KR100231360B1 - Composite form panel - Google Patents

Composite form panel Download PDF

Info

Publication number
KR100231360B1
KR100231360B1 KR1019970042257A KR19970042257A KR100231360B1 KR 100231360 B1 KR100231360 B1 KR 100231360B1 KR 1019970042257 A KR1019970042257 A KR 1019970042257A KR 19970042257 A KR19970042257 A KR 19970042257A KR 100231360 B1 KR100231360 B1 KR 100231360B1
Authority
KR
South Korea
Prior art keywords
board
sides
polyethylene
particle board
formwork panel
Prior art date
Application number
KR1019970042257A
Other languages
Korean (ko)
Other versions
KR19990018966A (en
Inventor
변무원
Original Assignee
변무원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 변무원 filed Critical 변무원
Priority to KR1019970042257A priority Critical patent/KR100231360B1/en
Publication of KR19990018966A publication Critical patent/KR19990018966A/en
Application granted granted Critical
Publication of KR100231360B1 publication Critical patent/KR100231360B1/en

Abstract

본발명은 굴곡단면을 가지는 파티클보드와 평평한 폴리에틸렌보드를 일체로서 접착하여서 내부에 중공부가 형성되는 안정적인 단면구조로서 경량화된 복합거푸집 패널에 관한 것으로, 본 발명의 기술적 구성상의 특징은 나무톱밥을 압축 성형하여서 요철파형(11)이 폭방향으로 반복 형성되는 파티클보드(10)와, 상기 파티클보드(10)양면에 맞대어지도록 배치되며 폴리에틸렌으로서 평활하게 성형된 표면에 섬유직포(a)를 각기 매립하여서 된 양측의 폴리에틸렌보드(20)들과, 상기 파티클보드(10)와 양측의 폴리에틸렌보드(20)사이에 도포되는 접착제로서 형성되는 접착층(30)으로 구성하여서, 상기 파티클보드(10)와 일체로서 접착되는 양측의 폴리에틸렌보드(20)들 사이의 내부에 중공부(1a)들이 형성되도록 한 것이다.The present invention relates to a lightweight composite formwork panel with a stable cross-sectional structure in which a hollow part is formed by bonding a particle board having a curved cross section and a flat polyethylene board as a single body, and a technical feature of the present invention is compression molding of wood sawdust. Thus, the irregular board 11 is repeatedly formed in the width direction and the particle board 10 is disposed so as to be opposed to both sides of the particle board 10 and is formed by embedding the fiber woven fabric (a) on the surface smoothly formed as polyethylene, respectively. It is composed of an adhesive layer 30 formed as an adhesive applied between the polyethylene boards 20 on both sides and the particle board 10 and the polyethylene board 20 on both sides, thereby adhering integrally with the particle board 10. Hollow parts 1a are formed in the interior between the polyethylene boards 20 on both sides.

Description

복합거푸집 패널Composite formwork panel

본발명은 각종의 건축공사에 사용되는 복합거푸집 패널에 관한 것으로, 특히 굴곡단면을 가지는 파티클보드와 평평한 폴리에틸렌보드를 일체로서 접착하여서 내부에 중공부가 형성되는 안정적인 단면구조로서 경량화된 복합거푸집 패널에 관한 것이다.The present invention relates to a composite formwork panel used in a variety of construction work, and more particularly to a lightweight composite formwork panel with a stable cross-sectional structure in which a hollow portion is formed by bonding the particle board having a curved cross section and a flat polyethylene board as a whole. will be.

일반적으로 건축공사용으로 사용되는 복합거푸집 패널은 재질적인 특성이 서로 다른 이질의 부재들을 접합 형성하여서, 그 이질의 부재들이 상호보완작용으로 하중에 대한 감당능력과 내구성 향상시켜주는 등의 실용적인 가치가 있는 것으로 알려져 있다.In general, the composite formwork panel used for building construction has the practical value of joining and forming heterogeneous members with different material properties, and improving the ability to handle loads and durability through complementary actions. It is known.

