KR100310114B1 - Melt-bonded ply yarn for using in mop and its manufacturing method - Google Patents
Melt-bonded ply yarn for using in mop and its manufacturing method Download PDFInfo
- Publication number
- KR100310114B1 KR100310114B1 KR1019990034529A KR19990034529A KR100310114B1 KR 100310114 B1 KR100310114 B1 KR 100310114B1 KR 1019990034529 A KR1019990034529 A KR 1019990034529A KR 19990034529 A KR19990034529 A KR 19990034529A KR 100310114 B1 KR100310114 B1 KR 100310114B1
- Authority
- KR
- South Korea
- Prior art keywords
- yarn
- yarns
- twisted
- fused
- twisted yarn
- Prior art date
Abstract
본 발명은 합연사의 연이 풀리지 않도록 합연사를 구성하는 원사들을 서로 융착시키는 것을 포함하는 모프(mop)용의 융착된 합연사 및 그 제조방법에 관한 것으로서, 도 2에 개략적으로 도시한 바와 같이, 본 발명에 따른 모프용의 융착된 합연사는, 두 올 이상의 원사(12)들을 저융점을 갖는 열융착사(13)와 함께 합사하고, 꼬임을 형성한 상태에서 원사(12)들을 열융착사(13)로 융착시켜서 이루어짐을 특징으로 한다.The present invention relates to a fused spliced twisted yarn for morph (mop) comprising a fusion of the yarns constituting the twisted twisted yarn so that the twisted yarn of the twisted yarn is not loosened, as shown in FIG. Fused fused twisted yarn for morphs according to the present invention, the two or more yarns 12 are fused together with a thermal fusion splicing yarn 13 having a low melting point, and the yarns 12 are thermally fused in a twisted state ( 13) is characterized in that it is made by fusion.
따라서, 수득된 합연사(11)를 임의의 부분에서 절단하여도 절단면에서 원사(12)간의 풀림현상이 일어나지 않으며, 원사(12)들이 서로에 대하여 직접 융착되어 있어 합연상태를 그대로 유지하고, 원사(12)의 분리 및 절단 등을 예방하여 내구성이 향상되며, 외관이 미려한 상태를 유지하는 등의 효과가 있다.Therefore, even if the obtained twisted yarn 11 is cut at any part, no loosening phenomenon occurs between the yarns 12 at the cut surface, and the yarns 12 are directly fused to each other to maintain the bonded state, The durability is improved by preventing the separation and cutting of (12), and the like is effective in maintaining a beautiful appearance.
Description
본 발명은 모프용의 융착된 합연사 및 그 제조방법에 관한 것이다. 보다 상세하게는 본 발명은 합연사의 연이 풀리지 않도록 합연사를 구성하는 원사들을 서로 융착시키는 것을 포함하는 모프용의 융착된 합연사 및 그 제조방법에 관한 것이다.The present invention relates to a fused welded twisted yarn for morphs and a method of manufacturing the same. More particularly, the present invention relates to a fused spliced twisted yarn for morphs and a method of manufacturing the same, comprising fusing the yarns constituting the twisted yarn together so that the twisted twisted yarn does not loosen.
합연은 단사 또는 2가닥 이상이 합사된 합사들 중에서 선택된 원사 두 올 이상을 합사한 후, 꼬임을 형성하는 것으로서, 합연하는 방법으로는 합사기에서 합사한 후 연사기에서 꼬임을 형성하는 방법과, 연사기에서 합사와 연사를 같이 하는 방법이 일반적으로 행하여지고 있으며, 이렇게 합연된 합연사(11)를 도 1에 나타내었다. 이러한 합연은 주로 저데니어의 단사들을 두 가닥 이상 서로 꼬아서 하나의 태데니어의 실을 만드는 데 사용되며, 특히 대걸레(mop)용 등 내구성과 흡습성 등이 우수한 제품을 만드는 데 사용될 수 있다.Plywood is a twisted yarn formed by twisting two or more selected yarns from a single yarn or two or more plywood yarns, and forming a twist, which is a method of forming a twist in a twisting machine after twisting in a twisting machine and a twisting machine. In general, a method of synthesizing with a plywood yarn is performed in general, and thus the combined plywood yarn 11 is shown in FIG. This joint is mainly used to make a single denier yarn by twisting two or more strands of low denier together, and may be used to make a product having excellent durability and hygroscopicity, such as for mops.
