JPH11151055A - Fishing rod - Google Patents
Fishing rodInfo
- Publication number
- JPH11151055A JPH11151055A JP31963697A JP31963697A JPH11151055A JP H11151055 A JPH11151055 A JP H11151055A JP 31963697 A JP31963697 A JP 31963697A JP 31963697 A JP31963697 A JP 31963697A JP H11151055 A JPH11151055 A JP H11151055A
- Authority
- JP
- Japan
- Prior art keywords
- rod
- reinforced resin
- fiber
- build
- fishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、釣り竿、特に釣り
竿用部品装着部分等に肉盛り部が形成された釣り竿に関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fishing rod, and more particularly to a fishing rod having a built-up portion formed on a fishing rod component mounting portion or the like.
【0002】[0002]
【従来の技術】一般に、釣り竿の竿本体は、ガラス繊維
や炭素繊維等の高強度繊維基材にエポキシ樹脂等の熱硬
化性樹脂を含浸させた高強度繊維強化樹脂のプリプレグ
を先細り棒状のマンドレルに巻回し、焼成して得られ
る。したがって、通常、釣り竿の竿本体は、先細り筒状
に形成される。この種の釣り竿の竿本体には、リールシ
ートやグリップや釣り糸ガイド等の各種部品が装着され
る。このような部品を装着する場合、部品の内径に竿本
体の外径を合わすために繊維強化樹脂製の肉盛り部が竿
本体に形成されることがある。2. Description of the Related Art Generally, a rod body of a fishing rod is made of a high-strength fiber reinforced resin prepreg obtained by impregnating a high-strength fiber base material such as glass fiber or carbon fiber with a thermosetting resin such as an epoxy resin, and has a tapered rod-shaped mandrel. And calcined. Therefore, usually, the rod body of the fishing rod is formed in a tapered cylindrical shape. Various parts such as a reel sheet, a grip and a fishing line guide are mounted on a rod body of this type of fishing rod. When such a component is mounted, a built-up portion made of fiber reinforced resin may be formed on the rod body in order to match the outer diameter of the rod body to the inner diameter of the component.
【0003】[0003]
【発明が解決しようとする課題】前記従来の肉盛り部が
形成された釣り竿では、肉盛り部と竿本体との境界部分
で剛性が極端に変化する。すなわち、肉盛り部が形成さ
れた部分では竿本体に比べて肉厚が増えた分急激に剛性
が高くなる。このように剛性が急激に変化すると、釣り
竿に繰り返し応力が作用したとき、剛性が急激に変化す
る境界部分で繊維が剥離することがある。繊維が剥離す
ると、その部分の強度が弱くなり竿本体が破損するおそ
れがある。In the conventional fishing rod having the built-up portion, the rigidity changes extremely at the boundary between the built-up portion and the rod body. In other words, the rigidity of the portion where the built-up portion is formed suddenly increases as compared with the rod body because of the increased thickness. When the rigidity changes suddenly in this way, when stress is repeatedly applied to the fishing rod, the fiber may peel off at the boundary where the rigidity changes rapidly. When the fibers are peeled off, the strength of the portion is weakened, and the rod body may be damaged.
【0004】本発明の課題は、肉盛り部を形成しても剛
性の極端な変動が少ない釣り竿を提供することにある。[0004] It is an object of the present invention to provide a fishing rod in which the rigidity is hardly fluctuated even if a built-up portion is formed.
【0005】[0005]
【課題を解決するための手段】発明1に係る釣り竿は、
釣りに使用される釣り竿であって、竿本体と、肉盛り部
と、つなぎ部とを備えている。竿本体は、高強度繊維強
化樹脂製の先細り筒状のものである。肉盛り部は、竿本
体の少なくとも一部に形成された繊維強化樹脂製のもの
である。つなぎ部は、肉盛り部の端部に設けられ、肉盛
り部より剛性が低い繊維強化樹脂製のものである。The fishing rod according to the first aspect of the present invention
A fishing rod used for fishing, comprising a rod body, a build-up part, and a connecting part. The rod body has a tapered cylindrical shape made of a high-strength fiber-reinforced resin. The build-up portion is made of a fiber-reinforced resin formed on at least a part of the rod body. The connecting portion is provided at an end of the build-up portion, and is made of a fiber-reinforced resin having lower rigidity than the build-up portion.
【0006】この釣り竿では、肉盛り部の端部に設けら
れたつなぎ部の剛性が肉盛り部より低いので、つなぎ部
での剛性は肉厚が厚い分だけ竿本体よりは高くなるが肉
盛り部よりは低くなる。このため肉盛り部から竿本体に
かけての剛性の変動が少なくなり、繊維が剥離しにくく
なる。発明2に係る釣り竿は、発明1に記載の竿におい
て、つなぎ部は、肉盛り部の端部から離れるに従い徐々
に薄肉になるように形成されている。この場合には、つ
なぎ部での肉厚が肉盛り部から離れるに従い徐々に小さ
くなるので剛性が滑らかに低くなり剛性の急激な変動が
ほとんどなくなる。[0006] In this fishing rod, the rigidity of the connecting portion provided at the end of the cladding portion is lower than that of the cladding portion. Part lower. For this reason, the variation in rigidity from the built-up portion to the rod body is reduced, and the fibers are less likely to peel. A fishing rod according to a second aspect of the present invention is the fishing rod according to the first aspect, wherein the connecting portion is formed so as to gradually become thinner as the distance from the end of the build-up portion increases. In this case, the thickness at the joint portion gradually decreases as the distance from the build-up portion increases, so that the rigidity is smoothly reduced, and there is almost no sharp change in the rigidity.
