JPH11228916A - Adhesive tape - Google Patents
Adhesive tapeInfo
- Publication number
- JPH11228916A JPH11228916A JP10028760A JP2876098A JPH11228916A JP H11228916 A JPH11228916 A JP H11228916A JP 10028760 A JP10028760 A JP 10028760A JP 2876098 A JP2876098 A JP 2876098A JP H11228916 A JPH11228916 A JP H11228916A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive tape
- yarns
- warp
- weft
- flat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、基布の表裏少なく
とも一方に粘着剤が塗布された粘着テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure-sensitive adhesive tape in which a pressure-sensitive adhesive is applied to at least one of the front and back of a base fabric.
【０００２】[0002]
【従来の技術】従来より、高強度で耐衝撃性の高い粘着
テープが、農業、土木、建築、運搬等の広い分野におけ
る資材や各種製品の固定用或いは収束用として盛んに使
用されている。この様な粘着テープのうち、引張り強度
の面で最も優れたものの一つとして、表層膜の長手方向
に沿ってマルチフィラメントを貼着した基布を有する粘
着テープが挙げられ、電化製品の梱包用としても、例え
ば、冷蔵庫の扉等を固定するなど比較的多く見受けられ
ている。2. Description of the Related Art Conventionally, adhesive tapes having high strength and high impact resistance have been actively used for fixing or converging materials and various products in a wide range of fields such as agriculture, civil engineering, construction, and transportation. Among such pressure-sensitive adhesive tapes, one of the most excellent in terms of tensile strength is a pressure-sensitive adhesive tape having a base cloth on which multifilaments are adhered along the longitudinal direction of a surface layer film, and is used for packing electric appliances. For example, it is relatively common to fix a door of a refrigerator or the like.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、この様
な粘着テープは、強度を高める為に比較的厚手の表層膜
が用いられているのみならず、当該表層膜に貼着されて
いるガラスやポリエステル製のマルチフィラメントにし
ても比較的強度の高いものが用いられているので柔軟性
に欠ける。その他、これらマルチフィラメント同士が個
々に独立しているので、ロールから引き剥がす際にテー
プの基布からマルチフィラメントが剥がれ、内側に存在
するテープの背にマルチフィラメントが残留することも
少なくない（以下、この様に、繊維の残留或いはロール
から剥がす際に大きな力を必要とする等ロールから好適
に剥がし難い状態を展開性が悪いと記す。）。その上、
更に、従来の粘着テープと同様に、心掛けて目印を付け
て置かない限り、テープの末端が判りにくいという課題
も存在するなど、作業性の面で多くの問題が在る。However, such an adhesive tape not only uses a relatively thick surface layer in order to increase the strength, but also uses glass or polyester adhered to the surface layer. Even a multifilament made of stainless steel has a relatively high strength and thus lacks flexibility. In addition, since these multifilaments are independent of each other, the multifilaments are peeled off from the base fabric of the tape when the multifilaments are peeled off from the roll, and the multifilaments often remain on the spine of the tape present inside (hereinafter, referred to as “multifilament”). In this manner, a state in which the fibers are hardly peeled off from the roll, such as a state in which the fibers remain or a large force is required when the fiber is peeled off from the roll, is referred to as poor expandability.) Moreover,
Further, there are many problems in terms of workability, such as a problem that the end of the tape is difficult to understand unless a mark is placed with care, as in the case of the conventional adhesive tape.
【０００４】本発明は、上記実情に鑑みて成されたもの
であって、請求項１記載の粘着テープは、柔軟性及び展
開性を好適に保ちつつ高い強度を持った粘着テープの提
供を目的とし、請求項２記載の粘着テープは、更に、目
印を付けて置かなくてもテープの末端を容易に見付ける
ことができるという付随的効果を持った粘着テープの提
供を目的とする。The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a pressure-sensitive adhesive tape having high strength while suitably maintaining flexibility and developability. Another object of the present invention is to provide a pressure-sensitive adhesive tape having an additional effect that the end of the tape can be easily found without placing a mark.
【０００５】[0005]
【課題を解決するための手段】上記課題を解決するため
に成された本発明による粘着テープは、熱可塑性樹脂を
主材とするフラットヤーンを経糸及び緯糸として織製し
た織布の表裏少なくとも一方の面に、熱可塑性樹脂より
成る表層膜を被着した基布を具備する粘着テープにおい
て、前記経糸又は緯糸の少なくとも一方に、同一方向に
配向するフラットヤーンが全体的に重なり合った重層部
を有することを特徴とする。The pressure-sensitive adhesive tape according to the present invention, which has been made to solve the above-mentioned problems, comprises at least one of a front and a back of a woven fabric woven as a warp and a weft using flat yarn mainly composed of a thermoplastic resin. In the pressure-sensitive adhesive tape comprising a base cloth having a surface layer made of a thermoplastic resin adhered to the surface thereof, at least one of the warp or weft has a multilayer portion in which flat yarns oriented in the same direction are entirely overlapped. It is characterized by the following.
【０００６】基布を構成するフラットヤーンの主材とし
て用いる熱可塑性樹脂としては、ポリオレフィンが一般
的であり、具体的にはポリプロピレン、最も好ましいも
のの一つとして高密度ポリエチレンが挙げられる。フラ
ットヤーンの態様としては、単層フラットヤーン或いは
複層フラットヤーンであって、５０ｄ〜２０００ｄ程度
で、糸幅：０．３〜４．０ｍｍ程度、引張強さ：５．０
〜１０ｇ／ｄ程度、伸び率：５．０〜４０．０％程度を
目安とする。As the thermoplastic resin used as the main material of the flat yarn constituting the base fabric, polyolefin is generally used, specifically, polypropylene, and one of the most preferable ones is high-density polyethylene. The mode of the flat yarn is a single-layer flat yarn or a multi-layer flat yarn, which is about 50d to 2000d, yarn width: about 0.3 to 4.0mm, and tensile strength: 5.0.
Approximately 10 to 10 g / d, elongation: approximately 5.0 to 40.0%.
【０００７】織組織としては、テープの長手方向或いは
幅方向への柔軟性及び強度を重視して、平織や斜文織を
採用することが望ましい。前記重層部は、経糸又は緯糸
の全ての糸が重層部を構成していても良いし、一部の糸
のみが重層部を構成していても良い。又、重層部におい
ては、各フラットヤーンの間に、それらのフラットヤー
ンと交差する他のフラットヤーンが所々に介在していて
も良い。尚、重層部においては、相重なるフラットヤー
ンを接着等によって一体化せず、織布の変形に伴って長
手方向へ多少ずれ得る状態にしておく。As the woven structure, it is desirable to use plain weave or oblique weave with emphasis on flexibility and strength in the longitudinal direction or width direction of the tape. In the multilayer portion, all the warp or weft yarns may form the multilayer portion, or only some of the yarns may form the multilayer portion. In the multilayer portion, other flat yarns intersecting with the flat yarns may be interposed between the flat yarns. In the multilayer portion, the overlapping flat yarns are not integrated by bonding or the like, but in a state where the flat yarns can be slightly shifted in the longitudinal direction as the woven fabric is deformed.