그러나, 종래의 합연사(11)는 단지 기계적으로만 연사하여 꼬임을 부여하기 때문에 꼬임이 풀리게 되며, 꼬임이 풀리게 되면 단사의 내구성이 약화되는 등의 문제가 있었다.However, the conventional twisted yarn 11 is twisted only by mechanically twisting to impart twist, so that the twist is released, and when the twist is released, the durability of the single yarn is weakened.
본 발명의 목적은 합연사의 연이 풀리지 않도록 합연사를 구성하는 원사들을 서로 융착시켜서 이루어진 모프용의 융착된 합연사를 제공하는 데 있다.SUMMARY OF THE INVENTION An object of the present invention is to provide a fused spliced twisted yarn for morphs formed by fusing the yarns constituting the spliced twisted yarn together so that the twisted twisted yarns are not loosened.
본 발명의 다른 목적은 합연사의 연이 풀리지 않도록 합연사를 구성하는 원사들을 서로 융착시켜서 이루어진 모프용의 융착된 합연사의 제조방법을 제공하는 데 있다.Another object of the present invention is to provide a method for manufacturing a fused spliced twisted yarn for morphs formed by fusing the yarns constituting the spliced twisted yarn together so that the twisted twisted yarn does not loosen.
도 1은 종래의 합연사를 개략적으로 도시한 사시도이다.1 is a perspective view schematically showing a conventional twisted yarn.
도 2는 본 발명의 일 실시예에 따른 융착사를 포함하여 융착된 합연사를 개략적으로 도시한 사시도이다.2 is a perspective view schematically showing a fused twisted yarn including a fused yarn according to an embodiment of the present invention.
도 3은 본 발명의 다른 일 실시예에 따른 융착사를 포함하여 융착된 합연사를 개략적으로 도시한 사시도이다.3 is a perspective view schematically showing a fused twisted yarn including a fused yarn according to another embodiment of the present invention.
※ 도면의 주요부분에 대한 부호의 설명※ Explanation of code for main part of drawing
11 : 합연사 12 : 원사11: combined yarn 12: yarn
13 : 열융착사13: heat fusion yarn
본 발명에 따른 모프용의 융착된 합연사는, 단사 또는 2가닥 이상이 합사된 합사들 중에서 선택된 원사 두 올 이상을 합사하고, 꼬임을 형성한 상태에서 원사들을 열융착사로 융착시켜서 이루어짐을 특징으로 한다.Fusion fusing twisted yarn for morph according to the present invention is characterized by being made by fusing two or more yarns selected from single yarns or two or more strands of plywood, and fusion splicing the yarns with heat fusion yarns in a twisted state. .
또한 본 발명에 따른 모프용의 융착된 합연사의 제조방법은, 단사 또는 2가닥 이상이 합사된 합사들 중에서 선택된 원사 두 올 이상을 저융점의 열가소성을 갖는 열융착사와 함께 합사하는 합사단계; 합사된 원사들에 꼬임을 형성하는 가연단계; 꼬임이 형성된 원사들을 가열시켜 열융착사로 융착시키는 융착단계;를 포함하여 이루어짐을 특징으로 한다.In addition, the method for producing a fused fused twisted yarn for morph according to the present invention, the step of pulverizing the two or more yarns selected from the fused twisted yarn with a thermal fusion yarn having a low melting point thermoplastic; A twisting step of forming a twist on the spun yarn; It characterized in that it comprises a; fusion step of fusion to heat-bonded yarn by heating the twisted yarns.
이하, 본 발명의 구체적인 실시예를 첨부한 도면을 참조하여 상세히 설명한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도 2에 개략적으로 도시한 바와 같이, 본 발명에 따른 모프용의 융착된 합연사는, 두 올 이상의 원사(12)들을 저융점을 갖는 열융착사(13)와 함께 합사하고, 꼬임을 형성한 상태에서 원사(12)들을 열융착사(13)로 융착시켜서 이루어짐을 특징으로 한다.As schematically shown in FIG. 2, the fused welded twisted yarn for morphs according to the present invention is a state in which two or more yarns 12 are fused together with a heat fused yarn 13 having a low melting point and twisted. In the yarn 12 is characterized in that it is made by fusing the thermal fusion yarn (13).
