JPS6197496A - Moisture-proof paper - Google Patents
Moisture-proof paperInfo
- Publication number
- JPS6197496A JPS6197496A JP21479084A JP21479084A JPS6197496A JP S6197496 A JPS6197496 A JP S6197496A JP 21479084 A JP21479084 A JP 21479084A JP 21479084 A JP21479084 A JP 21479084A JP S6197496 A JPS6197496 A JP S6197496A
- Authority
- JP
- Japan
- Prior art keywords
- component
- paper
- moisture
- weight
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、包装紙、紙器等に使用する防湿紙に関するも
のである。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention relates to moisture-proof paper used for wrapping paper, paper containers, etc.
従来の技術
従来より、包装紙、紙器などに、各種の防湿加工紙が使
用されている。その代表的な例としては、ターポリン紙
、ワックス加工紙、各種プラスチック加工紙等が挙げら
れる。BACKGROUND OF THE INVENTION Conventionally, various moisture-proof treated papers have been used for wrapping paper, paper containers, etc. Typical examples thereof include tarpaulin paper, wax-processed paper, and various plastic-processed papers.
発明が解決しＪ：うとする問題点
しかしながらこれらの防湿紙は、それぞれ多くの問題点
を有ｌノでいる。前記ターポリン紙は、各種の紙にアス
ファルトを塗二［シたものであり、防湿性に優れ、安価
ではあるが、アスファル１〜を使用しているために衛生
上問題があり、食品の包装等の用途には不向きである。Problems that the invention attempts to solve However, each of these moisture-proof papers has a number of problems. The above-mentioned tarpaulin paper is made by coating various types of paper with asphalt, and although it has excellent moisture resistance and is inexpensive, it has hygienic problems because it uses asphalt, and is used for food packaging, etc. It is unsuitable for this purpose.
また１ノックス加工紙は、パラフィンワックス浸漬、カ
ーテンコーティング法等の方法により製造され、また近
」、ワックスエマルジョンと合成樹脂エマルジョンの混
合塗工による製造も行われている。しかしながらこれら
のワックス加工紙は、防湿性が良好である反面、加工性
が悪く、また印刷適性や貼合性に問題がある。In addition, 1-Knox processed paper is manufactured by methods such as paraffin wax dipping and curtain coating, and in recent years, it has also been manufactured by mixed coating of wax emulsion and synthetic resin emulsion. However, although these wax-treated papers have good moisture resistance, they have poor processability and also have problems in printability and lamination properties.
またプラスチック加工紙においては、例えばポリ塩化ビ
ニリデン加工紙では、塗工量を多くしな（〕れば充分な
防湿性が得られにくく、ロス１−高になる。またポリ玉
チレンラミネート紙は、ポリニチレンシートにピンホー
ルが発生するため、予想外に防水、防湿性が悪い。In addition, in the case of plastic-processed paper, for example, with polyvinylidene chloride-processed paper, it is difficult to obtain sufficient moisture resistance unless the coating amount is increased, resulting in a loss of 1-high. Because pinholes occur in the polynylene sheet, the waterproof and moisture-proof properties are unexpectedly poor.
本発明はかかる事情に鑑みなされたものであって、防湿
性に優れ、安価で衛生的であり、且つ印刷特性や貼合性
に優れた新規な防湿紙を提供することを目的とするもの
で゛ある。The present invention was made in view of the above circumstances, and it is an object of the present invention to provide a novel moisture-proof paper that has excellent moisture-proof properties, is inexpensive, hygienic, and has excellent printing characteristics and lamination properties. There is.