【０００８】表層膜の素材としては、密度（ＴＩＳ Ｋ
ー６７６０）：０．８６０〜０．９６０ｇ／立方センチ
メートルのエチレン（直鎖状又は分岐状の）の単独重合
体、エチレンとＣ４〜Ｃ１０などのα−オレフィンを共
重合したエチレン・α−オレフィン共重合体、エチレン
・アクリル酸共重合体、エチレン・アクリル酸メタル共
重合体、エチレン・メタクリル酸共重合体、エチレン・
酢酸ビニル共重合体等のエチレン系樹脂、又は、これら
の混合物や、ポリプロピレン系樹脂等が挙げられる。柔
軟性や織布との接着性、コスト等を考慮すれば、密度：
０．８８０〜０．９３５ｇ／立方センチメートル程度の
エチレンの単独重合体、エチレン・α−オレフィン共重
合体、又は、これらの混合物が好ましい。厚みの実用値
としては１５μｍ〜２００μｍである。用途に合わせた
柔軟性を持たせるべく素材と厚みを適宜組み合わせれば
良い。As a material for the surface layer film, a density (TIS K
-6760): 0.860 to 0.960 g / cubic centimeter of ethylene (linear or branched) homopolymer, ethylene / α-olefin copolymer obtained by copolymerizing ethylene and α-olefin such as C4 to C10 Copolymer, ethylene / acrylic acid copolymer, ethylene / acrylic acid metal copolymer, ethylene / methacrylic acid copolymer, ethylene / acrylic acid copolymer
Examples include an ethylene resin such as a vinyl acetate copolymer, a mixture thereof, and a polypropylene resin. Taking into account flexibility, adhesion to woven fabric, cost, etc., the density:
An ethylene homopolymer, an ethylene / α-olefin copolymer, or a mixture thereof of about 0.880 to 0.935 g / cubic centimeter is preferred. A practical value of the thickness is 15 μm to 200 μm. The material and the thickness may be appropriately combined so as to have flexibility according to the application.
【０００９】前記重層部を構成するフラットヤーンは、
用途に応じて表側に位置するフラットヤーンと裏側に位
置するフラットヤーンの色を相異なる色に設定しても良
く、そうすることによって、粘着テープ自体の表裏の色
合いを異ならせることができる。尚、重層部を構成する
フラットヤーンのうち最上位に存在するフラットヤーン
と最下位に存在するフラットヤーンの色を、粘着テープ
の表裏の色として反映させるには、粘着テープの基布を
覆う表層膜や粘着剤として透明性を持ったものを選択す
る必要がある。又、前記重層部を構成するフラットヤー
ンには、物性を著しく損ねない範囲で、表側に位置する
フラットヤーンと裏側に位置するフラットヤーンの材質
が異なっていても良い、前記素材以外のフラットヤーン
を強度や柔軟性を高める目的で所々に介在させても良
い。[0009] The flat yarn constituting the multilayer portion is
The color of the flat yarn located on the front side and the color of the flat yarn located on the back side may be set to different colors depending on the application, so that the front and back colors of the adhesive tape itself can be different. In order to reflect the colors of the uppermost flat yarn and the lowermost flat yarn among the flat yarns forming the multilayer portion as the front and back colors of the adhesive tape, the surface layer covering the base cloth of the adhesive tape is required. It is necessary to select a transparent film or adhesive. Further, the flat yarn constituting the multilayer portion may have a different material from the flat yarn located on the front side and the flat yarn located on the back side, as long as the physical properties are not significantly impaired. It may be interposed in some places for the purpose of increasing strength and flexibility.
【００１０】[0010]
【発明の実施の形態】以下、本発明による粘着テープの
実施の形態を図面に基づき説明する。以下の例で用いた
織布４は、高密度ポリエチレンを素材とし、３８０ｄ，
１．１５ｍｍ幅で、引張強さ：７．５ｇ／ｄ，伸び率：
２０．０％のフラットヤーンを、経２２本／インチ（二
重であるため実際には４４本）、緯２０本／インチで打
ち込み織製したものである。この織布４の表裏に、溶融
ラミネート法等で厚さ２０μｍの低密度ポリエチレンか
ら成る表層膜５を各々被着することによって基布６を形
成し、当該基布６に粘着剤８を塗布することによって本
発明による粘着テープとなる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the pressure-sensitive adhesive tape according to the present invention will be described with reference to the drawings. The woven fabric 4 used in the following example is made of high-density polyethylene,
1.15 mm width, tensile strength: 7.5 g / d, elongation:
A 20.0% flat yarn is driven and woven at a warp of 22 yarns / inch (actually 44 yarns due to being double) and a weft of 20 yarns / inch. A base layer 6 is formed by applying a surface layer 5 made of low-density polyethylene with a thickness of 20 μm on the front and back of the woven cloth 4 by a melt lamination method or the like, and an adhesive 8 is applied to the base cloth 6. Thereby, the pressure-sensitive adhesive tape according to the present invention is obtained.
【００１１】粘着剤８は、前記基布６の表面へ、２０〜
６０ｇ／平方メートルの割合で塗布するが、基布６と粘
着剤８との投錨力を高めるべく、基布６の表面に対して
コロナ放電処理等の前処理を行うことが望ましい。粘着
剤８としては、アクリル系粘着剤、ウレタン系粘着剤、
ビニル系粘着剤、シリコン系粘着剤、ゴム系粘着剤等が
挙げられるが、接着強度、剥がれ具合の良さ（展開
性）、耐候性、経済性等の点ではアクリル系粘着剤が望
ましい。The adhesive 8 is applied to the surface of the base cloth 6 by 20 to 20.
The coating is applied at a rate of 60 g / m 2, but it is desirable to perform a pretreatment such as a corona discharge treatment on the surface of the base cloth 6 in order to increase the anchoring force between the base cloth 6 and the adhesive 8. Examples of the adhesive 8 include an acrylic adhesive, a urethane adhesive,
A vinyl-based adhesive, a silicone-based adhesive, a rubber-based adhesive, and the like can be given, and an acrylic-based adhesive is desirable in terms of adhesive strength, good peeling (developability), weather resistance, economy, and the like.
