JPS5923597B2 - Cleaner for marking rubber products - Google Patents
Cleaner for marking rubber productsInfo
- Publication number
- JPS5923597B2 JPS5923597B2 JP55073679A JP7367980A JPS5923597B2 JP S5923597 B2 JPS5923597 B2 JP S5923597B2 JP 55073679 A JP55073679 A JP 55073679A JP 7367980 A JP7367980 A JP 7367980A JP S5923597 B2 JPS5923597 B2 JP S5923597B2
- Authority
- JP
- Japan
- Prior art keywords
- cleaner
- weight
- water
- marking
- rubber products
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は、ゴム製品のマーキング用クリーナーに関する
。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to a cleaner for marking rubber products.
従来、加硫されたゴム製品として、例えば自動車等のタ
イヤ、ベルト、建築用ゴムシート等が知られている。Conventionally, vulcanized rubber products such as tires for automobiles, belts, rubber sheets for construction, etc. are known.
これらのゴム製品はその使用条件に応じて非常に複雑な
原料配合組成を有している。例えば、使用条件が非常に
苛酷な自動車用タイヤを例にとると、まずスチレン−ブ
タジエンゴム等をベースとして、これに紫外線による老
化防止剤、加硫剤、加硫促進剤、軟化剤、プロセスオイ
ル、カーボンブラック、補強繊維等を添加して製品化さ
れている。このような組成から成るタイヤは使用時に前
記油脂分、老化防止剤等の添加成分が表面層を滲出して
、ゴム質を保護するようになつている。These rubber products have extremely complex raw material compositions depending on their usage conditions. For example, in the case of automobile tires, which are used under very harsh conditions, they are first made of styrene-butadiene rubber, etc., then added with ultraviolet anti-aging agents, vulcanizing agents, vulcanization accelerators, softeners, and process oils. , carbon black, reinforcing fibers, etc. are added to the product. When a tire having such a composition is used, the above-mentioned oils and fats, anti-aging agents, and other additive components exude from the surface layer to protect the rubber.
ところで最近自動車用タイヤのマーキングとして白色の
ゴムをタイヤ製造時に埋め込むことによりタイヤのサイ
ドウォールに白色ラインの入つたタイヤが製造されたり
、あるいは特殊なマーキング用組成物を用いてタイヤの
サイドウォールに各種の模様等を描いたタイヤが見受け
られるようになつてきた。しかし、前記した如くタイヤ
はその使用中に原材料の一部であるステアリン酸、パラ
フィン類、タール、プロセスオイル、カーボンブラック
、硫黄、その他添加剤が表面層上に滲出してくるため、
マーキング層が著しく汚染される。By the way, recently, tires with white lines on the sidewalls of automobile tires have been manufactured by embedding white rubber during tire manufacturing as markings for automobile tires, or tires with various markings on the sidewalls of tires using special marking compositions. It is becoming common to see tires with patterns such as . However, as mentioned above, during use of tires, some of the raw materials such as stearic acid, paraffins, tar, process oil, carbon black, sulfur, and other additives ooze out onto the surface layer.
The marking layer is severely contaminated.
又、自動車等の走行中に油、アスファルト、砂、泥水等
が外部より飛散しタイヤ表面に付着するため、マーキン
グ層の汚染は更に増加する。Furthermore, while the vehicle is running, oil, asphalt, sand, muddy water, etc. are scattered from the outside and adhere to the tire surface, further increasing the contamination of the marking layer.
これらマーキング層表面に不着した物質は水あるいは石
鹸水等では全く除去できないため、マーキング層は非常
に見苦しいものとなつていた。Since these substances adhering to the surface of the marking layer cannot be removed at all with water or soapy water, the marking layer has become very unsightly.
従・ 来のタイヤは黒色であつた為、前記の如き付着物
は目立たなかつたが、特に白色あるいは淡色のマーキン
グ等はそれの汚れが非常に目立ち易く、極端な場合マー
キングを入れたがために全体の美観を著しく損ねる結果
ともなるのである。本発明者等は、これらマーキング層
上に滲出し、もしくは付着した汚染物の除去に関し種々
の検討を加えた結果、本発明に到達したものである。Conventional tires were black, so the deposits mentioned above were not noticeable, but dirt on white or light-colored markings is very noticeable, and in extreme cases, it is difficult to see dirt on the tires because of the markings. This results in a significant deterioration of the overall aesthetic appearance. The present inventors have arrived at the present invention as a result of various studies regarding the removal of contaminants that have oozed out or adhered to these marking layers.