問題点を解決する手段
而して本発明は、紙及び／又は板紙をホットメルト接着
剤で貼り合わせた、サンドインチ状の構造を有するもの
である。そしてそのホットヌル１〜接着剤として、スチ
レンブタン１ンブロツク共重合体、スチレンイソプレン
ブロック共重合体及びアタクチックポリプロピレンから
なる群より選ばれた、一種又は二種以」−の重合体より
なる第一成分５〜５０重量％と、ワックス類よりなる第
二成分９５〜３０重量％と、前記第一成分以外の天然樹
脂又は合成樹脂Ｊ：りなる第三成分０〜６５重量％とを
溶融混合してなる組成物を使用するものである。As a means of solving the problem, the present invention has a sandwich-like structure in which paper and/or paperboard are bonded together with a hot melt adhesive. The hot null 1 to adhesive is a first component consisting of one or more polymers selected from the group consisting of styrene-butane block copolymer, styrene isoprene block copolymer, and atactic polypropylene. 5 to 50% by weight of a second component consisting of waxes, 95 to 30% by weight of a second component consisting of waxes, and 0 to 65% of a third component consisting of a natural resin or synthetic resin other than the first component. The following composition is used.
本発明において使用するホットメルト接着剤は、前述の
Ｊ−う（こ第一成分ど第二成力どよりなり、イれ（こ所
望により第三成分を添加することしあるものである。The hot melt adhesive used in the present invention is composed of the above-mentioned first component, second component, etc., and a third component may be added if desired.
第一成分は、スチレンブタジエンブロック共重合体、ス
チレンイソプレンブ［コック共重合体又はアククチツク
ポリプロピレンを、中独で、又は二種以１を混合して使
用する。The first component is a styrene-butadiene block copolymer, a styrene-isoprene block copolymer, or an acidic polypropylene, either alone or in combination.
スブレンゾタジエンブロック共重合体及びスチレンイソ
プレンブロック共重合体は、それぞれ、ポリスヂレンー
ボリブタジＴンーボリスチレン及びポリスヂレンーボリ
イソブレンーボリスチレンのグロツタ共重合の構造を右
するゴム状樹脂である。而してポリスチレンブロックは
分子量が約５０００〜１２５０００稈度であり、さらに
好ましくは約８０００〜Ｉ′１５０００程度が適当であ
る。The sobrenzotadiene block copolymer and the styrene isoprene block copolymer represent the structures of polystyrene-bolybutadiene-boristyrene and polystyrene-bolyisoprene-boristyrene copolymers, respectively. It is a rubbery resin. The polystyrene block has a molecular weight of about 5,000 to 125,000, more preferably about 8,000 to I'15,000.
またポリブタジエン及びポリイソプレンブロックは、分
子量か１５０００〜２５００００Ｐｉ！麿であり、さら
に好ましくは約３５０００〜１５００００が適当である
。Moreover, the molecular weight of polybutadiene and polyisoprene blocks is 15,000 to 250,000 Pi! It is about 35,000 to 150,000, more preferably about 35,000 to 150,000.
またアククチツクポリプロピレンは、アイソタクチツク
ポリプロピレンの副生物として得られるものであって、
結晶構造をほとんど有しておらず、極めて柔軟である。In addition, active polypropylene is obtained as a by-product of isotactic polypropylene, and
It has almost no crystal structure and is extremely flexible.
このアタクチックポリプロピレンの分子量は、８０００
〜８００００程度のものが適当である。The molecular weight of this atactic polypropylene is 8000
~80,000 is appropriate.
次に、第二成分として使用されるワックス類としては、
パラフィンワックス、マイクロクリスタリンワックス、
低分子量ポリエチレンワックス等の、天然又は合成のワ
ックスが使用される。特に１２５〜１５５ のパラフィ
ンワックスが最も適している。Next, the waxes used as the second component are:
paraffin wax, microcrystalline wax,
Natural or synthetic waxes are used, such as low molecular weight polyethylene waxes. In particular, paraffin wax having a molecular weight of 125 to 155 is most suitable.
本発明においては、所望により第三成分を添加すること
ができる。第三成分としては、前記第一成分以外の天然
樹脂又は合成樹脂であって、脂肪族系若しくは芳香族系
の炭化水素樹脂、テルペン樹脂、ロジンエステル、変性
ロジンエステル等が挙げられる。In the present invention, a third component can be added if desired. Examples of the third component include natural resins or synthetic resins other than the first component, such as aliphatic or aromatic hydrocarbon resins, terpene resins, rosin esters, and modified rosin esters.