【００１２】粘着テープの基布６となる織布４の織り方
として平織と斜文織を挙げてその織組織を説明する。図
１は、経糸（緯糸３でも良い。以下、他の織り方につい
ても重層部７を構成するものとして経糸２を選択するか
緯糸３を選択するかで織組織に差異は生じない。よっ
て、経緯のいずれか一方の糸で重層部７を構成している
場合は、経糸２が重層部７を構成するものとして説明す
る。）２たる全ての糸が二重のフラットヤーン１から成
る重層部７を構成している平織の織組織を示したもので
あり、図２は、経糸２及び緯糸３たる全ての糸が重層部
７を構成している平織の織組織を示したものである。図
５（図中破線部はフラットヤーン一重の場合もあるし、
複数のフラットヤーンが重合している場合もある。）の
断面図が示す如く、緯糸３は、重層部７を構成する経糸
２を交互に掻い潜った状態に通され、隣接する緯糸３
は、相互に表裏相反する側へ露出して、それら緯糸３二
列を１単位として同じ組織パターンが繰り返される。The weaving structure of the woven fabric 4 serving as the base fabric 6 of the adhesive tape will be described with reference to plain weave and oblique weave. FIG. 1 shows a warp (weft 3 may be used. Hereinafter, there is no difference in the weaving structure depending on whether the warp 2 or the weft 3 is selected to constitute the multilayer part 7 in other weaving methods. In the case where the multilayer portion 7 is constituted by any one of the yarns, the description will be made on the assumption that the warp yarn 2 constitutes the multilayer portion 7.) The multilayer portion in which all the two yarns are formed of the double flat yarn 1. FIG. 2 shows a plain weave structure in which all the yarns, that is, the warp yarns 2 and the weft yarns 3, constitute the multilayer part 7. FIG. 5 (the broken line in the figure may be a single flat yarn,
A plurality of flat yarns may be superposed. As shown in the cross-sectional view of FIG. 3, the weft 3 is passed through the warp 2 constituting the multilayer part 7 alternately and sunk, and the adjacent weft 3
Are exposed to the opposite sides, and the same weave pattern is repeated with the three rows of wefts as one unit.
【００１３】図３に示す組織は、平織の変形例であり、
上記例の様に重層部７を構成する経糸２の各フラットヤ
ーン１，１を束にして打ち込むのではなく、図６の断面
図の如く、重層部７を構成する緯糸３の各フラットヤー
ン１，１について打ち込み状態を異ならせたものであ
る。即ち、二重の重層部７を構成する緯糸３の上位のフ
ラットヤーン１が、上下二重に配された二本のフラット
ヤーン１，１の間から経糸２一本毎に上方へ出没する一
方、緯糸３の下位のフラットヤーン１が、上下二重に配
された経糸２の下から、経糸２一本毎に当該経糸２の上
方へ出没する。先の緯糸３に隣接する緯糸３は、先の緯
糸３と互い違いに出没し、同様の断面形状を呈するよう
に打ち込まれる。そして、それら緯糸３二列を１単位と
して同じ組織パターンが繰り返される。The structure shown in FIG. 3 is a modification of a plain weave,
Instead of bundling the flat yarns 1 and 1 of the warp 2 constituting the multilayer portion 7 as in the above example, each flat yarn 1 of the weft 3 constituting the multilayer portion 7 is driven as shown in the sectional view of FIG. , 1 have different driving states. That is, the upper flat yarn 1 of the weft 3 constituting the double layer portion 7 protrudes upward and downward for every two warp yarns from between the two flat yarns 1, 1 arranged in the upper and lower double. The lower flat yarn 1 of the weft 3 protrudes and descends above the warp 2 for each warp 2 from under the warp 2 which is arranged vertically. The weft 3 adjacent to the previous weft 3 alternately appears and disappears with the previous weft 3, and is driven so as to have a similar cross-sectional shape. Then, the same texture pattern is repeated with the three rows of wefts as one unit.
【００１４】図４は、経糸２たる全ての糸が二重の重層
部７を構成している斜文織の織組織を示したものであ
る。図７の断面図が示すごとく、緯糸３は、重層部７を
三つ毎に掻い潜り、一列毎に経糸２一本分ずつ位相がず
れ、緯糸３三列を１単位として同じ組織パターンが繰り
返される。FIG. 4 shows the weave structure of the oblique weaving in which all the yarns as the warp yarns 2 constitute the double layer portion 7. As shown in the cross-sectional view of FIG. 7, the weft 3 scrapes down the multilayer portion 3 every three, the phase shifts by two warps in each row, and the same design pattern is repeated with three rows of the weft 3 as one unit. It is.
【００１５】上記織り方で形成された織布４は、重層部
７を構成する二本のフラットヤーン１，１としてそれぞ
れ異なる色のフラットヤーン１を用い、粘着剤８及び表
層膜５としてそれぞれ透明なものを用いることによっ
て、粘着テープの表裏が、重層部７の上位及び下位のフ
ラットヤーンの色彩を反映した異なる色と成る。The woven fabric 4 formed by the above-mentioned weaving method uses the flat yarns 1 of different colors as the two flat yarns 1 constituting the multilayer portion 7, and the adhesive 8 and the surface film 5 are transparent respectively. By using a suitable material, the front and back of the adhesive tape have different colors reflecting the colors of the upper and lower flat yarns of the multilayer portion 7.
【００１６】以上の如く織製された織布４と表層膜５と
で構成された基布６を具備する粘着テープは、前記重層
部７の存在によって、当該重層部７を構成するフラット
ヤーン１の配向方向に、５０ｍｍ幅の粘着テープで２０
０ｋｇを超える引張り強度を持ち、２５ｍｍ幅の粘着テ
ープで７００ｋｇを超える衝撃強度を持つこととなる。
それにも関わらず、重層部７を構成する各フラットヤー
ン１が各々独立しているために、当該粘着テープが湾曲
した際にも配向方向へそれぞれ比較的自由に動くことが
できるので、粘着テープ自体の柔軟性を失うことはな
い。又、各フラットヤーン１が織布４たる一体物となっ
て表層膜５と接合しているので、個々のフラットヤーン
１が表層膜５から剥離して内側に巻き付けられている粘
着テープの背面に残留するといった不具合も生じない。The adhesive tape provided with the base cloth 6 composed of the woven cloth 4 and the surface layer film 5 woven as described above, is provided by the flat yarn 1 forming the multilayer part 7 due to the existence of the multilayer part 7. 20mm with 50mm width adhesive tape
It has a tensile strength exceeding 0 kg and an impact strength exceeding 700 kg with a 25 mm wide adhesive tape.
