(Industrial Application Field) This invention relates to a video disc record made of a conductive resin composition, particularly a graft polymer obtained by graft polymerizing a vinyl chloride monomer to a copolymer of ethylene and vinyl acetate, and other materials. This invention relates to a video disc record made of a resin mixture with a vinyl chloride polymer. (Prior Art) Vinyl chloride resins have good weather resistance and excellent mechanical strength, so they are used for various molded products such as pipes, joints, and plates. Recently, attempts have been made to mix electrically conductive fillers with vinyl chloride resins to produce electrically conductive resin compositions. This conductive resin composition is said to be suitable for making capacitive video disc records. Typical conductive fillers include fine metal powder and carbon black, of which carbon black is the most commonly used. There are many types of carbon black that can be used as a conductive filler, but Akzo's ``Ketschen Black'' is particularly effective in imparting conductivity.
considered to be the most preferred. As the vinyl chloride-based resin used to blend carbon black, in addition to polyvinyl chloride, a homopolymer of vinyl chloride, it has been proposed to use a mixture of binary copolymers of vinyl chloride and other monomers. It was done. For example, JP-A-53-115104 discloses that 44 parts by weight of a vinyl chloride copolymer containing 5% by weight of propylene, 10 parts by weight of a vinyl chloride copolymer containing 15% by weight of vinyl acetate, and 25 parts by weight of a vinyl chloride copolymer containing 15% by weight of vinyl acetate. It states that a resin composition prepared by mixing 10 parts by weight of a vinyl chloride copolymer containing a maleic ester of 10% by weight and adding a conductive filler to this mixture is suitable for making video disc records. Also, RCA Review, March 1978 issue, pages 87-115, and JP-A-55-
Publication No. 97034 describes that homopolymers of vinyl chloride and copolymers of vinyl chloride and propylene are used in video disc records. By the way, in order to impart conductivity by blending a conductive filler, particularly carbon black, with these vinyl chloride resins, it has been necessary to blend a large amount of carbon black. However, when such a large amount of carbon black is blended, the melt fluidity and thermal stability of the composition deteriorate, making it difficult to mold. (Problems to be solved by the invention) This invention solves the problem of the weather resistance of vinyl chloride resin,
We improved the vinyl chloride resin while retaining good properties such as mechanical strength, added carbon black to the improved resin to give it electrical conductivity, and improved the resulting composition by improving its melt flowability and thermal stability. The object of the present invention is to provide a video disc record with excellent performance and suitable for manufacturing video disc records, thereby providing a video disc record suitable for practical use. (Means for Solving the Problem) The inventor first attempted to produce a vinyl chloride resin that retains the good properties of vinyl chloride resin and has good melt flowability and thermal stability. I planned it. Then, various vinyl chloride resins were produced, carbon black was blended therein, and the physical properties of the compositions thus obtained were measured. the result,
To a graft polymer having a specific average degree of polymerization obtained by graft polymerizing a vinyl chloride monomer to a copolymer of ethylene and vinyl acetate, another vinyl chloride resin having a specific degree of polymerization is added and mixed in a specific ratio, Furthermore, it has been found that when a specific proportion of carbon black is added to this resin mixture, the composition has excellent heat resistance, good melt flowability, and good thermal stability, making it suitable for making video disc records. I found it. Furthermore, it has been found that the composition thus obtained has improved impact resistance than a composition containing polyvinyl chloride as the main resin, and is therefore more suitable for making video disc records. This invention was made based on such knowledge. This invention provides a copolymer of ethylene and vinyl acetate containing 10 to 65% by weight of vinyl acetate.
An average degree of polymerization of 300 to 700 obtained by graft polymerizing 98 to 40 parts by weight of vinyl chloride to parts by weight.
A resin mixture is prepared by blending 3 to 90 parts by weight of the graft polymer with 97 to 10 parts by weight of another vinyl chloride polymer having an average degree of polymerization of 300 to 600, and 5 to 30 parts by weight of carbon to this resin mixture. This invention relates to a video disc record made by blending black into a conductive resin composition and molding this composition into a thin disk shape. (Example) The copolymer of ethylene and vinyl acetate used in this invention is commercially available in various grades depending on the content of vinyl acetate, molecular weight, and polymerization reaction method. ing.
