JPWO2020026529A1 - Pseudo-skin film, its manufacturing method and usage, and a cosmetic kit having the pseudo-skin film. - Google Patents
Pseudo-skin film, its manufacturing method and usage, and a cosmetic kit having the pseudo-skin film. Download PDFInfo
- Publication number
- JPWO2020026529A1 JPWO2020026529A1 JP2020534057A JP2020534057A JPWO2020026529A1 JP WO2020026529 A1 JPWO2020026529 A1 JP WO2020026529A1 JP 2020534057 A JP2020534057 A JP 2020534057A JP 2020534057 A JP2020534057 A JP 2020534057A JP WO2020026529 A1 JPWO2020026529 A1 JP WO2020026529A1
- Authority
- JP
- Japan
- Prior art keywords
- film
- pseudo
- skin
- skin film
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
貼り付け時及び貼り付け後のエア溜まりの不具合を改善し、かつ、自然な仕上がりを呈し得る、疑似皮膚フィルムを提供する。本発明の疑似皮膚フィルムは、JIS K6253に準拠したデュロメータータイプA硬度計によるゴム硬度が、20以下であり、膜厚が、600μm以下であり、貫通孔が、3〜500000個/cm2の割合で配置されており、かつ、貫通孔の面積が、70〜283000μm2/個である。Provided is a pseudo-skin film that can improve the problem of air accumulation at the time of sticking and after sticking and can give a natural finish. The pseudo-skin film of the present invention has a rubber hardness of 20 or less, a film thickness of 600 μm or less, and through holes at a ratio of 3 to 500,000 pieces / cm2 by a durometer type A hardness tester conforming to JIS K6253. It is arranged and the area of the through hole is 70 to 283000 μm 2 / piece.
Description
本発明は、疑似皮膚フィルム、その製造方法及び使用方法、並びに該疑似皮膚フィルムを有する化粧キットに関する。 The present invention relates to a pseudo-skin film, a method for producing and using the pseudo-skin film, and a cosmetic kit having the pseudo-skin film.
年をとるにつれて皮膚老化の1つの現象として皺が増加するが、美容等の観点から、特に、女性において皺の防止及び改善に対する関心が非常に高まっている。とりわけ、加齢を含めた肌の悩みの中で形状変化が顕著に表れる部位として唇が挙げられる。唇に関する悩みには、唇の荒れ又はくすみなどとともに、加齢に伴う唇の皺の多さ又はふっくら感の低下なども挙げられる。 Wrinkles increase as one of the phenomena of skin aging as we get older, but from the viewpoint of cosmetology and the like, there is a great deal of interest in preventing and improving wrinkles, especially in women. In particular, the lips can be mentioned as a part where the shape change is remarkable in the troubles of the skin including aging. Problems related to the lips include roughness or dullness of the lips, as well as a large number of wrinkles or a decrease in the feeling of plumpness with aging.
特許文献1及び2には、支持体層、粘着剤層及びセパレータ層をこの順に積層して備える、口唇用貼付材が開示されている。 Patent Documents 1 and 2 disclose a lip patch having a support layer, an adhesive layer, and a separator layer laminated in this order.
特許文献3には、皮膚に貼る基材であって、ポリウレタン、ポリオレフィン、又はポリアクリレートを含む可撓性材料製である基材と、基材上に形成されると共にスチレン樹脂、エポキシ樹脂又はアクリル樹脂を含み、着色材料をその上に担持する画像形成層であって、皮膚の修整カラー画像がその上に印刷されている画像形成層と、画像形成層に接触して形成されたホットメルト接着剤層と、ホットメルト接着剤層上に形成された透水保護層とを備える、皮膚の欠陥を隠蔽する化粧用積層構造体が開示されている。 Patent Document 3 describes a base material to be attached to the skin, which is a base material made of a flexible material containing polyurethane, polyolefin, or polyacrylate, and a styrene resin, epoxy resin, or acrylic, which is formed on the base material and is formed on the base material. An image-forming layer containing a resin and supporting a coloring material on the image-forming layer, on which a modified color image of the skin is printed, and a hot-melt adhesive formed in contact with the image-forming layer. A cosmetic laminated structure that conceals skin imperfections is disclosed, which comprises an agent layer and a water permeable protective layer formed on the hot melt adhesive layer.
特許文献1〜3に記載される口唇用貼付材及び構造体は、皮膚へ適用した場合、貼り付け不良又は皮膚呼吸に起因するエア溜まりが、これらの部材と皮膚との間で発生するという問題があった。 When the lip patch and the structure described in Patent Documents 1 to 3 are applied to the skin, there is a problem that air pooling due to poor sticking or cutaneous respiration occurs between these members and the skin. was there.
したがって、本発明の主題は、貼り付け時及び貼り付け後のエア溜まりの不具合を改善し、かつ、自然な仕上がりを呈し得る、疑似皮膚フィルムを提供することである。 Therefore, an object of the present invention is to provide a pseudo-skin film capable of improving the defect of air accumulation at the time of application and after application and exhibiting a natural finish.
〈態様1〉
JIS K6253に準拠したデュロメータータイプA硬度計によるゴム硬度が、20以下であり、
膜厚が、600μm以下であり、
貫通孔が、3〜500000個/cm2の割合で配置されており、かつ、
前記貫通孔の面積が、70〜283000μm2/個である、
疑似皮膚フィルム。
〈態様2〉
前記膜厚が、50〜200μmである、態様1に記載のフィルム。
〈態様3〉
前記疑似フィルムを構成する材料が、ウレタンゴム、オレフィンゴム、シリコーンゴム、アクリルゴム、天然ゴム、又はα−ゲルである、態様1又は2に記載のフィルム。
〈態様4〉
体表への貼り付け用である、態様1〜3のいずれか一項に記載のフィルム。
〈態様5〉
前記体表が、顔表面上の皮膚、耳表面上の皮膚、又は爪である、態様4に記載のフィルム。
〈態様6〉
剥離シートをさらに備えている、態様1〜5のいずれか一項に記載のフィルム。
〈態様7〉
非粘着性である、態様1〜6のいずれか一項に記載のフィルム。
〈態様8〉
態様1〜7のいずれか一項に記載のフィルムを有している、化粧キット。
〈態様9〉
密着剤をさらに有している、態様8に記載の化粧キット。
〈態様10〉
前記密着剤が、ポリブテン及びポリイソブテンから選ばれる少なくとも一種である、態様9に記載の化粧キット。
〈態様11〉
前記密着剤が、保湿成分をさらに含む、態様9又は10に記載の化粧キット。
〈態様12〉
射出成型法、カレンダー成型法、又はコンプレッション成形法によってフィルムを形成し、そして
前記フィルムにレーザーを照射して貫通孔を形成する、
態様1〜7のいずれか一項に記載の疑似皮膚フィルムの製造方法。
〈態様13〉
態様1〜7のいずれか一項に記載の疑似皮膚フィルムを体表に貼り付ける、疑似皮膚フィルムの使用方法。
〈態様14〉
体表に密着剤を適用した後に、前記疑似皮膚フィルムを体表に貼り付ける、態様13に記載の使用方法。
〈態様15〉
前記体表に貼り付けた後に、前記疑似皮膚フィルムにグロス、口紅、マニキュア又はリキッドファンデーションを適用する、態様13又は14に記載の使用方法。<Aspect 1>
The rubber hardness by the durometer type A hardness tester conforming to JIS K6253 is 20 or less.
