KR100305471B1 - Manufacturing method of gasket - Google Patents
Manufacturing method of gasket Download PDFInfo
- Publication number
- KR100305471B1 KR100305471B1 KR1019990000545A KR19990000545A KR100305471B1 KR 100305471 B1 KR100305471 B1 KR 100305471B1 KR 1019990000545 A KR1019990000545 A KR 1019990000545A KR 19990000545 A KR19990000545 A KR 19990000545A KR 100305471 B1 KR100305471 B1 KR 100305471B1
- Authority
- KR
- South Korea
- Prior art keywords
- plate
- gasket
- metal layer
- manufacturing
- thin
- Prior art date
Abstract
밀봉부를 형성하기 위한 가공을 간단하고 또한 저렴하게 제조할 수 있고, 확실한 밀봉효과를 얻을 수 있는 개스킷의 제조방법을 제공한다.Provided are a method for manufacturing a gasket which can be easily and inexpensively manufactured for forming a seal, and can obtain a reliable sealing effect.
플레이트(2)를 모재(母材)(2a)의 한쪽 면 또는 양 면에 연질의 금속층(2b)을 피복한 클래드(clad) 강판으로 구성한다. 플레이트(2)의 연질의 금속층(2b)에 두께가 얇은 부분(6)을 형성한 후, 두께가 얇은 부분(6)을 접는 것에 의해 밀봉부(8)를 형성한다.The plate 2 is comprised from the clad steel plate which coat | covered the soft metal layer 2b on one side or both sides of the base material 2a. After the thin part 6 is formed in the soft metal layer 2b of the plate 2, the sealing part 8 is formed by folding the thin part 6.
Description
본 발명은, 내연기관의 실린더 블록과 실린더 헤드와의 사이에 장착된 실린더 헤드 개스킷 등으로서 적합한 개스킷의 제조방법에 관한 것이다.TECHNICAL FIELD This invention relates to the manufacturing method of a gasket suitable as a cylinder head gasket etc. which were attached between the cylinder block and the cylinder head of an internal combustion engine.
종래부터 알려져 있는 개스킷에서는, 밀봉부의 적당한 면압을 확보하기 위해, 두께조정을 위한 금속박판으로 이루어진 심(shim)을 상기 밀봉부에 겹쳐서 설치하거나, 금속판의 끝가장자리를 접는 것에 의해 두꺼운 밀봉부를 형성하는 등의 수단이 이용되고 있다.In the conventionally known gasket, in order to secure a proper surface pressure of the seal, a thick seal is formed by overlapping the seal with a shim made of a metal sheet for thickness adjustment or by folding the edge of the metal plate. And the like are used.
그러나, 상기 종래의 개스킷은, 심의 미묘한 두께조정이 필요할 뿐만 아니라, 상기 심을 용접하는 등의 수고로움도 생기고, 또 금속판의 끝가장자리를 접는 경우에는 그 금속판의 두께만큼 밀봉부가 두꺼워지므로, 접는 금속판의 두께에 제약이 생기고, 특히 1장의 금속판으로 이루어진 개스킷에 대한 적용은 곤란하며, 따라서 이들 개스킷에 있어서 적당한 밀봉부를 형성하는 것이 번거롭고, 결과적으로 유효한 밀봉부를 갖는 개스킷을 저렴하게 제조할 수 없다라는 문제점이 있었다.However, in the conventional gasket, not only the delicate thickness adjustment of the shim is required, but also the trouble of welding the shim is caused, and when the edge of the metal plate is folded, the sealing portion is thickened by the thickness of the metal plate. The thickness is restricted, and in particular, application to a gasket composed of one metal plate is difficult, and therefore, it is cumbersome to form an appropriate seal in these gaskets, and as a result, there is a problem that a gasket having an effective seal can not be manufactured at low cost. there was.
이러한 문제점에 대처하여, 예를 들면 특개평 5-52267호 공보 등에 있어서는, 끝가장자리를 접는 부분을 미리 프레스성형, 에칭가공, 절삭가공 등에 의해 얇게 해 두는 것이 제안되고 있다.In order to cope with such a problem, for example, in Japanese Unexamined Patent Application Publication No. 5-52267, it is proposed to thin the portion of the edge folded in advance by press molding, etching, cutting, or the like.
