JPH11349692A - Article having frosted glass tone and its preparation - Google Patents
Article having frosted glass tone and its preparationInfo
- Publication number
- JPH11349692A JPH11349692A JP15633098A JP15633098A JPH11349692A JP H11349692 A JPH11349692 A JP H11349692A JP 15633098 A JP15633098 A JP 15633098A JP 15633098 A JP15633098 A JP 15633098A JP H11349692 A JPH11349692 A JP H11349692A
- Authority
- JP
- Japan
- Prior art keywords
- synthetic resin
- transparent synthetic
- product
- transparent
- refractive index
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、スリガラス調（透
明性があり、マット調（艶消し調）を有する外観）を有
する製品およびその製法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a product having a ground glass (transparent, matte (matte) appearance) and a method for producing the same.
【０００２】[0002]
【従来の技術】一般に、製品には、その製品によって様
々な特性が要求される。特に、化粧料容器部品には、耐
薬品性，保香性，機械的および熱的強度等の特性が要求
される。これらの要求を満たすため、ポリスチレン，ポ
リプロピレン，アクリロニトリルブタジエンスチレン共
重合体（ＡＢＳ）等の合成樹脂を用いたものが広範に使
用されている。さらに、特定の部品においては、装飾性
が優れていることも要求されている。このようなものの
一つとして、スリガラス調を有する化粧料容器部品があ
る。2. Description of the Related Art In general, various characteristics are required for a product depending on the product. In particular, cosmetic container parts are required to have properties such as chemical resistance, fragrance retention, mechanical and thermal strength, and the like. In order to satisfy these demands, those using synthetic resins such as polystyrene, polypropylene, acrylonitrile butadiene styrene copolymer (ABS) are widely used. Furthermore, it is also required that specific parts have excellent decorativeness. As one of such products, there is a cosmetic container part having a ground glass effect.
【０００３】このようなスリガラス調を有する化粧料容
器部品は、一般に、図３に示すように、表面がエッチン
グにより粗面化された金型１１を用いて透明性合成樹脂
を射出成形することにより成形される。成形された化粧
料容器部品１２の表面には、上記金型１１の表面の粗面
が転写されており、この粗面と化粧料容器部品１２の透
明性との調和により、スリガラス調を有することができ
る。As shown in FIG. 3, such a cosmetic container part having a ground glass effect is generally obtained by injection molding a transparent synthetic resin using a mold 11 whose surface is roughened by etching. Molded. On the surface of the molded cosmetic container part 12, the rough surface of the mold 11 is transferred, and the surface of the mold 11 has a ground-glass appearance due to harmony with the transparency of the cosmetic container part 12. Can be.
【０００４】しかしながら、金型１１の表面が粗面化さ
れている場合には、脱型に必要な抜け勾配は、それが粗
面化されていない場合よりも大きくなるため、化粧料容
器部品１２のデザインが限定される。また、同じ形状の
化粧料容器部品でスリガラス調を有しないものを成形す
る場合には、金型の表面が粗面化されていないものを別
に準備しなければならず、製造コストが高くなる。[0004] However, when the surface of the mold 11 is roughened, the draft required for demolding is larger than when the surface is not roughened. Is limited in design. Further, when molding a cosmetic container part having the same shape and not having a ground glass effect, a mold whose surface is not roughened must be separately prepared, which increases the manufacturing cost.
【０００５】そこで、金型１１の表面を粗面化すること
なくスリガラス調を有する合成樹脂成形体を成形する方
法が提案されている。この方法には、合成樹脂成形体の
母材となる透明性合成樹脂に、透明なガラス等の無機質
の粉粒体を混合し、この混合物を射出成形する方法があ
る。[0005] Therefore, there has been proposed a method of molding a synthetic resin molded article having a ground glass tone without roughening the surface of the mold 11. As this method, there is a method in which a transparent synthetic resin serving as a base material of a synthetic resin molded body is mixed with an inorganic powdery material such as transparent glass and the mixture is injection-molded.
