KR100378832B1 - Tape for preventing pipe leakage - Google Patents
Tape for preventing pipe leakage Download PDFInfo
- Publication number
- KR100378832B1 KR100378832B1 KR10-2000-0035696A KR20000035696A KR100378832B1 KR 100378832 B1 KR100378832 B1 KR 100378832B1 KR 20000035696 A KR20000035696 A KR 20000035696A KR 100378832 B1 KR100378832 B1 KR 100378832B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- tape
- polyurethane prepolymer
- ethylene glycol
- present
- Prior art date
Abstract
본 발명은 배관 누수 방지용 테이프에 관한 것으로서, 조성물 전체 중량을 기준으로 폴리이소시아네이트 18 내지 30중량％, 폴리프로필렌글리콜 35 내지 55중량％, 에틸렌글리콜 및 프로필렌글리콜 랜덤 공중합체 10 내지 25중량％, 수경화 촉매 1 내지 3중량％, 소포제 0.03 내지 0.3중량％, 안정제 0.01 내지 1.5중량％, 계면 활성제 2 내지 10중량％를 반응시켜서 얻은 폴리우레탄 프리폴리머 조성물을 직물 또는 편물 지지체에 함침시켜서 된 것을 특징으로 한다.The present invention relates to a pipe leakage preventing tape, based on the total weight of the composition, 18 to 30% by weight polyisocyanate, 35 to 55% by weight polypropylene glycol, 10 to 25% by weight ethylene glycol and propylene glycol random copolymer, water curing A polyurethane prepolymer composition obtained by reacting 1 to 3 wt% of a catalyst, 0.03 to 0.3 wt% of an antifoaming agent, 0.01 to 1.5 wt% of a stabilizer, and 2 to 10 wt% of a surfactant is impregnated into a woven or knitted support.
본 발명에 의한 배관 누수 방지용 테이프는 누수되는 배관을 교체하지 않고 짧은 시간에 보수가 가능하고, 또 보수한 부위를 장기간 사용이 가능한 효과가 있다.The pipe leakage preventing tape according to the present invention has the effect of being able to be repaired in a short time without replacing the leaking pipe, and to use the repaired part for a long time.
Description
본 발명은 배관 누수 방지용 테이프에 관한 것이다. 더욱 상세하게, 본 발명은 고무 성분에 가깝고, 신축성이 있으며, 누수되는 배관을 교체하지 않고 짧은 시간에 보수가 가능할 뿐 아니라 보수한 후에도 장기간 동안 사용이 가능한 배관 누수 방지용 테이프에 관한 것이다.The present invention relates to a tape for preventing a pipe leak. More particularly, the present invention relates to a pipe leakage preventing tape that is close to a rubber component, elastic, and which can be repaired in a short time without replacing a leaky pipe and can be used for a long time after repair.
현재, 사용되고 있는 배관 누수 방지용 테이프는 배관의 치수 변화에 대응하는 수축 이완성을 갖고 있지 않으며, 테이프가 대부분 유리 섬유로 조직되어 있어 신축성이 없고, 밀착성이 나쁘며, 앵글 부위에는 적용할 수 없는 단점들을 가지고 있다.Currently, the pipe leakage preventing tape used has no shrinkage and relaxation characteristics corresponding to the dimensional change of the pipe, and most of the tapes are made of glass fiber, and thus have no elasticity, poor adhesion, and are not applicable to angle parts. have.
따라서, 본 발명은 테이프에 신축성을 부여하기 위해서 수지가 고무 성분에 가깝도록 하고, 보수 부위가 장기간에 걸쳐 잘 견딜 수 있도록 주변 온도에 따른 배관의 치수 변화에 잘 대응하도록 함과 동시에 사용자가 불편을 느끼지 않고 사용할 수 있도록 하는데 그 기술적인 과제가 있다.Therefore, the present invention is to make the resin close to the rubber component in order to give elasticity to the tape, and to respond well to the dimensional change of the pipe according to the ambient temperature so that the repair site can withstand the long term well, and at the same time, the user is uncomfortable The technical challenge is to make it available without feeling.
