JPS638246A - Method of papering fiber reinforced inorganic sheet - Google Patents

Method of papering fiber reinforced inorganic sheet

Info

Publication number
JPS638246A
JPS638246A JP15015886A JP15015886A JPS638246A JP S638246 A JPS638246 A JP S638246A JP 15015886 A JP15015886 A JP 15015886A JP 15015886 A JP15015886 A JP 15015886A JP S638246 A JPS638246 A JP S638246A
Authority
JP
Japan
Prior art keywords
pulp
freeness
reinforced inorganic
fiber
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP15015886A
Other languages
Japanese (ja)
Inventor
正 吉井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kubota Corp
Original Assignee
Kubota Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kubota Corp filed Critical Kubota Corp
Priority to JP15015886A priority Critical patent/JPS638246A/en
Publication of JPS638246A publication Critical patent/JPS638246A/en
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

【発明の詳細な説明】 〔産業上の利用分野〕 この発明は、繊維補強無機質板の抄造方法に関する。[Detailed description of the invention] [Industrial application field] The present invention relates to a method for making a fiber-reinforced inorganic board.

〔従来の技術〕[Conventional technology]

セメントスラリーを抄造して製板する場合、石綿を無配
合とすると、セメント等の粉体原料がワイヤーシリンダ
から抜は落ち、抄造歩留が低下する、及び濾水量が増加
し、種膜が不均質になるため製品の地合が悪くなると言
った問題がをる。
When making sheets from cement slurry, if asbestos is not added, powder raw materials such as cement will fall out of the wire cylinder, the papermaking yield will decrease, the amount of drainage will increase, and the seed film will not be formed. This causes problems such as poor product consistency due to the homogeneity.

そこで、石綿無添加の場合に、これを補うためパルプを
添加することが行なわれる。
Therefore, when asbestos is not added, pulp is added to compensate for this.

〔従来技術の問題点〕[Problems with conventional technology]

ところで、パルプを添加する場合、パルプを所定の濾水
度まで叩解し、均一な材質とすることが通常行なわれる
が一定の濾水度まで均一にパルプを叩解するには別途、
叩解工程を必要とする上、その工程管理も必要となり工
数が増加すると言った問題が有った。
By the way, when adding pulp, it is usually done to beat the pulp to a predetermined freeness to make it into a uniform material, but in order to beat the pulp uniformly to a certain freeness, a separate process is required.
There was a problem in that it required a beating process and also required process control, which increased the number of man-hours.

〔問題点を解決する技術〕[Technology to solve problems]

この発明は、上記問題点に鑑み、石綿に代え、パルプを
添加する場合、パルプの叩解工程を省略し、あるいは、
叩解するにしても簡単に終了し得る改良された繊維補強
無機質板の抄造方法を得ることを目的としてなされたも
のである。
In view of the above problems, this invention omit the pulp beating process when pulp is added instead of asbestos, or
The purpose of this invention is to provide an improved method for manufacturing fiber-reinforced inorganic boards that can be easily completed even if beating is performed.

〔作用〕[Effect]

抄造効率を高めるためのパルプの濾水度は通常カナディ
アン濾水度で430〜47klとされる。そこで、種々
濾水度のパルプであって、濾水度の異なるものを混合し
、これらの平均濾水度が上記範囲となるようにすれば、
結果として充分な濾水度が得られる。
The freeness of pulp for increasing the papermaking efficiency is usually Canadian freeness of 430 to 47 kl. Therefore, if pulps with various freenesses are mixed and their average freeness falls within the above range,
As a result, sufficient freeness is obtained.

即ち、未叩解の濾水度の高いパルプと未叩解の濾水度の
低いパルプとを混合し、その平均濾水度を所定の値とす
れば、全(叩解工程を要することなく所定の抄造効率と
することが出来る。
In other words, if unbeaten pulp with high freeness and unbeaten pulp with low freeness are mixed and their average freeness is set to a predetermined value, the total It can be made efficient.

また、特に濾水度の低いパルプで、所定のものが得られ
ない場合は、この部分のパルプのみを叩解し、濾水度の
高いパルプとの平均濾水度が所定値となるようにするの
である。
In addition, if the specified pulp cannot be obtained especially with a pulp with a low freeness, only this part of the pulp is beaten so that the average freeness with the pulp with a high freeness becomes the specified value. It is.

なお、上記混合バルブの添加量は全固形分に対し6%以
上とすることが望ましい。
Note that the amount of the mixing valve added is preferably 6% or more based on the total solid content.

この理由は、6%より少ないと充分な抄き上げ効率とな
し得す、本発明の効果が得られなくなるからである。
The reason for this is that if it is less than 6%, sufficient paper-raising efficiency cannot be achieved, but the effects of the present invention cannot be obtained.

