JPS6389107A - Clock band - Google Patents
Clock bandInfo
- Publication number
- JPS6389107A JPS6389107A JP23399586A JP23399586A JPS6389107A JP S6389107 A JPS6389107 A JP S6389107A JP 23399586 A JP23399586 A JP 23399586A JP 23399586 A JP23399586 A JP 23399586A JP S6389107 A JPS6389107 A JP S6389107A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- watch band
- film
- elastomer resin
- resin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Abstract] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は腕時計に使用される時計バンドに関するもので
ある。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a watch band used for a wristwatch.
［従来の技術］
腕時計に使用される時計バンドには、従来、全屈製時計
バンド、天然皮革製時計バンド、更には合成皮革製時計
バンド等が利用されているが、最近、より廉価に生産し
得るという理由でエラストマー樹脂特にウレタン系樹脂
や軟質ポリ塩化ビニル系樹脂による時計バンドが利用さ
れ始めている。[Prior Art] Conventionally, watch bands used for wristwatches include fully bent watch bands, natural leather watch bands, and even synthetic leather watch bands, but recently, more inexpensively produced watch bands have been used. For this reason, watch bands made of elastomer resins, particularly urethane resins and soft polyvinyl chloride resins, have begun to be used.
［発明が解決しようとする問題点］
ところで、前記エラストマー樹脂による時計バンドは、
従来、前記エラストマー樹脂による単層構成か、あるい
は異なる着色剤が混入されている２種類の成形用樹脂に
よる２色成形体たる表、裏の色彩が相違する２層構成の
ものであり、所望により時計バンドの表面にシボ模様を
付設したものが利用されているが、いずれも意匠的な加
飾効果に乏しく、高品質感に欠けるという欠点を有して
いる。[Problems to be solved by the invention] By the way, the watch band made of elastomer resin has the following problems:
Conventionally, the elastomer resin has a single-layer structure, or it has a two-layer structure, which is a two-color molded product made of two types of molding resins mixed with different colorants, with the front and back sides having different colors. Watch bands with grained patterns on the surface have been used, but all of them have the drawback of lacking a decorative decorative effect and lacking a sense of high quality.
これに対して本発明は、安価に製造し得るエラストマー
樹脂による時計バンドで、しかもメタリック調の高品質
感を呈する高意匠性の時計バンドを提供し得たものであ
る。In contrast, the present invention provides a watch band made of elastomer resin that can be manufactured at low cost and has a high design quality and a high quality metallic appearance.
［問題点を解決するための手段］
本発明の時計バンドは、扁平状のエラストマー樹脂層中
に金属蒸着層を有する樹脂フィルムからなる金属蒸着フ
ィルムが、前記扁平状のエラストマー樹脂層の長さ方向
と全屈蒸着フィルムの長さ方向とが同一方向となるよう
にして埋没された構成から成るものである。[Means for Solving the Problems] In the watch band of the present invention, a metal vapor deposited film consisting of a resin film having a metal vapor deposited layer in a flat elastomer resin layer is arranged in a longitudinal direction of the flat elastomer resin layer. The film is buried so that the length direction of the film and the length direction of the fully bent vapor-deposited film are in the same direction.
前記構成からなる本発明の時計バンドは、金属蒸着フィ
ルムの表、表両面に既製のエラストマー樹脂フィルムを
接着剤で積層したり、あるいは金属蒸着フィルムをイン
サートして前記全屈蒸着フィルムの表、表両面にエラス
トマー樹脂を射出成形または注型キャスト成形したり、
更には、金属蒸着フィルムとエラストマー樹脂フィルム
との接着積層シートをインサートしてエラストマー樹脂
を射出成形ま′たは注型キャスト成形する等して容易に
得られるものである。The watch band of the present invention having the above-mentioned structure can be obtained by laminating a ready-made elastomer resin film on the front side of the metal-deposited film with an adhesive, or by inserting a metal-deposited film on the front side and both sides of the metal-deposited film. Injection molding or cast molding with elastomer resin on both sides,
Furthermore, it can be easily obtained by inserting an adhesive laminated sheet of a metal-deposited film and an elastomer resin film and then injection molding or casting the elastomer resin.
