 중요한 설계자료가 된다.In general, rubber materials have increased application in various industrial fields due to their large deformation characteristics and high elasticity in a large strain range, especially automobiles, aircraft, general machines, office machines, industrial machines, medical machines, etc. It is an important component part in the field, and its field of use is further expanded. Therefore, accurate physical property measurement of rubber material is an important factor in the design of component parts, and also becomes an important design data.
한편 최근에는 유한요소법을 이용한 설계기법이 많이 활용되고 있는데, 특히 고무류부품의 유한요소해석에서는 비선형특성을 나타내는 고무재료의 물성값을 정확하게 입력하는 것이 중요하기 때문에 고무재료의 정확한 응력과 변형률 특성을 얻어야 된다. 상기 물성을 측정하기 위해 단순인장 및 압축 그리고 순수전단시험등의 재료실험이 활용되고 있다.Recently, the design technique using the finite element method has been used a lot. Especially, in the finite element analysis of rubber parts, it is important to accurately input the physical property values of the rubber material exhibiting the nonlinear characteristics. Therefore, it is necessary to obtain accurate stress and strain characteristics of the rubber material. . In order to measure the physical properties, material experiments such as simple tensile and compression and pure shear tests are used.
그러나 고무시편의 단순압축시험의 경우, 상기 고무시편과 접촉하는 압축그립의 접촉면 표면마찰 때문에 고무재료 측면에 부풀어 오르는 현상(Barelling)이 발생되며, 이러한 현상 때문에 정확한 응력과 변형률값을 얻기가 불가능하다.However, in the simple compression test of rubber specimens, the swelling of the side of the rubber material occurs due to the surface friction of the contact surface of the compression grip in contact with the rubber specimen, and thus it is impossible to obtain accurate stress and strain values. .
이러한 문제점을 보완하기 위해 마찰면에 윤활제를 도포하고 압축실험을 실시하지만 높은 압축하중에서 접촉면의 윤활막 형성이 파괴되고 측면이 부풀어 오르는 현상이 발생된다. 높은 하중에서 완전히 마찰력을 제거하기는 현실적으로 불가능하기 때문에 압축고무시편의 단순압축시험에서 얻은 물성값을 신뢰하기 어렵게 된다.In order to compensate for this problem, a lubricant is applied to the friction surface and a compression test is carried out, but at high compression loads, the formation of the lubrication film on the contact surface is destroyed and the side swells. Since it is practically impossible to completely remove friction at high loads, it is difficult to trust the properties obtained from simple compression tests on compressed rubber specimens.
이러한 단순압축시험의 문제점을 해결하기 위해 고무시편의 이축인장시험을 통해 얻은 실험값(이축응력-이축변형률)을 수치적으로 환산하여 단축응력과 단축변형률값을 얻는 방법을 시행하여 왔다.In order to solve the problems of the simple compression test, a method of obtaining uniaxial stress and uniaxial strain value by numerically converting the experimental values (biaxial stress-biaxial strain) obtained through the biaxial tensile test of rubber specimens has been implemented.
상기 이축인장시험이 정확히 이루어지기 위해서는 고무시편의 중심점을 기준으로 원주방향으로 동일한 하중을 부여하는 방법이 보다 정확한 실험 데이터를 얻을 수 있는데, 이때 상기 고무시편의 신장전 중심점이 신장후의 중심점과 일치해야 되며, 방사방향으로 체결되는 그립이 신장전과 신장과정 그리고 신장후에 정확한 진원형상을 유지해야 한다.In order to perform the biaxial tensile test correctly, a method of applying the same load in the circumferential direction with respect to the center point of the rubber specimen can obtain more accurate experimental data, wherein the center point before extension of the rubber specimen must coincide with the center point after extension. The radially fastening grips must maintain the correct round shape before, during and after stretching.