The film thickness is 600 μm or less,
Through holes are arranged at a ratio of 3 to 500,000 pieces / cm 2, and
The area of the through hole is 70 to 283000 μm 2 / piece.
Pseudo skin film.
<Aspect 2>
The film according to aspect 1, wherein the film thickness is 50 to 200 μm.
<Aspect 3>
The film according to aspect 1 or 2, wherein the material constituting the pseudo film is urethane rubber, olefin rubber, silicone rubber, acrylic rubber, natural rubber, or α-gel.
<Aspect 4>
The film according to any one of aspects 1 to 3, which is used for attachment to a body surface.
<Aspect 5>
The film according to aspect 4, wherein the body surface is skin on the face surface, skin on the ear surface, or nails.
<Aspect 6>
The film according to any one of aspects 1 to 5, further comprising a release sheet.
<Aspect 7>
The film according to any one of aspects 1 to 6, which is non-adhesive.
<Aspect 8>
A cosmetic kit comprising the film according to any one of aspects 1 to 7.
<Aspect 9>
The cosmetic kit according to aspect 8, further comprising an adhesive.
<Aspect 10>
The cosmetic kit according to aspect 9, wherein the adhesive is at least one selected from polybutene and polyisobutene.
<Aspect 11>
The cosmetic kit according to aspect 9 or 10, wherein the adhesive further contains a moisturizing ingredient.
<Aspect 12>
A film is formed by injection molding, calendar molding, or compression molding, and the film is irradiated with a laser to form through holes.
The method for producing a pseudo-skin film according to any one of aspects 1 to 7.
<Aspect 13>
A method for using a pseudo-skin film, wherein the pseudo-skin film according to any one of aspects 1 to 7 is attached to a body surface.
<Aspect 14>
The method of use according to aspect 13, wherein the pseudo-skin film is attached to the body surface after applying the adhesive to the body surface.
<Aspect 15>
The method of use according to aspect 13 or 14, wherein a gloss, lipstick, nail polish or liquid foundation is applied to the pseudo-skin film after being attached to the body surface.
本発明によれば、貼り付け時及び貼り付け後のエア溜まりの不具合を改善し、かつ、自然な仕上がりを呈し得る、疑似皮膚フィルムを提供することができる。 According to the present invention, it is possible to provide a pseudo-skin film that can improve the problem of air accumulation during and after application and can exhibit a natural finish.
以下、本発明の実施の形態について詳述する。本発明は、以下の実施の形態に限定されるものではなく、発明の本旨の範囲内で種々変形して実施できる。 Hereinafter, embodiments of the present invention will be described in detail. The present invention is not limited to the following embodiments, and can be variously modified and implemented within the scope of the gist of the invention.
本発明の疑似皮膚フィルムは、JIS K6253に準拠したデュロメータータイプA硬度計によるゴム硬度が、20以下であり、膜厚が、600μm以下であり、貫通孔が、3〜500000個/cm2の割合で配置されており、かつ、該貫通孔の面積が、70〜283000μm2/個である。The pseudo-skin film of the present invention has a rubber hardness of 20 or less, a film thickness of 600 μm or less, and a ratio of 3 to 500,000 through holes / cm 2 by a durometer type A hardness tester conforming to JIS K6253. And the area of the through hole is 70 to 283000 μm 2 / piece.
本発明の疑似皮膚フィルムによれば、貼り付け時及び貼り付け後のエア溜まりの不具合を改善し、かつ、自然な仕上がりを呈することができる。 According to the pseudo-skin film of the present invention, it is possible to improve the problem of air accumulation at the time of sticking and after sticking, and to exhibit a natural finish.
原理によって限定されるものではないが、本発明の疑似皮膚フィルムが、貼り付け時及び貼り付け後のエア溜まりの不具合を改善し、かつ、自然な仕上がりを呈し得る作用原理は、以下のとおりであると考えている。 Although not limited by the principle, the principle of action that the pseudo-skin film of the present invention can improve the problem of air accumulation at the time of sticking and after sticking and give a natural finish is as follows. I think there is.
本発明の疑似皮膚フィルムは、特定の硬度を有しているため、皮膚における皺等の凹凸部位又は皮膚の動き等に対して追従させやすく、また、特定の厚さを有しているため、ふっくら感等の見栄えを自然と違和感なく提供することができるものと考えている。 Since the pseudo-skin film of the present invention has a specific hardness, it can easily follow uneven parts such as wrinkles on the skin or the movement of the skin, and has a specific thickness. We believe that it is possible to provide a plump appearance and other appearance without any discomfort.
本発明の疑似皮膚フィルムは、特定の大きさの貫通孔が特定の割合で形成されているため、見た目の自然さに対して悪影響を及ぼすことなく、通気性を呈することができ、その結果、貼り付け時又は貼り付け後の皮膚呼吸等に伴うエア(気泡)溜まりの発生を低減させることができ、自然な仕上がりを持続させることができるものと考えている。また、エア溜まりの改善は、フィルムと皮膚との接触面積の増大にもつながるため、フィルムの皮膚に対する密着性を改善させることもできると考えている。 Since the pseudo-skin film of the present invention has through holes of a specific size formed in a specific ratio, it can exhibit breathability without adversely affecting the naturalness of appearance, and as a result, it can exhibit breathability. It is believed that it is possible to reduce the generation of air (air bubbles) accumulation due to skin respiration during or after application, and to maintain a natural finish. Further, since the improvement of the air pool also leads to an increase in the contact area between the film and the skin, it is considered that the adhesion of the film to the skin can be improved.
この他、特定の大きさの貫通孔を有する本発明の疑似皮膚フィルムは、通気性とオクルージョン効果(肌から水分が抜けることを防ぐ効果)とのバランスに優れることから、係るフィルムを皮膚に適用した場合に、肌のかさつき又は荒れ等も改善し得るものと考えている。 In addition, the pseudo-skin film of the present invention having a through hole of a specific size has an excellent balance between breathability and an occlusion effect (effect of preventing water from escaping from the skin), and therefore, the film is applied to the skin. In that case, it is considered that the dryness or roughness of the skin can be improved.
疑似皮膚フィルムに形成される特定の貫通孔は、疑似皮膚フィルムの付着性を改良する。これは、例えば、唇に適用した密着剤が、貫通孔内に侵入してフィルムに付着しやすくなることによると考えている。また、例えば、フィルムがシリコーンゴムのような材料から形成された場合でも、フィルムへの付着性が増すため、グロス、口紅、マニキュア、リキッドファンデーション等の塗布剤の付着性も改良される。 The specific through holes formed in the pseudo-skin film improve the adhesion of the pseudo-skin film. It is considered that this is because, for example, the adhesive applied to the lips penetrates into the through hole and easily adheres to the film. Further, for example, even when the film is formed of a material such as silicone rubber, the adhesiveness to the film is increased, so that the adhesiveness of a coating agent such as gloss, lipstick, nail polish, or liquid foundation is also improved.