그러나, 개스킷을 구성하는 금속판을 프레스성형에 의해 두께를 얇게 하면, 그 두께가 얇은 부분에 내부응력이 잔류해서 변형이 발생하고, 금속판 자체에 휘어짐이 발생할 가능성이 크고, 또 상기 에칭가공이나 절삭가공은 공정수의 증가에 따라 비용이 높아지는 것을 피할 수 없는 것이다.However, if the metal plate constituting the gasket is made thin by press molding, the internal stress remains in the thin portion and the deformation is likely to occur, and the metal plate itself may be warped, and the etching or cutting process may be performed. Inevitably, the cost increases as the number of processes increases.
본 발명의 기술적 과제는, 밀봉부를 형성하기 위한 상기 두께를 얇게 하는 가공이 간단하고, 내부응력을 잔류시키지 않고, 확실한 밀봉효과를 얻을 수 있는개스킷을 저렴하게 제조할 수 있는 개스킷의 제조방법을 제공하는 데에 있다.The technical problem of this invention is providing the manufacturing method of the gasket which can manufacture the gasket which can process the thinning said thickness for forming a sealing part easily, and can obtain a reliable sealing effect, without remaining an internal stress. It's there.
상기 과제를 해결하기 위한 본 발명의 제1의 개스킷의 제조방법은, 1장의 플레이트, 또는 적층한 여러개의 플레이트로 이루어지고, 주위를 밀봉할 적어도 1개의 구멍을 갖는 개스킷의 제조방법에 있어서, 적어도 1장의 플레이트를, 경질의 금속판으로 이루어진 모재의 한쪽 면 또는 양 면에, 상기 모재보다 연질의 금속층을 피복해서 이루어진 클래드 강판으로 구성하고, 상기 클래드 강판으로 이루어진 플레이트에 있어서의 상기 구멍의 가장자리부의 연질의 금속층에 두께가 얇은 부분을 형성한 후, 상기 두께가 얇은 부분을 접는 것에 의해 다른 평탄부보다 두꺼운 밀봉부를 형성하는 것을 특징으로 하는 것이다.The manufacturing method of the 1st gasket of this invention for solving the said subject consists of one plate or the laminated several plate, The manufacturing method of the gasket which has the at least 1 hole which seals around, At least One plate is comprised by the clad steel plate which coat | covered the metal layer softer than the said base material on one side or both surfaces of the base material which consists of a hard metal plate, and is soft in the edge part of the said hole in the plate which consists of said clad steel plate. After the thin portion is formed in the metal layer of the thin layer, the thicker portion is formed by folding the thinner portion than the other flat portion.
또, 본 발명의 제2의 개스킷의 제조방법은, 적어도 1장의 플레이트를, 경질의 금속판으로 이루어진 모재의 한쪽 면 또는 양 면에, 상기 모재보다 연질의 비금속층을 피복해서 이루어진 합성재로 구성하고, 상기 합성재로 이루어진 플레이트에 있어서의 상기 구멍의 가장자리부의 연질의 비금속층에 두께가 얇은 부분을 형성한 후, 상기 두께가 얇은 부분을 접는 것에 의해 다른 평탄부보다 두꺼운 밀봉부를 형성하는 것을 특징으로 하는 것이다.Moreover, the manufacturing method of the 2nd gasket of this invention consists of a composite material which consists of at least 1 plate which coat | covers the nonmetallic layer softer than the said base material on one side or both surfaces of the base material which consists of a hard metal plate, And forming a thin portion in the soft nonmetallic layer of the edge portion of the hole in the plate made of the composite material, and then forming a sealing portion thicker than the other flat portions by folding the thin portion. It is.
상기 제1 및 제2의 개스킷의 제조방법에 있어서는, 두께가 얇은 부분을 가압성형함으로써 형성할 수 있다.In the manufacturing method of the said 1st and 2nd gasket, it can form by press-molding the thin part.