Nevertheless, since the flat yarns 1 constituting the multilayer portion 7 are independent of each other, the adhesive tape can move relatively freely in the orientation direction even when the adhesive tape is curved. You do not lose flexibility. In addition, since each flat yarn 1 is integrated with the surface film 5 as an integral member of the woven fabric 4, the individual flat yarns 1 are peeled off from the surface film 5 and are placed on the back surface of the adhesive tape wound inside. There is no problem of remaining.
【００１７】尚、前記引張り強度と衝撃強度の測定方法
は、以下の通りである。 引張り強度の測定方法（ＪＩＳ Ｌ−１０９６） ５０ｍｍ幅×３００ｍｍ長の試料９を用い、図９の如
く、長手方向の両端部を２００ｍｍの間隔で掴み、３０
０ｍｍ／分で引張る（上部移動、下部固定とした装置も
ある。）。 衝撃強度の測定方法（自社法） ２５ｍｍ幅×超１０００ｍｍ長の試料１０を用い、図１
０の如く、半径１０００ｍｍで揺動するウエイト（１
０．８ｋｇ）１１で試料１０の一端を支持し、当該ウエ
イト１１の垂下位置から水平方向へ１０００ｍｍ程度離
隔した定位置１２で試料１０の他端を支持（一端の支持
位置と他端の支持位置の間隔を１０００ｍｍとする。）
した状態で、前記ウエイト１１を、前記定位置１２に向
かって振り上げ次いで放すという一連の作業を行い、前
記試料１０の破断が生じた振り上げ角度θを次式へ代入
し、導かれた数値を衝撃強度とする。 衝撃強度（ｋｇ−ｃｍ／５０ｍｍ幅）＝（１−ｃｏｓ
θ）×Ｗ×Ｌ Ｗ（ウエイト重量）：１０．８ｋｇ Ｌ（揺動半径） ：１００ｃｍ（１０００ｍｍ）The method for measuring the tensile strength and the impact strength is as follows. Tensile strength measurement method (JIS L-1096) Using a sample 9 having a width of 50 mm and a length of 300 mm, as shown in FIG.
Pull at 0 mm / min. (Some devices are moved upward and fixed at the bottom.) Method for measuring impact strength (in-house method) Using a sample 10 having a width of 25 mm and a length of more than 1000 mm, FIG.
0, the weight (1
0.8 kg) 11 supports one end of the sample 10, and supports the other end of the sample 10 at a fixed position 12 separated from the hanging position of the weight 11 by about 1000 mm in the horizontal direction (a support position of one end and a support position of the other end) Is 1000 mm.)
In this state, the weight 11 is swung up toward the fixed position 12 and then released, and the swing angle θ at which the sample 10 is broken is substituted into the following equation. Strength. Impact strength (kg-cm / 50 mm width) = (1-cos
θ) × W × L W (weight of weight): 10.8 kg L (radius of oscillation): 100 cm (1000 mm)
【００１８】[0018]
【発明の効果】以上の如く本発明による粘着テープを使
用すれば、請求項１記載の粘着テープは、引張りや衝撃
に対し高い強度を必要とする用途に用いることができる
にも関わらず、良好な柔軟性と展開性によって高い作業
効率を実現することができ、請求項２記載の粘着テープ
にあっては、表裏に現われる色彩が異なることによっ
て、ガラス等の透明な部材に用いる場合には、表裏いず
れから見ても見苦しくない状態で使用することができる
他、ロール状に巻き付けられた粘着テープにあっては、
表裏の色彩に極端な差を付けることによって、粘着テー
プ表面の色彩と断面の色彩との違いから使用後に目印を
付けて置かなくても、テープの末端を容易に見付けるこ
とができるという付随的効果を奏する。As described above, when the pressure-sensitive adhesive tape according to the present invention is used, the pressure-sensitive adhesive tape according to claim 1 can be used in applications requiring high strength against tension and impact. High working efficiency can be realized by flexible and expandable, and in the pressure-sensitive adhesive tape according to claim 2, when the colors appearing on the front and back are different, when used for a transparent member such as glass, In addition to being able to be used in a state that is not difficult to see from both sides, in the case of adhesive tape wound in a roll shape,
By adding an extreme difference between the colors on the front and back, it is possible to easily find the end of the tape without having to place a mark after use because of the difference between the color of the adhesive tape surface and the color of the cross section. To play.
【図１】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 1 is a perspective view showing an example of a woven structure of a woven fabric of an adhesive tape according to the present invention.
【図２】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 2 is a perspective view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図３】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 3 is a perspective view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図４】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 4 is a perspective view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図５】（イ）（ロ）本発明による粘着テープの織布の
織組織の一例を示す断面図である。5 (a) and (b) are cross-sectional views showing an example of the woven structure of the woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図６】（イ）（ロ）本発明による粘着テープの織布の
織組織の一例を示す断面図である。FIG. 6 is a sectional view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図７】（イ）（ロ）（ハ）本発明による粘着テープの
織布の織組織の一例を示す断面図である。7 (a), (b) and (c) are cross-sectional views showing an example of the woven structure of the woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図８】本発明による粘着テープの一例を示す概略図で
ある。FIG. 8 is a schematic view showing an example of the pressure-sensitive adhesive tape according to the present invention.
【図９】引張り強度の測定方法を示す概念図である。FIG. 9 is a conceptual diagram showing a method for measuring tensile strength.
【図１０】衝撃強度の測定方法を示す概念図である。FIG. 10 is a conceptual diagram showing a method for measuring impact strength.
１ フラットヤーン ２ 経糸 ３ 緯糸 ４ 織布 ５ 表層膜 ６ 基布 ７ 重層部 ８ 粘着剤 DESCRIPTION OF SYMBOLS 1 Flat yarn 2 Warp 3 Weft 4 Woven cloth 5 Surface layer 6 Base cloth 7 Overlay part 8 Adhesive
─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成１１年１月２５日[Submission date] January 25, 1999
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】全文[Correction target item name] Full text
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【書類名】 明細書[Document Name] Statement
【発明の名称】 粘着テープ[Title of the Invention] Adhesive tape
【特許請求の範囲】[Claims]
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【発明の属する技術分野】本発明は、基布の表裏少なく
とも一方に粘着剤が塗布された粘着テープに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure-sensitive adhesive tape in which a pressure-sensitive adhesive is applied to at least one of the front and back of a base fabric.