これらの第一、第二及び第三の成分の比率は、第一成分
５〜５０重石％、第二成分９５〜３０重量％、第三成分
０−６５１１％とするのが良い。The ratio of these first, second and third components is preferably 5 to 50% by weight for the first component, 95 to 30% by weight for the second component, and 0 to 6511% for the third component.
第一成分と第ニー成分との比率では、第二成分の比率を
、少なくとも第一成分の比率と同等乃至それ以」どすべ
きである。そして第三成分は、所望により６５重量％以
下の範囲内で使用することかできる。Regarding the ratio of the first component to the second component, the ratio of the second component should be at least equal to or higher than the ratio of the first component. The third component can be used in an amount of 65% by weight or less, if desired.
なお本発明において使用するホラ１ヘメルｉ−接着剤に
は、第一、第二及び第三成分の他に、必要に応じて、熔
融時の接着剤の酸化を防止するための酸化防止剤、泡の
発生を防止する消泡剤等の他の付加的な成分を加えるこ
とができることは言うまでもない。In addition to the first, second and third components, the Hora 1 Hemel i-adhesive used in the present invention may optionally contain an antioxidant to prevent oxidation of the adhesive during melting. It goes without saying that other additional ingredients can be added, such as antifoaming agents to prevent the formation of foam.
作用
本発明においては、ワックス類を主成分とする前記ホラ
１−メル１へ接着剤を使用して紙及び／又は板紙を貼り
合わせているので、接着剤が紙又は板紙質内に含浸し、
防湿性を付与するのである。また本発明によれば、小ツ
１−メルｌ〜接着剤の主成分としＣの第二成分であるワ
ックス類に、軟質の第一成分を添加しているので、ホラ
１−メル１−接着剤としで極めて柔軟であって、特に防
湿紙を折り曲げた際の防湿性の低下が小さく、加工性が
良好である。Function In the present invention, since paper and/or paperboard are bonded to the Hola 1-Mel 1, which is mainly composed of waxes, using an adhesive, the adhesive impregnates the paper or paperboard.
It provides moisture resistance. Further, according to the present invention, since a soft first component is added to the waxes which are the main component of the adhesive and the second component of C, It is extremely flexible as an agent, and has good processability, with little deterioration in moisture resistance, especially when the moisture-proof paper is folded.
さらに第一成分、第二成分及び第三成分の種類及び混合
比を変化させることににす、高温及び低温時の流動↑４
や、軟化点を変化さｌることが可能である。Furthermore, we decided to change the type and mixing ratio of the first component, second component, and third component, and the flow at high and low temperatures ↑4
It is also possible to change the softening point.
発明の効果
本発明にｊ：れば、防湿性に優れ、包装紙や紙器用の防
湿紙として優れている。またこの防湿紙はアスファルト
等を使用しないので衛生的であり、食品用包装紙として
使用可能であり、また表面にはワックス等が何着してい
ないので、印刷適性や貼合性に優れたちのどなる。Effects of the Invention The present invention has excellent moisture resistance and is excellent as a moisture-proof paper for wrapping paper and paper containers. In addition, this moisture-proof paper is hygienic because it does not use asphalt, etc., and can be used as food wrapping paper.Also, since the surface is not coated with wax, it has excellent printability and pasting properties. Become.
さらに本発明では、接着剤の配合が柔軟なものであるの
で、防湿紙としても柔軟であり、折曲げ等により防湿性
が低下することがなく、取扱いが容易である。Furthermore, in the present invention, since the adhesive composition is flexible, the paper is also flexible as a moisture-proof paper, and its moisture-proof properties do not deteriorate due to bending or the like, making it easy to handle.
実施例 以下本発明の実施例について説明する。Example Examples of the present invention will be described below.