본 발명은 상기한 목적을 달성하기 위하여, 조성물 전체 중량을 기준으로 폴리이소시아네이트 18 내지 30중량％, 폴리프로필렌글리콜 35 내지 55중량％, 에틸렌글리콜 및 프로필렌글리콜 랜덤 공중합체 10 내지 25중량％, 수경화 촉매 1 내지 3중량％, 소포제 0.03 내지 0.3중량％, 안정제 0.01 내지 1.0중량％, 계면활성제 2 내지 10중량％를 반응시켜서 얻은 수경화성 폴리우레탄 프리폴리머 조성물을 제조하고, 이를 직물 또는 편물 지지체에 함침시키는 것을 특징으로 한다.In order to achieve the above object, the present invention, 18 to 30% by weight of polyisocyanate, 35 to 55% by weight of polypropylene glycol, 10 to 25% by weight of ethylene glycol and propylene glycol random copolymer, hydrocuring based on the total weight of the composition To prepare a hydrocurable polyurethane prepolymer composition obtained by reacting 1 to 3 wt% of a catalyst, 0.03 to 0.3 wt% of an antifoaming agent, 0.01 to 1.0 wt% of a stabilizer, and 2 to 10 wt% of a surfactant, and impregnating it into a woven or knitted support It is characterized by.
본 발명에 따른 배관 누수 방지용 테이프의 수경화성 폴리우레탄 프리폴리머 조성물에서 폴리이소시아네이트로는 4,4'--디페닐메탄디이소시아네이트(MDI)를 사용하며, 그 사용량은 조성물 전체를 기준으로 해서 18 내지 30중량％가 바람직하다.4,4′-diphenylmethane diisocyanate (MDI) is used as the polyisocyanate in the water-curable polyurethane prepolymer composition of the pipe leakage preventing tape according to the present invention, and its amount is 18 to 30 based on the entire composition. Weight% is preferable.
폴리올 성분으로는 폴리프로필렌글리콜 35 내지 55중량％, 에틸렌글리콜 및 프로필렌글리콜 랜덤 공중합체 10 내지 25중량％를 사용하며, 상기 폴리프로필렌글리콜은 중량 평균 분자량이 2,000 내지 4,000 정도인 것을 사용하는 것이 바람직하다. 그 이유는 에틸렌글리콜 및 프로필렌글리콜 랜덤 공중합체만으로는 요구하는 접착력과 탄성을 얻기 어렵기 때문이다.As the polyol component, 35 to 55% by weight of polypropylene glycol, 10 to 25% by weight of ethylene glycol and propylene glycol random copolymer are used, and the polypropylene glycol preferably has a weight average molecular weight of about 2,000 to 4,000. . This is because only the ethylene glycol and propylene glycol random copolymers are difficult to obtain the required adhesion and elasticity.
그리고, 상기 에틸렌글리콜 및 프로필렌 글리콜 랜덤 공중합체의 중량 평균 분자량은 2,000 내지 4,000이며, 에틸렌글리콜이 1 내지 15중량％ 비율로 공중합된 것을 사용하는 것이 바람직하다. 그 이유는 에틸렌글리콜 및 프로필렌글리콜 랜덤 공중합체가 친수성을 가지고 있어 물과의 결합이 빨라 경화 속도를 단축시키는 효과가 있기 때문이다.The weight average molecular weight of the ethylene glycol and propylene glycol random copolymers is 2,000 to 4,000, and it is preferable to use those in which ethylene glycol is copolymerized at a ratio of 1 to 15% by weight. This is because the ethylene glycol and propylene glycol random copolymers have hydrophilic properties, and thus, the bonding with water is fast, and the curing rate is shortened.
본 발명에 의하면, 상기 4,4'-디페닐메탄디이소시아네이트는 폴리프로필렌글리콜 및 에틸렌글리콜/프로필렌글리콜 랜덤 공중합체와 함께 30 내지 100℃의 온도에서 교반하면서 1 내지 6시간 동안 반응시키는 것이 바람직하다.According to the present invention, the 4,4'-diphenylmethane diisocyanate is preferably reacted with polypropylene glycol and ethylene glycol / propylene glycol random copolymer for 1 to 6 hours while stirring at a temperature of 30 to 100 ℃. .