【０００２】[0002]
【従来の技術】従来より、高強度で耐衝撃性の高い粘着
テープが、農業、土木、建築、運搬等の広い分野におけ
る資材や各種製品の固定用或いは収束用として盛んに使
用されている。この様な粘着テープのうち、引張り強度
の面で最も優れたものの一つとして、表層膜の長手方向
に沿ってマルチフィラメントを貼着した基布を有する粘
着テープが挙げられ、電化製品の梱包用としても、例え
ば、冷蔵庫の扉等を固定するなど比較的多く見受けられ
ている。2. Description of the Related Art Conventionally, adhesive tapes having high strength and high impact resistance have been actively used for fixing or converging materials and various products in a wide range of fields such as agriculture, civil engineering, construction, and transportation. Among such pressure-sensitive adhesive tapes, one of the most excellent in terms of tensile strength is a pressure-sensitive adhesive tape having a base cloth on which multifilaments are adhered along the longitudinal direction of a surface layer film, and is used for packing electric appliances. For example, it is relatively common to fix a door of a refrigerator or the like.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、この様
な粘着テープは、強度を高める為に比較的厚手の表層膜
が用いられているのみならず、当該表層膜に貼着されて
いるガラスやポリエステル製のマルチフィラメントにし
ても比較的強度の高いものが用いられているので柔軟性
に欠ける。その他、これらマルチフィラメント同士が個
々に独立しているので、ロールから引き剥がす際にテー
プの基布からマルチフィラメントが剥がれ、内側に存在
するテープの背にマルチフィラメントが残留することも
少なくない（以下、この様に、繊維の残留或いはロール
から剥がす際に大きな力を必要とする等ロールから好適
に剥がし難い状態を展開性が悪いと記す。）。その上、
更に、従来の粘着テープと同様に、心掛けて目印を付け
て置かない限り、テープの末端が判りにくいという課題
も存在するなど、作業性の面で多くの問題が在る。However, such an adhesive tape not only uses a relatively thick surface layer in order to increase the strength, but also uses glass or polyester adhered to the surface layer. Even a multifilament made of stainless steel has a relatively high strength and thus lacks flexibility. In addition, since these multifilaments are independent of each other, the multifilaments are peeled off from the base fabric of the tape when the multifilaments are peeled off from the roll, and the multifilaments often remain on the spine of the tape present inside (hereinafter, referred to as “multifilament”). In this manner, a state in which the fibers are hardly peeled off from the roll, such as a state in which the fibers remain or a large force is required when the fiber is peeled off from the roll, is referred to as poor expandability.) Moreover,
Further, there are many problems in terms of workability, such as a problem that the end of the tape is difficult to understand unless a mark is placed with care, as in the case of the conventional adhesive tape.
【０００４】本発明は、上記実情に鑑みて成されたもの
であって、請求項１記載の粘着テープは、柔軟性及び展
開性を好適に保ちつつ高い強度を持った粘着テープの提
供を目的とし、請求項２記載の粘着テープは、更に、目
印を付けて置かなくてもテープの末端を容易に見付ける
ことができるという付随的効果を持った粘着テープの提
供を目的とする。The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a pressure-sensitive adhesive tape having high strength while suitably maintaining flexibility and developability. Another object of the present invention is to provide a pressure-sensitive adhesive tape having an additional effect that the end of the tape can be easily found without placing a mark.
【０００５】[0005]
【課題を解決するための手段】上記課題を解決するため
に成された本発明による粘着テープは、熱可塑性樹脂を
主材とするフラットヤーンを経糸及び緯糸として織製し
た織布の表裏少なくとも一方の面に、熱可塑性樹脂より
成る表層膜を被着した基布を具備する粘着テープにおい
て、前記経糸又は緯糸の少なくとも一方に、同一方向に
配向するフラットヤーンが、非接着状態で全体的に重な
り合った重層部を有することを特徴とする。The pressure-sensitive adhesive tape according to the present invention, which has been made to solve the above-mentioned problems, comprises at least one of a front and a back of a woven fabric woven as a warp and a weft using flat yarn mainly composed of a thermoplastic resin. the surface, the adhesive tape comprising a base fabric having deposited a surface layer film composed of a thermoplastic resin, at least one of the warp or weft, flat yarn oriented in the same direction, overall manner in unbonded It is characterized by having overlapping layer portions.
【０００６】基布を構成するフラットヤーンの主材とし
て用いる熱可塑性樹脂としては、ポリオレフィンが一般
的であり、具体的にはポリプロピレン、最も好ましいも
のの一つとして高密度ポリエチレンが挙げられる。フラ
ットヤーンの態様としては、単層フラットヤーン或いは
複層フラットヤーンであって、５０ｄ〜２０００ｄ程度
で、糸幅：０．３〜４．０ｍｍ程度、引張強さ：５．０
〜１０ｇ／ｄ程度、伸び率：５．０〜４０．０％程度を
目安とする。As the thermoplastic resin used as the main material of the flat yarn constituting the base fabric, polyolefin is generally used, specifically, polypropylene, and one of the most preferable ones is high-density polyethylene. The mode of the flat yarn is a single-layer flat yarn or a multi-layer flat yarn, which is about 50d to 2000d, yarn width: about 0.3 to 4.0mm, and tensile strength: 5.0.
Approximately 10 to 10 g / d, elongation: approximately 5.0 to 40.0%.
【０００７】織組織としては、テープの長手方向或いは
幅方向への柔軟性及び強度を重視して、平織や斜文織を
採用することが望ましい。前記重層部は、経糸又は緯糸
の全ての糸が重層部を構成していても良いし、一部の糸
のみが重層部を構成していても良い。又、重層部におい
ては、各フラットヤーンの間に、それらのフラットヤー
ンと交差する他のフラットヤーンが所々に介在していて
も良い。尚、重層部においては、相重なるフラットヤー
ンを接着等によって一体化せず、織布の変形に伴って長
手方向へ多少ずれ得る状態にしておく。As the woven structure, it is desirable to use plain weave or oblique weave with emphasis on flexibility and strength in the longitudinal direction or width direction of the tape. In the multilayer portion, all the warp or weft yarns may form the multilayer portion, or only some of the yarns may form the multilayer portion. In the multilayer portion, other flat yarns intersecting with the flat yarns may be interposed between the flat yarns. In the multilayer portion, the overlapping flat yarns are not integrated by bonding or the like, but in a state where the flat yarns can be slightly shifted in the longitudinal direction as the woven fabric is deformed.