実施例１
− ７ ＝
第一成分°スチレンイソプレンブ
「１ツク」を手合体くシェル化学株
式会社製 商品名カリフレック
ス丁Ｒ１１１１） ２０重量％第二成
分： １４０ パラフィンワ
ックス ５０重量％第己成分：
アルペン樹脂（安原油
脂株式会ネ１製 商品名ＹＳレジ
ンＰｘ＃１１００） ３０重量％実施例２
第一成分：スヂレンイソプレンブ
ロック共重合体（シェル化学株
代金社製 商品名カリフレック
スＴＲ１１０７） ２０重量％第７二
成分：１４０ パラフィンワ
ックス ８０重量％実施例３
第一成分：スブレンブタジエンブ
１］ツク共千合体くシェル化学株
式会ネ１製 商品名フノリルック
スＴＲ１１１６） ２０重量％第二成分
：１４０ パラフィンワ
ックス ６０重量％第三成分：
ロジングリセリンエス
チル（播磨化成工業株式会社製
商品名バリスターＤＳ−９０） ２０重量％実施例４
第一成分：アタクチックポリプロ
ピレン（分子量２００００） ３０重量％第二成分
：１７ＩＯパラフィンワ
ックス ５０重量％第三成分：
テルペン樹脂（前掲） ２０重量％以上の各配合により
、各成分を溶融混合し、脱泡してホットメルト接着剤を
得た。得られた各接着剤を使用して、７４’Ｊ’ｍ’の
両更りラフ］〜紙を接着して防湿紙を得た。接着剤塗布
量は、２０Ｖｒｎ’とした。Example 1-7 = First component: Hand combine 1 piece of styrene isoprene (manufactured by Shell Chemical Co., Ltd., trade name: CARIFLEX® R1111) 20% by weight Second component: 140 Paraffin wax 50% by weight First component:
Alpine resin (trade name: YS Resin Px #1100, manufactured by Yasushi Oil Co., Ltd.) 30% by weight Example 2 First component: Styrene isoprene block copolymer (trade name: Cauliflex TR1107, manufactured by Shell Kagaku Kaisha, Ltd.) 20 Weight% 7th 2nd component: 140 Paraffin wax 80% by weight Example 3 1st component: Soblen butadiene 1] Tsukukyosengoitai Shell Kagaku Co., Ltd. (Product name: Funorilux TR1116) 20% by weight 2nd component :140 Paraffin wax 60% by weight Third component:
Rosin glycerin ester (product name Varistor DS-90 manufactured by Harima Kasei Kogyo Co., Ltd.) 20% by weight Example 4 First component: Atactic polypropylene (molecular weight 20,000) 30% by weight Second component: 17IO paraffin wax 50% by weight Three components:
Terpene resin (mentioned above) Each component was melt-mixed in a proportion of 20% by weight or more and defoamed to obtain a hot-melt adhesive. Using each of the obtained adhesives, 74'J'm' double-sided rough paper was adhered to obtain moisture-proof paper. The amount of adhesive applied was 20 Vrn'.
そしてこの各防湿紙について、その透湿度をＪＩｓ−Ｚ
−０２０８に基いて測定した。The moisture permeability of each moisture-proof paper is determined by JIs-Z.
-0208.
その測定の結果は、表の通りであった。The results of the measurement were as shown in the table.
−１０＝−10=
Claims (1)
ソプレンブロック共重合体及びアタクチックポリプロピ
レンからなる群より選ばれた一種又は二種以上の重合体
よりなる第一成分５〜５０重量％と、ワックス類よりな
る第二成分９５〜３０重量％と、前記第一成分以外の天
然樹脂又は合成樹脂よりなる第三成分０〜６５重量％と
からなるホットメルト接着剤で、紙及び／又は板紙を貼
り合わせたことを特徴とする、防湿紙1 A first component consisting of 5 to 50% by weight of one or more polymers selected from the group consisting of styrene-butadiene block copolymer, styrene isoprene block copolymer and atactic polypropylene, and a second component consisting of waxes. Bonding paper and/or paperboard with a hot melt adhesive consisting of 95 to 30% by weight of two components and 0 to 65% by weight of a third component made of a natural resin or synthetic resin other than the first component. Features: Moisture-proof paper