JPS6260899A - Traveler for spinning machine - Google Patents

Abstract

PURPOSE:To facilitate finishing in a production stage and the control of yarn count in a packing stage by forming color plated films having different colors for each count on the surfaces of metallic travelers by electrodeposition. CONSTITUTION:Color plated films 2 having different colors such as red, blue, gold, green, black and brown for each count are formed on the surfaces of horizontal metallic travelers 1 made of a hard steel wire rod or an alloy steel wire by electrodeposition after Ni plating is carried out on the surfaces of the travelers 1 as required. Thus, superior corrosion resistance including acid and alkali resistances is provided, the control of production and stock of products is facilitated and the occurrence of trouble by the simultaneous use of travelers in a spinning mill is prevented.

Description

[Detailed Description of the Invention] Industrial Application Field The present invention is directed to forming various color plating films on the surface of a metal traveler (by electrodeposition coating method) to prevent contamination of the traveler and to facilitate count control. This is related to the purpose of the spinning machine traveler.

BACKGROUND ART Conventionally, metal plates 2 used in spinning machines and yarn twisting machines are formed by cutting a hard steel wire into a predetermined size using a forming machine and simultaneously forming it into a predetermined vertical or horizontal shape. These metal travelers may be left as they are, or may be surface-treated with nickel or chrome plating. The above-mentioned travelers are available in dozens of counts (for example, 110 to 30/2) so that you can select the traveler with the appropriate count based on the spun yarn count, ring diameter, and spindle speed constant.

Travelers such as O, 5th to 30th) are available. Therefore, the weight difference between these numbers is, for example, 0.05 to 2.0% per 100 pieces for O-type 2-pellers.
07, so it cannot be determined just by its shape and appearance.
If they are accidentally mixed in during the manufacturing process or during use, they cannot be distinguished and may cause problems such as yarn breakage, yarn fuzz, and traveler burn during spinning.

Means for Solving the Problems The present invention has been made to solve the above-mentioned problems.The present invention has been made in order to solve the above-mentioned problems. Red and blue, each with a different color.

By forming a colored plating film such as gold, green, black, or brown, it has excellent corrosion resistance such as acid resistance and alkali resistance. The purpose is to eliminate problems caused by mixing and mixing.

An embodiment of the present invention will be described below with reference to the drawings.

Example 81￥1 The figure is a partially cutaway cross-sectional view of a traveler for a spinning machine showing one embodiment of the present invention. Electrodeposition was performed on the surface of a horizontal metal traveler (1) made of hard steel wire or alloy steel wire. Water-based resin paint colored with pigments or dyes as electrodeposition paint (for example, brown color) using a coating device.

Electrodeposition conditions were 1 o 6 o sec, 2 o sec, using the traveler as the cathode and the paint tank as the anode.
The charge traveler surface (1) is electrically coated by passing a direct current at 8°C. (!) is the brown colored plating film formed on the surface of the metal traveler base in this way, and is further washed with water and baked to dry to form a uniform film that is firmly adhered. The pigment and dye are red.

Each traveler size can be dyed using blue, yellow, black, white, green, etc., or intermediate colors obtained by mixing these colors.

FIG. 2 is a partially cutaway sectional view showing another embodiment,
A red (colored paint, such as a urethane-modified epoxy resin water-based paint) is electrically deposited on the nickel-plated IIX+31 surface of a vertical metal traveler (4) made of a hard steel wire on which a nickel-plated film (3) has been previously formed on the base surface. I let it happen.

fl+ is a red color plating film formed on the nickel plating film.

Effects of the Invention Since the present invention is constructed as described above, it improves the corrosion resistance of the metal traveler, and forms a beautiful and uniform color plated plate with different colors for each count, so that it can be easily applied in the finishing and packaging process at Nagisa Engineering. This makes it easier to manage the count, prevents mixing and mixing of different counts, and makes it easy to find even if they are mixed. In addition, it is possible to reliably manage the traveler type and count at the spinning factory based on color, eliminating problems such as yarn breakage due to the mixing of different types of travellers, occurrence of yarn fluff, and changes in the spinning pattern. This is an effective invention.

[Brief explanation of the drawing]

FIG. 1 is a partially cutaway sectional view of a traveler for a spinning machine showing one embodiment of the present invention, and FIG. 2 is a partially cutaway sectional view showing an embodiment on the same side. (1)...Horizontal metal traveler, +! l, fi+
... Color plating film, (3) ... Nickel plating film, (5) ... Brightly colored metal traveler.

Claims (2)

[Claims] (1) A traveler for a spinning machine, characterized in that a color plating film is formed on the surface of the metal traveler by electrodeposition. (2) The traveler for a spinning machine as set forth in claim 1, wherein the metal traveler is pre-plated with nickel.