KR100187009B1 - Display panel glass compositions - Google Patents
Display panel glass compositions Download PDFInfo
- Publication number
- KR100187009B1 KR100187009B1 KR1019960078251A KR19960078251A KR100187009B1 KR 100187009 B1 KR100187009 B1 KR 100187009B1 KR 1019960078251 A KR1019960078251 A KR 1019960078251A KR 19960078251 A KR19960078251 A KR 19960078251A KR 100187009 B1 KR100187009 B1 KR 100187009B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- display panel
- plasma display
- zno
- pbo
- Prior art date
Abstract
본 발명은 P2O559.90∼65.83 중량%와, Na2O 7.96∼11.49 중량%와, MgO 2.92∼3.96 중량%와, B2O32.00∼22.57 중량%와, Li2O 0∼5.49 중량%와, ZnO 0∼9.99 중량%와, Al2O30∼1.00 중량%와, As2O30∼0.97 중량%와, La2O30∼1.00 중량%와, F 0∼3.74 중량%로 조성된 플라즈마 디스플레이 패널 봉착용 유리 조성물에 관한 것으로서, 종래 기술의 PbO-B2O3계 또는 PbO-ZnO-B2O3계 유리 조성물보다 낮은 굴복점을 가지면서 동시에 PbO 성분을 전혀 포함하지 않기 때문에 플라즈마 디스플레이 패널 제품의 폐기시 환경오염 및 자연 생태계 파괴 등의 문제점을 근본적으로 해결할 수 있고, 플라즈마 디스플레이 패널 제품의 무게를 줄일 수 있는 효과가 있다.59.90 to 65.83 wt% of P 2 O 5, 7.96 to 11.49 wt% of Na 2 O, 2.92 to 3.96 wt% of MgO, 2.00 to 22.57 wt% of B 2 O 3 , and 0 to 5.49 wt% of Li 2 O %, 0 to 9.99% by weight of ZnO, 0 to 1.00% by weight of Al 2 O 3 , 0 to 0.97% by weight of As 2 O 3 , 0 to 1.00% by weight of La 2 O 3 , and 0 to 3.74% by weight of F 2. The present invention relates to a glass composition for encapsulating a plasma display panel, which has a lower yield point than the PbO-B 2 O 3 based or PbO-ZnO-B 2 O 3 based glass composition of the prior art and does not contain any PbO components. Therefore, it is possible to fundamentally solve problems such as environmental pollution and natural ecosystem destruction when disposing of the plasma display panel product, and it is effective to reduce the weight of the plasma display panel product.
Description
본 발명은 플라즈마 디스플레이 패널 봉착용 유리 조성물에 관한 것으로서, 특히 종래 기술의 주성분으로 사용되어 환경오염 및 제품의 무게 증가를 초래하던 PbO 성분을 포함하지 않는 동시에 낮은 굴복점을 가지는 플라즈마 디스플레이 패널 봉착용 유리 조성물에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a glass composition for sealing a plasma display panel. In particular, the present invention relates to a glass composition for sealing a plasma display panel, which does not include a PbO component, which is used as a main component of the prior art, resulting in environmental pollution and an increase in weight of a product. It relates to a composition.
일반적인 플라즈마 디스플레이 패널의 제조공정에서 전면 기판과 배면 기판 상에 격벽(barrier rib), 전극, 형광체층, 유전체층 등의 형성이 완료되면 상기 전면 기판과 배면 기판을 겹쳐 테두리를 유리로 봉착시키는데 이 때 사용되는 유리가 플라즈마 디스플레이 패널 봉착용 유리이다.In the manufacturing process of a general plasma display panel, when barrier ribs, electrodes, phosphor layers, and dielectric layers are formed on the front substrate and the rear substrate, the front substrate and the rear substrate are overlapped to seal the edges with glass. The glass used is glass for sealing a plasma display panel.
한편, 상기 전면 기판과 배면 기판의 테두리 봉착시 이미 형성되어 있는 격벽, 형광체층, 유전체층 등의 특성을 손상시키지 않기 위해서는 플라즈마 디스플레이 패널 봉착용 유리가 가능하면 낮은 굴복점을 가져야 한다.Meanwhile, the glass for sealing the plasma display panel should have a low yield point if possible in order not to impair the characteristics of the barrier ribs, the phosphor layer, the dielectric layer, and the like, which are already formed at the edge sealing of the front substrate and the rear substrate.