이에 따라 상기 고무시편을 방사방향으로 잡아당기도록 된 다수개의 그립 위치를 정확하게 선정하는 것이 중요한 역할을 하게 된다. 만약 상기 그립과 고무시편의 체결부위가 상이할 경우에는 그 시험과정에서 상기 고무시편이 전방향으로 동일하게 신장되지 못하고 일방향으로 편향되거나, 그 중심이 벗어나게 되면 정확한 물성값의 도출이 어렵게 되는 문제점이 있었다.Accordingly, it is important to accurately select a plurality of grip positions to radially pull the rubber specimen. If the grip portion and the rubber specimen are different from each other, the rubber specimen may not be stretched equally in all directions and may be deflected in one direction or may be out of the center. .
이에 본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로, 인장시험에 사용되는 최적의 고무시편을 제공하며, 상기 고무시편의 체결에 사용되는 그립과의 정확한 체결을 유도하도록 된 지그를 통해 실험과정에서 발생될 수 있는 오차를 감소시킬 수 있도록 된 고무시편 및 그 체결용 지그를 제공하는데 그 목적이 있다.Accordingly, the present invention has been made to solve the above problems, to provide an optimum rubber specimen used in the tensile test, and experiments through a jig to induce an accurate fastening with the grip used to fasten the rubber specimen An object of the present invention is to provide a rubber specimen and a jig for fastening thereof, which can reduce errors that may occur in the process.
도 1은 본 발명에 따른 고무시편의 사시도,1 is a perspective view of a rubber specimen according to the present invention,
도 2는 본 발명에 따른 고무시편의 평면도,2 is a plan view of a rubber specimen according to the present invention,
도 3은 본 발명에 따른 고무시편의 정면도,3 is a front view of a rubber specimen according to the present invention;
도 4는 본 발명에 따른 시편체결용 지그의 사시도,4 is a perspective view of a jig for specimen fastening according to the present invention;
도 5는 본 발명에 따른 시편체결용 지그의 평면도,5 is a plan view of a specimen fastening jig according to the invention,
도 6은 도 4의 I-I선 단면도,6 is a cross-sectional view taken along the line I-I of FIG. 4;
도 7은 본 발명에 따른 고무시편을 지그에 장착시켜 그립과 체결된 모습을 보여주는 평면도,7 is a plan view showing a state in which the grip and fastened by mounting the rubber specimen according to the invention jig,
도 8은 본 발명에 따른 고무시편을 체결하여 잡아당기도록 된 그립의 사시도이다.Figure 8 is a perspective view of the grip to fasten the rubber specimen in accordance with the present invention.
- 도면의 주요부분에 대한 부호의 설명 --Explanation of symbols for the main parts of the drawings-
10 : 고무시편 11 : 체결부10: rubber specimen 11: fastener
12 : 홈 13 : 내원12: Home 13: Visit
20 : 지그 21 : 그립하면지지판20: jig 21: support plate when grip
22 : 시편지지판 22a : 그립전면지지부22: specimen support plate 22a: grip front support
23 : 시편고정핀 24 : 그립측면지지블록23: specimen fixing pin 24: grip side support block
25 : 그립후면지지핀 30 : 그립25: grip back support pin 30: grip
31 : 볼트 D1,D2: 직경31: Bolt D 1 , D 2 : Diameter
T : 두께 W : 폭T: Thickness W: Width
상기와 같은 목적을 달성하기 위한 본 발명은, 평탄한 상부면을 갖는 그립하면지지판이 구비되고; 상기 그립하면지지판의 중앙에 동심상으로 돌출성형되며 상부면에는 고무시편이 안착되는 시편지지판이 형성되며; 상기 시편지지판의 상부면에는 가는 핀형상의 시편고정핀이 다수개 설치되고; 상기 시편지지판의 외곽으로 배치되되, 상기 시편지지판을 중심으로 등각으로 이격배치된 다수개의 그립측면지지블록이 형성되며; 상기 그립측면지지블록의 외곽으로 배치되되, 상기 시편지지판을 중심으로 등각으로 이격배치되는 다수개의 그립후면지지핀이 형성되어 이루어진 지그가 구비되는 것을 특징으로 한다.The present invention for achieving the above object is provided with a grip plate having a flat upper surface; When the grip is formed concentrically projected in the center of the support plate, the upper surface is formed with a specimen support plate on which the rubber specimen is seated; The upper surface of the specimen support plate is provided with a plurality of pin-shaped specimen fixing pins; A plurality of grip side support blocks disposed at an outer side of the specimen support plate, the plurality of grip side support blocks being equally spaced apart from the specimen support plate; It is disposed to the outside of the grip side support block, characterized in that the jig is provided with a plurality of grip back support pins are formed spaced apart equiangularly around the specimen support plate.