【０００８】表層膜の素材としては、密度（ＴＩＳ Ｋ
ー６７６０）：０．８６０〜０．９６０ｇ／立方センチ
メートルのエチレン（直鎖状又は分岐状の）の単独重合
体、エチレンとＣ４〜Ｃ１０などのα−オレフィンを共
重合したエチレン・α−オレフィン共重合体、エチレン
・アクリル酸共重合体、エチレン・アクリル酸メタル共
重合体、エチレン・メタクリル酸共重合体、エチレン・
酢酸ビニル共重合体等のエチレン系樹脂、又は、これら
の混合物や、ポリプロピレン系樹脂等が挙げられる。柔
軟性や織布との接着性、コスト等を考慮すれば、密度：
０．８８０〜０．９３５ｇ／立方センチメートル程度の
エチレンの単独重合体、エチレン・α−オレフィン共重
合体、又は、これらの混合物が好ましい。厚みの実用値
としては１５μｍ〜２００μｍである。用途に合わせた
柔軟性を持たせるべく素材と厚みを適宜組み合わせれば
良い。As a material for the surface layer film, a density (TIS K
-6760): 0.860 to 0.960 g / cubic centimeter of ethylene (linear or branched) homopolymer, ethylene / α-olefin copolymer obtained by copolymerizing ethylene and α-olefin such as C4 to C10 Copolymer, ethylene / acrylic acid copolymer, ethylene / acrylic acid metal copolymer, ethylene / methacrylic acid copolymer, ethylene / acrylic acid copolymer
Examples include an ethylene resin such as a vinyl acetate copolymer, a mixture thereof, and a polypropylene resin. Taking into account flexibility, adhesion to woven fabric, cost, etc., the density:
An ethylene homopolymer, an ethylene / α-olefin copolymer, or a mixture thereof of about 0.880 to 0.935 g / cubic centimeter is preferred. A practical value of the thickness is 15 μm to 200 μm. The material and the thickness may be appropriately combined so as to have flexibility according to the application.
【０００９】前記重層部を構成するフラットヤーンは、
用途に応じて表側に位置するフラットヤーンと裏側に位
置するフラットヤーンの色を相異なる色に設定しても良
く、そうすることによって、粘着テープ自体の表裏の色
合いを異ならせることができる。尚、重層部を構成する
フラットヤーンのうち最上位に存在するフラットヤーン
と最下位に存在するフラットヤーンの色を、粘着テープ
の表裏の色として反映させるには、粘着テープの基布を
覆う表層膜や粘着剤として透明性を持ったものを選択す
る必要がある。又、前記重層部を構成するフラットヤー
ンには、物性を著しく損ねない範囲で、表側に位置する
フラットヤーンと裏側に位置するフラットヤーンの材質
が異なっていても良い、前記素材以外のフラットヤーン
を強度や柔軟性を高める目的で所々に介在させても良
い。[0009] The flat yarn constituting the multilayer portion is
The color of the flat yarn located on the front side and the color of the flat yarn located on the back side may be set to different colors depending on the application, so that the front and back colors of the adhesive tape itself can be different. In order to reflect the colors of the uppermost flat yarn and the lowermost flat yarn among the flat yarns forming the multilayer portion as the front and back colors of the adhesive tape, the surface layer covering the base cloth of the adhesive tape is required. It is necessary to select a transparent film or adhesive. Further, the flat yarn constituting the multilayer portion may have a different material from the flat yarn located on the front side and the flat yarn located on the back side, as long as the physical properties are not significantly impaired. It may be interposed in some places for the purpose of increasing strength and flexibility.
【００１０】[0010]
【発明の実施の形態】以下、本発明による粘着テープの
実施の形態を図面に基づき説明する。以下の例で用いた
織布４は、高密度ポリエチレンを素材とし、３８０ｄ，
１．１５ｍｍ幅で、引張強さ：７．５ｇ／ｄ，伸び率：
２０．０％のフラットヤーンを、経２２本／インチ（二
重であるため実際には４４本）、緯２０本／インチで打
ち込み織製したものである。この織布４の表裏に、溶融
ラミネート法等で厚さ２０μｍの低密度ポリエチレンか
ら成る表層膜５を各々被着することによって基布６を形
成し、当該基布６に粘着剤８を塗布することによって本
発明による粘着テープとなる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the pressure-sensitive adhesive tape according to the present invention will be described with reference to the drawings. The woven fabric 4 used in the following example is made of high-density polyethylene,
1.15 mm width, tensile strength: 7.5 g / d, elongation:
A 20.0% flat yarn is driven and woven at a warp of 22 yarns / inch (actually 44 yarns due to being double) and a weft of 20 yarns / inch. A base layer 6 is formed by applying a surface layer 5 made of low-density polyethylene with a thickness of 20 μm on the front and back of the woven cloth 4 by a melt lamination method or the like, and an adhesive 8 is applied to the base cloth 6. Thereby, the pressure-sensitive adhesive tape according to the present invention is obtained.
【００１１】粘着剤８は、前記基布６の表面へ、２０〜
６０ｇ／平方メートルの割合で塗布するが、基布６と粘
着剤８との投錨力を高めるべく、基布６の表面に対して
コロナ放電処理等の前処理を行うことが望ましい。粘着
剤８としては、アクリル系粘着剤、ウレタン系粘着剤、
ビニル系粘着剤、シリコン系粘着剤、ゴム系粘着剤等が
挙げられるが、接着強度、剥がれ具合の良さ（展開
性）、耐候性、経済性等の点ではアクリル系粘着剤が望
ましい。The adhesive 8 is applied to the surface of the base cloth 6 by 20 to 20.
The coating is applied at a rate of 60 g / m 2, but it is desirable to perform a pretreatment such as a corona discharge treatment on the surface of the base cloth 6 in order to increase the anchoring force between the base cloth 6 and the adhesive 8. Examples of the adhesive 8 include an acrylic adhesive, a urethane adhesive,
A vinyl-based adhesive, a silicone-based adhesive, a rubber-based adhesive, and the like can be given, and an acrylic-based adhesive is desirable in terms of adhesive strength, good peeling (developability), weather resistance, economy, and the like.