상기한 바와 같은 복합거푸집 패널중의 하나는, 나무박판을 여러겹으로 적층하여서 성형된 합판과, 폴리에틸렌을 소재로하여 압출 성형된 폴리에틸렌보드 상호간을 나사못, 리벳 등의 고정수단으로 적절한 위치마다 결착 고정시키서 제작되었다.One of the composite formwork panels as described above is fixed by binding means such as screws, rivets and the like between the plywood formed by stacking multiple layers of wood and the polyethylene board extruded from polyethylene. Was made.

따라서, 이러한 복합거푸집 패널은 재질적인 특성이 다른 이질의 합판과 폴리에틸렌보드를 고정수단들로서 견고하게 접합 고정시켜서 제작됨으로써, 외적인 하중이나 충격에 대응하여 견고하면서도 타설되는 콘크리트의 하중에 대응하는 하중감당 능력과 표면 박리성이 우수한 장점을 가지는 것이 사실이다.Therefore, the composite formwork panel is manufactured by firmly bonding and fixing heterogeneous plywood and polyethylene boards having different material properties as fastening means, so that it can handle loads corresponding to the load of concrete that is solid while being installed in response to external loads or impacts. It is true that it has the advantage of excellent surface peelability.

그러나, 이와 같은 종래의 복합거푸집 패널은 몇가지 현실적인 문제점들을 수반하게 되었다.However, such conventional composite formwork panels have come with some practical problems.

즉, 첫째는 이질의 합판과 폴리에틸렌보드를 고정수단으로서 일일히 고정시켜야 하는 제작상의 번거로움과 함께, 반복사용시 폴리에틸렌 외표면에 노출된 고정수단이 마모되거나 손상되는 문제점이 있었으며, 둘째는 단위무게가 중량인 합판이 폴리에틸렌보드로서 감싸져서 내부가 빈틈없이 채워진 형태의 단면구조를 이루게 됨으로써, 제작된 복합거푸집 패널 전체의 무게 부담을 가중시켜서 중량화되는 문제점이 있었으며, 셋째는 동일한 치수의 규격품증 상대적으로 고가인 합판을 사용하게 됨으로써, 복합거푸집 패널의 제작원가를 상승시켜서 결과적으로 경제성을 상실하게 되는 등의 문제점이 있었다.That is, firstly, there is a problem in that it is necessary to fix heterogeneous plywood and polyethylene board as fixing means, and the fixing means exposed to the outer surface of polyethylene is worn or damaged during repeated use. The plywood, which is heavy, is wrapped as a polyethylene board to form a cross-sectional structure in which the interior is filled with gaps, thereby increasing the weight burden of the entire composite formwork panel, which is weighted. By using expensive plywood, there is a problem such as to increase the manufacturing cost of the composite formwork panel, resulting in loss of economical efficiency.

본발명의 목적은 굴곡단면을 가지는 파티클보드 양측에 섬유직포를 매개로 하여 접착되는 폴리에틸렌보드로서 내부에 중공부가 형성되도록 구성하여서, 첫째 이질의 부재를 접착제로서 견고하게 접착하여서 하중감당능력이 향상된 안정적인 단면구조를 부여하여 고품질의 제품을 제공하여 주며, 둘째 상대적으로 가벼운 부재로서 내부에 중공부를 가지도록 하여서 단위중량이 대폭적으로 감축된 경량의 제품을 제공하여 주며, 셋째 내부에 형성된 중공구들로서 원재료를 대폭으로 절감시켜서 보다 저렴한 제품을 제공하여 주는 데에 있다.The purpose of the present invention is a polyethylene board bonded to both sides of the fiber board having a curved cross-section is configured to form a hollow inside the hollow, so that the first heterogeneous member firmly bonded as an adhesive to improve the load carrying capacity stable It provides a high-quality product by providing a cross-sectional structure. Second, it provides a lightweight product with a significant reduction in unit weight by having a hollow part inside as a relatively light member, and thirdly, using raw materials as hollow spheres formed therein. It is to provide a cheaper product by drastically reducing.