본 발명에 따른 배관 누수 방지용 테이프의 사용하기 위하여 물에 적셨을 때, 상기 수경화성 촉매는 폴리우레탄 프리폴리머 조성물의 경화반응을 촉진시키는 역할을 하게 되는 바, 이러한 목적으로 사용할 수 있는 촉매 화합물로서는 아민계 화합물과 모르포린계 화합물 등이 있다. 아민계 화합물로는 예를 들면, 디에틸렌트리아민과 헥사메틸렌디아민이 있으며, 모르포린계 화합물로는 디모르포리노디에틸에테르와 비스(2,6-디메틸모르포리노)디에틸에테르, 비스(2-(4-모르포리노)프로필)에테르 등이 있다.When wetted with water for use of the pipe leakage preventing tape according to the present invention, the hydrocuring catalyst plays a role of promoting the curing reaction of the polyurethane prepolymer composition. And morpholine compounds. Examples of the amine compound include diethylenetriamine and hexamethylenediamine, and examples of the morpholine compound include dimorpholino diethyl ether, bis (2,6-dimethylmorpholino) diethyl ether, and bis ( 2- (4-morpholino) propyl) ether and the like.
이 중에서도, 특히 디모르포리노디에틸에테르가 본 발명에 따른 수경화성 촉매로 가장 바람직하다.Among these, especially dimorpholino diethyl ether is the most preferable as a hydrocurable catalyst which concerns on this invention.
수경화성 촉매의 사용량은 폴리우레탄 프리폴리머 조성물 총량을 기준으로 1 내지 3중량％가 바람직하다.The amount of the hydraulic curing catalyst is preferably 1 to 3% by weight based on the total amount of the polyurethane prepolymer composition.
상기 안정제로는 제품이 알루미늄 팩에서 테이프의 수분이 존재하지 않는 조건에서, 제품을 보관하는 동안 폴리우레탄 프리폴리머 조성물의 초기 경화 반응을 방지하는 역할을 하게 되며, 바람직한 안정제로는 인산을 들 수 있다.The stabilizer serves to prevent the initial curing reaction of the polyurethane prepolymer composition while the product is stored in the condition that the product does not have moisture in the tape in the aluminum pack, the preferred stabilizer may include phosphoric acid.
안정제의 사용량은 상기 폴리우레탄 프리폴리머 조성물의 총량을 기준으로 0.01 내지 1.5중량％가 바람직하다. 만일 0.01중량％ 미만으로 할 경우에는 안정화 효과를 얻을 수 없고, 반대로 1.5중량％를 초과할 경우에는 상기 폴리우레탄 프리폴리머 조성물의 수경화 반응시간이 과도하게 길어지는 문제점이 따르게 된다.The amount of the stabilizer is preferably 0.01 to 1.5% by weight based on the total amount of the polyurethane prepolymer composition. If it is less than 0.01% by weight, no stabilizing effect can be obtained. On the contrary, if it is more than 1.5% by weight, the problem of excessively long curing time of the polyurethane prepolymer composition is accompanied.
본 발명에서 계면활성제로는 폴리에톡시레이트 블록 코폴리머를 사용할 수 있으며, 그 사용량은 조성물 총량을 기준으로 2 내지 10중량％가 바람직하다. 만일 2중량％ 미만으로 사용할 경우에는 제품 사용시 몰딩성이 불량하게 되고, 10중량％를 초과하여 사용할 경우에는 접착력이 저하되고 수지 점도의 상승을 유발하게 되는 문제가 있게 된다.In the present invention, a polyethoxylate block copolymer may be used as the surfactant, and the amount thereof is preferably 2 to 10% by weight based on the total amount of the composition. If the content is less than 2% by weight, the moldability is poor when the product is used. If the content is more than 10% by weight, the adhesive strength is lowered and the resin viscosity is increased.
본 발명에 의하면, 소포제로는 폴리알킬렌옥시디메틸실록산을 0.03 내지 0.3중량％ 사용할 수 있다. 소포제는 폴리우레탄 프리폴리머의 이소시아네이트기와 물이 반응하여 발생되는 이산화탄소에 의한 발포 현상을 최소화시키기 위한 목적으로 사용된다.According to this invention, 0.03 to 0.3 weight% of polyalkylene oxydimethylsiloxane can be used as an antifoamer. Defoamer is used for the purpose of minimizing the foaming phenomenon by the carbon dioxide which is generated by the reaction of the isocyanate group and water of the polyurethane prepolymer.