さらに、本発明の疑似皮膚フィルムは、特定の貫通孔を有しているため、係る貫通孔を有さないフィルムに比べ、柔軟性を向上させることができるとともに、硬度を低減させることができるものと考えている。その結果、唇のような比較的動きの多い部位に対しても伸び縮みしやすくなるため、ヨレ又は剥がれ等の不具合を低減することができる。また、特定の貫通孔を形成することで、比較的硬くて従来は疑似皮膚フィルムに適していなかった材料であっても、係るフィルムの材料として使用することが可能となった。 Further, since the pseudo-skin film of the present invention has a specific through hole, the flexibility can be improved and the hardness can be reduced as compared with the film having no such through hole. I believe. As a result, it becomes easy to expand and contract even on a part having a relatively large movement such as lips, so that problems such as twisting or peeling can be reduced. Further, by forming a specific through hole, even a material that is relatively hard and is not suitable for a pseudo-skin film in the past can be used as a material for such a film.
《疑似皮膚フィルム》
〈ゴム硬度〉
本発明の疑似皮膚フィルムにおけるJIS K6253に準拠したデュロメータータイプA硬度計によるゴム硬度は、20以下である。係る硬度としては、皮膚への追従性等の観点から、15以下又は10以下であることが好ましく、また、強度等の観点から、1以上、2以上、又は3以上であることが好ましい。ここで、係るゴム硬度とは、疑似皮膚フィルムを構成する材料を用いて調製した厚さ6.0mm以上の試験片、又は、疑似フィルムを積層して調製した厚さ6.0mm以上の試験片におけるゴム硬度を意図することができる。《Pseudo-skin film》
<Rubber hardness>
The rubber hardness of the pseudo-skin film of the present invention by a durometer type A hardness tester conforming to JIS K6253 is 20 or less. The hardness is preferably 15 or less or 10 or less from the viewpoint of followability to the skin, and is preferably 1 or more, 2 or more, or 3 or more from the viewpoint of strength or the like. Here, the said rubber hardness is a test piece having a thickness of 6.0 mm or more prepared by using a material constituting the pseudo-skin film, or a test piece having a thickness of 6.0 mm or more prepared by laminating pseudo-films. The rubber hardness in can be intended.
〈膜厚〉
本発明の疑似皮膚フィルムの膜厚は、600μm以下である。係るフィルムの膜厚は、フィルムを貼り付ける部位又は使用目的等に応じて適宜調整することができ、次のものに限定されないが、例えば、500μm以下、400μm以下、300μm以下、又は200μm以下とすることもでき、また、50μm以上、70μm以上、又は100μm以上とすることもできる。<Film thickness>
The film thickness of the pseudo-skin film of the present invention is 600 μm or less. The film thickness of the film can be appropriately adjusted according to the site to which the film is attached, the purpose of use, etc., and is not limited to the following, but is, for example, 500 μm or less, 400 μm or less, 300 μm or less, or 200 μm or less. It can also be 50 μm or more, 70 μm or more, or 100 μm or more.
特に、唇のように頻繁に動くような部位に対し、唇をふっくらと見せることを目的にしてフィルムを使用する場合には、膜厚は、300μm以下、又は200μm以下とすることができ、また、50μm以上、70μm以上、又は100μm以上とすることができる。 In particular, when the film is used for the purpose of making the lips look plump for a part that moves frequently such as the lips, the film thickness can be 300 μm or less, or 200 μm or less, and also. , 50 μm or more, 70 μm or more, or 100 μm or more.
ここで、膜厚とは、精密厚み測定機(株式会社尾崎製作所製のPEACOCKダイヤルシックネスゲージ0.01mmタイプ)を使用し、疑似皮膚フィルムの任意の部分の膜厚を5回測定して算出した平均値であり、また、疑似皮膚フィルムが剥離シートを備える場合には、係る剥離シートの厚さを除いた状態の膜厚を意図している。 Here, the film thickness was calculated by measuring the film thickness of an arbitrary part of the pseudo-skin film five times using a precision thickness measuring machine (PEACOCK dial thickness gauge 0.01 mm type manufactured by Ozaki Seisakusho Co., Ltd.). It is an average value, and when the pseudo-skin film includes a release sheet, the film thickness is intended excluding the thickness of the release sheet.
本発明の疑似皮膚フィルムは、その適用部位又は使用目的に応じて、膜厚をフィルム面内において変動させてもよい。例えば、フィルムを唇に適用する場合には、係るフィルムの中央部を厚くし、周縁部分を薄くしてもよい。係る構成にすることによって、皮膚とフィルムとの境目を目立ちにくくすることができることに加え、唇のふっくら感をより向上させることができる。なお、この場合の、上記膜厚は、疑似皮膚フィルムの一番厚い部分(最厚部分)において上記と同様に測定した平均値である。 In the pseudo-skin film of the present invention, the film thickness may be varied in the film surface depending on the application site or the purpose of use. For example, when the film is applied to the lips, the central portion of the film may be thickened and the peripheral portion may be thinned. With such a configuration, the boundary between the skin and the film can be made inconspicuous, and the fluffy feeling of the lips can be further improved. In this case, the film thickness is an average value measured in the same manner as above in the thickest portion (thickest portion) of the pseudo-skin film.
疑似皮膚フィルムは、その適用部位に応じ、皺又は皮膚の動きに追従しやすくするために、例えば、唇又は目元等の皮膚に貼り付ける面に対し、スリット状の切込み線等を入れてもよい。 Depending on the application site, the pseudo-skin film may have slit-shaped cut lines or the like on the surface to be attached to the skin such as the lips or the eyes in order to easily follow the movement of wrinkles or skin. ..
〈貫通孔〉
本発明の疑似皮膚フィルムは、貫通孔が、3〜500000個/cm2の割合で配置されており、かつ、係る貫通孔は、70〜283000μm2/個の面積を有している。<Through hole>
In the pseudo-skin film of the present invention, through holes are arranged at a ratio of 3 to 500,000 pieces / cm 2 , and the through holes have an area of 70 to 283,000 μm 2 / piece.
(貫通孔の割合)
貫通孔の割合としては、エア溜まりの改善性、侵入性、柔軟性等の観点から、3個/cm2以上、5個/cm2以上、10個/cm2以上、30個/cm2以上、50個/cm2以上、100個/cm2以上、又は1000個/cm2以上とすることができ、また、500000個/cm2以下、450000個/cm2以下、400000個/cm2以下、200000個/cm2以下、100000個/cm2以下、又は50000個/cm2以下とすることができる。(Ratio of through holes)
The ratio of through holes is 3 pieces / cm 2 or more, 5 pieces / cm 2 or more, 10 pieces / cm 2 or more, 30 pieces / cm 2 or more from the viewpoint of improving air accumulation, permeability, flexibility, etc. , 50 pcs / cm 2 or more, 100 pcs / cm 2 or more, or 1000 pcs / cm 2 or more, and 500,000 pcs / cm 2 or less, 450,000 pcs / cm 2 or less, 400,000 pcs / cm 2 or less , 200,000 pieces / cm 2 or less, 100,000 pieces / cm 2 or less, or 50,000 pieces / cm 2 or less.