扁平状のエラストマー樹脂層中に埋没されている金ｆｉ
ｆｓｇ着フィルムは、例えば、ポリエチレンテレフタレ
ート樹脂フィルム、ナイロンフィルム、ポリプロピレン
フィルム、ポリ塩化ビニルフィルム等の樹脂フィルムに
、例えば、アルミニラム、金、銀、銅、ステンレス等の
金属を真空蒸着して得られるものが最も一般的なもの、
であるが、スパッタリングやイオンブレーティング法な
どの真空薄膜法で得られたものでも良い、また、金属蒸
着層面または樹脂フィルム面に、オフセット、グラビア
、シルクスクリーン等によるベタ刷り印刷層や絵柄印刷
層が形成されている所謂着色印刷層を有する金属蒸着フ
ィルムが金属蒸着フィルムとして利用される場合も存す
る。また、前記金属蒸着フィルムとして、エラストマー
樹脂に対する接着が良好なプライマー層を具備するもの
が利用される場合、例えばポリウレタン樹脂に対する接
着が良好なポリカーボネートやポリウレタンによるプラ
イマー層を具備するものが利用される場合には、金属蒸
着フィルムとエラストマー樹脂層との間に強固な接着が
達成され、特に、曲げや捩れ等に対する抵抗力の強い、
耐久性に優れた時計バンドとなる。なお、前記プライマ
ー層は、プライマー層となる樹脂フィルムがラミネート
加工されたり、あるいはプライマー層となる樹脂溶液が
塗布、屹燥される等して容易に形成されるものである。Gold fi embedded in flat elastomer resin layer
FSG-attached films are those obtained by vacuum-depositing metals such as aluminum, gold, silver, copper, and stainless steel onto resin films such as polyethylene terephthalate resin films, nylon films, polypropylene films, and polyvinyl chloride films. is the most common one,
However, it may also be one obtained by vacuum thin film methods such as sputtering or ion blating, or a solid printing layer or pattern printing layer by offset, gravure, silk screen, etc. on the metal vapor deposition layer surface or resin film surface. There are cases where a metal vapor deposited film having a so-called colored printed layer formed thereon is used as the metal vapor deposit film. Further, when the metallized film is provided with a primer layer that has good adhesion to elastomer resin, for example, when a film is used that has a primer layer made of polycarbonate or polyurethane that has good adhesion to polyurethane resin. A strong adhesion is achieved between the metallized film and the elastomer resin layer, and the film has particularly strong resistance to bending, twisting, etc.
This makes for a highly durable watch band. The primer layer is easily formed by laminating a resin film that will become the primer layer, or by applying and drying a resin solution that will become the primer layer.
前記金属蒸着フィルムを埋没させているエラストマー樹
脂層は、ポリウレタン、ポリオレフィン系、ポリスチレ
ン系、ポリエステル系、ポリアミド系等の熱可塑性エラ
ストマーや軟質ポリ塩化ビニル等のエラスティック性を
有する樹脂で構成されているものであるが、特に機械的
強度のうえからポリウレタンによるエラストマー樹脂層
が最適である。The elastomer resin layer in which the metal vapor-deposited film is buried is made of a thermoplastic elastomer such as polyurethane, polyolefin, polystyrene, polyester, or polyamide, or a resin having elasticity such as soft polyvinyl chloride. However, from the viewpoint of mechanical strength, an elastomer resin layer made of polyurethane is most suitable.
