JPS6063109A - Manufacture of cured body - Google Patents
Manufacture of cured bodyInfo
- Publication number
- JPS6063109A JPS6063109A JP15561684A JP15561684A JPS6063109A JP S6063109 A JPS6063109 A JP S6063109A JP 15561684 A JP15561684 A JP 15561684A JP 15561684 A JP15561684 A JP 15561684A JP S6063109 A JPS6063109 A JP S6063109A
- Authority
- JP
- Japan
- Prior art keywords
- release agent
- raw material
- hydraulic inorganic
- mixed
- mold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
この発明は、シリコン樹脂等の剥離剤適量を混合した水
硬性無機質系硬化原料を底型枠上に薄く展拡し、その上
に剥離剤を混合していない水硬性無機質系硬化原料を設
け、硬化後離型してなることを特徴とする、水硬性無機
質系硬化体の製造法に関する。Detailed Description of the Invention This invention involves spreading a thin layer of hydraulic inorganic curing raw material mixed with an appropriate amount of a release agent such as silicone resin on a bottom mold, and then applying a hydraulic inorganic hardening material containing no release agent mixed thereon. The present invention relates to a method for producing a hydraulic inorganic cured product, which comprises providing an inorganic cured raw material and releasing the mold after curing.
以下この発明の実施例を添付図面を参照して説明すれば
、第1図及び第2図はパネル1例を示し、該パネルは繊
維によつて補強された水硬性無機質系硬化体によつて枠
組1と中桟2及び表面層3、3′が形成されており、そ
の内部空間4には軽量体5が一体的に設けられていると
共に表面層3には凹凸によつて模様や図柄が形成され、
他の表面層3′には結合用ナツト6がその一側を露出し
て埋没されている。尚6′は枠組1の外側面にその一側
を露出して埋設された結合用ナツトである。上記パネル
は中桟2、2が交差してX形に設けられているが、第3
図に示されるように中桟2′、2′…は平行して枠組間
に設けてもよい。Embodiments of the present invention will be described below with reference to the accompanying drawings. FIGS. 1 and 2 show one example of a panel, which is made of a hydraulic inorganic cured material reinforced with fibers. A framework 1, a middle crosspiece 2, and surface layers 3, 3' are formed, and a lightweight body 5 is integrally provided in an internal space 4 of the framework 1, and a pattern or design is formed on the surface layer 3 by unevenness. formed,
A coupling nut 6 is buried in the other surface layer 3' with one side exposed. Reference numeral 6' denotes a coupling nut embedded in the outer surface of the framework 1 with one side thereof exposed. The above panel is provided in an X shape with the middle crosspieces 2 and 2 intersecting, but the third
As shown in the figure, the middle bars 2', 2', . . . may be provided in parallel between the frames.
上記のパネルを製造するには、先づ凹凸が形成されたモ
ルタル、繊維入りモルタル、コンクリート、金属板、合
成樹脂、発泡した合成樹脂(発泡スチロール等)等でつ
くられた底型枠上に剥離剤適量を混合した繊維入り水硬
性無機質系硬化原料を薄く展拡し、更にその上に剥離剤
を混合していない繊維入り水硬性無機質系硬化原料を設
けて表面層3を形成し、その上に所定の位置に発泡スチ
ロール、軽量コンクリート、ガラス繊維成形板等の軽量
体5を配設し、該軽量体と側型枠を利用して剥離剤を混
合していない繊維入り水硬性無機質系硬化原料を打設し
て枠組1と中桟2または2′を形成し、更にその上に剥
離剤を混合していない繊維入り水硬性無機質系硬化原料
を展拡して表面層3′を形成し、硬化後離型してつくる
ことができる。To manufacture the above panels, first, a release agent is applied onto the bottom form made of textured mortar, fiber-filled mortar, concrete, metal plate, synthetic resin, foamed synthetic resin (styrofoam, etc.), etc. A suitable amount of the fiber-containing hydraulic inorganic curing raw material mixed therein is spread thinly, and a fiber-containing hydraulic inorganic curing raw material not mixed with a release agent is further provided on top of it to form the surface layer 3. A lightweight body 5 such as styrofoam, lightweight concrete, glass fiber molded plate, etc. is placed at a predetermined position, and the fiber-containing hydraulic inorganic curing raw material without a release agent mixed therein is made using the lightweight body and the side formwork. A framework 1 and a middle crosspiece 2 or 2' are formed by pouring, and then a fiber-containing hydraulic inorganic curing raw material not mixed with a release agent is spread thereon to form a surface layer 3', and then hardened. It can be made by demolding afterwards.
