JPH1193094A - Antirust paper - Google Patents
Antirust paperInfo
- Publication number
- JPH1193094A JPH1193094A JP25360197A JP25360197A JPH1193094A JP H1193094 A JPH1193094 A JP H1193094A JP 25360197 A JP25360197 A JP 25360197A JP 25360197 A JP25360197 A JP 25360197A JP H1193094 A JPH1193094 A JP H1193094A
- Authority
- JP
- Japan
- Prior art keywords
- rust
- paper
- benzotriazole
- preventive
- lead frame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、リードフレーム等
の金属枚葉体に用いられる防錆紙に関するもので、特に
使用するパッケージの材料がセラミックである半導体に
用いるリードフレーム用防錆紙に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rust preventive paper used for a metal sheet such as a lead frame, and more particularly to a rust preventive paper for a lead frame used for a semiconductor whose package material is ceramic.
【０００２】[0002]
【従来の技術】リードフレームの保管、輸送中の錆止め
は、一般に、防錆紙とリードフレームを交互に重ね、各
防錆紙間に各リードフレームが挟まれている状態にして
おく。このように保たれていても、保管、輸送中の条件
によって、また、使用するパッケージの材料がセラミッ
クである際にはセラミックの焼成処理によって、４２材
（ニッケル４２重量％、残部鉄）表面の酸化などによる
変色、錆発生をすることがある。すなわち、防錆紙の防
錆性能は十分なものではない。2. Description of the Related Art In general, rust prevention during storage and transportation of a lead frame is performed by alternately stacking rust-preventive papers and lead frames so that each lead frame is sandwiched between the rust-preventive papers. Even if kept in this way, depending on the conditions during storage and transportation, and when the package material to be used is ceramic, the ceramic material is subjected to a sintering process, so that the surface of the 42 material (nickel 42% by weight, balance iron) can be used. Discoloration and rust may occur due to oxidation. That is, the rustproofing performance of the rustproof paper is not sufficient.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、上記のよう
な保管、輸送中の酸化などによる、また、セラミックの
焼成処理による、変色、錆発生が起こらないよう、防錆
性能を向上させた防錆紙を提供するものである。SUMMARY OF THE INVENTION The present invention has improved rust prevention performance so that discoloration and rust do not occur due to oxidation or the like during storage or transportation as described above, or due to firing of ceramics. It provides rust-proof paper.
【０００４】[0004]
【課題を解決するための手段】本発明は、紙に防錆剤を
含浸させた防錆紙において、ベンゾトリアゾール系防錆
剤に有機アミン塩を添加した防錆剤を用いていることを
特徴とする防錆紙である。Means for Solving the Problems The present invention is characterized in that in a rust preventive paper obtained by impregnating a paper with a rust preventive, a rust preventive obtained by adding an organic amine salt to a benzotriazole-based rust preventive is used. Rust-proof paper.
【０００５】また、本発明は、上記発明の防錆紙におい
て、前記防錆剤がベンゾトリアゾール系防錆剤１００重
量部に対し有機アミン塩の添加量が３０〜７０重量部で
ある防錆紙である。Further, the present invention provides the rust-proofing paper according to the above-mentioned invention, wherein the rust-preventing agent comprises 30 to 70 parts by weight of an organic amine salt per 100 parts by weight of a benzotriazole-based rust-preventing agent. It is.
【０００６】また、本発明は、上記発明の防錆紙におい
て、前記防錆剤の紙への含浸量が４〜６ｇ／ｍ2 である
防錆紙である。[0006] The present invention also relates to the rust-preventive paper according to the above-mentioned invention, wherein the impregnating amount of the rust-preventive agent into the paper is 4 to 6 g / m 2 .