본 발명에 의하면, 앞에서 설명한 바와 같이 4,4'-디페닐메탄디이소시아네이트, 폴리프로필렌글리콜 및 에틸렌글리콜/프로필렌글리콜 랜덤 공중합체의 반응 혼합물에 추가로 소포제로서 폴리알킬렌옥시디메틸실록산, 수경화 촉매로서 디모르포리노디에틸에테르, 안정제로서 인산 및 계면활성제로서 폴리에톡시레이트 블록 코폴리머를 투입하고 소정 시간 동안 추가로 반응시키게 되면 본 발명에 따른 폴리우레탄 프리폴리머가 얻어지게 된다.According to the present invention, as described above, in addition to the reaction mixture of 4,4'-diphenylmethane diisocyanate, polypropylene glycol and ethylene glycol / propylene glycol random copolymer, polyalkyleneoxydimethylsiloxane as a defoamer, a hydrocuring catalyst Dimorpholinodiethyl ether as a stabilizer, phosphoric acid as a stabilizer, and a polyethoxylate block copolymer as a surfactant are further reacted for a predetermined time to obtain a polyurethane prepolymer according to the present invention.
본 발명에 따른 수경성 폴리우레탄 프리폴리머 조성물은 필요에 따라 조성물의 점도를 조절하기 위해서 가소제, 예를 들면 디부틸프탈레이트를 0.5 내지 3.0중량％를 추가로 포함할 수 있다.The hydraulic polyurethane prepolymer composition according to the present invention may further comprise 0.5 to 3.0% by weight of a plasticizer, for example dibutylphthalate, in order to adjust the viscosity of the composition as necessary.
상기 수경성 폴리우레탄 프리폴리머 조성물의 점도는 20℃에서 10,000 내지50,000 cps, 바람직하게는 10,000 내지 30,000 cps로 조절하는 것이 좋다.The viscosity of the hydraulic polyurethane prepolymer composition is preferably adjusted to 10,000 to 50,000 cps, preferably 10,000 to 30,000 cps at 20 ° C.
만일, 상기 조성물의 점도가 50,000 cps를 초과할 경우에는 제품의 제조 공정에서 테이프에 수지를 함침시킬 때, 작업성이 떨어지게 되며, 반대로 점도가 10,000 cps 미만일 경우에는 테이프에서 수지 침출이 발생될 가능성이 있으므로 상기 범위로 점도를 조절하는 것이 바람직하다.If the viscosity of the composition exceeds 50,000 cps, when the resin is impregnated into the tape in the manufacturing process of the product, the workability is reduced, on the contrary, if the viscosity is less than 10,000 cps, the leaching of the resin from the tape may occur. Therefore, it is preferable to adjust the viscosity in the above range.
한편, 본 발명에 따라 제조된 폴리우레탄 프리폴리머는 미반응 이소시아네이트기를 3 내지 9몰％를 함유하도록 하는 것이 바람직하다. 이러한 미반응 이소시아네이트기는 다음 반응식과 같이 물과 반응하여 이산화탄소 가스를 발생하면서 우레아 결합을 형성하여 폴리우레탄 프리폴리머를 경화시키게 된다.On the other hand, it is preferable that the polyurethane prepolymer prepared according to the present invention contain 3 to 9 mol% of unreacted isocyanate groups. These unreacted isocyanate groups react with water to generate carbon dioxide gas to form urea bonds to cure the polyurethane prepolymers as shown in the following scheme.
―NCO＋HOH＋OCN－-NCO + HOH + OCN-
⇒ [―NH―CO―O―OC―HN―]―NHCONH＋CO2－⇒ [-NH-CO-O-OC-HN-]-NHCONH + CO 2-
상기 폴리우레탄 프리폴리머가 함유하는 미반응 이소시아네이트기의 함량이 3％ 미만일 경우에는 점도가 높아 작업성이 불량하고, 저장 안정성도 저하되게 되고, 반대로 미반응 이소시아네이트기의 함량이 9％를 초과할 경우에는 경화시 이산화탄소의 발생량이 과다하여 에어홀에 의한 누수 방지에 심각한 악영향을 미칠 수 있게 된다.When the content of the unreacted isocyanate group contained in the polyurethane prepolymer is less than 3%, the viscosity is high, the workability is poor, and the storage stability is also lowered. On the contrary, when the content of the unreacted isocyanate group exceeds 9%, The amount of carbon dioxide generated during curing may have a serious adverse effect on the prevention of leakage by air holes.
경화된 테이프의 누수 방지 효과는 경화된 폴리우레탄 수지의 양과 테이프 품질에 의하여 결정된다. 본 발명에 의하면, 테이프에 함침된 프리폴리머 조성물의 양은 시용하고자 하는 목적에 따라 달라질 수 있으며, 상기 지지체 중량에 대해2.5 내지 4.5배로 하는 것이 바람직하다.The anti-leak effect of the cured tape is determined by the amount of cured polyurethane resin and the tape quality. According to the present invention, the amount of the prepolymer composition impregnated on the tape may vary depending on the purpose to be applied, and is preferably 2.5 to 4.5 times the weight of the support.