Generally, as the content of vinyl acetate increases, the compatibility with vinyl chloride improves, but the effect of improving impact resistance decreases, and conversely, as the content of vinyl acetate decreases, the effect of improving impact resistance improves. But,
Compatibility decreases. Therefore, the appropriate content of vinyl acetate in the copolymer is 10 to 65% by weight. The molecular weight of the copolymer of ethylene and vinyl acetate is expressed by the melt index or Mooney viscosity. Among these, the method of expressing melt index is specified in ASTM D-1238;
If the melt index is 100 or more, the melt fluidity will be good, but the impact resistance will be insufficient, and if the melt index is 0.1 or less, the impact resistance will be good, but the melt fluidity will be poor. This property shows that when a graft polymer is obtained by graft polymerizing vinyl chloride onto a copolymer,
It serves as a guideline for predicting the impact resistance or melt flowability of the resulting graft polymer. In addition, the copolymer of ethylene and vinyl acetate is
Its properties differ somewhat depending on the polymerization method used to make it. Generally, when used as a conductive composition, the copolymer may be produced by any of suspension polymerization, emulsion polymerization, solution polymerization, and high-pressure polymerization. When making such a video disc record, since impurities are a problem, it is preferable to use a copolymer produced by a solution polymerization method or a high-pressure polymerization method, which contains fewer impurities. The copolymer of ethylene and vinyl acetate used in this invention may contain not only ethylene and vinyl acetate components but also other monomer components. Other monomer components include various vinyl esters, such as vinyl propionate,
Vinyl butyrate, vinyl esters of branched carboxylic acids having nine or more carbon atoms as shown in Japanese Patent Publication No. 46-12741, or carbon monoxide as shown in Japanese Patent Publication No. 48-26228 are used. It will be done. To graft-polymerize vinyl chloride onto a copolymer of ethylene and vinyl acetate, various methods such as emulsion polymerization, suspension polymerization, solution polymerization, and bulk polymerization can be used. Among these,
It is preferable to use a suspension polymerization method. because,
This is because, according to the suspension polymerization method, fine particles that can be easily mixed uniformly with carbon black can be obtained immediately. Methods for producing graft polymers by suspension polymerization are described, for example, in Japanese Patent Publication No. 39-27876 and Japanese Patent Publication No. 51-1989.
It is described in Publication No. 24391. Specifically, ion-exchanged water, a suspension stabilizer such as polyvinyl alcohol, a radical generator, and, if necessary, a degree-of-polymerization reducing agent are placed in a jacketed polymerization reactor, and ethylene and vinyl acetate are mixed together. The copolymer is added and suspended, then the air inside the can is removed, and then vinyl chloride is forced into the can. Thereafter, the inside of the can is heated from the jacket to dissolve the copolymer in the vinyl chloride and initiate graft polymerization. When graft polymerization begins, heat is generated, so the jacket is cooled afterwards to allow polymerization to proceed to the desired point. After that, unreacted vinyl chloride is collected and removed outside the can.
A thriller-like graft polymer is obtained. The chiller is dehydrated and sieved to obtain fine graft polymer particles. When obtaining the graft polymer as described above,
When vinyl chloride is not used alone, but other monomers coexist with it, a graft polymer is obtained by graft copolymerizing vinyl chloride and other monomers onto a copolymer of ethylene and vinyl acetate. . The graft polymer used in this invention may be a polymer in which other monomers are graft-polymerized together with vinyl chloride. As other monomers, it is preferable to use ethylene and propylene. The content of other monomers is desirably 10% by weight or less based on vinyl chloride. When graft polymerizing vinyl chloride alone to a copolymer of ethylene and vinyl acetate, the ratio of graft polymerization is 2 to 60 parts by weight of the former copolymer and 98 to 98 to 60 parts by weight of the latter vinyl chloride.
40 parts by weight. The degree of polymerization of the graft polymer needs to be within an appropriate range. This is because if the degree of polymerization of the graft polymer becomes too high, the melt fluidity will deteriorate, and conversely, if the degree of polymerization of the graft polymer becomes low, the impact resistance and heat resistance will deteriorate. The appropriate range of polymerization degree varies depending on the intended use. Like a video disc record,
When blending a large amount of carbon black and requiring precise molding, the degree of polymerization of the graft polymer may be adjusted.