종래 기술에 의한 플라즈마 디스플레이 패널 봉착용 유리 조성물은 주로 PbO-B2O3계나 PbO-ZnO-B2O3계로 조성되는데 일례로 일본 NEG의 LS-0118, LS-0206, GA-0951, LS-7201, LS-7105 등이 이에 속하며, 그 굴복점은 약 340∼400℃로 알려져 있다.The glass composition for sealing a plasma display panel according to the prior art is mainly composed of PbO-B 2 O 3 system or PbO-ZnO-B 2 O 3 system. For example, LS-0118, LS-0206, GA-0951, LS- 7201, LS-7105, etc. belong to this, and the yield point is known as about 340-400 degreeC.
그러나, 상기와 같은 종래 기술에 의한 플라즈마 디스플레이 패널 봉착용 유리 조성물은 인체에 유해한 PbO 성분을 함유하고 있기 때문에 제품 폐기시 환경오염, 자연 생태계 파괴 등을 초래하여 생태계에 악영향을 미치고, 아울러 상기 PbO 성분은 분자량이 커서 플라즈마 디스플레이 패널 제품의 무게 증가를 초래하는 문제점이 있었다.However, since the glass composition for sealing a plasma display panel according to the related art includes a PbO component harmful to a human body, it causes environmental pollution and destruction of a natural ecosystem when the product is disposed of, thus adversely affecting the ecosystem, and at the same time, the PbO component The large molecular weight has a problem that causes an increase in the weight of the plasma display panel product.
본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 플라즈마 디스플레이 패널의 전면 기판과 배면 기판의 테두리 봉착에 적합한 낮은 굴복점을 가지면서 환경오염을 유발시키는 PbO 성분을 전혀 포함하지 않는 플라즈마 디스플레이 패널 봉착용 유리 조성물을 제공함에 그 목적이 있다.The present invention has been made to solve the above problems, the plasma display panel having a low yield point suitable for sealing the edge of the front substrate and the rear substrate of the plasma display panel and does not contain any PbO component that causes environmental pollution. The purpose is to provide a sealing glass composition.
상기와 같은 목적을 달성하기 위하여 본 발명에 의한 플라즈마 디스플레이 패널 봉착용 유리 조성물은 P2O559.90∼65.83 중량%와, Na2O 7.96∼11.49 중량%와, MgO 2.92∼3.96 중량%와, B2O32.00∼22.57 중량%와, Li2O 0∼5.49 중량%와, ZnO 0∼9.99 중량%와, Al2O30∼1.00 중량%와, As2O30∼0.97 중량%와, La2O30∼1.00 중량%와, F 0∼3.74 중량%로 조성된 것을 특징으로 한다.In order to achieve the above object, the glass composition for sealing a plasma display panel according to the present invention includes 59.90 to 65.83 wt% of P 2 O 5, 7.96 to 11.49 wt% of Na 2 O, 2.92 to 3.96 wt% of MgO, and B 2 O 3 2.00 to 22.57 wt%, Li 2 O 0 to 5.49 wt%, ZnO 0 to 9.99 wt%, Al 2 O 3 0 to 1.00 wt%, As 2 O 3 0 to 0.97 wt%, La 2 O 3 It is characterized by consisting of 0 to 1.00% by weight, and F 0 to 3.74% by weight.
본 발명은 실시예에 의하면 상기 P2O563.33 중량%와, 상기 Na2O 11.49 중량%와, 상기 MgO 3.96 중량%와, 상기 B2O32.00 중량%와, 상기 Li2O 5.49 중량%와, 상기 ZnO 9.99 중량%와, 상기 F 3.74 중량%로 조성되거나; 상기 P2O562.70 중량%와, 상기 Na2O 11.37 중량%와, 상기 MgO 3.92 중량%와, 상기 B2O31.98 중량%와, 상기 Li2O 5.44 중량%와, 상기 ZnO 9.89 중량%와, 상기 La2O31.00 중량%와, 상기 F 3.70 중량%로 조성되거나; 상기 P2O565.82 중량%와, 상기 Na2O 11.49 중량%와, 상기 MgO 3.96 중량%와, 상기 B2O32.00 중량%와, 상기 Li2O 5.49 중량%와, 상기 ZnO 7.50 중량%와, 상기 F 3.74 중량%로 조성되는 것이 바람직하다.According to the embodiment 63.33% by weight of the P 2 O 5 , 11.49% by weight of Na 2 O, 3.96% by weight of MgO, 2.00% by weight of B 2 O 3 , 5.49% by weight of Li 2 O And 9.99% by weight of ZnO and 3.74% by weight of F; 62.70 wt% of P 2 O 5 , 11.37 wt% of Na 2 O, 3.92 wt% of MgO, 1.98 wt% of B 2 O 3 , 5.44 wt% of Li 2 O, 9.89 wt% of ZnO And 1.00 wt% of La 2 O 3 and 3.70 wt% of F; 65.82% by weight of P 2 O 5 , 11.49% by weight of Na 2 O, 3.96% by weight of MgO, 2.00% by weight of B 2 O 3 , 5.49% by weight of Li 2 O, 7.50% by weight of ZnO And, it is preferred that the F 3.74% by weight.
