KR100190598B1 - Sealed decorative panels of a flower and method for producing thereof - Google Patents
Sealed decorative panels of a flower and method for producing thereof Download PDFInfo
- Publication number
- KR100190598B1 KR100190598B1 KR1019910020608A KR910020608A KR100190598B1 KR 100190598 B1 KR100190598 B1 KR 100190598B1 KR 1019910020608 A KR1019910020608 A KR 1019910020608A KR 910020608 A KR910020608 A KR 910020608A KR 100190598 B1 KR100190598 B1 KR 100190598B1
- Authority
- KR
- South Korea
- Prior art keywords
- film
- low melting
- dry
- melting point
- point film
- Prior art date
Abstract
건조압화를 장기간에 걸쳐 변색이나 퇴색 없이 우미성을 유지시키기 위하여 건조압화를 거의 절건상태이고 또한 공기나 수분이 없는 상태에서 저융점 필름으로 완전 밀봉하고 있는 건조압화 밀봉장식품이다.Dry pressurization is a dry pressurized hermetic food which is completely sealed with a low melting point film in a state in which dry pressurization is almost dry in the absence of air or moisture in order to maintain aesthetics without discoloration or fading over a long period of time.
건조압화는 거의 절건상태이고 또한 공기나 수분이 없는 상태에서 저융점 필름으로 완전 밀봉되며, 또한 기재에 고착되어 있고, 필요에 따라 저융점 필름으로 완전 밀봉되며, 또한 기재에 고착되어 있고, 필요에 따라 저융점 필름 외측에 커버필름이 고착되어 있으며, 필요에 따라 다시 최우층은 피복수지로 피복되어 있는 건조압화 밀봉작식품이다.The dry press is almost completely abraded and completely sealed with a low melting film in the absence of air or moisture, and is also fixed to the substrate, if necessary, completely sealed with a low melting film, and also adhered to the substrate, Accordingly, the cover film is fixed to the outside of the low melting point film, and if necessary, the uppermost layer is a dry pressurized sealed crop which is coated with a coating resin.
이 건조압화 밀봉장식품을 얻기 위하여 건조압화를 저융점 필름으로 밀봉할 때, 감압분위기에 내맡겨지고, 감압분위기 상태에서 저융점 필름을 건조압화에 가압하여 저융점 필름을 용융하는 것이며, 필요에 따라 저융점 필름을 기재 및/ 또는 커버필름과 겹쳐서 가압가열 처리하는 건조압화 밀봉장식품의 제조법이다.When the dry pressurization is sealed with a low melting point film in order to obtain this dry pressurized sealing decoration, it is entrusted to a low pressure atmosphere, and a low melting point film is pressurized by dry pressurization in a reduced pressure atmosphere to melt a low melting point film as needed. It is a manufacturing method of a dry pressurized sealing decoration which pressurizes and heats a low melting film with a base material and / or a cover film.
Description
제1도는 본발명에 관한 건조압화 밀봉장식품의 일부를 절단한 사면도,1 is a perspective view of a part of a dry pressurized sealing ornament according to the present invention;
제2도는 제1도와는 다른 실시 태양에 있어서의 본발명의 건조압화 장식품의 일부를 절단한 사시도,2 is a perspective view of a part of the dry press ornament of the present invention in an embodiment different from the first embodiment,
제3도는 제1도 및 제2도와는 다른 실시 태양에 있어서의 본발명의 건조압화 장식품의 일부를 절단한 사시도.3 is a perspective view of a part of the dry press ornament of the present invention in an embodiment different from FIGS. 1 and 2;
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
1 : 기재 2 : 건조압화1: base material 2: dry compression
3 : 저융점필름 4 : 커버필름3: low melting film 4: cover film
5 : 피복수지5: coating resin
본발명은 건조압화(押花)를 종이, 포(布), 필름, 피혁 등에 첩부하거나 유리, 금속, 나무, 도자기 등에 접착시켜 장식하는 장식품에 관한 것이다. 더 상세하게는, 이와같은 장식품에 있어서 건조압화를 밀봉하여 건조압화의 형태를 안전하게 보호하고, 나아가서는 압화의 윤기와 색깔을 장기간 보존 가능하게 하는 데에 관한 것이다.The present invention relates to an ornament in which dry pressing is applied to paper, cloth, film, leather, or the like or adhered to glass, metal, wood, ceramics, or the like. More particularly, the present invention relates to sealing dry pressurization in such an ornament to safely protect the form of dry pressurization, and further to enable long term preservation of the gloss and color of the pressurization.
종래부터 꺽은 꽃을 건조시켜 그 아름다움을 유지하여 장식품으로서 사용하고 있다.Conventionally, a flower is dried and its beauty is maintained and used as an ornament.
가령, 꽃을 건조하여 건조압화로 하고, 이것을 종이에 첩부하여 그리팅카드(greeting care)로서 사용하든지, 혹은 포에 첩부하여 포에 꽃모양을 부여하는 등에 사용되고 있다.For example, it is used to dry a flower to dry and pressurize it, to affix it to paper, to use it as a greeting card, or to affix it to a cloth to impart a flower shape.
이 경우, 건조압화를 얻는데는, 꺾은 꽃을 종이에 끼워서 이것을 누른 상태로 적당한 일수를 경과한 후, 꺼내는 것이 전통적인 방법이다.In this case, in order to obtain dry pressurization, it is a conventional method to insert a cut flower in paper, and to take it out after passing a suitable number of days, pressing this.
최근에는 꺾어 마련된 꽃의 색을 유지하기 위하여 작은 상자 바닥에 가령 실리카겔과 같은 건조제를 넣고, 그 위에 구멍 뚫린 판자를 얹어 두고, 이 판자위에 종이, 꺾은 꽃, 종이, 부드럽고 통기성이 있는 우레탄쉬트, 다시 종이, 꽃, 종이, 이와같이 번갈아 중합하여 꽃을 3 내지 4단 넣고, 작은 상자를 닫아 이 작은 상자 중의 공기를 뽑으면서 2일 내지 7일 정도 방치해 두는 것이 행해지고 있다.Recently, in order to maintain the color of the flower, a desiccant such as silica gel is placed on the bottom of a small box, and a perforated board is placed on the bottom of the box. Paper, flowers, paper, and polymerization are alternately placed in such a manner that three to four steps of flowers are placed, and a small box is closed and left in a small box for 2 to 7 days while removing air from the small box.
이 방법으로 작은 상자에서 꺼낸 것은 생화에 가까운 윤기와 색을 가지고 있어 비교적 장시간 그 아름다움을 유지하고 있다.Taken out of a small box in this way, it has a shine and color that is close to natural flowers and maintains its beauty for a relatively long time.
