KR0185507B1 - Process for the preparation of mineral powder - Google Patents

Abstract

(Ag) was attached to the inner surface of the alumina crucible (4), and 20 weight% of turquoise, 20 weight% of flamethrower, 5 weight% of jade, 5 weight% of white plaster and 50 weight% And fired powder of about 200 mesh on the inner surface of the heat transfer plate 2 and the inner surface of the heat transfer plate 2 is pressurized to about 200 mesh and then heated to about 1,000 ° C. through the heat transfer plate 2 for about 9 days, (4), which are obtained by pulverizing the above-mentioned five types of ores in an amount of about 325 meshes or more, and a multipurpose ore which releases a large amount of anion and oxygen heat.

Description

Multipurpose ore min

FIG. 1 is a schematic view showing a furnace for producing a multipurpose ore powder of the present invention,

FIG. 2 is a block diagram showing a process for producing the versatile stone powder of the present invention.

DESCRIPTION OF THE REFERENCE NUMERALS

2: heat transfer plate 4: inside

5: inner wall

The present invention relates to a versatile feldspar (ore powder) which emits a large amount of far infrared rays and anion and oxygen heat.

The space on earth we live in is the space of the earth's magnetic force, and the earth is essentially a huge photon stone. Earth is one of the ninth planets of the solar system.

In addition to light emission and heat generation, the sun launches a kind of solar energy (Ki), and the wavelength of the air is 6 million meters, which is also called super low energy (Ki). The Jaffa of the sun constantly shone on the earth and made the earth become a lump of glory. Then the earth was able to emit a ziji wave (energy 气). The solar energy wave is a natural Jaffa. This keeps our living space covered enough to protect and maintain our human health, and at the same time keeps everything alive and grows constantly vividly.

If one day suddenly disappears, the creatures will be destroyed.

Natural ziapa (energy 气) is so important, but it is very weak for people who are fine but weak for healthy people and natural ziapa (energy 气) is not enough. Thus, we have developed a special furnace (baking pot) by selecting various kinds of special semi-precious stones and ores that have a lot of natural energy waves (radiant), and invented ore powders that emit far infrared ray, anion and oxygen heat.

This natural geophysical energy device includes a far infrared ray, an anion and an oxygen. Generally speaking, infrared is an electromagnetic wave having a wavelength ranging from 0.76 to 1.5 microns and a wavelength ranging from 0.76 to 1000 microns. Micron is called mid-infrared, and 5.6 to 1000 microns is far-infrared (Far Infrared Business, Sunmark Publishing, December 25, 1988).

Far infrared rays are used in a wide variety of applications such as heating, drying, aging, nourishing, analgesic action, and sweating and analgesic action which, when applied to the human body, It is known. In addition, there have been many attempts to use far-infrared rays in the health industry or the food industry since the publication of a clinical experiment that shows a good effect on the biorhythm of the human body (Japanese Far Infrared Radiation Committee, Far Infrared Heat Theory and Practice pp226 ~ 230).

Thus, nowadays products using far-infrared rays are being produced in large quantities. For example, far infrared saunas can enhance the sweating action of the human body at a temperature lower than that of steam sauna water.

In other words, steam sauna sauna can not withstand long time in the bathtub because it supplies high temperature steam (about 70 ~ 80 ℃) to the sauna room. However, even if the inside temperature of the far infrared sauna room is maintained at about 40 ° C, the sweating action is higher than that of the steam sauna bath.

This is due to the fact that far-infrared rays are absorbed by the human body and cause self-heating by the resonance action of water molecules in the human body.

It is well known that anions are opposite to cations. According to the theory that Bert Sakman and E. Necher have jointly published a Nobel Prize in physiology-medicine in 1991 for the human body, Movement can identify disease structure.

In other words, there is a growing interest in anion in the intention of supplementing anion with food or living peripheral equipment to compensate for the increase in the number of positive ions due to external or internal influences of the entirely neutral human body.

It is known that when anion is appropriately added to a human body having a large number of positive ions, autonomic regulation, blood purification, cell activation and cell resistance enhancement are known.

Various ions in the air change according to the weather conditions. When passing through low pressure such as a discontinuous cold wire, positive ions are increased. As a result, negative ions are decreased in the human body and positive ions are increased. Therefore, It is known that the incidence of diseases such as stroke increases.

A material that emits far-infrared rays using a material called a conventional product name bioceramic has been put on the market. This is achieved by mixing minerals having specific functions in ceramic materials or adding chemicals to maximize the effects of certain functions such as antimicrobial, anti-discoloration, and deodorization, and are supplied in powder or granular form or liquid form.