이하, 본 발명에 의한 플라즈마 디스플레이 패널 봉착용 유리 조성물의 바람직한 실시예를 상세히 설명한다.Hereinafter, the preferred embodiment of the glass composition for sealing a plasma display panel according to the present invention will be described in detail.
본 발명의 바람직한 실시예에 의한 플라즈마 디스플레이 봉착용 유리 조성물은 P2O559.90∼65.83 중량%와, Na2O 7.96∼11.49 중량%와, MgO 2.92∼3.96 중량%와, B2O32.00∼22.57 중량%와, Li2O 0∼5.49 중량%와, ZnO 0∼9.99 중량%와, Al2O30∼1.00 중량%와, As2O30∼0.97 중량%와, La2O30∼1.00 중량%와, F 0∼3.74 중량%로 조성된다.Glass composition for sealing a plasma display according to a preferred embodiment of the present invention is 59.90 to 65.83% by weight of P 2 O 5, 7.96 to 11.49% by weight of Na 2 O, 2.92 to 3.96% by weight of MgO, and B 2 O 3 2.00 to 22.57 wt%, Li 2 O 0-5.49 wt%, ZnO 0-9.99 wt%, Al 2 O 3 0-1.00 wt%, As 2 O 3 0-0.97 wt%, La 2 O 3 0 And 1.00 wt% and F 0 to 3.74 wt%.
상기 P2O5는 유리를 구성하기 위한 필수성분인 유리형성산화물로서, 상기 P2O5의 함량이 전체 유리 조성물 100 중량%에 대해 59.90 중량% 미만이면 유리연화온도를 상승시키고, 65.83 중량%를 초과하면 화학적 내구성이 나빠진다.The P 2 O 5 is a glass forming oxide which is an essential component for constituting the glass. When the content of the P 2 O 5 is less than 59.90 wt% with respect to 100 wt% of the total glass composition, the glass softening temperature is increased, and 65.83 wt% If exceeded, the chemical durability worsens.
상기 Na2O와 Li2O는 알칼리금속산화물로서, 유리화를 용이하게 하고 연화온도를 저하시키기 위하여 사용하는 성분이다.The Na 2 O and Li 2 O are alkali metal oxides, which are components used to facilitate vitrification and lower the softening temperature.
상기 MgO는 알칼리토류금속산화물로서, 유리의 안정성을 향상시키고 내화학성을 증가시키기 위하여 사용하는 성분이다.The MgO is an alkaline earth metal oxide, and is a component used to improve the stability of the glass and to increase chemical resistance.
상기 B2O3는 유리의 안정화 및 균질화에 유리하고 화학적 내구성을 높이는데 특히 유효한 성분으로서, 상기 B2O3의 함량이 전체 유리 조성물 100 중량%에 대해 22.57 중량%를 초과하면 연화온도를 상승시키고 화학적 내구성을 열화시킨다.The B 2 O 3 is particularly effective for stabilizing and homogenizing glass and increasing chemical durability. When the content of the B 2 O 3 exceeds 22.57 wt% with respect to 100 wt% of the total glass composition, the softening temperature is increased. And degrade chemical durability.
상기 ZnO는 내실투성 및 내화학성을 향상시키기 위하여 사용하는 알칼리토류금속산화물로서, 상기 ZnO의 함량이 전체 유리 조성물 100 중량%에 대해 9.99 중량%를 초과하면 내실투성이 나빠져서 실투(의도하지 않은 결정화: devitrification)되기 쉽다.The ZnO is an alkaline earth metal oxide used to improve the devitrification resistance and chemical resistance, and when the content of the ZnO exceeds 9.99 wt% with respect to 100 wt% of the total glass composition, devitrification resistance is worsened, resulting in devitrification (unintended crystallization: devitrification It is easy to become
상기 As2O3는 유리의 용융시 기포를 제거하는 청징제(refining agent)로 쓰이는 성분이다.As 2 O 3 is a component used as a refining agent to remove bubbles when melting glass.
상기 La2O3는 화학적 내구성을 향상시키는데 유효한 성분으로서, 상기 La2O3의 함량이 전체 유리 조성물 100 중량%에 대해 1.00 중량%를 소량만 초과하여도 연화온도가 급격히 상승한다.The La 2 O 3 is an effective component for improving chemical durability, and the softening temperature rises rapidly even if the content of La 2 O 3 exceeds 1.00 wt.% Based on 100 wt.% Of the total glass composition.
