JPH1192199A - Cement composition - Google Patents

Cement composition

Info

Publication number
JPH1192199A
JPH1192199A JP25242597A JP25242597A JPH1192199A JP H1192199 A JPH1192199 A JP H1192199A JP 25242597 A JP25242597 A JP 25242597A JP 25242597 A JP25242597 A JP 25242597A JP H1192199 A JPH1192199 A JP H1192199A
Authority
JP
Japan
Prior art keywords
weight
cement
fineness
comparative example
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP25242597A
Other languages
Japanese (ja)
Inventor
Hideji Yoshida
秀司 吉田
Shinobu Uchihata
忍 内畠
Shoji Shibuta
祥司 渋田
Tatsuo Isohata
達夫 五十畑
Masaoki Yoshihara
正興 吉原
Shusuke Harada
修輔 原田
Norifumi Uchimura
典文 内村
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Osaka Cement Co Ltd
Original Assignee
Sumitomo Osaka Cement Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Osaka Cement Co Ltd filed Critical Sumitomo Osaka Cement Co Ltd
Priority to JP25242597A priority Critical patent/JPH1192199A/en
Publication of JPH1192199A publication Critical patent/JPH1192199A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To shorten curing time and to shorten the time required to produce a wood chip or wood wool cement board by adding a specified amt. of aluminum sulfate to cement having a specified fineness of powder and contg. specified amts. of SO3 , 3CaO.Al2 O3 and 3CaO.SiO2 . SOLUTION: Aluminum sulfate is added by 1.0-5.0 pts.wt. to 100 pts.wt. cement having 4,300-8,000 cm<2> /g fineness of powder and contg. 3.5-15 wt.% SO3 , 8-20 wt.% 3Ca0.Al2 03 and 40-70 wt.% 3CaO.SiO2 to obtain the objective cement compsn. The cement has a large surface area due to the high fineness, hydration reaction proceeds early because the cement is liable to contact with water and the strength of the cement is increased in an early stage. Since the aluminum sulfate is added, the pH of a liq. phase lowers, the alkali hydrolysis reaction of an org. retarder is inhibited and the retardation of hydration of the cement by the org. retarder is prevented.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、セメント組成物、
主として木片又は木毛セメント板用のセメント組成物に
関するものである。The present invention relates to a cement composition,
The present invention mainly relates to a cement composition for wood chips or wood wool cement boards.

【０００２】[0002]

【従来の技術】一般に、木片又は木毛セメント板は、削
片化した木材を、そのまま処理し、又は溶出除去、不溶
化固定、封じ込め等の木材中のセメント硬化阻害成分の
硬化阻害対策処理をした後、セメントを単独又は塩化カ
ルシウム、塩化鉄、塩化アルミニウム等の硬化促進剤と
併用し、注水・混練後、成形して、所定の強度が得られ
るまで室温下で又は加温して養生して製造される。2. Description of the Related Art In general, wood chips or wool cement boards are prepared by directly treating the wood that has been cut into pieces, or by taking measures such as elution removal, insolubilization, fixation, and containment to prevent the hardening of cement hardening components in the wood. After that, cement alone or in combination with a hardening accelerator such as calcium chloride, iron chloride, aluminum chloride, etc., after water injection and kneading, molding, curing at room temperature or heating until a predetermined strength is obtained. Manufactured.

【０００３】[0003]

【発明が解決しようとする課題】しかし、従来の木片又
は木毛セメント板用セメント組成物は、木材中の硬化阻
害成分によって硬化阻害を受けやすく、この対策とし
て、溶出除去、不溶化固定、封じ込め等の木材の硬化阻
害対策処理、硬化促進剤の併用、加温養生を行なって
も、所定の強度を得るためには、長い養生時間を必要と
していた。However, conventional cement compositions for wood chips or wood wool cement boards are susceptible to hardening inhibition by hardening inhibitory components in wood, and as a countermeasure against this, elution removal, insolubilization fixing, containment, etc. Even if the hardening inhibition treatment of wood, the combined use of a hardening accelerator, and the heating and curing were performed, a long curing time was required to obtain a predetermined strength.

【０００４】本発明は、このような問題点を解決するた
めになされたもので、養生時間を短縮し、ひいては木片
又は木毛セメント板の製造時間を短縮することを課題と
する。The present invention has been made to solve such problems, and has as its object to reduce the curing time and, consequently, the manufacturing time of wood chips or wood wool cement boards.

【０００５】[0005]

【課題を解決するための手段】すなわち、本発明が上記
課題を解決するための手段は、粉末度4300〜8000cm2/g
で、ＳＯ3 量が 3.5〜15重量％、３ＣａＯ・Ａｌ2 Ｏ3
が 8〜20重量％及び３ＣａＯ・ＳｉＯ2 が40〜70重量％
含有されたセメント（以下「特定セメント」という。）
100重量部に、硫酸アルミニウムが 1.0〜 5.0重量部添
加されてなるセメント組成物を、木片又は木毛セメント
板の材料として用いる。That is, the means for solving the above-mentioned problems according to the present invention is a fineness of 4300 to 8000 cm 2 / g.
And the amount of SO 3 is 3.5 to 15% by weight, 3CaO.Al 2 O 3
Is 8 to 20% by weight and 3CaO.SiO 2 is 40 to 70% by weight
Cement contained (hereinafter referred to as “specified cement”)
A cement composition obtained by adding 1.0 to 5.0 parts by weight of aluminum sulfate to 100 parts by weight is used as a material for wood chips or wood wool cement boards.

【０００６】ここで、ＳＯ3 量とは、セメント組成物中
のＳＯ3 の量であり、主として石膏を配合することによ
って含有されることとなるものである。[0006] Here, the SO 3 content is the amount of SO 3 in the cement composition, is intended to be included by mainly blending gypsum.

【０００７】上記特定セメントの粉末度の範囲を 4300
〜8000cm2/g とするのは、4300cm2/g 未満では、所望の
強度が得られず、また、8000cm2/g を越えると、製造が
困難となる一方で、強度の増加が見られなくなるからで
ある。[0007] The fineness range of the specific cement is 4300
To the ~8000cm 2 / g, in less than 4300cm 2 / g, the desired strength can not be obtained, and if it exceeds 8000 cm 2 / g, while the manufacturing is difficult, not an increase in strength is observed Because.

【０００８】また、ＳＯ3 等の配合割合を上記範囲に設
定するのは、以下の理由による。すなわち、ＳＯ3 およ
び３ＣａＯ・Ａｌ2 Ｏ3 （以下Ｃ3 Ａと略す）は、セメ
ントの初期強度を増加させるエトリンガイト生成に寄与
するが、エトリンガイト生成反応において、いずれかが
過剰に存在すると、セメントの強度が落ちる。The reason for setting the mixing ratio of SO 3 and the like within the above range is as follows. That is, SO 3 and 3CaO.Al 2 O 3 (hereinafter abbreviated as C 3 A) contribute to ettringite formation which increases the initial strength of the cement. Strength drops.

【０００９】一方、ＳＯ3 量が 3.5重量％未満ではエト
リンガイトの生成量が少なくなるためセメントの強度が
落ちる。そこで、ＳＯ3 とＣ3 Ａとを過不足なく反応さ
せるとともに、できるだけ多量のエトリンガイトを生成
させるため、ＳＯ3 は 3.5〜15重量％、Ｃ3 Ａは 8〜20
重量％含有させる。つまり、ＳＯ3 量とＣ3 Ａ量のバラ
ンスを前記の通りにすることにより、適切量のエトリン
ガイトが生成されて、目標とするセメント強度が得られ
る。On the other hand, if the amount of SO 3 is less than 3.5% by weight, the strength of cement is reduced because the amount of ettringite produced is small. Therefore, together with reacted in just proportion with SO 3 and C 3 A, in order to as far as possible produce large quantities of ettringite, SO 3 is 3.5 to 15 wt%, the C 3 A 8 to 20
% By weight. That is, by setting the balance between the SO 3 amount and the C 3 A amount as described above, an appropriate amount of ettringite is generated, and a target cement strength can be obtained.

【００１０】また、３ＣａＯ・ＳｉＯ2 （以下Ｃ3 Ｓと
略す）は、木片又は木毛セメント板の製造工程におい
て、セメントの硬化を阻害して強度を下げる木材中の水
溶性有機物の生成を抑えることにより、セメントの強度
を上げる働きを有する。ところが、Ｃ3 Ｓ量が70重量％
を越えると、水酸化カルシウムの生成量が多くなること
により、水溶性有機物が多くなり、強度が低下するもの
と推定される。一方、Ｃ3 Ｓ量が40重量％未満では、そ
もそも所定の強度が得られない。そこで、Ｃ3 Ｓは40〜
70重量％含有させることとする。[0010] Further, 3CaO.SiO 2 (hereinafter abbreviated as C 3 S) suppresses the formation of water-soluble organic substances in wood which lowers the strength by inhibiting the hardening of cement in the process of producing wood chips or wood wool cement boards. This has the effect of increasing the strength of the cement. However, the C 3 S content was 70% by weight.
It is presumed that, when the amount exceeds the above range, the amount of generated calcium hydroxide increases, so that the amount of water-soluble organic substances increases and the strength decreases. On the other hand, if the amount of C 3 S is less than 40% by weight, a predetermined strength cannot be obtained in the first place. Therefore, C 3 S is 40 ~
70% by weight.

【００１１】更に、本発明のセメント組成物は、上記特
定セメント 100重量部に対して 1.0〜5.0 重量部の硫酸
アルミニウム（以下ＡＳ'3と略す）が添加されてなる。
より好ましくはＡＳ'3は 2.0〜4.0 重量部添加される。
ＡＳ'3の添加量を上記範囲とするのは、 1.0重量部未満
では、所望の強度発現性及び養生時間が得られず、ま
た、 5.0重量部を越えると、硬化が早すぎるため作業性
が悪くなるからである。つまり、ＡＳ'3の添加量が 1.0
重量部未満又は 5.0重量部を越える場合には、1.0〜5.0
重量部添加する場合に比べ、同じ養生時間をかけて
も、得られた木毛セメント板の強度が低くなる。Furthermore, the cement composition of the present invention, (hereinafter referred to as AS '3) of aluminum sulfate of 1.0 to 5.0 parts by weight with respect to the specific cement 100 parts by weight is added.
More preferably AS '3 are added 2.0 to 4.0 parts by weight.
To the amount of AS '3 and above-described range, it is less than 1.0 part by weight, not to obtain desired strength development and curing time, and if it exceeds 5.0 parts by weight, workability for curing is too fast Because it gets worse. In other words, the addition amount of the AS '3 1.0
1.0 to 5.0 if less than 5.0 parts by weight
Compared with the case of adding parts by weight, even if the same curing time is applied, the strength of the obtained wool cement board becomes lower.

【００１２】[0012]

【作用】上述のように、本発明に係るセメント組成物
は、 (1)粉末度が高く、 (2)ＳＯ 3 量が多く、 (3)Ｃ3
Ａ量が多い上記特定セメント 100重量部に、 (4)ＡＳ'3
を1.0〜5.0 重量部添加してなることを特徴とするた
め、以下のような作用を奏する。As described above, the cement composition according to the present invention
(1) high fineness, (2) SO ThreeLarge amount, (3) CThree
(4) AS 'Three
Characterized by adding 1.0 to 5.0 parts by weight of
Therefore, the following operation is achieved.

【００１３】すなわち、 (1)粉末度が高いため、セメン
トの表面積が大きく、セメントと水が接触しやすいた
め、水和反応が早く進み、セメントの強度が早期に高く
なる。 (2)液相中の硫酸イオンは、エトリンガイトの生成を促
進し、セメントの初期強度を増加させるものであるとこ
ろ、多量のＳＯ3 が含有されるうえ、ＡＳ'3が添加され
るため、硫酸イオンの量が一層増加する。 (3)Ｃ3 Ａは、セメントの水和初期にカルシウムアルミ
ネート水和物を多量に生成する働きを有し、このカルシ
ウムアルミネート水和物が、有機遅延物質を吸着固定す
ることにより、有機遅延物質によるセメントの水和阻害
が防止されるところ、多量のＣ3 Ａが含有されるうえ、
ＡＳ'3が添加されるため、カルシウムアルミネート水和
物の生成量が一層増加する。 (4)ＡＳ'3が添加されることにより、液相のｐＨが低下
し（酸性側にシフトし）、有機遅延物質のアルカリ加水
分解反応が抑制され、これによって生成する遅延作用の
大きな有機遅延物質によるセメントの水和遅延が防止さ
れる。[0013] (1) Since the fineness is high, the surface area of the cement is large, and the cement and water are easily brought into contact with each other. Therefore, the hydration reaction proceeds quickly, and the strength of the cement is quickly increased. (2) sulfate ions in the liquid phase promotes the formation of ettringite, where those that increase the early strength of the cement, after a large amount of SO 3 is contained, since the AS '3 is added, sulfate The amount of ions is further increased. (3) C 3 A has a function of generating a large amount of calcium aluminate hydrate in the early stage of cement hydration, and this calcium aluminate hydrate adsorbs and fixes an organic retardant, thereby forming an organic substance. Where the inhibition of hydration of cement by retarding substances is prevented, a large amount of C 3 A is contained, and
Since AS '3 is added, the amount of calcium aluminate hydrate is increased further. (4) The addition of AS ′ 3 lowers the pH of the liquid phase (shifts to the acidic side), and suppresses the alkaline hydrolysis reaction of the organic retardant, thereby producing a large organic retardant having a retarding action. The substance is prevented from delaying the hydration of the cement.

【００１４】[0014]

【実施例】以下、本発明の実施例について説明する。Embodiments of the present invention will be described below.

【００１５】実施例１−１ 本実施例では、後述する粉末度で、 4.0重量％のＳ
Ｏ3 、10重量％のＣ3 Ａ、45重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 2.0重量部添加したセ
メントを用いた。粉末度は、4300、5000、6000、7000、
8000cm2/g の５種類のものを用いた。ＳＯ3 、Ｃ3 Ａ、
Ｃ3 Ｓ以外の他の成分としては、主として２ＣａＯ・Ｓ
ｉＯ 2 （以下Ｃ2 Ｓと略す）、４ＣａＯ・Ａｌ2 Ｏ3 ・
Ｆｅ2 Ｏ3 （以下Ｃ4 ＡＦと略す）等が含まれている。[0015]Example 1-1 In the present embodiment, 4.0% by weight of S
OThree, 10% by weight CThreeA, 45% by weight CThreeS is included
AS 'in 100 parts by weight of cementThree2.0 parts by weight of
Was used. Fineness is 4300, 5000, 6000, 7000,
8000cmTwo/ g was used. SOThree, CThreeA,
CThreeOther components other than S mainly include 2CaO · S
iO Two(Hereinafter CTwoAbbreviated as S), 4CaO.AlTwoOThree・
FeTwoOThree(Hereinafter CFourAF).

【００１６】上記セメントに所定量の木毛を混合し、加
水・混合後、成形することにより、木毛セメント板を得
た。A predetermined amount of wood wool was mixed with the above cement, mixed with water, and then molded to obtain a wood wool cement board.

【００１７】比較例１−１−１ 比較例１−１−１として、粉末度3800cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例１−１と同様で
あるため、その説明は省略する。 Comparative Example 1-1-1 As Comparative Example 1-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 using cement having a fineness of 3800 cm 2 / g. The other components are the same as those in Example 1-1, and the description thereof is omitted.

【００１８】比較例１−１−２ 比較例１−１−２として、粉末度9000cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例１−１と同様で
あるため、その説明は省略する。ＳＯ3 、Ｃ3 Ａ、Ｃ3
Ｓ以外の他の成分としては、主としてＣ2 Ｓ、Ｃ4 ＡＦ
等が含まれている。 Comparative Example 1-1-2 As Comparative Example 1-1-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using cement having a fineness of 9000 cm 2 / g. The other components are the same as those in Example 1-1, and the description thereof is omitted. SO 3 , C 3 A, C 3
Components other than S mainly include C 2 S and C 4 AF
Etc. are included.

【００１９】実施例１−２ 本実施例では、後述する粉末度で、14.0重量％のＳ
Ｏ3 、15重量％のＣ3 Ａ、55重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 2.0重量部添加したセ
メントを用いて、上記実施例１−１と同様の方法で木毛
セメント板を得た。粉末度は、4300、5000、6000、700
0、8000cm2/g の５種類のものを用いた。 Example 1-2 In this example, 14.0% by weight of S
O 3, 15 wt% of C 3 A, 55 wt% of C 3 100 parts by weight of cement S include, using cement with AS '3 was added 2.0 part by weight, the same manner as in Example 1-1 Wood wool cement board was obtained by the method. Fineness is 4300, 5000, 6000, 700
Five types of 0, 8000 cm 2 / g were used.

【００２０】比較例１−２−１ 比較例１−２−１として、粉末度3800cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例１−２と同様で
あるため、その説明は省略する。 Comparative Example 1-2-1 As Comparative Example 1-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using cement having a fineness of 3800 cm 2 / g. The other components are the same as those in Example 1-2, and the description thereof is omitted.

【００２１】比較例１−２−２ 比較例１−２−２として、粉末度9000cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例１−２と同様で
あるため、その説明は省略する。 Comparative Example 1-2-2 As Comparative Example 1-2-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using cement having a fineness of 9000 cm 2 / g. The other components are the same as those in Example 1-2, and the description thereof is omitted.

【００２２】実施例２−１ 本実施例では、粉末度が 5000cm2/gで、後述する量のＳ
Ｏ3 、10重量％のＣ3Ａ、45重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 2.0重量部添加したセ
メントを用いて、上記実施例１−１と同様の方法で木毛
セメント板を得た。ＳＯ3 の含有量は、3.5 、4.0 、8.
0 、14.0、15.0重量％の５種類のものを用いた。Ｓ
Ｏ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主とし
てＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 2-1 In this example, the fineness was 5000 cm 2 / g and the amount of S
O 3, 10 wt% of C 3 A, 45 wt% of C 3 100 parts by weight of cement S include, using cement with AS '3 was added 2.0 part by weight, the same manner as in Example 1-1 Wood wool cement board was obtained by the method. The content of SO 3 is 3.5, 4.0, 8.
Five types of 0, 14.0 and 15.0% by weight were used. S
Components other than O 3 , C 3 A and C 3 S mainly include C 2 S and C 4 AF.

【００２３】比較例２−１−１ 比較例２−１−１として、ＳＯ3 を3.0 重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
２−１と同様であるため、その説明は省略する。 Comparative Example 2-1-1 As Comparative Example 2-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 3.0% by weight of SO 3 . Since the fineness and other components are the same as those in Example 2-1 above, description thereof will be omitted.

【００２４】比較例２−１−２ 比較例２−１−１として、ＳＯ3 を16.0重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
２−１と同様であるため、その説明は省略する。 Comparative Example 2-1-2 As Comparative Example 2-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 16.0% by weight of SO 3 . Since the fineness and other components are the same as those in Example 2-1 above, description thereof will be omitted.

【００２５】実施例２−２ 本実施例では、粉末度が 7000cm2/gで、後述する量のＳ
Ｏ3 、13重量％のＣ3Ａ、54重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 2.0重量部添加したセ
メントを用いて、上記実施例１−１と同様の方法で木毛
セメント板を得た。ＳＯ3 の含有量は、3.5 、4.0 、8.
0 、14.0、15.0重量％の５種類のものを用いた。Ｓ
Ｏ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主とし
てＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 2-2 In this example, the fineness was 7000 cm 2 / g and the amount of S
O 3, 13 to 100 parts by weight of cement that contains by weight percent of C 3 A, 54 wt% of C 3 S, using cement with AS '3 was added 2.0 part by weight, the same manner as in Example 1-1 Wood wool cement board was obtained by the method. The content of SO 3 is 3.5, 4.0, 8.
Five types of 0, 14.0 and 15.0% by weight were used. S
Components other than O 3 , C 3 A and C 3 S mainly include C 2 S and C 4 AF.

【００２６】比較例２−２−１ 比較例２−２−１として、ＳＯ3 を3.0 重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
２−２と同様であるため、その説明は省略する。 Comparative Example 2-2-1 As Comparative Example 2-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 3.0% by weight of SO 3 . Since the fineness and other components are the same as those in Example 2-2, description thereof is omitted.

【００２７】比較例２−２−２ 比較例２−２−１として、ＳＯ3 を16.0重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
２−２と同様であるため、その説明は省略する。 Comparative Example 2-2-2 As Comparative Example 2-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 16.0% by weight of SO 3 . Since the fineness and other components are the same as those in Example 2-2, description thereof is omitted.

【００２８】実施例３−１ 本実施例では、粉末度が 5000cm2/gで、 4.0重量％のＳ
Ｏ3 、後述する量のＣ 3 Ａ、45重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 2.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ａの含有量は、８、10、15、
18、20重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0028]Example 3-1 In this embodiment, the fineness is 5000 cm.Two/ g, 4.0% by weight of S
OThree, The amount of C described below ThreeA, 45% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree2.0 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. CThreeThe content of A is 8, 10, 15,
Five kinds of 18, 20% by weight were used. SOThree, C
ThreeA, CThreeOther components other than S mainly include C
TwoS, CFourAF and the like are included.

【００２９】比較例３−１−１ 比較例３−１−１として、Ｃ3 Ａを６重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例３
−１と同様であるため、その説明は省略する。 Comparative Example 3-1-1 As Comparative Example 3-1-1, a cement containing 6% by weight of C 3 A was used, and a wood wool cement board was obtained in the same manner as in Example 1-1. . The fineness and other compounding ingredients are as described in Example 3 above.
Since it is the same as -1, the description is omitted.

【００３０】比較例３−１−２ 比較例３−１−２として、Ｃ3 Ａを22重量％含むセメン
トを用いて、上記実施例１と同様の方法で木毛セメント
板を得た。粉末度及び他の配合成分は上記実施例２と同
様であるため、その説明は省略する。 Comparative Example 3-1-2 As Comparative Example 3-1-2, a wood wool cement board was obtained in the same manner as in Example 1 above, using a cement containing 22% by weight of C 3 A. Since the fineness and other components are the same as those in Example 2, the description is omitted.

【００３１】実施例３−２ 本実施例では、粉末度が 7000cm2/gで、10.0重量％のＳ
Ｏ3 、後述する量のＣ 3 Ａ、55重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 2.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ａの含有量は、８、10、15、
18、20重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0031]Example 3-2 In this example, the fineness is 7000 cmTwo/ g, 10.0% by weight of S
OThree, The amount of C described below ThreeA, 55% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree2.0 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. CThreeThe content of A is 8, 10, 15,
Five kinds of 18, 20% by weight were used. SOThree, C
ThreeA, CThreeOther components other than S mainly include C
TwoS, CFourAF and the like are included.

【００３２】比較例３−２−１ 比較例３−２−１として、Ｃ3 Ａを６重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例３
−２と同様であるため、その説明は省略する。 Comparative Example 3-2-1 As a comparative example 3-2-1, a cement containing 6% by weight of C 3 A was used to obtain a wood wool cement board in the same manner as in Example 1-1. . The fineness and other compounding ingredients are as described in Example 3 above.
Since this is the same as -2, its description is omitted.

【００３３】比較例３−２−２ 比較例３−２−２として、Ｃ3 Ａを22重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例３
−２と同様であるため、その説明は省略する。 Comparative Example 3-2-2 As Comparative Example 3-2-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 22% by weight of C 3 A. . The fineness and other compounding ingredients are as described in Example 3 above.
Since this is the same as -2, its description is omitted.

【００３４】実施例４−１ 本実施例では、粉末度が 5000cm2/gで、 4.0重量％のＳ
Ｏ3 、10重量％のＣ3Ａ、後述する量のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 2.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ｓの含有量は、40、45、55、
65、70重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 4-1 In this example, a fineness of 5000 cm 2 / g and 4.0% by weight of S
O 3, 10 wt% of C 3 A, in 100 parts by weight of cement that contains the C 3 S in an amount which will be described later, by using a cement with AS '3 was added 2.0 part by weight, the same manner as in Example 1-1 Wood wool cement board was obtained by the method. The content of C 3 S is 40, 45, 55,
Five types of 65 and 70% by weight were used. SO 3 , C
Components other than 3 A and C 3 S include mainly C
2 S, C 4 AF, etc. are included.

【００３５】比較例４−１−１ 比較例４−１−１として、Ｃ3 Ｓを30重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例４
−１と同様であるため、その説明は省略する。 Comparative Example 4-1-1 As Comparative Example 4-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 30% by weight of C 3 S. . The fineness and other compounding ingredients were determined in Example 4 above.
Since it is the same as -1, the description is omitted.

【００３６】比較例４−１−２ 比較例４−１−２として、Ｃ3 Ａを75重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例４
−１と同様であるため、その説明は省略する。 Comparative Example 4-1-2 As Comparative Example 4-1-2, a cement containing 75% by weight of C 3 A was used, and a wood wool cement board was obtained in the same manner as in Example 1-1. . The fineness and other compounding ingredients were determined in Example 4 above.
Since it is the same as -1, the description is omitted.

【００３７】実施例４−２ 本実施例では、粉末度が 7000cm2/gで、 6.0重量％のＳ
Ｏ3 、12重量％のＣ3Ａ、後述する量のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 2.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ｓの含有量は、40、45、55、
65、70重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 4-2 In this example, the fineness was 7000 cm 2 / g and 6.0% by weight of S
The same method as in Example 1-1 above, except that 2.0 parts by weight of AS ′ 3 was added to 100 parts by weight of cement containing O 3 , 12% by weight of C 3 A, and the amount of C 3 S described below. Wood wool cement board was obtained by the method. The content of C 3 S is 40, 45, 55,
Five types of 65 and 70% by weight were used. SO 3 , C
Components other than 3 A and C 3 S include mainly C
2 S, C 4 AF, etc. are included.

【００３８】比較例４−２−１ 比較例４−２−１として、Ｃ3 Ｓを30重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例４
−２と同様であるため、その説明は省略する。 Comparative Example 4-2-1 As Comparative Example 4-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 30% by weight of C 3 S. . The fineness and other compounding ingredients were determined in Example 4 above.
Since this is the same as -2, its description is omitted.

【００３９】比較例４−２−２ 比較例４−２−２として、Ｃ3 Ａを75重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例４
−２と同様であるため、その説明は省略する。 Comparative Example 4-2-2 As a comparative example 4-2-2, a cement containing 75% by weight of C 3 A was used to obtain a wood wool cement board in the same manner as in Example 1-1. . The fineness and other compounding ingredients were determined in Example 4 above.
Since this is the same as -2, its description is omitted.

【００４０】実施例５−１ 本実施例では、後述する粉末度で、 4.0重量％のＳ
Ｏ3 、10重量％のＣ3 Ａ、45重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 4.0重量部添加したセ
メントを用いて、上記実施例１−１と同様の方法で木毛
セメント板を得た。粉末度は、4300、5000、6000、700
0、8000cm2/g の５種類のものを用いた。ＳＯ3 、Ｃ3
Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ2 Ｓ、
Ｃ4 ＡＦ等が含まれている。 Example 5-1 In this example, 4.0% by weight of S
O 3, 10 wt% of C 3 A, 45 wt% of C 3 100 parts by weight of cement S include, using the added cement AS '3 4.0 parts by weight, of the same manner as in Example 1-1 Wood wool cement board was obtained by the method. Fineness is 4300, 5000, 6000, 700
Five types of 0, 8000 cm 2 / g were used. SO 3 , C 3
Components other than A and C 3 S include mainly C 2 S,
C 4 AF and the like are included.

【００４１】比較例５−１−１ 比較例５−１−１として、粉末度3800cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例５−１と同様で
あるため、その説明は省略する。 Comparative Example 5-1-1 As Comparative Example 5-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using cement having a fineness of 3800 cm 2 / g. The other components are the same as in Example 5-1 above, and a description thereof will not be repeated.

【００４２】比較例５−１−２ 比較例５−１−２として、粉末度9000cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例５−１と同様で
あるため、その説明は省略する。 Comparative Example 5-1-2 As Comparative Example 5-1-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using cement having a fineness of 9000 cm 2 / g. The other components are the same as in Example 5-1 above, and a description thereof will not be repeated.

【００４３】実施例５−２ 本実施例では、後述する粉末度で、14.0重量％のＳ
Ｏ3 、15重量％のＣ3 Ａ、55重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 4.0重量部添加したセ
メントを用いて、上記実施例１−１と同様の方法で木毛
セメント板を得た。粉末度は、4300、5000、6000、700
0、8000cm2/g の５種類のものを用いた。ＳＯ3 、Ｃ3
Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ2 Ｓ、
Ｃ4 ＡＦ等が含まれている。 Example 5-2 In this example, 14.0% by weight of S
The same method as in Example 1-1 above, except that 4.0 parts by weight of AS ′ 3 was added to 100 parts by weight of cement containing O 3 , 15% by weight of C 3 A, and 55% by weight of C 3 S. Wood wool cement board was obtained by the method. Fineness is 4300, 5000, 6000, 700
Five types of 0, 8000 cm 2 / g were used. SO 3 , C 3
Components other than A and C 3 S include mainly C 2 S,
C 4 AF and the like are included.

【００４４】比較例５−２−１ 比較例５−２−１として、粉末度3800cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例５−２と同様で
あるため、その説明は省略する。 Comparative Example 5-2-1 As Comparative Example 5-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using cement having a fineness of 3800 cm 2 / g. The other components are the same as those in Example 5-2, and the description thereof is omitted.

【００４５】比較例５−２−２ 比較例５−２−２として、粉末度9000cm2/g のセメント
を用いて、上記実施例１−１と同様の方法で木毛セメン
ト板を得た。他の配合成分は上記実施例５−２と同様で
あるため、その説明は省略する。 Comparative Example 5-2-2 As Comparative Example 5-2-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using cement having a fineness of 9000 cm 2 / g. The other components are the same as those in Example 5-2, and the description thereof is omitted.

【００４６】実施例６−１ 本実施例では、粉末度が 5000cm2/gで、後述する量のＳ
Ｏ3 、10重量％のＣ3Ａ、45重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 4.0重量部添加したセ
メントを用いて、上記実施例１−１と同様の方法で木毛
セメント板を得た。ＳＯ3 の含有量は、3.5 、4.0 、8.
0 、14.0、15.0重量％の５種類のものを用いた。Ｓ
Ｏ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主とし
てＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 6-1 In this example, the fineness was 5000 cm 2 / g, and the amount of S
O 3, 10 wt% of C 3 A, 45 wt% of C 3 100 parts by weight of cement S include, using the added cement AS '3 4.0 parts by weight, of the same manner as in Example 1-1 Wood wool cement board was obtained by the method. The content of SO 3 is 3.5, 4.0, 8.
Five types of 0, 14.0 and 15.0% by weight were used. S
Components other than O 3 , C 3 A and C 3 S mainly include C 2 S and C 4 AF.

【００４７】比較例６−１−１ 比較例６−１−１として、ＳＯ3 を3.0 重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
６−１と同様であるため、その説明は省略する。 Comparative Example 6-1-1 As a comparative example 6-1-1, a wood wool cement board was obtained in the same manner as in the above Example 1-1, using a cement containing 3.0% by weight of SO 3 . The fineness and other components are the same as those in Example 6-1 and will not be described.

【００４８】比較例６−１−２ 比較例６−１−１として、ＳＯ3 を16.0重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
６−１と同様であるため、その説明は省略する。 Comparative Example 6-1-2 As Comparative Example 6-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 16.0% by weight of SO 3 . The fineness and other components are the same as those in Example 6-1 and will not be described.

【００４９】実施例６−２ 本実施例では、粉末度が 7000cm2/gで、後述する量のＳ
Ｏ3 、13重量％のＣ3Ａ、54重量％のＣ3 Ｓが含まれる
セメント 100重量部に、ＡＳ'3を 4.0重量部添加したセ
メントを用いて、上記実施例１−１と同様の方法で木毛
セメント板を得た。ＳＯ3 の含有量は、3.5 、4.0 、8.
0 、14.0、15.0重量％の５種類のものを用いた。Ｓ
Ｏ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主とし
てＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 6-2 In this example, the fineness was 7000 cm 2 / g and the amount of S
The same method as in Example 1-1 above, except that 4.0 parts by weight of AS ′ 3 was added to 100 parts by weight of cement containing O 3 , 13% by weight of C 3 A, and 54% by weight of C 3 S. Wood wool cement board was obtained by the method. The content of SO 3 is 3.5, 4.0, 8.
Five types of 0, 14.0 and 15.0% by weight were used. S
Components other than O 3 , C 3 A and C 3 S mainly include C 2 S and C 4 AF.

【００５０】比較例６−２−１ 比較例６−２−１として、ＳＯ3 を3.0 重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
６−２と同様であるため、その説明は省略する。 Comparative Example 6-2-1 As Comparative Example 6-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 3.0% by weight of SO 3 . Since the fineness and other components are the same as those in Example 6-2, description thereof will be omitted.

【００５１】比較例６−２−２ 比較例６−２−２として、ＳＯ3 を16.0重量％含むセメ
ントを用いて、上記実施例１−１と同様の方法で木毛セ
メント板を得た。粉末度及び他の配合成分は上記実施例
６−２と同様であるため、その説明は省略する。 Comparative Example 6-2-2 As Comparative Example 6-2-2, a wood wool cement board was obtained in the same manner as in Example 1-1, using a cement containing 16.0% by weight of SO 3 . Since the fineness and other components are the same as those in Example 6-2, description thereof will be omitted.

【００５２】実施例７−１ 本実施例では、粉末度が 5000cm2/gで、 4.0重量％のＳ
Ｏ3 、後述する量のＣ 3 Ａ、45重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 4.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ａの含有量は、８、10、15、
18、20重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0052]Example 7-1 In this embodiment, the fineness is 5000 cm.Two/ g, 4.0% by weight of S
OThree, The amount of C described below ThreeA, 45% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree4.0 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. CThreeThe content of A is 8, 10, 15,
Five kinds of 18, 20% by weight were used. SOThree, C
ThreeA, CThreeOther components other than S mainly include C
TwoS, CFourAF and the like are included.

【００５３】比較例７−１−１ 比較例７−１−１として、Ｃ3 Ａを６重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例７
−１と同様であるため、その説明は省略する。 Comparative Example 7-1-1 As Comparative Example 7-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 6% by weight of C 3 A. . The fineness and other compounding ingredients were determined in Example 7 above.
Since it is the same as -1, the description is omitted.

【００５４】比較例７−１−２ 比較例７−１−２として、Ｃ3 Ａを22重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例７
−１と同様であるため、その説明は省略する。 Comparative Example 7-1-2 As Comparative Example 7-1-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 22% by weight of C 3 A. . The fineness and other compounding ingredients were determined in Example 7 above.
Since it is the same as -1, the description is omitted.

【００５５】実施例７−２ 本実施例では、粉末度が 7000cm2/gで、10.0重量％のＳ
Ｏ3 、後述する量のＣ 3 Ａ、55重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 4.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ａの含有量は、８、10、15、
18、20重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0055]Example 7-2 In this example, the fineness is 7000 cmTwo/ g, 10.0% by weight of S
OThree, The amount of C described below ThreeA, 55% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree4.0 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. CThreeThe content of A is 8, 10, 15,
Five kinds of 18, 20% by weight were used. SOThree, C
ThreeA, CThreeOther components other than S mainly include C
TwoS, CFourAF and the like are included.

【００５６】比較例７−２−１ 比較例７−２−１として、Ｃ3 Ａを６重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例７
−２と同様であるため、その説明は省略する。 Comparative Example 7-2-1 As Comparative Example 7-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 6% by weight of C 3 A. . The fineness and other compounding ingredients were determined in Example 7 above.
Since this is the same as -2, its description is omitted.

【００５７】比較例７−２−２ 比較例７−２−２として、Ｃ3 Ａを22重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例７
−２と同様であるため、その説明は省略する。 Comparative Example 7-2-2 As Comparative Example 7-2-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 22% by weight of C 3 A. . The fineness and other compounding ingredients were determined in Example 7 above.
Since this is the same as -2, its description is omitted.

【００５８】実施例８−１ 本実施例では、粉末度が 5000cm2/gで、 4.0重量％のＳ
Ｏ3 、10重量％のＣ3Ａ、後述する量のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 4.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ｓの含有量は、40、45、55、
65、70重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 8-1 In this example, the fineness was 5000 cm 2 / g, and 4.0% by weight of S
O 3, 10 wt% of C 3 A, in 100 parts by weight of cement that contains the C 3 S in an amount which will be described later, by using a cement with AS '3 4.0 parts by weight was added, the same manner as in Example 1-1 Wood wool cement board was obtained by the method. The content of C 3 S is 40, 45, 55,
Five types of 65 and 70% by weight were used. SO 3 , C
Components other than 3 A and C 3 S include mainly C
2 S, C 4 AF, etc. are included.

【００５９】比較例８−１−１ 比較例８−１−１として、Ｃ3 Ｓを30重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例８
−１と同様であるため、その説明は省略する。 Comparative Example 8-1-1 As Comparative Example 8-1-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 30% by weight of C 3 S. . The fineness and other compounding ingredients were determined in Example 8 above.
Since it is the same as -1, the description is omitted.

【００６０】比較例８−１−２ 比較例８−１−２として、Ｃ3 Ａを75重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例８
−１と同様であるため、その説明は省略する。 Comparative Example 8-1-2 As Comparative Example 8-1-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 75% by weight of C 3 A. . The fineness and other compounding ingredients were determined in Example 8 above.
Since it is the same as -1, the description is omitted.

【００６１】実施例８−２ 本実施例では、粉末度が 7000cm2/gで、 6.0重量％のＳ
Ｏ3 、12重量％のＣ3Ａ、後述する量のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 4.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。Ｃ3 Ｓの含有量は、40、45、55、
65、70重量％の５種類のものを用いた。ＳＯ3 、Ｃ
3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主としてＣ
2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Example 8-2 In this example, the fineness was 7000 cm 2 / g, and 6.0% by weight of sulfur was used.
The same procedure as in Example 1-1 was performed by using a cement obtained by adding 4.0 parts by weight of AS ′ 3 to 100 parts by weight of a cement containing O 3 , 12% by weight of C 3 A, and the amount of C 3 S described below. Wood wool cement board was obtained by the method. The content of C 3 S is 40, 45, 55,
Five types of 65 and 70% by weight were used. SO 3 , C
Components other than 3 A and C 3 S include mainly C
2 S, C 4 AF, etc. are included.

【００６２】比較例８−２−１ 比較例８−２−１として、Ｃ3 Ｓを30重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例８
−２と同様であるため、その説明は省略する。 Comparative Example 8-2-1 As Comparative Example 8-2-1, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 30% by weight of C 3 S. . The fineness and other compounding ingredients were determined in Example 8 above.
Since this is the same as -2, its description is omitted.

【００６３】比較例８−２−２ 比較例８−２−２として、Ｃ3 Ａを75重量％含むセメン
トを用いて、上記実施例１−１と同様の方法で木毛セメ
ント板を得た。粉末度及び他の配合成分は上記実施例８
−２と同様であるため、その説明は省略する。 Comparative Example 8-2-2 As Comparative Example 8-2-2, a wood wool cement board was obtained in the same manner as in Example 1-1 above, using a cement containing 75% by weight of C 3 A. . The fineness and other compounding ingredients were determined in Example 8 above.
Since this is the same as -2, its description is omitted.

【００６４】比較例９−１ 比較例９−１として、後述する粉末度で、 4.0重量％の
ＳＯ3 、10重量％のＣ 3 Ａ、45重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 0.5重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。粉末度は、3800、4300、5000、60
00、7000、8000、9000cm2/g の７種類のものを用いた。
ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主と
してＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0064]Comparative Example 9-1 As Comparative Example 9-1, a fineness of 4.0 wt%
SOThree, 10% by weight C ThreeA, 45% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree0.5 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. Fineness is 3800, 4300, 5000, 60
00, 7000, 8000, 9000cmTwo/ g was used.
SOThree, CThreeA, CThreeOther components other than S include
Then CTwoS, CFourAF and the like are included.

【００６５】比較例９−２ 比較例９−２として、後述する粉末度で、14.0重量％の
ＳＯ3 、15重量％のＣ 3 Ａ、55重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 0.5重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。粉末度は、3800、4300、5000、60
00、7000、8000、9000cm2/g の７種類のものを用いた。
ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主と
してＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0065]Comparative Example 9-2 As Comparative Example 9-2, a fineness of 14.0 wt%
SOThree, 15% by weight C ThreeA, 55% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree0.5 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. Fineness is 3800, 4300, 5000, 60
00, 7000, 8000, 9000cmTwo/ g was used.
SOThree, CThreeA, CThreeOther components other than S include
Then CTwoS, CFourAF and the like are included.

【００６６】比較例10−１ 比較例10−１として、粉末度が 5000cm2/gで、後述する
量のＳＯ3 、10重量％のＣ3 Ａ、45重量％のＣ3 Ｓが含
まれるセメント 100重量部に、ＡＳ'3を 0.5重量部添加
したセメントを用いて、上記実施例１−１と同様の方法
で木毛セメント板を得た。ＳＯ3 の含有量は、3.0 、3.
5 、4.0 、8.0 、14.0、15.0、16.0重量％の７種類のも
のを用いた。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分と
しては、主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 10-1 As Comparative Example 10-1, a cement having a fineness of 5000 cm 2 / g and containing the following amounts of SO 3 , 10% by weight of C 3 A, and 45% by weight of C 3 S was used. to 100 parts by weight, using a cement aS '3 was added 0.5 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of SO 3 is 3.0, 3.
5, 4.0, 8.0, 14.0, 15.0 and 16.0% by weight of seven kinds were used. Components other than SO 3 , C 3 A, and C 3 S mainly include C 2 S, C 4 AF, and the like.

【００６７】比較例10−２ 比較例10−２として、粉末度が 7000cm2/gで、後述する
量のＳＯ3 、13重量％のＣ3 Ａ、54重量％のＣ3 Ｓが含
まれるセメント 100重量部に、ＡＳ'3を 0.5重量部添加
したセメントを用いて、上記実施例１−１と同様の方法
で木毛セメント板を得た。ＳＯ3 の含有量は、3.0 、3.
5 、4.0 、8.0 、14.0、15.0、16.0重量％の７種類のも
のを用いた。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分と
しては、主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 10-2 As Comparative Example 10-2, a cement having a fineness of 7000 cm 2 / g and containing SO 3 , 13% by weight of C 3 A, and 54% by weight of C 3 S described later. to 100 parts by weight, using a cement aS '3 was added 0.5 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of SO 3 is 3.0, 3.
5, 4.0, 8.0, 14.0, 15.0 and 16.0% by weight of seven kinds were used. Components other than SO 3 , C 3 A, and C 3 S mainly include C 2 S, C 4 AF, and the like.

【００６８】比較例11−１ 比較例11−１として、粉末度が 5000cm2/gで、 4.0重量
％のＳＯ3 、後述する量のＣ3 Ａ、45重量％のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 0.5重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ａの含有量は、６、
８、10、15、18、20、22重量％の７種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 11-1 As Comparative Example 11-1, a cement having a fineness of 5000 cm 2 / g and containing 4.0% by weight of SO 3 , C 3 A in an amount described below, and 45% by weight of C 3 S was used. to 100 parts by weight, using a cement aS '3 was added 0.5 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 A is 6,
Seven types of 8, 10, 15, 18, 20, and 22% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００６９】比較例11−２ 比較例11−２として、粉末度が 7000cm2/gで、10.0重量
％のＳＯ3 、後述する量のＣ3 Ａ、55重量％のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 0.5重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ａの含有量は、６、
８、10、15、18、20、22重量％の７種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 11-2 As Comparative Example 11-2, a cement having a fineness of 7000 cm 2 / g and containing 10.0% by weight of SO 3 , C 3 A in an amount described below, and 55% by weight of C 3 S was used. to 100 parts by weight, using a cement aS '3 was added 0.5 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 A is 6,
Seven types of 8, 10, 15, 18, 20, and 22% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００７０】比較例12−１ 比較例12−１として、粉末度が 5000cm2/gで、 4.0重量
％のＳＯ3 、10重量％のＣ3 Ａ、後述する量のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 0.5重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ｓの含有量は、30、4
0、45、55、65、70、75重量％の７種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 12-1 As Comparative Example 12-1, a cement having a fineness of 5000 cm 2 / g and containing 4.0% by weight of SO 3 , 10% by weight of C 3 A, and the amount of C 3 S described below. to 100 parts by weight, using a cement aS '3 was added 0.5 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 S is 30, 4
Seven types of 0, 45, 55, 65, 70 and 75% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００７１】比較例12−２ 比較例12−２として、粉末度が 7000cm2/gで、 6.0重量
％のＳＯ3 、12重量％のＣ3 Ａ、後述する量のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 0.5重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ｓの含有量は、30、4
0、45、55、65、70、75重量％の７種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 12-2 As Comparative Example 12-2, a cement having a fineness of 7000 cm 2 / g and containing 6.0% by weight of SO 3 , 12% by weight of C 3 A, and the amount of C 3 S described below. to 100 parts by weight, using a cement aS '3 was added 0.5 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 S is 30, 4
Seven types of 0, 45, 55, 65, 70 and 75% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００７２】比較例13−１ 比較例13−１として、後述する粉末度で、 4.0重量％の
ＳＯ3 、10重量％のＣ 3 Ａ、45重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 6.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。粉末度は、3800、4300、5000、60
00、7000、8000、9000cm2/g の７種類のものを用いた。
ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主と
してＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0072]Comparative Example 13-1 As Comparative Example 13-1, a fineness of 4.0 wt%
SOThree, 10% by weight C ThreeA, 45% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree6.0 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. Fineness is 3800, 4300, 5000, 60
00, 7000, 8000, 9000cmTwo/ g was used.
SOThree, CThreeA, CThreeOther components other than S include
Then CTwoS, CFourAF and the like are included.

【００７３】比較例13−２ 比較例13−２として、後述する粉末度で、14.0重量％の
ＳＯ3 、15重量％のＣ 3 Ａ、55重量％のＣ3 Ｓが含まれ
るセメント 100重量部に、ＡＳ'3を 6.0重量部添加した
セメントを用いて、上記実施例１−１と同様の方法で木
毛セメント板を得た。粉末度は、3800、4300、5000、60
00、7000、8000、9000cm2/g の７種類のものを用いた。
ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、主と
してＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。[0073]Comparative Example 13-2 As Comparative Example 13-2, with a fineness described later, 14.0% by weight
SOThree, 15% by weight C ThreeA, 55% by weight CThreeS is included
AS 'to 100 parts by weight of cementThree6.0 parts by weight
Using cement, wood was produced in the same manner as in Example 1-1.
A wool cement board was obtained. Fineness is 3800, 4300, 5000, 60
00, 7000, 8000, 9000cmTwo/ g was used.
SOThree, CThreeA, CThreeOther components other than S include
Then CTwoS, CFourAF and the like are included.

【００７４】比較例14−１ 比較例14−１として、粉末度が 5000cm2/gで、後述する
量のＳＯ3 、10重量％のＣ3 Ａ、45重量％のＣ3 Ｓが含
まれるセメント 100重量部に、ＡＳ'3を 6.0重量部添加
したセメントを用いて、上記実施例１−１と同様の方法
で木毛セメント板を得た。ＳＯ3 の含有量は、3.0 、3.
5 、4.0 、8.0 、14.0、15.0、16.0重量％の７種類のも
のを用いた。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分と
しては、主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 14-1 As Comparative Example 14-1, a cement having a fineness of 5000 cm 2 / g and containing the following amounts of SO 3 , 10% by weight of C 3 A, and 45% by weight of C 3 S was used. to 100 parts by weight, using a cement aS '3 was added 6.0 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of SO 3 is 3.0, 3.
5, 4.0, 8.0, 14.0, 15.0 and 16.0% by weight of seven kinds were used. Components other than SO 3 , C 3 A, and C 3 S mainly include C 2 S, C 4 AF, and the like.

【００７５】比較例14−２ 比較例14−２として、粉末度が 7000cm2/gで、後述する
量のＳＯ3 、13重量％のＣ3 Ａ、54重量％のＣ3 Ｓが含
まれるセメント 100重量部に、ＡＳ'3を 6.0重量部添加
したセメントを用いて、上記実施例１−１と同様の方法
で木毛セメント板を得た。ＳＯ3 の含有量は、3.0 、3.
5 、4.0 、8.0 、14.0、15.0、16.0重量％の７種類のも
のを用いた。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分と
しては、主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 14-2 As Comparative Example 14-2, a cement having a fineness of 7000 cm 2 / g and containing the following amounts of SO 3 , 13% by weight of C 3 A, and 54% by weight of C 3 S to 100 parts by weight, using a cement aS '3 was added 6.0 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of SO 3 is 3.0, 3.
5, 4.0, 8.0, 14.0, 15.0 and 16.0% by weight of seven kinds were used. Components other than SO 3 , C 3 A, and C 3 S mainly include C 2 S, C 4 AF, and the like.

【００７６】比較例15−１ 比較例15−１として、粉末度が 5000cm2/gで、 4.0重量
％のＳＯ3 、後述する量のＣ3 Ａ、45重量％のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 6.0重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ａの含有量は、６、
８、10、15、18、20、22重量％の７種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 15-1 As Comparative Example 15-1, a cement having a fineness of 5000 cm 2 / g and containing 4.0% by weight of SO 3 , the amount of C 3 A described later, and 45% by weight of C 3 S was used. to 100 parts by weight, using a cement aS '3 was added 6.0 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 A is 6,
Seven types of 8, 10, 15, 18, 20, and 22% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００７７】比較例15−２ 比較例15−２として、粉末度が 7000cm2/gで、10.0重量
％のＳＯ3 、後述する量のＣ3 Ａ、55重量％のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 6.0重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ａの含有量は、６、
８、10、15、18、20、22重量％の５種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 15-2 As Comparative Example 15-2, a cement having a fineness of 7000 cm 2 / g and containing 10.0% by weight of SO 3 , C 3 A in an amount described later, and 55% by weight of C 3 S to 100 parts by weight, using a cement aS '3 was added 6.0 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 A is 6,
Five kinds of 8, 10, 15, 18, 20, and 22% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００７８】比較例16−１ 比較例16−１として、粉末度が 5000cm2/gで、 4.0重量
％のＳＯ3 、10重量％のＣ3 Ａ、後述する量のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 6.0重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ｓの含有量は、30、4
0、45、55、65、70、75重量％の７種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 16-1 As Comparative Example 16-1, a cement having a fineness of 5000 cm 2 / g and containing 4.0% by weight of SO 3 , 10% by weight of C 3 A, and the amount of C 3 S described below. to 100 parts by weight, using a cement aS '3 was added 6.0 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 S is 30, 4
Seven types of 0, 45, 55, 65, 70 and 75% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００７９】比較例16−２ 比較例16−２として、粉末度が 7000cm2/gで、 6.0重量
％のＳＯ3 、12重量％のＣ3 Ａ、後述する量のＣ3 Ｓが
含まれるセメント 100重量部に、ＡＳ'3を 6.0重量部添
加したセメントを用いて、上記実施例１−１と同様の方
法で木毛セメント板を得た。Ｃ3 Ｓの含有量は、30、4
0、45、55、65、70、75重量％の７種類のものを用い
た。ＳＯ3 、Ｃ3 Ａ、Ｃ3 Ｓ以外の他の成分としては、
主としてＣ2 Ｓ、Ｃ4 ＡＦ等が含まれている。 Comparative Example 16-2 As Comparative Example 16-2, a cement having a fineness of 7000 cm 2 / g and containing 6.0% by weight of SO 3 , 12% by weight of C 3 A, and an amount of C 3 S described below. to 100 parts by weight, using a cement aS '3 was added 6.0 part by weight, to obtain a wood wool cement board in the same manner as in example 1-1. The content of C 3 S is 30, 4
Seven types of 0, 45, 55, 65, 70 and 75% by weight were used. Other components other than SO 3 , C 3 A and C 3 S include:
It mainly contains C 2 S, C 4 AF, and the like.

【００８０】上記実施例１−１〜８−２及び比較例１−
１−１〜16−２で得られた木毛セメント板について、セ
メント組成物の比強度の変化を以下の方法により算出し
た。Examples 1-1 to 8-2 and Comparative Example 1
For the wood wool cement board obtained in 1-1 to 16-2, the change in the specific strength of the cement composition was calculated by the following method.

【００８１】既存のセメント（ＪＩＳ規格に従った普通
ポルトランドセメントなど）に所定量の木毛を混合して
組成物とし、混練・成形後、６０℃で１２時間養生した
後、室温まで冷却し、３点曲げ試験を実施して、得られ
た曲げ強度を「目標強度」とした。上記実施例及び比較
例のセメントに所定量の木毛を混合して組成物とし、混
練・成形後、６０℃で６時間養生した後、室温まで冷却
し、３点曲げ試験を実施して、該セメントの曲げ強度を
測定した。得られた曲げ強度を「目標強度」で除して
「比強度」とした。A predetermined amount of wood wool is mixed with an existing cement (such as ordinary Portland cement according to JIS) to form a composition, kneaded and molded, cured at 60 ° C. for 12 hours, cooled to room temperature, A three-point bending test was performed, and the obtained bending strength was defined as “target strength”. A predetermined amount of wood wool was mixed with the cement of the above Examples and Comparative Examples to obtain a composition, kneaded and molded, cured at 60 ° C. for 6 hours, cooled to room temperature, and subjected to a three-point bending test. The flexural strength of the cement was measured. The obtained bending strength was divided by “target strength” to obtain “specific strength”.

【００８２】測定結果を表１〜16および図１〜16に示
す。The measurement results are shown in Tables 1 to 16 and FIGS.

【００８３】[0083]

【表１】 [Table 1]

【００８４】[0084]

【表２】 [Table 2]

【００８５】[0085]

【表３】 [Table 3]

【００８６】[0086]

【表４】 [Table 4]

【００８７】[0087]

【表５】 [Table 5]

【００８８】[0088]

【表６】 [Table 6]

【００８９】[0089]

【表７】 [Table 7]

【００９０】[0090]

【表８】 [Table 8]

【００９１】[0091]

【表９】 [Table 9]

【００９２】[0092]

【表10】 [Table 10]

【００９３】[0093]

【表11】 [Table 11]

【００９４】[0094]

【表12】 [Table 12]

【００９５】[0095]

【表13】 [Table 13]

【００９６】[0096]

【表14】 [Table 14]

【００９７】[0097]

【表15】 [Table 15]

【００９８】[0098]

【表16】 [Table 16]

【００９９】これらの結果より、ＡＳ'3の添加量が 0.5
または 6.0重量％である比較例９−１〜16−２では、比
強度が全て１未満であった、また、ＡＳ'3の添加量が
2.0または 4.0重量％である場合において、粉末度3800c
m2/g （比較例１−１−１、１−２−１、５−１−１、
５−２−１）では、比強度が１未満となり、粉末度9000
cm2/g （比較例１−１−２、１−２−２、５−１−２、
５−２−２）では、比強度が１以上となるものの、粉末
度8000cm2/g の場合と差がなかった。更に、ＳＯ3 の含
有量が、 3.0または16.0重量％である場合（比較例２−
１−１、２−１−２等）、Ｃ3 Ａの含有量が６または２
２重量％である場合（比較例３−１−１、３−１−２
等）、Ｃ3 Ｓの含有量が30または75重量％である場合
（比較例４−１−１、４−１−２等）に、比強度が１未
満であった。これに対し、粉末度が 4300 〜8000cm2/g
で、ＳＯ3 量が 3.5〜15重量％、Ｃ 3 Ａが 8〜20重量％
及びＣ3 Ｓが40〜70重量％含有されるセメント 100重量
部にＡＳ'3を 2.0または 4.0重量部添加した実施例１−
１〜８−２では、比強度は全て１以上であった。From these results, AS 'Three0.5
Or, in Comparative Examples 9-1 to 16-2 which are 6.0% by weight,
All the strengths were less than 1, and AS 'ThreeAmount of
2.0% or 4.0% by weight, fineness 3800c
mTwo/ g (Comparative Examples 1-1-1, 1-2-1, 5-1-1,
In 5-2-1), the specific strength was less than 1, and the fineness was 9000.
cmTwo/ g (Comparative Examples 1-1-2, 1-2-2, 5-1-2,
In 5-2-2), although the specific strength is 1 or more, powder
Degree 8000cmTwoThere was no difference from the case of / g. Furthermore, SOThreeIncluding
When the amount is 3.0 or 16.0% by weight (Comparative Example 2-
1-1, 2-1-2), CThreeA content of 6 or 2
2% by weight (Comparative Examples 3-1-1, 3-1-2)
Etc.), CThreeWhen the content of S is 30 or 75% by weight
(Comparative Examples 4-1-1, 4-1-2, etc.) have a specific strength of not more than 1.
It was full. On the other hand, fineness is 4300-8000cmTwo/ g
And SOThree3.5 to 15% by weight, C ThreeA is 8-20% by weight
And CThree100% cement containing 40-70% by weight of S
AS 'in the partThreeExample 1 wherein 2.0 or 4.0 parts by weight of
In the cases of 1 to 8-2, the specific intensities were all 1 or more.

【０１００】[0100]

【発明の効果】以上のように、粉末度が 4300 〜8000cm
2/g で、ＳＯ3 量が 3.5〜15重量％、Ｃ3 Ａが 8〜20重
量％及びＣ3 Ｓが40〜70重量％含有されるセメント 100
重量部にＡＳ'3を 1.0〜 5.0重量部添加してなる本発明
のセメント組成物を用いることにより、従来品と同程度
の強度を有する木毛セメントを得ることができる。As described above, the fineness is 4300 to 8000 cm.
2 / g, cement containing 3.5 to 15% by weight of SO 3 , 8 to 20% by weight of C 3 A and 40 to 70% by weight of C 3 S 100
By using the cement composition of the parts by weight of AS '3 to 1.0 to 5.0 parts by weight added to become the present invention, it is possible to obtain a cemented excelsior with conventional products comparable strength.

【０１０１】すなわち、ＳＯ3 量およびＣ3 Ａ量を、上
記範囲にすることにより、ＳＯ3 とＣ3 Ａが過不足なく
反応して多量のエトリンガイトを生成し、セメントの硬
化が促進され、また、Ｃ3 Ｓ量を上記範囲にすることに
より、セメントの硬化阻害成分である水溶性有機物を増
加させる水酸化カルシウムの生成を抑えつつ、セメント
の強度を増加させることができる。That is, by setting the amounts of SO 3 and C 3 A within the above ranges, SO 3 and C 3 A react without excess or shortage to generate a large amount of ettringite, and the hardening of the cement is accelerated. By setting the amount of C 3 S in the above range, it is possible to increase the strength of the cement while suppressing the production of calcium hydroxide, which increases the amount of water-soluble organic substances that are the hardening inhibiting components of the cement.

【０１０２】また、上記特定セメント 100重量部にＡ
Ｓ'3を 1.0〜5.0 重量部添加することにより、硫酸イオ
ン及びアルミニウムイオンの量が更に増加し、エトリン
ガイト及びカルシウムアルミネート水和物の生成が一層
促進されるとともに、液相のｐＨが低下することによ
り、セメントの水和阻害が防止され、優れた強度発現性
が得られる。Further, A was added to 100 parts by weight of the specific cement.
By S '3 is added 1.0 to 5.0 parts by weight, further increase in the amount of sulfate ions and aluminum ions, with the generation of ettringite and calcium aluminate hydrate is further promoted, pH of the liquid phase is reduced Thereby, hydration inhibition of the cement is prevented, and excellent strength development is obtained.

【０１０３】従って、本発明のセメント組成物を、木片
又は木毛セメント板の製造に用いることにより、硬化が
促進され、従来品と同程度の強度を得るために必要な養
生時間が短縮でき、ひいては、製造時間を短縮すること
ができるという効果を得た。Therefore, by using the cement composition of the present invention for the production of wood chips or wood wool cement boards, hardening is promoted, and the curing time required to obtain the same strength as conventional products can be shortened. As a result, the effect that the manufacturing time can be shortened is obtained.

【図面の簡単な説明】[Brief description of the drawings]

【図１】粉末度と比強度との関係を示すグラフ。FIG. 1 is a graph showing the relationship between fineness and specific strength.

【図２】ＳＯ3 量と比強度との関係を示すグラフ。FIG. 2 is a graph showing a relationship between SO 3 amount and specific intensity.

【図３】Ｃ3 Ａ量と比強度との関係を示すグラフ。FIG. 3 is a graph showing the relationship between C 3 A content and specific intensity.

【図４】Ｃ3 Ｓ量と比強度との関係を示すグラフ。FIG. 4 is a graph showing a relationship between C 3 S amount and specific intensity.

【図５】粉末度と比強度との関係を示すグラフ。FIG. 5 is a graph showing the relationship between fineness and specific strength.

【図６】ＳＯ3 量と比強度との関係を示すグラフ。FIG. 6 is a graph showing the relationship between the amount of SO 3 and the specific intensity.

【図７】Ｃ3 Ａ量と比強度との関係を示すグラフ。FIG. 7 is a graph showing a relationship between C 3 A amount and specific intensity.

【図８】Ｃ3 Ｓ量と比強度との関係を示すグラフ。FIG. 8 is a graph showing a relationship between C 3 S amount and specific intensity.

【図９】粉末度と比強度との関係を示すグラフ。FIG. 9 is a graph showing the relationship between fineness and specific strength.

【図10】ＳＯ3 量と比強度との関係を示すグラフ。FIG. 10 is a graph showing a relationship between SO 3 amount and specific intensity.

【図11】Ｃ3 Ａ量と比強度との関係を示すグラフ。FIG. 11 is a graph showing a relationship between C 3 A amount and specific intensity.

【図12】Ｃ3 Ｓ量と比強度との関係を示すグラフ。FIG. 12 is a graph showing a relationship between C 3 S amount and specific intensity.

【図13】粉末度と比強度との関係を示すグラフ。FIG. 13 is a graph showing a relationship between fineness and specific strength.

【図14】ＳＯ3 量と比強度との関係を示すグラフ。FIG. 14 is a graph showing the relationship between the amount of SO 3 and the specific intensity.

【図15】Ｃ3 Ａ量と比強度との関係を示すグラフ。FIG. 15 is a graph showing a relationship between C 3 A amount and specific intensity.

【図16】Ｃ3 Ｓ量と比強度との関係を示すグラフ。FIG. 16 is a graph showing a relationship between C 3 S amount and specific intensity.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 渋田 祥司 大阪市大正区南恩加島７丁目１番55号 住 友大阪セメント株式会社セメント・コンク リート研究所内 (72)発明者 五十畑 達夫 大阪市大正区南恩加島７丁目１番55号 住 友大阪セメント株式会社セメント・コンク リート研究所内 (72)発明者 吉原 正興 東京都千代田区神田美土代町１番地 住友 大阪セメント株式会社内 (72)発明者 原田 修輔 東京都千代田区神田美土代町１番地 住友 大阪セメント株式会社内 (72)発明者 内村 典文 東京都千代田区神田美土代町１番地 住友 大阪セメント株式会社内 ──────────────────────────────────────────────────続 き Continued on the front page (72) Inventor Shoji Shibuda 7-55 Minamionkajima, Taisho-ku, Osaka Sumitomo Osaka Cement Co., Ltd. Cement Concrete Research Laboratory (72) Inventor Tatsuo Ishihata Taisho-ku, Osaka-shi 7-55 Minamienkajima Sumitomo Osaka Cement Co., Ltd. Cement Concrete Research Laboratory (72) Inventor Masako Yoshihara 1 Kanda Midoshiro-cho, Chiyoda-ku, Tokyo Sumitomo Osaka Cement Co., Ltd. (72) Inventor Shusuke Harada, Sumitomo Osaka Cement Co., Ltd. (72) Inventor Norifumi Uchimura 1 Sumitomo Osaka Cement Co., Ltd. (72) Inventor Norifumi Uchimura, Kamidachi-cho, Chiyoda-ku, Tokyo

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 粉末度が4300〜8000cm2/g 、ＳＯ3 量が
3.5〜15重量％、３ＣａＯ・Ａｌ2 Ｏ3 が 8〜20重量％
及び３ＣａＯ・ＳｉＯ2 が40〜70重量％含有されたセメ
ント 100重量部に、硫酸アルミニウムが 1.0〜5.0 重量
部添加されてなることを特徴とするセメント組成物。1. A fineness of 4300 to 8000 cm 2 / g and an SO 3 amount
3.5 to 15% by weight, 8 to 20% by weight of 3CaO.Al 2 O 3
And 3CaO · SiO 2 is 100 parts by weight of cement contained 40 to 70 wt%, a cement composition characterized by comprising the addition of aluminum sulfate 1.0 to 5.0 parts by weight.
JP25242597A 1997-09-17 1997-09-17 Cement composition Pending JPH1192199A (en)