However, conventional far-infrared ray emitting materials have disadvantages of emitting only far-infrared rays or emitting far-infrared rays. In addition, since various chemical substances are mixed, there is a problem that it is difficult to utilize chemical substances in health foods to be avoided.

In particular, the ore has oxygen heat. In the quarse ore ore used in the present invention, a large amount of oxygen heat is released. For example, there is a tendency to bake meat or stone rice, taste of meat, What is not done is due to the heat of oxygen coming from the ore. When the heat is applied to this ore, the oxygen heat is generated from about 70 to 100 shell cells of the human body. The cells are very small in size, and are measured in micron units of 1 / 1,000th of a millimeter. The thickness of the cells is in microns The length is very long. Muscle cells are usually 1 to 40 mm, and thighs are 30 mm. The nerve cells are 2m long, and the shape is also very different. The skin cells are wide and flat like a sidewalk block, the nerve cells are thin and long like a thread, the red blood cells are donut shaped in the center and the white blood cells have no uniform shape. These various cells start from one cell at first, that is, a single cell called a fertilized egg that is made up of a sperm and an egg, and the number of cells is increased and changed into cells with various shapes and functions. These cells release a large amount of mysterious natural oxygen heat, which is a great help to the cells of the natural ore oxygen heat to the tissues of the body.

Accordingly, it is an object of the present invention to provide a versatile ore having a large amount of far infrared rays, anions, and line heat, which is made of only natural ores excluded from chemical substances.

BRIEF DESCRIPTION OF THE DRAWINGS FIG.

Referring to FIG. 1, a furnace 1 for producing a multipurpose stone according to the present invention comprises a heat transfer plate 2, an inner furnace 4, and an inner wall 5 coated on the inner surface with silver (Ag) have.

The heat transfer plate 2 can be heated by electricity or heated by gas or other fuel.

Inside (4) is furnace furnace, in which 20% by weight of turquoise, 20% by weight of flour, 5% by weight of jade, 5% by weight of plagioclase and 50% Crush it with a mesh and charge it. Reference numeral 6 denotes a mixed powder of the ores.

Between the inner surface of the heat transfer plate 2 and the outer surface of the inner heat transfer plate 4, a disintegrator 3 pulverized to about 200 mesh is charged and then heated through the heat transfer plate 2 for about 9 days at about 1000 ° C. Then, it starts to overheat at the initial temperature of 1000 ° C., and the temperature rises to about 1500 ° C. due to the self-heating heat (ore heat) during the superheating process. The above-mentioned five kinds of ores in the inside (4) are thermally denatured due to high heat, and the heavy metals harmful to the human body are burned and disappear. As shown in Table 1, 20 kinds of natural minerals are mainly composed and found in the ores And 36 kinds of mineral water.

After the burns are burned, they are slowly cooled.

As shown in FIG. 2, this lump is crushed again to about 325 mesh or more.

[Table 1]

Test Result (Test Resu1t)

Analysis of the gates of the components according to the present invention is as shown in Table 1, which is in accordance with the test report of the attached Korean Chemical Testing and Research Institute.

The ores in Table 1 according to the present invention emit far infrared ray, anion and oxygen heat which are very beneficial to the human body.

The multipurpose stone according to the embodiment of the present invention has a far infrared ray emission rate of 99.0% or more at a wavelength of 8 to 14 microns at 37 ° C, more than 600,000 or more anions per kg of ore minerals, and a calorific value of 56 kcal. The test method was KS.A 5302-91 for far infrared rays and MDK-01C for anion measurement device from Schomandl, Germany. The calorific value of oxygen was measured by KS.E 3707-90.

The pH of the above-mentioned limonite is 7.4 to 7.9.

The multipurpose stone according to the present invention is a mineral ore which generates a large amount of far infrared rays, anion and oxygen heat and is used as food or oil, cosmetics, building materials, electronic products, wallpaper, physiotherapeutic apparatuses, pharmaceuticals plastic, glass, steel, , Soap, health water, medical instruments, health fibers, various types of hot air balloon products, paints, and the like.

Claims (1)

A silver (Ag) green sheet was attached to the inner surface of the alumina crucible (4), and 20 wt% of turquoise, 20 wt% of flamethrower, 5 wt% of oxalate, 5 wt% of white water and 50 wt% Crushed and charged, and disintegrated into 200 meshes between the inner surface of the heat transfer plate 2 and the outer surface of the inner heat transfer plate 4, and then heated at 1000 캜 for 9 days through the heat transfer plate 2, The heat-denatured five ore minerals are again pulverized into 325 meshes, and the minerals ore and the minerals ore ore ore ore ore ore ore ore ore ore ore ore ore ore ore ore.