前記扁平状のエラストマー樹脂層中に金属蒸着フィルム
が埋没されてなる時計バンドは、該時計バンドの表面側
を構成しているエラストマー樹脂層の表面にレーザー光
線によるスクライビング（溝掘り）加工が施され、立体
的で繊細な溝加工を有するものにすることもできる。こ
の所望に応じて施されるレーザー光線によるスクライビ
ング（溝掘り）加工は、炭酸ガスやＹＡＧなどのいずれ
のレーザー光線によるもめでも良く、また、連続出力方
式でもパルス方式でも良いが、パルス方式によるものの
場合には幅違い線などの特長のあるパターン加工が施さ
れるので、微細な線による複雑な模様からなるスクライ
ビング加工を有するファツション性に富む時計バンドと
なる。なお、レーザー光線によるスクライビング加工に
際しては、エラストマー樹脂の蒸発物が揮散して周辺に
付着するので、空気やＮ２ガスを吹き付けながら加工を
行なうようにして前記蒸発物の揮散を防止するのが良い
、また、レーザー光線処理の出力の加減によってスクラ
イビング溝の深さが調節され、溝の深さに変化を有する
立体的なスクライビング加工カ得うレルノテ、Ｎ ＣＦ
ｔＪＩ ＩＩＩ Ｘ −Ｙテーブル装この使用により各
種の模様を呈するスクライビング加工が容易に行なえる
。The watch band in which a metal vapor-deposited film is embedded in the flat elastomer resin layer has a scribing (grooving) process performed on the surface of the elastomer resin layer constituting the front side of the watch band using a laser beam, It can also have three-dimensional and delicate grooves. This scribing (grooving) process using a laser beam performed as desired may be performed using any laser beam such as carbon dioxide gas or YAG, and may be a continuous output method or a pulse method, but in the case of a pulse method, The watch band is processed with distinctive patterns such as lines of different widths, resulting in a highly fashionable watch band with a scribing process consisting of a complex pattern of fine lines. In addition, when performing the scribing process using a laser beam, the evaporated matter of the elastomer resin evaporates and adheres to the surrounding area, so it is better to perform the process while blowing air or N2 gas to prevent the evaporated matter from evaporating. The depth of the scribing groove is adjusted by adjusting the output of the laser beam processing, and a three-dimensional scribing process with a change in the depth of the groove can be achieved.NCF
tJI III X-Y Table Setup By using this, scribing processing that presents various patterns can be easily performed.
更に、前記扁平状のエラストマー樹脂層中に全屈蒸着フ
ィルムが埋没されてなる時計バンドは、該時計バンドの
表面側を構成しているエラストマー樹脂層の表面が所望
によりマット（艶消し）加工に付される際には、艶消し
状の雅趣に富むメタリック調が発揮されている時計バン
ドとされるものである。また、このマット加工面に部分
的に透明な印刷層が形成される場合には、印刷層が形成
された部分のマット加工面が透明印刷インキで平滑面と
されることにより、該部分が部分的に透明となり、マッ
ト加工部分との間に艶差を発揮する高品質感のある時計
バンドとなるが、前記透明印刷層が多色刷りの透明印刷
層とされている場合には、前述の高品質感が更に増大す
る。なお、前記マット加工は、時計バンドの表面層とな
るエラストマー樹脂フィルムの製造時にマツトロールに
よる加圧を施すことにより得られるマット加工フィルム
、すなわち、マツトロール表面の微細凹凸が転写されて
いるマット加工フィルムを使用したり、あるいは、射出
成形やキャスト成形によって時計バンドの表面層となる
エラストマー樹脂層を成形する際に、金型の表面がサン
ドブラストや機械掘り等によるマット加工面とされてい
る金型を利用する等して容易に得られるものである。Furthermore, in the watch band in which the fully bent vapor-deposited film is embedded in the flat elastomer resin layer, the surface of the elastomer resin layer constituting the front side of the watch band may be matte (matte) processed as desired. When worn, it is said to be a watch band that exhibits a matte, elegant metallic tone. In addition, when a partially transparent printing layer is formed on this matte-processed surface, the matte-processed surface of the part on which the printing layer is formed is made smooth with transparent printing ink, so that the part becomes partially transparent. However, if the transparent printing layer is a multicolor transparent printing layer, the above-mentioned high quality The sense of quality will further increase. Note that the matte processing is a matte processed film obtained by applying pressure with a pine roll during the manufacture of the elastomer resin film that will become the surface layer of the watch band, that is, a matte processed film on which fine irregularities on the surface of the pine roll are transferred. Or, when molding the elastomer resin layer that will become the surface layer of the watch band by injection molding or cast molding, use a mold whose surface is matte-finished by sandblasting or machine digging. It can be easily obtained by, for example,
また、本発明の時計バンドは、その用途腕の動きに応じ
て曲げや捩れ等の外方を受ける。すなわち、通常、時計
バンドの表面が伸び裏面が収縮する力を受けるもので、
これによって金属蒸着フィルムにおける金属蒸着層に皺
が生じたり、艶の低下が起こったり、更には、金属蒸着
層と樹脂フィルムとの間に剥離が生じたり等の虞れが存
するが、一般的な厚さ１〜３Ｈの時計バンドに構成され
る場合には、前記金属蒸着フィルムの金属蒸着層面側に
おけるエラストマー樹脂層の厚さと樹脂フィルム層面側
におけるエラストマー樹脂層の厚さとの比が、１００：
２５〜４００の範囲内にあるときには、前述の外力によ
る金属蒸着層への影響が小さく、金属蒸着フィルムによ
る加飾効果に耐久性のある時計バンドとなる。Further, the watch band of the present invention is subjected to bending, twisting, etc. depending on the movement of the wrist for which it is used. In other words, the front side of the watch band usually experiences a force that stretches and the back side contracts.