이 경우, 생화를 작은 상자에 넣기 전에 구연산으로 처리해 두면 적색이나 핑크색이 거무스름해지는 것을 방지하는데 적합하다고 되어 있다.In this case, it is said that it is suitable to prevent red or pinkish black from being treated with citric acid before putting the flowers in a small box.
압화의 이용법으로서는 많은 방법이 사용되고 있다. 예컨대, 종이 위에 건조압화를 직접 레이아웃하여 필름과 얇은 종이를 일체로 한 커버용 재료를 준비하고, 압화 위에서 덮어 전체를 가열가압하여 포스트카드로 한 이용법이 특공소 63-239091호 공보에 의해 알려져 있다.Many methods are used as a method of using compression. For example, a method of laying a dry press on paper directly to prepare a cover material in which a film and a thin paper are integrated, and covering the press on the press to heat and pressurize the whole to be a post card is known by Japanese Patent Application No. 63-239091. .
이 이용법에 있어서는 건조압화 표면은 필름에 의해 커버되어 있고, 표면으로부터의 기계적 접촉은 방지할 수 있으며, 또, 물이 표면에서 직접 잘린 꽃에 침입할 수는 없다.In this application method, the dry pressurized surface is covered with a film, mechanical contact from the surface can be prevented, and water cannot penetrate the flower cut directly from the surface.
그러나, 뒤쪽은 종이가 있을 뿐이기 때문에 공기는 물론, 수증기도 약간의 제한을 받을 뿐으로 자유롭게 통과할 수 있다.However, since there is only a paper at the rear, the air as well as the water vapor can pass freely with only a few restrictions.
따라서, 건조압화는 하등의 보호수단도 없는 상태와 같다.Therefore, dry compression is the same as there is no other protection means.
수증기나 물과의 접촉은 10∼20%의 수분을 가지고 있는 건조압화에 있어 바람직한 상황은 아니며, 시간 경과와 함께 흡수, 산화가 진행되어 퇴색이 진척되고, 수주간 이내에 생화가 가지고 있던 색이나 윤기는 완전히 소실된다.Contact with water vapor or water is not a desirable situation for dry pressurization with 10 to 20% water content. Absorption and oxidation progresses over time, causing fading, and the color and gloss of the naturalization within a few weeks. Is completely lost.
이 이용법의 결점을 개선하기 위하여 건조압화를 2매의 저융점 필름으로 끼우고, 이 2매의 필름을 용융시켜, 건조압화를 상하에서 밀봉하는 것을 목적으로 한 방법이 특개소 62-231091호에서 알려져 있다.In order to improve the shortcomings of this method, a method for the purpose of sandwiching the dry presses with two low melting films, melting the two films and sealing the dry presses up and down is disclosed in Japanese Patent Application Laid-Open No. 62-231091. Known.
다시 저융점 필름 위에 그 보다 융점이 높은 필름을 겹쳐서 전체를 포에 고착하는 이용방법이 특허공개 공보소 63-112784호에서 알려져 있다.A method of laminating a film having a higher melting point on a low melting film again and fixing the whole to a fabric is known from Japanese Patent Application Laid-Open No. 63-112784.
이 두 예는 어느 쪽이나 포에 꽃을 부착하기 위하여 궁리한 것이며, 특개소 62-231091호에서는 95℃ 정도로 융해되는 저융점 필름으로 건조압화를 끼워 이것을 가압가열하여 건조압화를 저융점 필름과 일체화하고, 이어서 이것을 포에 얹어 다시 가압가열하여 포에 꽃을 놓는 것을 제안하고 있다.Both of these examples are devised for attaching flowers to fabrics. In Japanese Patent Laid-Open No. 62-231091, a dry melting press is sandwiched with a low melting point film that melts at about 95 ° C, and is heated under pressure to integrate dry pressing with a low melting point film. It is then proposed to place the flower on the cloth by putting it on a cloth and pressurizing it again.
특개소 63-112784호에서는 95℃ 정도의 저융점 필름 위에 110℃ 정도로 융해되는 필름을 겹치고, 우선 꽃과 저융점 필름과 고융점 필름을 일체화하여, 계속해서 이것을 포 위에 놓고, 가압가열하여 고융점 필름을 녹여서 포와 일체로 하고 있다.In Japanese Patent Application Laid-Open No. 63-112784, a film melted at about 110 ° C. is laminated on a low melting point film of about 95 ° C., first, a flower, a low melting point film, and a high melting point film are integrated. I melt a film and am united with cloth.
이 공보에 의하면 가압가열의 수단으로서 아이론을 이용하고 있으며, 손수건이나 명주천 등의 위에 꽃을 놓았을 때 세탁하여도 탈락하지 않는다고 되어 있다.According to this publication, iron is used as a means of pressurized heating, and when a flower is placed on a handkerchief or silk cloth, it does not fall off even after washing.
이 두 공지예는 앞의 공지예에 비해 뒤쪽에도 필름이 존재하고 있기 때문에 외부로 부터의 기계적 손상에 대하여, 또 공기나 수증기의 침입에 대하여 충분히 방어할 수 있을 것같이 보인다.These two known examples seem to be able to provide sufficient protection against mechanical damage from the outside and from intrusion of air or water vapor since the film is present at the rear side compared to the previous known examples.
그러나, 외부에서 공기나 물이 침입하지 않더라도 이 공지예에서는 건조압화는 열화되는 것이다. 즉, 저융점 필름 사이, 혹은 화판과 화판 사이 작은 줄기 표면의 터럭 사이에는 물이나 수증기, 공기가 존재한다.However, even if no air or water penetrates from the outside, the dry compression is deteriorated in this known example. That is, water, water vapor, and air exist between the low melting film, or the turret of the stem surface between the drawing board and the drawing board.
이것은 상하 2매의 저융점 필름으로 끼우고 가압가열하여 일체로 하더라도 이들 공기나 물이나 수증기는 대부분이 그대로 갇혀 버린다.This air, water, or water vapor is mostly trapped as it is, even though it is sandwiched by two upper and lower low melting films and pressurized heating.
이들 공기나 수증기는 때때로 상하가 일체가 된 필름 안에 기포와 같은 형으로 존재하여 보기 싫은 것이 된다.These air or water vapors sometimes become unsatisfactory because they exist in a bubble-like form in a film in which the top and bottom are integrated.
시간 경과와 함께 갇힌 공기나 물, 수증기는 차츰 꽃에 작용하여 색이나 윤기를 변화시킨다.Over time, trapped air, water, or water vapor gradually acts on the flower, changing its color or gloss.
