KR100356313B1 - Streel strand for prestressed concrete using indented wire and device for manufacturing the same - Google Patents
Streel strand for prestressed concrete using indented wire and device for manufacturing the same Download PDFInfo
- Publication number
- KR100356313B1 KR100356313B1 KR1020000037419A KR20000037419A KR100356313B1 KR 100356313 B1 KR100356313 B1 KR 100356313B1 KR 1020000037419 A KR1020000037419 A KR 1020000037419A KR 20000037419 A KR20000037419 A KR 20000037419A KR 100356313 B1 KR100356313 B1 KR 100356313B1
- Authority
- KR
- South Korea
- Prior art keywords
- wire
- indent
- strand
- concrete
- strands
- Prior art date
Abstract
본 발명은 피씨 콘크리트의 내부에 매입되어 콘크리트의 강도보강을 하는 피씨 강연선 및 그 제조장치에 관한 것이다.The present invention relates to a PC strand and embedded in the PC concrete to strengthen the strength of the concrete and its manufacturing apparatus.
본 발명의 피씨 강연선은 여러 가닥의 소선이 꼬여진 피씨 강연선에 있어서, 상기 소선중 적어도 외층 소선은 길이방향을 따라 그 외주면에 3조의 인덴트 라인이 구비되고, 인접하는 인덴트 라인의 중심간에는 120°의 각도를 이루며, 각 인덴트 라인의 단위 인덴트는 타원형으로서 그 장축방향이 소선의 길이방향에 대하여 경사지게 형성된 구조이다.The PC strand of the present invention is a PC strand in which strands of several strands are twisted, wherein at least the outer layer strands of the strands are provided with three sets of indent lines on the outer circumferential surface thereof in the longitudinal direction, and between the centers of adjacent indent lines. The unit indent of each indent line is oval, and its long axis direction is inclined with respect to the longitudinal direction of the element wire.
본 발명의 피씨 강연선 제조장치는, 피씨 강연선 제조라인에서 신선장치를 빠져 나온 신선선의 이동경로상에 설치되는 것으로, 3개의 인덴트 롤러가 신선선의 주위를 완전히 감싸도록 120°의 각도로 배열되고, 각각의 인덴트 롤러는 그 접촉 외주면(CS)이 원호상 오목곡면을 이루며, 그 오목곡면상에는 청구항 1항 또는 2항에서의 단위 인덴트의 형상과 일치하는 인덴트 형성용 돌기가 형성되어 있다.The PC strand wire manufacturing apparatus of the present invention is installed on the movement path of the fresh wire which has exited the drawing device in the PC strand wire manufacturing line, and the three indent rollers are arranged at an angle of 120 ° so as to completely surround the wire. Each indent roller has its contact outer circumferential surface CS having an arcuate concave surface, and on the concave curved surface, indentation forming projections are formed that match the shape of the unit indent in claim 1.
본 발명의 이형 소선이 사용된 피씨 강연선은 이를 구성하고 있는 소선의 외주면상에 인덴트가 연속적으로 형성되어 요철면을 이루고 있기 때문에 피씨 콘크리트 제품의 제조시 긴장을 위해서 양 단부에 장착되는 장착구의 슬립발생이 억제되어 피씨 제품이 품질특성 저하를 방지할 수 있는 효과가 있고, 또한 그 외주면의 표면적이 증대되어 콘크리트와의 접촉면적이 확대됨과 아울러 요철표면에 의한 콘크리트의 록킹작용에 의해 콘크리트와의 접착력 증대가 이루어지는 장점이 있다.In the case of the PC strand in which the release element wire of the present invention is used, indents are continuously formed on the outer circumferential surface of the element wire constituting the same to form an uneven surface, so slips of mounting holes mounted at both ends for tension during manufacture of the PC concrete product It is possible to prevent the occurrence of deterioration of quality characteristics of PC products, and also increase the surface area of its outer circumferential surface to increase the contact area with concrete, and the adhesive force with concrete by the locking action of concrete by the uneven surface. There is an advantage that the increase is made.