상기 수경성 폴리우레탄 프리폴리머 조성물의 적용량을 2.5배 미만으로 할 경우에는 고압의 누수나 에어 차단용으로 사용할 수 없게 되고, 반대로 4.5배를 초과할 경우에는 초기 경화열이 과도하게 발생하여 가사 시간이 짧아 사용하기에 불편하고, 제품으로부터 수지가 침출되는 단점이 나타나게 된다.When the applied amount of the hydraulic polyurethane prepolymer composition is less than 2.5 times, it cannot be used for high pressure leakage or air blocking. On the contrary, when it exceeds 4.5 times, the initial curing heat is excessively generated and the pot life is short. It is inconvenient to follow, and the disadvantages of leaching the resin from the product appear.
본 발명에서 폴리우레탄 프리폴리머 조성물이 함침되게 되는 테이프 지지체로는 폴리에스터 DTY(DEXTURED YARN) 능직 조직이 가장 바람직하다. 그 이유는 상기 조직이 많은 양의 수지를 함유할 뿐 아니라 조직이 치밀하고, 신율이 좋기 때문이다.As the tape support on which the polyurethane prepolymer composition is impregnated in the present invention, polyester DTY (DEXTURED YARN) twill tissue is most preferred. The reason is that the tissue contains not only a large amount of resin but also the structure is dense and the elongation is good.
본 발명에 따른 테이프의 지지체로는 폴리에스터 DTY 50 ~ 400 데니아, 20 ~ 200 필러를 고속 평직기를 이용하여 능직한 것으로 1인치 당 20 내지 40개, 중량은 1인치당 3 내지 10 g으로 직조한 것을 사용하는 것이 바람직하다.As a support for the tape according to the present invention, polyester DTY 50 to 400 denier and 20 to 200 fillers were made by using a high speed weaving machine, and 20 to 40 pieces per inch, and the weight was woven at 3 to 10 g per inch. It is preferable to use.
본 발명에 따른 배관 누수 방지용 테이프는, 상기 폴리우레탄 프리폴리머 조성물이 담겨 있는 함침기를 이용하되 적당량의 조성물이 묻어 있는 롤라에 직물 또는 편물 지지체를 밀착 통과시켜서 상기 조성물을 상기 지지체에 함침시켜서 테이프를 제조할 수 있다. 이렇게 상기 조성물이 함침된 누수 방지용 테이프는 공기와 접촉되지 않도록 알루미늄 박에 넣어 완전히 밀봉시켜서 보관할 수 있다.Pipe leakage preventing tape according to the present invention, using the impregnator containing the polyurethane prepolymer composition, but impregnating the composition to the support by passing the fabric or knitted support in close contact with the roll of the appropriate amount of the composition to prepare a tape Can be. Thus, the leakage preventing tape impregnated with the composition may be stored in a completely sealed aluminum foil so as not to contact with air.
이하 본 발명을 실시예에 의거하여 더욱 상세히 설명하면 다음과 같으며, 다음의 실시예는 본 발명을 예시하기 위한 것으로 본 발명이 다음의 실시예에 국한되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples. The following Examples are provided to illustrate the present invention, but the present invention is not limited to the following Examples.