변화에 소요되는 시간은 뒤쪽이 종이였던 제 1의 공지예 보다 길이가 충분하다고는 할 수 없다.The time required for the change is not necessarily longer than that of the first known example in which the back side is a paper.
본발명은 이와같은 종래기술의 결점을 보강하고, 더욱 장기간 건조압화가 가지고 있는 색이나 윤기를 유지시켜서 그대로 사용할 수 있는 건조압화 밀봉 장식품을 제공하고자 하는 것이다.The present invention is to reinforce the drawbacks of the prior art, and to provide a dry pressurized sealing ornament that can be used as it is to maintain the color or gloss of the dry press for a long time.
본 발명은 건조압화가 대략 절건상태(absolutely dried state)이고 또한 공기나 수분이 없는 상태로 저융점 필름으로 완전 밀봉되어 있다. 이 사실로 인하여 건조압화가 장기간에 걸쳐 변색이나 퇴색이 없는 건조압화 밀봉 장식품을 얻을 수 있다.The present invention is completely sealed with a low melting film in a state in which the dry compaction is in an approximately dried state and in the absence of air or moisture. Due to this fact, it is possible to obtain a dry pressurized sealing ornament in which dry pressurization does not discolor or fade over a long period of time.
또, 건조압화가 대략 절건상태이고 또한 공기나 수분이 없는 상태로 저융점 필름으로 완전 밀봉되고, 또한 기재에 고착되어 있다. 이 사실로 인하여 건조압화의 우미성을 장기간에 걸쳐 유지함과 동시에 장식품으로서의 다양한 사용을 가능하게 하는 건조압화 밀봉 장식품을 얻는 것이다.In addition, the dry compression is in a completely dry state and is completely sealed with a low melting point film in the absence of air or moisture, and adhered to the substrate. Due to this fact, it is possible to obtain a dry pressurized seal ornament which enables various uses as an ornament while at the same time maintaining the dominance of the dry press.
또, 저융점 필름의 외측에 커버필름이 저융점 필름으로 고착되어 있다. 이 사실로 인하여 상기 두 건조압화 장식품의 보호를 더욱 강고하게 하는 것이다.Moreover, the cover film is fixed by the low melting film at the outer side of the low melting film. This fact makes the protection of the two dry presser ornaments even more robust.
또, 상기 세 경우, 최외층에 수지피복을 시공하고 있다. 이 사실로 인하여 제품이 광택이 있고, 더욱 우미한 건조압화 밀봉 장식품을 얻을 수 있다.In the above three cases, resin coating is applied to the outermost layer. This fact gives the product a glossy, more elegant dry press sealing ornament.
또, 상기 네 경우, 저융점 필름 또는/ 및 커버필름에 항산화제 및/ 또는 자외선 흡수제에 의한 처리가 행해지고 있다. 이 사실로 인하여 외부로 부터의 빛에 의한 필름 및 건조압화의 열화를 방지하고, 장기간의 사용에 견딜 수 있는 건조압화 밀봉 장식품을 얻을 수 있다.In the above four cases, the low melting point film and / or the cover film are treated with an antioxidant and / or an ultraviolet absorber. Due to this fact, it is possible to prevent the deterioration of the film and the dry compression by the light from the outside, and to obtain a dry press sealing ornament which can withstand long-term use.
또, 제조에 있어서, 건조압화를 저융점 필름으로 밀봉함에 있어서, 감암 분위기에 내맡겨지고, 감압분위기 상태에서 저융점 필름을 건조압화에 가압하여 저융점 필름을 용융한다. 이 사실로 인하여 장기간에 걸쳐 퇴색, 변색이 없는 건조압화가 대략 절건상태로 공기나 수분이 없는 상태에서 저융점 필름에 의해 완전히 밀봉되어 있는 건조압화 밀봉 장식품을 제조할 수 있는 것이다.Moreover, in manufacture, when sealing a dry compression with a low melting point film, it is enclosed by a darkening atmosphere, and a low melting point film is melted by pressurizing a low melting point film in dry pressure in a reduced pressure atmosphere. Due to this fact, it is possible to manufacture a dry pressurized sealing ornament in which dry pressurization without fading and discoloration over a long period of time is approximately dry and completely sealed by a low melting film in the absence of air or moisture.
또, 상기 제조에 있어서 저융점 필름을 기재 및/ 또는 커버필름과 겹쳐서 가압가열 처리한다. 이 사실로 인하여 일거에 장기간에 걸쳐 퇴색, 변색되지 않는 건조압화 밀봉 장식품을 제조할 수 있는 것이다.In addition, in the production, the low melting point film is overlaid with the base material and / or the cover film and subjected to pressure heating. Due to this fact, it is possible to manufacture a dry pressurized sealing ornament which does not fade and discolor over a long period of time.
또, 전기 또는 전전기의 제조에 있어서, 표면이 조밀한 기재 위에 건조압화를 얹고, 다시 커버필름을 겹쳐서 처리한다. 이 사실로 인하여 도판(陶板)과 같은 표면이 조밀한 기재상에 전체를 일거에 제조하는 건조압화 밀봉 장식품의 제조품을 얻을 수 있는 것이다.Moreover, in manufacture of an electric or an electric machine, dry compression is put on the board | substrate with a dense surface, and a cover film is piled up again and processed. Due to this fact, it is possible to obtain a product of a dry pressurized sealing ornament which is manufactured entirely on a substrate having a dense surface such as a plate.
본발명에 있어서는 저융점 필름이 사용된다. 저융점 필름은 적어도 1매 필요하고, 2매 이상이라도 좋다. 저융점 필름은 약 70℃∼120℃ 범위의 온도에서 용융되는 것이면 폴리프로필렌, 폴리부틸랄, 에틸렌비닐아세테이트, 폴리아미드 등, 특별히 한정되지는 않는다. 또, 저융점 필름의 두께로 꽃 종류와 형상에 따라 적절히 선택하면 된다.In the present invention, a low melting point film is used. At least one low melting point film is required, and two or more sheets may be used. The low melting point film is not particularly limited as long as it is melted at a temperature in the range of about 70 ° C to 120 ° C, such as polypropylene, polybutylral, ethylene vinyl acetate, polyamide, and the like. Moreover, what is necessary is just to select suitably according to a flower kind and a shape with the thickness of a low melting-point film.