【０００６】例えば、透明な合成樹脂成形体の母材とな
る高温状態のポリエチレンテレフタレート樹脂液中に、
粒径が２０μｍ以下の透明なガラスの粉粒体を１０重量
％以下添加し、充分に混合してポリエチレンテレフタレ
ート樹脂液中に分散させる。そして、この混合物を射出
成形すると、スリガラス調を有する化粧料容器部品が得
られる。この化粧料容器部品の容壁の一部を図４に示
す。このように、容壁１３の中では、平板状をした無機
質（ガラス）の粉粒体１４が分散されており、容壁１３
の表面では、無機質の粉粒体１４が突出している。For example, in a polyethylene terephthalate resin liquid in a high temperature state which is a base material of a transparent synthetic resin molded body,
10% by weight or less of a transparent glass powder having a particle size of 20 μm or less is added, mixed well, and dispersed in a polyethylene terephthalate resin solution. Then, when this mixture is injection-molded, a cosmetic container part having a ground glass effect is obtained. FIG. 4 shows a part of the wall of the cosmetic container part. As described above, in the container wall 13, the plate-like inorganic (glass) powder particles 14 are dispersed, and the container wall 13 is dispersed.
On the surface of, the inorganic powdery granules 14 protrude.
【０００７】このような方法によると、金型の表面を粗
面化する必要なく、スリガラス調を有する化粧料容器部
品が得られ、このため、抜け勾配を小さくすることがで
き、同じ形状の化粧料容器部品でスリガラス調を有しな
いものを成形する場合には、この金型を用いることがで
き、別に金型を準備する必要がない。[0007] According to such a method, it is possible to obtain a ground-glass-like cosmetic container part without having to roughen the surface of the mold. This mold can be used for molding a container material having no ground glass effect, and there is no need to prepare a separate mold.
【０００８】また、他の方法として、製品の表面にスリ
ガラス調の塗装を施す方法もある。As another method, there is a method of applying a ground glass-like coating to the surface of a product.
【０００９】[0009]
【発明が解決しようとする課題】しかしながら、前者の
方法によると、充分に満足できるスリガラス調を得るた
めには、無機質の粉粒体を３０〜５０重量％混合する必
要があるが、この混合物を射出成形すると、成形品の引
っ張り強度，曲げ強度，曲げ弾性率，衝撃強度等が大き
く低下する。また、無機質の比重は約２以上であり、そ
の粉粒体を３０〜５０重量％混合すると、成形品は重く
なる。これらのため、上記成形品は、実用上問題があ
り、上記成形品を商品化することが困難である。このた
め、成形品を化粧料容器部品として商品化するために
は、無機質の粉粒体を５〜１０重量％の少量しか混合す
ることができない。しかしながら、このものでは、光沢
がなくなる程度で、スリガラス調が充分に満足できるも
のではない。また、図４に示すように、無機質の粉粒体
１４は、平板状をしているため、化粧料容器部品の容壁
１３の表面で無機質の粉粒体１４の様々な部分が突出し
ていると、容壁１３の表面は、不均一となり、手触りが
悪く、滑らかでない。However, according to the former method, in order to obtain a sufficiently satisfactory ground glass effect, it is necessary to mix 30 to 50% by weight of inorganic powders. Injection molding greatly reduces the tensile strength, bending strength, flexural modulus, impact strength, and the like of the molded product. Further, the specific gravity of the inorganic substance is about 2 or more, and if the powdery and granular materials are mixed at 30 to 50% by weight, the molded product becomes heavy. For these reasons, the molded article has a practical problem, and it is difficult to commercialize the molded article. Therefore, in order to commercialize the molded article as a cosmetic container part, only a small amount of 5 to 10% by weight of the inorganic powder can be mixed. However, in this case, the ground glass effect is not sufficiently satisfactory, as the gloss disappears. In addition, as shown in FIG. 4, since the inorganic powder 14 has a flat plate shape, various portions of the inorganic powder 14 protrude from the surface of the container wall 13 of the cosmetic container part. Then, the surface of the container wall 13 becomes uneven, the touch is poor, and the surface is not smooth.
【００１０】また、後者の方法によると、塗装工程が必
要となり、その製造が煩わしくなるとともに、製造コス
トが高くなる。According to the latter method, a painting step is required, which makes the production troublesome and increases the production cost.
【００１１】本発明は、このような事情に鑑みなされた
もので、商品として充分に満足できる高質感のスリガラ
ス調を有しつつも実用上問題がない製品およびその製法
の提供をその目的とする。The present invention has been made in view of such circumstances, and an object of the present invention is to provide a product having a high quality ground glass tone which is sufficiently satisfactory as a product, but which has no practical problem and a method for producing the same. .