As a result, there is a risk that the metal vapor deposited layer in the metal vapor deposited film may wrinkle, the gloss may decrease, and furthermore, peeling may occur between the metal vapor deposited layer and the resin film. In the case of a watch band having a thickness of 1 to 3H, the ratio of the thickness of the elastomer resin layer on the metal vapor deposition layer side of the metal vapor deposition film to the thickness of the elastomer resin layer on the resin film layer side of the metal vapor deposition film is 100:
When it is within the range of 25 to 400, the influence of the external force mentioned above on the metal vapor deposited layer is small, and the watch band has durability against the decorative effect of the metal vapor deposited film.
［実施例］
本発明の時計バンドの具体的な構成を製造実施例に基づ
いて説明する。[Example] The specific structure of the watch band of the present invention will be described based on manufacturing examples.
実施例１
厚さ０．０１２ｔ＋ｇのポリエチレンテレフタレートフ
ィルムの片面に厚さ５ｏｏＸのアルミニウム蒸着層を形
成した金属蒸着フィルムを得た後、前記金属蒸着フィル
ムの金属蒸着層面にグラビア印刷にて透明黄色からな−
る着色印刷層を設けた。Example 1 After obtaining a metal-deposited film in which an aluminum vapor-deposited layer with a thickness of 5ooX was formed on one side of a polyethylene terephthalate film with a thickness of 0.012t+g, a transparent yellow color was printed on the surface of the metal-deposited layer of the metal-deposited film by gravure printing. −
A colored printed layer was provided.
次いで、前記金属蒸着フィルムの着色印刷層面に厚さ０
．８１鳳のポリウレタン樹脂のＴダイ押出層からなる表
面層を形成すると共に、同じく前記金属蒸着フィルムの
ポリエチレンテレフタレートフィルム面に厚さ１．０ｍ
ｍのポリウレタン樹脂の注型キャスト層からなる裏面層
を形成して時計バンド素材を得た後、前記時計バンド素
材を所定のサイズの帯状物に截断することにより本発明
の１実施例品たる時計バンドを得た。Next, a layer with a thickness of 0 is applied to the colored printed layer surface of the metal vapor deposited film.
．． A surface layer consisting of a T-die extrusion layer of polyurethane resin of No. 81 was formed, and a 1.0 m thick layer was also formed on the polyethylene terephthalate film surface of the metal vapor deposited film.
A watch which is an embodiment of the present invention is obtained by forming a back layer consisting of a cast layer of polyurethane resin of 100 mL to obtain a watch band material, and then cutting the watch band material into strips of a predetermined size. I got a band.
実施例２
厚さ０．０１２＋ｕ＋のポリエチレンテレフタレートフ
ィルムの片面に厚さ５００Ｘのアルミニウム蒸着層を形
成した金属蒸着フィルムを得た後、前記金Ｅ４Ｍ−Ｊｉ
フィルムのポリエチレンテレフタレートフィルム面にグ
ラビア印刷にて透明黄色からなる着色印刷層を設けた。Example 2 After obtaining a metal vapor deposited film in which an aluminum vapor deposited layer with a thickness of 500X was formed on one side of a polyethylene terephthalate film with a thickness of 0.012+u+, the gold E4M-Ji
A colored printed layer consisting of transparent yellow was provided on the polyethylene terephthalate film surface of the film by gravure printing.
次いで、前記金属蒸着フィルムの着色印刷層面に厚さ０
．８Ｈのポリウレタン樹脂のＴダイ押出層からなる表面
層を形成すると共に、同じく前記金属蒸着フィルムの金
属蒸着層面に厚さ０．０５ｍ厘のポリカーボネート樹脂
層からなるプライマー層を介して厚さ１．５１のポリウ
レタン樹脂の射出成形層からなる裏面層を形成して時計
バンド用素材を得た後、前記時計バンド素材を所定のサ
イズの帯状物に截断することにより本発明の１実施例品
たる時計バンドを得た。Next, a layer with a thickness of 0 is applied to the colored printed layer surface of the metal vapor deposited film.