Description
본 발명은 이형선(異形線)으로 이루어진 피씨(Prestressed Concrete) 강연선에 관한 것으로, 보다 자세하게는 피씨 강연선을 구성하는 소선의 표면에 3방향의 인덴트(indent)를 형성하여 슬립(slip)이 방지되고 표면적의 증가에 따른 콘크리트와의 부착력 향상이 이루어지도록 한 이형 소선이 사용된 피씨 강연선에 관한 것이다.The present invention relates to a Ps (Prestressed Concrete) strand consisting of a deformed line, more specifically, to form an indent in three directions on the surface of the element wire constituting the PC strand, the slip is prevented The present invention relates to a PC strand in which a release element wire is used to improve adhesion to concrete according to an increase in surface area.
피씨 제품의 내부에 매입되어 강도의 보강 역할을 하는 피씨용 보강재는 크게 단일 강선과 여러 가닥의 강선이 서로 꼬여진 강연선의 두종류로 구분되며, 강선 또는 강연선을 구성하는 소선의 외형적 형태에 따라 원형선과 이형선으로 나뉘어진다.The reinforcement for PC, which is embedded in PC products and serves to reinforce strength, is divided into two types of stranded wires in which a single steel wire and strands of multiple strands are twisted together, and depending on the external shape of the wires forming the steel wire or steel wire It is divided into circular line and shape line.
이와 같은 피씨용 강선이나 강연선은 피아노선과 같은 고강도 강선을 모재로 하여 이를 파텐팅 처리한 후 다단계에 걸친 냉간 신선을 행하여 소정의 직경을 갖는 신선선을 얻은 다음 소위 블루잉 열처리를 하여 최종 제품으로서의 피씨용 강선으로 제조되거나, 이같은 공정을 통해서 얻어진 강선을 연선하여 피씨용 강연선으로 제조되는 과정을 거치게 된다.This steel wire or stranded wire is made of high strength steel wire such as piano wire, and after it is subjected to tenting treatment, cold drawing is carried out in multiple stages to obtain a fresh wire having a predetermined diameter. It is manufactured from molten steel or stranded steel wire obtained through such a process to be manufactured into PC stranded steel wire.
상기 제조 공정중 블루잉 열처리시에는 소정의 기계적 성질(인장강도 및 신율)을 확보하기 위하여 열처리 대상 선재에 인장력을 부여한 상태에서 열처리가 이루어지도록 하는 이른바 "스테빌라이징(stabilizing)"이 일반적으로 행해지고있다.In the process of bluing during the manufacturing process, so-called "stabilizing" is generally performed so that the heat treatment is performed in a state in which a tensile force is applied to the wire to be heat-treated to secure predetermined mechanical properties (tensile strength and elongation). .
피씨 강선이나 피씨 강연선을 이용한 피씨 제품은, 형틀 내부에 피씨 강선이나 피씨 강연선을 위치시킨 후 양 단부를 통해서 인장하중을 가한 상태에서 형틀 내부로 콘크리트를 채워넣어 양생시키는 과정을 통해서 제작된다.A PC product using a PC steel wire or a PC strand is manufactured by placing a PC steel wire or a PC strand in the mold and curing the concrete by filling the concrete into the mold under a tensile load through both ends.
한편, 피씨 강연선의 경우에는 피씨 제품의 제조과정에서 양단부에 인장력이 작용하였을 때 원래의 인장상태가 그대로 유지되어야 할 것이 요구됨과 아울러 그 주위에 채워져 양생되는 콘크리트와의 양호한 접착상태를 이룰 것이 요구된다.On the other hand, in case of PC strand, it is required to maintain the original tensile state when tension is applied to both ends in the manufacturing process of PC products, and to achieve good adhesion with the concrete which is filled around and cured. .
그런데, 통상의 원형 소선이 꼬여져 구성된 피씨 강연선의 경우에는 인장력이 가해졌을 때 인장력 부여를 위하여 강연선의 단부 외주면을 클램핑하는 인장력 부여장치의 장착구와 연선 외주면간에 슬립이 발생하게 되어 원래 의도했던 수준의 인장력 보다 낮은 인장력이 가해지거나 인장상태가 유지되지 못하게 되고, 또한 주위에 채워지는 콘크리트와의 사이에 완벽한 접착상태를 이루지 못하여 피씨 제품의 인장응력 향상 효과를 충분히 기대할 수 없게 된다.However, in the case of a PC strand composed of twisted circular wires, a slip occurs between the mounting holes of the tension applying device which clamps the outer peripheral surface of the end of the strand to give a tensile force when a tensile force is applied, and a slip occurs between the strands of the stranded wire. Tensile force lower than tensile force is not applied or tensile state is not maintained, and perfect adhesion between concrete and surroundings is not achieved, so it is impossible to fully expect tensile effect improvement effect of PC products.