【００１２】[0012]
【課題を解決するための手段】上記の目的を達成するた
め、本発明は、製品の母材となる透明性合成樹脂中に、
この透明性合成樹脂と略同じ屈折率を有する透明性合成
樹脂の粉粒体が分散され、それによって製品がスリガラ
ス調に構成されているスリガラス調を有する製品を第１
の要旨とし、製品の母材となる透明性合成樹脂に、この
透明性合成樹脂と略同じ屈折率を有しこの透明性合成樹
脂よりも融点の高い透明性合成樹脂の粉粒体を混合し、
上記透明性合成樹脂の融点と上記透明性合成樹脂の粉粒
体の融点の間の温度で、上記混合物を射出成形すること
によりスリガラス調に構成されている製品を製造するス
リガラス調を有する製品の製法を第２の要旨とする。Means for Solving the Problems To achieve the above object, the present invention provides a transparent synthetic resin which is a base material of a product.
A ground-glass-like product having a ground glass-like product in which powdery granules of a transparent synthetic resin having a refractive index substantially the same as that of the transparent synthetic resin are dispersed, whereby the product is configured as a ground-glass-like first product
The powder of the transparent synthetic resin having substantially the same refractive index as the transparent synthetic resin and a melting point higher than that of the transparent synthetic resin is mixed with the transparent synthetic resin serving as the base material of the product. ,
At a temperature between the melting point of the transparent synthetic resin and the melting point of the granular material of the transparent synthetic resin, the above mixture is subjected to injection molding to produce a product having a ground glass-like product. The manufacturing method is the second gist.
【００１３】すなわち、本発明のスリガラス調を有する
製品は、製品の母材となる合成樹脂中に分散されている
ものが合成樹脂の粉粒体という比重の小さいものであ
る。このため、合成樹脂の粉粒体よりも比重の大きい無
機質の粉粒体が合成樹脂の粉粒体と同じ重量％分散され
ている場合（従来の技術）と比較すると、合成樹脂の粉
粒体のほうが多量分散されていることとなり、製品は、
合成樹脂の粉粒体が分散されているほうが綺麗なマット
調を有することとなる。このことから、比重の小さい合
成樹脂の粉粒体が分散されている場合は、分散されてい
る重量％の値が小さくても、綺麗なマット調を有しうる
ため、その量は、実用上問題がある程度まで必要としな
い。したがって、実用上問題がない範囲内で合成樹脂の
粉粒体が多量に分散されているため、本発明のスリガラ
ス調を有する製品は、商品として充分に満足できる高質
感のマット調を有しつつも実用上問題がない。また、製
品の母材となる透明性合成樹脂の屈折率と透明性合成樹
脂の粉粒体の屈折率とが略同じであるため、本発明のス
リガラス調を有する製品は、透明なマット調、すなわち
スリガラス調を有するものとなる。また、製品の母材と
なる透明な合成樹脂中にこの透明性合成樹脂と略同じ屈
折率を有する透明性合成樹脂の粉粒体が分散されている
ことにより、スリガラス調を得ているため、塗装工程
（従来の技術）が不要になる。また、スリガラス調の塗
装に比べて耐久性も高くなる。さらに、全体が合成樹脂
材料で構成されており、塗膜のような異種材料が用いら
れてないことから、リサイクルも容易となる。In other words, the ground glass product of the present invention is a product having a small specific gravity of synthetic resin powder or granules dispersed in a synthetic resin as a base material of the product. For this reason, compared with the case where the inorganic particles having a higher specific gravity than the synthetic resin particles are dispersed in the same weight% as the synthetic resin particles (conventional technology), the synthetic resin particles are Is more dispersed and the product is
A fine matte tone is obtained when the synthetic resin particles are dispersed. From this fact, when synthetic resin particles having a small specific gravity are dispersed, a fine matte tone can be obtained even if the dispersed weight% value is small. The problem does not need to some extent. Therefore, since the synthetic resin powder and granules are dispersed in a large amount within a range in which there is no practical problem, the product having a ground glass tone of the present invention has a high quality matte tone which is sufficiently satisfactory as a product. There is no practical problem. Further, since the refractive index of the transparent synthetic resin serving as the base material of the product is substantially the same as the refractive index of the granular material of the transparent synthetic resin, the product having the ground glass of the present invention has a transparent matte, That is, it has a ground glass tone. In addition, since a transparent synthetic resin powder having substantially the same refractive index as the transparent synthetic resin is dispersed in the transparent synthetic resin serving as the base material of the product, a ground glass effect is obtained. The painting process (conventional technology) becomes unnecessary. Also, the durability is higher than that of a ground glass-like coating. Furthermore, since the whole is made of a synthetic resin material, and no different material such as a coating film is used, recycling becomes easy.