1매만 사용할 경우, 100μ정도 이상의 것이 바람직하나 사용 조건에 따라서는 20∼30μ 정도라도 좋다. 2매를 사용할 경우, 2매의 두께가 같아야할 필요는 없다. 한쪽은 30μ 정도로 충분하다. 또한, 필름의 넓이는 녹였을 때 꽃을 쌀만한 넓이가 있으면 이 이상 큰 것은 상관없다.When only one sheet is used, it is preferably about 100 mu or more, but may be about 20 to 30 mu depending on the use conditions. If two sheets are used, the two sheets do not have to have the same thickness. 30 μm is enough for one side. In addition, if the width of the film is enough to disperse the flowers when melted, it does not matter much larger than this.
저융점 필름은 그 단독으로 사용될 경우가 있다. 또, 커버필름과 미리 일체로 겹쳐져서, 혹은 별도의 상태로 겹쳐서 사용된다.The low melting film may be used alone. Moreover, it overlaps with a cover film previously, and is used by overlapping in a separate state.
커버필름은 저융점 필름의 용융 온도에 있어서 필름의 형상을 확보하고 있을 만큼의 융점을 가지고 있지 않으면 안된다. 폴리에스테르필름은 투명한 것을 구하기 쉽다는 점, 기계적 강도, 치수 안정성이 우수하다는 점에서 가장 바람직한 커버필름의 소재이다. 다른 소재라도 상기 온도 조건의 기계적 특성을 가지고 있으면 사용할 수 있다.The cover film must have a melting point sufficient to ensure the shape of the film at the melting temperature of the low melting point film. Polyester film is the most preferable material of cover film in that it is easy to obtain a transparent thing, and is excellent in mechanical strength and dimensional stability. Any other material can be used as long as it has mechanical properties of the above temperature conditions.
본 발명에 있어서는 가장 외층에 수지코팅을 실시할 경우가 있다. 수지코팅은 도포, 분무 같은 방법으로 행하는 것이 일반적 이지만 때로는 필름 형상의 것을 피복하고 이것을 녹여서 전체를 싸도 좋다.In this invention, resin coating may be given to the outermost layer. It is common to apply resin coating by a method such as coating or spraying, but sometimes it is possible to cover the whole of film-like thing by melting it.
본발명에 있어서 사용되는 기재는 나무, 유리, 금속, 도자기, 합성수지판과 같이 일반적으로 단단하고, 표면이 조밀한 것이라도 좋고, 또, 섬유 천, 종이와 같이 부드럽고 표면이 거친 것, 필름과 같이 부드럽고 표면이 조밀한 것, 피혁과 같이 부드럽고 표면이 거칠고, 또는 조밀한 것 중의 어느 것이라도 상관 없다.The base material used in the present invention is generally hard, such as wood, glass, metal, porcelain, or synthetic resin board, and may have a dense surface, and is soft like a fabric cloth, paper, or rough surface, such as a film. Either soft or dense surface, soft or rough surface such as leather, or dense may be used.
본발명에 있어서 감압하란, 밀봉된 실(室)을 형성한 후, 일반적으로 시판되고 있는 진공펌프를 사용하여 실내 공기를 배출하고, 진공펌프에 부착된 미터의 표시가 작동전에 있어서 760㎜ 수은주 높이를 표시할 경우 200㎜ 이하, 가장 바람직하게는 0 의 표시를 하는 상태를 말한다.In the present invention, under reduced pressure, after the sealed chamber is formed, indoor air is discharged using a commercially available vacuum pump, and the indication of the meter attached to the vacuum pump is 760 mm high. In the case of indicating, the state of displaying 200 mm or less, most preferably 0.
또한 본발명에 있어서 사용되는 건조압화는 꺾은 후 적절한 방법으로 제작된 것을 말한다. 가령, 종이에 끼워서 가압 적층하고, 매일 1회 혹은 2회 종이를 교환하여 가압 적층 상태를 계속하여 얻어진 것, 또는 가압 적층한 상태로 작은 방에 넣고 건조제를 넣어 실내 공기를 배출하면서 수일경과시킨 후 꺼낸 것 등, 제작방법은 한정되지 않는다.In addition, the dry compression used in this invention means what was produced by the appropriate method after bending. For example, after pressing and laminating the paper, and replacing the paper once or twice a day, the pressure lamination is continuously obtained, or the pressure lamination is carried out in a small room and the desiccant is put in the room to discharge the air. The production method such as the one taken out is not limited.
본발명에 있어서 가압이란, 건조압화와 저융점 필름을 압접하여 저융점 필름을 녹이는데 있어서 가해지는 압력으로 1.5 기압 정도의 것이며, 녹은 저융점 필름이 수축해버리는 것을 막기 위하여 압력을 가하는 것을 말한다.In the present invention, the pressurization means a pressure applied to dry-press the low-melting-point film and melt the low-melting point film, and is about 1.5 atm, and applies pressure to prevent the melted low-melting film from shrinking.
본발명에 있어서의 제 1의 실시 태양은, 건조압화를 대판(台板)에 얹고, 그 위에 저융점 필름을 얹고, 위에서 가압한 상태로 분위기를 감압상태로해 가서 충분한 감압 상태를 확보한 채 가열하여 저융점 필름을 녹여 저융점 필름과 건조압화를 밀착시킴으로써 얻어지는 제품과 제조법이다.According to a first embodiment of the present invention, dry pressure is placed on a large plate, a low melting point film is placed thereon, the atmosphere is reduced in pressure while being pressed from above, and a sufficient pressure reduction state is ensured. It is a product and a manufacturing method obtained by melt | dissolving a low melting film and heating a low melting film and making it dry contact closely.
제 2의 실시 태양은, 대판 위에 저융점 필름을 얹고, 이어서 건조압화를 얹고 다시 저융점 필름을 얹어 위에서 감압한 상태 그대로 분위기를 감압 상태로 해 가서 충분한 감압상태를 확보한 채 가열하여 저융점 필름을 녹이고 건조압화와 상하의 저융점 필름을 밀착시킴으로써 얻어지는 제품 및 제조법을 말한다.According to the second embodiment, a low melting point film is placed on a base plate, followed by dry compression, and then a low melting point film, and then the low pressure point film is heated in a reduced pressure state as it is in a reduced pressure state. It refers to a product and a manufacturing method obtained by melt | dissolving melt | dissolution, and contact | adhering a dry compression and an upper and lower low melting film.
제 1, 제 2 어느 실시 태양에 있어서도 대판 위에는 이형지를 얹고나서 건조압화 혹은 저융점 필름을 얹을 필요가 있다. 또, 대판 위에 기재를 얹음으로써 이형지를 생략하고, 저융점 필름이 가열된 후, 냉각되어 재차 굳어질 때, 기재와 접착하여 일거에 기재를 갖는 제품으로 할 수 있는 것이다. 이렇게 함으로써 기재에의 접착공정을 생략할 수 잇는 것이다.In either of the first and second embodiments, it is necessary to put a release paper or a dry compression film or a low melting point film on the base plate. Moreover, a release paper is abbreviate | omitted by putting a base material on a base board, when a low melting film is heated, and when it cools and hardens again, it adheres with a base material and can be made into the product which has a base material at once. By doing in this way, the adhesion process to a base material can be skipped.
