JPS62206783A - Cartridge heater - Google Patents
Cartridge heaterInfo
- Publication number
- JPS62206783A JPS62206783A JP4883786A JP4883786A JPS62206783A JP S62206783 A JPS62206783 A JP S62206783A JP 4883786 A JP4883786 A JP 4883786A JP 4883786 A JP4883786 A JP 4883786A JP S62206783 A JPS62206783 A JP S62206783A
- Authority
- JP
- Japan
- Prior art keywords
- cartridge heater
- core
- electrode wire
- magnesia
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、樹脂成型の金型等の加熱源として使用される
カートリッジヒータに関し、特にアース電極線を有する
カートリッジヒータに関するものである。DETAILED DESCRIPTION OF THE INVENTION Field of the Invention The present invention relates to a cartridge heater used as a heating source for resin molding molds, etc., and particularly to a cartridge heater having a ground electrode wire.
従来の技術
一般にカートリッジヒータは従来より樹脂成型の金型加
熱用など生産設備の加熱源として広く使用されている。2. Description of the Related Art In general, cartridge heaters have been widely used as heating sources in production equipment, such as for heating molds for resin molding.
このような分野における電源電圧は設備のラン二ｙグコ
スト等の理由により、国内では、２ｏｏ■電源が一般に
使用されており、安全性の面から絶縁特性に優れたカー
トリッジヒータが望まれている０
しかし、従来のカートリッジヒータでは、発熱素線を巻
きつけるためにマグネシア焼結体からなるコアを使用し
ているが、このマグネシア焼結体は吸湿性に富むため、
絶縁特性の低下が生じ易い。Due to equipment running costs and other reasons, power supply voltage in such fields is generally 200 mm in Japan, and cartridge heaters with excellent insulation properties are desired from a safety standpoint. However, conventional cartridge heaters use a core made of magnesia sintered body to wrap the heating element wire, but this magnesia sintered body is highly hygroscopic, so
Deterioration of insulation properties is likely to occur.
このため、シーズヒータの場合と同様に、＜１） シ
リコーン樹脂による封止、（２）無機接着剤による封止
、（３）低融点ガラスによる封止などいろいろな対策が
考えられているが、いずれの場合においても一長一短が
あり、より安全性の確保の 面から設備の接地が行
なわれつつある。For this reason, as in the case of sheathed heaters, various countermeasures have been considered, such as <1) sealing with silicone resin, (2) sealing with inorganic adhesive, and (3) sealing with low melting point glass. In either case, there are advantages and disadvantages, and equipment is increasingly being grounded to ensure safety.
しかし、カートリッジヒータを金型等の穴に挿入して使
用する一般的な場合において、熱伝導をよくするために
穴とカートリッジヒータとのクリアランスは、ごくわず
かに設計されている。このため、直接アース端子をカー
トリッジヒータより取り出すことができず、厄介であっ
た。（例えば、特公昭５９−２３０７１号公報）
このため、本発明者らは、すでに金属パイプの片側を封
止する封止金具の中央部に金属ビンを金属パイプの内側
方向に立設させ、かつマグネシア焼結体からなるコアの
中心部に設けた貫通穴に貫通させてアース電極線とする
方法を提案している。However, in the general case where a cartridge heater is inserted into a hole in a mold or the like, the clearance between the hole and the cartridge heater is designed to be very small in order to improve heat conduction. For this reason, it was not possible to directly take out the ground terminal from the cartridge heater, which was troublesome. (For example, Japanese Patent Publication No. 59-23071) For this reason, the present inventors have already installed a metal bottle in the center of the sealing fitting that seals one side of the metal pipe, and A method has been proposed in which a ground electrode wire is formed by passing the wire through a through hole provided in the center of a core made of a magnesia sintered body.
発明が解決しようとする問題点
しかしながら、前述した方法では、アース電極線と電気
取り出し線の絶縁特性が悪く、そのため、金属パイプの
端末部を低融点ガラス等にて封止する必要があり、極め
て厄介なものであった。Problems to be Solved by the Invention However, in the method described above, the insulation properties of the earth electrode wire and the electrical lead-out wire are poor, and therefore the end portion of the metal pipe must be sealed with low melting point glass, etc., which is extremely difficult. It was troublesome.