상기 F는 액상온도를 저하시키고 내실투성을 향상시키는 성분으로서, 상기 F의 함량이 전체 유리 조성물 100 중량%에 대해 3.74 중량%를 초과하면 화학적 내구성이 악화된다.The F is a component that lowers the liquidus temperature and improves the devitrification resistance. When the content of the F exceeds 3.74 wt% with respect to 100 wt% of the total glass composition, chemical durability deteriorates.
제 1 내지 3 실시예First to third embodiment
먼저, 본 발명의 원료인 인산암모늄(NH4H2PO4), 질산나트륨(NaNO3), 붕사(Na2B4O7), 인산나트륨(Na3PO4·12H2O), 인산리튬(Li3PO4), 불화마그네슘(MgF2), 인산아연(Zn3(PO4)2·4H2O), BPO4, La2O3를 아래 표 1에 표시된 제 1, 2, 3 실시예의 각 조성비에 따라 칭량하여 교반기에 넣고 균질하게 혼합한다.First, the raw material of the present invention ammonium phosphate (NH 4 H 2 PO 4 ), sodium nitrate (NaNO 3 ), borax (Na 2 B 4 O 7 ), sodium phosphate (Na 3 PO 4 · 12H 2 O), lithium phosphate (Li 3 PO 4 ), magnesium fluoride (MgF 2 ), zinc phosphate (Zn 3 (PO 4 ) 2 · 4H 2 O), BPO 4 , La 2 O 3 to the 1, 2, 3 implementation shown in Table 1 below It weighs according to each composition ratio of the example, and puts into a stirrer and mixes homogeneously.
상기와 같이 혼합된 원료 혼합물(이하, 배치(batch)라 함)을 도가니에 넣고 약 1000℃까지 승온시켜 용융시킨 다음 시편을 제조하여 본 발명이 속하는 기술분야에서 통상적으로 사용되는 방법으로 각 실시예에 대한 물성(전이점과 굴복점)을 측정하여 아래 표 1에 기재하였다.The mixed raw material mixture (hereinafter, referred to as a batch) in the crucible was put in a crucible, heated to about 1000 ° C., melted, and then prepared to prepare a specimen, each of which is commonly used in the art. Physical properties (transition point and yield point) for the measurement are shown in Table 1 below.
표 1Table 1
상기 표 1에서 알 수 있듯이 본 발명의 제 1, 2, 3 실시예는 모두 종래 기술의 340∼400℃보다 낮은 굴복점을 가지면서 환경오염 및 플라즈마 디스플레이 패널 제품의 무게 증가를 초래하는 PbO 성분을 전혀 포함하지 않아 플라즈마 디스플레이 패널의 전면 기판과 배면 기판의 테두리를 봉착시키는데 적합하다.As can be seen in Table 1, the first, second, and third embodiments of the present invention all have PbO components that cause lowering of environmental pollution and weight of plasma display panel products while having lower yield points than 340 to 400 ° C. of the prior art. It is not included at all and is suitable for sealing the edges of the front substrate and the back substrate of the plasma display panel.
이와 같이 본 발명은 종래 기술의 PbO-B2O3계 또는 PbO-ZnO-B2O3계 유리 조성물보다 낮은 굴복점을 가지면서 동시에 PbO 성분을 전혀 포함하지 않기 때문에 플라즈마 디스플레이 패널 제품의 폐기시 환경오염 및 자연 생태계 파괴 등의 문제점을 근본적으로 해결할 수 있고, 플라즈마 디스플레이 패널 제품의 무게를 줄일 수 있는 효과가 있다.As described above, the present invention has a lower yield point than the PbO-B 2 O 3 -based or PbO-ZnO-B 2 O 3 -based glass compositions of the prior art and does not include any PbO components. It can fundamentally solve problems such as environmental pollution and destruction of natural ecosystems, and can reduce the weight of plasma display panel products.
아울러, 본 발명은 소수의 실시예로 설명되어 있지만 첨부된 청구 범위 내에서 그 이상의 실시예 조성이 가능하고, 당 업계에 숙련된 사람이면 본 발명을 다양하게 변화 및 변형시킬 수 있으나 그러한 변화 및 변형은 첨부된 본 발명의 청구 범위 영역에 속하는 것임을 알 수 있다.In addition, although the invention has been described in terms of a few embodiments, further embodiments of the invention can be made within the scope of the appended claims, and those skilled in the art can vary and modify the invention in various ways, but such changes and modifications may be made. It can be seen that belongs to the scope of the appended claims.
Claims (4)