貫通孔は、上記の割合で形成されている限り、疑似皮膚フィルムの全面に均一に若しくは不均一に分布していてもよく、又は、疑似皮膚フィルムの一部に均一に若しくは不均一に分布していてもよい。ここで、疑似皮膚フィルムの一部に貫通孔が形成されている場合には、1箇所以上、2箇所以上、又は3箇所以上で、上記の割合を満足していればよい。 The through holes may be uniformly or non-uniformly distributed over the entire surface of the pseudo-skin film, or may be uniformly or non-uniformly distributed over a part of the pseudo-skin film as long as they are formed in the above proportions. You may be. Here, when a through hole is formed in a part of the pseudo-skin film, the above ratio may be satisfied at one or more, two or more, or three or more.
(貫通孔の面積)
貫通孔の面積としては、エア溜まりの改善性、侵入性、柔軟性等の観点から、70μm2/個以上、80μm2/個、100μm2/個、又は150μm2/個以上とすることができ、また、283000μm2/個以下、233000μm2/個以下、183000μm2/個以下、又は133000μm2/個以下とすることができる。ここで、貫通孔の面積とは、疑似皮膚フィルムの上面及び底面における貫通孔の面積のうち最小の面積を意図する。例えば、貫通孔が、円錐の上部を底面に対して平行に切断した円錐台のような形状の場合には、係る円錐台の上面の面積を指し、また、上面及び底面の面積が等しい円柱形状の場合には、上面又は底面のいずれかの面積を指す。(Area of through hole)
The area of the through hole can be 70 μm 2 / piece or more, 80 μm 2 / piece, 100 μm 2 / piece, or 150 μm 2 / piece or more from the viewpoint of improving air accumulation, penetrability, flexibility, and the like. Further, it can be 283000 μm 2 / piece or less, 233000 μm 2 / piece or less, 183000 μm 2 / piece or less, or 133000 μm 2 / piece or less. Here, the area of the through hole is intended to be the smallest area of the area of the through hole on the upper surface and the bottom surface of the pseudo-skin film. For example, when the through hole has a shape like a truncated cone in which the upper part of the cone is cut parallel to the bottom surface, it refers to the area of the upper surface of the cone and the cylindrical shape in which the areas of the upper surface and the bottom surface are equal. In the case of, it refers to the area of either the upper surface or the bottom surface.
(貫通孔の形状)
貫通孔の形状としては、エア溜まりの改善性等の性能が発揮されている限り、特に限定されるものではないが、例えば、略円柱状、略楕円柱状、底面が多角形である略角柱状、略円錐台状、略楕円錐台状、底面が多角形である略角錐台状などを挙げることができる。中でも、生産性、エア溜まりの改善性等の観点から、略円柱状及び略円錐台状であることが好ましい。ここで、「略」とは、製造誤差などによって生じるバラつきを含むことを意味し、±約20%程度の変動が許容されることを意図する。(Shape of through hole)
The shape of the through hole is not particularly limited as long as the performance such as improvement of air accumulation is exhibited, but for example, a substantially columnar shape, a substantially elliptical columnar shape, and a substantially angular columnar shape having a polygonal bottom surface. , A substantially truncated cone, a substantially elliptical cone, a substantially angular cone with a polygonal bottom surface, and the like. Above all, from the viewpoint of productivity, improvement of air accumulation, etc., it is preferable that the shape is substantially columnar or substantially truncated cone. Here, "omitted" means that variations caused by manufacturing errors and the like are included, and it is intended that fluctuations of about ± 20% are allowed.
貫通孔の形状が、略円柱状及び略円錐台状の場合には、エア溜まりの改善性等の観点から、フィルム上面及び底面における係る貫通孔の略円形状部のうちの最小の直径は、0.01mm以上、0.02mm以上、又は0.03mm以上であることが好ましく、また、0.60mm以下、0.50mm以下、又は0.40mm以下であることが好ましい。 When the shape of the through hole is substantially columnar or substantially conical cone, the minimum diameter of the substantially circular portion of the through hole on the upper surface and the bottom surface of the film is set from the viewpoint of improving air accumulation and the like. It is preferably 0.01 mm or more, 0.02 mm or more, or 0.03 mm or more, and preferably 0.60 mm or less, 0.50 mm or less, or 0.40 mm or less.
〈材料〉
本発明の疑似皮膚フィルムの材料としては、ゴム硬度が20以下となるような材料であればいかなるものでもよく、次のものに限定されないが、例えば、オレフィンゴム、ウレタンゴム、シリコーンゴム、アクリルゴム等の合成ゴム、α−ゲルのような弾性を呈し得るゲル状物、天然ゴムなどを挙げることができる。中でも、肌への安全性、耐久性、透明性等の観点から、シリコーンゴムが好ましい。これらの材料は、単独で又は複数組み合わせて使用することができる。また、疑似皮膚フィルムは、これらの材料の単一層又は積層構造であってもよい。<material>
The material of the pseudo-skin film of the present invention may be any material as long as it has a rubber hardness of 20 or less, and is not limited to the following, but for example, olefin rubber, urethane rubber, silicone rubber, acrylic rubber. Synthetic rubber such as α-gel, gel-like material capable of exhibiting elasticity such as α-gel, natural rubber and the like can be mentioned. Of these, silicone rubber is preferable from the viewpoint of skin safety, durability, transparency and the like. These materials can be used alone or in combination of two or more. The pseudo-skin film may also have a single layer or laminated structure of these materials.
好ましい材料であるシリコーンゴムとしては、次のものに限定されないが、例えば、加熱によって短時間で成形できる等の観点から、付加(ヒドロシリル化)反応硬化型のシリコーンゴム組成物又は有機過酸化物硬化型のシリコーンゴム組成物を硬化して得られたものが好ましい。 Silicone rubber, which is a preferable material, is not limited to the following, but is, for example, an addition (hydrosilylation) reaction-curable silicone rubber composition or organic peroxide curing from the viewpoint of being able to be molded in a short time by heating. The one obtained by curing the silicone rubber composition of the mold is preferable.
付加反応硬化型のシリコーンゴム組成物としては、公知の組成のものを使用することができ、例えば、ビニル基に代表されるアルケニル基を1分子中に2個以上有するアルケニル基含有オルガノポリシロキサンと、SiH基を2個以上、好ましくは3個以上有するオルガノハイドロジェンポリシロキサン(通常、アルケニル基に対するSiH基のモル比が0.5〜4となる量)と、白金又は白金化合物に代表される白金族金属系付加反応触媒(通常、アルケニル基含有オルガノポリシロキサンに対し1〜1000ppm)とを含有するものが用いられる。 As the addition reaction curing type silicone rubber composition, a known composition can be used, for example, an alkenyl group-containing organopolysiloxane having two or more alkenyl groups in one molecule represented by a vinyl group. , Organohydrogenpolysiloxane having 2 or more, preferably 3 or more SiH groups (usually, an amount such that the molar ratio of SiH groups to alkenyl groups is 0.5 to 4), and platinum or platinum compounds. Those containing a platinum group metal-based addition reaction catalyst (usually 1 to 1000 ppm with respect to an alkenyl group-containing organopolysiloxane) are used.