또, 저융점 필름을 미리 커버필름에 접착시켜 두고, 저융점 필름측을 건조압화를 향하도록 해놓고 가열 융착할 수 있다.In addition, the low melting film can be adhered to the cover film in advance, and the low melting film can be heated and welded with the low melting point film facing toward dry compression.
이렇게 함으로써 저융점 필름 외측에 보호용 커버필름을 접착하는 공정을 생략할 수 있다. 이 경우도 이형지는 필요로 하지 않는다.By doing so, the step of adhering the protective cover film to the outside of the low melting point film can be omitted. In this case, no release paper is needed.
그리고, 저융점 필름 또는/ 및 커버필름에 항산화제 또는/ 및 자외선 흡수제를 도포하든지 또는 혼입해 두는 것은 바람직한 일이다.It is also desirable to apply or incorporate an antioxidant or / and an ultraviolet absorber into the low melting point film and / or the cover film.
또한, 기재를 이용할 경우에 있어서 저융점 필름 또는 커버필름의 기재를 향하고 있는 쪽과 반대쪽에 피복수지를 도포하는 것 또는 피복용 필름을 얹어 기재와 함께 저융점 필름 및 건조압화의 모두 또는 다시 커버필름 전부를 일체로 싸는 것도 매우 바람직한 일이다.In the case of using the base material, coating the coating resin on the opposite side of the low melting point film or the cover film toward the base material or placing the coating film together with the base material or both of the low melting point film and the dry compression or the cover film again. It is also very desirable to wrap everything in one piece.
이하 도면을 이용하여 설명한다.A description with reference to the drawings below.
제 1도와 제 2도와 제 3도는 각각 다른 실시태양을 도시하고 있으며, 제 1도에 있어서는 저융점 필름은 1매 사용되고 있고, 제 2도에 있어서는 2매 사용되고 있다. 제 3도에 있어서는 저융점 필름외에 커버필름이 사용되고 있다.1, 2, and 3 show different embodiments. In FIG. 1, one low melting point film is used, and in FIG. 2, two sheets are used. In FIG. 3, a cover film is used besides a low melting film.
1은 기재, 2는 건조압화, 3은 저융점 필름, 4는 커버필름, 5는 피복수지이다.1 is a base material, 2 is dry compression, 3 is a low melting film, 4 is a cover film, and 5 is a coating resin.
제 1도, 제 2도에 있어서 기재(1), 건조압화(2) 와, 저융점 필름(3)은 겹쳐져서 위로부터 가압된 상태로, 도시되지 않는 대판 위에 얹혀진다. 제 3도에 있어서는 저융점 필름과 함께 커버필름(4)이 겹쳐져서 대판 위에 얹혀진다. 대판에 얹은 후, 대판을 포함한 전체 분위기를 감압하여 진공펌프의 표시가 0을 나타내는 상태도, 도시되지 않는 가열수단에 의해 가열하여 저융점 필름을 녹인다. 이어서 감압을 멈추고 가열을 정지하여 방치상태로 저융점 필름을 재차 고화시킨다. 그 후, 대판에서 기재까지 함께 전체를 꺼낸다.In FIG. 1 and FIG. 2, the base material 1, the dry compression 2, and the low melting film 3 are piled up and put on the board which is not shown in the state pressed from the top. In FIG. 3, the cover film 4 overlaps with the low melting film, and is mounted on a base plate. After mounting on the base plate, the whole atmosphere including the base plate is depressurized, and the low melting point film is melted by heating by a heating means (not shown) even in a state where the indication of the vacuum pump is zero. Subsequently, the pressure reduction is stopped, the heating is stopped, and the low melting film is solidified again in a standing state. Then, the whole is taken out from a large plate to a base material together.
이 경우, 저융점 필름을 기재에 가압하는 압력은 1.5 기압 정도가 바람직하다. 너무 강하면 저융점 필름이 녹은 상태에 있어서 건조압화가 저융점 필름에서 튕겨 나오거나 하여 건조압화의 저융점 필름에 의한 밀봉이 불충분해져 버리기 때문이다. 또, 너무 압력이 낮으면 저융점 필름이 고화되는 과정에서 수축되어 버려서 원래의 평판(平板) 상태로 복귀하지 않기 때문이다.In this case, about 1.5 atmospheres are preferable for the pressure which pressurizes a low melting film to a base material. It is because when it is too strong, dry pressurization will jump out of a low melting point film in the melted state of a low melting point film, and sealing by the low melting point film of dry pressurization will become inadequate. If the pressure is too low, the low melting point film shrinks in the process of solidification and does not return to the original flat state.
감압은 수은주 약 200㎜ 이하가 필요하고, 바람직하게는 진공펌프미터 표시가 0의 상태이다. 실질적으로 대판을 포함한 작은 방을 형성시키고, 이 방을 밀봉하여 진공펌프로 공기를 배출하여 감압해 가는 것으로서, 저융점 필름이 녹는 순간에는 펌프미터 표시가 0 까지 감압되어 있는 것이 효과적이다.The reduced pressure requires about 200 mm or less of mercury liquor, and preferably the vacuum pump meter display is in a state of zero. It is effective to form a small room including a large plate, to seal the room, to discharge the air with a vacuum pump, and to reduce the pressure. When the low melting film melts, it is effective that the pump meter display is reduced to zero.
감압의 목적은, 저융점 필름이 녹아서 건조압화의 화판이 중합된 부분이나 앞표면의 미세한 터럭으로 싸여 있는 부분에 침투할 때, 그 부분에 공기나 수증기나 물을 존재시키지 않는 것이며, 녹은 필름이 건조압화의 각 부분과 직접 밀착하여 공기나 수증기나 물을 동시에 싸들이지 않기 위함이다.The purpose of the pressure reduction is to prevent air, water vapor or water from being present when the low melting point film melts and penetrates into the polymerized part or the part covered with the fine turret on the front surface. It is in direct contact with each part of the dry compaction so as not to simultaneously enclose air, steam or water.
만일, 녹은 필름이 공기나 수증기나, 물을 가진채 이들을 싸들여서 냉각되면 공기나 수증기나 물은 필름중에 기포를 만들어 버린다. 이 기포는 완성된 제품의 아름다움을 손상시키게 되므로 바람직하지 못하다.If the melted film is wrapped with air, water vapor, or water and cooled, the air, water vapor, or water creates bubbles in the film. This bubble is undesirable because it damages the beauty of the finished product.
