JPS63266796A - Electric heater unit - Google Patents
Electric heater unitInfo
- Publication number
- JPS63266796A JPS63266796A JP10037687A JP10037687A JPS63266796A JP S63266796 A JPS63266796 A JP S63266796A JP 10037687 A JP10037687 A JP 10037687A JP 10037687 A JP10037687 A JP 10037687A JP S63266796 A JPS63266796 A JP S63266796A
- Authority
- JP
- Japan
- Prior art keywords
- heat insulating
- alumina
- fiber
- silica
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、一般家庭において、主に調理用に使用される
電熱ユニットに関するものである。DETAILED DESCRIPTION OF THE INVENTION FIELD OF INDUSTRIAL APPLICATION The present invention relates to an electric heating unit used mainly for cooking in ordinary households.
従来の技術
従来より、一般家庭で使用される調理用の電熱ユニット
としては、陶器の上に、螺旋状に巻いた電熱線を配設し
た電気こんろや、シーズヒータを渦巻状に巻いてユニッ
ト化した電気レンジなどがある。Conventional technology Traditionally, electric heating units for cooking used in general households include electric stoves with spirally wound heating wires placed on ceramics, and units with sheathed heaters wound in a spiral pattern. There are modern electric ranges.
これら以外に、欧米では、螺旋状に巻いた電熱線を断熱
材に設けた溝に配設し、この上にセラミックガラス板を
置き、このセラミックガラス板を加熱面とするスムーズ
トップと呼ばれる電熱ユニットなどが広く使用されてい
る。In addition to these, in Europe and the United States, there is an electric heating unit called a smooth top, in which a spirally wound heating wire is placed in a groove in the insulation material, a ceramic glass plate is placed on top of this, and this ceramic glass plate serves as the heating surface. etc. are widely used.
発明が解決しようとする問題点
しかしながら、スムーズトップと呼ばれる電熱ユニット
で使用される断熱材は、耐熱性や断熱性に優れているた
め、高温で使用されても実際の使用上大きな問題はない
が、断熱材そのものが吸湿性に富んでいるため、多湿雰
囲気中に放置されると、電気特性の著しい劣化が生じる
という問題があった。Problems to be Solved by the Invention However, the heat insulating material used in the electric heating unit called Smooth Top has excellent heat resistance and heat insulation properties, so there are no major problems in actual use even if it is used at high temperatures. However, since the heat insulating material itself is highly hygroscopic, there is a problem in that if it is left in a humid atmosphere, its electrical characteristics will significantly deteriorate.
本発明はこのような問題点を解決するもので、多湿雰囲
気中に放置されても電気特性が優れている電熱ユニット
を提供することを目的とするものである。The present invention solves these problems and aims to provide an electric heating unit that has excellent electrical characteristics even when left in a humid atmosphere.
問題点を解決するだめの手段
上記問題点を解決するために本発明は、金属板もしくは
結晶化ガラス板からなる天板と、螺旋状に巻かれた電熱
線と、この電熱線を渦巻状に配設する溝を有し、かつシ
リカ−アルミナ繊維を主成分とする断熱材からなる断熱
基盤と、この断熱基盤を収納する収納ケースとを備え、
前記シリカ−アルミナ繊維を主成分とする断熱材として
、数αの長繊維と、数１００μｍの短繊維の混合物から
なり、かつ結合材としてアルミナゾルを使用したものを
用いたものである。Means for Solving the Problems In order to solve the above problems, the present invention provides a top plate made of a metal plate or a crystallized glass plate, a spirally wound heating wire, and a spirally wound heating wire. A heat insulating base made of a heat insulating material mainly composed of silica-alumina fibers and a storage case for storing the heat insulating base,
The heat insulating material mainly composed of silica-alumina fibers is made of a mixture of long fibers of several α and short fibers of several 100 μm, and uses alumina sol as a binder.
作 用
従来よりスムーズトップ等の電熱器に使用されている断
熱材は、シリカ−アルミナ繊維を主成分とし、かつシリ
カゾルを結合材としたものである。Function The heat insulating materials conventionally used in electric heaters such as smooth tops have silica-alumina fibers as a main component and silica sol as a binder.
そしてこれを真空成型し、約２０６℃の温度で乾燥する
ことにより、製造される。このため、結合材として使用
されたシリカゾルは、不安定な非晶質状態のままで存在
し、多湿雰囲気中に放置されると容易に水分を吸湿し、
電気特性の著しい低下現象が生じ、実際の使用上問題が
あった。Then, this is vacuum formed and dried at a temperature of about 206° C., thereby producing the product. For this reason, the silica sol used as a binder exists in an unstable amorphous state and easily absorbs moisture when left in a humid atmosphere.
This caused a phenomenon in which the electrical properties were significantly deteriorated, posing a problem in actual use.