그리고, 본 발명은 얇은 원판형상으로 다수개의 체결부가 방사방향으로 형성되되, 그 두께는 1mm 이고 전체 직경은 75mm이며 상기 체결부의 끝단을 이루는 가상의 내원의 직경은 54mm로 형성되며, 상기 체결부와 인접한 체결부 사이에는 홈이형성되며 그 폭은 2.5mm로 형성되는 고무시편이 구비되는 것을 특징으로 한다.In addition, the present invention is a thin disk shape of a plurality of fastening portions are formed in the radial direction, the thickness is 1mm, the total diameter is 75mm and the diameter of the virtual inner circle forming the end of the fastening portion is formed of 54mm, and the fastening portion A groove is formed between the adjacent fastening portions, and a rubber specimen having a width of 2.5 mm is provided.
이하 본 발명을 첨부된 예시도면을 참조로 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 고무시편의 사시도이고, 도 2는 본 발명에 따른 고무시편의 평면도이며, 도 3은 본 발명에 따른 고무시편의 정면도이고, 도 4는 본 발명에 따른 시편체결용 지그의 사시도이며, 도 5는 본 발명에 따른 시편체결용 지그의 평면도이고, 도 6은 도 4의 I-I선 단면도이며, 도 7은 본 발명에 따른 고무시편을 지그에 장착시켜 그립과 체결된 모습을 보여주는 평면도이고, 도 8은 본 발명에 따른 고무시편을 체결하여 잡아당기도록 된 그립의 사시도이다.1 is a perspective view of a rubber specimen according to the invention, Figure 2 is a plan view of a rubber specimen according to the invention, Figure 3 is a front view of the rubber specimen according to the invention, Figure 4 is a jig for fastening the specimen according to the invention 5 is a plan view of a test piece fastening jig according to the present invention, FIG. 6 is a cross-sectional view taken along line II of FIG. 4, and FIG. 7 shows a state in which a rubber test piece according to the present invention is mounted on a jig and fastened with a grip. Figure 8 is a plan view showing, Figure 8 is a perspective view of the grip to be pulled by fastening the rubber specimen according to the present invention.
본 발명은 평탄한 상부면을 갖는 그립하면지지판(21)이 구비되고; 상기 그립하면지지판(21)의 중앙에 동심상으로 돌출성형되며 상부면에는 상기 고무시편(10)이 안착되는 시편지지판(22)이 형성되며; 상기 시편지지판(22)의 상부면에는 가는 핀형상의 시편고정핀(23)이 다수개 설치되고; 상기 시편지지판(22)의 외곽으로 배치되되, 상기 시편지지판(22)을 중심으로 등각으로 이격배치된 다수개의 그립측면지지블록(24)이 형성되며; 상기 그립측면지지블록(24)의 외곽으로 배치되되, 상기 시편지지판(22)을 중심으로 등각으로 이격배치되는 다수개의 그립후면지지핀(25)이 형성되어 이루어진 지그(20)가 구비되어 이루어진다.According to the present invention, there is provided a support plate 21 having a grip having a flat top surface; When the grip is formed in the center of the support plate 21 concentrically protruding and the upper surface is formed with a specimen support plate 22 on which the rubber specimen 10 is seated; On the upper surface of the specimen support plate 22, a plurality of fine pin-shaped specimen fixing pins 23 are installed; A plurality of grip side support blocks (24) disposed at an outer side of the specimen support plate (22) and spaced at an equidistant center around the specimen support plate (22); The grip side support block 24 is disposed outside the jig 20 is formed with a plurality of grip back support pins 25 are formed to be equally spaced about the specimen support plate 22 is formed.