실시예Example
폴리이소시아네이트 성분으로 4,4'-디페닐메탄디이소시아네이트 [상품명: I-125MK, 다우 케미칼사제] 27.8중량％, 폴리올 성분으로 평균 분자량이 2,000인 폴리프로필렌글리콜[상품명: H-2000, 미원유화제] 39.8중량％, 평균 분자량이 4,000인 에틸렌글리콜/프로필렌글리콜 랜덤공중합체[상품명: H-4701, 한국폴리올사제] 22중량％를 반응기에 부가하였다. 상기 혼합물을 60℃에서 2 시간 동안 반응시킨 후, 계속해서, 소포제인 폴리알킬렌옥시디메틸실록산[상품명: SAG-1000, 미국 OS: Specialitites 사제] 0.3중량％, 계면활성제인 폴리에톡시레이트 블록 코폴리머[상품명: F-108, 미국 BASF사제] 8중량％, 수경화 촉매로서 디모르포리노디에틸에테르 1.1중량％ 및 안정제로서 인산을 1.0중량％를 투입하고 약 1시간 추가로 반응시켰다.4,4'-diphenylmethane diisocyanate as a polyisocyanate component [trade name: I-125MK, manufactured by Dow Chemical Company] 27.8% by weight, polypropylene glycol having an average molecular weight of 2,000 as a polyol component [trade name: H-2000, microemulsifier] 22 weight% of ethylene glycol / propylene glycol random copolymers [brand name: H-4701, the product made by Korean Polyol] of 39.8 weight% and an average molecular weight of 4,000 were added to the reactor. The mixture was reacted at 60 DEG C for 2 hours, and then 0.3 wt% of a polyalkyleneoxydimethylsiloxane [trade name: SAG-1000, manufactured by Specialtyites, Inc.], an antifoaming agent, and a polyethoxylate block nose as a surfactant. 8 weight% of a polymer (trade name: F-108, manufactured by BASF Corporation), 1.1 weight% of dimorpholino diethyl ether as a water curing catalyst, and 1.0 weight% of phosphoric acid as a stabilizer were added and reacted for about 1 hour.
이렇게 하여 얻어진 폴리우레탄 프리폴리머 조성물의 점도는 20℃에서 회전식 점도계를 사용하여 4번 회전자를 12 속도로 회전시키면서 측정한 결과 12,000 cps이었다.The viscosity of the polyurethane prepolymer composition thus obtained was 12,000 cps as measured by rotating the fourth rotor at 12 speeds using a rotary viscometer at 20 ° C.
이렇게 하여 얻어진 프리폴리머 조성물을 이용하여 다음 방법에 따라 배관 누수방지용 테이프를 제조하였다.Using the prepolymer composition thus obtained, a tape for preventing leakage of pipes was manufactured according to the following method.
먼저, 중량 5g/인치, 밀도 25개/인치의 폴리에스터 DTY 능직물에 상기 조성물의 함침량이 상기 폴리에스터 능직물 100g 당 300g이 되도록 조정하여 함침 누수방지용 테이프를 완성하였다.First, the impregnated leakage preventing tape was completed by adjusting the impregnated amount of the composition to a polyester DTY twill having a weight of 5 g / inch and a density of 25 / inch to 300 g per 100 g of the polyester twill.
이와 같은 방법으로 제조된 누수방지용 테이프를 다음과 같은 방법으로 배관에 적용하였다.The leakage preventing tape prepared in this manner was applied to the pipe in the following manner.
상기 누수 방지용 테이프를 21 내지 24℃의 물에 2 내지 3번 빠르게 담근 후, 물기를 힘있게 짜고, 2 내지 3분 이내에 배관의 누수부위에 5겹이 되도록 함과 동시에 누수부위에서 5cm 밖으로 힘있게 감아서 고정시켰다. 이때 상기 테이프의 경화속도는 3분/20℃이었으며, 작업성과 강도 및 접착력이 양호하였다.After fast soaking the leak prevention tape in water at 21 to 24 ° C. 2-3 times, squeeze the water tightly, and make a five-ply on the leaking part of the pipe within 2 to 3 minutes, and at the same time, winding it tightly 5 cm out of the leaking part. Fixed. At this time, the curing rate of the tape was 3 minutes / 20 ℃, the workability and strength and adhesion was good.
본 발명에 따른 배관 누수방지용 테이프는 누수 배관을 교체하지 않고, 빠른 시간 내에 보수가 가능하며, 배관 교체 및 작업 지연으로 인한 손실도 절감할 수 있는 효과가 있다.Pipe leakage preventing tape according to the present invention can be repaired in a short time without replacing the leaking pipe, there is an effect that can reduce the loss due to pipe replacement and work delay.
또한, 본 발명은 테이프에 신축성을 부여되어 있으므로 주변 온도에 따른 배관의 치수 변화에 잘 대응하여 보수 부위가 장기간에 걸쳐 잘 견딜 수 있다는 특징이 있다.In addition, the present invention is characterized in that the elasticity is given to the tape, so that the repair part can withstand the long term well in response to the dimensional change of the pipe according to the ambient temperature.
또한, 폴리에스터 DTY를 이용하게 됨으로 인하여 사용 후에 환경의 오염 없이 폐기 처분이 가능하다는 효과가 있다.In addition, the use of the polyester DTY has the effect that can be disposed of without pollution after use.
Claims (4)