〔実施例〕〔Example〕

次に、この発明の詳細な説明する。 Next, the present invention will be explained in detail.

〈実施例1〉 未叩解のパルプであって、カナディアン濾水度(以下単
に濾水度と言う)が707m l、及び未叩解のパルプ
であって、濾水度が114mlのものを同量ずつ配合し
、該配合バルブを無石綿とされたセメントスラリーに供
給し、ワイヤーシリンダーで種膜を抄造し、これを積層
して製板した。
<Example 1> Equal amounts of unbeaten pulp with a Canadian freeness (hereinafter simply referred to as freeness) of 707 ml and unbeaten pulp with a freeness of 114 ml The blending valve was supplied to asbestos-free cement slurry, and a seed film was formed using a wire cylinder, which was laminated to form a plate.

このときの抄造歩留、濾水速度、地合等は別表の通りで
あった。
The papermaking yield, drainage rate, formation, etc. at this time were as shown in the attached table.

なお、別表において比較例は、添加されるパルプをすべ
て均一に濾水度457となるまで叩解処理したものであ
る。
In addition, in the comparative example in the attached table, all the added pulps were uniformly beaten until the freeness level was 457.

〈実施例2〉 セメントスラリーに添加必要量の濾水度が707mAの
パルプのうち、その半量のみを濾水度110となるまで
叩解し、これを残りの未叩解のパルプと混合し、実施例
1と同様な抄造を行なったところ、実施例1と同じ結果
が得られた。
<Example 2> Of the required amount of pulp with a freeness of 707 mA to be added to the cement slurry, only half of it was beaten until the freeness became 110, and this was mixed with the remaining unbeaten pulp. When papermaking was carried out in the same manner as in Example 1, the same results as in Example 1 were obtained.

〈実施例3〉 濾水度が90011112のパルプを濾水度が100m
 lとなるまで叩解処理し、次いで、その半量を取り出
し、残りのパルプを濾水度が110mlとなるまで叩解
し、先のパルプと混合し、これを必要量、石綿無添加の
スラリーに添加し、実施例1と同様の抄造を行なった。
<Example 3> Pulp with a freeness of 90011112 and a freeness of 100 m
The remaining pulp was beaten until the freeness reached 110 ml, mixed with the previous pulp, and the required amount was added to the asbestos-free slurry. The same papermaking as in Example 1 was carried out.

この場合も実施例1と全(同様な結果が得られた。In this case as well, the same results as in Example 1 were obtained.

〔効果〕〔effect〕

この発明は、以上のように構成されているので、石綿無
配合のセメントスラリーにパルプを添加する場合、濾水
度の大小異なるパルプを混合して、その平均濾水度を所
定の濾水度とする構成であるから、叩解処理を全く必要
としないか、叩解処理をするにしても従来に比し、その
処理が著しく簡略化されるため、省エネルギが図られる
といった効果を有する。
Since this invention is configured as described above, when adding pulp to asbestos-free cement slurry, pulps with different freenesses are mixed and the average freeness is adjusted to a predetermined freeness level. Because of this structure, there is no need for beating treatment at all, or even if beating treatment is performed, the treatment is significantly simplified compared to the conventional method, so it has the effect of saving energy.

Claims (3)

【特許請求の範囲】[Claims] (1)セメント及びパルプを含むスラリーを抄造して板
材を製造する場合において、濾水度の高いパルプと濾水
度の低いパルプとを混合してセメントスラリーに混入し
、該スラリーを抄造することを特徴とする繊維補強無機
質板の抄造方法。
(1) When manufacturing board materials by paper-making a slurry containing cement and pulp, pulp with high freeness and pulp with low freeness are mixed into cement slurry and the slurry is made into paper. A method for making a fiber-reinforced inorganic board.
(2)使用するパルプの濾水度がカナディアン濾水度で
濾水度の高いパルプが700ml以上、濾水度の低いパ
ルプが200ml以下であり、かつ、両パルプを1:1
で混合して成る特許請求の範囲1項記載の繊維補強無機
質板の抄造方法。
(2) The freeness of the pulp used is Canadian freeness, and the pulp with high freeness is 700 ml or more and the pulp with low freeness is 200 ml or less, and both pulps are mixed at a ratio of 1:1.
A method for making a fiber-reinforced inorganic board according to claim 1, wherein the fiber-reinforced inorganic board is mixed with:
(3)パルプ全体の配合量が全固形分に対し6%以上で
ある特許請求の範囲第1項、又は第2項記載の繊維補強
無機質板の抄造方法。
(3) The method for making a fiber-reinforced inorganic board according to claim 1 or 2, wherein the content of the entire pulp is 6% or more based on the total solid content.
JP15015886A 1986-06-25 1986-06-25 Method of papering fiber reinforced inorganic sheet Pending JPS638246A (en)