また、有機過酸化物硬化型のシリコーンゴム組成物としても、公知の組成のものを使用することができ、例えば、好ましくはアルケニル基を1分子中に2個以上有するオルガノポリシロキサンに硬化剤として有機過酸化物を硬化有効量(通常、上記オルガノポリシロキサン100質量部に対し1〜10質量部)配合したものが用いられる。 Further, as the organic peroxide curing type silicone rubber composition, a known composition can be used. For example, an organopolysiloxane having two or more alkenyl groups in one molecule can be used as a curing agent. An organic peroxide blended in an effective amount for curing (usually 1 to 10 parts by mass with respect to 100 parts by mass of the above-mentioned organopolysiloxane) is used.
上記シリコーンゴム組成物としては、市販品を使用することができる。例えば、付加反応硬化型のシリコーンゴム組成物である、信越化学工業株式会社製のLIMS(商標)(液状シリコーンゴム射出成形システム)、中でも、KE−1950−10A/B、KE−1950−20A/B、KE−2004−3A/B、KE−2004−5A/Bなどを挙げることができる。 As the silicone rubber composition, a commercially available product can be used. For example, LIMS (trademark) (liquid silicone rubber injection molding system) manufactured by Shin-Etsu Chemical Co., Ltd., which is an addition reaction curing type silicone rubber composition, among others, KE-1950-10A / B, KE-1950-20A / B, KE-2004-3A / B, KE-2004-5A / B and the like can be mentioned.
(任意の成分)
本発明の疑似皮膚フィルムは、本発明の効果に影響を及ぼさない範囲で、顔料、染料等の着色剤、充填剤、安定化剤、保湿剤、紫外線吸収剤、紫外線散乱剤、滑剤等の各種添加剤を適宜配合することができる。なお、透明な疑似皮膚フィルムは、皮膚に適用した後に目立ちにくくなるため、着色剤は含まれないことが好ましい。(Arbitrary ingredient)
The pseudo-skin film of the present invention includes various colorants such as pigments and dyes, fillers, stabilizers, moisturizers, ultraviolet absorbers, ultraviolet scattering agents, lubricants, etc., as long as the effects of the present invention are not affected. Additives can be added as appropriate. It is preferable that the transparent pseudo-skin film does not contain a colorant because it becomes less noticeable after being applied to the skin.
〈任意の構成層〉
本発明の疑似皮膚フィルムは、任意に、粘着剤層、接着剤層、剥離シート等の構成層を適宜有していてもよい。特に、本発明の疑似皮膚フィルムは、厚さが600μm以下と薄いため、保護又は取り扱い性等の観点から、フィルムの片面又は両面に剥離シートを備えることが好ましい。<Arbitrary constituent layer>
The pseudo-skin film of the present invention may optionally have a constituent layer such as an adhesive layer, an adhesive layer, and a release sheet. In particular, since the pseudo-skin film of the present invention has a thin thickness of 600 μm or less, it is preferable to provide a release sheet on one side or both sides of the film from the viewpoint of protection or handleability.
係る剥離シートの材料としては、特に限定されるものではないが、取扱い性の観点から、ポリエチレン、ポリプロピレン等のポリオレフィン、ポリエチレンテレフタレート等のポリエステル、紙等を挙げることができ、また、剥離シートの表面にはシリコーン等の離型処理が施されていてもよい。このような剥離シートは、疑似皮膚フィルムに対し、静電的作用により密着させることができる。 The material of the release sheet is not particularly limited, and examples thereof include polyolefins such as polyethylene and polypropylene, polyester such as polyethylene terephthalate, and paper from the viewpoint of handleability, and the surface of the release sheet. May be subjected to a mold release treatment such as silicone. Such a release sheet can be brought into close contact with the pseudo-skin film by an electrostatic action.
また、粘着剤層及び接着剤層は、皮膚への負担又は違和感を生じさせやすく、また、皺等への追従性を低下させるとともに、貼り付け時の取り扱い性を悪化させるおそれがあるため、疑似皮膚フィルムは、これらの層を備えない、非粘着性のフィルムであることが好ましい。 In addition, the adhesive layer and the adhesive layer are likely to cause a burden on the skin or a feeling of strangeness, reduce the ability to follow wrinkles, etc., and may deteriorate the handleability at the time of sticking. The skin film is preferably a non-adhesive film that does not have these layers.
〈疑似皮膚フィルムの適用部位〉
本発明の疑似皮膚フィルムは、体のあらゆる部分における皮膚の表面上、即ち、体表上であれば、いかなる箇所に貼り付けることができ、次のものに限定されないが、例えば、顔(唇、目元、鼻など)、耳、手、腕、脚、足、胸、下腹、背中等の皮膚表面に対して適宜貼り付けることができる。傷のある皮膚表面に対して疑似皮膚フィルム貼り付けた場合には、該フィルムが傷の凹凸に追従するため傷を目立たなくさせることができる。ここで、皮膚には、皮膚の表皮の角質が変化して硬化した爪なども含まれる。<Application site of pseudo-skin film>
The pseudo-skin film of the present invention can be applied to any part of the body on the surface of the skin, that is, on the surface of the body, and is not limited to the following, but for example, the face (lips,). It can be appropriately attached to the skin surface such as (eyes, nose, etc.), ears, hands, arms, legs, legs, chest, lower abdomen, back, etc. When a pseudo-skin film is attached to a scratched skin surface, the film follows the unevenness of the scratch and makes the scratch inconspicuous. Here, the skin also includes nails and the like in which the keratin of the epidermis of the skin is changed and hardened.
本発明の疑似皮膚フィルムは、貼り付けた後のエア溜まりが改善されて目立ちにくく、密着性にも優れ、また、皺等の皮膚表面の凹凸などに対して追従しやすいため、係るフィルムは、上記適用部位の中でも、顔(特に、唇、目元、鼻)、耳、又は爪に対して貼り付けることが好ましい。 The pseudo-skin film of the present invention has improved air accumulation after application, is less noticeable, has excellent adhesion, and easily follows irregularities on the skin surface such as wrinkles. Among the above-mentioned application sites, it is preferable to attach it to the face (particularly, lips, eyes, nose), ears, or nails.
《化粧キット》
本発明の疑似皮膚フィルムは、係るフィルムを有する化粧キットとして提供することができる。係る化粧キットには、疑似皮膚フィルム以外に、例えば、フィルムを皮膚へ貼り付けやすくしたり、化粧をさらに施すための任意の部材を有していてもよい。《Makeup kit》
The pseudo-skin film of the present invention can be provided as a cosmetic kit having such a film. In addition to the pseudo-skin film, the cosmetic kit may include, for example, any member for facilitating the attachment of the film to the skin or for further applying makeup.