【００１４】また、透明性合成樹脂の粉粒体が合成樹脂
のビーズである場合には、透明性合成樹脂の粉粒体が綺
麗な球状になっているため、本発明のスリガラス調を有
する製品の表面は、滑らかになり、手触りが良くなる。When the transparent synthetic resin particles are synthetic resin beads, the transparent synthetic resin particles have a beautiful spherical shape. Has a smooth surface and a good feel.
【００１５】また、本発明のスリガラス調を有する製品
の製法は、製品の母材となる合成樹脂中に混合するもの
が合成樹脂の粉粒体という比重の小さいものである。こ
のため、合成樹脂の粉粒体よりも比重の大きい無機質の
粉粒体を合成樹脂の粉粒体と同じ重量％混合する場合
（従来の技術）と比較すると、合成樹脂の粉粒体のほう
が多量混合されることとなり、製品は、合成樹脂の粉粒
体が混合されているほうが綺麗なマット調を有すること
となる。このことから、比重の小さい合成樹脂の粉粒体
が混合される場合は、混合される重量％の値が小さくて
も、綺麗なマット調を有しうるため、その量は、実用上
問題がある程度まで必要としない。したがって、実用上
問題がない範囲内で合成樹脂の粉粒体を多量に混合する
ため、本発明のスリガラス調を有する製品の製法によれ
ば、商品として充分に満足できる高質感のマット調を有
しつつも実用上問題がない製品を製造することができ
る。また、製品の母材となる透明性合成樹脂に、この透
明性合成樹脂と略同じ屈折率を有する透明性合成樹脂の
粉粒体が混合されるため、透明なマット調、すなわちス
リガラス調を有する製品を製造することができる。ま
た、製品の母材となる透明な合成樹脂中にこの透明性合
成樹脂と略同じ屈折率を有する透明性合成樹脂の粉粒体
を分散させることにより、スリガラス調を得ているた
め、塗装工程（従来の技術）が不要になる。また、スリ
ガラス調の塗装に比べて耐久性も高くなる。さらに、全
体が合成樹脂材料で構成されており、塗膜のような異種
材料が用いられてないことから、リサイクルも容易とな
る。In the method for producing a ground-glass-like product according to the present invention, what is mixed into a synthetic resin as a base material of the product is a powder having a small specific gravity of a synthetic resin powder. Therefore, when compared with the case where the inorganic powder having a higher specific gravity than the synthetic resin powder is mixed with the same weight% as the synthetic resin powder (conventional technology), the synthetic resin powder is more preferable. A large amount is mixed, and the product has a more beautiful matte tone when the synthetic resin particles are mixed. From this fact, when synthetic resin particles having a small specific gravity are mixed, even if the value of the weight% to be mixed is small, a beautiful matte tone can be obtained. Not required to some extent. Therefore, in order to mix a large amount of the synthetic resin powder within a range where there is no practical problem, the method for producing a ground glass-like product of the present invention has a high quality matte tone that can be sufficiently satisfied as a product. In addition, it is possible to manufacture a product having no practical problem. In addition, since a transparent synthetic resin powder having substantially the same refractive index as the transparent synthetic resin is mixed with the transparent synthetic resin serving as a base material of the product, the transparent synthetic resin has a transparent matte tone, that is, a ground glass tone. Products can be manufactured. In addition, by dispersing powder particles of a transparent synthetic resin having substantially the same refractive index as the transparent synthetic resin in a transparent synthetic resin serving as a base material of the product, a ground glass effect is obtained. (Conventional technology) becomes unnecessary. Also, the durability is higher than that of a ground glass-like coating. Furthermore, since the whole is made of a synthetic resin material, and no different material such as a coating film is used, recycling becomes easy.
【００１６】なお、屈折率が略同じであるとは、両者の
屈折率の差が０．０１未満であることをいう。Here, that the refractive indexes are substantially the same means that the difference between the two refractive indexes is less than 0.01.