本発明はこのような問題点を解決するもので、絶縁特性
に優れたアース電極線を有するカートリッジヒータを提
供することを目的とするものである０
問題点を解決するための手段
上記問題点を解決するために本発明は、金属パイプの片
側を封止する封止金具に接続されるアース電極線を有す
るカートリッジヒータにおいて、マグネシア焼結体から
なる各種コアとして、あらかじめシリコーンフェスを含
浸させたものを用いるとともに、前記金属パイプと各種
コアとの隙間に充填される電気絶縁粉末としてシリコー
ン樹脂粉末を添加したマグネシア粉末を用いたものであ
るＯ
作 用
従来よりカートリッジヒータでは、発熱素線を巻き２け
たシ、金属パイプと電気取り出し線および発熱素線との
位置決めのために、マグネシア焼結体からなる各種コア
が使用されておシ、このマグネシア焼結体は吸湿性が著
しい。このため、マグネシア焼結体からなるコアに、ア
ース電極線および電気取り出し線を貫通させる本発明の
構造では、両者間もしくはアース電極線と接続している
金属パイプと電気取り出し線との間の絶縁特性は悪くな
る。The present invention is intended to solve these problems, and aims to provide a cartridge heater having a ground electrode wire with excellent insulation properties. In order to solve the problem, the present invention provides a cartridge heater having a ground electrode wire connected to a sealing fitting that seals one side of a metal pipe, which is pre-impregnated with a silicone face as various cores made of magnesia sintered body. At the same time, magnesia powder to which silicone resin powder has been added is used as electrical insulating powder to be filled in the gaps between the metal pipe and various cores. Various types of cores made of sintered magnesia are used to position the girders, metal pipes, electrical lead-out wires, and heat-generating wires, and this sintered magnesia is highly hygroscopic. For this reason, in the structure of the present invention in which the earth electrode wire and the electrical lead-out line are passed through the core made of magnesia sintered body, the insulation between the two or between the metal pipe connected to the ground electrode wire and the electrical lead-out line is Characteristics become worse.
しかし、本発明では、マグネシア焼結体からなるコアに
、あらかじめシリコーンフェスを含浸させているため、
吸湿することはない。さらに、アース電極線に接続され
ている金属パイプと電気取り出し線との隙間にも、シリ
コーン樹脂粉末を添加したマグネシア粉末を電気絶縁粉
末として使用しているため、吸湿性の心配はない。However, in the present invention, since the core made of magnesia sintered body is impregnated with silicone face in advance,
It does not absorb moisture. Furthermore, since magnesia powder to which silicone resin powder is added is used as electrical insulating powder in the gap between the metal pipe connected to the ground electrode wire and the electrical lead-out wire, there is no need to worry about hygroscopicity.
このような理由により、金属パイプの端末部を低融点ガ
ラス等にて封止する必要がなくなるとともに、絶縁特性
に優れたアース電極線を有するカートリッジヒータを得
ることが可能となる。For these reasons, there is no need to seal the end portion of the metal pipe with low-melting glass or the like, and it is possible to obtain a cartridge heater having a ground electrode wire with excellent insulation properties.
なお、マグネシア焼結体からなるコアへのシリコーンフ
ェスの含浸け、アセトン、トルエン、キシレン等の有機
溶剤に、シリコーンフェス（例えば、信越化学工業■製
のＫＲ２２０等）を溶解させた溶液を準備し、これに前
記コアを浸漬した後、取り出し、熱風乾燥させることに
より、容易に行なうことができる。In addition, impregnating a core made of magnesia sintered body with a silicone face, and preparing a solution in which a silicone face (for example, KR220, manufactured by Shin-Etsu Chemical Co., Ltd.) is dissolved in an organic solvent such as acetone, toluene, or xylene. This can be easily done by immersing the core in this, taking it out, and drying it with hot air.
実施例
以下、本発明の具体的な実施例を第１図〜第４図にもと
づいて説明する。EXAMPLES Hereinafter, specific examples of the present invention will be described based on FIGS. 1 to 4.