도 4 내지 도 6에서 보는 바와 같이, 상기 시편고정핀(23)은 4개로 이루어지는 것이 바람직하며 경우에 따라 그 설치갯수를 변경할 수 있음은 물론이며, 상기 고무시편(10)의 홈(12)의 폭(W)보다는 작은 직경으로 형성되어, 상기 시편고정핀(23)에 고무시편(10)의 홈(12)을 삽입시켜 상기 고무시편(10)을 정위치시키는 역할을 수행하게 된다.As shown in Figure 4 to Figure 6, the specimen fixing pin 23 is preferably made of four and can be changed in some cases, of course, of the groove 12 of the rubber specimen 10 It is formed with a diameter smaller than the width (W), it serves to position the rubber specimen 10 by inserting the groove 12 of the rubber specimen 10 in the specimen fixing pin (23).
한편, 상기 시편지지판(22)는 원판형상으로 성형되며, 상기 고무시편(10)을 체결하도록 된 그립(30)들의 전면부가 상기 시편지지판(22)의 그립전면지지부(22a)에 밀착되어 상기 그립(30)의 전방을 지지하는 역할을 수행하게 된다.On the other hand, the specimen support plate 22 is formed in the shape of a disc, the front portion of the grips 30 to fasten the rubber specimen 10 is in close contact with the grip front support portion 22a of the specimen support plate 22 and the grip It serves to support the front of the (30).
그리고, 상기 그립측면지지블록(24)은 16개로 이루어지며, 상기 그립측면지지블록(24)과 인접한 그립측면지지블록(24) 사이에 상기 그립(30)이 삽입되면서 밀착되어 상기 그립(30)의 양측을 지지하는 역할을 수행하게 된다.And, the grip side support block 24 is made of 16, the grip 30 is in close contact with the grip 30 is inserted between the grip side support block 24 and the adjacent grip side support block 24, the grip 30 Will support both sides of the role.
또한, 상기 그립후면지지핀(25)은 핀형상으로 성형되어 상기 그립(30)의 후면을 지지하는 역할을 수행하게 된다.In addition, the grip back support pin 25 is formed in a pin shape to serve to support the rear surface of the grip (30).
그리고, 본 발명은 얇은 원판형상으로 다수개의 체결부(11)가 방사방향으로 형성되되, 그 두께(T)는 1mm이고 전체 직경(D1)은 75mm이며 상기 체결부(11)의 끝단을 이루는 가상의 내원(13)의 직경(D2)은 54mm로 형성되며, 상기 체결부(11)와 인접한 체결부(11) 사이에는 홈(12)이 형성되며 그 폭(W)은 2.5mm로 형성되는 고무시편(10)이 구비되어 이루어진다.In addition, in the present invention, a plurality of fastening portions 11 are formed in a radial direction in a thin disk shape, the thickness T of which is 1 mm, the total diameter D 1 is 75 mm, and forms the ends of the fastening portions 11. The diameter D 2 of the imaginary inner circle 13 is formed to be 54 mm, and a groove 12 is formed between the fastening part 11 and the adjacent fastening part 11, and the width W is 2.5 mm. The rubber specimen 10 is provided.
여기서, 상기 고무시편(10)의 체결부(11)는 16개로 이루어지는 것이 바람직한데, 이는 본 출원인이 고무재료의 이축인장특성을 고려하여 여러 번에 걸친 실험결과에 따른 것으로, 상기 체결부(11)의 숫자 및 각각의 치수를 변경하여 상기 고무시편(10)을 방사방향으로 신장시켰을 때 전술한 조건에서 가장 이상적인 실험결과를 나타냈다.Here, the fastening portion 11 of the rubber specimen 10 is preferably made of 16, which is the applicant according to the results of several times in consideration of the biaxial tensile characteristics of the rubber material, the fastening portion 11 When the rubber specimen 10 was elongated in the radial direction by changing the numerals and respective dimensions of), the most ideal test result was obtained under the above-described conditions.
이하 본 발명의 바람직한 실시예를 설명한다.Hereinafter, preferred embodiments of the present invention will be described.
