JPS5937307B2 - fibrous coating material - Google Patents
fibrous coating materialInfo
- Publication number
- JPS5937307B2 JPS5937307B2 JP4123181A JP4123181A JPS5937307B2 JP S5937307 B2 JPS5937307 B2 JP S5937307B2 JP 4123181 A JP4123181 A JP 4123181A JP 4123181 A JP4123181 A JP 4123181A JP S5937307 B2 JPS5937307 B2 JP S5937307B2
- Authority
- JP
- Japan
- Prior art keywords
- coating material
- fibrous
- fibers
- fibrous coating
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
この発明は、繊維質塗り材を製造するに当たり、接着成
分として使用されるカルボキシルメチルセルローズナト
リウム（通常ＣＭＣと称す。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to sodium carboxymethyl cellulose (usually referred to as CMC), which is used as an adhesive component in the production of fibrous coating materials.
）を短繊維状に形成することを特徴とする繊維質塗材に
関するものである。従来繊維質上塗り材として提案され
ているものとしては、例えば特公昭５３−２９３３２号
においては、接着成分として使用されるカルボキシメチ
ルセルローズナトリウムの粉末或は粒度のものを使用さ
れているが、この方法であると、素材が繊維であつて接
着成分のカルボキシメチルセルローズナトリウムの形状
が粒子であるので、繊維と顆粒子或は粉末とでは比重や
粒度が異なるので分離して攪拌混合が出来ず混練の場合
に均一な糊状とならず、所謂糊玉を生じて成分が分散し
ない欠点があつた。) is formed into short fibers. For example, in Japanese Patent Publication No. 53-29332, a powder or granular version of carboxymethyl cellulose sodium used as an adhesive component has been proposed as a fibrous top coating material. In this case, the material is fiber and the adhesive component sodium carboxymethylcellulose is in the form of particles, so the fibers and granules or powder have different specific gravity and particle size, so they cannot be separated and mixed by stirring, making it difficult to knead. In some cases, it does not form a uniform paste-like state, resulting in the formation of so-called glue balls, which prevent the components from being dispersed.
この発明は素材と同様にカルボキシルメチルセルローズ
ナトリウムを短繊維状に形成して、他の繊維と同様の繊
維質に形成して互に絡ませやすくなして均一に混合させ
、これに水を加えて混練することにより均一の糊状化を
図ることを目的とするものである。This invention involves forming carboxymethyl cellulose sodium into short fibers similar to the raw material, forming them into the same fibrous quality as other fibers so that they can be easily entangled with each other, and mixing uniformly, and then adding water and kneading. The purpose of this is to achieve a uniform paste-like state by doing so.
この発明において、カルボキシルメチルセルローズナト
リウムを短繊維状の形状に形成することは、素材として
の合成樹脂製繊維或は綿繊維と同一形状の繊維質として
混合することによつて互に絡み合つて分離することがな
く水を入れて混練するに当たり直ちに溶解しないので、
塗材料が充分攪拌されて均一に分散するので糊玉もでき
ず均一なる接着力を増大させるものである。In this invention, carboxymethylcellulose sodium is formed into short fibers by mixing the fibers of the same shape with synthetic resin fibers or cotton fibers as raw materials so that they are entangled with each other and separated. Because it does not dissolve immediately when adding water and kneading,
Since the coating material is thoroughly stirred and dispersed uniformly, no glue balls are formed and uniform adhesion is increased.
従つて、均一な撹拌混合によつて分離ができなければ、
カルボキシルメチルセルローズナトリウムの量が１０％
〜２０％も少くても接着力及び保水率が良好である。Therefore, if separation cannot be achieved by uniform stirring and mixing,
The amount of sodium carboxymethyl cellulose is 10%
Adhesion and water retention are good even if the amount is as low as ~20%.
上述のようにこの発明は繊維素材例えば合成樹脂製繊維
或は綿繊維等の繊維質物に混合配合素材としてカルボキ
シルメチルセルローズナトリウムの短繊維を混合撹拌す
ると、素材が互に繊維質物であるので、容易に絡み合つ
て分離することがなく、混合が均一に行われて、これを
水で混練するも、分解酵素（セルラーゼ）の発生が少な
いので粘度が低下しないことは勿論糊玉も生ぜず而かも
接着力を増大するものである。As mentioned above, the present invention provides a method of mixing and stirring short fibers of sodium carboxymethyl cellulose as a blended material with a fibrous material such as synthetic resin fiber or cotton fiber, and the materials are both fibrous materials, so it is easy to mix and stir. There is no entanglement and separation, and the mixture is uniformly mixed. Even when this is kneaded with water, there is little generation of degrading enzymes (cellulase), so the viscosity does not decrease and no glue balls may form. This increases adhesive strength.
次に本発明の実施例について説明すると次のと等を撹拌
混合して得た繊維塗材に水量５０００部を加えて混練し
、コテ塗り施工したところ、下表の通り良好な結果が得
られた。Next, to explain an example of the present invention, 5000 parts of water was added to a fiber coating material obtained by stirring and mixing the following materials, and the mixture was kneaded and applied with a trowel. As shown in the table below, good results were obtained. Ta.
実施例 ２
等を混合して攪拌して得たる繊維塗材に水量、５５００
部を加えて混練し、コテ塗り施工したところ下表の結果
を得たのである。Example 2 The amount of water in the fiber coating material obtained by mixing and stirring was 5500.
When the mixture was mixed and applied with a trowel, the results shown in the table below were obtained.
Claims (1)
ムとする繊維質上塗り材において、混合配合する前記カ
ルボキシルメチルセルローズナトリウムを短繊維状に形
成して互に絡ませ易くなして均一に混合させ、これに水
を加えて混練して均一の糊状化しうるようにしたことを
特徴とする繊維質塗材。1. In a fibrous top coating material whose adhesive component is carboxymethylcellulose sodium, the carboxymethylcellulose sodium to be mixed and blended is formed into short fibers so that they can be easily entangled with each other and mixed uniformly, and then water is added and kneaded. A fibrous coating material characterized by being able to be made into a uniform paste-like material.