It is required to be within the range of 300 to 700. This range is approximately 65 to 90°C, expressed as the temperature at which the graft polymer is polymerized.
In addition, in cases where a small amount of carbon black is sufficient, such as non-static packaging materials,
It is advantageous to have a higher degree of polymerization because a product with higher strength can be obtained. Other vinyl chloride polymers are mixed with the above graft polymer. Various other vinyl chloride polymers can be used. That is, not only a vinyl chloride homopolymer but also a vinyl chloride copolymer can be used. Ethylene and propylene are suitable as copolymerization partner monomers in vinyl chloride polymers. Copolymers containing these monomers are preferred because they improve melt fluidity. The ratio of vinyl chloride to other monomers in the copolymer is preferably 50% by weight or more of vinyl chloride, but 90% by weight or more of vinyl chloride and 50% by weight or more of vinyl chloride and Particularly preferred is a content of 10% by weight or less. Other vinyl chloride polymers may be produced by any method. That is, polymers and copolymers obtained by various polymerization methods such as suspension polymerization, bulk polymerization, and emulsion polymerization can be used. It is desirable that the particle size of the other vinyl chloride polymer is approximately equal to the particle size of the graft polymer to be mixed.
This is because when particles are of equal size, they are easier to mix together. When making a resin mixture by mixing the graft polymer and other vinyl chloride polymers, the following general trends should be taken into account, and the properties specifically required should be expressed. Determine the composition and mixing ratio of the polymer. Generally, as the amount of the copolymer of ethylene and vinyl acetate increases, melt flowability and impact resistance improve, but heat resistance decreases. On the contrary, when the amount of the copolymer of ethylene and vinyl acetate decreases, the opposite trend is shown. Furthermore, when the degree of polymerization of each polymer is low, the melt fluidity improves, but the impact resistance decreases, and conversely, when the degree of polymerization of each polymer is high, the opposite tendency is shown. Based on these trends, the composition is determined appropriately depending on each case. For use with video disc records, 65
Graft polymers polymerized at temperatures above ℃ and the degree of polymerization
300 to 600 vinyl chloride homopolymer or copolymer, and mix these so that the proportion of the copolymer of ethylene and vinyl acetate contained in this resin mixture is 1 to 20% by weight. This is desirable. In order to prepare a composition by blending carbon black into a mixture of the above-mentioned graft polymer and other vinyl chloride polymer, they may be mixed together and kneaded using a common mixer. Carbon black generally has a low bulk density and tends to aggregate, so care must be taken to thoroughly knead it and uniformly disperse it. For example, it is desirable to use a mixer that can provide high shear energy, such as a Henschel mixer. Furthermore, as taught in JP-A-55-158919, it is desirable that the carbon black be made into fine particles of 0.044 mm or less and that these fine particles be added to the polyvinyl chloride resin particles in stages. As mentioned above, there are many types of carbon black, but in any case, carbon black is blended in an amount of 10 to 30% by weight based on the resin mixture. Since the graft polymer is a vinyl chloride resin, it is easily decomposed by heating during molding. Therefore, in order to facilitate the molding process, it is desirable to add various auxiliary agents conventionally added to vinyl chloride resins, such as stabilizers and lubricants. In addition to the auxiliary agent, a small amount of other resin can also be added. For example, resins commonly used to improve the impact resistance of vinyl chloride resins, such as methyl methacrylate-styrene-butadiene copolymer, chlorinated polyethylene, etc., can be added. Furthermore, commonly used resins such as Tellalloy (manufactured by Kanebuchi Kagaku Co., Ltd.) and PN resin (manufactured by Showa Denko Co., Ltd.) can be added to improve heat resistance. The amount of these resins added is 20% by weight or less of the resin mixture, preferably
10% by weight or less. Furthermore, when adding an auxiliary agent, particular attention must be paid to the type and amount of the auxiliary agent. This is because when used as a video disc record, if these adjuvants leached onto the surface of the stamper during use, clear images could no longer be obtained. (Effect of the invention) The composition obtained by uniformly kneading the above-mentioned mixture is
It has conductive properties. Furthermore, although this composition has improved heat resistance compared to vinyl chloride homopolymers or dipolymers, it is easy to mold due to its high melt flowability, and has impact resistance. It has the property of being hard to break due to its high strength. Therefore, this composition can be used in various applications that take advantage of its conductive properties. In particular, this composition is easy to mold, so it can be easily molded into a disk having fine grooves, and it is also excellent in heat resistance and impact resistance, making it suitable for video disc records. Therefore, a video disc record made from this composition can accurately record and reproduce audio and video, and is stable in shape and strong in mechanical strength, making it suitable for practical use. Therefore, we can expect great use in this field. (Example) Next, the details of the present invention will be explained with reference to Examples. Example 1 First, the production of a graft polymer as a raw material will be explained. In a jacketed polymerization reactor equipped with a stirrer and with a pressure resistance of 60 kg/cm ² G and an internal volume of 160 liters, ion-exchanged water, a poval-based dispersant, an organic peroxide-based radical generator, and a combination of ethylene and vinyl acetate were added. After loading the polymer and sealing, remove the remaining air,
Next, vinyl chloride and other monomers were charged and suspension polymerization was carried out to produce a graft polymer. After the polymerization reaction was completed, the remaining monomers were collected and removed, dehydrated and dried, coarse particles were removed using a 28-mesh sieve, and the remaining fine particles were collected to obtain a graft polymer. The composition and degree of polymerization of the graft polymer thus obtained are shown in the table below.
As shown in the table. However, in the table below, EVA represents a copolymer of ethylene and vinyl acetate, VAC represents vinyl acetate content, and MI represents melt index.

【table】

[Table] When carbon black is blended into a mixture of the above graft polymer and other vinyl chloride polymers shown in Table 2 to form a resin composition, the blending ratio is as follows:
It was as shown in Table 3 below.

【table】

[Table] For mixing, the graft polymer and other vinyl chloride polymer were placed in a 10 liter Henschel mixer, carbon black was added while stirring, and the temperature was raised to 50°C to ensure uniform dispersion. Afterwards, add the above stabilizer and lubricant and raise the temperature to 50~50℃.
Mixing was continued for 5 minutes while maintaining the temperature at 60°C. Thereafter, it was cooled and the blended powder was taken out. Next, 150 grams of this blended powder was kneaded using two 8-inch rolls to form a sheet with a thickness of 0.5 mm. Next, this sheet was sandwiched between herotype plates and press-molded to obtain a plate with a thickness of 1 mm and a smooth surface. In addition, we created test pieces for heat resistance measurement by press molding, and used these to measure melt flowability.
Heat resistance, thermal stability, bending strength, impact resistance, electrical conductivity, moisture absorption resistance, etc. were investigated. The test methods for each are as follows. Melt fluidity: After cutting the above sheet into 2mm squares, put it into a Koka type flow tester and check the fluidity under a pressure of 150Kg/cm ² and a temperature of 180℃ using a 1φ x 10mm nozzle. Ta. Heat resistance: Using the plate obtained by the above press forming,
Measured according to the method of ASTM D-648 (load: 18.6 kg). Thermal stability: The above sheet was heated in a gear oven at 170°C and evaluated based on the time until foaming. Impact resistance: Test pieces were prepared by cutting a press plate with a thickness of 1 mm into a rectangle of 2 cm on a side, and evaluated using a DuPont impact tester in the following manner. Striking core 1/2R, striking center flat, weight 300g, falling height 2.5cm, measurement temperature 20°C. Measurements were made on 12 evaluation test pieces and quantified using the following criteria. 0: Not broken. 1: Cracks appear. 2: Cracks but does not scatter. 3: Breaks and scatters. Conductivity: Width 10mm and length 70mm from a 1mm thick press plate
A test piece of mm in diameter was prepared, and after polishing 10 mm of each end of the test piece with sandpaper, a silver paste paint was applied thereto, and the test piece was left in a room at 20°C and 50% RH for 24 hours. Then apply a DC voltage,
Volume resistivity was measured. Moisture absorption resistance: 5mm due to the smooth surface of the pressed plate
Cut out a corner specimen and heat at 50℃, 95%
It was left at RH for 6 hours. The number of abnormal bubbles was then examined using a 40x magnification microscope. The results of examining the above properties are shown in Table 4 below along with the composition of the resin mixture.