또, 기포의 존재는 싸들여진 공기나 수증기나 물이 건조압화에 작용하여 그 퇴색이나 변색은 촉진시켜 버려 애써 밀봉하여도 그 의미를 상실시키기 때문에 절대로 피할 필요가 있다.In addition, the presence of air bubbles must be avoided because the enclosed air, water vapor, or water acts on the dry compression, which promotes the discoloration and discoloration, and loses its meaning even if it is sealed.
가열은 사용하는 저유점 필름의 융점에 따라 결정된다. 저융점 필름은 일반적으로 70∼120℃의 것이 입수가 쉽고 또 취급하기 좋다.Heating is determined by the melting point of the low viscosity film used. Generally low melting | fusing point film of 70-120 degreeC is easy to obtain and is easy to handle.
기재가 유리나 도자기의 경우, 승온에 시간이 걸리기 때문에 미리 기재만, 혹은 기재와 이에 직접 접촉하는 필름을 가열시키는 것이 행해진다. 이렇게 함으로써 건조압화가 높은 온도에 내맡겨지는 시간을 적게할 수 있다. 가령, 건조압화가 높은 온도에 내맡겨질 경우에도 전체 분위기를 되도록 0에 가까운 갑압하에 둠으로써 건조압화의 변색 가능성을 낮게 억제할 수 있는 것이다.In the case where the substrate is glass or porcelain, heating takes time, so that only the substrate or a film in direct contact with the substrate is heated in advance. By doing in this way, time to which dry compression is put to high temperature can be reduced. For example, even when the drying pressure is left at a high temperature, the possibility of discoloration of the drying pressure can be reduced by keeping the overall atmosphere under the reduced pressure as close to zero as possible.
감압과 가열은 급격히 행하면 안된다. 건조압화가 소형일 경우에도 수분간, 더욱 바람직하게는 10분 정도의 시간이 걸리도록 서서히 진공펌프의 표시를 0 로 해야 한다. 승온에 있어서도, 분위기가 감압상태가 된 후에 행해야 하며, 너무 조기에 행하는 것은 바람직하지 않다. 너무 급격한 감압진행은 건조압화 표면에 상처를 낼 가능성이 있고, 너무 조기의 가열은 남아 있는 공기나 수증기가 물을 저융점 필름으로 가두어 버릴 가능성이 있기 때문이다.Decompression and heating should not be carried out rapidly. Even when the drying pressure is small, the indication of the vacuum pump should be gradually made zero so that it takes several minutes, more preferably about 10 minutes. Also in temperature rising, it is necessary to carry out after the atmosphere becomes a reduced pressure, and it is not preferable to carry out too early. Too much depressurization may damage the dry pressurized surface, and too early heating may cause the remaining air or steam to trap the water in the low melting point film.
건조압화는 미리 충분히 건조시켜 사용해야 한다. 그러나, 항상 충분한 건조가 부여되기란 보증하기 어렵다. 즉, 사용시의 실내의 약간의 상황 변화나 취급방법에 따라 순간적으로 흡수해 버려 건조도를 저하시킨다. 이 상태로 저융점 필름에 의한 밀봉이 행해지면 제품은 균일성을 잃고, 사용에 견딜 수 없는 것이 된다.Drying compression should be used after drying sufficiently. However, it is difficult to guarantee that sufficient drying is always given. That is, it absorbs instantaneously according to the slight situational change and handling method in the room at the time of use, and reduces dryness. When sealing with a low melting film is performed in this state, a product will lose uniformity and it cannot endure use.
따라서, 건조압화를 공급하고나서, 감압에 시간이 걸리는 것은 매우 중요하다. 이에 의해 건조압화는 최후의 건조의 마무리공정을 받게 되는 것이다.Therefore, it is very important to take time to depressurize after supplying dry pressurization. As a result, the drying pressure is subjected to the final drying process.
실질적인 측정은 곤란하지만 저융점 필름이 녹는 순간의 건조압화의 수분은 매우 낮고, 절건상태에 가까운 것이라 생각된다.Although practical measurement is difficult, it is thought that the moisture of the dry pressurization at the time of melting a low melting point film is very low, and it is close to a dry state.
이 상태로 건조압화는 저융점 필름에 의해 밀봉되는 것이다.In this state, dry compression is sealed by a low melting film.
이리하여 얻어진 제품에 있어서는 건조압화는 그 모두가 저융점 필름에 밀착되어 있고, 저융점 필름 안에는 기포는 존재하지 않는다. 따라서, 건조압화는 외부공기나 수분과는 완전히 차단되어 있어 외부로 부터의 공기, 물 등의 침입에 의한 변화가 없기 때문에 장시간에 걸쳐 그 색과 윤기를 유지할 수 있다.In the product thus obtained, all of the dry compression is in close contact with the low melting point film, and no bubbles exist in the low melting point film. Therefore, the drying pressure is completely blocked from the external air or moisture, and there is no change due to invasion of air, water, etc. from the outside, so that the color and gloss can be maintained for a long time.
또, 내부에도 공기나 수증기나 물이 존재하지 않기 때문에 내부도 부터의 변화가 생기지 않고, 색깔과 윤기의 유지는 더욱 장기화한다. 또한, 내부에 기포가 생기지 않으므로 미관을 해치는 일이 없다.In addition, since there is no air, steam, or water inside, no change occurs from the inside, and the maintenance of color and gloss is prolonged. In addition, since bubbles are not generated inside, the appearance is not impaired.
덧붙여, 저융점 필름이 건조압화와 밀착되어 있으므로 꽃은 건조되어 있음에도 불구하고, 싱싱한 광택을 지니고 있으며, 종래 존재하지 않는 우미성을 갖는 것이다.In addition, since the low-melting-point film is in close contact with the dry compression, the flower has a fresh luster even though the flower is dried, and has a non-existent uminess.
제품의 최외측을 수지층으로 피복하는 것은 유효한 보호방법이다.Covering the outermost side of the product with a resin layer is an effective protection method.
제 1도, 제 2도, 제 3도에 있어서는 저융점 필름의 외측에서 기재까지를 수지로 피복한 것이 도시되어 있다. 수지는 도포, 분무, 등에 의해 저융점 필름 외측에 접착되어 있다.In FIG. 1, FIG. 2, and FIG. 3, what covered the resin from the outer side of the low melting film to the base material is shown. The resin is adhered to the outside of the low melting point film by coating, spraying, or the like.