また、この吸湿性を防止するために、結合材として、非
吸湿性に比較的優れたアルミナゾルを使用する方法があ
るが、この場合、断熱材の強度を確保することが難しく
、電熱線を配設する渦巻状の溝加工等は、不可能に近か
った。In addition, in order to prevent this hygroscopicity, there is a method of using alumina sol, which has relatively excellent non-hygroscopicity, as a binding material, but in this case, it is difficult to ensure the strength of the insulation material, and heating wires are used. It was nearly impossible to create spiral grooves.
しかし、本発明の断熱材では、従来よりアルミナゾルを
結合材として使用した際の強度の確保の困難さを、シリ
カ−アルミナ繊維の繊維長の異なるものを混合すること
により解決したものである。However, in the heat insulating material of the present invention, the difficulty in securing strength when using alumina sol as a binder has been solved by mixing silica-alumina fibers with different fiber lengths.
これは、長繊維のものと短繊維のものとが複雑にからみ
合うため、アルミナゾルのように、比較的結合力の弱い
結合材を使用した際にも、強度を保つことができるもの
と推定される。This is because the long fibers and short fibers are intricately intertwined, so it is presumed that the strength can be maintained even when using a binder with relatively weak binding force, such as alumina sol. Ru.
一方、この方法で得られた断熱材は、結合材としてアル
ミナゾルを使用しているため、吸湿性も少なく、したが
って多湿雰囲気中に放置されても電気特性の著しい低下
は見られない。On the other hand, since the heat insulating material obtained by this method uses alumina sol as a binding material, it has low hygroscopicity, and therefore, even when left in a humid atmosphere, no significant deterioration in electrical properties is observed.
以上の理由により、前述した断熱材を断熱基盤として用
いた電熱ユニットでは、多湿雰囲気中に放置されても電
気特性は優れたものとなる。For the above reasons, an electric heating unit using the above-mentioned heat insulating material as a heat insulating base has excellent electrical characteristics even when left in a humid atmosphere.
実施例
以下、本発明の具体的な実施例を図面に基づいて説明す
る。図において、１は結晶化ガラス板からなる天板であ
る。２は平均繊維長が２〜３１の長繊維のシリカ−アル
ミナ繊維と、平均繊維長が６００μｍの短繊維のシリカ
−アルミナ繊維を混合したものを主成分とし、かつアル
ミナゾルを結合材として、真空成型された断熱材からな
る断熱基盤で、この断熱基盤２には渦巻状の溝２ａが設
けられている。３は螺旋状に巻かれた電熱線で、この電
熱線３は断熱基盤２に設けられた溝２ａに配設されてい
る。４は電熱線３を配設した断熱基盤２を収納する収納
ケースで、この収納ケース４はステンレス鋼により構成
されている。Embodiments Hereinafter, specific embodiments of the present invention will be described based on the drawings. In the figure, 1 is a top plate made of a crystallized glass plate. 2 has a mixture of long silica-alumina fibers with an average fiber length of 2 to 31 and short silica-alumina fibers with an average fiber length of 600 μm as the main component, and uses alumina sol as a binder, and is vacuum formed. The heat insulating base 2 is made of a heat insulating material, and the heat insulating base 2 is provided with a spiral groove 2a. Reference numeral 3 denotes a spirally wound heating wire, and this heating wire 3 is disposed in a groove 2a provided in the heat insulating base 2. Reference numeral 4 denotes a storage case that stores the heat insulating base 2 on which the heating wire 3 is arranged, and this storage case 4 is made of stainless steel.
６は絶縁碍子であり、６は電気取り出し端子であり、こ
れらは収納ケース４の下側に設けられている。6 is an insulator, and 6 is an electrical outlet terminal, which are provided on the lower side of the storage case 4.
このような構成を有する本発明の電熱ユニットの多湿雰
囲気中での電気特性を評価するため、４０℃で相対湿度
９６％の多湿雰囲気中に１週間投入し、この後、絶縁抵
抗および耐電圧を測定した。In order to evaluate the electrical characteristics of the electric heating unit of the present invention having such a configuration in a humid atmosphere, it was placed in a humid atmosphere at 40°C and a relative humidity of 96% for one week, and then the insulation resistance and withstand voltage were measured. It was measured.
なお、これらの電気特性は、収納ケース４と電気取り出
し端子６の間で測定した。Note that these electrical characteristics were measured between the storage case 4 and the electrical outlet terminal 6.
また、比較のために、断熱基盤２として、シリカ−アル
ミナ繊維を主成分とし、かつシリカゾルをバインダーと
した断熱材を用いてなる従来の電熱ユニットについても
、上記と同様にして電気特性を測定した。For comparison, the electrical properties of a conventional electric heating unit using a heat insulating material mainly composed of silica-alumina fibers and silica sol as a binder as the heat insulating base 2 were also measured in the same manner as above. .