제1도는 본발명 복합거푸집 패널의 사시도.1 is a perspective view of the composite formwork panel of the present invention.

제2도는 본발명 복합거푸집 패널의 정단면도.2 is a front sectional view of the composite formwork panel of the present invention.

제3도는 본발명 복합거푸집 패널의 요부발췌 단면도.3 is a cross-sectional view of the main portion of the composite formwork panel of the present invention.

제4도는 본발명 폴리에틸렌보드를 예시한 일부분 사시도.Figure 4 is a partial perspective view illustrating the present invention polyethylene board.

제5a도는 본발명 파티클보드의 변형예를 나타낸 일부분 사시도.Figure 5a is a partial perspective view showing a modification of the particleboard of the present invention.

제5b도는 제5a도의 A-A선 단면도.FIG. 5B is a cross-sectional view taken along the line A-A of FIG. 5A.

제6a도는 본발명 다른실시예의 복합거푸집 패널을 나타낸 사시도.Figure 6a is a perspective view of a composite formwork panel of another embodiment of the present invention.

제6b도는 제5a도의 정단면도.FIG. 6B is a sectional front view of FIG. 5A.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

1 : 복합거푸집 패널 1a : 중공부1: composite formwork panel 1a: hollow part

10 : 파티클보드 11 : 요철파형10: Particle board 11: Uneven waveform

20 : 폴리에틸렌보드 a : 섬유직포20: polyethylene board a: textile fabric

30 : 접착층30: adhesive layer

본발명의 복합거푸집 패널(1)은 제1도 내지 제3도에 도시되는 바와 같이, 나무톱밥을 압축 성형하여서 요철파형(11)이 폭방향으로 반복 형성되는 파티클보드(10)와, 상기 파티클보드(10)양면에 맞대어지도록 배치되며 폴리에틸렌으로서 평활하게 성형된 표면에 섬유직포(a)를 각기 매립하여서 된 양측의 폴리에틸렌보드(20)들과, 상기 파티클보드(10)와 양측의 폴리에틸렌보드(20)사이에 도포되는 접착제로서 형성되는 접착층(30)으로 구성하여서, 상기 파티클보드(10)와 일체로서 접착되는 양측의 폴리에틸렌보드(20)들 사이의 내부에 중공부(1a)들이 형성되도록 함을 기술적 구성상의 특징으로 한다.The composite formwork panel 1 of the present invention, as shown in Figures 1 to 3, the particle board 10, the irregular board 11 is formed repeatedly in the width direction by compression-molding wood sawdust, and the particles The boards 10 are arranged to face each other, and the polyethylene boards 20 on both sides of the fabric woven fabric a are embedded in the surface smoothly formed as polyethylene, and the particle board 10 and the polyethylene boards on both sides ( 20, the hollow layer 1a is formed between the polyethylene boards 20 on both sides which are integrally bonded to the particle board 10 by forming an adhesive layer 30 formed as an adhesive applied therebetween. It is characterized by the technical configuration.

이와 같이 구성되는 본발명의 복합거푸집 패널(1)은 요철파형(11)들이 형성되는 파티클보드(10)와 섬유직포(a)를 표면에 매립하여서 된 양측의 폴리에틸렌보드(20)들 상호간이, 그 섬유직포(a)를 매개로하여서 도포되는 접착제가 견고하면서도 치밀하게 형성되는 접착층(30)을 통하여 접착됨으로써, 일차적으로는 재질적인 특성이 다른 이질의 부재 상호간이 접착제에 의하여 견고한 접합을 가능하게 하여서 간편, 용이하게 제작할 수 있는 장점을 가지게 되는것이다.The composite formwork panel 1 of the present invention configured as described above is mutually interposed between the polyethylene boards 20 on both sides formed by embedding the particle board 10 and the fiber woven fabric a on which the uneven wave shapes 11 are formed. Since the adhesive applied through the textile fabric (a) is adhered through the adhesive layer 30 which is firmly and precisely formed, the adhesive between the members of the heterogeneous members having different material properties may be solidly bonded. It will have the advantage of being easy and easy to manufacture.