도포, 분무 등에 있어서 용제를 사용하거나 혹은 반응액과 함께 사용하거나 한다. 또, 감광성 수지를 사용하여 최외측을 피복한 후, 여기에 소정의 빛을 조사하여 경화시키는 것은 완성된 수지의 표면을 단단하게, 또한 두껍게 하고 나아가 윤기 있는 것으로 하는데에 적합하다.In application | coating, spraying, etc., a solvent is used or it is used with a reaction liquid. Moreover, after coating the outermost side using photosensitive resin, it hardens | cures by irradiating predetermined light to it, and it is suitable for making the surface of the completed resin hard, thickening, and also shiny.
제 3도에 있어서는 저융점 필름(3)이 커버필름(4)과 일체로 된 것을 사용하고 있다. 이 예에 있어서는 커버필름의 존재에 의해 보호하는 한층 강고한 것이 된다.In FIG. 3, the low-melting-point film 3 integrated with the cover film 4 is used. In this example, it becomes even stronger to be protected by the presence of the cover film.
이 경우, 피복수지는 내부를 보호하는 것에 대한 기대도 있으나 이에 더하여 외측에 광택을 부여하여 전체를 화려하고 아름다운 것으로 하는 기대하에서 사용되고 있다.In this case, the coating resin is expected to protect the interior, but in addition, it is used under the expectation that the whole is made colorful and beautiful by giving gloss to the outside.
기재(1)에 대해서는 이미 설명한 바와같이, 나무, 유리, 금속, 도자기, 합성 수지판과 같이 단단하고 표면이 조밀한 것, 섬유천, 종이와 같이 유연하고 표면이 거친 것, 필름과 같이 유연하고 표면이 조밀한 것, 피혁과 같이 부드럽고 표면이 거칠거나 혹은 조밀한 것 등, 어느 것이라도 사용할 수 있다.As described above, the substrate 1 is hard and dense, such as wood, glass, metal, porcelain, or synthetic resin board, fibrous cloth, flexible, rough surface, such as film, and flexible, such as film. Any surface may be used, such as a dense surface or soft and rough or dense like a leather.
이들 기재와의 접착은 본발명에 있어서의 중요사항인 건조압화의 밀봉과 동시에 행할 수 있고, 또한 동시에 해하는 것이 유리하다.Adhesion with these base materials can be carried out simultaneously with the sealing of the dry compression which is an important point in this invention, and it is advantageous to do it simultaneously.
특히 제 1도에 도시한 바와같이 저융점 필름을 건조압화의 한쪽에만 사용하여 밀봉하는 실시 태양에 있어서는 기재를 나무, 유리, 금속, 도자기, 합성수지판, 필름과 같이 표면이 조밀한 것을 사용하여 밀봉과 부착을 동시에 행하는 것이 특히 유리하다.In particular, as shown in FIG. 1, in the embodiment in which the low melting point film is sealed using only one side of the dry press, the substrate is sealed using a dense surface such as wood, glass, metal, porcelain, synthetic resin board or film. It is particularly advantageous to carry out and attach at the same time.
저융점 필름을 기재에 접착할 경우, 기재 표면이 조밀한 것일때 저융점 필름을 얹기 전에 미리 얹을 장소를 조면(粗面) 가공해 두는 것은 저융점 필름의 접착에 대하여 대단히 유리하며, 저융점 필름이 기재표면에 아주 강고하게 접착된다.When the low melting point film is adhered to the substrate, it is very advantageous for the adhesion of the low melting point film to roughen the place to be placed before placing the low melting point film when the surface of the substrate is dense. It adheres very firmly to this substrate surface.
조면가공의 방법으로는, 샌드페이퍼를 이용하여 기재의 필요 부위를 거칠게해둔다거나, 샌드블라스트(Sand blast; 모래분무) 가공을 실시한다거나, 혹은 적당한 약제를 사용하여 표면을 침식시켜 거칠게해 둔다거나 하는 등의 적절한 방법이 채용된다.As the roughening method, sandpaper is used to roughen the necessary portion of the substrate, sandblasting is performed, or the surface is eroded and roughened with a suitable chemical. Appropriate method of is employed.
이하 실시예에 대하여 설명한다.Examples will be described below.
(실시예 1)(Example 1)
꺾은 야생 제비꽃을 신문지로 사이에 끼우고, 이것을 적층하여 가압하였다. 신문지를 하루 2회 교환하여 일주일간 반복하였다.The cut wild violet was sandwiched between newspapers, and this was laminated and pressed. Newspapers were exchanged twice a day and repeated for a week.
얻어진 야생 제비꽃의 수분량은 15% 였다.The moisture content of the obtained wild violet was 15%.
다음에, 진공펌프를 구비한 작은 방 안에 두께 5㎜, 폭 15㎝, 길이 15㎝의 도자기판을 두고, 이 위에 두께 300μ, 폭 15㎝, 길이 15㎝의 아세트산 비닐계 저융점 필름(융점 95℃)을 얹어 이 위에 준비한 야생 제비꽃을 소정 모양으로 놓았다.Next, a 5 mm thick, 15 cm wide, 15 cm long porcelain plate was placed in a small room equipped with a vacuum pump, and a 300 μm thick, 15 cm wide, 15 cm long vinyl acetate-based low melting film (melting point 95 And the wild violet prepared thereon was placed in a predetermined shape.
야생 제비꽃 위에 앞서 사용한 저융점 필름과 같은 크기, 두께, 재질의 필름을 겁쳐 얹었다.On top of the wild violet was a film of the same size, thickness and material as the low melting film used previously.
소실내를 상온, 상압 상태에서 20분 걸려 서서히 감압승온하여 100㎜Hg 90℃로 한 후 1.5 기압으로 도자기판과 저융점 필름, 야생 제비꽃, 저융점 필름을 가압하면서 승온시키고 저융점 필름을 용융한 후, 가열을 멈추고 강압을 중지하였다. 저융점 필름은 고화되고 야생 제비꽃을 밀봉함과 동시에 도자기판에 밀착시켰다.After the chamber was heated at room temperature and atmospheric pressure for 20 minutes, the pressure was gradually increased to 100 mmHg at 90 ° C., and then heated at a pressure of 1.5 atm while pressing the porcelain plate, the low melting film, the wild violet, and the low melting film, and melting the low melting film. After that, the heating was stopped and the step down was stopped. The low melting film solidified and tightly adhered to the porcelain plate while sealing the wild violets.