상기 원형선 피씨 강연선에서 지적되고 있는 문제점의 해결방안의 하나로 다이폼드(dyformed) 피씨 강연선이 알려져 있다. 다이폼드 피씨 강연선은 보이스를 통한 연선공정이나 꼬임이 완료된 연선의 외주에 강한 압착력을 가하여 소선간에 면접촉을 이루도록 함과 아울러 외주면이 원래의 형태로부터 변형되도록 한 구조이다.As a solution to the problems pointed out in the circular line PC strand, a dieformed PC strand is known. The die-formed PC strand has a structure in which the outer circumferential surface is deformed from its original shape by applying a strong compressive force to the outer circumference of the stranded twisted wire process or twisted twisted wire through voice.
이같은 다이폼드 피씨 강연선의 경우 인장력 부여를 위한 장치의 장착구와 강연선의 외주면간에 면접촉이 이루어짐으로써 슬립이 억제되는 이점이 있긴 하나,그 제조과정이 까다롭고 이에 소요되는 장치가 고가이어서 결과적으로 제조비용의 증가를 피할 수 없기 때문에 널리 사용되고 있지는 못한 실정이다.Such a die-formed PC strand has the advantage that slip is suppressed by the surface contact between the mounting holes of the device for imparting tensile force and the outer circumferential surface of the strand, but the manufacturing process is difficult and the required apparatus is expensive, resulting in manufacturing cost. It is not widely used because the increase of is inevitable.
한편, 강선의 표면에 돌기나 요홈이 형성된 이형선 피씨 강선이나 이러한 강선이 꼬여진 이형선 피씨 강연선의 경우에는 상기 원형선 강선이나 강연선에 비해 슬립 방지효과나 콘크리트와의 접착성이 우수하다는 면이 있긴 하나, 그 제조비용면을 함께 고려할 경우 그다지 경제적이지는 못하다는 지적이 있다.On the other hand, in the case of the release line PC steel wire with protrusions or grooves formed on the surface of the steel wire or the release line PC strand wire with such wires twisted, there are aspects that have better slip prevention effect or adhesion to concrete than the circular wire steel wire or strand wire. In addition, some point out that the cost of manufacturing is not very economical.
본 발명은 종래 피씨 강연선에서 지적되고 있는 상기의 제반 문제점을 해결하기 위하여 창안된 것으로, 피씨 강연선용 소선의 외주면에 인덴트가 연속적으로 형성되도록 하여 강연선의 표면적 확대 및 요철표면에 의한 콘크리트와의 접착특성을 향상시키는 한편 인장력 부여장치의 장착구 클램핑시 슬립이 억제되도록 한 이형 소선이 사용된 피씨 강연선을 제공함에 있다.The present invention was devised to solve the above-mentioned problems which are pointed out in the conventional PC strand, and the indentation is continuously formed on the outer circumferential surface of the element strand for the PC strand, the expansion of the surface area of the strand and the adhesion to the concrete by the uneven surface The present invention provides a PC strand in which a release element wire is used to improve characteristics and suppress slip when clamping a mounting hole of a tension applying device.
본 발명의 다른 목적은 냉간 신선공정을 통하여 선선되어 나오는 소선이 인덴트 형성용 요철면이 구비된 3개의 인덴트 형성롤러를 통과하면서 그 외주면에 인덴트가 규칙적으로 형성되도록 함으로써 소선의 외주면상에 간편하게 인덴트를 형성할 수 있도록 한 이형 소선이 사용된 피씨 강연선 제조장치를 제공함에 있다.Another object of the present invention is to ensure that indents are regularly formed on the outer circumferential surface of the element wire while passing through the three indent forming rollers provided with the indentation forming concave-convex surface through the cold wire drawing process. The present invention provides a PC strand wire manufacturing apparatus using a release element wire that can easily form an indent.
도1은 본 발명의 피씨 강연선용 인덴티트 소선에 대한 사시도.1 is a perspective view of an indented element wire for the PC strand of the present invention.