상기 구성을 갖는 본 발명의 제조방법은, 클래드 강판으로 이루어진 플레이트에 있어서의 연질의 금속층, 또는 합성재로 이루어진 플레이트에 있어서의 연질의 비금속층에 두께가 얇은 부분을 형성한 후, 상기 두께가 얇은 부분을 접는 것에의해 다른 평탄부보다 두꺼운 밀봉부를 형성하도록 하고 있으므로, 플레이트의 두께조정 등의 가공이 간단할 뿐만 아니라, 내부응력의 잔류에 따른 휘어짐이 발생하지 않고, 따라서, 밀봉부 두께의 적당화에 따른 면압조정을 쉽게 행할 수 있고, 결과적으로, 확실한 밀봉효과를 얻을 수 있는 개스킷을 저렴하게 제조할 수 있다.In the manufacturing method of this invention which has the said structure, after forming a thin part in the soft metal layer in the plate which consists of a clad steel plate, or the soft nonmetal layer in the plate which consists of synthetic materials, the said thickness is thin By folding the part, it is possible to form a sealing part thicker than other flat parts, so that processing such as adjusting the thickness of the plate is not only simple, but also bending due to residual stress does not occur, and hence the thickness of the sealing part is appropriate. Can be easily adjusted, and as a result, it is possible to manufacture a gasket at a low cost which can achieve a reliable sealing effect.
도 1은, 본 발명에 근거해서 제조된 개스킷의 부분 파단 평면도이다.1 is a partially broken plan view of a gasket manufactured according to the present invention.
도 2는, 금속판에 코이닝에 의해 두께가 얇은 부분을 형성한 상태를 설명한 단면도이다.2 is a cross-sectional view illustrating a state in which a thin portion is formed on a metal plate by coining.
도 3은, 도 1의 A-A의 확대 단면도이다.3 is an enlarged cross-sectional view of A-A of FIG. 1.
도 4는, 도 2와 동일한 위치에서의 단면도이다.4 is a cross-sectional view at the same position as in FIG. 2.
도 5는, 상기 개스킷의 다른 구성의 실시예를 나타낸 도 3과 동일한 위치에서의 확대 단면도이다.5 is an enlarged cross-sectional view at the same position as in FIG. 3 showing an embodiment of another configuration of the gasket.
*도면의 주요부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *
2…플레이트 2a…모재(母材)2… Plate 2a... Base material
2b…금속층 6…두께가 얇은 부분2b... Metal layer 6.. Thin section
8…밀봉부8… Seal
이하에, 본 발명의 실시예를 도면에 근거해서 상세하게 설명한다. 도 1 내지 도 3은, 본 발명을, 내연기관의 실린더 블록과 실린더 헤드와의 사이에 장착된, 1장의 금속제 플레이트(2)로 이루어진 실린더 헤드 개스킷의 제조에 적용한 경우의 실시예를 나타내고 있다.EMBODIMENT OF THE INVENTION Below, the Example of this invention is described in detail based on drawing. 1 to 3 show an example in which the present invention is applied to the production of a cylinder head gasket composed of one metal plate 2 mounted between a cylinder block and a cylinder head of an internal combustion engine.
이 실린더 헤드 개스킷은, 플레이트(2)의 적당한 위치에 실린더 블록의 연소실에 대응하는 복수의 연소실구멍(4)외에, 상기 연소실구멍(4) 주위에 분산해서 필요한 만큼의 물구멍 및 오일구멍 등을 구비하고, 또한, 연소실구멍(4) 주위에 대략 균등하게 설치된 볼트구멍을 구비하고 있다.The cylinder head gasket has a plurality of combustion chamber holes 4 corresponding to the combustion chamber of the cylinder block at appropriate positions of the plate 2, and includes as many water holes and oil holes as necessary to be distributed around the combustion chamber holes 4 as necessary. And a bolt hole that is provided substantially evenly around the combustion chamber hole 4.