[Table] The following can be gleaned from Table 4. That is, from experiment numbers 6 and 8 in Table 4, as the degree of polymerization increases, melt fluidity deteriorates, but impact resistance improves. Moreover, from Experiment Nos. 5 to 7, as the ethylene and vinyl acetate copolymer component in the resin mixture increases, the impact resistance improves, but the heat resistance deteriorates. Furthermore, from Experiment No. 11, when a copolymer containing a large amount of vinyl acetate was used, the impact resistance did not improve very well. Furthermore, when using a copolymer of ethylene and vinyl acetate produced by emulsion polymerization,
It becomes highly hygroscopic. In general, all of these compositions have good electrical conductivity, and can be said to have good properties in terms of melt flowability, heat resistance, and impact resistance. When these compositions were molded into video disc records, they were easy to mold, could accurately record and reproduce audio and video, were stable in shape, had high mechanical strength, and were suitable for practical use. Comparative Example 1 A formulation similar to that of Example 1 was prepared using only the other vinyl chloride polymers shown in Table 2, and the physical properties of the formulation were measured in the same manner. The results are shown in Table 5.

[Table] (Comparison of effects) Comparing Tables 4 and 5, it is found that graft polymerization of vinyl chloride to a copolymer of ethylene and vinyl acetate is more effective than using other vinyl chloride polymers alone. It can be seen that when used in combination with a grafted polymer, the melt fluidity, heat resistance, impact resistance, and thermal stability are superior. In particular, with regard to heat resistance, it is generally said that mixing a graft polymer with a vinyl chloride polymer lowers the heat resistance, but when carbon black is added to this, the content of ethylene-vinyl acetate copolymer increases. On the contrary, as long as the content is within the range of 2 to 10% by weight, the heat resistance is improved. This is completely unexpected. It is unclear why such an unexpected phenomenon occurs. However, when examining the solubility in tetrahydrofuran, the composition with improved heat resistance is poorly soluble, so it is assumed that cross-linking is generated. Specifically, conductive compositions made by adding carbon black to a vinyl chloride polymer alone or a resin composition in which an ethylene-vinyl acetate copolymer is added are easily soluble in tetrahydrofuran. . However, the composition of the present invention, in which a graft polymer is added thereto, is poorly soluble in tetrahydrofuran. Therefore, in certain physical properties, the composition of this invention is not simply a mixture. Incidentally, carbon black was added to a vinyl chloride polymer alone or to a resin composition in which an ethylene-vinyl acetate polymer was added to make a conductive composition, and this was molded into a video disc record, but the molding was difficult. It was difficult, and it was impossible to accurately mold even the smallest grooves. As described above, the composition of the present invention has a good balance between melt fluidity and other physical properties, and therefore, video disc records made with this composition have precisely formed grooves. Because it is conductive, it does not attract dust, has a stable shape, and has strong mechanical strength, so it was recognized as being of high quality and suitable for practical use.

Claims (1)

[Claims] 1. 2 to 60 parts by weight of a copolymer of ethylene and vinyl acetate containing 10 to 65% by weight of a vinyl acetate component,
3 to 90 parts by weight of a graft polymer having an average degree of polymerization of 300 to 700 obtained by graft polymerization of 98 to 40 parts by weight of vinyl chloride, and 97 to 10 parts by weight of another vinyl chloride-based polymer having an average degree of polymerization of 300 to 600. A video disc record is produced by mixing parts by weight to form a resin mixture, adding 5 to 30% by weight of carbon black to this resin mixture to form a conductive resin composition, and molding this composition into a thin disk shape. 2. The video disc record according to claim 1, wherein a graft polymer obtained by polymerization at a temperature of 65 to 90°C is used. 3 2 to 60 parts by weight of a copolymer of ethylene and vinyl acetate containing 10 to 65% by weight of vinyl acetate component,
98 to 40 parts by weight of vinyl chloride and
Average degree of polymerization obtained by graft polymerization with 10% by weight or less of ethylene, propylene or vinyl acetate
A resin mixture is prepared by mixing 3 to 90 parts by weight of a graft polymer of 300 to 700 with 97 to 10 parts by weight of another vinyl chloride polymer having an average degree of polymerization of 300 to 600, and 5 to 30 parts by weight of this resin mixture. % of carbon black to form a conductive resin composition, and this composition is molded into a thin disk shape.