まず、第２図に示すように、電気取り出し線１およびア
ース電極線２を貫通させる穴ｓａ、ｓｂ。First, as shown in FIG. 2, holes sa and sb are made through which the electrical outlet wire 1 and the ground electrode wire 2 are passed.
３Ｃをそれぞれ設けたマグネシア焼結体からなるコア３
を準備した。Core 3 made of magnesia sintered body each provided with 3C
prepared.
一方、信越化学工業■製シリコーンフェス（商品名ＫＲ
２２０）をアセトンに溶解させたシリコーンフェス溶液
を準備し、この溶液中に上記コア３を浸漬した。そして
数分後、コア３を取り出し、熱風乾燥炉によりアセトン
を蒸発させ、シリコーンフェスのみ含浸させたコア３を
準備した。On the other hand, silicone face made by Shin-Etsu Chemical Co., Ltd. (product name: KR)
A silicone face solution was prepared by dissolving 220) in acetone, and the core 3 was immersed in this solution. After a few minutes, the core 3 was taken out and the acetone was evaporated in a hot air drying oven to prepare a core 3 impregnated with only the silicone face.
このコア３に、発熱素線４を巻きつけるとともに、電気
取り出し線１を穴３ａ、３ｂに貫通させた。A heating element wire 4 was wound around this core 3, and the electrical lead-out wire 1 was passed through the holes 3a and 3b.
一方、封止金具５の中央に、アース電極線２をスポット
溶接し、そして第３図に示すアース電極線２、付き封止
金具６を準備し、これを金属バイブロの片側にアーク溶
接により溶接し、金属バイブロの片側を封止した。On the other hand, the earth electrode wire 2 is spot welded to the center of the sealing metal fitting 5, and the earth electrode wire 2 and the sealing metal fitting 6 shown in FIG. 3 are prepared, and this is welded to one side of the metal vibro by arc welding. Then, one side of the metal vibro was sealed.
なお、この時、アース電極線２は金属バイブロの内側に
くるようにした。At this time, the ground electrode wire 2 was placed inside the metal vibro.
この後、あらかじめ発熱素線４等を装備して準備したコ
ア３を、第４図に示すマグネシア焼結体からなる先端コ
ア７を介して、第１図に示すように金属バイブロの中央
部に位置させた。この時、アース電極線２は、コア３の
中央に設けられた穴３Ｃおよび先端コア７の中央に設け
られた穴７ａに貫通させた。After this, the core 3, which has been prepared in advance with the heat generating wire 4 etc., is inserted into the center of the metal vibro as shown in Fig. 1 via the tip core 7 made of magnesia sintered body shown in Fig. 4. positioned. At this time, the ground electrode wire 2 was passed through the hole 3C provided in the center of the core 3 and the hole 7a provided in the center of the tip core 7.
このようにして、金属バイブロの中央部にコア３を挿入
した後、シリコーン樹脂粉末を添加したマグネシア粉末
からなる電気絶縁粉末８を金属バイブロとコア３の隙間
に充填し、そして圧延減径した。この後、熱処理し、電
気絶縁粉末８およびシリコーンフェスを含浸したコア３
の撥水化処理を行なうことにより、本発明のカートリッ
ジヒータを完成した。After inserting the core 3 into the center of the metal vibro in this manner, the gap between the metal vibro and the core 3 was filled with electrical insulating powder 8 made of magnesia powder to which silicone resin powder was added, and the diameter was reduced by rolling. After this, the core 3 is heat treated and impregnated with electrical insulation powder 8 and silicone face.
The cartridge heater of the present invention was completed by carrying out water repellent treatment.
このようにして完成した本発明のカートリッジヒータを
評価するために、耐湿雰囲気中（４０″Ｃ９相対湿度９
６％）に２週間投入した０そして２週間投入した後、ア
ース電極線２もしくは金属バイブロと電気取り出し線１
との絶縁抵抗を測定したところ、その絶縁抵抗は２０ｏ
ＯＭＱ 以上あり優れた電気特性を示した。In order to evaluate the cartridge heater of the present invention completed in this way, we conducted a test in a humidity-resistant atmosphere (40" C9 relative humidity 9
6%) for 2 weeks, and after 2 weeks, earth electrode wire 2 or metal vibro and electrical outlet wire 1
When the insulation resistance was measured, the insulation resistance was 20o
OMQ or higher, indicating excellent electrical properties.