これらの測定結果を次表に示した。The results of these measurements are shown in the table below.
表
表から明らかなように、従来のシリカゾルをバインダー
として使用した断熱材を用いてなる電熱ユニットでは、
絶縁抵抗が０．１ＭΩ、耐電圧が８００■であり、実際
の使用上、問題があった。As is clear from the table, in electric heating units using conventional heat insulating materials using silica sol as a binder,
The insulation resistance was 0.1 MΩ and the withstand voltage was 800 μm, which caused problems in actual use.
一方、本発明のようにアルミナゾルを結合材として使用
した断熱材を用いてなる電熱ユニットでは、絶縁抵抗が
２０ＭΩ、耐電圧が３０００Ｖ以上と優れた電気特性を
示した。On the other hand, an electric heating unit using a heat insulating material using alumina sol as a binding material as in the present invention exhibited excellent electrical properties with an insulation resistance of 20 MΩ and a withstand voltage of 3000 V or more.
このように、アルミナゾルを結合材として使用した断熱
材を用いることにより、多湿雰囲気中に放置されても電
気特性に優れた電熱ユニットを得ることができる。As described above, by using a heat insulating material using alumina sol as a binding material, it is possible to obtain an electric heating unit that has excellent electrical properties even when left in a humid atmosphere.
また、シリカ−アルミナ繊維の繊維長の異なる長繊維と
短繊維のものを混合し、これを真空成型することにより
、渦巻状等の種々の形状に成型し得る強度を確保するこ
とができる。Further, by mixing long fibers and short fibers of silica-alumina fibers with different fiber lengths and vacuum forming the mixture, it is possible to ensure the strength that allows molding into various shapes such as a spiral shape.
なお、本発明の実施例においては、天板を結晶化ガラス
で構成したものについて説明したが、特にこれに限定さ
れるものではなく、金属板で構成してもよいものである
。In the embodiments of the present invention, the top plate is made of crystallized glass, but the top plate is not limited to this, and may be made of a metal plate.
発明の効果
上記実施例の説明から明らかなように本発明によれば、
金属板もしくは結晶化ガラス板からなる天板と、螺旋状
に巻かれた電熱線と、この電熱線を渦巻状に配設する溝
を有し、かつシリカ−アルミナ繊維を主成分とする断熱
材からなる断熱基盤と、この断熱基盤を収納する収納ケ
ースとを備え、前記シリカ−アルミナ繊維を主成分とす
る断熱材として、数１の長繊維と、数１００μｍの短繊
維の混合物からなり、かつ結合材としてアルミナゾルを
使用したものを用いているため、多湿雰囲気中に放置さ
れても電気特性に優れている電熱ユニットを提供するこ
とができるものである。Effects of the Invention As is clear from the description of the above embodiments, according to the present invention,
A heat insulating material that has a top plate made of a metal plate or a crystallized glass plate, a spirally wound heating wire, and a groove in which the heating wire is arranged in a spiral shape, and whose main component is silica-alumina fiber. and a storage case for storing the heat insulating base, and the heat insulating material mainly composed of silica-alumina fibers is made of a mixture of long fibers of several 1 and short fibers of several 100 μm, and Since alumina sol is used as the binding material, it is possible to provide an electric heating unit that has excellent electrical characteristics even when left in a humid atmosphere.
図は本発明の一実施例を示す電熱ユニットの断面図であ
る。
１・・・・・・天板、２・・・・・・断熱基盤、２ａ・
・・・・・溝、３・・・・・・電熱線、４・・・・・・
収納ケース。The figure is a sectional view of an electric heating unit showing an embodiment of the present invention. 1...Top plate, 2...Insulation base, 2a.
...Groove, 3...Heating wire, 4...
storage case.
Claims (1)
に巻かれた電熱線と、この電熱線を渦巻状に配設する溝
を有し、かつシリカ−アルミナ繊維を主成分とする断熱
材からなる断熱基盤と、この断熱基盤を収納する収納ケ
ースとを備え、前記シリカ−アルミナ繊維を主成分とす
る断熱材として、数ｃｍの長繊維と、数１００μｍの短
繊維の混合物からなり、かつ結合材としてアルミナゾル
を使用したものを用いたことを特徴とする電熱ユニット
。A heat insulating material that has a top plate made of a metal plate or a crystallized glass plate, a spirally wound heating wire, and a groove in which the heating wire is arranged in a spiral shape, and whose main component is silica-alumina fiber. and a storage case for storing this heat insulating base, the heat insulating material mainly consisting of silica-alumina fibers is made of a mixture of long fibers of several cm and short fibers of several 100 μm, and An electric heating unit characterized by using alumina sol as a binding material.