본 발명에 따르면 상기 지그(20)의 시편지지판(22) 상부에 형성된 시편고정핀(23)에 상기 고무시편(10)의 홈(12)을 끼우게 되는데, 이때 상기 4개의 시편고정핀(23)에 의해 상기 고무시편(10)의 유동이 억제되고 중심점이 일치하게 된다.According to the present invention, the groove 12 of the rubber specimen 10 is inserted into the specimen fixing pin 23 formed on the specimen support plate 22 of the jig 20. In this case, the four specimen fixing pins 23 ), The flow of the rubber specimen 10 is suppressed and the center point coincides.
이후, 도 7에서 보는 바와 같이, 상기 그립(30)들을 상기 지그(20)의 그립측면지지블록(24)과 그립측면지지블록(24) 사이로 삽입시키면서 상기 시편지지판(22) 및 그립후면지지핀(25)에 밀착시키게 되면, 상기 그립(30)은 상기 고무시편(10)의 체결부(11)와 맞물리는 위치로 정확하게 배치됨은 물론, 상기 지그(20)의 그립하면지지판(21), 시편지지판(22), 그립측면지지블록(24) 및 그립후면지지핀(25)에 의해 그립(30)의 저면과 전·후·좌·우 사면이 확실하게 고정된다.Subsequently, as shown in FIG. 7, the specimen supporting plate 22 and the grip rear support pin are inserted while the grips 30 are inserted between the grip side support block 24 and the grip side support block 24 of the jig 20. When it comes in close contact with the 25, the grip 30 is precisely disposed in a position to be engaged with the fastening portion 11 of the rubber specimen 10, as well as the support plate 21 and the specimen when the grip of the jig 20 is gripped. The bottom face of the grip 30 and the front, rear, left and right slopes are securely fixed by the support plate 22, the grip side support block 24 and the grip back support pin 25.
이후 상기 그립(30)의 볼트(31)를 풀어 상기 고무시편(10)의 체결부(11)와 체결을 완료한 후, 상기 지그(20)로부터 이탈시키게 되면 상기 고무시편(10)과 그립(30)의 체결작업이 완료된다.Then, after loosening the bolt 31 of the grip 30 and completing the fastening with the fastening part 11 of the rubber specimen 10, when detached from the jig 20, the rubber specimen 10 and the grip ( The tightening work of 30) is completed.
본 발명에 따른 고무시편(10)과 그립(30)들은 본 출원인에 의해 기출원된 특허(국내특허출원 제2000-68371호)에서 제시된 시험기에 체결되어 실험할 수 있다.Rubber specimens 10 and grips 30 according to the present invention can be tested by being fastened to the tester presented in the patent (Domestic Patent Application No. 2000-68371) filed by the applicant.
이상 설명한 바와 같이 본 발명에 따르면, 인장시험에 사용되는 최적의 고무시편을 제공함은 물론, 상기 고무시편의 체결에 사용되는 그립을 정확하게 위치시켜 고정하는 지그가 마련되어, 상기 고무시편을 원하는 위치에 손쉽게 안착시킬 수 있음은 물론, 지그의 그립하면지지판, 시편지지판, 그립측면지지블록 및 그립후면지지핀을 통해 상기 그립을 확실하게 지지·고정함으로써 그립과 고무시편이 정확하게 체결될 수 있어 인장시험의 신뢰성을 향상시킬 수 있는 효과가 있을 뿐만 아니라, 고무시편 체결에 요구되는 시간을 수작업으로 체결하는 것과 비교할 때 50% 이상 체결시간을 단축시킬 수 있으며, 고무시편의 체결과정에서 고무시편의 파손을 방지할 수 있는 효과가 있다.As described above, according to the present invention, a jig for precisely positioning and fixing the grip used for fastening the rubber specimen is provided, as well as providing an optimum rubber specimen used for the tensile test. As well as the grip of the jig, the grip and the rubber specimen can be precisely fastened by the support plate, the specimen support plate, the grip side support block, and the grip back support pin. In addition to improving the pressure, the time required for fastening the rubber specimen can be shortened by more than 50% compared to manual tightening, and it can prevent the rubber specimen from being damaged during the fastening of the rubber specimen. It can be effective.
Claims (7)