JPS6111182A - Manufacture of colored resinous molded article having metallic luster - Google Patents
Manufacture of colored resinous molded article having metallic lusterInfo
- Publication number
- JPS6111182A JPS6111182A JP13201684A JP13201684A JPS6111182A JP S6111182 A JPS6111182 A JP S6111182A JP 13201684 A JP13201684 A JP 13201684A JP 13201684 A JP13201684 A JP 13201684A JP S6111182 A JPS6111182 A JP S6111182A
- Authority
- JP
- Japan
- Prior art keywords
- metallic luster
- molded article
- paint
- colored
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、金属光沢を有する着色された樹脂成形品の製
造方法に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to a method for producing a colored resin molded article having metallic luster.
従来%着色された樹脂成形品を製造する方法としては、
樹脂原料そのものに顔料等を加え着色したもの全成形す
る方法、あるいは樹脂成形品に着色された塗料を塗工す
る方法があり、またメッキ処理あるいはスパッタリング
等の光輝処理も行われている。Conventionally, the method of manufacturing colored resin molded products is as follows:
There are two methods: one is to add pigments etc. to the resin raw material itself and then mold the entire product, or one is to apply a colored paint to the resin molded product.Also, brightening treatments such as plating or sputtering are also performed.
一方金属光沢を有する樹脂成形品を得る方法としては、
i料樹脂中にメタリック顔料を混入する方法、あるいは
樹脂成形品にメタリック色の塗料を塗工する方法、ある
いは該塗料を塗工した上に更に透明な塗料を塗工する方
法等があるが、樹脂原料中にメタリック顔料を混入する
場合、成形時に流れ模様が出来る場合が多く、かつ顔料
を多量に用いなければならないという欠点があり、しか
も側斜の物性面においてもろくなるという欠点もある。On the other hand, as a method for obtaining resin molded products with metallic luster,
There are methods such as mixing a metallic pigment into the i-based resin, coating a resin molded product with a metallic paint, or coating the paint with a transparent paint, etc. When a metallic pigment is mixed into a resin raw material, there are disadvantages in that flow patterns are often formed during molding, a large amount of pigment must be used, and the physical properties of the side slopes are brittle.
一方メタリック顔料を含有する塗料を塗工する場合、1
コートの場合外観が悪くかつ耐久性において劣p1また
メタリック顔料を含有する塗料を塗工した後更に透明な
塗料全塗工する場合2回塗工する必要があり、作業工数
、材料費のアップ等の欠点がある。また着色された金属
光沢含有する塗料を用いる場合、顔料等高濃度のものを
用いる必要があり1色、外観のバラツキが大となるばか
りでなく、各色別の塗料全準備しておかなければならな
いという欠点がある。On the other hand, when applying paint containing metallic pigments, 1
In the case of a coat, the appearance is poor and the durability is poor.Also, if you apply a paint containing metallic pigment and then apply a complete coat of transparent paint, it is necessary to apply two coats, which increases work man-hours and material costs. There are drawbacks. Furthermore, when using paints containing colored metallic luster, it is necessary to use highly concentrated pigments, which not only results in large variations in appearance per color, but also requires preparation of all paints for each color. There is a drawback.
不発明は1着色された樹脂成形品に、少量の金属光沢を
有する顔料を混合した透明度の高い塗料を塗工すること
を特徴とする金属光沢を有する着色された樹脂成形品を
製造する方法である。The non-invention is (1) a method for producing a colored resin molded article with a metallic luster, which is characterized by coating the colored resin molded article with a highly transparent paint containing a small amount of a pigment with a metallic luster. be.
本発明者は前記従来技術の欠点を解消するため種々検討
を行った結果本発明をなすに到った。The present inventor conducted various studies in order to eliminate the drawbacks of the above-mentioned prior art, and as a result, the present invention was completed.
即ち1着色顔料等を混入、することによシ清色した樹脂
を用いて成形した成形品に、塗膜の表面から成形品本体
の色が見える程度の少量の金属光沢を有する顔料を混入
した透明度の高い塗料を塗工することにより、金属光沢
を有する着色製品を得ることができることを見出だした
。In other words, a small amount of pigment with a metallic luster is mixed into a molded product molded using a resin that has been made clear by mixing a colored pigment, etc., to the extent that the color of the molded product itself can be seen from the surface of the coating film. It has been discovered that a colored product with metallic luster can be obtained by coating with a highly transparent paint.
樹脂成形品成形用樹脂原料に混入する顔料としては通常
用いられている顔料の中から必要な色の顔料を選んで混
入すればよい。また樹脂成形品の変褪色あるいは樹脂の
劣化を防ぐ為1通常、光安定剤等も混入されているが1
本発明の場合、風雨、湿度、結露した水分等による直接
の影響がないので無塗工の場合に比し少量混入すれば足
りる。また、樹脂成形品には希望する外観に応じてシボ
會つけてもよく、また、成形品表面をサンドブラスト処
理或いは溶剤処理により処理する場合、輝度等の異った
金属光沢面を得ることができ、また文字等凹凸模様に形
成した後本発明の塗料を塗工する場合、立体感が強調さ
れ文字をエフくっきりと浮び上がらせることができる。As the pigment to be mixed into the resin raw material for molding a resin molded article, a pigment of a required color may be selected from among commonly used pigments and mixed therein. In addition, to prevent discoloration of resin molded products or deterioration of the resin, light stabilizers are usually mixed in.
In the case of the present invention, since there is no direct influence from wind and rain, humidity, condensed moisture, etc., it is sufficient to mix in a smaller amount than in the case of no coating. Additionally, resin molded products may be textured depending on the desired appearance, and when the surface of the molded product is treated with sandblasting or solvent treatment, a metallic luster surface with different brightness can be obtained. Furthermore, when the paint of the present invention is applied after forming letters in a concavo-convex pattern, the three-dimensional effect is emphasized and the letters can stand out clearly.
なお、樹脂としてはポリオレフィンの外ポリアセタール
、ポリカーボネート、ナイロン等測れをも使用すること
ができる。In addition, as the resin, in addition to polyolefin, polyacetal, polycarbonate, nylon, etc. can also be used.
本発明で使用する塗料としては、透明度が高く且つ耐光
性に富み、適用する樹脂の柔軟性に追従できるものてあ
れば、ウレタン系、アクリル系のもの等測れをも使用し
うるが、アクリル系の塗料が好ましい。The paint used in the present invention may be urethane-based, acrylic-based, etc., as long as it has high transparency, high light resistance, and can follow the flexibility of the resin to be applied, but acrylic-based Paints are preferred.
塗料へ混入する金属光沢を有する顔料としては、平均粒
径10μ以下の粒度を有するアルミ粉末等何れを用いて
もよく、混入量は塗料の固形物重量を基にして0.00
1〜0.3重量%の範囲内で混入するのが好ましい。0
.001%以下の場合には十分な金属光沢が得られず、
また、0.3%以上混入すると整形品の色が見えなくな
るばかりでなく、塗膜の耐久性が低下するので好ましく
ない。As the pigment with metallic luster to be mixed into the paint, any aluminum powder having an average particle size of 10 μm or less may be used, and the amount mixed is 0.00 μm based on the solid weight of the paint.
It is preferable to mix within the range of 1 to 0.3% by weight. 0
.. If it is less than 0.001%, sufficient metallic luster cannot be obtained,
Moreover, if it is mixed in at a rate of 0.3% or more, not only the color of the shaped article becomes invisible, but also the durability of the coating film decreases, which is not preferable.
樹脂成形品への塗料の塗工方法としては、スプレー法、
刷毛塗り、ディピング法、クォーター等測れの方法を用
いてもよいが、塗料の付着性を良好にするため、樹脂成
形品を予めプラズマ処理等前処理金施すのが好ましい。Methods for applying paint to resin molded products include spraying,
Brush coating, dipping, quartering, and other methods may be used, but in order to improve the adhesion of the paint, it is preferable to pre-treat the resin molded product in advance, such as plasma treatment.
実施例
ボリグロピレン(三菱油化製 IF−15OA)製放形
体(A:シボ有1着色・ダークグレー。Example: Released body made of polyglopyrene (IF-15OA manufactured by Mitsubishi Yuka) (A: 1 color with grain, dark gray.
B:シボ無し1着色・クリーム色)を下記条件下でプラ
ズマ処理した後日本ビーケミカル社製R−266クリヤ
ー塗料に、その固形分に対し0.25重重量のアルξ粉
末(板状:平均粒径約5μm)k混入し、約35μmの
膜厚に塗工し、90℃で40分焼付けを行った。成形体
Aについては、シボ感が5き出したダークグレーの金属
光沢を有する製品が得られ、また成形体Bについてはク
リーム色で金属光沢のある製品が得られた。B: No grain (1 color, cream color) was plasma treated under the following conditions, and then added to R-266 clear paint manufactured by Nippon B Chemical Co., Ltd., with 0.25 weight of Al ξ powder (plate shape: average It was coated to a film thickness of about 35 μm and baked at 90° C. for 40 minutes. For the molded body A, a dark gray product with a grainy appearance and a metallic luster was obtained, and for the molded body B, a cream-colored product with a metallic luster was obtained.
プラズマ処理条件
装置: BRANSON IPC社製3005−110
203TQA AUTOMATICPLASMA SY
STICM高周波: 13.56 MH2,出カニ 2
0ON反応ガス二〇□
処理室内反応ガス圧カニ 1.OTorr処理時間=3
0秒
〔発明の効果〕
(1) 同一の塗料で成形品の色に応じた今までにな
い外観の金属光沢を有する樹脂成形品を得ることが出来
る。Plasma processing condition equipment: BRANSON IPC 3005-110
203TQA AUTOMATIC PLASMA SY
STICM high frequency: 13.56 MH2, out crab 2
0ON reaction gas 20□ Reaction gas pressure crab in processing chamber 1. OTorr processing time = 3
0 seconds [Effects of the invention] (1) With the same paint, it is possible to obtain a resin molded product with an unprecedented appearance of metallic luster that corresponds to the color of the molded product.
(2) 塗料に混入する顔料が少ないので、塗膜の付
着力が強(、従って長期に亘って耐久性を有する塗膜を
得ることができる。(2) Since there is less pigment mixed into the paint, the adhesion of the paint film is strong (therefore, a paint film with long-term durability can be obtained).
Claims (1)
を混合した透明度の高い塗料を塗工することを特徴とす
る金属光沢を有する着色された樹脂成形品の製造方法。A method for producing a colored resin molded article having a metallic luster, which comprises coating the colored resin molded article with a highly transparent paint containing a small amount of a pigment having a metallic luster.