このような任意の部材としては、例えば、密着剤、カッター、ハサミ、グロス、口紅、マニキュア、リキッドファンデーション、鏡等を挙げることができる。中でも、皮膚表面に塗布して使用する密着剤は、疑似皮膚フィルムの皮膚への密着性を向上させることができるため、粘着剤層又は接着剤層を有さない非粘着性の疑似皮膚フィルムを使用する場合には特に好ましい。 Examples of such an arbitrary member include an adhesive, a cutter, scissors, a gloss, a lipstick, a nail polish, a liquid foundation, a mirror and the like. Among them, the adhesive used by applying it to the skin surface can improve the adhesion of the pseudo-skin film to the skin. Therefore, a non-adhesive pseudo-skin film having no adhesive layer or an adhesive layer is used. Especially preferred when used.
〈密着剤〉
このような密着剤としては、皮膚への負担が少なく、疑似皮膚フィルムの皮膚への密着性を向上させ得る剤であればいかなるものでもよく、次のものに限定されないが、例えば、ポリブテン及びポリイソブテンから選ばれる少なくとも一種を使用することができる。密着性、耐久性等の観点から、ポリブテンの数平均分子量としては、1000以上又は1500以上とすることができ、また、5000以下又は4000以下とすることができ、ポリイソブテンの数平均分子量としては、8000以上、9000以上、又は10000以上とすることができ、また、30000以下、25000以下、又は22000以下とすることができる。ここで、数平均分子量とは、ゲルパーミエーションクロマトグラフ測定における、ポリスチレン換算の数平均分子量を意図する。<Adhesive agent>
The adhesive may be any agent that has less burden on the skin and can improve the adhesion of the pseudo-skin film to the skin, and is not limited to, but is limited to, for example, polybutene and polyisobutene. At least one selected from can be used. From the viewpoint of adhesion, durability, etc., the number average molecular weight of polybutene can be 1000 or more or 1500 or more, and can be 5000 or less or 4000 or less, and the number average molecular weight of polybutene can be set to 5000 or less or 4000 or less. It can be 8000 or more, 9000 or more, or 10000 or more, and can be 30,000 or less, 25000 or less, or 22000 or less. Here, the number average molecular weight is intended to be a polystyrene-equivalent number average molecular weight in gel permeation chromatograph measurement.
本発明における密着剤としては、市販品を用いることができる。例えば、ポリブテンとしては、脱臭ポリブテン−P200SH(日興リカ株式会社製)などを用いることができ、ポリイソブテンとしては、Oppanol(商標)B12SFN/12N、Oppanol(商標)B13SFN、Oppanol(商標)B14SFN/14N、Oppanol(商標)B15SFN/15N(以上、BASF社製)などを用いることができる。 As the adhesive in the present invention, a commercially available product can be used. For example, as polybutene, deodorizing polybutene-P200SH (manufactured by Nikko Rika Co., Ltd.) can be used, and as polyisobutene, Oppanol (trademark) B12SFN / 12N, Oppanol (trademark) B13SFN, Oppanol (trademark) B14SFN / 14N, Oppanol ™ B15SFN / 15N (above, manufactured by BASF) and the like can be used.
密着剤には、保湿成分が含まれていてもよい。係る保湿成分としては、通常化粧料に用いられているものを一種以上使用することができ、例えば、ポリエチレングリコール、プロピレングリコール、グリセリン、1,3−ブチレングリコール、ジプロピレングリコール、キシリトール、ソルビトール、マルチトール、コンドロイチン硫酸、ヒアルロン酸、ムコイチン硫酸、カロニン酸、アテロコラーゲン、乳酸ナトリウム、ピロリドンカルボン酸、短鎖可溶性コラーゲン等が挙げられる。 The adhesive may contain a moisturizing component. As the moisturizing ingredient, one or more of those usually used in cosmetics can be used, for example, polyethylene glycol, propylene glycol, glycerin, 1,3-butylene glycol, dipropylene glycol, xylitol, sorbitol, mulch. Examples thereof include toll, chondroitin sulfate, hyaluronic acid, mucoitin sulfate, caronic acid, atelocollagen, sodium lactate, pyrrolidone carboxylic acid, short chain soluble collagen and the like.
保湿成分の配合割合は、密着剤全量に対し、0.01質量%以上、0.05質量%以上、又は0.1質量%以上であることが好ましく、また、10質量%以下、9質量%以下、又は8質量%以下であることが好ましい。 The blending ratio of the moisturizing component is preferably 0.01% by mass or more, 0.05% by mass or more, or 0.1% by mass or more, and 10% by mass or less, 9% by mass, based on the total amount of the adhesive. It is preferably less than or equal to 8% by mass or less.
《疑似皮膚フィルムの製造方法》
本発明の疑似皮膚フィルムは、公知の方法により製造することができる。具体的には、例えば、圧縮成型法、注入成型法、射出成型法、カレンダー成型法、コンプレッション成型法などによりフィルムを形成した後、係るフィルムに対し、レーザー照射又は打ち抜き加工等を適用して貫通孔を形成し、疑似皮膚フィルムを得ることができる。中でも、生産性、精度等の観点から、射出成型法、カレンダー成型法又はコンプレッション成型法、特には、カレンダー成型法によってフィルムを形成することが好ましく、レーザー照射によって貫通孔を形成することが好ましい。<< Manufacturing method of pseudo-skin film >>
The pseudo-skin film of the present invention can be produced by a known method. Specifically, for example, after forming a film by a compression molding method, an injection molding method, an injection molding method, a calendar molding method, a compression molding method, or the like, the film is penetrated by applying laser irradiation or punching. Pore can be formed and a pseudo-skin film can be obtained. Above all, from the viewpoint of productivity, accuracy and the like, it is preferable to form a film by an injection molding method, a calendar molding method or a compression molding method, particularly a calendar molding method, and it is preferable to form through holes by laser irradiation.
また、得られた疑似皮膚フィルムは、使用者が任意の形状及び大きさに適宜カットして使用することができ、或いは、レーザー加工、打ち抜き加工等によって、任意の形状及び大きさに事前に加工してもよい。 Further, the obtained pseudo-skin film can be appropriately cut into an arbitrary shape and size by the user, or can be pre-processed into an arbitrary shape and size by laser processing, punching or the like. You may.
貫通孔の形成及び任意形状の加工に関しては、疑似皮膚フィルム単体に対して実施してもよく、或いは、剥離シートを片面又は両面に備えた状態の疑似皮膚フィルムに対して実施してもよい。 The formation of the through hole and the processing of an arbitrary shape may be carried out on the pseudo-skin film alone, or may be carried out on the pseudo-skin film in a state where the release sheet is provided on one side or both sides.
《疑似皮膚フィルムの使用方法》
本発明の疑似皮膚フィルムは、剥離シートが存在する場合には該シートを適宜除去した後に、上述した体の皮膚表面(体表)に貼り付けて使用することができる。<< How to use pseudo skin film >>
If a release sheet is present, the pseudo-skin film of the present invention can be used by appropriately removing the sheet and then attaching it to the skin surface (body surface) of the body described above.