．． A surface layer made of a T-die extrusion layer of 8H polyurethane resin is formed, and a primer layer made of a polycarbonate resin layer with a thickness of 0.05 m is interposed on the metal vapor deposited layer surface of the metal vapor deposited film to a thickness of 1.5 mm. After forming a back layer consisting of an injection molded layer of polyurethane resin to obtain a watch band material, the watch band material is cut into strips of a predetermined size to obtain a watch band, which is an embodiment of the present invention. I got it.
実施例３
前記実施例２における時計バンド素材の表面層たるポリ
ウレタン樹脂層面に、出力３０Ｗの炭酸ガスレーザーを
ｉｎ／分の速度で照射し、表面が細溝加工されている時
計バンド素材を得た後、該時計バンド素材を所定のサイ
ズの帯状物に截断することにより本発明の１実施例品た
る時計バンドを得た。Example 3 A carbon dioxide laser with an output of 30 W was irradiated on the surface of the polyurethane resin layer, which was the surface layer of the watch band material in Example 2, at a speed of in/min to obtain a watch band material whose surface was processed with fine grooves. Thereafter, the watch band material was cut into strips of a predetermined size to obtain a watch band as an example of the present invention.
実施例４
前記実施例２における厚さ０．８ｍｉ＋のポリウレタン
樹脂のＴダイ押出層からなる表面層の形成工程を、表面
にシボ模様を有する冷却ロールによる加圧、冷却工程を
付して得られた厚さ０．８層ｍのポリウレタン樹脂フィ
ルムを得た後、これを金属蒸着フィルムの着色印刷層面
に積層することによって形成する工程に置き代える以外
は、全て前記実施例２と同様に処置し、本発明の１実施
例品たる時計バンドを得た。Example 4 The process of forming a surface layer consisting of a T-die extrusion layer of polyurethane resin having a thickness of 0.8 mi+ in Example 2 was performed by adding pressure and a cooling process using a cooling roll having a textured pattern on the surface. All procedures were carried out in the same manner as in Example 2, except that after obtaining a polyurethane resin film with a thickness of 0.8 m, this was formed by laminating it on the colored printed layer surface of the metallized film. A watch band, which is an example of the present invention, was obtained.
実施例５
前記実施例４における時計バンド素材の表面層たるマッ
ト加工表面を有するポリウレタン樹脂層の表面に１着色
インキと透明インキとによる印刷層をシルクスクリーン
印刷で形成し、透明インキによる印刷層を有する部分の
みに光沢が現出されている時計バンド素材を得た後、該
時計バンド素材を所定のサイズの帯状物に裁断すること
により本発明の１実施例品たる時計バンドを得た。Example 5 A printed layer of a colored ink and a transparent ink was formed by silk screen printing on the surface of the polyurethane resin layer having a matte surface, which was the surface layer of the watch band material in Example 4, and the printed layer of the transparent ink was formed by silk screen printing. After obtaining a watch band material with luster appearing only in the areas where the watch band is present, the watch band material was cut into strips of a predetermined size to obtain a watch band as an example of the present invention.
［作用および効果］
本発明の時計バンドは、扁平状のエラストマー樹脂層中
に金属蒸着フィルムが前記扁平状のエラストマー樹脂層
の長さ方向と金属蒸着フィルムの長さ方向とが同一方向
となるようにして埋没された構成からなる積層構成とさ
れているものであり、エラストマー樹脂と金属蒸着フィ
ルムとで得られるものであるから、メタリック調の高品
質感を呈する意匠効果に優れた時計バンドを、簡単かつ
安価に製造し得るという作用。[Operations and Effects] The watch band of the present invention has a metal vapor deposited film in the flat elastomer resin layer such that the length direction of the flat elastomer resin layer and the length direction of the metal vapor deposit film are in the same direction. It has a laminated structure consisting of a buried structure, and is made of elastomer resin and metal vapor deposited film, so it is possible to create a watch band with an excellent design effect that has a metallic-like high quality feel. The effect is that it can be manufactured easily and inexpensively.