상기에서 원사(12)는 그 종류에 제한이 없으며, 단사 또는 2합 이상의 합사들이 사용될 수 있다. 상기 원사(12)로는 천연섬유나 합성섬유들이 모두 사용이 가능함은 당연하며, 특히 합성섬유의 경우, 본 발명에서 사용되는 열융착사(13) 보다 높은 융점을 갖는 것이 수득되는 합연사(11)의 형태안정성 등을 위하여 바람직하다. 특히, 대걸레(mop)용 등 내구성과 흡습성 등이 우수한 면과 같은 천연섬유가 바람직하게 사용될 수 있으며, 더욱 바람직하게는 면번수 0.5 내지 10 정도의 태번수의 면섬유를 사용할수 있다.The yarn 12 is not limited in kind, and single yarn or two or more ply yarns may be used. Natural yarns or synthetic fibers may be used as the yarn 12, and in particular, in the case of synthetic fibers, the conjugated yarn 11 obtained having a higher melting point than the heat-sealed yarn 13 used in the present invention. It is preferable for morphological stability and the like. In particular, natural fibers such as cotton having excellent durability and hygroscopicity, such as mop, may be preferably used. More preferably, cotton fibers having a cotton number of about 0.5 to about 10 can be used.
다. 상기 원사(12)는 수득되는 합연사(11)의 용도에 따라 적절한 섬유들이 선택되어 사용될 수 있음은 당업자에게는 용이하게 이해될 수 있는 것이다. 도 2에는 본 발명에 따라 합연사(11)를 제조함에 있어 원사(12)로서 단사를 사용한 상태를 개략적으로 도시하였으며, 도 3에는 원사(12)로서 합사를 사용한 상태를 개략적으로 도시하였다.All. It will be readily understood by those skilled in the art that the yarn 12 may be selected and used appropriate fibers depending on the use of the twisted yarn 11 obtained. 2 schematically illustrates a state using single yarn as yarn 12 in manufacturing the twisted yarn 11 according to the present invention, and FIG. 3 schematically illustrates a state of using yarn as yarn 12.
상기 원사(12)들의 합사는 당업계에서는 상용화된 통상의 합사기에 의하여 합사될 수 있음은 당업자에게는 자명한 것으로 이해될 수 있다.It will be understood by those skilled in the art that the yarns of the yarns 12 may be yarnd by conventional yarns commercially available in the art.
상기 원사(12)들의 합사에는 상기 원사(12)들을 서로 융착시킬 수 있는 열융착사(13)가 함께 합사된다.The fused yarns of the yarns 12 are fused together with a thermal fusion yarn 13 capable of fusion of the yarns 12 with each other.
합사된 상기 원사(12)들은 역시 당업계에서는 상용화된 통상의 연사기에 의하여 연사되어 꼬임이 형성될 수 있음은 당업자에게는 자명한 것으로 이해될 수 있다. 특히 바람직하게는 모프용의 가연은 3 내지 8TPI(Twist per inch)로 연사하는 것이 바람직하다.It will be appreciated by those skilled in the art that the yarns 12 that have been plyed can also be twisted by conventional yarns commercially available in the art to form twists. Particularly preferably, the morphology for morph is twisted at 3 to 8 TPI (Twist per inch).
수득된 합연사(11)는 가열에 의하여 상기 열융착사(13)의 열가소성에 의하여 합연사(11)를 구성하는 원사(12)들이 서로에 대하여 융착되게 된다. 상기 합연사(11)는 열융착사(13)를 포함하여 총 데니어 6,000 내지 8,000D(데니어)가 되도록 하는 것이 바람직하다. 그러나, 이러한 수치의 제한은 상기한 바와 같이 본 발명에 따른 합연사를 대걸레 용으로 사용하는 경우를 기준으로 한 것으로서, 합연사의 총 데니어나 원사(12)의 재질 등은모두 수득되는 합연사의 용도에 따라 적절히 선택될 수 있음은 당업자에게는 당연히 이해될 수 있는 것이다.The obtained twisted yarn 11 is fused to each other by the yarns 12 constituting the twisted yarn 11 by thermoplasticity of the heat-sealed yarn 13 by heating. The twisted yarn 11 may include a thermal fusion yarn 13 so as to have a total denier of 6,000 to 8,000 D (denier). However, the limitation of these values is based on the case where the twisted yarn according to the present invention is used for a mop as described above, and the total denier of the twisted yarn or the material of the yarn 12 is obtained. It can be understood by those skilled in the art that it can be appropriately selected depending on the intended use.
따라서, 이렇게 수득된 본 발명에 따른 융착된 합연사(11)는 합사 및 연사되어 꼬임이 형성된 합연사(11)를 구성하는 원사(12)들 간에 열융착사(13)에 의한 융착이 이루어져 풀림이 방지되게 된다.Therefore, the fused plywood yarn 11 according to the present invention thus obtained is fused by heat fusion yarn 13 between the yarns 12 constituting the plywood twisted yarn 11 that is twisted and twisted to form twist. This will be prevented.