도2는 본 발명의 피씨 강연선용 소선 표면에 인덴트를 형성하는 3방향 인덴트 롤러의 구조를 보인 정면도.Figure 2 is a front view showing the structure of the three-way indent roller to form indentation on the element wire surface for the PC strand of the present invention.
도3은 본 발명의 일실시예 피씨 강연선 구조를 보인 단면도.Figure 3 is a cross-sectional view showing an embodiment of a PC strand structure of the present invention.
(( 도면의 주요부분에 대한 부호의 설명 ))((Description of the code for the main part of the drawing))
1. 소선 2. 인덴트1. Wire 2. Indent
3. 3방향 인덴트 롤러 4. 신선선3. 3-way indent roller 4. Fresh wire
5. 인덴트 롤러 6. 인덴트 형성용 돌리5. Indent Roller 6. Indent Forming Dolly
7. 신선선 통과공 8. 강연선7. Fresh wire passing hole 8. Strand
IL. 인덴트 라인IL. Indent line
본 발명의 이형 소선이 사용된 피씨 강연선은, 여러 가닥의 소선이 꼬여진 피씨 강연선에 있어서, 상기 소선은 길이 방향을 따라 그 외주면에 3조의 인덴트 라인이 구비되고, 인접하는 두 인덴트 라인들의 중심들은 소선 중심에 대하여 120°의 중심각을 이루며, 각 인덴트 라인의 단위 인덴트는 타원형으로서 그 장축방향이 소선의 길이 방향에 대하여 경사지게 형성됨에 기술적 특징이 있다.In the PC strand in which the release element wire of the present invention is used, in the PC strand in which strands of twisted strands are twisted, the element wire is provided with three sets of indent lines on its outer circumferential surface along a longitudinal direction, and the two adjacent indent lines The centers form a central angle of 120 ° with respect to the center of the element wire, and the unit indent of each indent line is oval, and its long axis direction is inclined with respect to the length direction of the element wire.
상기 소선의 직경은 5.0 ∼ 5.5mm가 바람직하며, 이때 단위 인덴트의 깊이는 0.02 ∼ 0.05mm이고 폭은 대략 5 ∼6 mm이며, 단위 인덴트 사이의 간격은 2 ∼ 3mm로 하는 것이 유리하다.The diameter of the element wire is preferably 5.0 to 5.5 mm, wherein the depth of the unit indentation is 0.02 to 0.05 mm, the width is approximately 5 to 6 mm, and the spacing between the unit indents is preferably 2 to 3 mm.
그리고, 각 인덴트 라인간의 단위 인덴트 장축방향은 적어도 한 라인이 다른 라인과 상이한 방향을 유지하도록 하는 것이 바람직하다.The unit indent major axis direction between each indent line is preferably such that at least one line maintains a different direction from the other lines.
본 발명의 피씨 강연선은 2연선, 3연선, 7연선 및 19연선을 비롯한 다양한 구조를 취할 수 있으며, 그 중 대표적인 구조로는 7연선(1+6구조)을 들 수 있다.The PC strand of the present invention may take various structures including two strands, three strands, seven strands, and 19 strands, and a representative strand thereof includes seven strands (1 + 6).
그리고, 본 발명의 피씨 강연선을 구성하는 소선의 재질로는 피씨 강선 또는 강연선 재질로 널리 사용되고 있는 피아노 선재(KS D 3509) 등의 고탄소 강선이 바람직하다.As the material of the element wire constituting the PC strand of the present invention, a high carbon steel wire such as a piano wire (KS D 3509) widely used as a PC steel wire or a stranded wire material is preferable.