効果を奏するものである。It is effective.
Claims (11)
備する樹脂フィルムからなる金属蒸着フィルムが、前記
扁平状のエラストマー樹脂層の長さ方向と金属蒸着フィ
ルムの長さ方向とが同一方向となるようにして埋没され
ていることを特徴とする時計バンド。(1) A metallized film consisting of a resin film having a metallized layer in a flat elastomer resin layer is such that the length direction of the flat elastomer resin layer and the length direction of the metallized film are in the same direction. A watch band characterized by being buried in a manner that makes it look like a watch band.
蒸着フィルムが着色印刷層を有する金属蒸着フィルムで
ある特許請求の範囲第１項記載の時計バンド。(2) The watch band according to claim 1, wherein the metallized film made of a resin film having a metallized layer is a metallized film having a colored printed layer.
ストマー樹脂層が、前記金属蒸着フィルムに積層されて
いるエラストマー樹脂フィルムで構成されている特許請
求の範囲第１項または第２項記載の時計バンド。(3) The watch band according to claim 1 or 2, wherein the elastomer resin layer on the side of the metallized layer of the metallized film is composed of an elastomer resin film laminated on the metallized film.
ーボネートからなるプライマー層を具備している金属蒸
着フィルムである特許請求の範囲第１、第２、または第
３項記載の時計バンド。(4) The watch band according to claim 1, 2, or 3, wherein the metallized film is a metallized film comprising a primer layer made of polyurethane or polycarbonate.
樹脂層の表面がレーザー光線によるスクライビング（溝
掘り）加工されている特許請求の範囲第１〜４のうちの
いずれかの１項記載の時計バンド。(5) The watch band according to any one of claims 1 to 4, wherein the surface of the elastomer resin layer constituting the front side of the watch band is scribed (grooved) with a laser beam. .
樹脂層の表面がマット（艶消し）加工されている特許請
求の範囲第１〜５のうちのいずれかの１項記載の時計バ
ンド。(6) The watch band according to any one of claims 1 to 5, wherein the surface of the elastomer resin layer constituting the front side of the watch band is matte processed.
樹脂層の表面におけるマット加工面に部分的な透明印刷
層が形成されている特許請求の範囲第６項記載の時計バ
ンド。(7) The watch band according to claim 6, wherein a partial transparent printing layer is formed on the matte surface of the elastomer resin layer constituting the front side of the watch band.
ラストマー樹脂層が、射出成形または注型キャスト成形
によるエラストマー樹脂層で構成されている特許請求の
範囲第１〜７のうちのいずれかの１項記載の時計バンド
。(8) Any one of claims 1 to 7, wherein the elastomer resin layer on the side of the non-metal-deposited layer of the metal-deposited film is composed of an elastomer resin layer formed by injection molding or cast cast molding. Watch band as described.
ストマー樹脂層が、射出成形またな注型キャスト成形に
よるエラストマー樹脂層で構成されている特許請求の範
囲第１、第２、第４、第５、第６、第７、または第８項
記載の時計バンド。(9) Claims 1, 2, 4, 5, etc., wherein the elastomer resin layer on the side of the metal evaporated layer of the metal evaporated film is formed by injection molding or cast cast molding. The watch band according to item 6, 7, or 8.
レフィン系、ポリスチレン系、ポリエステル系、ポリア
ミド系、軟質ポリ塩化ビニルの中から選択される樹脂で
構成されている特許請求の範囲第１〜９のうちのいずれ
かの１項記載の時計バンド。(10) Any one of claims 1 to 9, wherein the elastomer resin layer is made of a resin selected from polyurethane, polyolefin, polystyrene, polyester, polyamide, and soft polyvinyl chloride. The watch band described in item 1 above.
ラストマー樹脂層の厚さと非金属蒸着層面側におけるエ
ラストマー樹脂層の厚さとの比が１００：２５〜４００
の範囲内である特許請求の範囲第１〜１０のうちのいず
れかの１項記載の時計バンド。(11) The ratio of the thickness of the elastomer resin layer on the metal vapor deposited layer side of the metal vapor deposited film to the thickness of the elastomer resin layer on the nonmetal vapor deposited layer side is 100:25 to 400.
A watch band according to any one of claims 1 to 10 falling within the scope of the invention.