【００１２】粘着テープの基布６となる織布４の織り方
として平織と斜文織を挙げてその織組織を説明する。図
１は、経糸（緯糸３でも良い。以下、他の織り方につい
ても重層部７を構成するものとして経糸２を選択するか
緯糸３を選択するかで織組織に差異は生じない。よっ
て、経緯のいずれか一方の糸で重層部７を構成している
場合は、経糸２が重層部７を構成するものとして説明す
る。）２たる全ての糸が二重のフラットヤーン１から成
る重層部７を構成している平織の織組織を示したもので
あり、図２は、経糸２及び緯糸３たる全ての糸が重層部
７を構成している平織の織組織を示したものである。図
５（図中破線部はフラットヤーン一重の場合もあるし、
複数のフラットヤーンが重合している場合もある。）の
断面図が示す如く、緯糸３は、重層部７を構成する経糸
２を交互に掻い潜った状態に通され、隣接する緯糸３
は、相互に表裏相反する側へ露出して、それら緯糸３二
列を１単位として同じ組織パターンが繰り返される。The weaving structure of the woven fabric 4 serving as the base fabric 6 of the adhesive tape will be described with reference to plain weave and oblique weave. FIG. 1 shows a warp (weft 3 may be used. Hereinafter, there is no difference in the weaving structure depending on whether the warp 2 or the weft 3 is selected to constitute the multilayer part 7 in other weaving methods. In the case where the multilayer portion 7 is constituted by any one of the yarns, the description will be made on the assumption that the warp yarn 2 constitutes the multilayer portion 7.) The multilayer portion in which all the two yarns are formed of the double flat yarn 1. FIG. 2 shows a plain weave structure in which all the yarns, that is, the warp yarns 2 and the weft yarns 3, constitute the multilayer part 7. FIG. 5 (the broken line in the figure may be a single flat yarn,
A plurality of flat yarns may be superposed. As shown in the cross-sectional view of FIG. 3, the weft 3 is passed through the warp 2 constituting the multilayer part 7 alternately and sunk, and the adjacent weft 3
Are exposed to the opposite sides, and the same weave pattern is repeated with the three rows of wefts as one unit.
【００１３】図３に示す組織は、平織の変形例であり、
上記例の様に重層部７を構成する経糸２の各フラットヤ
ーン１，１を束にして打ち込むのではなく、図６の断面
図の如く、重層部７を構成する緯糸３の各フラットヤー
ン１，１について打ち込み状態を異ならせたものであ
る。即ち、二重の重層部７を構成する緯糸３の上位のフ
ラットヤーン１が、上下二重に配された二本のフラット
ヤーン１，１の間から経糸２一本毎に上方へ出没する一
方、緯糸３の下位のフラットヤーン１が、上下二重に配
された経糸２の下から、経糸２一本毎に当該経糸２の上
方へ出没する。先の緯糸３に隣接する緯糸３は、先の緯
糸３と互い違いに出没し、同様の断面形状を呈するよう
に打ち込まれる。そして、それら緯糸３二列を１単位と
して同じ組織パターンが繰り返される。The structure shown in FIG. 3 is a modification of a plain weave,
Instead of bundling the flat yarns 1 and 1 of the warp 2 constituting the multilayer portion 7 as in the above example, each flat yarn 1 of the weft 3 constituting the multilayer portion 7 is driven as shown in the sectional view of FIG. , 1 have different driving states. That is, the upper flat yarn 1 of the weft 3 constituting the double layer portion 7 protrudes upward and downward for every two warp yarns from between the two flat yarns 1, 1 arranged in the upper and lower double. The lower flat yarn 1 of the weft 3 protrudes and descends above the warp 2 for each warp 2 from under the warp 2 which is arranged vertically. The weft 3 adjacent to the previous weft 3 alternately appears and disappears with the previous weft 3, and is driven so as to have a similar cross-sectional shape. Then, the same texture pattern is repeated with the three rows of wefts as one unit.
【００１４】図４は、経糸２たる全ての糸が二重の重層
部７を構成している斜文織の織組織を示したものであ
る。図７の断面図が示すごとく、緯糸３は、重層部７を
三つ毎に掻い潜り、一列毎に経糸２一本分ずつ位相がず
れ、緯糸３三列を１単位として同じ組織パターンが繰り
返される。FIG. 4 shows the weave structure of the oblique weaving in which all the yarns as the warp yarns 2 constitute the double layer portion 7. As shown in the cross-sectional view of FIG. 7, the weft 3 scrapes down the multilayer portion 3 every three, the phase shifts by two warps in each row, and the same design pattern is repeated with three rows of the weft 3 as one unit. It is.
【００１５】上記織り方で形成された織布４は、重層部
７を構成する二本のフラットヤーン１，１としてそれぞ
れ異なる色のフラットヤーン１を用い、粘着剤８及び表
層膜５としてそれぞれ透明なものを用いることによっ
て、粘着テープの表裏が、重層部７の上位及び下位のフ
ラットヤーンの色彩を反映した異なる色と成る。The woven fabric 4 formed by the above-mentioned weaving method uses the flat yarns 1 of different colors as the two flat yarns 1 constituting the multilayer portion 7, and the adhesive 8 and the surface film 5 are transparent respectively. By using a suitable material, the front and back of the adhesive tape have different colors reflecting the colors of the upper and lower flat yarns of the multilayer portion 7.
【００１６】以上の如く織製された織布４と表層膜５と
で構成された基布６を具備する粘着テープは、前記重層
部７の存在によって、当該重層部７を構成するフラット
ヤーン１の配向方向に、５０ｍｍ幅の粘着テープで２０
０ｋｇを超える引張り強度を持ち、２５ｍｍ幅の粘着テ
ープで７００ｋｇを超える衝撃強度を持つこととなる。
それにも関わらず、重層部７を構成する各フラットヤー
ン１が各々独立しているために、当該粘着テープが湾曲
した際にも配向方向へそれぞれ比較的自由に動くことが
できるので、粘着テープ自体の柔軟性を失うことはな
い。又、各フラットヤーン１が織布４たる一体物となっ
て表層膜５と接合しているので、個々のフラットヤーン
１が表層膜５から剥離して内側に巻き付けられている粘
着テープの背面に残留するといった不具合も生じない。The adhesive tape provided with the base cloth 6 composed of the woven cloth 4 and the surface layer film 5 woven as described above, is provided by the flat yarn 1 forming the multilayer part 7 due to the existence of the multilayer part 7. 20mm with 50mm width adhesive tape
It has a tensile strength exceeding 0 kg and an impact strength exceeding 700 kg with a 25 mm wide adhesive tape.
Nevertheless, since the flat yarns 1 constituting the multilayer portion 7 are independent of each other, the adhesive tape can move relatively freely in the orientation direction even when the adhesive tape is curved. You do not lose flexibility. In addition, since each flat yarn 1 is integrated with the surface film 5 as an integral member of the woven fabric 4, the individual flat yarns 1 are peeled off from the surface film 5 and are placed on the back surface of the adhesive tape wound inside. There is no problem of remaining.