상기 본 발명의 피씨 강연선용 소선의 직경 범위 5.0 ∼ 5.5mm는 일반적인 피씨 강연선용 소선의 직경이며, 이러한 소선의 표면에 형성되는 단위 인덴트의 깊이를 0.02 ∼ 0.05mm로 한정한 것은, 0.02mm 미만의 깊이로 되는 때에는 인덴트 형성에 의해 기대되는 효과, 즉 표면 요홈부가 되는 각 인데트에 채워진 콘크리트가 소선의 표면에 박힌 앵커의 역할을 수행하므로써 콘크리트에 대한 소선의 유동이 방지되는 효과를 거의 기대할 수 없고, 반대로 0.05mm를 초과하는 깊이가 되면 소선 자체의 인장강도나 연신율 등의 기계적 특성이 저하됨과 아울러 인덴트 형성을 무리한 압착력을 가하는 과정에서 인덴트 롤러의 손상이 초래되거나 소선의 정상적인 이동이 어렵게 된다.물론, 인덴트의 깊이를 감안할 때 소선의 표면으로부터 들어간 콘크리트의 깊이가 충분히 깊다고는 할 수 없으나, 인덴트의 수가 매우 많고, 인덴트에 채워지는 콘크리트는 거의 탄성변형이 없기 때문에 무리없이 앵커의 역할을 수행할 수 있게 된다.The diameter range 5.0 to 5.5 mm of the PC strand strand element wire of the present invention is the diameter of a general PC strand strand element wire, and the depth of the unit indentation formed on the surface of such element strand is limited to 0.02 to 0.05 mm, less than 0.02 mm In the case of the depth of the wire, the effect expected by the indentation, that is, the concrete filled in each indent that becomes the surface groove, serves as an anchor embedded in the surface of the wire, almost prevents the flow of the wire to the concrete. On the contrary, if the depth exceeds 0.05mm, the mechanical properties such as the tensile strength and elongation of the wire itself are lowered, and the indent roller is damaged or the normal movement of the wire is not applied during the process of applying excessive pressing force. Of course, considering the depth of the indentation, the depth of the concrete from the surface of the element wire is sufficiently Although not deep, the number of indents is very large, and the concrete filled in the indents can almost perform the role of anchor without difficulty because there is almost no elastic deformation.
그리고, 본 발명에서 인덴트의 폭을 5 ∼ 6 mm로 하고, 단위 인덴트 사이의 간격을 2 ∼ 3mm로 하는 것은, 반복적인 실험 결과 이러한 범위에서 인덴트 롤러의 가공성과 슬립방지 및 표면적 확대 등의 여러 면에서 가장 유리하다는 사실이 밝혀졌기 때문이다.In the present invention, the width of the indentation is set to 5 to 6 mm, and the spacing between unit indents is set to 2 to 3 mm. As a result of repeated experiments, the workability of the indent roller, the slip prevention, the surface area expansion, etc. Because it turned out to be most advantageous in many ways.
상기 본 발명의 이형 소선이 사용된 피씨 강연선은 통상의 강연선 제조공정, 즉 모재 선재에 대한 전처리후 냉간 신선에 의해 신선선을 얻은 후에 연선기를 이용하여 연선하고 이어서 스테빌라이징 처리를 수행함으로써 강연선을 얻는 과정에 있어서, 상기 신선라인의 최종 신선다이와 권취기 사이의 신선선 이동경로상에 설치되는 본 발명의 인덴트 성형장치에 의해 그 외주면에 인덴트 라인이 형성되어 진다.The PC strand in which the release element wire of the present invention is used is obtained by drawing a stranded wire by using a stranding machine after obtaining a stranded wire by a conventional stranded wire manufacturing process, that is, by cold drawing after pretreatment of the base material wire, and then obtaining a stranded wire by performing a stabilizing treatment. In the process, an indent line is formed on the outer circumferential surface of the indent forming apparatus of the present invention, which is installed on the wire transfer path between the final draw die of the drawing line and the winding machine.
이와같은 본 발명의 인덴트 성형장치는 그 외주면에 인덴트 형성돌기가 구비된 인덴트 형성롤러 3개가 신선선을 중심으로 120°각도로 설치되어 그 사이를 통과하는 신선선의 외주면에 3개의 인덴트 라인이 형성되도록 구성된다.In the indent forming apparatus of the present invention, three indentation forming rollers having indentation forming projections on the outer circumferential surface thereof are installed at an angle of 120 ° with respect to the fresh wire and three indents on the outer circumferential surface of the fresh wire passing therebetween. The line is configured to be formed.
본 발명의 상기 목적과 기술적 구성 및 그에 따른 작용효과는 본 발명의 바람직한 실시예를 도시하고 있는 도면을 참조한 아래의 상세한 설명에 의해서 명확하게 이해될 것이다.The above objects and technical configurations of the present invention and the effects thereof will be clearly understood by the following detailed description with reference to the drawings showing preferred embodiments of the present invention.