상기 개스킷을 구성하는 플레이트(2)는, 도 2에 상세하게 나타내듯이, 스테인레스 등의 경질의 금속판으로 이루어진 모재(2a)의 한쪽 면에, 상기 모재(2a)보다 연질의 알루미늄, 구리, 혹은 아연 등의 금속층(2b)을 피복해서 이루어진 클래드 강판으로 구성되어 있고, 이 피복한 연질의 금속층(2b)에 코이닝에 의해 두께가 얇은 부분(6)을 형성한 후, 상기 두께가 얇은 부분(6)을 도 3에 나타내듯이 상기 금속층(2b)으로 접는 것에 의해, 상기 플레이트(2)의 다른 평탄부보다 약간 두꺼운 밀봉부(8)를 형성해서, 이 부분에 조임부착시의 면압을 집중시키도록 하고 있다.이 두께가 얇은 부분(6)은, 상기 두께가 얇은 부분(6)을 접는 것에 의해 형성되는 밀봉부(8)의 전체적인 두께를 조정하기 위한 것으로, 두께가 얇게 된 부위의 두께와, 상기 부위에 있어서의 코이닝가공의 깊이와의 차만큼, 상기 밀봉부(8)가, 플레이트(2)의 다른 평탄부보다 두껍게 형성되게 된다.As shown in detail in FIG. 2, the plate 2 constituting the gasket has aluminum, copper, or zinc softer than the base material 2a on one surface of the base material 2a made of a hard metal plate such as stainless steel. It consists of the clad steel plate which coat | covered the metal layer 2b, such as etc., After forming the thin part 6 by coining on this coated soft metal layer 2b, the said thin part 6 ) By folding the metal layer 2b into the metal layer 2b to form a sealing portion 8 which is slightly thicker than the other flat portions of the plate 2, so as to concentrate the surface pressure at the time of fastening. The thin portion 6 is for adjusting the overall thickness of the sealing portion 8 formed by folding the thin portion 6, and the thickness of the thinned portion, Coining at the site As the difference between the depth of the sealing portion (8), it is formed to be thicker than the other flat portion of the plate (2).
상기 구성을 갖는 개스킷은, 상기 클래드 강판으로 이루어진 플레이트(2)에 있어서의 연질의 금속층(2b)에 코이닝을 행함으로써 두께가 얇은 부분(6)을 형성하고 있으므로, 플레이트(2)의 두께조정 등의 가공이 간단할 뿐만 아니라, 내부응력의 잔류에 따른 휘어짐이 발생하지 않고, 따라서, 밀봉부(8) 두께의 적당화에 의한 면압조정을 간단하게 행할 수 있어, 결과적으로 상기 개스킷을 저렴하게 제조할 수 있고, 게다가 확실한 밀봉효과를 얻을 수 있다.The gasket having the above structure forms a thin portion 6 by coining the soft metal layer 2b in the plate 2 made of the clad steel sheet, so that the thickness of the plate 2 is adjusted. Not only is the processing simple, but the warpage does not occur due to the residual stress, and thus, the surface pressure adjustment can be easily performed by appropriately adjusting the thickness of the sealing portion 8, and as a result, the gasket can be made inexpensively. It can manufacture, and also the reliable sealing effect can be acquired.
여기서, 상술한 실시예에 있어서는, 클래드강판으로 이루어진 플레이트(2)를, 연질의 금속판으로 이루어진 모재(2a)의 한쪽 면에 연질의 금속층(2b)을 피복하고, 그 연질의 금속층(2b)측에 코이닝가공을 실시해서 두께가 얇은 부분(6)을 형성한 구성으로 하고 있지만, 이것에 한정되지 않고, 도 4에 나타내듯이, 모재(2a)의 양 면에 연질의 금속층(2b)을 피복한 클래드 강판을 이용해서, 그 양 면에 코이닝가공을 행함으로써 표리 양 면에 두께가 얇은 부분(6)을 형성하여, 그 두께가 얇은 부분을 도 5에 나타내듯이 접은 구성으로 할 수 있다.Here, in the above embodiment, the plate 2 made of the clad steel sheet is covered with the soft metal layer 2b on one side of the base material 2a made of the soft metal plate, and the soft metal layer 2b side thereof. Coining is performed to form a thin portion 6, but the configuration is not limited to this. As shown in Fig. 4, the soft metal layer 2b is coated on both sides of the base material 2a. By using a clad steel sheet, coining is applied to both surfaces to form thin portions 6 on both front and back surfaces, and the thin portions can be folded as shown in FIG.
또, 본 발명을 기초로 해서 제조된 개스킷은, 상기 플레이트가 1장인 것에 한정되지 않고, 적층한 여러개의 플레이트 중 적어도 1장을 상기 클래드 강판에 의해 형성한 것으로 할 수 있고, 필요에 따라 어느 하나의 플레이트에 비드를 설치할수도 있다.The gasket manufactured on the basis of the present invention is not limited to one plate, and at least one of the laminated plates may be formed of the clad steel sheet. Beads can also be placed on the plate.