【００１７】尚、前記引張り強度と衝撃強度の測定方法
は、以下の通りである。 引張り強度の測定方法（ＪＩＳ Ｌ−１０９６） ５０ｍｍ幅×３００ｍｍ長の試料９を用い、図９の如
く、長手方向の両端部を２００ｍｍの間隔で掴み、３０
０ｍｍ／分で引張る（上部移動、下部固定とした装置も
ある。）。 衝撃強度の測定方法（自社法） ２５ｍｍ幅×超１０００ｍｍ長の試料１０を用い、図１
０の如く、半径１０００ｍｍで揺動するウエイト（１
０．８ｋｇ）１１で試料１０の一端を支持し、当該ウエ
イト１１の垂下位置から水平方向へ１０００ｍｍ程度離
隔した定位置１２で試料１０の他端を支持（一端の支持
位置と他端の支持位置の間隔を１０００ｍｍとする。）
した状態で、前記ウエイト１１を、前記定位置１２に向
かって振り上げ次いで放すという一連の作業を行い、前
記試料１０の破断が生じた振り上げ角度θを次式へ代入
し、導かれた数値を衝撃強度とする。 衝撃強度（ｋｇ−ｃｍ／５０ｍｍ幅）＝（１−ｃｏｓ
θ）×Ｗ×Ｌ Ｗ（ウエイト重量）：１０．８ｋｇ Ｌ（揺動半径） ：１００ｃｍ（１０００ｍｍ）The method for measuring the tensile strength and the impact strength is as follows. Tensile strength measurement method (JIS L-1096) Using a sample 9 having a width of 50 mm and a length of 300 mm, as shown in FIG.
Pull at 0 mm / min. (Some devices are moved upward and fixed at the bottom.) Method for measuring impact strength (in-house method) Using a sample 10 having a width of 25 mm and a length of more than 1000 mm, FIG.
0, the weight (1
0.8 kg) 11 supports one end of the sample 10, and supports the other end of the sample 10 at a fixed position 12 separated from the hanging position of the weight 11 by about 1000 mm in the horizontal direction (a support position of one end and a support position of the other end) Is 1000 mm.)
In this state, the weight 11 is swung up toward the fixed position 12 and then released, and the swing angle θ at which the sample 10 is broken is substituted into the following equation. Strength. Impact strength (kg-cm / 50 mm width) = (1-cos
θ) × W × L W (weight of weight): 10.8 kg L (radius of oscillation): 100 cm (1000 mm)
【００１８】[0018]
【発明の効果】以上の如く本発明による粘着テープを使
用すれば、請求項１記載の粘着テープは、引張りや衝撃
に対し高い強度を必要とする用途に用いることができる
にも関わらず、良好な柔軟性と展開性によって高い作業
効率を実現することができ、請求項２記載の粘着テープ
にあっては、表裏に現われる色彩が異なることによっ
て、ガラス等の透明な部材に用いる場合には、表裏いず
れから見ても見苦しくない状態で使用することができる
他、ロール状に巻き付けられた粘着テープにあっては、
表裏の色彩に極端な差を付けることによって、粘着テー
プ表面の色彩と断面の色彩との違いから使用後に目印を
付けて置かなくても、テープの末端を容易に見付けるこ
とができるという付随的効果を奏する。As described above, when the pressure-sensitive adhesive tape according to the present invention is used, the pressure-sensitive adhesive tape according to claim 1 can be used in applications requiring high strength against tension and impact. High working efficiency can be realized by flexible and expandable, and in the pressure-sensitive adhesive tape according to claim 2, when the colors appearing on the front and back are different, when used for a transparent member such as glass, In addition to being able to be used in a state that is not difficult to see from both sides, in the case of adhesive tape wound in a roll shape,
By adding an extreme difference between the colors on the front and back, it is possible to easily find the end of the tape without having to place a mark after use because of the difference between the color of the adhesive tape surface and the color of the cross section. To play.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 1 is a perspective view showing an example of a woven structure of a woven fabric of an adhesive tape according to the present invention.
【図２】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 2 is a perspective view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図３】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 3 is a perspective view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図４】本発明による粘着テープの織布の織組織の一例
を示す斜視図である。FIG. 4 is a perspective view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図５】（イ）（ロ）本発明による粘着テープの織布の
織組織の一例を示す断面図である。5 (a) and (b) are cross-sectional views showing an example of the woven structure of the woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図６】（イ）（ロ）本発明による粘着テープの織布の
織組織の一例を示す断面図である。FIG. 6 is a sectional view showing an example of a woven structure of a woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図７】（イ）（ロ）（ハ）本発明による粘着テープの
織布の織組織の一例を示す断面図である。7 (a), (b) and (c) are cross-sectional views showing an example of the woven structure of the woven fabric of the pressure-sensitive adhesive tape according to the present invention.
【図８】本発明による粘着テープの一例を示す概略図で
ある。FIG. 8 is a schematic view showing an example of the pressure-sensitive adhesive tape according to the present invention.
【図９】引張り強度の測定方法を示す概念図である。FIG. 9 is a conceptual diagram showing a method for measuring tensile strength.
【図１０】衝撃強度の測定方法を示す概念図である。FIG. 10 is a conceptual diagram showing a method for measuring impact strength.
【符号の説明】 １ フラットヤーン ２ 経糸 ３ 緯糸 ４ 織布 ５ 表層膜 ６ 基布 ７ 重層部 ８ 粘着剤[Description of Signs] 1 Flat yarn 2 Warp 3 Weft 4 Woven cloth 5 Surface layer 6 Base cloth 7 Overlay section 8 Adhesive
Claims (2)
ン（１）を経糸（２）及び緯糸（３）として織製した織
布（４）の表裏少なくとも一方の面に、熱可塑性樹脂よ
り成る表層膜（５）を被着した基布（６）を具備し、当
該基布（６）の表裏少なくとも一方に粘着剤（８）が塗
布された粘着テープにおいて、前記経糸（２）又は緯糸
（３）の少なくとも一方に、同一方向に配向するフラッ
トヤーン（１）が全体的に重なり合った重層部（７）を
有する粘着テープ。1. A woven fabric (4) woven as a warp (2) and a weft (3) with a flat yarn (1) mainly composed of a thermoplastic resin as a warp (2) and at least one surface thereof is made of a thermoplastic resin. An adhesive tape comprising a base fabric (6) having a surface layer film (5) applied thereon, and an adhesive (8) applied to at least one of the front and back surfaces of the base fabric (6), wherein the warp (2) or the weft ( 3) An adhesive tape having a multilayer part (7) on which at least one of flat yarns (1) oriented in the same direction is entirely overlapped.
るフラットヤーン（１）と裏側に位置するフラットヤー
ン（１）の色を相異なる色に設定し、透明性を持つ表層
膜（５）と透明性を持つ粘着剤（８）を用いた請求項１
記載の粘着テープ。2. A transparent surface layer (5) in which the color of the flat yarn (1) located on the front side and the color of the flat yarn (1) located on the back side are set to different colors in the multilayer part (7). And an adhesive (8) having transparency.
The adhesive tape as described.