먼저, 도1은 본 발명의 피씨 강연선용 소선의 구조를 보인 사시도로서, 도시된 바와 같이, 소선(1)은 길이 방향을 따라 그 외주면에 3조의 인덴트 라인(IL)이 구비되고, 인접하는 인덴트 라인의 중심, 즉, 장축과 단축이 교차하는 한 인덴트의 교차점과 그 인접 인덴트의 교차점은, 소선 중심에 대하여 120°의 중심각을 이루며, 각 인덴트 라인의 단위 인덴트(2)는 타원형으로서 그 장축방향(Q)이 소선(1)의 길이방향(P)에 대하여 경사지게 형성된다.First, Figure 1 is a perspective view showing the structure of the PC strand wire of the present invention, as shown, the element wire 1 is provided with three sets of indent lines (IL) on its outer peripheral surface along the longitudinal direction, adjacent to The center of the indent line, that is, the intersection point of one indent and the adjacent indent at the intersection of the long axis and the short axis form a center angle of 120 ° with respect to the center of the element wire, and the unit indent of each indent line (2) Is an ellipse and its long axis direction Q is formed to be inclined with respect to the longitudinal direction P of the element wire 1.
상기 소선의 직경(D)이 5.0 ∼ 5.5mm인 경우, 단위 인덴트(2)의 깊이(t)는 0.02 ∼ 0.05mm이고 폭(n)은 대략 5 ∼ 6 mm이며, 단위 인덴트 사이의 간격(p)은 2 ∼ 3mm로 하는 것이 유리하다.When the diameter D of the element wire is 5.0 to 5.5 mm, the depth t of the unit indent 2 is 0.02 to 0.05 mm and the width n is about 5 to 6 mm, and the interval between the unit indents is It is advantageous to set (p) 2-3 mm.
그리고, 각 인덴트 라인(IL)간의 단위 인덴트(2) 장축방향(Q)은 적어도 한 라인이 다른 라인과 상이한 방향을 유지한다.In addition, the major axis Q of the unit indent 2 between each indent line IL maintains at least one line different from the other lines.
다음, 도2는 본 발명의 피씨 강연선용 소선 표면에 인덴트를 형성하는 3방향 인덴트 롤러의 구조를 보인 정면도이다.Next, FIG. 2 is a front view showing the structure of a three-way indent roller forming an indent on the surface of the element strand for the PC strand of the present invention.
상기, 3방향 인덴트 롤러(3)는 냉간 신선되어 나오는 신선선(4)의 이동경로상에 설치되는 데, 그 설치형태는 도시된 바와같이 동일한 구조와 형태는 갖는 인덴트 롤러(5) 3개가 신선선(4)의 주위를 완전히 감싸도록 120°의 각도로 배열된다.The three-way indent roller (3) is installed on the moving path of the cold wire drawn out cold drawn, the installation form of the indent roller (5) having the same structure and shape as shown 3 The dog is arranged at an angle of 120 ° so as to completely wrap around the fresh wire 4.
상기 각각의 인덴트 롤러(5)는 그 접촉 외주면(CS)이 원호상 오목곡면을 이루며, 그 원호상 오목곡면상에는 상기 도1에서 살펴본 바의 단위 인덴트(2)의 형상과 일치하는 인덴트 형성용 돌기(6)가 배열되어 있다.Each of the indent rollers 5 has a contact outer circumferential surface CS that forms an arcuate concave surface, and an indent corresponding to the shape of the unit indent 2 shown in FIG. The forming projections 6 are arranged.
이들 3개의 인덴트 롤러(5) 사이에 형성되는 신선선 통과공(7)의 직경은 이를 통과하게 되는 신선선(4)의 외경과 동일하거나 약간 적은 크기를 유지함으로써 그 신선선 통과공(7)을 통과하는 신선선(4)은 인덴트 형성용 돌기(6)와 접촉하는부위에서 인덴트(2)가 형성됨으로써 3방향 인덴트 롤러(3)를 빠져 나온 소선(1)은 그 외주면상에 3조의 인덴트 라인(IL)이 성형이 이루어지게 된다.The diameter of the drawing wire through hole 7 formed between these three indent rollers 5 is the same as or slightly less than the outer diameter of the drawing wire 4 through which the drawing wire through hole 7 The wire (4) passing through) is formed in the indent (2) in contact with the indentation forming projection (6), the element wire (1) exiting the three-way indent roller (3) on the outer peripheral surface Three sets of indent lines IL are formed.