【０００７】[0007]
【発明の実施の形態】本発明を一実施の形態に基づいて
以下に説明する。図１は、本発明による防錆紙が使用さ
れる状態の一実施例を説明する側面図である。図１の側
面図に示すように、防錆紙（２）が使用される際は、２
枚以上のリードフレーム（３）が直接に接触して重なる
ことがないように、１枚のリードフレーム（３）と１枚
の防錆紙（２）とを交互に重ね合わせる状態で、防錆紙
は使用されるものである。図２は、その状態の平面図で
あり、図２に示すようにリードフレーム（３）に対し防
錆紙（２）は面積の大きなものになっている。図３は、
リードフレーム（３）が、６ピース連なる状態で保管、
輸送される一例を示している。図４は、１ピース（４）
分のリードフレーム（３）の平面図である。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below based on one embodiment. FIG. 1 is a side view illustrating an embodiment of a state in which the rust-proof paper according to the present invention is used. As shown in the side view of FIG. 1, when rust-proof paper (2) is used,
In order to prevent more than one lead frame (3) from coming into direct contact and overlapping each other, one lead frame (3) and one rust-preventive paper (2) are alternately overlapped with each other. Paper is what is used. FIG. 2 is a plan view of this state. As shown in FIG. 2, the rust-proof paper (2) has a larger area than the lead frame (3). FIG.
The lead frame (3) is stored in a state of 6 pieces,
An example of transportation is shown. Figure 4 shows one piece (4)
FIG. 6 is a plan view of a minute lead frame (3).
【０００８】上記のように使用される防錆紙に含浸させ
る防錆剤として、ベンゾトリアゾール系防錆剤を用いる
際に、例えば、紙中の酸性の度合いが強いほど、ベンゾ
トリアゾール系防錆剤の防錆力が抑制されてしまうもの
であり、防錆剤としてベンゾトリアゾール系防錆剤を用
いる際に、ベンゾトリアゾール系防錆剤に有機アミン塩
を添加することにより、有機アミン塩が紙中の酸性の度
合いを弱める働きをし、ベンゾトリアゾール系防錆剤自
体の防錆力が抑制されず、本来の防錆力を保ち、その効
果を発揮するものとなる。ベンゾトリアゾール系防錆剤
としては、ベンゾトリアゾール、トリルトリアゾール、
カルボキシベンゾトリアゾールなどが好適なものであ
る。When a benzotriazole-based rust preventive is used as an rust preventive for impregnating the rust-proof paper used as described above, for example, the stronger the acidity in the paper is, the more the benzotriazole-based rust preventive is used. The rust-preventive power of the benzotriazole-based rust inhibitor is reduced by adding the organic amine salt to the benzotriazole-based rust-preventive agent. Acts to reduce the degree of acidity of the benzotriazole-based rust preventive agent itself, without inhibiting the rust-preventive power of the benzotriazole-based rust-preventive agent itself. Benzotriazole rust inhibitors include benzotriazole, tolyltriazole,
Carboxybenzotriazole and the like are preferred.
【０００９】また、有機アミン塩としては、ジシクロヘ
キシルアンモニウムナイトライト、ジシクロヘキシルア
ンモニウムカプリレート、シクロヘキシルアミンカーバ
メイト、シクロヘキシルアンモニウムラウレート、ジイ
ソプロピルアンモニウムナイトライト、ニトロナフタリ
ンアンモニウムナイトライトなどが好適なものである。Preferred examples of the organic amine salt include dicyclohexylammonium nitrite, dicyclohexylammonium caprylate, cyclohexylamine carbamate, cyclohexylammonium laurate, diisopropylammonium nitrite, and nitronaphthalin ammonium nitrite.
【００１０】また、ベンゾトリアゾール系防錆剤に対す
る有機アミン塩の添加量については、ベンゾトリアゾー
ル系防錆剤１００重量部に対し有機アミン塩の添加量が
３０重量部以下では、その効果が少なくなる傾向にあ
り、また、有機アミン塩の添加量が７０重量部以上にお
いても、その効果が少なくなる傾向にある。また、上記
のような防錆効果は、リードフレームの材料としては、
４２材（ニッケル４２％，残部鉄）において、その効果
が著しく表れるものである。The effect of the organic amine salt on the benzotriazole-based rust preventive is reduced when the amount of the organic amine salt is 30 parts by weight or less based on 100 parts by weight of the benzotriazole-based rust preventive. When the amount of the organic amine salt is 70 parts by weight or more, the effect tends to be reduced. In addition, the rust prevention effect as described above, as a lead frame material,
With 42 materials (42% nickel, balance iron), the effect is remarkably exhibited.