【００１７】[0017]
【発明の実施の形態】つぎに、本発明の実施の形態を図
面にもとづいて詳しく説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS Next, embodiments of the present invention will be described in detail with reference to the drawings.
【００１８】[0018]
【実施例１】図１および図２は、本発明の製品の一実施
例を示している。この実施例では、製品として、図１に
示すような、化粧料容器部品である有天筒状のキャップ
Ａを用いている。このキャップＡの容壁は、図２に示す
ように、これの母材となる無色透明なポリスチレン樹脂
１中に平均粒径１２μｍの無色透明なポリスチレン樹脂
（架橋によって多次元構造になっている）２のビーズ
（粉粒体）が全体の２０重量％分散されているものであ
る。Embodiment 1 FIGS. 1 and 2 show an embodiment of the product of the present invention. In this embodiment, as shown in FIG. 1, a cap A having a cylindrical shape as a cosmetic container part is used as a product. As shown in FIG. 2, the wall of the cap A is a colorless and transparent polystyrene resin having an average particle diameter of 12 μm in a colorless and transparent polystyrene resin 1 serving as a base material thereof (having a multidimensional structure by crosslinking). No. 2 beads (granules) are dispersed in 20% by weight of the whole.
【００１９】上記キャップＡは、つぎのようにして得ら
れる。すなわち、まず、無色透明な合成樹脂成形体の母
材となる高温状態のポリスチレン樹脂１液中に平均粒径
１２μｍのポリスチレン樹脂２のビーズを全体の２０重
量％添加し、充分に混合してポリスチレン樹脂１液中に
分散させる。ついで、この混合物を射出成形する。この
ようにして、上記キャップＡが製造される。The cap A is obtained as follows. That is, first, 20% by weight of beads of polystyrene resin 2 having an average particle diameter of 12 μm are added to 1 part of polystyrene resin 1 in a high temperature state, which is a base material of a colorless and transparent synthetic resin molded body, and thoroughly mixed with polystyrene. Disperse in resin 1 liquid. The mixture is then injection molded. Thus, the cap A is manufactured.
【００２０】ここで、融点は、ビーズのポリスチレン樹
脂２の方が、母材のポリスチレン樹脂１よりも高くなっ
ており、上記射出成形する際の温度は、母材のポリスチ
レン樹脂１の融点と、ビーズのポリスチレン樹脂２の融
点との間の温度である。このため、ビーズのポリスチレ
ン樹脂２が溶解されずに残っている。Here, the melting point of the polystyrene resin 2 of the beads is higher than that of the polystyrene resin 1 of the base material, and the temperature at the time of the injection molding is the same as the melting point of the polystyrene resin 1 of the base material. The temperature is between the melting point of the polystyrene resin 2 of the beads. Therefore, the polystyrene resin 2 of the beads remains without being dissolved.
【００２１】また、ポリスチレン樹脂２の比重は、無機
質の比重の約半分であるため、同じ重量％混合すると、
ポリスチレン樹脂２のビーズのほうが無機質の粉粒体よ
りも約２倍の量混合される。したがって、キャップＡに
は、充分な量のポリスチレン樹脂２のビーズが混合され
ている。Further, since the specific gravity of the polystyrene resin 2 is about half of the specific gravity of the inorganic substance, when the same weight% is mixed,
The beads of the polystyrene resin 2 are mixed about twice as much as the inorganic particles. Therefore, a sufficient amount of beads of the polystyrene resin 2 are mixed in the cap A.
【００２２】さらに、ポリスチレン樹脂１の屈折率が
１．５９、ポリスチレン樹脂２の屈折率が１．５９であ
り、両者の屈折率は同じである。このような場合には、
キャップＡは、商品として充分に満足できる高質感の透
明なマット調、すなわち高質感のスリガラス調を有する
ことができる。Further, the refractive index of the polystyrene resin 1 is 1.59 and the refractive index of the polystyrene resin 2 is 1.59, and the two have the same refractive index. In such a case,
The cap A can have a high quality transparent matte tone, which is sufficiently satisfactory as a product, that is, a high quality ground glass tone.
【００２３】また、上記ポリスチレン樹脂２のビーズ
は、架橋剤を用いて共重合されている。この重合方法
は、懸濁重合で行われ、重合体は綺麗な球状になってい
る。The beads of the polystyrene resin 2 are copolymerized using a crosslinking agent. This polymerization method is carried out by suspension polymerization, and the polymer has a beautiful spherical shape.