고화된 저융점 필름 위에 액상 광택내기 감광성 수지를 0.6㎜의 두께로 브러시로 도포한 후, 무진상태에서 레벨링하여 자외선을 조사하여 감광성 수지를 경화시켰다.After the liquid-gloss photosensitive resin was applied with a brush to a thickness of 0.6 mm on the solidified low melting point film, it was leveled in a dust-free state and irradiated with ultraviolet rays to cure the photosensitive resin.
얻어진 제품은 제비꽃의 자연색을 유지하고 있으며, 꽃은 하등의 손상을 입지 않았고, 내부에는 기포가 전혀 없이 외부는 윤기가 있고 투명감이 뛰어난 것이 었다.The resultant product retained the natural color of the violet, the flowers were not damaged at all, and there was no bubble inside, and the outside was shiny and transparent.
얻어진 제품을 수중에 침지하고, 베란다에 방치하여 1년 경과하였으나 꽃은 변색, 퇴색하지 않았다.The obtained product was immersed in water and left on the veranda for 1 year, but the flowers did not discolor or fade.
(실시예 2)(Example 2)
실시예 1에 있어서 저융점 필름을 2매 사용한 것에 비해, 1매 사용하였다. 도자기판 표면을 샌드페이퍼로 문질러 조면가공한 것 이외는 실시예 1과 같은 것을 사용하였다. 이 도자기판을 예열시킨 후, 도자기판 위에 실시예 1에서 사용한 야생 제비꽃과 같은 가공을 시공한 것을 직접 얹었다. 이어서 이 위에 두께가 400μ인 것 이외는 실시예 1과 같은 조건의 저융점 필름 1매를 겹쳐 놓았다. 이 이외의 조건은 모두 실시예 1과 같게 하여 가공을 행하였다.In Example 1, compared with using two low melting-point films, one sheet was used. The same thing as in Example 1 was used except that the surface of the porcelain plate was roughened by sand paper. After preheating this porcelain plate, the thing which processed the same process as the wild violet used in Example 1 was directly mounted on the porcelain plate. Subsequently, one low-melting-point film under the same conditions as in Example 1 was stacked except that the thickness was 400 µ. All other conditions were the same as Example 1, and the process was performed.
얻어진 제품은 실시예 1의 경우와 같고 꽃의 상태, 무기포인 점, 외부는 윤기가 있는 점, 장기간 꽃이 퇴색, 변색하지 않는 등, 우수한 것이 었다.The obtained product was the same as that of Example 1, and was excellent in the state of a flower, the point which is an inorganic cloth, the point which has a gloss on the outside, and a flower does not fade and discolor for a long time.
(실시예 3)(Example 3)
실시예 1에서 사용한 도자기판 대신 판지제인 포스트카드를 사용하였다.A post card made of cardboard was used instead of the porcelain plate used in Example 1.
기재를 변경한 것 이외의 조건은 실시예 1과 같게하여 가공하였다.The conditions other than having changed the base material were processed similarly to Example 1.
얻어진 제품은 포스트카드 위에 제비꽃이 부상한 것처럼 보이는 멋진 것이었다. 이것을 베란다에 방치하였으나 6개월 경과하여도 아무런 변색, 퇴색을 보이지 않았다.The product obtained was a wonderful thing that seemed to have a violet on the post card. This was left on the porch, but after 6 months, there was no discoloration or fading.
본발명은 상기와 같이 우수한 성과를 내는 것이었고, 그 효과를 요약하면 다음과 같다.The present invention was to produce excellent results as described above, summarize the effect is as follows.
(1) 건조시킨 압화를 미리 필요한 기재나 저융점 필름과 겹친 상태로 서서히 감압하여 가열함으로써 꽃은 밀봉전에 건조의 마무리 손질을 받는다. 따라서, 가열가압하여 저융점 필름이 꽃을 밀봉하는 순간에 있어서는 꽃 주위에는 밀봉되어 적합하지 않은 것은 일체 배제되어 있으며, 꽃도 절건상태에 가까운 상태가 부여되어 있다.(1) The dried compaction is gradually depressurized and heated in a state of overlapping with a necessary base material or a low melting point film in advance, and the flower is subjected to the finishing treatment of drying before sealing. Therefore, at the moment when the low melting point film seals a flower by heating and pressurizing, it is excluded around the flower and unsuitable at all, and the flower is also given the state close to a dry state.
이 사실은, 밀봉된 후의 상태에 매우 바람직한 상태를 부여하게 되며, 꽃은 저융점 필름에 의해 완전히 밀봉된다.This fact imparts a very desirable state to the state after being sealed, and the flower is completely sealed by the low melting film.
(2) 이 결과, 제품중에는 꽃의 장기간에 걸친 색깔과 윤기 유지에 악영향을 부여하는 것은 일절 존재하지 않고 배제되어 있다. 또, 밀봉은 완전히 행해지기 때문에 제품중에 사용기간중에 악영향을 주는 것이 외부에서 침입하는 일은 없다.(2) As a result, none of the products adversely affects the long-term color and glossiness of flowers. In addition, since sealing is carried out completely, it does not invade from the outside that adversely affects during the use period in the product.
따라서, 제품은 장기간에 걸쳐 우미성을 확보할 수 있는 것이다.Therefore, the product can secure dominance over a long period of time.
(3) 적당한 기재, 특히 표면이 조밀한 기재 및 저융점 필름과 커버필름의 선택은 공정의 생략에 유효하며, 일거에 완성품을 얻을 수 있다.(3) The selection of a suitable substrate, particularly a substrate with a dense surface, a low melting point film and a cover film is effective for eliminating the process, and a finished product can be obtained in one step.
(4) 적당한 기재의 선택, 커버필름의 사용, 피복수지의 사용, 자외선 흡수제 혹은 항산화제의 채용, 등의 수단을 가함으로써 제품의 특성을 여러 갈래에 걸쳐 확장할 수 있기 때문에 제품의 사용범위를 매우 광범위한 것으로 할 수 있다.(4) The product's range of use can be extended by selecting appropriate substrates, using cover films, using coated resins, applying ultraviolet absorbers or antioxidants, and so on. It can be very broad.
본발명은 건조압화를 단시간에, 완전하게 수증기나 물이나 공기를 배제한 상태로 저융점 필름으로 밀봉하기 때문에 건조압화를 색깔이나 윤기의 우미성을 장기간에 걸쳐 유지할 수 있다.In the present invention, the dry pressurization is sealed with a low melting point film in a state in which water vapor, water, or air is completely removed in a short time, and thus the dry pressurization can maintain color and glossiness for a long time.
따라서, 제품은 단독으로, 혹은 각종 기재와 조합시켜 각종 장식품으로서 널리 이용할 수 있는 것이다.Therefore, the product can be widely used as various ornaments, alone or in combination with various substrates.
Claims (7)