도3은 본 발명의 일실시예 피씨 강연선에 대한 단면구조도로서, 이는 상기 도2에 도시된 본 발명의 3방향 인덴트 롤러(3)를 이용하여 얻어진 바의 도1에서와 같은 피씨 강연선용 소선(1) 7가닥이 연합되어진 1+6 구조의 피씨 강연선(8)이다.FIG. 3 is a cross-sectional structure diagram of an embodiment of a PC strand of a present invention, which is an element for a PC strand as shown in FIG. 1 as obtained by using the three-way indent roller 3 of the present invention shown in FIG. (1) 7 strands of 1 + 6 PC strand (8).
도3에 도시된 실시예의 강연선은 심선을 비롯한 외층 소선 모두가 인덴티트 소선으로 구성되어 있으나, 경우에 따라서는 심선은 일반적인 원형선으로 하고, 외층 소선만을 인덴티드 소선으로 구성할 수도 있을 것이다.In the strand of the embodiment shown in FIG. 3, all the outer layer wires including the core wires are composed of indented wires, but in some cases, the core wires may be general circular wires, and only the outer wires may be composed of indented wires.
본 발명의 실시예는 다음과 같다.Embodiments of the present invention are as follows.
먼저, 직경이 13mm인 피아노 선재(KS D 3509의 화학조성을 갖는 강선)에 대한 전처리로서 염산조에서의 산세 후 수세와 건조를 행하고, 신선성의 향상을 위하여 인산염 피막코팅을 행하였다.First, as a pretreatment for a piano wire having a diameter of 13 mm (steel wire having a chemical composition of KS D 3509), washing with water in a hydrochloric acid bath followed by washing with water and drying, and phosphate coating was performed to improve freshness.
상기 인산염 피막코팅된 선재를 고속 신선설비(36"X8HPS)로 신선하여 80% 정도의 선경감소가 이루어지도록 냉간인발 가공을 행하였다.The wire coated with the phosphate coating was cold drawn at a high speed drawing facility (36 "X8HPS) to perform a cold drawing process to achieve a wire reduction of about 80%.
상기 신선되어 나오는 신선선의 이동경로상에 도2에서와 같은 3방향 인덴트 롤러(3) 장치를 설치하여 신선선의 표면에 3조의 인덴트 라인이 형성되도록 한 후 권취기에 권취되도록 하였다.The three-way indenting roller 3 device as shown in FIG. 2 was installed on the moving path of the drawn wire so that three sets of indented lines were formed on the surface of the drawn wire, and then wound on a winding machine.
상기 인덴트가 형성된 소선을 공급 소선으로 하여 스킵형 연선기(36"X6SKIP)에서 소선의 연합이 이루어지도록 하여 도3에서와 같은 1+6구조의 연선을 얻었다.A stranded wire having a 1 + 6 structure as shown in FIG. 3 was obtained by associating a stranded wire in a skip type twisted pair machine (36 "X6SKIP) using the strand in which the said indentation was formed as a supply strand.
상기 연선이 권취기로 이동하기 전에 고주파 유도로를 통과하도록 하여 열처리를 행하였다. 이때 제어반을 통해서 1,2차 캡스턴의 구동을 제어하여 고주파 유도로를 통과하는 연선에 절단하중의 약 45%의 긴장이 부여되도록 하였다.Heat treatment was performed by passing the high-frequency induction furnace before the stranded wire moved to the winding machine. At this time, by controlling the driving of the first and second capstan through the control panel, the tension of about 45% of the cutting load was applied to the stranded wire passing through the high frequency induction furnace.
상기의 제조과정을 통해서 얻어진 본 발명의 피씨 강연선에 대한 기계적 물성치를 측정하여 본 바, KS D 7002 SWPC 7B L종에서 규정된 물성치를 만족하는 것으로 확인되었다.As a result of measuring the mechanical properties of the PC strand of the present invention obtained through the above manufacturing process, it was confirmed that the physical properties specified in KS D 7002 SWPC 7B L class.