【００２４】このため、キャップＡの表面では、綺麗な
球状になったポリスチレン樹脂２のビーズの一部が突出
することとなり、キャップＡの表面は、滑らかになり、
手触りが良くなる。For this reason, on the surface of the cap A, a part of the bead of the polystyrene resin 2 which has become a beautiful sphere projects, and the surface of the cap A becomes smooth.
The feel improves.
【００２５】[0025]
【実施例２】この実施例２では、母材となる無色透明な
ポリプロピレン樹脂中に平均粒径１２μｍの無色透明な
ポリメタクリル酸メチル樹脂（架橋によって多次元構造
になっている）のビーズ（粉粒体）が全体の１５重量％
分散されている。そして、実施例１と同様にして、キャ
ップＡが製造される。それ以外の部分は、上記実施例１
と同様である。Example 2 In Example 2, a colorless transparent polymethyl methacrylate resin (having a multidimensional structure by crosslinking) having an average particle diameter of 12 μm was mixed in a colorless transparent polypropylene resin as a base material. 15% by weight of the whole)
Distributed. Then, the cap A is manufactured in the same manner as in the first embodiment. Other parts are the same as those in the first embodiment.
Is the same as
【００２６】そして、ポリプロピレン樹脂の屈折率が
１．４９、ポリメタクリル酸メチル樹脂の屈折率が１．
４９であり、両者の屈折率は同じである。このため、上
記実施例１と同様、キャップＡは、商品として充分に満
足できる高質感の透明なマット調、すなわち高質感のス
リガラス調を有することができる。その他の作用・効果
は上記実施例１と同様である。The polypropylene resin has a refractive index of 1.49, and the polymethyl methacrylate resin has a refractive index of 1.49.
49, and both have the same refractive index. Therefore, similarly to the first embodiment, the cap A can have a high-quality transparent matte tone, that is, a high-quality ground glass tone, which is sufficiently satisfactory as a product. Other functions and effects are the same as those in the first embodiment.
【００２７】なお、上記実施例において、母材となる透
明性合成樹脂と透明性合成樹脂のビーズとの組み合わせ
は、上記実施例に限定されるものではなく、両者の屈折
率が略同じであれば、他の組み合わせでもよい。In the above embodiment, the combination of the transparent synthetic resin serving as the base material and the beads of the transparent synthetic resin is not limited to the above embodiment, but may be any combination having substantially the same refractive index. Other combinations may be used.
【００２８】また、母材となる透明性合成樹脂および透
明性合成樹脂のビーズは、着色され、有色透明なもので
もよい。The transparent synthetic resin and the transparent synthetic resin beads serving as the base material may be colored and colored and transparent.
【００２９】また、合成樹脂のビーズの粒径は、特に限
定されるものではないが、５０μｍ以下であることが好
ましい。この粒径が５０μｍを上回ると、キャップは、
綺麗なスリガラス調を有さなくなる。The particle size of the synthetic resin beads is not particularly limited, but is preferably 50 μm or less. When the particle size exceeds 50 μm, the cap is
It no longer has a beautiful ground glass effect.
【００３０】また、合成樹脂のビーズの量も、特に限定
されるものではないが、全体の５〜５０重量％であるこ
とが好ましい。この量が全体の５重量％を下回ると、綺
麗なスリガラス調を有さなくなり、５０重量％を上回る
と、キャップは、引っ張り強度等が大きく低下する。The amount of the synthetic resin beads is not particularly limited, but is preferably 5 to 50% by weight of the whole. If this amount is less than 5% by weight of the whole, it will not have a fine ground glass effect, and if it exceeds 50% by weight, the tensile strength of the cap will be greatly reduced.
【００３１】また、上記各実施例では、スリガラス調を
有する製品として化粧料容器部品のキャップを用いてい
るが、容器本体等各種の化粧料容器部品，コップ等の他
の容器等の他の製品を用いてもよい。In each of the above embodiments, the cap of the cosmetic container part is used as the product having the ground glass effect. However, other cosmetic container parts such as the container body, and other products such as other containers such as cups. May be used.