또한, 본 발명에 따른 모프용의 융착된 합연사의 제조방법은, 단사 또는 2가닥 이상이 합사된 합사들 중에서 선택된 원사(12) 두 올 이상을 저융점의 열가소성을 갖는 열융착사(13)와 함께 합사하는 합사단계; 합사된 원사(12)들에 꼬임을 형성하는 가연단계; 꼬임이 형성된 원사(12)들을 가열시켜 열융착사(13)로 융착시키는 융착단계;를 포함하여 이루어짐을 특징으로 한다.In addition, according to the present invention, a method of manufacturing a fused spliced twisted yarn for morphing includes heat-bonding yarn 13 having a low melting point thermoplastic of two or more yarns 12 selected from single yarn or two or more stranded plywood. A step of envoying together with the envoy; A twisting step of forming a twist on the yarn 12; It characterized in that it comprises a; fusion step of fusion to heat-bonded yarn 13 by heating the twisted yarn 12 is formed.
상기에서의 원사(12)들의 합사를 수행하는 합사단계는 통상의 합사기에 의하여 달성될 수 있음은 당업자에게는 용이하게 이해될 수 있으며, 가연단계 역시 통상의 가연기에 의하여 달성될 수 있음은 당업자에게는 용이하게 이해될 수 있는 것이다.It can be easily understood by those skilled in the art that the step of weaving the yarn 12 is carried out by a common weaving machine, and it can be easily understood by those skilled in the art that the burning step can also be accomplished by a common combustor. It can be understood.
본 발명에서는 합사단계에서 합사되고, 가연단계에서 꼬임이 형성된 상기 합연사에 상기 합사단계에서 원사(12)들과 함께 열융착사(13)가 합사되어 꼬임이 형성된 합연사를 가열하여 그 내부에 포함된 열융착사(13)의 가열에 의하여 원사(12)들을 서로에 대하여 융착시킨 점에 특징이 있는 것이다.In the present invention, the plywood yarn is twisted in the plywood step, the twisted yarn is formed in the twisting step in the plywood step in the plywood step together with the yarns 12 in the heat fusion yarn 13 is fused to heat the twisted plywood yarn is formed therein It is characterized in that the yarns 12 are fused to each other by heating the included thermal fusion yarn 13.
상기 열융착사(13)는 종래 사용되던 일반 나이론 등 화학섬유 및 면사등이 220 내지 260℃에서 용융되는 것에 비하여 80 내지 125℃의 낮은 온도에서 용융되는 저융점의 열가소성수지를 섬유상으로 형성한 것으로서, 가열에 의하여 낮은 온도에서 전체적으로 용융되거나 또는 적어도 부분적으로 용융되어 열가소성 및 열융착성을 가지게 되고, 다시 냉각됨에 따라 고화되어 원사(12)들을 서로 융착, 고정시키는 역할을 한다. 이러한 열융착사(13)는 역시 당업자에게는 상용적으로 구입하여 사용할 수 있을 정도로 공지된 것으로서, 저융점의 폴리에틸렌섬유 또는 폴리아미드섬유 등을 예로 들 수 있다. 특히, 본딩방법에서는 종래에는 연사코드를 습열처리에 의한 방법으로 비교적 높은 용융점에서 접합시킴으로써 불균일한 결과를 초래할 수 있었으나, 본 발명에 따르면 전기열에 의한 가열에 의하여 수행될 수 있으며, 예를 들면 전열방식의 가열드럼을 사용하여 드럼의 온도와 회전속도 등의 조절로 균일하면서도 용이하게 열처리가가 가능하도록 하여 생산성을 향상시킬 수 있다.The heat-sealed yarn 13 is formed of a low melting thermoplastic resin melted at a low temperature of 80 to 125 ℃ in the form of fibers compared to the conventionally used chemical fibers such as nylon and cotton yarn melt at 220 to 260 ℃ By heating, at a low temperature as a whole or at least partially melted to have a thermoplastic and heat sealability, and solidified as it is cooled again to serve to fuse and fix the yarns 12 to each other. The heat-sealed yarn 13 is also known to those skilled in the art to be commercially available and used, and examples thereof include polyethylene fibers or polyamide fibers having a low melting point. Particularly, in the bonding method, conventionally, the twisted yarn cord is bonded by a method of wet heat treatment at a relatively high melting point, which may result in nonuniform results, but according to the present invention, it may be performed by heating by electric heat. By using the heating drum of the drum temperature and rotation speed, such as to control the uniformity and easy heat treatment can be improved productivity.