即ち、本発明は、（１）ブチルカルビトール７０〜９９
重量％とアセトン１〜３０重量％から成るゴム製品のマ
ーキング用クリーナー（２）ブチルカルビトール４０〜
６０重量％、アセトン１〜３０重量％、および５０重量
％以下の水および／または水溶性多価アルコールから成
るゴム製品のマーキング用クリーナー、（３）ブチルカ
ルビトール６８〜９７重量％、アセトン１〜３０重量％
、および界面活性剤２重量％以下から成るゴム製品のマ
ーキング用クリーナーに関する。That is, the present invention provides (1) butyl carbitol 70-99
Cleaner for marking rubber products consisting of 1% to 30% by weight of acetone (2) Butyl carbitol 40% to 30% by weight
Cleaner for marking rubber products consisting of 60% by weight, 1-30% by weight of acetone, and 50% by weight or less of water and/or water-soluble polyhydric alcohol, (3) 68-97% by weight of butyl carbitol, 1-30% by weight of acetone. 30% by weight
, and a cleaning agent for marking rubber products comprising 2% by weight or less of a surfactant.
つまり、本発明はブチルカルビトール（ジエチレングリ
コールモノブチルエーテル）を主とするクリーナーであ
り、特にゴム製品に用いられているマーキング表面の汚
れ除去のためクリーナーである。That is, the present invention is a cleaner mainly containing butyl carbitol (diethylene glycol monobutyl ether), and is particularly a cleaner for removing stains from marking surfaces used in rubber products.
本発明に使用されるブチルカルビトールは、ゴム製品の
内部から滲出し、マーキング層表面に付着する汚染物質
の除去に極めて有効である。Butyl carbitol used in the present invention is extremely effective in removing contaminants that exude from the inside of rubber products and adhere to the surface of the marking layer.
即ち、ゴム製品の内部から滲出しマーキング層表面に付
着したパラフイン類、タール、プロセスオイル等は、ブ
チルカルビトールを塗布することにより簡単に除去でき
るとともに、該溶剤はマーキング層を全く侵すことがな
く、しかも水に対する溶解性が非常に大きいため、最後
に水洗いすることによつて汚染物質を溶解したクリーナ
ーを洗い流すことができる。本発明の第１の態様として
のクリーナーは、前記ブチルカルビトールにアセトンを
添加したクリーナーである。In other words, paraffin, tar, process oil, etc. that ooze out from inside the rubber product and adhere to the surface of the marking layer can be easily removed by applying butyl carbitol, and the solvent does not attack the marking layer at all. Moreover, since the solubility in water is very high, the cleaner containing the dissolved contaminants can be washed away by washing with water at the end. A cleaner according to the first aspect of the present invention is a cleaner in which acetone is added to the above-mentioned butyl carbitol.
ここにおいて使用されるアセトンは、例えば自動車の走
行中に外部から飛散してマーキング層表面に付着した油
脂等の除去に有効である。The acetone used here is effective for removing, for example, oils and fats that are scattered from the outside and adhered to the surface of the marking layer while the car is running.
しかして、該アセトンがクリーナー中において３０重量
％をこえて使用されると、マーキング層がクリーナーに
より溶解、膨潤されるようになる為好ましくない。However, if the amount of acetone exceeds 30% by weight in the cleaner, the marking layer will be dissolved and swollen by the cleaner, which is not preferable.
当然のことながらアセトンも水に対する溶解度が大きい
ので、クリーナー塗布後、最後に水洗除去できる。又、
本発明の第２の態様においてはブチルカルビトールおよ
びアセトンの他の水および／または水溶性多価アルコー
ルを使用する。Naturally, acetone also has a high solubility in water, so it can be removed by washing with water after applying the cleaner. or,
A second embodiment of the invention uses other water and/or water-soluble polyhydric alcohols such as butyl carbitol and acetone.
本発明のクリーナーにおいて水を使用することにより、
タイヤ等外部から飛散、付着した泥等を洗い流す作用と
ともに、クリーナー自身の着火の危険性を多少なりとも
低下させる役割を果すことができる。By using water in the cleaner of the present invention,
It has the effect of washing away mud and the like that are scattered and adhered to the outside of tires, etc., and also serves to reduce the risk of the cleaner itself igniting to some extent.
一方、水溶性多価アルコールは、クリーナー液を増粘さ
せることによつてブチルカルビトールとアセトン溶液の
ダレや流下を防止するために使用される。On the other hand, the water-soluble polyhydric alcohol is used to thicken the cleaner liquid and thereby prevent the butyl carbitol and acetone solution from dripping or flowing down.
勿論、該多価アルコールも最後に水洗除去できなければ
ならないため水溶性であることが必要である。Of course, the polyhydric alcohol must also be water-soluble since it must be able to be removed by washing with water at the end.