例えば、唇に貼り付ける場合には、唇の形状及び大きさに調製した疑似皮膚フィルムを唇に貼り付けて使用する。この場合、係るフィルムが粘着剤層又は接着剤層を有さない場合には、唇に対して、上述した密着剤を指又は筆等によって唇に塗布した後、特に、塗布した直後に疑似皮膚フィルムを唇に貼り付けると、係る密着剤がフィルムの貫通孔に侵入するため密着性をより向上させることができる。その結果、他の部位よりも比較的動きの多い唇であっても、ヨレ、剥がれ等の不具合を防止することができる。 For example, when it is attached to the lips, a pseudo-skin film prepared to have the shape and size of the lips is attached to the lips for use. In this case, if the film does not have an adhesive layer or an adhesive layer, the above-mentioned adhesive is applied to the lips with a finger, a brush, or the like, and then the pseudo-skin is applied, especially immediately after the application. When the film is attached to the lips, the adhesive penetrates into the through holes of the film, so that the adhesiveness can be further improved. As a result, it is possible to prevent problems such as twisting and peeling even on the lips that move relatively more than other parts.
本発明の疑似皮膚フィルムに対し、グロス、口紅、マニュキュア、リキッドファンデーション等の塗布剤を別途適用してもよい。このような塗布剤は、疑似皮膚フィルムに対し、事前に適用してもよく、或いは、皮膚表面にフィルムを貼り付けた後に適用してもよい。 A coating agent such as gloss, lipstick, nail polish, or liquid foundation may be separately applied to the pseudo-skin film of the present invention. Such a coating agent may be applied to the pseudo-skin film in advance, or may be applied after the film is attached to the skin surface.
本発明の疑似皮膚フィルムは、特定の貫通孔を有しているため、上記のような塗布剤が、貫通孔に侵入しやすくなる。その結果、係る塗布剤を適用しにくい素材であったとしても、疑似皮膚フィルムの材料として使用することが可能となった。 Since the pseudo-skin film of the present invention has specific through-holes, the above-mentioned coating agent easily penetrates into the through-holes. As a result, even if the material is difficult to apply the coating agent, it can be used as a material for a pseudo-skin film.
以下に実施例を挙げて、本発明についてさらに詳しく説明を行うが、本発明はこれらに限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited thereto.
《実施例1〜3、比較例1及び2》
実施例1〜3、比較例1及び2に記載される処方及び製造方法により得た疑似皮膚フィルムについて、以下に示す各種性能について目視によって評価した。その結果を表1にまとめる。<< Examples 1 to 3, Comparative Examples 1 and 2 >>
The pseudo-skin films obtained by the formulations and manufacturing methods described in Examples 1 to 3 and Comparative Examples 1 and 2 were visually evaluated for various performances shown below. The results are summarized in Table 1.
なお、疑似皮膚フィルムを唇に貼り付ける場合には、ポリブテン(数平均分子量2650)及びポリイソブテン(数平均分子量16000)を含む密着剤を唇に塗布した直後に、係るフィルムを貼り付けた。また、疑似皮膚フィルムをウレタン製の評価用皮膚モデルに貼り付ける場合には、係る皮膚モデルには密着剤を塗布せずに、そのまま疑似皮膚フィルムを貼り付けた。 When the pseudo-skin film was attached to the lips, the film was attached immediately after applying an adhesive containing polybutene (number average molecular weight 2650) and polyisobutene (number average molecular weight 16000) to the lips. Further, when the pseudo-skin film was attached to the evaluation skin model made of urethane, the pseudo-skin film was attached as it was without applying the adhesive to the skin model.
〈疑似皮膚フィルムの評価〉
(エア溜まりの改善持続性)
40〜50代のパネラーの唇に疑似皮膚フィルムを貼り付け、3時間後のフィルムの状態を目視観察した。評価項目は以下のとおりである。この結果から、疑似皮膚フィルムのエア溜まりの改善持続性を評価することができる。ここで、エア溜まりの改善持続性とは、貼り付け時及び貼り付け後(3時間後)のエア溜まりの改善性を意図している。<Evaluation of pseudo-skin film>
(Sustainability of improvement of air pool)
A pseudo-skin film was attached to the lips of panelists in their 40s and 50s, and the state of the film after 3 hours was visually observed. The evaluation items are as follows. From this result, it is possible to evaluate the improvement sustainability of the air pool of the pseudo-skin film. Here, the improvement sustainability of the air pool is intended to improve the air pool at the time of pasting and after pasting (3 hours later).
A 貼付箇所に気泡が存在しない。
B 貼付箇所に気泡が1〜3個存在している。
C 貼付箇所に気泡が4個以上存在している。A There are no bubbles at the sticking point.
B There are 1 to 3 bubbles at the sticking point.
C There are 4 or more bubbles at the sticking point.
(自然な仕上がり性)
40〜50代のパネラーの唇に疑似皮膚フィルムを貼り付け、飲食をしながら3時間経過直後のフィルムの状態を目視観察した。評価項目は以下のとおりである。この結果から、疑似皮膚フィルムの自然な仕上がり性を評価することができる。(Natural finish)
A pseudo-skin film was attached to the lips of panelists in their 40s and 50s, and the state of the film was visually observed immediately after 3 hours had passed while eating and drinking. The evaluation items are as follows. From this result, the natural finish of the pseudo-skin film can be evaluated.
A 貼付箇所が目立たず自然さを感じる。
B 貼付箇所がやや目立つが遠目には自然さを感じる。
C 貼付箇所が目立ち自然さを感じない。A The sticking part is inconspicuous and feels natural.
B The sticking part is a little noticeable, but it feels natural from a distance.
C The sticking part is conspicuous and does not feel natural.
(グロスの塗布性)
40〜50代のパネラーの唇に疑似皮膚フィルムを貼り付け、グロスを塗布した後のフィルムの状態を目視観察した。評価項目は以下のとおりである。この結果から、疑似皮膚フィルムにおけるグロスの塗布性を評価することができる。(Gloss coating property)
A pseudo-skin film was attached to the lips of panelists in their 40s and 50s, and the state of the film after applying the gloss was visually observed. The evaluation items are as follows. From this result, the applicability of the gloss in the pseudo-skin film can be evaluated.
A 塗布ムラが全く認められず自然さを感じる。
B フィルムの一部において塗布ムラが認められるが、遠目には自然さを感じる。
C 塗布ムラが認められ不自然さを感じる。A No uneven coating is observed and it feels natural.
B Coating unevenness is observed on a part of the film, but it feels natural at a distance.
C Coating unevenness is observed and it feels unnatural.
(リキッドファンデーションの塗布性)
ウレタン製の皮膚評価モデル(Beulax社製の頬部肌模型)に疑似皮膚フィルムを貼り付け、リキッドファンデーションを塗布した後のフィルムの状態を目視観察した。評価項目は以下のとおりである。この結果から、疑似皮膚フィルムにおけるリキッドファンデーションの塗布性を評価することができる。(Applicability of liquid foundation)
A pseudo-skin film was attached to a urethane skin evaluation model (a buccal skin model manufactured by Beaulux), and the state of the film after applying the liquid foundation was visually observed. The evaluation items are as follows. From this result, the applicability of the liquid foundation in the pseudo-skin film can be evaluated.
A 毛穴が全く認められず、均一で自然な仕上がり感が得られる。
B フィルムの一部において塗布ムラ及び又は毛穴が認められるが、遠目には自然な仕上がり感が得られる。
C 塗布ムラ及び又は毛穴が認められ、仕上がりに不自然さを感じる。A No pores are observed, and a uniform and natural finish can be obtained.