【００３２】[0032]
【発明の効果】以上のように、本発明のスリガラス調を
有する製品は、製品の母材となる合成樹脂中に分散され
ているものが合成樹脂の粉粒体という比重の小さいもの
である。このため、合成樹脂の粉粒体よりも比重の大き
い無機質の粉粒体が合成樹脂の粉粒体と同じ重量％分散
されている場合（従来の技術）と比較すると、合成樹脂
の粉粒体のほうが多量分散されていることとなり、製品
は、合成樹脂の粉粒体が分散されているほうが綺麗なマ
ット調を有することとなる。このことから、比重の小さ
い合成樹脂の粉粒体が分散されている場合は、分散され
ている重量％の値が小さくても、綺麗なマット調を有し
うるため、その量は、実用上問題がある程度まで必要と
しない。したがって、実用上問題がない範囲内で合成樹
脂の粉粒体が多量に分散されているため、本発明のマッ
ト調を有する製品は、商品として充分に満足できる高質
感のマット調を有しつつも実用上問題がない。また、製
品の母材となる透明性合成樹脂の屈折率と透明性合成樹
脂の粉粒体の屈折率とが略同じであるため、本発明のス
リガラス調を有する製品は、透明なマット調、すなわち
スリガラス調を有するものとなる。As described above, the ground-glass-like product of the present invention is a product having a small specific gravity, that is, powdery synthetic resin particles dispersed in a synthetic resin as a base material of the product. For this reason, compared with the case where the inorganic particles having a higher specific gravity than the synthetic resin particles are dispersed in the same weight% as the synthetic resin particles (conventional technology), the synthetic resin particles are Is dispersed in a larger amount, and the product has a more beautiful matte tone when the synthetic resin powder is dispersed. From this fact, when synthetic resin particles having a small specific gravity are dispersed, a fine matte tone can be obtained even if the dispersed weight% value is small. The problem does not need to some extent. Therefore, since the synthetic resin powder and granules are dispersed in a large amount within a range where there is no practical problem, the product having the matte tone of the present invention has a high quality matte tone that is sufficiently satisfactory as a product. There is no practical problem. Further, since the refractive index of the transparent synthetic resin serving as the base material of the product is substantially the same as the refractive index of the granular material of the transparent synthetic resin, the product having the ground glass of the present invention has a transparent matte, That is, it has a ground glass tone.
【００３３】また、透明性合成樹脂の粉粒体が透明性合
成樹脂のビーズである場合には、透明性合成樹脂の粉粒
体が綺麗な球状になっているため、本発明のスリガラス
調を有する製品の表面は、滑らかになり、手触りが良く
なる。When the particles of the transparent synthetic resin are beads of the transparent synthetic resin, the particles of the transparent synthetic resin have a beautiful spherical shape. The surface of the product having it becomes smooth and feels good.
【００３４】また、本発明のスリガラス調を有する製品
の製法は、製品の母材となる合成樹脂中に混合するもの
が合成樹脂の粉粒体という比重の小さいものである。こ
のため、合成樹脂の粉粒体よりも比重の大きい無機質の
粉粒体を合成樹脂の粉粒体と同じ重量％混合する場合
（従来の技術）と比較すると、合成樹脂の粉粒体のほう
が多量混合されることとなり、製品は、合成樹脂の粉粒
体が混合されているほうが綺麗なマット調を有すること
となる。このことから、比重の小さい合成樹脂の粉粒体
が混合される場合は、混合される重量％の値が小さくて
も、綺麗なマット調を有しうるため、その量は、実用上
問題がある程度まで必要としない。したがって、実用上
問題がない範囲内で合成樹脂の粉粒体を多量に混合する
ため、本発明のマット調を有する製品の製法によれば、
商品として充分に満足できる高質感のマット調を有しつ
つも実用上問題がない製品を製造することができる。ま
た、製品の母材となる透明性合成樹脂に、この透明性合
成樹脂と略同じ屈折率を有する透明性合成樹脂の粉粒体
が混合されるため、透明なマット調、すなわちスリガラ
ス調を有する製品を製造することができる。また、製品
の母材となる透明な合成樹脂中にこの透明性合成樹脂と
略同じ屈折率を有する透明性合成樹脂の粉粒体を分散さ
せることにより、スリガラス調を得ているため、塗装工
程（従来の技術）が不要になる。また、スリガラス調の
塗装に比べて耐久性も高くなる。さらに、全体が合成樹
脂材料で構成されており、塗膜のような異種材料が用い
られてないことから、リサイクルも容易となる。In the method for producing a ground-glass-like product of the present invention, a product mixed with a synthetic resin serving as a base material of the product is a powder having a small specific gravity of a synthetic resin powder. Therefore, when compared with the case where the inorganic powder having a higher specific gravity than the synthetic resin powder is mixed with the same weight% as the synthetic resin powder (conventional technology), the synthetic resin powder is more preferable. A large amount is mixed, and the product has a more beautiful matte tone when the synthetic resin particles are mixed. From this fact, when synthetic resin particles having a small specific gravity are mixed, even if the value of the weight% to be mixed is small, a beautiful matte tone can be obtained. Not required to some extent. Therefore, according to the method for producing a product having a matte tone according to the present invention, in order to mix a large amount of powdery synthetic resin within a range where there is no practical problem.