그리고, 상기 실시예에서는, 밀봉부를 두께가 얇은 부분(6)의 범위내에서 접은 경우를 나타내고 있지만, 상기 두께가 얇은 부분(6)을 플레이트에 있어서의 코이닝가공을 행하지 않은 부분으로 접을 수도 있다.Incidentally, in the above embodiment, the sealing portion is folded in the range of the thin portion 6, but the thin portion 6 may be folded into a portion which is not subjected to coining processing on the plate. .
상술한 실시예에 있어서는, 플레이트(2)를 클래드 강판으로 구성하고, 상기 클래드 강판으로 이루어진 플레이트(2)의 가장자리부에 있어서의 연질의 금속층(2b)에, 코이닝에 의해 두께가 얇은 부분(6)을 형성함과 함께, 그 두께가 얇은 부분(6)을 접음으로써 밀봉부(8)를 설치한 것으로 하고 있지만, 이것에 한정되지 않고, 상기 플레이트를, 경질의 금속판으로 이루어진 모재에, 상기 모재보다 연질의 카본 등의 비금속층을 피복해서 이루어진 합성재로 구성하여, 그 합성재로 이루어진 플레이트의 가장자리부에서의 연질의 비금속층에, 가압성형에 의해 두께가 얇은 부분을 형성함과 함께, 그 두께가 얇은 부분을 접는 것에 의해 밀봉부를 설치한 구성으로 할 수도 있다.In the above-described embodiment, the plate 2 is composed of a clad steel sheet, and the thin metal layer 2b at the edge of the plate 2 made of the clad steel sheet is thinned by coining ( 6) and the sealing part 8 was provided by folding the thin part 6 in thickness, but it is not limited to this, The said plate is attached to the base material which consists of a hard metal plate, It is composed of a composite material formed by coating a non-metal layer such as carbon softer than the base material, and forms a thin portion by press molding on the soft non-metal layer at the edge portion of the plate made of the composite material. It can also be set as the structure which provided the sealing part by folding the thin part.
이상으로 상술한 바와 같이, 본 발명의 개스킷의 제조방법은, 클래드 강판으로 이루어진 플레이트에 있어서의 연질의 금속층, 또는 합성재로 이루어진 플레이트에 있어서의 연질의 비금속층에 두께가 얇은 부분을 형성한 후, 상기 두께가 얇은 부분을 접음으로써 다른 평탄부보다 두꺼운 밀봉부를 형성하므로, 플레이트의 두께조정 등의 가공이 간단할 뿐만 아니라, 내부응력의 잔류에 의한 휘어짐이 생기지 않고, 따라서, 밀봉부의 두께의 적당화에 의한 면압조정을 용이하게 행할 수 있고, 게다가, 상기 두께가 얇은 부분을 형성한 후, 상기 두께가 얇은 부분을 접는 것에 의해 다른 평탄부보다 두꺼운 밀봉부를 형성하고, 이들 두께가 얇은 부분의 형성 및 접는 가공을 개별적으로 행하기 때문에, 이들 각 가공이 간단하고, 결과적으로, 밀봉부 두께의 정밀도를 높혀 확실한 밀봉효과를 얻을 수 있는 개스킷을 저렴하게 제조할 수 있다.As described above, in the method of manufacturing the gasket of the present invention, the thin metal layer in the plate made of the clad steel sheet or the soft nonmetal layer in the plate made of the composite material forms a thin portion. By folding the thin part, the sealing part is formed thicker than other flat parts, so that the processing such as adjusting the thickness of the plate is not only simple, but also the bending due to the residual of internal stress does not occur, and hence the thickness of the sealing part is appropriate. Surface pressure adjustment by sizing can be easily performed, and furthermore, after forming the thin portion, the sealing portion thicker than the other flat portion is formed by folding the thin portion, thereby forming the thin portion. And folding processing, respectively, so that each of these processing is simple, and consequently, High-density gaskets can be manufactured at low cost, which ensures a tight sealing effect.
Claims (4)