Although uneven coating and / or pores are observed in a part of the B film, a natural finish can be obtained from a distance.
C Coating unevenness and / or pores are observed, and the finish feels unnatural.
(リキッドファンデーションの剥がれ落ち性)
ウレタン製の皮膚評価モデル(Beulax社製の頬部肌模型)に疑似皮膚フィルムを貼り付け、リキッドファンデーションを塗布し、約1分間経過した後、ティッシュオフを10回繰り返したフィルムの状態を目視観察した。評価項目は以下のとおりである。この結果から、疑似皮膚フィルムにおけるリキッドファンデーションの剥がれ落ち性、即ち、ファンデーションの密着性を評価することができる。(Liquid foundation peeling off)
A pseudo-skin film was attached to a urethane skin evaluation model (Beulux cheek skin model), a liquid foundation was applied, and after about 1 minute had passed, the state of the film was visually observed by repeating tissue-off 10 times. did. The evaluation items are as follows. From this result, it is possible to evaluate the peeling property of the liquid foundation in the pseudo-skin film, that is, the adhesion of the foundation.
A リキッドファンデーションの剥がれ落ちが全く認められず、自然な仕上がり感が得られる。
B フィルムの一部においてリキッドファンデーションの剥がれ落ちが認められるが、遠目には自然な仕上がり感が得られる。
C リキッドファンデーションの剥がれ落ちが認められ、仕上がりに不自然さを感じる。A No peeling of the liquid foundation is observed, and a natural finish is obtained.
Although the liquid foundation is peeled off in a part of the B film, a natural finish can be obtained from a distance.
C The liquid foundation is peeled off, and the finish feels unnatural.
〈実施例1〉
信越化学工業株式会社製のLIMS(商標)KE−2004−3A/Bを、カレンダー装置に投入し、加熱して硬化させながら、複数の金属ロールで圧延して、2枚の剥離シートに挟まれた状態の厚さ100μmのシリコーンゴムフィルムを調製した。<Example 1>
LIMS (trademark) KE-2004-3A / B manufactured by Shin-Etsu Chemical Co., Ltd. is put into a calendar device, rolled with multiple metal rolls while being heated and cured, and sandwiched between two release sheets. A silicone rubber film having a thickness of 100 μm was prepared.
ここで、剥離シートを除去したシリコーンゴムフィルムを積層して厚さ6.0mmの試験片を調製した。係る試験片のJIS K6253に準拠したデュロメータータイプA硬度計によるゴム硬度は3であった。 Here, a silicone rubber film from which the release sheet was removed was laminated to prepare a test piece having a thickness of 6.0 mm. The rubber hardness of the test piece by the durometer type A hardness tester conforming to JIS K6253 was 3.
次いで、ビデオジェット社製のレーザー照射機を用い、得られたシリコーンゴムフィルムに対してCO2レーザー光を照射し、1250個/cm2の割合で貫通孔をフィルム全面に形成し、疑似皮膚フィルムを作製した。ここで、貫通孔は、略円錐台の形状を呈しており、フィルム表面における貫通孔の最小面積及びその略円形状部の直径は、約1300μm2及び40μmであった。Next, a laser irradiator manufactured by Videojet Co., Ltd. was used to irradiate the obtained silicone rubber film with CO 2 laser light to form through holes at a ratio of 1250 pieces / cm 2 on the entire surface of the film to form a pseudo-skin film. Was produced. Here, the through hole has a substantially truncated cone shape, and the minimum area of the through hole on the film surface and the diameter of the substantially circular portion thereof are about 1300 μm 2 and 40 μm.
〈実施例2〉
疑似皮膚フィルムの厚さを200μmに変更したことを除いて、実施例1と同様にして、実施例2の疑似皮膚フィルムを作製した。<Example 2>
A pseudo-skin film of Example 2 was prepared in the same manner as in Example 1 except that the thickness of the pseudo-skin film was changed to 200 μm.
〈実施例3〉
疑似皮膚フィルムの厚さを300μmに変更したことを除いて、実施例1と同様にして、実施例3の疑似皮膚フィルムを作製した。<Example 3>
A pseudo-skin film of Example 3 was prepared in the same manner as in Example 1 except that the thickness of the pseudo-skin film was changed to 300 μm.
〈比較例1〉
疑似皮膚フィルムに貫通孔を形成しなかったことを除いて、実施例1と同様にして、比較例1の疑似皮膚フィルムを作製した。<Comparative example 1>
A pseudo-skin film of Comparative Example 1 was prepared in the same manner as in Example 1 except that no through hole was formed in the pseudo-skin film.
〈比較例2〉
疑似皮膚フィルムの厚さを700μmに変更したことを除いて、実施例1と同様にして、比較例2の疑似皮膚フィルムを作製した。<Comparative example 2>
A pseudo-skin film of Comparative Example 2 was prepared in the same manner as in Example 1 except that the thickness of the pseudo-skin film was changed to 700 μm.
〈結果〉
表1の結果から分かるように、実施例1〜3の疑似皮膚フィルムは、比較例1及び2の疑似皮膚フィルムに比べて、エア溜まりの改善持続性及び自然な仕上がり性が向上していることが確認できた。<result>
As can be seen from the results in Table 1, the pseudo-skin films of Examples 1 to 3 have improved sustainability of air accumulation and natural finish as compared with the pseudo-skin films of Comparative Examples 1 and 2. Was confirmed.
また、貫通孔を有していない比較例1及び貫通孔を有している実施例1の疑似皮膚フィルムを比べると、グロス及びリキッドファンデーションの塗布性、並びにリキッドファンデーションの剥がれ落ち性において、実施例1の疑似皮膚フィルムの方が優れていることが確認できた。これは、所定の大きさの貫通孔が、所定の割合で疑似皮膚フィルムに配置されているため、グロス及びリキッドファンデーションが、係る貫通孔に侵入したためであると考えられる。 Further, comparing the pseudo-skin film of Comparative Example 1 having a through hole and Example 1 having a through hole, the examples were in terms of the coatability of the gloss and the liquid foundation and the peeling property of the liquid foundation. It was confirmed that the pseudo-skin film of No. 1 was superior. It is considered that this is because the through holes of a predetermined size are arranged in the pseudo-skin film at a predetermined ratio, so that the gloss and the liquid foundation have invaded the through holes.
Claims (15)
膜厚が、600μm以下であり、
貫通孔が、3〜500000個/cm2の割合で配置されており、かつ、
前記貫通孔の面積が、70〜283000μm2/個である、
疑似皮膚フィルム。The rubber hardness by the durometer type A hardness tester conforming to JIS K6253 is 20 or less.
The film thickness is 600 μm or less,
Through holes are arranged at a ratio of 3 to 500,000 pieces / cm 2, and
The area of the through hole is 70 to 283000 μm 2 / piece.
Pseudo skin film.
前記フィルムにレーザーを照射して貫通孔を形成する、
請求項1〜7のいずれか一項に記載の疑似皮膚フィルムの製造方法。A film is formed by injection molding, calendar molding, or compression molding, and the film is irradiated with a laser to form through holes.
The method for producing a pseudo-skin film according to any one of claims 1 to 7.