【００１１】表１は、本発明において用いる防錆剤の組
成、及び防錆剤の量を実施例として示したものである。
また、比較例として従来の防錆紙における防錆剤の組
成、及び防錆剤の量を示したものである。また、表１に
は、本発明における防錆紙を用いた際の、リードフレー
ム４２材の表裏面における錆の発生状態の試験結果を上
記実施例と比較例とを対比して示したものである。Table 1 shows the composition of the rust preventive used in the present invention and the amount of the rust preventive as examples.
As comparative examples, the composition of the rust inhibitor and the amount of the rust inhibitor in the conventional rust-proof paper are shown. Table 1 shows test results of the state of rust generation on the front and back surfaces of the lead frame 42 when the rust-preventing paper of the present invention was used, comparing the above-mentioned example with the comparative example. is there.
【００１２】[0012]
【表１】 [Table 1]
【００１３】本発明においては、表１に示すように、リ
ードフレームの表面にて、上記防錆剤の量４．２〜５．
７ｇ／ｍ2 において、上記実施例は錆の発生が殆どなく
「異常なし」であるのに対し、上記比較例は錆が発生し
「変色あり」であり、比較例と比べ実施例の防錆性能が
優れているものである。また、リードフレームの裏面に
て、上記防錆剤の量３．７ｇ／ｍ2 において錆が少々発
生しているが、防錆剤の量４．２〜６．７ｇ／ｍ2 にお
いては「変色あり」であるのに対し、上記比較例は錆が
多数発生しており、比較例と比べ実施例の防錆性能が優
れているものである。In the present invention, as shown in Table 1, the amount of the rust preventive on the surface of the lead frame is 4.2 to 5.
At 7 g / m 2 , in the above example, there was almost no rust and “no abnormality”, whereas in the above comparative example, rust was generated and “discoloration occurred”. It has excellent performance. On the back surface of the lead frame, a little rust was generated at the amount of the rust preventive of 3.7 g / m 2 , but when the amount of the rust preventive was 4.2 to 6.7 g / m 2 , “discoloration” occurred. On the other hand, "Comparative" indicates that a large amount of rust was generated in the comparative example, and the rust prevention performance of the example was superior to that of the comparative example.
【００１４】ここで、リードフレームは本試験における
リードフレームの表面がワイヤボンデイング面として使
用されるものなので、実施例の防錆性能は十分に得られ
ているとの評価がされるものであり、一方、リードフレ
ームの裏面は「変色あり」の結果ではあるが、比較例と
比べ実施例の防錆性能が優れているとの評価がされるも
のである。Since the lead frame used in this test has the surface of the lead frame used as a wire bonding surface, it is evaluated that the rust prevention performance of the embodiment is sufficiently obtained. On the other hand, although the result of “discolored” on the back surface of the lead frame, it is evaluated that the rust prevention performance of the example is superior to that of the comparative example.
【００１５】図５は、本発明における防錆紙の防錆性能
を試験する試料片の状態を示す側面図であり、約８×８
ｃｍの大きさの３枚の試料防錆紙（１２）の間に、約５
×５ｃｍの大きさの２枚の試料リードフレーム（１３）
（４２材）を交互に重ね、各試料防錆紙間に各試料リー
ドフレームが挟まれている状態である。図５において、
６はリードフレームの表面を、７はリードフレームの裏
面を示している。FIG. 5 is a side view showing a state of a sample piece for testing the rustproofing performance of the rustproof paper according to the present invention.
Approximately 5 cm between three sample rust-proof papers (12)
Two sample lead frames (13 x 5 cm)
(42 materials) are alternately stacked, and each sample lead frame is sandwiched between each sample rustproof paper. In FIG.
Reference numeral 6 denotes a front surface of the lead frame, and reference numeral 7 denotes a rear surface of the lead frame.