このように、本発明のカートリッジヒータにおいては、
優れた絶縁特性を示すとともに、金属バイブロの外周へ
突出することなくアース電極線２を形成しているため、
カートリッジヒータ全体を金型等の穴に挿入して使用す
る場合、その挿入が支障なく行なえ、その結果、アース
回路の形成が確実になり、電気的に安全性が向上する。In this way, in the cartridge heater of the present invention,
In addition to exhibiting excellent insulation properties, the ground electrode wire 2 is formed without protruding to the outer periphery of the metal vibro.
When the entire cartridge heater is used by being inserted into a hole in a mold or the like, the insertion can be performed without any problem, and as a result, the formation of a ground circuit is ensured, and electrical safety is improved.
発明の効果
以上の説明から明らかなように本発明によれば、金属パ
イプの片側を封止する封止金具に接続されるアース電極
線を有するカートリッジヒータにおいて、マグネシア焼
結体からなる各種コアとして、あらかじめシリコーンフ
ェスを含浸させたものを用いるとともに、前記金属パイ
プと各種コアとの隙間に充填される電気絶縁粉末として
シリコーン樹脂粉末を添加したマグネシア粉末を用いて
いるだめ、絶縁特性に優れたアース電極線を有するカー
トリッジヒータを提供することが可能となるものである
。Effects of the Invention As is clear from the above description, according to the present invention, in a cartridge heater having a ground electrode wire connected to a sealing fitting that seals one side of a metal pipe, various types of cores made of magnesia sintered body can be used. In addition to using a silicone face impregnated in advance, magnesia powder to which silicone resin powder is added is used as electrical insulation powder to be filled in the gaps between the metal pipe and various cores, making it a ground with excellent insulation properties. This makes it possible to provide a cartridge heater having electrode wires.
第１図は本発明の一実施例を示すカートリッジヒータの
断面図、第２図は同カートリッジヒータで使用するコア
の斜視図、第３図は同カートリッジヒータで使用するア
ース電極線と封止金具の接続状態を示す斜視図、第４図
は同カー） ＩＪツジヒータで使用する先端コアの斜視
図である。
２・・・・・・アース電極線、３・・・・・・コア、５
・・・・・・封止金具、６・・・・・・金属パイプ、８
・・・・・・電気絶縁粉末。
代理人の氏名 弁理士 中 尾 敏 男 ほか１名２−
−−アースを才亙壕 ５−一一封上金具第２図
３−コア、３
第４図Fig. 1 is a sectional view of a cartridge heater showing an embodiment of the present invention, Fig. 2 is a perspective view of a core used in the cartridge heater, and Fig. 3 is a ground electrode wire and sealing metal fitting used in the cartridge heater. FIG. 4 is a perspective view of the tip core used in the IJ Tsuji heater. 2... Earth electrode wire, 3... Core, 5
... Sealing fitting, 6 ... Metal pipe, 8
・・・・・・Electrical insulation powder. Name of agent: Patent attorney Toshio Nakao and 1 other person2-
---Earth 5-11 upper metal fittings Figure 2
3-Core, 3 Figure 4
Claims (1)
ス電極線を有するカートリッジヒータにおいて、マグネ
シア焼結体からなる各種コアとして、あらかじめシリコ
ーンワニスを含浸させたものを用いるとともに、前記金
属パイプと各種コアとの隙間に充填される電気絶縁粉末
としてシリコーン樹脂粉末を添加したマグネシア粉末を
用いたことを特徴とするカートリッジヒータ。In a cartridge heater having a ground electrode wire connected to a sealing fitting that seals one side of a metal pipe, various types of cores made of magnesia sintered body impregnated with silicone varnish are used, and the metal pipe and A cartridge heater characterized in that magnesia powder to which silicone resin powder is added is used as an electrically insulating powder that is filled into gaps between various cores.