前記水溶性多価アルコールとしては、例えばエチレング
リコール、１・２−プロピレングリコール、１・３−ブ
チレングリコール、２・３−ブチレングリコール、２−
メチル−２・４−ペンタンジオール、ヘキサンジオール
−２・５、ヘプタンジオール一２・４、ジプロピレング
リコール、トリエチレングリコール、ポリエチレングリ
コール、グリセリン等が挙げられ、これらは１種もしく
は２種以上の混合物として使用される。Examples of the water-soluble polyhydric alcohol include ethylene glycol, 1,2-propylene glycol, 1,3-butylene glycol, 2,3-butylene glycol, 2-
Examples include methyl-2,4-pentanediol, hexanediol-2,5, heptanediol-2,4, dipropylene glycol, triethylene glycol, polyethylene glycol, glycerin, etc., and these may be used alone or in a mixture of two or more. used as.
前記水および／または水溶性多価アルコールは、クリー
ナー全成分中５０重量％以下、好ましくは１０〜４０重
量％の範囲で使用される。The water and/or water-soluble polyhydric alcohol is used in an amount of 50% by weight or less, preferably from 10 to 40% by weight, based on the total cleaner components.
水および／または、水溶性多価アルコールの量が５０重
量％をこえて使用されると、汚染物質除去成分の濃度が
薄くなるため好ましくない。If the amount of water and/or water-soluble polyhydric alcohol used exceeds 50% by weight, it is not preferable because the concentration of the contaminant removing component becomes diluted.
更に本発明の第３の態様においては、ブチルカルビトー
ルとアセトンの他に界面活性剤を使用する。該界面活性
剤の使用は、クリーナー液のマーキング層中への浸透を
助けるために好ましい。Furthermore, in a third aspect of the invention, a surfactant is used in addition to butyl carbitol and acetone. The use of the surfactant is preferred to aid in the penetration of the cleaner fluid into the marking layer.
界面活性剤の使用量は、クリーナー全成分中２重量％以
下、好ましくは０．１重量％以上である。前記界面活性
剤としては、市販のアニオン系界面活性剤、カチオン系
界面活性剤、ノニオン系界面活性剤のいずれも使用可能
であるが、特に油、タール、鉱物油等に浸透性のよいア
ニオン系界面活性剤又はノニオン系界面活性剤が好まし
い。以上で本発明の主たる態様について詳述したが前記
記載内容から明らかに、本発明のクリーナーにおいては
（１）ブチルカルビトールと５０重量％以下の水および
／または水溶性多価アルコール、（６）ブチルカルビト
ールと２重量％以下の界面活性剤、（！１１）４０〜６
０重量％のブチルカルビトール、１〜３０重量％のアセ
トン、５０重量％以下の水および／または水溶性多価ア
ルコール、および２重量％以下の界面活性剤等の組合せ
も好ましいものである。前記の如き本発明のクリーナー
は、そのまま、もしくはジメチルエーテル、ＬＰＧ、フ
ツソガス等と共にエアゾール化して市販に供される。The amount of surfactant used is 2% by weight or less, preferably 0.1% by weight or more based on the total cleaner components. As the surfactant, commercially available anionic surfactants, cationic surfactants, and nonionic surfactants can be used, but anionic surfactants that have good permeability to oil, tar, mineral oil, etc. are particularly suitable. Surfactants or nonionic surfactants are preferred. The main aspects of the present invention have been described in detail above, but it is clear from the above description that the cleaner of the present invention includes (1) butyl carbitol and 50% by weight or less of water and/or water-soluble polyhydric alcohol; Butyl carbitol and 2% by weight or less surfactant, (!11) 40-6
Combinations such as 0% by weight of butyl carbitol, 1 to 30% by weight of acetone, 50% by weight or less of water and/or water-soluble polyhydric alcohol, and 2% by weight or less of a surfactant are also preferred. The cleaner of the present invention as described above is commercially available as it is or after being made into an aerosol together with dimethyl ether, LPG, fluorogas, etc.
かくして得られた本発明のクリーナーは、ゴム製品のマ
ーキング層上にハケ、スプレー等の方法により塗布され
、少時放置後ふきとるかもしくは水で洗い流すことによ
り、マーキング層上の汚れを簡単に除去することができ
る。本発明のクリーナーは、前記の通りマーキング層の
汚れを除去することは勿論のこと、ゴム製品そのものに
付着した油分等の除去も可能であり、従つてゴム製品の
マ一゛−キング部分以外の部分にはみ出して塗布されて
も一向に差しつかえない。The thus obtained cleaner of the present invention is applied onto the marking layer of a rubber product by a method such as brushing or spraying, and after being left for a while, the dirt on the marking layer can be easily removed by wiping it off or washing it off with water. be able to. The cleaner of the present invention can not only remove dirt from the marking layer as described above, but also remove oil adhering to the rubber product itself. There is no problem even if the product is applied to some areas.