특히, 요철파형(11)들이 형성된 파티클보드(10)와 일체로 접착된 양측의 폴리에틸렌보드(20)들 사이의 내부에 형성된 중공부(1a)들로서 작용되는 휨응력이나 콘크리트 하중에 효과적으로 대응할 수 있는 중공단면를 가지게 됨으로써, 원재료의 사용량을 대폭적으로 감축히켜서 제작원가를 대폭적으로 절감하여 주면서도, 원재료의 사용량에 비하여 콘크리트 하중감당능력이 향상된 복합거푸집 패널(1)을 얻을 수 있게 되는 것이다.In particular, the hollow that can effectively cope with the bending stress or concrete load acting as the hollow portion (1a) formed between the polyethylene board 20 of the two sides integrally bonded to the particle board 10 having the uneven wave shape 11 is formed By having a cross-section, it is possible to obtain a composite formwork panel (1) with improved concrete load-bearing capacity compared to the amount of raw materials, while significantly reducing the production cost by significantly reducing the amount of raw materials used.

상기 파티클보드(10)는 나무톱밥을 성형틀로서 압축 성형하여서 폭방향으로 반복되는 사각형상의 요철파형(11)들이 길이방향으로서 길게 형성하여서 된다. 따라서, 이러한 파티클보드(10)는 그 요철파형(11)들로서 제작되어지는 복합거푸집 패널(1)의 경량화 및 내부에 중공부(1a)가 형성되는 안정적인 단면구조를 부여하여주는 직접적인 기능을 가지게 된다.The particle board 10 is formed by elongating the rectangular concave-convex waveforms 11 which are repeated in the width direction by compression-molding wood sawdust as a mold. Therefore, the particle board 10 has a direct function of giving a stable cross-sectional structure in which the hollow form 1a is formed and the weight of the composite formwork panel 1 manufactured as the uneven waveforms 11 is formed therein. .

상기 폴리에틸렌보드(20)은 제4도에서와 같이, 압출 성형시에 표면에 섬유직포(a)가 매립되도록 성형하여서 만들어지게 된다. 이와 같이 폴리에틸렌보드(20)표면에 매립되는 섬유직포(a)는 일정한 크기의 간극을 두고 종횡으로 엮어서 망체형상으로 직조되도록 함이 중요하다. 그 이유는, 상기 섬유직포(a)가 폴리에틸렌보드(20)표면 내부에 뿌리깊게 박혀져서 표출되게 매립되도록 하면서도, 도포되는 접착제가 침투되어서 채워지면서 견고하면서도 치밀한 접착층(30)을 이루도록 하기 위함이다.The polyethylene board 20 is made by molding so that the fiber woven fabric (a) is embedded in the surface during extrusion molding as shown in FIG. As such, it is important that the fiber woven fabric (a) embedded in the surface of the polyethylene board 20 is woven in a network shape by weaving vertically and horizontally with a gap of a predetermined size. The reason is that the fiber fabric (a) is embedded in the surface of the polyethylene board 20 so as to be embedded to be exposed, while the applied adhesive is penetrated and filled to form a solid yet dense adhesive layer 30.

또한, 상기 섬유직포(a)는 인장력과 흡습성이 양호한 마닐라 삼, 삼베, 면등을 심재로하여서 제사된 식물성 섬유사로서 직조하여서 될 수도 있으며, 필요에 따라서는 유리섬유를 심재로하여 제사된 광물성 섬유사로서 직조하여서 될 수도 있음을 밝혀 둔다.In addition, the fiber woven fabric (a) may be woven as a vegetable fiber yarn manufactured using manila hemp, burlap, cotton, etc. having good tensile strength and hygroscopicity as a core material, and if necessary, mineral fiber manufactured using glass fiber as a core material It may be possible to weave it as a yarn.

상기 접착층(30)은 파티클보드(10)과 양측의 폴리에틸렌보드(20)들 각각의 섬유직포(a)에 도포되는 접착제로서 형성된다. 이때, 접착층(30)은 도포되는 접착제가 상기 파티클보드(10)를 이루는 요철파형(11)들의 접합부위 외표면과, 폴리에틸렌보드(20)표면의 섬유직포(a)내부에 모세관현상으로 깊숙히 침투되면서 채워지게 됨으로써, 이질의 파니클보드(10)와 양측의 폴리에틸렌보드(20)들 상호간의 부착력을 획기적으로 증대시켜주게 것이다.The adhesive layer 30 is formed as an adhesive applied to the fiber board (a) of each of the particle board 10 and the polyethylene boards 20 on both sides. At this time, the adhesive layer 30 penetrates deeply into the outer surface of the joint portions of the uneven waveforms 11 forming the particle board 10 and the capillary phenomenon inside the fiber woven fabric a of the polyethylene board 20 surface. By being filled while being, it will significantly increase the adhesion between the foreign board 10 and the polyethylene board 20 of both sides.

여기에서, 상기 접착층(30)은 일반적인 접착제나 폴리우레탄, 에폭시 또는 폴리에스테르계열의 접착제가 사용될 수 있다.Here, the adhesive layer 30 may be a general adhesive or a polyurethane, epoxy or polyester-based adhesive.

그리고, 본발명의 실시예에서 파티클보드(10)는 나무톱밥을 성형틀로서 압축 성형하여서 폭방향으로 반복되는 사각형상의 요철파형(11)들이 길이방향으로서 길게 형성하여서 된 것으로 예시되어 있으나, 상기 파티클보드(10)는 제5a도 및 제5b도에 예시된 변형예에서와 같이, 나무톱밥을 성형틀로서 압축하여서 평평하게 성형된 양면에서 내부를 향하여 교효로서 반복되게 요입형성되는 다수개의 요입홈(11a)들을 가지도록 하여서 단면상 요철파형(11)을 이루도록 형성할 수도 있음을 밝혀 둔다.In addition, in the embodiment of the present invention, the particle board 10 is exemplified by forming the sawtooth irregular waveforms 11 repeated in the width direction by compression molding the wood sawdust as a molding frame in the longitudinal direction, but the particles The board 10 has a plurality of recess grooves which are repeatedly recessed and formed alternately inwardly from both flatly molded surfaces by compressing wood sawdust as a molding frame, as in the modification illustrated in FIGS. 5A and 5B. 11a) to be formed to have a concave-convex waveform 11 in cross section.

한편, 제6a도 및 제6b도는 본발명의 다른실시예를 나타낸 것으로, 상기 파티클보드(10)과 접착된 양측의 폴리에틸렌보드(20)사이의 내부에 형성된 중공부(1a)를 포함한 사방의 테두리를 접착제로서 도포하여서 외부와 차단되도록 피막층(40)을 형성하여서 된 것이다.On the other hand, Figures 6a and 6b shows another embodiment of the present invention, the four sides including a hollow portion (1a) formed between the particle board 10 and the polyethylene board 20 of both sides bonded to the four sides By coating with an adhesive to form a coating layer 40 to be blocked from the outside.

따라서, 이는 내부에 형성된 중공부(1a)를 포함한 사방의 테두리를 통하여 파티클보드(10)내부로 물이 침투되어 내구성을 저하시키는 것을 방지하여 주는 잇점을 기대할 수 있게 되는 것이다.Therefore, this can be expected to benefit from preventing water from penetrating the inside of the particle board 10 through the four sides including the hollow portion (1a) formed therein to reduce the durability.

이와 같이 구성되고 실시되는 본발명은 굴곡단면을 가지는 파티클보드 양측에 섬유직포를 매개로하여 접착되는 폴리에틸렌보드로서 내부에 중공부가 형성되도록 함으로써, 첫째, 이질의 부재 상호간을 접착제로서 접착하여서 간편, 용이하게 제작할 수 있도록 하여주며, 둘째, 구조적으로 안정된 중공단면을 가지도록 하여서 작용되는 휨응력이나 콘크리트 하중에 대응하는 하중감당능력을 향상시켜주며, 셋째, 내부에 형성되는 중공부들로서 원재료의 사용량을 대폭적으로 감축시켜서 제작원가의 절감과 경량화를 동시에 실현시켜주는 등의 효과를 가지게 되는 것이다.The present invention constructed and carried out as described above is a polyethylene board which is bonded to both sides of a particle board having a curved cross section through a fiber woven fabric so that a hollow part is formed therein. Second, it has a structurally stable hollow section to improve the load-bearing capacity corresponding to the bending stress or concrete load applied, and third, the use of raw materials significantly as hollow parts formed inside It will reduce the manufacturing cost and reduce the weight at the same time.

Claims (3)

나무톱밥을 압축 성형하여서 요철파형(11)들이 폭방향으로 반복 형성되는 파티클보드(10)와, 상기 파티클보드(10)양면에 맞대어지도록 배치되며 폴리에틸렌으로서 평활하게 성형된 표면에 섬유직포(a)를 각기 매립하여서 된 양측의 폴리에틸렌보드(20)들과, 상기 파티클보드(10)와 양측의 폴리에틸렌보드(20)사이에 도포되는 접착제로서 형성되는 접착층(30)으로 구성하여서, 상기 파티클보드(10)와 일체로서 접착되는 양측의 폴리에틸렌보드(20)들 사이의 내부에 중공부(1a)들이 형성되도록 함을 특징으로 하는 복합거푸집 패널.Particle board 10, which is formed by repeatedly compressing wood sawdust and having irregularities 11 formed in the width direction, and is arranged to face both sides of the particle board 10, and is formed on a surface smoothly formed as polyethylene (a) It consists of the polyethylene board (20) on both sides of the buried, and the adhesive layer (30) formed as an adhesive applied between the particle board (10) and the polyethylene board (20) on both sides, the particle board (10) Composite die panel, characterized in that the hollow portion (1a) is formed between the polyethylene board 20 of both sides to be bonded as a unit. 제1항에 있어서, 상기 파티클보드(10)는 나무톱밥을 성형틀로서 압축하여서 평평하게 성형된 양면에서 내부를 향하여 교효로서 반복되게 요입형성되는 다수개의 요입홈(11a)들을 가지도록 하여서 단면상 요철파형(11)을 이루도록 형성함을 특징으로 하는 복합거푸집 패널.The method of claim 1, wherein the particle board 10 has a plurality of concave-convex grooves (11a) is formed by repeatedly compressing the wood sawdust as a molding frame toward the inside from the flat molded both sides to be indented repeatedly Composite formwork panel, characterized in that formed to form a wave (11). 제1항에 있어서, 강기 파티클보드(10)과 접착된 양측의 폴리에틸렌보드(20)사이의 내부에 형성된 중공부(1a)를 포함한 사방의 테두리를 접착제로서 도포하여서 외부와 차단되도록 피막층(40)을 형성하여서 됨을 특징으로 하는 복합거푸집 패널.The film layer (40) according to claim 1, wherein the film layer (40) is coated with an edge of the four sides including the hollow portion (1a) formed between the rigid particle board (10) and the polyethylene board (20) of both sides bonded with an adhesive. Composite formwork panel, characterized in that by forming a.
KR1019970042257A 1997-08-28 1997-08-28 Composite form panel KR100231360B1 (en)