상기 본 발명 실시예의 피씨 강연선으로 피씨 콘크리트 제품을 제작하기 위하여 이를 형틀상에 위치시킨 후 양 단부에 인장력 부여장치의 장착구를 물려 긴장상태가 유지되도록 한 후 형틀 내부에 콘크리트 슬러리를 채워 양생시켜 피씨 제품을 얻었다.In order to manufacture the PC concrete product with the PC strand of the embodiment of the present invention, it is placed on the mold, and the tension is maintained by biting the mounting holes of the tension applying device at both ends, and then the concrete slurry is filled into the mold to cure the PC. The product was obtained.
상기와 같은 피씨 제조과정중 강연선의 양 단부에서 장착구의 슬립은 전혀 나타나지 않았으며, 콘크리트 내부에 매입된 피씨 강연선과 콘크리트 간의 접착력 측정결과 종래의 피씨 제품에 비해 향상된 접착력을 나타내는 것으로 밝혀졌다.During the manufacturing process of the PC, the slippage of the mounting holes was not shown at both ends of the strand, and the adhesion between the PC strand and the embedded embedded concrete was found to show improved adhesion as compared to conventional PC products.
이와 같은 본 발명의 피씨 강연선이 사용된 피씨 제품에서의 강연선과 콘크리트간의 접착력 향상은 강연선의 외층 소선이 표면적이 증대되어 콘크리트와의 접촉면적이 증대된 점, 외층 소선의 인덴트 형성에 의해 요철구조로 콘크리트와의 록킹 상태가 강화된 점 및 외층 소선간의 접촉부에서 인덴트가 개방홈을 형성하는 역할을 하여 콘크리트 슬러리가 강연선의 안쪽으로 까지 충분히 충진된 상태로 양생된 점 등에 기인하는 것으로 판단된다.The improvement of adhesion between the stranded wire and the concrete in the PC product using the stranded steel of the present invention increases the surface area of the stranded wire of the stranded wire so that the contact area with the concrete is increased, and the uneven structure is formed by the indentation of the outer layered wire. It is believed that this is due to the fact that the indentation forms an open groove at the point of contact with the furnace concrete and the contact point between the outer layer wires, and the concrete slurry is sufficiently cured to the inside of the strand.
이상에서와 같이, 본 발명의 이형 소선이 사용된 피씨 강연선은 이를 구성하고 있는 소선의 외주면상에 인덴트가 연속적으로 형성되어 요철면을 이루고 있기 때문에 피씨 콘크리트 제품의 제조시 긴장을 위해서 양 단부에 장착되는 장착구의 슬립발생이 억제되어 피씨 제품이 품질특성 저하를 방지할 수 있는 효과가 있다.As described above, the PC strand in which the release element wire of the present invention is used has an indentation continuously formed on the outer circumferential surface of the element wire constituting the same so as to form an uneven surface at both ends for tension in the manufacture of the PC concrete product. Slip occurrence of the mounting fixture to be mounted is suppressed, thereby preventing the deterioration of the quality characteristics of the PC product.
그리고, 본 발명의 피씨 강연선은 그 외주면의 표면적이 증대되어 콘크리트와의 접촉면적이 확대됨과 아울러 요철표면에 의한 콘크리트의 록킹작용에 의해 콘크리트와의 접착력 증대가 이루어지는 장점이 있다.In addition, the PC strand of the present invention has the advantage that the surface area of the outer peripheral surface is increased to increase the contact area with the concrete and the adhesion to the concrete is increased by the locking action of the concrete by the uneven surface.
이에 더하여, 본 발명의 피씨 강연선은 신선라인상에 설치되는 간단한 구조의 3방향 인덴트 롤러 장치에 의해서 신선선의 이동간에 그 외주면에 대한 3조의 인덴트 라인이 성형되므로 종래의 다이폼드 피씨 강연선에 비해 그 제조비용을 현격히 줄이면서도 다이폼드 피씨 강연선에서와 동등한 수준의 슬립방지 효과를 도모할 수 있다.In addition, the PC strand of the present invention is formed by a three-way indent roller device of a simple structure installed on the drawing line, compared to the conventional die-formed PC strand because three sets of indentation lines for the outer peripheral surface are formed between the movement of the drawing wire. The manufacturing cost can be reduced considerably, while the slip prevention effect equivalent to that of a die-formed PC strand can be achieved.
Claims (4)