이하에서 본 발명의 바람직한 실시예 및 비교예들이 기술되어질 것이다.Hereinafter, preferred embodiments and comparative examples of the present invention will be described.
이하의 실시예들은 본 발명을 예증하기 위한 것으로서 본 발명의 범위를 국한시키는 것으로 이해되어져서는 안될 것이다.The following examples are intended to illustrate the invention and should not be understood as limiting the scope of the invention.
실시예 1Example 1
면번수 1.5의 비교적 굵은 면사로 된 원사 2가닥을 합연할 때 Z연의 원사 사이에 75D의 열융착사 2가닥이 위치하도록 합연하고, 7TPI로 S연사한다음, 수득된 합연사를 약 120℃로 가열하여 대걸레용으로 사용될 수 있는 본 발명에 따른 모프용의 융착된 합연사를 수득하였다.When joining two strands of relatively thick cotton yarn with a cotton number of 1.5, the two strands of 75D heat-fused yarns are positioned between the yarns of Z, and S-spun at 7TPI, and the obtained twisted yarn is about 120 ° C. Heating yielded a fused spliced twisted yarn for morphs according to the invention that can be used for mops.
수득된 합연사는 중간의 절단에 의하여도 절단면에서의 원사간의 풀림이 일어나지 않음을 육안으로 확인할 수 있었다.The obtained twisted yarn was visually confirmed that the yarn was not loosened at the cut surface even by the intermediate cutting.
실시예 2Example 2
120D, 27가닥의 분할 극세사를 통상의 방법으로 합연하여서 된 3,240D의 합연사로 된 원사 2가닥을 합연할 때 원사 사이에 75D의 열융착사 2가닥이 위치하도록 합연하고, 5.5TPI로 Z연사한 다음, 수득된 합연사를 약 150℃로 가열하여 대걸레용으로 사용될 수 있는 본 발명에 따른 모프용의 융착된 합연사를 수득하였다. 수득된 합연사에서의 열융착사는 거의 합연사의 중심에서 용융되고, 원사를 구성하는 각각의 분할 극세사들은 표면에 돌출되기도 하고 내부를 통과하기도 하면서 뒤틀린 상태(Spiral state)로 각 원사의 접착상태는 순차 접착된 상태를 유지하는 구조로 이루어짐을 확인하였다.When joining two strands of 3,240D twisted yarns by combining 120D and 27 split microfibers in a conventional manner, the two strands of 75D heat-bonded yarns are positioned between the yarns, and the Z twisted yarn is 5.5TPI. The obtained twisted yarn was then heated to about 150 ° C. to obtain a fused bonded twisted yarn for morphs according to the present invention, which can be used for mops. The heat-bonded yarn in the obtained twisted yarn is almost melted at the center of the twisted yarn, and each of the split microfibers constituting the yarn is in a spiral state while protruding from and passing through the surface. It was confirmed that it consists of a structure to maintain a state in which they are sequentially bonded.
수득된 합연사는 중간의 절단에 의하여도 절단면에서의 원사간의 풀림이 일어나지 않음을 육안으로 확인할 수 있었다.The obtained twisted yarn was visually confirmed that the yarn was not loosened at the cut surface even by the intermediate cutting.
따라서, 본 발명에 의하면 절단면에서 원사(12)간의 풀림현상이 일어나지 않으며, 원사(12)들이 서로에 대하여 직접 융착되어 있어 합연상태를 그대로 유지하고, 원사(12)의 분리 및 절단 등을 예방하여 내구성이 향상되며, 외관이 미려한 상태를 유지하는 등의 효과가 있다.Therefore, according to the present invention, the loosening phenomenon between the yarns 12 does not occur in the cut surface, and the yarns 12 are directly fused to each other to maintain the coalescing state and to prevent the separation and cutting of the yarns 12. Durability is improved, and there is an effect of maintaining a beautiful appearance.
이상에서 본 발명은 기재된 구체예에 대해서만 상세히 설명되었지만 본 발명의 기술사상 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속함은 당연한 것이다.Although the present invention has been described in detail only with respect to the described embodiments, it will be apparent to those skilled in the art that various modifications and variations are possible within the technical scope of the present invention, and such modifications and modifications are within the scope of the appended claims.
Claims (3)