It is possible to manufacture a product having a high quality matte tone that is sufficiently satisfactory as a product, but having no practical problem. In addition, since a transparent synthetic resin powder having substantially the same refractive index as the transparent synthetic resin is mixed with the transparent synthetic resin serving as a base material of the product, the transparent synthetic resin has a transparent matte tone, that is, a ground glass tone. Products can be manufactured. In addition, by dispersing powder particles of a transparent synthetic resin having substantially the same refractive index as the transparent synthetic resin in a transparent synthetic resin serving as a base material of the product, a ground glass effect is obtained. (Conventional technology) becomes unnecessary. Also, the durability is higher than that of a ground glass-like coating. Furthermore, since the whole is made of a synthetic resin material, and no different material such as a coating film is used, recycling becomes easy.
【図１】本発明のスリガラス調を有する化粧料容器部品
の一実施例を示す斜視図である。FIG. 1 is a perspective view showing an embodiment of a cosmetic container part having a ground glass effect of the present invention.
【図２】上記化粧料容器部品の容壁の説明図である。FIG. 2 is an explanatory view of a wall of the cosmetic container part.
【図３】従来の化粧料容器部品の製造方法を示す説明図
である。FIG. 3 is an explanatory view showing a conventional method for producing a cosmetic container part.
【図４】従来の化粧料容器部品の容壁を示す説明図であ
る。FIG. 4 is an explanatory view showing a container wall of a conventional cosmetic container part.
Ａ キャップ １ ポリスチレン樹脂（母材） ２ ポリスチレン樹脂（ビーズ） A cap 1 Polystyrene resin (base material) 2 Polystyrene resin (beads)
Claims (4)
この透明性合成樹脂と略同じ屈折率を有する透明性合成
樹脂の粉粒体が分散され、それによって製品がスリガラ
ス調に構成されていることを特徴とするスリガラス調を
有する製品。1. A transparent synthetic resin as a base material of a product,
A ground-glass-like product characterized in that a powder of a transparent synthetic resin having substantially the same refractive index as that of the transparent synthetic resin is dispersed, whereby the product is configured in a ground-glass-like manner.
その母材に分散される透明性合成樹脂の粉粒体の屈折率
との差が０．０１未満である請求項１記載のスリガラス
調を有する製品。2. The refractive index of a transparent synthetic resin as a base material,
2. The product having a ground glass effect according to claim 1, wherein the difference from the refractive index of the transparent synthetic resin powder dispersed in the base material is less than 0.01.
脂のビーズである請求項１または２記載のスリガラス調
を有する製品。3. The product having a ground glass effect according to claim 1, wherein the transparent synthetic resin powder is beads of the transparent synthetic resin.
の透明性合成樹脂と略同じ屈折率を有しこの透明性合成
樹脂よりも融点の高い透明性合成樹脂の粉粒体を混合
し、上記透明性合成樹脂の融点と上記透明性合成樹脂の
粉粒体の融点の間の温度で、上記混合物を射出成形する
ことによりスリガラス調に構成されている製品を製造す
ることを特徴とするスリガラス調を有する製品の製法。4. A transparent synthetic resin serving as a base material of a product is mixed with a powder of a transparent synthetic resin having substantially the same refractive index as the transparent synthetic resin and having a higher melting point than the transparent synthetic resin. Then, at a temperature between the melting point of the transparent synthetic resin and the melting point of the granular material of the transparent synthetic resin, by manufacturing the mixture is injection-molded to produce a product having a ground glass-like structure. A method for producing a product with a ground-glass appearance.