前記の通り、本発明のクリーナーはゴム製品を全く侵す
ことなくマーキング層の汚れを完全に除去でき、しかも
、最後に簡単に水洗することができるため、自動車のタ
イヤマーキング用クリーナーとして非常に有用であると
ともに、その他のゴム製品のマーキング用クリーナーと
しても有用である。以下本発明の詳細を実施例により説
明する。As mentioned above, the cleaner of the present invention can completely remove dirt from the marking layer without damaging rubber products, and can be easily washed with water at the end, making it very useful as a cleaner for car tire markings. It is also useful as a marking cleaner for other rubber products. The details of the present invention will be explained below with reference to Examples.
「部」又は［％」は「重量部」又は「重量％」を示す。
実施例
まず、下記配合によりマーキング用組成物を得た。"Part" or "%" indicates "part by weight" or "% by weight".
Example First, a marking composition was obtained using the following formulation.
前記組成物を以下のようにして乗用車のタイヤのサイド
ウオールに塗布した。The composition was applied to the sidewall of a passenger car tire as follows.
まず夕。First, evening.
イャのサイドウオール部の塗布部分を中性洗剤で拭いた
後、更に溶剤で拭き取り表面調整を行つた。ついで必要
な模様以外の部分にマスキングテープを貼つた後、前記
マーキング組成物を薄く２回塗りした。塗布後、２０〜
３０分したらマスキングテープを除去し、さらに常温で
２時間程度乾燥せしめてマーキング層を形成させた。（
参考写真Ｂ）かくしてマーキングされたタイヤを乗用車
に取りつけて実際に７日間（３００ｋｍ）走行させた。After wiping the coated area on the sidewall of the ear with a neutral detergent, the surface was adjusted by wiping with a solvent. Next, masking tape was applied to areas other than the required pattern, and then the marking composition was applied thinly twice. After application, 20~
After 30 minutes, the masking tape was removed and further dried at room temperature for about 2 hours to form a marking layer. (
Reference photo B) The thus marked tires were attached to a passenger car and the car was actually driven for 7 days (300 km).
次に以下の配合により本発明のクリーナーを得た。該ク
リーナーを前記走行後のタイヤマーキング層の半分に塗
布し、少時放置後水洗した所、マーキング層上の汚れは
簡単に除去でき、走行前の色とほとんどかわらない色に
もどすことが出来た。Next, a cleaner of the present invention was obtained using the following formulation. When the cleaner was applied to half of the tire marking layer after running, and the tire was left for a while and then washed with water, the dirt on the marking layer could be easily removed, and the color could be returned to almost the same as before running. .
（参考写真Ａ１タイヤの中心から各マーキング層に向つ
て右半分は本発明のクリーナーにより汚れを除去したも
のであり、同じく左半分の茶褐色を帯びた色相はクリー
ナーで汚れを除去する前を各々示す。）前記実施例より
明らかに、本発明のクリーナーは、ゴム製品のマーキン
グ用クリーナーとして優れた汚れ除去性を有している。(Reference Photo A1 The right half of the tire from the center of the tire to each marking layer is the one after dirt has been removed using the cleaner of the present invention, and the brownish hue on the left half shows the state before dirt was removed with the cleaner. ) It is clear from the above examples that the cleaner of the present invention has excellent stain removal properties as a cleaner for marking rubber products.
Claims (1)
〜３０重量％から成るゴム製品のマーキング用クリーナ
ー。 ２ ブチルカルビトール４０〜６０重量％、アセトン１
〜３０重量％、および５０重量％以下の水および／また
は水溶性多価アルコールから成るゴム製品のマーキング
用クリーナー。 ３ ブチルカルビトール６８〜９７重量％、アセトン１
〜３０重量％、および界面活性剤２重量％以下から成る
ゴム製品のマーキング用クリーナー。[Claims] 1. Butyl carbitol 70-99% by weight and acetone 1
Cleaner for marking rubber products consisting of ~30% by weight. 2 Butyl carbitol 40-60% by weight, acetone 1
A cleaner for marking rubber products, comprising up to 30% by weight and up to 50% by weight of water and/or water-soluble polyhydric alcohol. 3 Butyl carbitol 68-97% by weight, acetone 1
A cleaner for marking rubber products, comprising ~30% by weight and 2% by weight or less of a surfactant.