また第4図は底型枠7上に剥離剤適量を混合した繊維入
り水硬性無機質系硬化原料を薄く展拡し、更にその上に
剥離剤を混合していない繊維入り水硬性無機質系硬化原
料を設けて表面層3を形成し、その上に金属板、繊維に
よつて補強された無機質系硬化板、合成樹脂板、或いは
合板等によつて形成された中空型8を配設し、該中空型
8と側型枠9内に剥離剤を混合しない繊維入り水硬性無
機質系硬化原料を打設して枠組と中桟を形成し、その内
部空間にパーライトを混合した軽量モルタル10を充填
し、更にその上に剥離剤を混合していない繊維入り水硬
性無機質系硬化原料を展拡して表面層3′を形成したパ
ネル製造法他例を示す。尚この製造法では中型枠8はパ
ネル内に埋没される。Fig. 4 shows a thin layer of fiber-containing hydraulic inorganic curing raw material mixed with an appropriate amount of release agent on the bottom form 7, and a fiber-containing hydraulic inorganic curing raw material with no release agent mixed thereon. A hollow mold 8 made of a metal plate, an inorganic hardened plate reinforced with fibers, a synthetic resin plate, plywood, etc. is placed on top of the surface layer 3. A fiber-containing hydraulic inorganic curing material not mixed with a release agent is poured into the hollow mold 8 and the side formwork 9 to form a framework and a middle crosspiece, and the internal space thereof is filled with lightweight mortar 10 mixed with perlite. Further, another example of the panel manufacturing method is shown in which a surface layer 3' is formed by spreading a fiber-containing hydraulic inorganic curing raw material with no release agent mixed thereon. In this manufacturing method, the medium form frame 8 is buried within the panel.
以上パネル製造法2例について説明したが、硬化原料内
に鉄筋、ワイヤメツミユ等の配筋11を行つて更に補強
してよいことはいう迄もない。またシリコン樹脂等の剥
離剤の水硬化無機質系硬化原料に対する混合比は、重量
比で1〜2%程度が望ましい。Although two examples of panel manufacturing methods have been described above, it goes without saying that reinforcing bars 11 such as reinforcing bars or wire mesh may be placed inside the hardened raw material for further reinforcement. Further, the mixing ratio of the release agent such as silicone resin to the water-cured inorganic curing raw material is preferably about 1 to 2% by weight.
従来コンクリート等を打設するときは型枠に油等の剥離
剤を塗布して打設しており、剥離剤の塗布作業が煩雑で
あるばかりかコンクリート等と型枠の間に剥離剤が介在
するため型枠の面をコンクリート等の表面に忠実に転写
できない等の欠点があつた。しかるにこの発明は前記の
ように構成されるから、型枠に剥離剤を塗布することな
く離型することができると共に、硬化体表面に型枠の表
面を忠実に転写することができて、塗装を美しく施すこ
とが可能であり、特に型枠表面に凹凸模様が設けられて
いるときは効果的で、仕上りの美しい硬化体を製造する
ことができる等の効果を有する。Conventionally, when pouring concrete, etc., a release agent such as oil is applied to the formwork, and not only is the work of applying the release agent complicated, but the release agent is interposed between the concrete, etc. and the formwork. Therefore, there were drawbacks such as the inability to faithfully transfer the surface of the formwork to the surface of concrete, etc. However, since the present invention is constructed as described above, it is possible to release the mold without applying a release agent to the mold, and the surface of the mold can be faithfully transferred to the surface of the cured product, making it possible to paint. This method is particularly effective when the surface of the mold is provided with an uneven pattern, and has the effect of producing a cured product with a beautiful finish.
まだこの発明では水硬性無機質系硬化原料にセメント系
または石膏系等の水硬性無機質系硬化原料が使用され、
これに混合される繊維にはガラス繊維、耐アルカリ性硝
子繊維、シラスウール、石綿繊維、炭化珪素繊維、金属
繊維、ナイロン繊維等の有機質繊維等が使用される。However, in this invention, a cement-based or gypsum-based hydraulic inorganic hardening raw material is used as the hydraulic inorganic hardening raw material.
The fibers to be mixed therein include organic fibers such as glass fibers, alkali-resistant glass fibers, shirasu wool, asbestos fibers, silicon carbide fibers, metal fibers, and nylon fibers.
添付図面はこの発明の実施例を示すものであつて、第1
図はパネル1例を説明するための斜視図、第2図は第1
図のパネル背面図、第3図はパネル他例の背面図、第4
図はパネル製造法1例を説明するための縦断面図である
。
特許出願人 高津和夫
満尾ミツ子The attached drawings show embodiments of the present invention, and show the first embodiment.
The figure is a perspective view for explaining one example of the panel, and the second figure is the first one.
Figure 3 is a rear view of the panel shown in Figure 3. Figure 4 is a rear view of another example of the panel.
The figure is a longitudinal sectional view for explaining one example of a panel manufacturing method. Patent applicant Kazuo Takatsu Mitsuko Mitsuo
Claims (1)
上に薄く展拡し、その上に剥離剤を混合していない水硬
性無機質系硬化原料を設け、硬化後離型してなることを
特徴とする水硬性無機質系硬化体の製造法。A hydraulic inorganic curing raw material mixed with an appropriate amount of a release agent is spread thinly on the bottom mold, a hydraulic inorganic curing raw material without a release agent mixed therein is placed on top of it, and the mold is released after curing. A method for producing a hydraulic inorganic cured product characterized by: