JPH1142737A - Fireproof precious wood decorative sheet, its production, and fire proof precious wood decorative panel having the sheet bonded thereto - Google Patents
Fireproof precious wood decorative sheet, its production, and fire proof precious wood decorative panel having the sheet bonded theretoInfo
- Publication number
- JPH1142737A JPH1142737A JP21710897A JP21710897A JPH1142737A JP H1142737 A JPH1142737 A JP H1142737A JP 21710897 A JP21710897 A JP 21710897A JP 21710897 A JP21710897 A JP 21710897A JP H1142737 A JPH1142737 A JP H1142737A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- precious wood
- veneer
- decorative sheet
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【発明の属する技術分野】本発明は、難燃化技術がさら
に改良された防燃性銘木化粧シートに関し、また該シー
トの製造方法並びに該シートを貼着した防燃性銘木化粧
板に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative sheet for a flameproof precious wood having a further improved flame retarding technology, a method for producing the sheet, and a decorative board for the decorative wood to which the sheet is adhered.
【０００２】それゆえ、本発明は、以下に掲げる化粧単
板シートの一般的な用途に利用されうるものである。：
建築内装材例えば壁面材、天井表面材、柱被覆材および
可動間仕切り等の表面材：自動車、船舶の内装製品の表
面材：箪笥等の家具の外面化粧材：什器等の一般木製品
の外面化粧材：並びに電子機器および楽器の外面化粧材
など。Therefore, the present invention can be used for the following general applications of decorative veneer sheets. :
Architectural interior materials, such as wall materials, ceiling surface materials, column covering materials, and movable partitions: Surface materials for interior products of automobiles and ships: Exterior materials for furniture such as wardrobes: Exterior materials for general wood products such as furniture : Exterior decoration materials for electronic devices and musical instruments.
【０００３】[0003]
【従来の技術】従来、特開昭 61-47250 号公報に開示さ
れる銘木化粧単板シート、即ち銘木単板；接着剤；クラ
フト紙、薄葉紙、含浸加工紙等の紙あるいは不織布；ポ
リエチレン層またはポリプロピレン層；アルミニウム箔
または鉄箔；ポリエチレン層またはポリプロピレン層；
クラフト紙、薄葉紙、含浸加工紙等の紙あるいは不織布
という積層構成を有する銘木化粧単板シートは、製品化
された後、上記の用途において広く使用されている。2. Description of the Related Art Conventionally, decorative veneer veneer sheets disclosed in Japanese Patent Application Laid-Open No. 61-47250, that is, precious veneer veneers; adhesives; paper or nonwoven fabric such as kraft paper, tissue paper, impregnated paper; Polypropylene layer; aluminum foil or iron foil; polyethylene layer or polypropylene layer;
A nameplate decorative veneer sheet having a laminated structure of paper such as kraft paper, tissue paper, impregnated paper or a nonwoven fabric has been widely used in the above applications after it has been commercialized.
【０００４】しかし、この銘木化粧単板シートは、特別
な難燃化処理が施されておらず、不燃性能の点で劣るた
め、改良すべきものであった。そこで、本出願人は、特
願平 4-296350 号（特開平 6-115008 号公報）にて、
『紙または不織布：第１の接着性樹脂層：アルミニウム
箔または鉄箔：第２の接着性樹脂層：紙または不織布：
接着剤層：銘木単板が最下層より順に積層され、一体に
圧着成形されてなる化粧シートであって、ブロム系難燃
剤が第１の接着性樹脂層もしくは第２の接着性樹脂層の
いずれか一方または第１および第２の接着性樹脂層の双
方に含有されてなる、防燃性銘木化粧シート』を提案し
た。この新たに開発された防燃性銘木化粧シートは、高
い難燃性を有し、防火材料における準不燃の性能を発揮
することができる製品であって、その上、突板の変色に
よる製品価値の低下、並びに接着性の悪化による不良製
品の発生などの問題が起きないという利点を有するもの
である。[0004] However, this decorative veneer veneer sheet has not been subjected to a special flame-retardant treatment, and is inferior in non-combustibility. Therefore, the present applicant has filed Japanese Patent Application No. 4-296350 (JP-A-6-115008).
"Paper or nonwoven fabric: first adhesive resin layer: aluminum foil or iron foil: second adhesive resin layer: paper or nonwoven fabric:
Adhesive layer: A decorative sheet formed by laminating precious wood veneers in order from the lowermost layer and integrally press-molding, wherein the bromo-based flame retardant is either a first adhesive resin layer or a second adhesive resin layer. At least one or both of the first and second adhesive resin layers. " This newly developed fireproof precious wood decorative sheet is a product that has high flame retardancy and can exhibit semi-flammable performance in fire protection materials. This has the advantage that problems such as lowering and occurrence of defective products due to deterioration of adhesiveness do not occur.
【０００５】[0005]
【発明が解決しようとする課題】しかし、上記の防燃性
銘木化粧シートは、積層要素として金属箔、特にアルミ
ニウム箔を含むため、熱伝導性が相当に高いものになる
ので、実際の火災等においては、火炎伝播の現象が起き
やすいものとなる。かような性質は、防火材料として望
ましくない性質である。従って、火災において火炎伝播
が起きにくい性質のものに改良することが要求されてい
た。また、アルミニウム箔等の金属箔は一般に樹脂フィ
ルムとの接着性が悪い。このため、従来の防燃性銘木化
粧シートにあっては、シート材料相互間、特に接着性樹
脂層とアルミニウム箔（鉄箔）との間の接着性能が経時
的に弱化し、稀ではあるが、長期間の使用のうちにそれ
ら両要素の界面にて剥離し、準不燃の性能を発揮し得な
くなってしまう場合もあった。従って、接着性能の面に
ついてもさらに改良すべき必要性があった。ところで、
特開平 9-52316号公報、特開平 9-52317号公報および特
開平 9-52318号公報などに示されるように、ガラス繊維
織布などのガラス繊維材料を一要素として積層成形した
木質系合板は、既に提案されているが、かようなガラス
繊維材料を含む銘木化粧シート、特に防燃性銘木化粧シ
ートは、本発明者の知るかぎり、未だ提案されておら
ず、また、そのような製品も今現在製造・販売されてい
ない。However, since the above flame-resistant decorative wood decorative sheet contains a metal foil, especially an aluminum foil as a laminated element, it has a considerably high thermal conductivity, so that it can be used in actual fires and the like. In this case, the phenomenon of flame propagation is likely to occur. Such properties are undesirable properties as a fire protection material. Therefore, it has been demanded to improve the property to a property in which flame propagation is unlikely to occur in a fire. Further, a metal foil such as an aluminum foil generally has poor adhesion to a resin film. For this reason, in the conventional flameproof precious wood decorative sheet, the bonding performance between the sheet materials, particularly between the adhesive resin layer and the aluminum foil (iron foil), weakens with time, and is rare. In some cases, during use for a long period of time, it peels off at the interface between these two elements, and the quasi-incombustible performance cannot be exhibited. Therefore, there is a need to further improve the adhesive performance. by the way,
As shown in JP-A-9-52316, JP-A-9-52317 and JP-A-9-52318, wood-based plywood laminated and formed using glass fiber material such as glass fiber woven fabric as one element is As far as the present inventor knows, a nameplate decorative sheet containing such a glass fiber material, particularly a flameproof nameplate decorative sheet, has not yet been proposed, and such a product has also been proposed. It is not currently manufactured or sold.
【０００６】本発明は、以上の事情を考慮してなされた
もので、その課題は、高い難燃性を有し防火材料におけ
る準不燃の性能を発揮できるのは勿論のこと、火災にお
いて火炎伝播の現象が起きにくく、防火材料として大変
優れており、その上、シート材料間の接着性能が経時的
に劣化せず、耐久性の面でも優れているところの防燃性
銘木化粧シートを提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and it is an object of the present invention to provide not only a fire-retardant material but also a quasi-non-combustible performance of a fire-retardant material. To provide a fire-resistant precious wood decorative sheet that is excellent as a fire-resistant material, does not deteriorate over time, and is excellent in durability. It is in.
【０００７】また、本発明の別の課題は、防燃性銘木化
粧シートを確実にかつ生産性高く製造することができる
製造方法を提供することにある。さらに、本発明の他の
課題は、防燃性銘木化粧シートを表面材とする防燃性銘
木化粧板を提供することにある。Another object of the present invention is to provide a production method capable of producing a flame-resistant decorative wood decorative sheet reliably and with high productivity. Still another object of the present invention is to provide a fire-resistant precious wood decorative board having a fire-resistant precious wood decorative sheet as a surface material.
【０００８】[0008]
【課題を解決するための手段】本発明者は、鋭意研究の
結果、防燃性銘木化粧シート内の要素として、アルミニ
ウム箔（鉄箔）に代えて、ガラス繊維不織布、ガラス繊
維紙もしくはガラス繊維織布またはこれらの組合せを適
用したところ、火炎燃焼試験（実際の火災を模擬した試
験）において、アルミニウム箔を使用する従来の防燃性
銘木化粧シートとは異なり、火炎伝播の現象が起きにく
く、壁装材料協会制定の紙壁紙２級の防火性能を有する
ものとなり、一層優れた防火材料が得られるという事実
を見い出し、さらに、これらガラス繊維材料を使用する
防燃性銘木化粧シートは、従来品と同様に、難燃性能が
高く、昭和５９年９月２９日建設省告示第１３７２号に
基づく表面試験（加熱試験）において防火材料として準
不燃の性能を満足に発揮するものであるという事実を確
認し、ここに本発明を完成した。また、本発明者は、上
記の防燃性銘木化粧シートの中のガラス繊維材料（ガラ
ス繊維不織布など）と紙もしくは不織布との積層体に代
えて、難燃性ガラス混抄紙（ガラス繊維が混抄された紙
であってさらに難燃剤が配合されているもの）を適用し
た場合も、その防燃性銘木化粧シートは、ガラス繊維材
料を使用する防燃性銘木化粧シートと同様に、火炎伝播
の現象が起きにくくかつ難燃性能が高く、壁装材料協会
制定の紙壁紙２級の防火性能を有し、そして昭和５９年
９月２９日建設省告示第１３７２号に基づく表面試験
（加熱試験）において防火材料として準不燃の性能を満
足に発揮するものであるという事実を確認し、ここに本
発明を完成した。Means for Solving the Problems As a result of intensive studies, the present inventor has found that a glass fiber non-woven fabric, glass fiber paper or glass fiber is used as an element in a flame-resistant precious wood decorative sheet instead of aluminum foil (iron foil). When a woven fabric or a combination of these is applied, in the flame combustion test (test simulating an actual fire), unlike the conventional fireproof precious wood decorative sheet using aluminum foil, the phenomenon of flame propagation hardly occurs, It has the fire protection performance of the second grade of paper wallpaper established by the Wall Covering Materials Association, and has found the fact that a more excellent fire prevention material can be obtained. Furthermore, the fire-resistant precious wood decorative sheet using these glass fiber materials is a conventional product. Similar to the above, it has high flame retardancy and satisfies the quasi-incombustibility performance as a fire protection material in a surface test (heating test) based on Ministry of Construction Notification No. 1372 on September 29, 1984 Make sure the fact that is intended to demonstrate, the present invention has been completed here. Further, the present inventor has proposed a flame-retardant glass mixed paper (glass fiber mixed paper) instead of a laminate of glass fiber material (glass fiber non-woven fabric or the like) and paper or non-woven fabric in the above flame-resistant precious wood decorative sheet. Paper that is further blended with a flame retardant), the flame-resistant precious wood decorative sheet, like the flame-resistant precious wood decorative sheet using a glass fiber material, Phenomena are unlikely to occur and flame retardancy is high, it has the second class of fire prevention performance of paper wallpaper established by the Wall Covering Materials Association, and surface test (heating test) based on Ministry of Construction Notification No. 1372 on September 29, 1984 The present inventors have confirmed the fact that the material exhibits satisfactory quasi-incombustibility as a fire protection material, and completed the present invention.
【０００９】したがって、本発明は、上から順に、銘木
単板：接着剤層：紙または不織布：難燃剤が混入された
第１の接着性樹脂層；ガラス繊維不織布、ガラス繊維紙
もしくはガラス繊維織布またはこれらの組合せ；難燃剤
が混入された第２の接着性樹脂層：紙または不織布が積
層され一体に圧着成形されてなり、そして、必要により
塗料膜、典型的にはウレタン樹脂塗膜が前記銘木単板の
上に形成されている、防燃性銘木化粧シートに関する。
本発明のより好ましい態様は、上記の防燃性銘木化粧シ
ートにおいて、銘木単板として、適量の難燃剤が塗布ま
たは含浸された銘木単板が適用されている場合である。
また別の発明として、本発明は、上から順に、銘木単
板：接着剤層：難燃性ガラス混抄紙が積層され一体に圧
着成形されてなり、そして、必要により塗料膜、典型的
にはウレタン樹脂塗膜が前記銘木単板の上に形成されて
いる、防燃性銘木化粧シートに関する。この発明におけ
るより好ましい態様は、ガラス混抄紙を使用する上記の
防燃性銘木化粧シートにおいて、銘木単板として、適量
の難燃剤が塗布または含浸された銘木単板が適用されて
いる場合である。その上、本発明は、上記態様の各々の
防燃性銘木化粧シートが、木質系、無機質系または金属
系基材の上に貼着されてなる防燃性銘木化粧板に関す
る。Accordingly, the present invention provides, in order from the top, a nameplate veneer: adhesive layer: paper or nonwoven fabric: first adhesive resin layer mixed with a flame retardant; glass fiber nonwoven fabric, glass fiber paper or glass fiber woven fabric Cloth or combination thereof; second adhesive resin layer mixed with flame retardant: paper or non-woven fabric is laminated and compression molded integrally, and if necessary, paint film, typically urethane resin coating film The present invention relates to a flame-retardant precious wood decorative sheet formed on the precious wood veneer.
A more preferred embodiment of the present invention is a case in which, in the above-mentioned decorative sheet made of flame-retardant precious wood, a veneer veneer coated or impregnated with an appropriate amount of a flame retardant is applied as the veneer veneer.
As another invention, the present invention provides, in order from the top, a nameplate veneer: an adhesive layer: a flame-retardant glass-mixed paper laminated and integrally press-molded, and if necessary, a paint film, typically a paint film. The present invention relates to a flame-resistant precious wood decorative sheet having a urethane resin coating film formed on the precious wood veneer. A more preferred embodiment of the present invention is a case where the above-mentioned decorative sheet made of glass-blended paper uses a precious wood veneer coated or impregnated with an appropriate amount of a flame retardant as the precious wood veneer. . In addition, the present invention relates to a decorative board made of a fireproof precious wood in which each of the decorative sheets of the fireproof precious wood of the above embodiment is adhered onto a wood-based, inorganic-based or metal-based substrate.
【００１０】また、本発明は、上記の防燃性銘木化粧シ
ートの製造方法にも関する。すなわち、本発明は、一つ
の製造方法として、一方で、押出しラミネートまたは熱
圧ラミネートに従い、難燃剤が混入された第１の接着性
樹脂層：ガラス繊維不織布、ガラス繊維紙もしくはガラ
ス繊維織布またはこれらの組合せ：難燃剤が混入された
第２の接着性樹脂層：紙または不織布よりなる積層体を
成形する段階と、他方で、熱圧接着により、銘木単板：
接着剤層：紙または不織布よりなる単板裏打ちシートを
作る段階と、前記積層体と前記単板裏打ちシートを熱圧
接着して、一体に成形する段階と、そして必要により、
塗装によって塗料膜を、作られた防燃性銘木化粧シート
の単板表面に形成する段階よりなる、防燃性銘木化粧シ
ートの製造方法に関する。また本発明は、他の製造方法
として、押出しラミネートまたは熱圧ラミネートに従
い、紙または不織布：難燃剤が混入された第１の接着性
樹脂層：ガラス繊維不織布、ガラス繊維紙もしくはガラ
ス繊維織布またはこれらの組合せ：難燃剤が混入された
第２の接着性樹脂層：紙または不織布よりなる積層体を
成形する段階と、接着剤を該積層体の上側の紙または不
織布の上に塗布し、続いて銘木単板をその上にオーバー
レイする段階と、オーバーレイされた積層体を熱圧接着
して、一体に成形する段階と、そして必要により、塗装
によって塗料膜を、作られた防燃性銘木化粧シートの単
板表面に形成する段階よりなる、防燃性銘木化粧シート
の製造方法に関する。これら発明のうちより好ましい態
様は、塗料膜の形成の前に、難燃剤を、作られた防燃性
銘木化粧シートの単板表面に塗布または含浸する段階を
さらに含む、上記各々の防燃性銘木化粧シートの製造方
法に関する。[0010] The present invention also relates to a method for producing the above-mentioned decorative sheet for flameproof precious wood. That is, the present invention provides, as one production method, on the other hand, a first adhesive resin layer mixed with a flame retardant according to extrusion lamination or hot-press lamination: glass fiber nonwoven fabric, glass fiber paper or glass fiber woven fabric or These combinations: a second adhesive resin layer mixed with a flame retardant: a step of forming a laminate made of paper or non-woven fabric;
Adhesive layer: a step of forming a veneer backing sheet made of paper or nonwoven fabric, a step of hot-pressing the laminate and the veneer backing sheet to form a single body, and, if necessary,
The present invention relates to a method for producing a flame-retardant precious wood decorative sheet, comprising a step of forming a paint film on a veneer surface of a produced fire-resistant precious wood decorative sheet by painting. The present invention also provides, as another production method, a paper or nonwoven fabric: a first adhesive resin layer mixed with a flame retardant, a glass fiber nonwoven fabric, a glass fiber paper or a glass fiber woven fabric, in accordance with extrusion lamination or hot-press lamination. Combination of these: a second adhesive resin layer mixed with a flame retardant: a step of forming a laminate made of paper or nonwoven fabric, and applying an adhesive onto the paper or nonwoven fabric on the upper side of the laminate, A step of overlaying a veneer veneer thereon, a step of hot-pressing the overlying laminate to form an integral unit, and, if necessary, a paint film, and a flame-retardant precious wood decoration made by painting. The present invention relates to a method for producing a flame-resistant precious wood decorative sheet, comprising a step of forming the decorative sheet on a veneer surface of a sheet. A more preferred embodiment of these inventions further comprises a step of applying or impregnating a flame retardant on the veneer surface of the made flame-resistant precious wood decorative sheet before forming the paint film. The present invention relates to a method for manufacturing a precious wood decorative sheet.
【００１１】[0011]
【発明の実施の形態】以下、本発明の防燃性銘木化粧シ
ートの積層要素を順に説明する。ガラス繊維不織布、ガ
ラス繊維紙もしくはガラス繊維織布またはこれらの組合
せ（以下、これらをガラス繊維材と称する場合もあ
る。）は、いずれも、主にガラス繊維で作られた不燃の
材料であり、銘木化粧シートに難燃性を付与するため
に、従来の金属箔（アルミニウム箔）に代えて積層要素
とされるものである。また、これらガラス繊維材は、不
燃性の他、強い剛性を有し、電気絶縁性であり、また耐
腐食性、耐薬品性に優れ、さらに温湿変化に対して伸縮
・反り等の変形が生じにくい材料である。よって、この
材料を積層要素とすることにより、ガラス繊維材は、適
度の強度を化粧シートに与える他、銘木単板のあばれ、
反りを抑え、高い寸法安定性を化粧シートに付与せしめ
る。従って、本発明の防燃性銘木化粧シートは、不燃性
に優れるだけでなく、強度、寸法安定性、電気絶縁性、
耐腐食性さらに耐薬品性の面でも良好なものとなる。本
発明で用いるガラス繊維材としては、例えばグラスパー
ＧＨＮ−２５（王子製紙株式会社製、坪量２５ｇ／ｍ
2 ）、グラベスト（オリベスト株式会社製）等が挙げら
れる。ガラス繊維材は、約１０ｇ／ｍ2 以上の坪量を有
するものであれば、本発明に適用することができるが、
約８０ｇ／ｍ2 の坪量を有するガラス繊維材は、経済性
の面で好ましくない。従って、１５〜５０ｇ／ｍ2 の坪
量を有するガラス繊維材がより好ましく、２０〜３０ｇ
／ｍ2 の坪量を有するガラス繊維材が最も好ましい。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the laminated elements of the flameproof precious wood decorative sheet of the present invention will be described in order. Glass fiber nonwoven fabric, glass fiber paper or glass fiber woven fabric, or a combination thereof (hereinafter, these may be referred to as a glass fiber material) are all non-combustible materials mainly made of glass fiber, In order to impart flame retardancy to the precious wood decorative sheet, it is a laminated element instead of a conventional metal foil (aluminum foil). In addition, these glass fiber materials have strong rigidity in addition to nonflammability, are electrically insulating, are excellent in corrosion resistance and chemical resistance, and undergo deformation such as expansion and contraction and warpage in response to changes in temperature and humidity. It is a material that does not easily occur. Therefore, by using this material as a laminated element, the glass fiber material gives a moderate strength to the decorative sheet, as well as the appearance of the precious wood veneer,
Suppresses warpage and imparts high dimensional stability to decorative sheets. Therefore, the flameproof precious wood decorative sheet of the present invention is not only excellent in nonflammability, but also strength, dimensional stability, electric insulation,
It also has good corrosion resistance and chemical resistance. As the glass fiber material used in the present invention, for example, Graspar GHN-25 (manufactured by Oji Paper Co., Ltd., basis weight 25 g / m2)
2 ) and Gravest (manufactured by Olivet Co., Ltd.). The glass fiber material can be applied to the present invention as long as it has a basis weight of about 10 g / m 2 or more.
Glass fiber materials having a basis weight of about 80 g / m 2 are not preferred in terms of economy. Therefore, a glass fiber material having a basis weight of 15 to 50 g / m 2 is more preferable, and 20 to 30 g.
Glass fiber materials having a basis weight of / m 2 are most preferred.
【００１２】紙または不織布は、下地の凹凸を緩衝して
化粧シートの浮き上がりを防止するために、積層要素と
されるものである。本発明で用いられる紙または不織布
としては、和紙、洋紙（上質紙、中質紙など）、クラフ
ト紙、薄葉紙または樹脂含浸紙、並びに、ポリエチレン
不織布、ポリエステル／パルプ不織布等の各種不織布な
ど、すべての繊維質シートが包含される。紙または不織
布の坪量は、例えば、１５〜１００ g/m2 、より好まし
くは２０〜５０ g/m2 である。Paper or non-woven fabric is used as a laminating element in order to buffer the unevenness of the base and prevent the decorative sheet from floating. Examples of the paper or nonwoven fabric used in the present invention include all types of nonwoven fabrics such as Japanese paper, Western paper (high quality paper, medium quality paper, etc.), kraft paper, thin paper or resin impregnated paper, and various types of nonwoven fabrics such as polyethylene nonwoven fabric and polyester / pulp nonwoven fabric. A fibrous sheet is included. The basis weight of the paper or nonwoven fabric is, for example, 15 to 100 g / m 2 , and more preferably 20 to 50 g / m 2 .
【００１３】第１および第２の接着性樹脂層は、紙また
は不織布とガラス繊維材との接着一体化を可能とするた
めに、また化粧シートに適度の柔軟性を付与して施工時
下地の凹凸を吸収するために、また化粧シートに十分な
可撓性を与えて曲面部や角部の下地にも適合可能とする
ために、さらにガラス繊維材と一緒になって銘木単板の
あばれ、反りを抑えるために、積層要素とされるもので
ある。本発明で用いる第１および第２の接着性樹脂層
は、同種であっても異種であっても、また各樹脂層は単
層であっても複層であってもよい。その厚さは、１５〜
１００μｍ、好ましくは２０〜５０μｍであり、最も好
ましくは３０〜４５μｍである。接着性樹脂層の例とし
ては、ポリオレフィン共重合体、例えばポリエチレンコ
ポリマー、エチレン−酢酸アクリル共重合体（ＥＡ
Ａ）、エチレン−アクリル酸共重合体、アイオノマー、
ポリアミド樹脂等が挙げることができるが、これらに限
定されず、広範囲にわたって適用することができる。し
かしながら、より好ましくは、エチレン−酢酸アクリル
共重合体（ＥＡＡ）、エチレン−アクリル酸共重合体お
よびアイオノマーであり、最も好ましくは、エチレン−
酢酸アクリル共重合体（ＥＡＡ）である。The first and second adhesive resin layers are used to bond and integrate the paper or non-woven fabric with the glass fiber material, and to give the decorative sheet an appropriate flexibility so that the decorative sheet can be used as a base material at the time of construction. In order to absorb irregularities and to give the decorative sheet sufficient flexibility so that it can also be applied to the base of curved surfaces and corners, furthermore, together with the glass fiber material, the precious wood veneer is exposed, In order to suppress warpage, it is a laminated element. The first and second adhesive resin layers used in the present invention may be the same or different, and each resin layer may be a single layer or a multilayer. Its thickness is 15
It is 100 μm, preferably 20 to 50 μm, and most preferably 30 to 45 μm. Examples of the adhesive resin layer include polyolefin copolymers such as polyethylene copolymers and ethylene-acrylic acetate copolymers (EA).
A), ethylene-acrylic acid copolymer, ionomer,
Examples thereof include polyamide resins, but are not limited thereto, and can be applied over a wide range. However, more preferred are ethylene-acetic acid acrylic copolymers (EAA), ethylene-acrylic acid copolymers and ionomers, most preferably ethylene-acrylic acid copolymers.
Acrylic acetate copolymer (EAA).
【００１４】本発明にあっては、銘木化粧シート全体の
防燃化に向けて、その難燃性を高めるために、難燃剤が
第１の接着性樹脂層層および第２の接着性樹脂層の双方
に混入されている。混入される難燃剤としては、例え
ば、三酸化アンチモン、燐酸系、ハロゲン系のものが挙
げられる。より好ましい難燃剤は、臭素系難燃剤であ
る。この難燃剤の混入量は、通常、重量比で１５％以下
の量である。また、より好ましい態様にあっては、銘木
化粧シート全体の防燃化に向けて、特に銘木単板の難燃
性を高めるために、難燃剤が銘木単板の表面に塗布され
またはその中に含浸されている。この難燃剤は、上記の
難燃剤と同種のものでも、異種のものでもよい。単板表
面に付加される難燃剤は、より好ましくは、燐・窒素化
合物の難燃剤である。In the present invention, a flame retardant is added to the first adhesive resin layer and the second adhesive resin layer in order to enhance the flame retardancy of the entire decorative wood decorative sheet. Are mixed in both. Examples of the flame retardant to be mixed include antimony trioxide, a phosphoric acid type, and a halogen type. More preferred flame retardants are brominated flame retardants. The mixing amount of the flame retardant is usually 15% or less by weight. Further, in a more preferred embodiment, a flame retardant is applied to the surface of the precious wood veneer or in the flame retardant of the precious wood veneer sheet, in particular, in order to enhance the flame retardancy of the precious wood veneer. Impregnated. The flame retardant may be the same or different from the above flame retardant. The flame retardant added to the veneer surface is more preferably a phosphorus / nitrogen compound flame retardant.
【００１５】また、本発明において、銘木単板として
は、各種の銘木より、例えば０．０５ないし３．０mmの
厚さに、好ましくは０．１０ないし０．４mmの厚さに、
切削加工された挽板または突板を適用することができ
る。銘木単板の木理は、特に限定されず、柾目、追柾、
板目またはこぶ杢など、いずれでもよい。また、銘木単
板の樹種も特には、限定されないが、好ましい樹種の例
は、次の通りである。：檜、楢、欅、桜、楡、黒柿、
栃、桂、楓、槐、楠木等：ローズウッド、チーク、マホ
ガニー、コクタン（黒壇）、シタン（紫檀）、バーズア
イメープル、アメリカンブラックウォールナット、クラ
ロウォールナット、ラテヌォールナット、クィンスラン
ドウォールナット、ゼブラウッド、マンガシロ、ブラジ
リアンローズ、カリン（花梨）、バーシモン、シルバー
ローズ、パルマ、レッドウッド、パープルウッド、シル
キーオーク、タイワンクス、チェリー、マグノリヤ、黒
レオ（ダオ）、白レオ、サベリ、ブビンカ、マコレ、マ
ドローナー、ミルトル、メープル、アッシン、インブイ
ヤー等。Further, in the present invention, the precious wood veneer may be made of various precious woods, for example, to a thickness of 0.05 to 3.0 mm, preferably 0.10 to 0.4 mm.
A cut plate or veneer that has been cut can be used. The grain of the precious wood veneer is not particularly limited.
Any of a board or a knotted heather may be used. In addition, although the tree species of the precious wood veneer is not particularly limited, examples of preferred tree species are as follows. : Cypress, oak, zelkova, cherry, yu, black persimmon,
Tochi, Katsura, Maple, Sophora, Kusunoki, etc .: Rosewood, teak, mahogany, kokutan (black altar), rosewood (red sandalwood), bird's eye maple, American black walnut, claro walnut, latine walnut, quinsland walnut, zebra wood, Manga Shiro, Brazilian Rose, Karin (Karin), Versimon, Silver Rose, Parma, Redwood, Purplewood, Silky Oak, Thai Wanks, Cherry, Magnolia, Black Leo (Dao), White Leo, Savery, Bubinka, Makole, Madrone, Miltor , Maple, Assin, Inbuyer etc.
【００１６】接着剤層は、銘木単板と紙または不織布と
を接着するために、積層要素とされる。単板と紙または
不織布との接着が比較的容易であるため、本発明におい
て使用される接着剤の種類は特に限定されないが、例え
ば、エチレン酢酸ビニル樹脂（ＥＶＡ）接着剤、酢酸ビ
ニル−アクリル共重合体接着剤、水性ビニルウレタン系
接着剤、またはアクリル系粘着剤などが有利に利用する
ことができる。The adhesive layer is a laminated element for adhering the veneer veneer and paper or nonwoven fabric. The type of adhesive used in the present invention is not particularly limited because the adhesion between veneer and paper or nonwoven fabric is relatively easy. For example, ethylene vinyl acetate resin (EVA) adhesive, vinyl acetate-acrylic A polymer adhesive, an aqueous vinyl urethane-based adhesive, an acrylic adhesive, or the like can be advantageously used.
【００１７】また、本発明にあっては、銘木化粧シート
の表面保護のために、塗料膜、例えばウレタン樹脂塗膜
を銘木単板の上に形成することができる。この塗料膜
は、一般の塗装法に従い形成され、例えば塗料ウレタン
樹脂塗膜にあっては、ウレタン樹脂塗料を銘木単板の表
面に塗布し続いて紫外線照射により塗膜を硬化せしめる
というプロセスを経て形成される。Further, in the present invention, a paint film, for example, a urethane resin coating film, can be formed on the precious wood veneer to protect the surface of the precious wood decorative sheet. This paint film is formed according to a general coating method.For example, in the case of a paint urethane resin paint film, a urethane resin paint is applied to the surface of a veneer veneer, and then the paint film is cured by ultraviolet irradiation. It is formed.
【００１８】また、本発明にあっては、接着剤層：紙ま
たは不織布：難燃剤が混入された第１の接着性樹脂層；
ガラス繊維不織布、ガラス繊維紙もしくはガラス繊維織
布またはこれらの組合せ；難燃剤が混入された第２の接
着性樹脂層：紙または不織布よりなる積層体に代えて、
難燃性ガラス混抄紙という単独の要素のみを適用するこ
とも可能であり、本発明は、その態様をも包含するもの
である。難燃性ガラス混抄紙とは、紙の内部にガラス繊
維が混抄された紙であって、さらに難燃剤がその中に混
入されているものを指す。従って、本発明は、上から順
に、銘木単板：接着剤層：難燃性ガラス混抄紙が積層さ
れ一体に圧着成形されてなり、そして、必要により塗料
膜、例えばウレタン樹脂塗膜が前記銘木単板の上に形成
されている、防燃性銘木化粧シートに関する。In the present invention, the adhesive layer: paper or nonwoven fabric: a first adhesive resin layer mixed with a flame retardant;
Glass fiber nonwoven fabric, glass fiber paper or glass fiber woven fabric or a combination thereof; second adhesive resin layer mixed with flame retardant: instead of a laminate made of paper or nonwoven fabric,
It is also possible to apply only a single element, that is, a flame-retardant glass-mixed paper, and the present invention also includes such an embodiment. The flame-retardant glass-mixed paper refers to a paper in which glass fibers are mixed in the paper, and further contains a flame retardant. Accordingly, the present invention comprises, in order from the top, laminated veneer veneer: adhesive layer: flame-retardant glass-mixed paper, and integrally press-molded, and if necessary, paint film, for example, urethane resin coating film, The present invention relates to a flameproof precious wood decorative sheet formed on a veneer.
【００１９】また、本発明における防燃性銘木化粧板
は、上述の各要素より成る防燃性銘木化粧シートを表面
材とし、これを厚肉の基材の上に貼着してなるものであ
る。かかる基材としては、有利には、木質系の基材（例
えば、合板、ＭＤＦ、パーティクルボードハニカムボー
ド等）、無機質系の基材（例えば、石膏ボード、ケイカ
ル板、石綿パーライト板等）、または金属系の基材（例
えば、アルミニウム板、鉄板等）が適用される。Further, the decorative board made of flame retardant wood according to the present invention comprises a decorative sheet made of fire resistant wood consisting of the above-mentioned elements as a surface material, which is adhered to a thick base material. is there. As such a substrate, a wood-based substrate (for example, plywood, MDF, particle board honeycomb board, etc.), an inorganic-based substrate (for example, gypsum board, silica gel, asbestos pearlite board, etc.), or A metal base material (for example, an aluminum plate, an iron plate, or the like) is used.
【００２０】また、本発明の防燃性銘木化粧シートは、
次の２通りの方法により製造することができる。いずれ
の製法も、最初に、ロール練り等によって難燃剤を第１
および第２の接着性樹脂に均質に混和することにより、
難燃剤混入の接着性樹脂を調製するか、あるいは、予め
同種の樹脂製品を商業的に入手する。一の方法は、一方
で、押出しラミネートまたは熱圧ラミネートに従い、難
燃剤が混入された第１の接着性樹脂層：ガラス繊維不織
布、ガラス繊維紙もしくはガラス繊維織布またはこれら
の組合せ：難燃剤が混入された第２の接着性樹脂層：紙
または不織布よりなる積層体を成形し、他方で、熱圧接
着により、銘木単板：接着剤層：紙または不織布よりな
る単板裏打ちシートを作り、そして前記積層体と前記単
板裏打ちシートを熱圧接着して、一体に成形し、その
後、必要により、塗料膜、例えばウレタン樹脂塗料膜
を、圧着成形により作られた防燃性銘木化粧シートの単
板表面に形成するという手順により、防燃性銘木化粧シ
ートを製造する方法である。また、別の方法は、押出し
ラミネートまたは熱圧ラミネートに従い、紙または不織
布：難燃剤が混入された第１の接着性樹脂層：ガラス繊
維不織布、ガラス繊維紙もしくはガラス繊維織布または
これらの組合せ：難燃剤が混入された第２の接着性樹脂
層：紙または不織布よりなる積層体を成形し、次に、接
着剤を該積層体の上側の紙または不織布の上に塗布し、
続いて銘木単板をその上にオーバーレイし、そして、オ
ーバーレイされた積層体を熱圧接着して、一体に成形
し、その後、必要により、塗料膜、例えばウレタン樹脂
塗料膜を、圧着成形により作られた防燃性銘木化粧シー
トの単板表面に形成するという手順により、防燃性銘木
化粧シートを製造する方法である。なお、これらの製造
方法において、塗料膜の形成の前に、難燃剤を、作られ
た防燃性銘木化粧シートの単板表面に塗布または含浸す
ることも可能である。Further, the flame-resistant precious wood decorative sheet of the present invention comprises:
It can be manufactured by the following two methods. In any of the manufacturing methods, first, the flame retardant is first mixed by roll kneading or the like.
And by homogeneously mixing with the second adhesive resin,
An adhesive resin mixed with a flame retardant is prepared, or a resin product of the same kind is commercially obtained in advance. One method, on the other hand, involves a first adhesive resin layer mixed with a flame retardant according to extrusion lamination or hot-press lamination: glass nonwoven fabric, glass fiber paper or glass fiber woven fabric or a combination thereof: A second adhesive resin layer mixed therein: forming a laminate made of paper or non-woven fabric, and, on the other hand, making a nameplate veneer: adhesive layer: a veneer backing sheet made of paper or non-woven fabric by hot-press bonding; Then, the laminate and the veneer backing sheet are hot-press bonded and integrally formed, and then, if necessary, a paint film, for example, a urethane resin paint film, of a flame-resistant precious wood decorative sheet made by compression molding. This is a method of producing a flame-resistant precious wood decorative sheet by a procedure of forming on a veneer surface. Another method is extrusion lamination or hot-press lamination according to paper or non-woven fabric: a first adhesive resin layer mixed with a flame retardant: glass fiber non-woven fabric, glass fiber paper or glass fiber woven fabric, or a combination thereof: A second adhesive resin layer mixed with a flame retardant: forming a laminate made of paper or nonwoven fabric, and then applying an adhesive on the paper or nonwoven fabric on the upper side of the laminate,
Subsequently, a precious wood veneer is overlaid thereon, and the overlying laminate is hot-pressed and bonded to form an integral body, and then, if necessary, a paint film, for example, a urethane resin paint film is formed by press-fitting. This is a method of manufacturing a flame-resistant precious wood decorative sheet by a procedure of forming it on the surface of a veneer of the obtained fire-resistant precious wood decorative sheet. In these production methods, it is also possible to apply or impregnate the flame retardant on the veneer surface of the made flameproof precious wood decorative sheet before forming the paint film.
【００２１】[0021]
【実施例】以下、本発明の実施例を図面により説明す
る。Embodiments of the present invention will be described below with reference to the drawings.
【００２２】実施例１ この実施例は、図１に示す防燃性銘木化粧シート１に関
する。これは、上から順に、銘木単板２（厚さ０．１５
〜０２５ｍｍ、重量５０〜１２０ｇ／ｍ2 、樹種楢、マ
ホガニー等、各種突板）：接着剤層３（酢酸ビニルアク
リル共重合体接着剤）：紙または不織布４（例えば坪量
３７ｇ／ｍ2 の紙）：ブロム系難燃剤が混入された第１
の接着性樹脂層５（厚さ２０〜５０μｍのエチレン−酢
酸アクリル共重合体（ＥＡＡ）樹脂層）：ガラス繊維不
織布、ガラス繊維紙もしくはガラス繊維織布またはこれ
らの組合せ６（例えばグラスパーＧＨＮ−２５（王子製
紙株式会社製、坪量２５ｇ／ｍ2 ）：ブロム系難燃剤が
混入された第２の接着性樹脂層７（厚さ２０〜５０μｍ
のエチレン−酢酸アクリル共重合体（ＥＡＡ）樹脂
層）：紙または不織布８（例えば坪量３０ｇ／ｍ2 の
紙）が積層され、一体に圧着成形された化粧シートであ
って、難燃剤９（燐・窒素化合物）が銘木単板２上に塗
布され（その一部は含浸している）、さらにその上に塗
料膜（ウレタン樹脂塗膜）１０が形成されている。 Example 1 This example relates to a decorative sheet 1 for flameproof precious wood shown in FIG. This is, in order from the top, precious wood veneer 2 (thickness 0.15
０２025 mm, weight of 50 to 120 g / m 2 , various kinds of veneers such as tree seed oak, mahogany, etc.): adhesive layer 3 (vinyl acetate acrylic copolymer adhesive): paper or nonwoven fabric 4 (for example, paper having a basis weight of 37 g / m 2 ) ): No. 1 with brominated flame retardant
Adhesive resin layer 5 (ethylene-acrylic acetate copolymer (EAA) resin layer having a thickness of 20 to 50 μm): glass fiber nonwoven fabric, glass fiber paper or glass fiber woven fabric, or a combination thereof 6 (for example, Grasper GHN-25) (Manufactured by Oji Paper Co., Ltd., basis weight 25 g / m 2 ): the second adhesive resin layer 7 (20 to 50 μm in thickness) mixed with a bromo-based flame retardant
Ethylene-acetate acrylic copolymer (EAA) resin layer): a decorative sheet in which paper or non-woven fabric 8 (for example, paper having a basis weight of 30 g / m 2 ) is laminated and integrally pressed and formed, and a flame retardant 9 ( Phosphorus / nitrogen compound) is applied on the precious wood veneer 2 (a part of which is impregnated), and a coating film (urethane resin coating film) 10 is further formed thereon.
【００２３】本実施例の化粧シート１は、例えば以下の
手順(A) 、(B) 、(C) に従い製造することができた。 手順(A) 図２および図３に示すように、まず一方で、市販のペレ
ット状のＥＡＡ樹脂粒子（ブロム系難燃剤混入）、紙
（坪量３０ｇ／ｍ2 ）、およびガラス繊維不織布（グラ
スパーＧＨＮ−２５）を準備し、押出しラミネート法に
従い、難燃剤が混入された第１の接着性樹脂（ＥＡＡ）
層（厚さ４０μｍ）５：坪量２５ｇ／ｍ2のガラス繊維
不織布（グラスパーＧＨＮ−２５）６：難燃剤が混入さ
れた第２の接着性樹脂（ＥＡＡ）層（厚さ４０μｍ）
７：紙（坪量３０ｇ／ｍ2 ）８よりなる積層体１１を成
形し（図(A) ）、また他方で、熱圧接着（ 110℃× 7kg
/cm2×3分の条件による熱圧締）により、銘木単板（厚
さ０．２４ｍｍの楢突板）２：酢酸ビニルアクリル共重
合体接着剤層３：紙（坪量３７ｇ／ｍ2 ）４よりなる単
板裏打ちシート１２を作り（図(B) ）、そして、積層体
１１と単板裏打ちシート１２とをホット・コールド連続
プレス機の中に入れ、これらを 125℃× 7kg/cm2×15分
の条件で熱圧締し、続いて同じプレス圧を維持したま
ま、強制冷却により常温に降温するまで圧締を続け（図
(C) ）、この熱圧接着により一体に成形し、その後、必
要により、サンドペーパー＃ 240を用いて単板２の表面
を研磨し、続いて、難燃剤（燐・窒素化合物）９を銘木
単板１の表面に塗布し（図(D) ）、そして然る後、その
上に、ポリウレタン樹脂塗料（固形分塗布量 10 g/m2）
をさらに塗布して塗料膜１０を形成することにより（図
(E) ）、防燃性銘木化粧シート１を作り上げた（図
１）。この手順における押出しラミネートには、一回で
総ての積層要素をラミネートする手法の他、より好まし
くは、例えば最初にガラス繊維不織布（グラスパーＧＨ
Ｎ−２５）６と第２の接着性樹脂（ＥＡＡ）７と紙８と
をラミネートし、続いてこのラミネート物のガラス繊維
不織布６の上に第１の接着性樹脂（ＥＡＡ）５をラミネ
ートするという連続ラミネート方式が採用される。 手順(B) 図４および図５に示すように、最初に、市販のペレット
状ＥＡＡ樹脂粒子（ブロム系難燃剤混入）、紙（坪量３
０ｇ／ｍ2 ）、およびガラス繊維不織布（グラスパーＧ
ＨＮ−２５）を準備し、次いで、押出しラミネート法に
従い、紙（坪量３７ｇ／ｍ2 ）４：難燃剤が混入された
第１の接着性樹脂（ＥＡＡ）層（厚さ４０μｍ）５：坪
量２５ｇ／ｍ2 のガラス繊維不織布（グラスパーＧＨＮ
−２５）６：難燃剤が混入された第２の接着性樹脂（Ｅ
ＡＡ）層（厚さ４０μｍ）７：紙（坪量３０ｇ／ｍ2 ）
８よりなる積層体１３を成形し（図(A) ）、次に酢酸ビ
ニルアクリル共重合体接着剤３を積層体１３表面の紙４
の上に適量塗布し（図(B)）、続いて銘木単板（厚さ
０．２４ｍｍの楢突板）２をその上にオーバーレイし
（図(C) ）、そしてこれら全体を熱圧締することにより
一体に成形し（図(D) ）、その後必要により、サンドペ
ーパー＃ 240を用いて単板２の表面を研磨し、続いて、
難燃剤（燐・窒素化合物）９を単板１の表面に塗布し
（図(E) ）、そして然る後、その上に、ポリウレタン樹
脂塗料（固形分塗布量 10 g/m2）をさらに塗布して塗料
膜１０を形成することにより（図(F) ）、防燃性銘木化
粧シート１を作り上げた（図１）。この手順における押
出しラミネートには、一回で総ての積層要素をラミネー
トする手法の他、より好ましくは、例えば、最初にガラ
ス繊維不織布（グラスパーＧＨＮ−２５）６と第２の接
着性樹脂（ＥＡＡ）７と紙８とをラミネートし、続いて
このラミネート物のガラス繊維不織布６の上に第１の接
着性樹脂（ＥＡＡ）５および紙４を同時にラミネートす
るという連続ラミネート方式が採用される。 手順(C) 最初に、紙（坪量３０ｇ／ｍ2 ）およびガラス繊維不織
布（グラスパーＧＨＮ−２５）を準備するとともに、イ
ンフレーション法等によりＥＡＡ樹脂フィルム（ブロム
系難燃剤混入）を作り、次いで、熱圧ラミネート法に従
い、一回のラミネートまたは連続ラミネートにより、難
燃剤が混入された第１の接着性樹脂（ＥＡＡ）層（厚さ
４０μｍ）：坪量２５ｇ／ｍ2 のガラス繊維不織布（グ
ラスパーＧＨＮ−２５）：難燃剤が混入された第２の接
着性樹脂（ＥＡＡ）層（厚さ４０μｍ）：紙（坪量３０
ｇ／ｍ2 ）よりなる積層体（図示せず）を成形し、また
他方で熱圧接着（ 110℃× 7kg/cm2× 3分の条件による
熱圧締）により、銘木単板（厚さ０．２４ｍｍの楢突
板）：酢酸ビニルアクリル共重合体接着剤層：紙（坪量
３７ｇ／ｍ2 ）よりなる単板裏打ちシート（図示せず）
を作り、そして、この積層体と単板裏打ちシートとをホ
ット・コールド連続プレス機の中に入れ、これらを 125
℃× 7kg/cm2×15分の条件で熱圧締し、続いて同じプレ
ス圧を維持したまま、強制冷却により常温に降温するま
で圧締を続け、この熱圧接着により一体に成形し、その
後、必要により、サンドペーパー＃ 240を用いて単板の
表面を研磨し、続いて、難燃剤（燐・窒素化合物）を銘
木単板の表面に塗布し、そして然る後、その上に、ポリ
ウレタン樹脂塗料（固形分塗布量 10 g/m2）をさらに塗
布して塗料膜を形成することにより、防燃性銘木化粧シ
ートを作り上げた。また、別の変法として、熱圧ラミネ
ート法に従い、一回のラミネートまたは連続ラミネート
により、紙（坪量３７ｇ／ｍ2 ）：難燃剤が混入された
第１の接着性樹脂（ＥＡＡインフレーションフィルム）
層（厚さ４０μｍ）：坪量２５ｇ／ｍ2 のガラス繊維不
織布（グラスパーＧＨＮ−２５）：難燃剤が混入された
第２の接着性樹脂（ＥＡＡインフレーションフィルム）
層（厚さ４０μｍ）：紙（坪量３０ｇ／ｍ2 ）よりなる
積層体（図示せず）を成形し、次に、酢酸ビニルアクリ
ル共重合体接着剤をこの積層体の紙の上に適量塗布し、
続いて銘木単板（厚さ０．２４ｍｍの楢突板）をその上
にオーバーレイし、そしてこれら全体を熱圧締すること
により一体に成形し、その後必要により、サンドペーパ
ー＃ 240を用いて単板の表面を研磨し、続いて、難燃剤
（燐・窒素化合物）を単板の表面に塗布し、そして然る
後、その上に、ポリウレタン樹脂塗料（固形分塗布量 1
0 g/m2）をさらに塗布して塗料膜を形成することによ
り、防燃性銘木化粧シートを作り上げることもできる。The decorative sheet 1 of this embodiment could be manufactured, for example, according to the following procedures (A), (B) and (C). Procedure (A) As shown in FIGS. 2 and 3, first, commercially available EAA resin particles in the form of pellets (containing a bromo-based flame retardant), paper (basis weight 30 g / m 2 ), and glass fiber nonwoven fabric (grasper) GHN-25) and a first adhesive resin (EAA) mixed with a flame retardant according to an extrusion lamination method.
Layer (thickness: 40 μm) 5: Glass fiber nonwoven fabric having a basis weight of 25 g / m 2 (Glasper GHN-25) 6: Second adhesive resin (EAA) layer mixed with a flame retardant (thickness: 40 μm)
7: A laminate 11 made of paper (basis weight 30 g / m 2 ) 8 was formed (FIG. (A)), and on the other hand, hot-press bonding (110 ° C. × 7 kg)
by heat / pressure compression under the condition of / cm 2 × 3 minutes), a single veneer (a 0.24 mm thick veneer) 2: a vinyl acetate acrylic copolymer adhesive layer 3: paper (basis weight 37 g / m 2 ) Then, the laminate 11 and the veneer backing sheet 12 were placed in a hot-cold continuous press machine, and these were placed at 125 ° C. × 7 kg / cm 2. Heat-pressing under the conditions of × 15 minutes, and then, while maintaining the same press pressure, continue pressing until the temperature is reduced to room temperature by forced cooling (Fig.
(C)), integrally formed by this hot-press bonding, and then, if necessary, the surface of the veneer 2 is polished using sandpaper # 240, and then the flame retardant (phosphorus / nitrogen compound) 9 Apply to the surface of veneer 1 (Figure (D)) and then apply a polyurethane resin paint (solids applied 10 g / m 2 )
Is further applied to form a paint film 10 (see FIG.
(E)), a flameproof precious wood decorative sheet 1 was produced (FIG. 1). In the extrusion lamination in this procedure, besides a method of laminating all the laminated elements at one time, more preferably, for example, first, a glass fiber nonwoven fabric (Glasper GH)
N-25) 6, a second adhesive resin (EAA) 7 and paper 8 are laminated, and then a first adhesive resin (EAA) 5 is laminated on the glass fiber nonwoven fabric 6 of the laminate. Is adopted. Procedure (B) As shown in FIGS. 4 and 5, first, commercially available EAA resin particles in the form of pellets (containing a bromo-based flame retardant) and paper (basis weight 3)
0 g / m 2 ), and glass fiber nonwoven fabric (Glaspar G
HN-25) was prepared, and then, according to the extrusion lamination method, paper (basis weight 37 g / m 2 ) 4: first adhesive resin (EAA) layer mixed with a flame retardant (thickness 40 μm) 5: basis weight 25 g / m 2 glass fiber nonwoven fabric (Glasper GHN
-25) 6: The second adhesive resin (E
AA) layer (thickness: 40 μm) 7: paper (basis weight: 30 g / m 2 )
8 is molded (FIG. (A)), and then the vinyl acetate acrylic copolymer adhesive 3 is applied to the paper 4 on the surface of the laminate 13.
(Fig. (B)), followed by overlaying a precious wood veneer (0.24mm thick coarse veneer) 2 thereon (Fig. (C)), and heat-pressing them all. Then, the surface of the veneer 2 is polished with sandpaper # 240 if necessary.
A flame retardant (phosphorus / nitrogen compound) 9 is applied to the surface of the veneer 1 (FIG. (E)), and thereafter, a polyurethane resin paint (solid content applied amount 10 g / m 2 ) is further applied thereon. By coating to form a paint film 10 (FIG. 1F), a flameproof precious wood decorative sheet 1 was made (FIG. 1). In the extrusion lamination in this procedure, in addition to the method of laminating all the laminated elements at one time, more preferably, for example, first, a glass fiber nonwoven fabric (Glasper GHN-25) 6 and a second adhesive resin (EAA) are used. 7) and paper 8 are laminated, and then the first adhesive resin (EAA) 5 and paper 4 are simultaneously laminated on the glass fiber nonwoven fabric 6 of the laminate. Procedure (C) First, paper (basis weight 30 g / m 2 ) and glass fiber non-woven fabric (grasper GHN-25) are prepared, and an EAA resin film (brominated flame retardant is mixed) is formed by an inflation method or the like. A first adhesive resin (EAA) layer (thickness: 40 μm) mixed with a flame retardant by a single lamination or a continuous lamination according to a hot-pressure lamination method: a glass fiber nonwoven fabric having a basis weight of 25 g / m 2 (Glasper GHN) -25): Second adhesive resin (EAA) layer mixed with a flame retardant (thickness: 40 μm): Paper (basis weight: 30)
g / m 2 ), and, on the other hand, a precious wood veneer (thickness: 110 ° C. × 7 kg / cm 2 × 3 minutes) by hot-pressure bonding. 0.24 mm veneer): vinyl acetate acrylic copolymer adhesive layer: veneer backing sheet (not shown) made of paper (basis weight 37 g / m 2 )
And place the laminate and veneer backing sheet in a hot-cold continuous press and
C. × 7 kg / cm 2 × 15 minutes hot-pressing, then, while maintaining the same press pressure, continue to press down until the temperature is reduced to room temperature by forced cooling, molded integrally by this hot-press bonding, Thereafter, if necessary, the surface of the veneer is polished using sandpaper # 240, and then a flame retardant (phosphorus / nitrogen compound) is applied to the surface of the veneer veneer, and thereafter, A polyurethane resin paint (solid content applied amount: 10 g / m 2 ) was further applied to form a paint film, thereby producing a flame-resistant precious wood decorative sheet. As another modification, paper (basis weight: 37 g / m 2 ): a first adhesive resin mixed with a flame retardant (EAA blown film) by one-time lamination or continuous lamination according to a hot-pressure lamination method.
Layer (thickness: 40 μm): Glass fiber nonwoven fabric having a basis weight of 25 g / m 2 (Glasper GHN-25): Second adhesive resin mixed with a flame retardant (EAA blown film)
Layer (thickness: 40 μm): Form a laminate (not shown) consisting of paper (basis weight 30 g / m 2 ), then apply an appropriate amount of vinyl acetate acrylic copolymer adhesive on the paper of this laminate. Apply,
Subsequently, a precious wood veneer (oak veneer having a thickness of 0.24 mm) is overlaid thereon, and the whole is integrally formed by hot pressing, and thereafter, if necessary, veneer using sandpaper # 240. The surface of the veneer is polished, and then a flame retardant (phosphorus / nitrogen compound) is applied to the surface of the veneer, and thereafter, a polyurethane resin paint (solid content 1
0 g / m 2 ) can be further applied to form a paint film, thereby producing a flame-resistant precious wood decorative sheet.
【００２４】実施例２ この実施例は、防燃性銘木化粧板に関する。これは、図
示しないが、実施例１の防燃性銘木化粧シートが木質系
基材（合板、ＭＤＦ等）の上に貼着されてなる化粧板で
ある。実施例１の化粧シートも、実施例２の化粧板も、
高い難燃性を有し、満足な防火性能を発揮するものであ
った。このことは、以下の試験例の結果からも確認する
ことができた。 Example 2 This example relates to a flame-resistant decorative wood veneer. Although not shown, this is a decorative board obtained by sticking the flame-resistant precious wood decorative sheet of Example 1 on a wooden base material (plywood, MDF, etc.). Neither the decorative sheet of Example 1 nor the decorative plate of Example 2
It had high flame retardancy and exhibited satisfactory fire protection performance. This was also confirmed from the results of the following test examples.
【００２５】比較例 この例の防燃性銘木化粧シートは、ガラス繊維材６の代
わりにアルミニウム箔（厚さ１５μｍ）を使用した点を
除いて、実施例１の防燃性銘木化粧シートと同一の材料
および積層構成よりなる。この比較例の化粧シートは、
実施例１で記載した製法に準じて作られた。COMPARATIVE EXAMPLE The decorative sheet of the fireproof precious wood of this example is the same as the decorative sheet of the fireproof precious wood of Example 1 except that the glass fiber material 6 was replaced with an aluminum foil (thickness: 15 μm). And a laminated structure. The decorative sheet of this comparative example is
It was produced according to the production method described in Example 1.
【００２６】試験例１：昭和59年建設省告示第1372号お
よび JIS A 1321 に従う表面試験 実施例および比較例の防燃性銘木化粧シートについてそ
れぞれ、防火材料の昭和59年建設省告示第1372号および
JIS A 1321 に従う表面試験を以下のとおり行ない、そ
の中の加熱試験の結果より、防火性能、特に火炎伝播特
性に関して両者を比較してみた。なお、この試験より、
排気温度および標準温度についてそれぞれ試験開始から
の経時的な変化を表わすところの排気温度曲線および標
準温度曲線のグラフが得られる。本発明において、火炎
伝播特性とは、試験開始から３分後までの期間内（３分
以内はガスバーナーの熱源のみ）における排気温度曲線
と標準温度曲線との温度差を意味し（つまり火炎伝播特
性Ｅ＝排気温度−標準温度（℃））、そして図６に示す
ように、上記の３分の期間において排気温度曲線ａが標
準温度曲線ｂより下回っているときには、排気温度曲線
ａがその上方の標準温度曲線ｂに最も接近している部位
における排気温度と標準温度の温度差（マイナス値）を
いい、また図７に示すように、上記の３分の期間におい
て排気温度曲線ａが標準温度曲線ｂより上回っていると
きには、排気温度曲線ａが標準温度曲線ｂより上回って
いる域のうち該曲線ｂより最も離れている部位における
排気温度と標準温度の温度差（プラス値）をいう。従っ
て、火炎伝播特性は−５０℃が最小であり、通常それよ
り大きい値で表わされる。この火炎伝播特性がマイナス
値であってかつその絶対値がより大きい程、火炎伝播は
より発生しにくく、防火材料としてより適することを意
味し、反対に、火炎伝播特性がプラス値であるとき、火
炎伝播が起き、かつ、火炎伝播特性の値がより大きい
程、火炎伝播はより発生し易く、防火材料として不合格
であることを意味する。 −防燃性銘木化粧シートの積層構成− 各防燃性銘木化粧シートは、次の構成よりなる積層体を
圧着成形してなる。 防燃性銘木化粧シートＡ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布／第二の接着性樹脂層／紙２ 防燃性銘木化粧シートＢ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／アル
ミニウム箔／第二の接着性樹脂層／紙２ −防燃性銘木化粧シートの各材料− 銘木単板：カバ単板、気乾重量１２５ｇ／ｍ2 、表面塗
装無し 接着剤層：酢酸ビニル系接着剤、塗布量（固形分）２０
ｇ／ｍ2 紙１：坪量３７ｇ／ｍ2 紙２：坪量３０ｇ／ｍ2 第一の接着性樹脂層：ブロム系難燃剤含有のエチレン−
酢酸アクリル共重合体樹脂フィルム、厚さ４０μｍ 第二の接着性樹脂層：ブロム系難燃剤含有のエチレン−
酢酸アクリル共重合体樹脂フィルム、厚さ４０μｍ ガラス繊維不織布：坪量２５ｇ／ｍ2 アルミニウム箔：厚さ１５μｍ −表面試験に用いた基材− 法定準不燃材料の石膏ボード（９．５mm厚）および法定
不燃材料の石綿パーライト板（１０mm厚）の２種類の基
材を使用した。 −表面試験の手順− 防燃性銘木化粧シートＡ、Ｂ各６枚を上記２種の基材の
表面に各基材に３枚ずつ貼着し、そして作成された試験
体の加熱試験を行なった。その詳細は、昭和59年建設省
告示第1372号および JIS A 1321 に規定する手順および
条件に従うものとした。なお、該化粧シートの貼着に
は、酢酸ビニルエマルジョン接着剤（固形分の塗布量４
０ｇ／ｍ2 ）が使用された。 Test Example 1 : Surface test according to Notification No. 1372 of Ministry of Construction and JIS A 1321 in 1984 Regarding the fireproof precious wood decorative sheets of Examples and Comparative Examples, notification No. 1372 of Ministry of Construction in 1984 for fireproof materials, respectively. and
A surface test according to JIS A 1321 was performed as follows, and based on the results of the heating test, the two were compared with respect to fire prevention performance, particularly flame propagation characteristics. From this test,
A graph of an exhaust gas temperature curve and a graph of a standard temperature curve representing changes with time from the start of the test for the exhaust gas temperature and the standard temperature is obtained. In the present invention, the flame propagation characteristic means a temperature difference between an exhaust temperature curve and a standard temperature curve within a period of 3 minutes after the start of the test (within 3 minutes only the heat source of the gas burner) (that is, flame propagation). (Characteristic E = exhaust gas temperature−standard temperature (° C.)), and as shown in FIG. 6, when the exhaust gas temperature curve “a” is lower than the standard temperature curve “b” in the above-mentioned three-minute period, the exhaust gas temperature curve “a” is higher than the standard temperature curve “b”. Means the temperature difference (minus value) between the exhaust temperature and the standard temperature at the portion closest to the standard temperature curve b. As shown in FIG. When the temperature is higher than the curve b, it means a temperature difference (plus value) between the exhaust temperature and the standard temperature at a part farthest from the curve b in a region where the exhaust temperature curve a is higher than the standard temperature curve b. Therefore, the flame propagation characteristic is the minimum at -50 ° C, and is usually expressed by a value larger than -50 ° C. When the flame propagation characteristic is a negative value and the absolute value is larger, the flame propagation is less likely to occur, which means that the flame propagation material is more suitable, and conversely, when the flame propagation characteristic is a positive value, The greater the value of the flame propagation property occurs and the value of the flame propagation property, the more likely the flame propagation occurs, which means that the material is rejected as a fire protection material. -Laminated Structure of Flame-Retardant Precious Wood Decorative Sheet- Each of the flame-retardant precious wood decorative sheets is formed by pressure-bonding a laminate having the following configuration. Flameproof precious wood decorative sheet A: Precious wood veneer / adhesive layer / paper 1 / first adhesive resin layer / glass fiber nonwoven fabric / second adhesive resin layer / paper 2 Flameproof precious wood decorative sheet B: precious wood Veneer / Adhesive layer / Paper 1 / First adhesive resin layer / Aluminum foil / Second adhesive resin layer / Paper 2 -Each material of flameproof precious wood decorative sheet- Precious wood veneer: birch veneer, Air-dry weight 125 g / m 2 , no surface coating Adhesive layer: vinyl acetate-based adhesive, coating amount (solid content) 20
g / m 2 paper 1: basis weight 37 g / m 2 paper 2: basis weight 30 g / m 2 First adhesive resin layer: bromo-based flame retardant-containing ethylene-
Acrylic acetate copolymer resin film, thickness of 40 μm Second adhesive resin layer: ethylene-containing bromo-based flame retardant
Acrylic acetate copolymer resin film, thickness 40 μm, glass fiber nonwoven fabric: basis weight 25 g / m 2 aluminum foil: thickness 15 μm-base material used for surface test-gypsum board (9.5 mm thickness) of legally quasi-noncombustible material and Two types of base materials of legally incombustible asbestos perlite board (10 mm thick) were used. -Surface test procedure- Three pieces of each of the flame retardant precious wood decorative sheets A and B are stuck on the surfaces of the above two types of base materials three by three, and a heating test of the prepared test body is performed. Was. The details followed the procedures and conditions specified in the Ministry of Construction Notification 1372 and JIS A 1321. In addition, a vinyl acetate emulsion adhesive (solid content application amount 4
0 g / m 2 ).
【００２７】−表面試験の結果− 防燃性銘木化粧シートＡ、Ｂ各６枚（Ａ−１ないしＡ−
６、Ｂ−１ないしＢ−６）について加熱試験で得られた
温度曲線を図８ないし図１９のグラフにそれぞれ示す。
これらのグラフは、試験体の排気温度曲線ａを標準温度
曲線ｂと対比して示すものである。しかして、表面試験
の結果は、以下の表１、表２にまとめて表される。 図８ないし図１９に示す各排気温度曲線、並びに、表１
および表２よりわかるように、ガラス繊維不織布を含む
防燃性銘木化粧シートは、これを不燃基材の上に貼着し
た試験体の場合の火炎伝播特性が平均値で−２７℃とな
り、またこれを準不燃基材の上に貼着した試験体の場合
の火炎伝播特性が平均値で−２４℃となり、どちらも、
火炎伝播がほとんど発生せず、かつ、準不燃の性能を有
する。これに対して、アルミニウム箔を含む防燃性銘木
化粧シートは、これを不燃基材の上に貼着した試験体の
場合の火炎伝播特性が総てプラス値となり、またこれを
準不燃基材の上に貼着した試験体の場合の火炎伝播特性
が平均値で−１５℃となり、火炎伝播がかなり発生す
る。特に、アルミニウム箔を含む防燃性銘木化粧シート
を準不燃基材の上に貼着した試験体にあっては、その排
気温度曲線が表面試験（加熱試験）の開始後３分以内に
標準温度曲線を越えており、明らかに、準不燃の性能を
満たすものでない。-Results of Surface Test- Six sheets of A and B flame-retardant precious wood decorative sheets (A-1 to A-
6, B-1 to B-6) are shown in the graphs of FIGS. 8 to 19, respectively.
These graphs show the exhaust temperature curve a of the test body in comparison with the standard temperature curve b. The results of the surface test are summarized in Tables 1 and 2 below. Each exhaust temperature curve shown in FIGS. 8 to 19 and Table 1
As can be seen from Table 2 and Table 2, the flame-retardant precious wood decorative sheet containing the glass fiber nonwoven fabric has an average flame propagation characteristic of -27 ° C. in the case of a test piece in which this is adhered on a non-combustible base material. The flame propagation characteristics in the case of a test specimen stuck on a quasi-noncombustible substrate were -24 ° C on average,
Flame propagation hardly occurs and it has semi-flammable performance. On the other hand, the flame retardant precious wood decorative sheet containing aluminum foil has a positive flame propagation characteristic in the case of a test piece in which this is adhered on a non-combustible base material, and the flammable non-combustible base material The flame propagation characteristic of the test piece stuck on the surface becomes −15 ° C. on average, and considerable flame propagation occurs. In particular, in the case of a specimen in which a flame-resistant precious wood decorative sheet containing an aluminum foil is stuck on a quasi-non-combustible substrate, the exhaust temperature curve has a standard temperature within 3 minutes after the start of the surface test (heating test). It is beyond the curve and clearly does not meet the quasi-noncombustibility performance.
【００２８】試験例２：寸法安定性の試験 ガラス繊維不織布の含有量が異なる実施例の各防燃性銘
木化粧シートおよび比較例の防燃性銘木化粧シートにつ
いてそれぞれ、膨潤率の測定試験を行ない、その結果よ
り、寸法安定性に関して、それらを対比してみた。−試
験の方法−各々の防燃性銘木化粧シートより、図２０に
示されるストリップ形状の試験体（同図に表わす縦・横
の寸法を有する）を作成する。そして、試験体を常温の
室内に２４時間の間放置し、次いで、点Ｘおよび点Ｙを
凡そ１８０ｍｍの間隔にて試験体の表面に記し、続い
て、間隔Ｘ−Ｙの長さ（ｍｍ）を小数点以下２桁の位ま
で正確に計測する（これを寸法Ｉとする。）。その後、
試験体を２０℃の水の中に３０分間の間浸漬し、次い
で、これを水中より取り出し、そして当初と同様に間隔
Ｘ−Ｙの長さ（ｍｍ）を小数点以下２桁の位まで正確に
計測する（これを寸法IIとする。）。膨潤率は、次の式
より算出される。 膨潤率（％）＝｛（寸法II÷寸法Ｉ）−１｝×１００ 算出された膨潤率がより低いほど、防燃性銘木化粧シー
トの寸法安定性がより高いことを表わす。 −防燃性銘木化粧シートの積層構成− 各防燃性銘木化粧シートは、次の構成よりなる積層体を
圧着成形してなる。 防燃性銘木化粧シートＣ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２０ｇ／ｍ2 ）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＤ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２５ｇ／ｍ2 ）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＦ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／アル
ミニウム箔（坪量４０ｇ／ｍ2 ）／第二の接着性樹脂層
／紙２ −防燃性銘木化粧シートの各材料− 銘木単板：カバ単板、気乾重量９３ｇ／ｍ2 、表面塗装
無し 接着剤層：酢酸ビニル系接着剤、塗布量（固形分）２０
ｇ／ｍ2 紙１：坪量３７ｇ／ｍ2 紙２：坪量３０ｇ／ｍ2 第一の接着性樹脂層：ブロム系難燃剤含有のエチレン−
酢酸アクリル共重合体樹脂フィルム、厚さ４０μｍ 第二の接着性樹脂層：ブロム系難燃剤含有のエチレン−
酢酸アクリル共重合体樹脂フィルム、厚さ４０μｍ ガラス繊維不織布：坪量２０、２５ｇ／ｍ2 アルミニウム箔：坪量４０ｇ／ｍ2 Test Example 2 Test of Dimensional Stability A swelling ratio measurement test was carried out on each of the fire-resistant decorative wood decorative sheets of Examples having different contents of the glass fiber nonwoven fabric and the fire-resistant decorative wood decorative sheet of Comparative Example. Based on the results, the dimensional stability was compared. -Test method-From each flame-resistant precious wood decorative sheet, a strip-shaped specimen (having vertical and horizontal dimensions shown in Fig. 20) is prepared. Then, the specimen is left in a room at room temperature for 24 hours, and then points X and Y are marked on the surface of the specimen at intervals of about 180 mm, and subsequently, the length (mm) of the interval XY Is accurately measured to two digits after the decimal point (this is referred to as dimension I). afterwards,
The test specimen is immersed in water at 20 ° C. for 30 minutes, then removed from the water, and the length (mm) of the interval X-Y is accurately set to two decimal places as before. Measure (this is dimension II). The swelling ratio is calculated from the following equation. Swelling ratio (%) = {(dimension II ÷ dimension I) -1} × 100 The lower the calculated swelling ratio, the higher the dimensional stability of the flameproof precious wood decorative sheet. -Laminated Structure of Flame-Retardant Precious Wood Decorative Sheet- Each of the flame-retardant precious wood decorative sheets is formed by pressure-bonding a laminate having the following configuration. Flame retardant precious wood decorative sheet C: Precious wood veneer / adhesive layer / paper / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 20 g / m 2 ) / second adhesive resin layer / paper 2 Flammable precious wood decorative sheet D: Precious wood veneer / adhesive layer / paper / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 25 g / m 2 ) / second adhesive resin layer / paper 2 Decorative precious wood decorative sheet F: Precious wood veneer / adhesive layer / paper / first adhesive resin layer / aluminum foil (basis weight 40 g / m 2 ) / second adhesive resin layer / paper 2-Flameproof Each material of precious wood decorative sheet-Precious wood veneer: birch veneer, air-dry weight 93 g / m 2 , no surface coating Adhesive layer: vinyl acetate adhesive, coating amount (solid content) 20
g / m 2 paper 1: basis weight 37 g / m 2 paper 2: basis weight 30 g / m 2 First adhesive resin layer: bromo-based flame retardant-containing ethylene-
Acrylic acetate copolymer resin film, thickness of 40 μm Second adhesive resin layer: ethylene-containing bromo-based flame retardant
Acrylic copolymer resin film acetate, thickness 40μm glass fiber nonwoven fabric: basis weight 20,25g / m 2 aluminum foil: basis weight 40 g / m 2
【００２９】−試験の結果− 防燃性銘木化粧シートＣ、ＤおよびＦの各々３枚につい
て膨潤率の値を算出した。その結果は、以下の表３にま
とめて表される。 この表より、ガラス繊維不織布を含む防燃性銘木化粧シ
ートは、ガラス繊維不織布の含有量がより増大する程、
寸法安定性がより高まることがわかる。また、坪量２０
ｇ／ｍ2 のガラス繊維不織布を含む防燃性銘木化粧シー
トは、坪量４０ｇ／ｍ2 のアルミニウム箔を含む防燃性
銘木化粧シートに匹敵する良好な寸法安定性を有するも
のとわかる。-Results of Test- The value of the swelling ratio was calculated for each of the three fire-resistant decorative wood decorative sheets C, D and F. The results are summarized in Table 3 below. From this table, the flame retardant precious wood decorative sheet containing the glass fiber nonwoven fabric, as the content of the glass fiber nonwoven fabric increases,
It can be seen that the dimensional stability is further improved. In addition, basis weight 20
It can be understood that the flameproof precious wood decorative sheet containing g / m 2 glass fiber nonwoven fabric has good dimensional stability comparable to that of the flameproof precious wood decorative sheet including aluminum foil having a basis weight of 40 g / m 2 .
【００３０】試験例３：昭和59年建設省告示第1372号お
よび JIS A 1321 に従う表面試験 ガラス繊維不織布の含有量が異なる実施例の各防燃性銘
木化粧シートについてそれぞれ、防火材料の昭和59年建
設省告示第1372号および JIS A 1321 に従う表面試験を
以下のとおり行ない、その中の加熱試験の結果より、防
火性能、特に火炎伝播特性に関してそれらを対比してみ
た。 −防燃性銘木化粧シートの積層構成− 各防燃性銘木化粧シートは、次の構成よりなる積層体を
圧着成形してなる。 防燃性銘木化粧シートＧ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２０ｇ／ｍ2 ）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＨ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２５ｇ／ｍ2 ）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＩ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量３０ｇ／ｍ2 ）／第二の接着性樹脂
層／紙２ −防燃性銘木化粧シートの各材料− 銘木単板：カバ単板、気乾重量１０５ｇ／ｍ2 、表面塗
装無し 接着剤層：酢酸ビニル系接着剤、塗布量（固形分）２０
ｇ／ｍ2 紙１：坪量３７ｇ／ｍ2 紙２：坪量３０ｇ／ｍ2 第一の接着性樹脂層：ブロム系難燃剤含有のエチレン−
酢酸アクリル共重合体樹脂フィルム、厚さ４０μｍ 第二の接着性樹脂層：ブロム系難燃剤含有のエチレン−
酢酸アクリル共重合体樹脂フィルム、厚さ４０μｍ ガラス繊維不織布：坪量２０、２５、３０ｇ／ｍ2 −表面試験に用いた基材− 法定準不燃材料の石膏ボード（９．５mm厚）を基材とし
て使用した。 −表面試験の手順− 防燃性銘木化粧シートＧ、Ｈ、Ｉ各２枚を上記基材の表
面に貼着し、そして作成された試験体の加熱試験を行な
った。その詳細は、昭和59年建設省告示第1372号および
JIS A 1321 に規定する手順および条件に従うものとし
た。なお、これら化粧シートの貼着には、酢酸ビニルエ
マルジョン接着剤（固形分の塗布量４０ｇ／ｍ2 ）が使
用された。 Test Example 3 : Surface test according to Notification No. 1372 of Ministry of Construction and JIS A 1321 in 1984 For each of the fireproof precious wood decorative sheets of Examples having different contents of glass fiber nonwoven fabric, the fireproof material was used in 1984. The following surface tests were conducted in accordance with the Ministry of Construction Notification No. 1372 and JIS A 1321, and based on the results of the heating tests, fire protection performance, especially flame propagation characteristics, were compared. -Laminated Structure of Flame-Retardant Precious Wood Decorative Sheet- Each of the flame-retardant precious wood decorative sheets is formed by pressure-bonding a laminate having the following configuration. Flame retardant precious wood decorative sheet G: Precious wood veneer / adhesive layer / paper / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 20 g / m 2 ) / second adhesive resin layer / paper 2 Flammable precious wood decorative sheet H: Precious wood veneer / adhesive layer / paper 1 / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 25 g / m 2 ) / second adhesive resin layer / paper 2 Decorative precious wood decorative sheet I: Precious wood veneer / adhesive layer / paper 1 / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 30 g / m 2 ) / second adhesive resin layer / paper 2-fireproof Each material of the nature precious wood decorative sheet-Precious wood veneer: birch veneer, air-dried weight 105 g / m 2 , no surface coating Adhesive layer: vinyl acetate adhesive, coating amount (solid content) 20
g / m 2 paper 1: basis weight 37 g / m 2 paper 2: basis weight 30 g / m 2 First adhesive resin layer: bromo-based flame retardant-containing ethylene-
Acrylic acetate copolymer resin film, thickness of 40 μm Second adhesive resin layer: ethylene-containing bromo-based flame retardant
Acrylic acetate copolymer resin film, thickness 40 μm Glass fiber non-woven fabric: basis weight 20, 25, 30 g / m 2- substrate used for surface test-gypsum board (9.5 mm thickness) of legally quasi-noncombustible material Used as -Surface Test Procedure- Two pieces each of the fireproof precious wood decorative sheets G, H, and I were attached to the surface of the base material, and a heating test was performed on the prepared specimen. For details, see Notification No. 1372 of the Ministry of Construction in 1984 and
The procedure and conditions specified in JIS A 1321 were followed. Note that a vinyl acetate emulsion adhesive (solid content application amount 40 g / m 2 ) was used for attaching these decorative sheets.
【００３１】−表面試験の結果− 防燃性銘木化粧シートＧ、Ｈ、Ｉ各２枚（Ｇ−１、Ｇ−
２、Ｈ−１、Ｈ−２、Ｉ−１、Ｉ−２）について加熱試
験を行ない、それより試験体の排気温度曲線を得た。し
かして、表面試験の結果は、以下の表４、表５にまとめ
て表される。 表４および表５より、ガラス繊維不織布を含む防燃性銘
木化粧シートはいずれも、これを準不燃基材の上に貼着
した試験体において、火炎伝播特性が−２３℃〜−３１
℃となり、火炎伝播がほとんど発生せず、準不燃の性能
を有するものであるが、ガラス繊維不織布の含有量をよ
り増加する程、ｔｄθの平均値がより一層大きくなるこ
とがわかる。-Results of Surface Test- Two pieces of flame-resistant precious wood decorative sheets G, H, I (G-1, G-
2, H-1, H-2, I-1, I-2) were subjected to a heating test, from which an exhaust temperature curve of the test specimen was obtained. The results of the surface test are summarized in Tables 4 and 5 below. From Tables 4 and 5, all of the flame-resistant precious wood decorative sheets containing the glass fiber non-woven fabric have a flame propagation characteristic of −23 ° C. to −31 in the test piece in which this is adhered on the quasi-non-combustible substrate.
° C, the flame propagation hardly occurs, and the quasi-nonflammable performance is obtained. However, it can be seen that the average value of tdθ increases as the content of the glass fiber nonwoven fabric increases.
【００３２】[0032]
【発明の効果】以上説明したように、本発明によれば、
積層要素としてアルミニウム箔等の金属箔を採用しなく
とも、高い難燃性を有し、防火材料として準不燃の性能
（昭和５９年９月２９日建設省告示第１３７２号に基づ
く）を発揮できるのは勿論のこと、火災等において火炎
伝播の現象が起きにくく、壁装材料協会制定の紙壁紙２
級の防火性能を有し、防火材料として一層優れており、
その上、シート材料間の接着性能が経時的に劣化せず、
耐久性にも大変優れているところの防燃性銘木化粧シー
トが提供される。また、本発明によれば、本発明の防燃
性銘木化粧シートの使用により、大変高い防火性能を有
する防燃性銘木化粧板が提供される。さらに、本発明の
製造方法によれば、本発明の防燃性銘木化粧シートを確
実にかつ生産性高く製造することができるという効果が
得られる。As described above, according to the present invention,
Even if metal foil such as aluminum foil is not used as the laminated element, it has high flame retardancy and can exhibit semi-incombustible performance (based on Ministry of Construction Notification No. 1372 on September 29, 1984) as a fire protection material. Needless to say, flame propagation phenomena are unlikely to occur in fires and the like.
It has a class fire protection performance and is more excellent as a fire protection material.
In addition, the adhesive performance between the sheet materials does not deteriorate over time,
There is provided a flameproof precious wood decorative sheet which is very excellent in durability. Further, according to the present invention, there is provided a decorative board made of a fire-resistant precious wood having extremely high fire protection performance by using the decorative sheet of the fire-proof precious wood of the present invention. Further, according to the production method of the present invention, there is obtained an effect that the decorative sheet for fireproof precious wood of the present invention can be produced reliably and with high productivity.
【図１】本発明の実施例の防燃性銘木化粧シートを示す
断面図である。FIG. 1 is a cross-sectional view illustrating a flameproof precious wood decorative sheet according to an embodiment of the present invention.
【図２】図(A) ないし図(C) は、図１の防燃性銘木化粧
シートの製造工程の前半を示す図である。FIGS. 2 (A) to 2 (C) are diagrams showing the first half of the manufacturing process of the flameproof precious wood decorative sheet of FIG. 1;
【図３】図(C) ないし図(E) は、図１の防燃性銘木化粧
シートの製造工程の後半を示す図である。FIGS. 3 (C) to 3 (E) are diagrams showing the latter half of the manufacturing process of the decorative sheet for flameproof precious wood of FIG. 1;
【図４】図(A) ないし図(C) は、図１の防燃性銘木化粧
シートの別の製造工程の前半を示す図である。4 (A) to 4 (C) are diagrams showing the first half of another manufacturing process of the flameproof precious wood decorative sheet of FIG. 1;
【図５】図(D) ないし図(F) は、図１の防燃性銘木化粧
シートの別の製造工程の後半を示す図である。5 (D) to FIG. 5 (F) are views showing the latter half of another manufacturing process of the flameproof precious wood decorative sheet of FIG. 1;
【図６】JIS A 1321 に従う表面試験より得られるグラ
フであって、火炎伝播特性の定義（マイナス値の場合）
を説明するための模範的な曲線を示すグラフである。FIG. 6 is a graph obtained from a surface test according to JIS A 1321, which is a definition of a flame propagation characteristic (in the case of a negative value).
5 is a graph showing an exemplary curve for explaining the following.
【図７】JIS A 1321 に従う表面試験より得られるグラ
フであって、火炎伝播特性の定義（プラス値の場合）を
説明するための模範的な曲線を示すグラフである。FIG. 7 is a graph obtained from a surface test according to JIS A 1321, showing an exemplary curve for explaining the definition of flame propagation characteristics (in the case of a positive value).
【図８】防燃性銘木化粧シート（試料Ａ−１）について
JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 8: Flameproof precious wood decorative sheet (Sample A-1)
4 is a graph showing the results of a surface test according to JIS A 1321.
【図９】防燃性銘木化粧シート（試料Ａ−２）について
JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 9: Flameproof precious wood decorative sheet (Sample A-2)
4 is a graph showing the results of a surface test according to JIS A 1321.
【図１０】防燃性銘木化粧シート（試料Ａ−３）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 10 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample A-3).
【図１１】防燃性銘木化粧シート（試料Ａ−４）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 11 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample A-4).
【図１２】防燃性銘木化粧シート（試料Ａ−５）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 12 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample A-5).
【図１３】防燃性銘木化粧シート（試料Ａ−６）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 13 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample A-6).
【図１４】防燃性銘木化粧シート（試料Ｂ−１）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 14 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample B-1).
【図１５】防燃性銘木化粧シート（試料Ｂ−２）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 15 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample B-2).
【図１６】防燃性銘木化粧シート（試料Ｂ−３）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 16 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample B-3).
【図１７】防燃性銘木化粧シート（試料Ｂ−４）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 17 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample B-4).
【図１８】防燃性銘木化粧シート（試料Ｂ−５）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 18 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample B-5).
【図１９】防燃性銘木化粧シート（試料Ｂ−６）につい
て JIS A 1321 に従う表面試験の結果を示すグラフであ
る。FIG. 19 is a graph showing the results of a surface test according to JIS A 1321 for a flameproof precious wood decorative sheet (sample B-6).
【図２０】防燃性銘木化粧シートについての寸法安定性
の試験に使用されたストリップを示す図である。FIG. 20 is a view showing a strip used for a dimensional stability test on a flameproof precious wood decorative sheet.
１ 防燃性銘木化粧シート ２ 銘木単板 ３ 接着剤層 ４ 紙または不織布 ５ 難燃剤が混入された第１の接着性樹脂層 ６ ガラス繊維不織布、ガラス繊維紙もしくはガラス
繊維織布またはこれらの組合せ ７ 難燃剤が混入された第２の接着性樹脂層 ８ 紙または不織布 ９ 難燃剤 １０ 塗料膜 １１ 積層体 １２ 単板裏打ちシート １３ 積層体DESCRIPTION OF SYMBOLS 1 Flameproof precious wood decorative sheet 2 Precious wood veneer 3 Adhesive layer 4 Paper or nonwoven fabric 5 First adhesive resin layer mixed with flame retardant 6 Glass fiber nonwoven fabric, glass fiber paper or glass fiber woven fabric or a combination thereof Reference Signs List 7 Second adhesive resin layer mixed with flame retardant 8 Paper or nonwoven fabric 9 Flame retardant 10 Paint film 11 Laminate 12 Single sheet backing sheet 13 Laminate
─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成１０年１月２３日[Submission date] January 23, 1998
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００５[Correction target item name] 0005
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【０００５】[0005]
【発明が解決しようとする課題】しかし、上記の防燃性
銘木化粧シートは、積層要素として金属箔、特にアルミ
ニウム箔を含むことから、熱伝導性が相当に高いものと
なり、よって、実際の火災等においては、火炎伝播の現
象が起きやすいものとなる。かような性質は、防火材料
として望ましくない性質である。従って、火災において
火炎伝播が起きにくい性質のものに改良することが要求
されていた。また、アルミニウム箔等の金属箔は一般に
樹脂フィルムとの接着性が悪い。このため、従来の銘木
化粧シートにあっては、シート材料相互間、特にアルミ
ニウム箔（鉄箔）とこれに隣接する合成樹脂層との間の
接着性能が経時的に弱化するという問題があった。従っ
て、接着性能の面についても、さらに改良すべき必要性
があった。ところで、特開平９−５２３１６号公報、特
開平９−５２３１７号公報および特開平９−５２３１８
号公報などに示されるように、ガラス繊維織布などのガ
ラス繊維材料を一要素として積層成形した木質系合板
は、既に提案されているが、かようなガラス繊維材料を
含む銘木化粧シート、特に防燃性銘木化粧シートは、本
発明者の知るかぎり、未だ提案されておらず、また、そ
のような製品も今現在製造・販売されていない。However, the above-mentioned decorative sheet made of flame-retardant precious wood has a considerably high thermal conductivity since it contains a metal foil, especially an aluminum foil, as a laminated element, and therefore has an actual fire. In such cases, the phenomenon of flame propagation is likely to occur. Such properties are undesirable properties as a fire protection material. Therefore, it has been demanded to improve the property to a property in which flame propagation is unlikely to occur in a fire. Further, a metal foil such as an aluminum foil generally has poor adhesion to a resin film. For this reason, the conventional precious wood decorative sheet has a problem that the adhesive performance between the sheet materials, particularly between the aluminum foil (iron foil) and the synthetic resin layer adjacent thereto, is weakened with time. . Therefore, there is a need to further improve the adhesive performance. Incidentally, JP-A-9-52316, JP-A-9-52317 and JP-A-9-52318
As shown in the publication, a wood-based plywood formed by laminating a glass fiber material such as a glass fiber woven fabric as one element has already been proposed, but a fancy wood decorative sheet containing such a glass fiber material, particularly As far as the present inventor knows, a flameproof precious wood decorative sheet has not yet been proposed, and such a product has not been manufactured or sold at present.
【手続補正２】[Procedure amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１３[Correction target item name] 0013
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００１３】第１および第２の接着性樹脂層は、紙また
は不織布とガラス繊維材との接着一体化を可能とするた
めに、また化粧シートに適度の柔軟性を付与して施工時
下地の凹凸を吸収するために、また化粧シートに十分な
可撓性を与えて曲面部や角部の下地にも適合可能とする
ために、さらにガラス繊維材と一緒になって銘木単板の
あばれ、反りを抑えるために、積層要素とされるもので
ある。本発明で用いる第１および第２の接着性樹脂層
は、同種であっても異種であっても、また各樹脂層は単
層であっても複層であってもよい。その厚さは、１５〜
１００μｍ、好ましくは２０〜５０μｍであり、最も好
ましくは３０〜４５μｍである。接着性樹脂層の例とし
ては、ポリオレフィン共重合体、例えばポリエチレンコ
ポリマー、エチレン−アクリル酸共重合体（ＥＡＡ）、
アイオノマー、ポリアミド樹脂等が挙げることができる
が、これらに限定されず、広範囲にわたって適用するこ
とができる。しかしながら、より好ましくは、エチレン
−アクリル酸共重合体（ＥＡＡ）およびアイオノマーで
あり、最も好ましくは、エチレン−アクリル酸共重合体
（ＥＡＡ）である。The first and second adhesive resin layers are used to bond and integrate the paper or non-woven fabric with the glass fiber material, and to give the decorative sheet an appropriate flexibility so that the decorative sheet can be used as a base material at the time of construction. In order to absorb irregularities and to give the decorative sheet sufficient flexibility so that it can also be applied to the base of curved surfaces and corners, furthermore, together with the glass fiber material, the precious wood veneer is exposed, In order to suppress warpage, it is a laminated element. The first and second adhesive resin layers used in the present invention may be the same or different, and each resin layer may be a single layer or a multilayer. Its thickness is 15
It is 100 μm, preferably 20 to 50 μm, and most preferably 30 to 45 μm. Examples of the adhesive resin layer include polyolefin copolymers such as polyethylene copolymer, ethylene-acrylic acid copolymer (EAA),
Examples thereof include ionomers and polyamide resins, but are not limited thereto, and can be applied over a wide range. However, more preferred are ethylene-acrylic acid copolymers (EAA) and ionomers, most preferred are ethylene-acrylic acid copolymers (EAA).
【手続補正３】[Procedure amendment 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２２[Correction target item name] 0022
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００２２】実施例１ この実施例は、図１に示す防燃性銘木化粧シート１に関
する。これは、上から順に、銘木単板２（厚さ０．１５
〜０２５ｍｍ、重量５０〜１２０ｇ／ｍ２、樹種楢、マ
ホガニー等、各種突板）：接着剤層３（酢酸ビニルアク
リル共重合体接着剤）：紙または不織布４（例えば坪量
３７ｇ／ｍ２の紙）：ブロム系難燃剤が混入された第１
の接着性樹脂層５（厚さ２０〜５０μｍのエチレン−ア
クリル酸共重合体（ＥＡＡ）樹脂層）：ガラス繊維不織
布、ガラス繊維紙もしくはガラス繊維織布またはこれら
の組合せ６（例えばグラスパーＧＨＮ−２５（王子製紙
株式会社製、坪量２５ｇ／ｍ２）：ブロム系難燃剤が混
入された第２の接着性樹脂層７（厚さ２０〜５０μｍの
エチレン−アクリル酸共重合体（ＥＡＡ）樹脂層）：紙
または不織布８（例えば坪量３０ｇ／ｍ２の紙）が積層
され、一体に圧着成形された化粧シートであって、難燃
剤９（燐・窒素化合物）が銘木単板２上に塗布され（そ
の一部は含浸している）、さらに、その上に塗料膜（ウ
レタン樹脂塗膜）１０が形成されている。 Example 1 This example relates to a decorative sheet 1 for flameproof precious wood shown in FIG. This is, in order from the top, precious wood veneer 2 (thickness 0.15
０２025 mm, weight of 50 to 120 g / m 2 , various kinds of veneers such as tree seed oak, mahogany, etc.): adhesive layer 3 (vinyl acetate acrylic copolymer adhesive): paper or nonwoven fabric 4 (for example, paper having a basis weight of 37 g / m 2 ) ): No. 1 with brominated flame retardant
Adhesive resin layer 5 (ethylene-acrylic acid copolymer (EAA) resin layer having a thickness of 20 to 50 μm): glass fiber nonwoven fabric, glass fiber paper or glass fiber woven fabric, or a combination thereof 6 (for example, Grasper GHN-25) (Manufactured by Oji Paper Co., Ltd., basis weight 25 g / m 2 ): the second adhesive resin layer 7 (ethylene-acrylic acid copolymer (EAA) resin layer having a thickness of 20 to 50 μm) mixed with a bromo-based flame retardant ): A decorative sheet in which paper or nonwoven fabric 8 (for example, paper having a basis weight of 30 g / m 2 ) is laminated and integrally press-formed, and a flame retardant 9 (phosphorus / nitrogen compound) is applied on precious wood veneer 2. (Partially impregnated), and a coating film (urethane resin coating film) 10 is formed thereon.
【手続補正４】[Procedure amendment 4]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２６[Correction target item name] 0026
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００２６】試験例１：昭和５９年建設省告示第１３７
２号およびＪＩＳ Ａ １３２１に従う表面試験 実施例および比較例の防燃性銘木化粧シートについてそ
れぞれ、防火材料の昭和５９年建設省告示第１３７２号
およびＪＩＳ Ａ １３２１に従う表面試験を以下のと
おり行ない、その中の加熱試験の結果より、防火性能、
特に火炎伝播特性に関して両者を比較してみた。なお、
この試験より、排気温度および標準温度について試験開
始からの経時的な変化を表わすところの排気温度曲線お
よび標準温度曲線のグラフが得られる。本発明におい
て、火炎伝播特性とは、試験開始から３分後までの期間
内（３分以内はガスバーナーの熱源のみ）における排気
温度曲線と標準温度曲線との温度差を意味し（つまり火
炎伝播特性Ｅ＝排気温度−標準温度（℃））、そして図
６に示すように、上記の３分の期間において排気温度曲
線ａが標準温度曲線ｂより下回っているときには、排気
温度曲線ａが標準温度曲線ｂに最も接近している部位に
おける排気温度と標準温度の温度差（マイナス値）をい
い、また図７に示すように、上記の３分の期間において
排気温度曲線ａが標準温度曲線ｂより上回っているとき
には、排気温度曲線ａが標準温度曲線ｂより最も離れて
いる部位における排気温度と標準温度の温度差（プラス
値）をいう。従って、火炎伝播特性は−５０℃が最小で
あり、通常それより大きい値で表わされる。この火炎伝
播特性がマイナス値であってかつその絶対値がより大き
い程、火炎伝播はより発生しにくく、防火材料としてよ
り適することを意味し、反対に、火炎伝播特性がプラス
値であるとき、火炎伝播が起き、かつ、火炎伝播特性の
値がより大きい程、火炎伝播はより発生し易く、防火材
料として不合格であることを意味する。 −防燃性銘木化粧シートの積層構成− 各防燃性銘木化粧シートは、次の構成よりなる積層体を
圧着成形してなる。 防燃性銘木化粧シートＡ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布／第二の接着性樹脂層／紙２ 防燃性銘木化粧シートＢ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／アル
ミニウム箔／第二の接着性樹脂層／紙２ −防燃性銘木化粧シートの各材料− 銘木単板：カバ単板、気乾重量１２５ｇ／ｍ２、表面塗
装無し 接着剤層：酢酸ビニル系接着剤、塗布量（固形分）２０
ｇ／ｍ２ 紙１：坪量３７ｇ／ｍ２ 紙２：坪量３０ｇ／ｍ２ 第一の接着性樹脂層：ブロム系難燃剤含有のエチレン−
アクリル酸共重合体（ＥＡＡ）樹脂フィルム、厚さ４０
μｍ 第二の接着性樹脂層：ブロム系難燃剤含有のエチレン−
アクリル酸共重合体（ＥＡＡ）樹脂フィルム、厚さ４０
μｍ ガラス繊維不織布：坪量２５ｇ／ｍ２ アルミニウム箔：厚さ１５μｍ −表面試験に用いた基材− 法定準不燃材料の石膏ボード（９．５ｍｍ厚）および法
定不燃材料の石綿パーライト板（１０ｍｍ厚）の２種類
の基材を使用した。 −表面試験の手順− 防燃性銘木化粧シートＡ、Ｂ各６校を上記２種の基材の
表面に各基材に３枚ずつ貼着し、そして作成された試験
体の加熱試験を行なった。その詳細は、昭和５９年建設
省告示第１３７２号およびＪＩＳ Ａ １３２１に規定
する手順および条件に従うものとした。なお、該化粧シ
ートの貼着には、酢酸ビニルエマルジョン接着剤（固形
分の塗布量４０ｇ／ｍ２）が使用された。 Test Example 1 : Notification No. 137 of Ministry of Construction, 1984
No. 2 and surface test according to JIS A 1321 For the fireproof precious wood decorative sheets of Examples and Comparative Examples, respectively, surface tests according to Ministry of Construction Notification No. 1372 and JIS A 1321 of fire prevention materials were conducted as follows, and From the results of the heating test during
Especially, the flame propagation characteristics were compared. In addition,
From this test, a graph of an exhaust gas temperature curve and a standard temperature curve showing changes over time from the start of the test for the exhaust gas temperature and the standard temperature is obtained. In the present invention, the flame propagation characteristic means a temperature difference between an exhaust temperature curve and a standard temperature curve within a period of 3 minutes after the start of the test (within 3 minutes only the heat source of the gas burner) (that is, flame propagation). (Characteristic E = exhaust gas temperature−standard temperature (° C.)), and as shown in FIG. 6, when the exhaust gas temperature curve “a” is lower than the standard temperature curve “b” during the above-mentioned three-minute period, the exhaust gas temperature curve “a” becomes the standard temperature. The temperature difference (minus value) between the exhaust temperature and the standard temperature at the portion closest to the curve b. As shown in FIG. 7, the exhaust temperature curve a is smaller than the standard temperature curve b during the above-mentioned three-minute period. When the temperature exceeds the standard temperature curve b, the temperature difference (plus value) between the exhaust temperature and the standard temperature at a position where the exhaust temperature curve a is farthest from the standard temperature curve b. Therefore, the flame propagation characteristic is the minimum at -50 ° C, and is usually expressed by a value larger than -50 ° C. When the flame propagation characteristic is a negative value and the absolute value is larger, the flame propagation is less likely to occur, which means that the flame propagation material is more suitable, and conversely, when the flame propagation characteristic is a positive value, The greater the value of the flame propagation property occurs and the value of the flame propagation property, the more likely the flame propagation occurs, which means that the material is rejected as a fire protection material. -Laminated Structure of Flame-Retardant Precious Wood Decorative Sheet- Each of the flame-retardant precious wood decorative sheets is formed by pressure-bonding a laminate having the following configuration. Flameproof precious wood decorative sheet A: Precious wood veneer / adhesive layer / paper 1 / first adhesive resin layer / glass fiber nonwoven fabric / second adhesive resin layer / paper 2 Flameproof precious wood decorative sheet B: precious wood Veneer / Adhesive layer / Paper 1 / First adhesive resin layer / Aluminum foil / Second adhesive resin layer / Paper 2 -Each material of flameproof precious wood decorative sheet- Precious wood veneer: birch veneer, Air-dry weight 125 g / m 2 , no surface coating Adhesive layer: vinyl acetate adhesive, coating amount (solid content) 20
g / m 2 paper 1: basis weight 37 g / m 2 paper 2: basis weight 30 g / m 2 first adhesive resin layer: bromo-based flame retardant-containing ethylene-
Acrylic acid copolymer (EAA) resin film, thickness 40
μm Second adhesive resin layer: Brom-based flame retardant-containing ethylene-
Acrylic acid copolymer (EAA) resin film, thickness 40
μm glass fiber non-woven fabric: basis weight 25 g / m 2 aluminum foil: thickness 15 μm-base material used for surface test-gypsum board (9.5 mm thick) of legally non-combustible material and asbestos pearlite board (10 mm thick) of legally noncombustible material ) Were used. -Surface test procedure- Three sheets of each of the fireproof precious wood decorative sheets A and B were stuck on the surfaces of the above two types of base materials three by three, and a heating test of the prepared test pieces was performed. Was. The details followed the procedures and conditions specified in the Ministry of Construction Notification No. 1372 and JIS A 1321. Note that a vinyl acetate emulsion adhesive (solid content application amount 40 g / m 2 ) was used for attaching the decorative sheet.
【手続補正５】[Procedure amendment 5]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２８[Correction target item name] 0028
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００２８】試験例２：寸法安定性の試験 ガラス繊維不織布の含有量が異なる実施例の各防燃性銘
木化粧シートおよび比較例の防燃性銘木化粧シートにつ
いてそれぞれ、膨潤率の測定試験を行ない、その結果よ
り、寸法安定性に関して、それらを対比してみた。 −試験の方法− 各々の防燃性銘木化粧シートより、図２０に示されるス
トリップ形状の試験体（同図に表わす縦・横の寸法を有
する）を作成する。そして、試験体を常温の室内に２４
時間の間放置し、次いで、点Ｘおよび点Ｙを凡そ１８０
ｍｍの間隔にて試験体の表面に記し、続いて、間隔Ｘ−
Ｙの長さ（ｍｍ）を小数点以下２桁の位まで正確に計測
する（これを寸法Ｉとする。）。その後、試験体を２０
℃の水の中に３０分間の間浸漬し、次いで、これを水中
より取り出し、そして当初と同様に間隔Ｘ−Ｙの長さ
（ｍｍ）を小数点以下２桁の位まで正確に計測する（こ
れを寸法ＩＩとする。）。膨潤率は、次の式より算出さ
れる。 膨潤率（％）＝｛（寸法ＩＩ÷寸法Ｉ）−１｝×１００ 算出された膨潤率がより低いほど、防燃性銘木化粧シー
トの寸法安定性がより高いことを表わす。 −防燃性銘木化粧シートの積層構成− 各防燃性銘木化粧シートは、次の構成よりなる積層体を
圧着成形してなる。 防燃性銘木化粧シートＣ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２０ｇ／ｍ２）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＤ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２５ｇ／ｍ２）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＦ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／アル
ミニウム箔（坪量４０ｇ／ｍ２）／第二の接着性樹脂層
／紙２ −防燃性銘木化粧シートの各材料− 銘木単板：カバ単板、気乾重量９３ｇ／ｍ２、表面塗装
無し 接着剤層：酢酸ビニル系接着剤、塗布量（固形分）２０
ｇ／ｍ２ 紙１：坪量３７ｇ／ｍ２ 紙２：坪量３０ｇ／ｍ２ 第一の接着性樹脂層：ブロム系難燃剤含有のエチレン−
アクリル酸共重合体（ＥＡＡ）樹脂フィルム、厚さ４０
μｍ 第二の接着性樹脂層：ブロム系難燃剤含有のエチレン−
アクリル酸共重合体（ＥＡＡ）樹脂フィルム、厚さ４０
μｍ ガラス繊維不織布：坪量２０、２５ｇ／ｍ２ アルミニウム箔：坪量４０ｇ／ｍ２ Test Example 2 Test of Dimensional Stability A swelling ratio measurement test was carried out on each of the fire-resistant decorative wood decorative sheets of Examples having different contents of the glass fiber nonwoven fabric and the fire-resistant decorative wood decorative sheet of Comparative Example. Based on the results, the dimensional stability was compared. -Test method-From each of the flameproof precious wood decorative sheets, a strip-shaped specimen (having vertical and horizontal dimensions shown in Fig. 20) is prepared as shown in Fig. 20. Then, place the specimen in a room at room temperature for 24 hours.
Let stand for a time and then move point X and point Y approximately 180
mm on the surface of the specimen at intervals of mm
The length (mm) of Y is accurately measured to two places after the decimal point (this is defined as dimension I). After that, the specimen is
Immersed in water at 30 ° C. for 30 minutes, then taken out of the water, and measured exactly the length (mm) of the interval XY to two decimal places as before (this Is dimension II). The swelling ratio is calculated from the following equation. Swelling ratio (%) = {(dimension II {dimension I) -1} × 100 The lower the calculated swelling ratio, the higher the dimensional stability of the flameproof precious wood decorative sheet. -Laminated Structure of Flame-Retardant Precious Wood Decorative Sheet- Each of the flame-retardant precious wood decorative sheets is formed by pressure-bonding a laminate having the following configuration. Flameproof precious wood decorative sheet C: Precious wood veneer / adhesive layer / paper / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 20 g / m 2 ) / second adhesive resin layer / paper 2 Flammable precious wood decorative sheet D: Precious wood veneer / adhesive layer / paper 1 / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 25 g / m 2 ) / second adhesive resin layer / paper 2 Decorative precious wood decorative sheet F: Precious wood veneer / adhesive layer / paper 1 / first adhesive resin layer / aluminum foil (basis weight 40 g / m 2 ) / second adhesive resin layer / paper 2—flammability Each material of precious wood decorative sheet-Precious wood veneer: birch veneer, air-dry weight 93 g / m 2 , no surface coating Adhesive layer: vinyl acetate-based adhesive, coating amount (solid content) 20
g / m 2 paper 1: basis weight 37 g / m 2 paper 2: basis weight 30 g / m 2 first adhesive resin layer: bromo-based flame retardant-containing ethylene-
Acrylic acid copolymer (EAA) resin film, thickness 40
μm Second adhesive resin layer: Brom-based flame retardant-containing ethylene-
Acrylic acid copolymer (EAA) resin film, thickness 40
μm glass fiber nonwoven fabric: basis weight 20,25g / m 2 aluminum foil: basis weight 40 g / m 2
【手続補正６】[Procedure amendment 6]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００３０[Correction target item name] 0030
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００３０】試験例３：昭和５９年建設省告示第１３７
２号およびＪＩＳ Ａ １３２１に従う表面試験 ガラス繊維不織布の含有量が異なる実施例の各防燃性銘
木化粧シートについてそれぞれ、防火材料の昭和５９年
建設省告示第１３７２号およびＪＩＳ Ａ １３２１に
従う表面試験を以下のとおり行ない、その中の加熱試験
の結果より、防火性能、特に火炎伝播特性に関してそれ
らを対比してみた。 −防燃性銘木化粧シートの積層構成− 各防燃性銘木化粧シートは、次の構成よりなる積層体を
圧着成形してなる。 防燃性銘木化粧シートＧ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２０ｇ／ｍ２）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＨ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量２５ｇ／ｍ２）／第二の接着性樹脂
層／紙２ 防燃性銘木化粧シートＩ： 銘木単板／接着剤層／紙１／第一の接着性樹脂層／ガラ
ス繊維不織布（坪量３０ｇ／ｍ２）／第二の接着性樹脂
層／紙２ −防燃性銘木化粧シートの各材料− 銘木単板：カバ単板、気乾重量１０５ｇ／ｍ２、表面塗
装無し 接着剤層：酢酸ビニル系接着剤、塗布量（固形分）２０
ｇ／ｍ２ 紙１：坪量３７ｇ／ｍ２ 紙２：坪量３０ｇ／ｍ２ 第一の接着性樹脂層：ブロム系難燃剤含有のエチレン−
アクリル酸共重合体（ＥＡＡ）樹脂フィルム、厚さ４０
μｍ 第二の接着性樹脂層：ブロム系難燃剤含有のエチレン−
アクリル酸共重合体（ＥＡＡ）樹脂フィルム、厚さ４０
μｍ ガラス繊維不織布：坪量２０、２５、３０ｇ／ｍ２ −表面試験に用いた基材− 法定準不燃材料の石膏ボード（９．５ｍｍ厚）を基材と
して使用した。 −表面試験の手順− 防燃性銘木化粧シートＧ、Ｈ、Ｉ各２校を上記基材の表
面に貼着し、そして作成された試験体の加熱試験を行な
った。その詳細は、昭和５９年建設省告示第１３７２号
およびＪＩＳ Ａ １３２１に規定する手順および条件
に従うものとした。なお、これら化粧シートの貼着に
は、酢酸ビニルエマルジョン接着剤（固形分の塗布量４
０ｇ／ｍ２）が使用された。 Test Example 3 Notification of Ministry of Construction No. 137 of 1984
No. 2 and surface test according to JIS A 1321 For each of the fireproof precious wood decorative sheets of Examples having different contents of the glass fiber nonwoven fabric, a surface test according to the Ministry of Construction Notification No. 1372 and JIS A 1321 of the Ministry of Construction in 1984 was carried out for each fireproof material. The following tests were conducted, and based on the results of the heating tests therein, the fire prevention performance, particularly the flame propagation characteristics, were compared. -Laminated Structure of Flame-Retardant Precious Wood Decorative Sheet- Each of the flame-retardant precious wood decorative sheets is formed by pressure-bonding a laminate having the following configuration. Flameproof precious wood decorative sheet G: Precious wood veneer / adhesive layer / paper / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 20 g / m 2 ) / second adhesive resin layer / paper 2 Flammable precious wood decorative sheet H: Precious wood veneer / adhesive layer / paper 1 / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 25 g / m 2 ) / second adhesive resin layer / paper 2 Decorative precious wood decorative sheet I: Precious wood veneer / adhesive layer / paper / first adhesive resin layer / glass fiber nonwoven fabric (basis weight 30 g / m 2 ) / second adhesive resin layer / paper 2-fireproof Each material of the nature precious wood decorative sheet-Precious wood veneer: birch veneer, air-dry weight 105 g / m 2 , no surface coating Adhesive layer: vinyl acetate adhesive, coating amount (solid content) 20
g / m 2 paper 1: basis weight 37 g / m 2 paper 2: basis weight 30 g / m 2 first adhesive resin layer: bromo-based flame retardant-containing ethylene-
Acrylic acid copolymer (EAA) resin film, thickness 40
μm Second adhesive resin layer: Brom-based flame retardant-containing ethylene-
Acrylic acid copolymer (EAA) resin film, thickness 40
μm glass fiber nonwoven fabric: basis weight 20, 25, 30 g / m 2 -substrate used for surface test- A plaster board (9.5 mm thick) of a legally quasi-noncombustible material was used as a substrate. -Surface Test Procedure- Each of the fireproof precious wood decorative sheets G, H, and I was attached to the surface of the base material, and a heating test was performed on the prepared specimen. The details followed the procedures and conditions specified in the Ministry of Construction Notification No. 1372 and JIS A 1321. In addition, the vinyl acetate emulsion adhesive (solid content application amount 4
0 g / m 2 ) was used.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ // Ｅ０４Ｆ 13/08 Ｅ０４Ｆ 13/08 Ａ ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI // E04F 13/08 E04F 13/08 A
Claims (7)
たは不織布：難燃剤が混入された第１の接着性樹脂層；
ガラス繊維不織布、ガラス繊維紙もしくはガラス繊維織
布またはこれらの組合せ；難燃剤が混入された第２の接
着性樹脂層：紙または不織布が積層され一体に圧着成形
されてなり、そして、必要により塗料膜が前記銘木単板
の上に形成されている、防燃性銘木化粧シート。1. In order from the top, a veneer veneer: adhesive layer: paper or nonwoven fabric: first adhesive resin layer mixed with a flame retardant;
Glass fiber non-woven fabric, glass fiber paper or glass fiber woven fabric or a combination thereof; a second adhesive resin layer mixed with a flame retardant: paper or non-woven fabric is laminated and pressure-formed integrally, and if necessary, paint A flame-retardant precious wood decorative sheet, wherein a film is formed on the precious wood veneer.
性ガラス混抄紙が積層され一体に圧着成形されてなり、
そして、必要により塗料膜が前記銘木単板の上に形成さ
れている、防燃性銘木化粧シート。2. In the order from the top, a laminated veneer: an adhesive layer: a flame-retardant glass-mixed paper is laminated and integrally press-formed.
And a fire-resistant precious wood decorative sheet, wherein a paint film is formed on the precious wood veneer as required.
たは含浸された銘木単板である、請求項１または請求項
２に記載の防燃性銘木化粧シート。3. The decorative sheet according to claim 1, wherein the veneer veneer is a veneer veneer coated or impregnated with an appropriate amount of a flame retardant.
銘木化粧シートが木質系、無機質系または金属系基材の
上に貼着されてなる、防燃性銘木化粧板。4. A decorative board made of flame-retardant precious wood, comprising the decorative sheet of fire-proof precious wood according to claim 1 stuck on a wood-based, inorganic-based or metal-based substrate.
ミネートに従い、難燃剤が混入された第１の接着性樹脂
層：ガラス繊維不織布、ガラス繊維紙もしくはガラス繊
維織布またはこれらの組合せ：難燃剤が混入された第２
の接着性樹脂層：紙または不織布よりなる積層体を成形
する段階と、 他方で、熱圧接着により、銘木単板：接着剤層：紙また
は不織布よりなる単板裏打ちシートを作る段階と、 前記積層体と前記単板裏打ちシートを熱圧接着して、一
体に成形する段階と、 そして必要により、塗装によって塗料膜を、作られた防
燃性銘木化粧シートの単板表面に形成する段階よりな
る、防燃性銘木化粧シートの製造方法。5. On the other hand, a first adhesive resin layer mixed with a flame retardant according to extrusion lamination or hot-press lamination: glass fiber non-woven fabric, glass fiber paper or glass fiber woven fabric or a combination thereof: flame retardant Mixed 2nd
Adhesive resin layer: forming a laminate made of paper or non-woven fabric; and, on the other hand, making a nameplate veneer: adhesive layer: making a veneer backing sheet made of paper or non-woven fabric by hot-pressure bonding. Bonding the laminate and the veneer backing sheet by heat and pressure, and forming them integrally; and, if necessary, forming a paint film on the veneer surface of the made flame-resistant precious wood decorative sheet by painting. A method for producing a flame-resistant precious wood decorative sheet.
に従い、紙または不織布：難燃剤が混入された第１の接
着性樹脂層：ガラス繊維不織布、ガラス繊維紙もしくは
ガラス繊維織布またはこれらの組合せ：難燃剤が混入さ
れた第２の接着性樹脂層：紙または不織布よりなる積層
体を成形する段階と、 接着剤を該積層体の上側の紙または不織布の上に塗布
し、続いて銘木単板をその上にオーバーレイする段階
と、 オーバーレイされた積層体を熱圧接着して、一体に成形
する段階と、 そして必要により、塗装によって塗料膜を、作られた防
燃性銘木化粧シートの単板表面に形成する段階よりな
る、防燃性銘木化粧シートの製造方法。6. A paper or non-woven fabric: a first adhesive resin layer mixed with a flame retardant according to an extrusion lamination or a hot-press lamination: a glass fiber non-woven fabric, a glass fiber paper or a glass fiber woven fabric or a combination thereof: a flame retardant A second adhesive resin layer mixed with: a step of forming a laminate made of paper or non-woven fabric; applying an adhesive onto the paper or non-woven fabric on the upper side of the laminate; A step of overlaying on the top, a step of hot-pressing the laminated body to form an integral body, and, if necessary, a paint film on the veneer surface of the fire-resistant precious wood decorative sheet made by painting. A method for producing a flameproof precious wood decorative sheet, comprising a step of forming.
た防燃性銘木化粧シートの単板表面に塗布または含浸す
る段階をさらに含む、請求項５または６に記載の防燃性
銘木化粧シートの製造方法。7. The flame retardant according to claim 5, further comprising a step of applying or impregnating a flame retardant on a veneer surface of the made flame retardant precious wood decorative sheet before forming the paint film. A method of manufacturing a decorative precious wood decorative sheet.