【００１６】試験条件としては、［（６５°Ｃ、９０
％、１８ｈ）、（−１０°Ｃ、９０％、６ｈ）］×１０
サイクルで行ない、また、結果の判定は、拡大鏡にてリ
ードフレームの表裏面を観察することにより行ったもの
である。The test conditions were [(65 ° C., 90
%, 18 h), (−10 ° C., 90%, 6 h)] × 10
The cycle was performed, and the result was determined by observing the front and back surfaces of the lead frame with a magnifying glass.
【００１７】また、本発明における防錆紙を用いた際の
リードフレームが、セラミックの焼成処理による、変
色、錆などの発生状態を示す焼成試験の結果は、上記実
施例においてはいずれも良好な結果が得られている。
（表示せず）。焼成条件としては、４８０°Ｃ、５分間
で行ない、また、結果の判定は、拡大鏡にてリードフレ
ームの表裏面を観察することにより行ったものである。In addition, the results of the firing test showing that the lead frame using the rust-proof paper of the present invention causes discoloration, rust, etc. due to the firing process of the ceramic are all good in the above examples. The results have been obtained.
(Not shown). The firing was performed at 480 ° C. for 5 minutes, and the result was determined by observing the front and back surfaces of the lead frame with a magnifying glass.
【００１８】[0018]
【発明の効果】本発明による防錆紙は、ベンゾトリアゾ
ール系防錆剤に有機アミン塩を添加した防錆剤を用いる
ので、ベンゾトリアゾール系防錆剤自体の防錆力が抑制
されず、本来の防錆力を保ち、その効果を発揮するもの
となり、保管、輸送中の防錆性能がが向上する。また、
セラミックの焼成処理による、変色、錆などの発生しな
いリードフレームが得られる。The rust preventive paper according to the present invention uses a rust inhibitor obtained by adding an organic amine salt to a benzotriazole rust preventive, so that the rust preventive power of the benzotriazole rust preventive itself is not suppressed, and the rust preventive itself is not suppressed. The rust-preventing ability is maintained and the effect is exhibited, and the rust-preventing performance during storage and transportation is improved. Also,
A lead frame free from discoloration, rust, and the like due to ceramic firing can be obtained.
【図１】本発明による防錆紙が使用される状態の一実施
例を説明する側面図である。FIG. 1 is a side view illustrating an embodiment in which a rust-proof paper according to the present invention is used.
【図２】本発明による防錆紙が使用される状態の一実施
例を説明する平面図である。FIG. 2 is a plan view illustrating one embodiment of a state in which the rust-proof paper according to the present invention is used.
【図３】リードフレームが６ピースで構成されている一
般的なリードフレームの状態を説明する図である。FIG. 3 is a view for explaining a state of a general lead frame in which a lead frame is composed of six pieces.
【図４】１ピース分のリードフレームの平面図である。FIG. 4 is a plan view of a lead frame for one piece.
【図５】本発明による防錆紙の防錆性能を試験する試料
片の状態を示す側面図である。FIG. 5 is a side view showing a state of a sample piece for testing the rustproofing performance of the rustproofing paper according to the present invention.
２…防錆紙 ３…リードフレーム ４…１ピース分のリードフレーム ６…リードフレームの表面 ７…リードフレームの裏面 １２…試料防錆紙 １３…試料リードフレーム 2: Rustproof paper 3: Lead frame 4: Lead frame for one piece
Claims (3)
ベンゾトリアゾール系防錆剤に有機アミン塩を添加した
防錆剤を用いていることを特徴とする防錆紙。1. A rust-proof paper obtained by impregnating a paper with a rust-preventive agent,
An anticorrosion paper comprising an anticorrosion agent obtained by adding an organic amine salt to a benzotriazole-based anticorrosion agent.
１００重量部に対し有機アミン塩の添加量が３０〜７０
重量部である請求項１記載の防錆紙。2. The rust preventive according to claim 1, wherein the amount of the organic amine salt is 30 to 70 parts by weight based on 100 parts by weight of the benzotriazole rust preventive.
The rust-proofing paper according to claim 1, which is in parts by weight.
2 である請求項１又は請求項２記載の防錆紙。3. The paper impregnated with said rust inhibitor has an amount of 4 to 6 g / m.
The rust-preventive paper according to claim 1 or 2, which is 2 .