【0007】発明3に係る釣り竿は、発明1又は2に記
載の釣り竿において、肉盛り部は高強度繊維強化樹脂製
である。この場合には、肉盛り部が高強度繊維樹脂製で
あるので、薄い肉厚で強度が向上する。発明4に係る釣
り竿は、発明3に記載の釣り竿において、つなぎ部は高
強度繊維強化樹脂製である。この場合には、つなぎ部が
高強度繊維樹脂製であるので、肉盛り部及び竿本体とな
じみやすくなる。A fishing rod according to a third aspect of the present invention is the fishing rod according to the first or second aspect, wherein the build-up portion is made of a high-strength fiber-reinforced resin. In this case, since the built-up portion is made of a high-strength fiber resin, the strength is improved with a small thickness. A fishing rod according to a fourth aspect of the present invention is the fishing rod according to the third aspect, wherein the connecting portion is made of a high-strength fiber-reinforced resin. In this case, since the connecting portion is made of a high-strength fiber resin, the connecting portion is easily compatible with the build-up portion and the rod body.
【0008】発明5に係る釣り竿は、発明4に記載の釣
り竿において、竿本体及び肉盛り部の主たる高強度繊維
は炭素繊維であり、つなぎ部の高強度繊維はガラス繊維
である。この場合には、引張弾性率が小さく剛性が低い
ガラス繊維で強化された樹脂をつなぎ部に用いたので、
つなぎ部の肉厚が厚くなっても剛性の増加を抑えること
ができる。A fishing rod according to a fifth aspect of the present invention is the fishing rod according to the fourth aspect, wherein the main high-strength fibers of the rod main body and the build-up portion are carbon fibers, and the high-strength fibers of the connecting portion are glass fibers. In this case, since the resin reinforced with glass fiber having a low tensile modulus and low rigidity was used for the joint,
An increase in rigidity can be suppressed even when the thickness of the connecting portion is increased.
【0009】発明6に係る釣り竿は、発明5に記載の釣
り竿において、竿本体及び肉盛り部に用いる炭素繊維強
化樹脂の引張弾性率は20トン/mm2 から40トン/
mm 2 であり、つなぎ部に用いるガラス繊維強化樹脂の
引張弾性率は5トン/mm2から10トン/mm2 であ
る。なお、ここでいう繊維強化樹脂の引張弾性率とは、
高強度繊維の引張弾性率のことである。この場合には、
ガラス繊維強化樹脂の引張弾性率が肉盛り部に比べて格
段に小さいので、剛性の極端な変動をより抑えることが
できる。A fishing rod according to a sixth aspect of the present invention is the fishing rod according to the fifth aspect.
Carbon fiber strength used for rod body and overlay
Resin has a tensile modulus of 20 tons / mmTwoTo 40 tons /
mm TwoOf the glass fiber reinforced resin used for the joint
Tensile modulus is 5 ton / mmTwoFrom 10 tons / mmTwoIn
You. In addition, the tensile elastic modulus of the fiber reinforced resin here is,
It is the tensile modulus of high strength fiber. In this case,
The tensile modulus of glass fiber reinforced resin is lower than that of
Because it is small in steps, it is possible to further suppress extreme fluctuations in rigidity
it can.
【0010】[0010]
【発明の実施の形態】図1において、本発明の一実施形
態による振出竿は、手元竿1と、手元竿1に振出形式で
装着された穂先側竿体ユニット2とを有している。手元
竿1はわずかに先細りの筒状に形成され、その外周面に
は、釣り糸Lを巻き取るリール3が装着されるリールシ
ート4が形成されている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS In FIG. 1, a drawing rod according to an embodiment of the present invention has a hand rod 1 and a tip-side rod unit 2 mounted on the hand rod 1 in a drawing manner. The wand 1 is formed in a slightly tapered cylindrical shape, and a reel sheet 4 on which a reel 3 for winding the fishing line L is mounted is formed on an outer peripheral surface thereof.
【0011】穂先側竿体ユニット2は、穂先ガイド10
を有する最も先端側(穂先側)の1番竿11と、1番竿
11を支持するとともにこの1番竿11を内部に収納可
能な2番竿12と、2番竿12を内部に収納可能でかつ
手元竿1に挿入可能な3番竿13とを有している。この
ように、穂先側竿体ユニット2を構成する3本の竿1
1、12、13は振出形式で連結されている。各竿11
〜13の外周面にはリング状の釣り糸ガイド14〜16
が遊動自在に装着されている。The tip side rod body unit 2 includes a tip guide 10
No. 1 pole 11 on the most distal end side (ear end side), a No. 2 pole 12 that supports the No. 1 pole 11 and can store the No. 1 rod 11 inside, and a No. 2 pole 12 can be stored inside And a third rod 13 that can be inserted into the hand rod 1. Thus, the three rods 1 constituting the tip side rod body unit 2
1, 12, and 13 are connected in a draw-out format. Each pole 11
Ring shaped fishing line guides 14 to 16
Is freely mounted.
【0012】手元竿1及び各竿11〜13は、主として
炭素繊維強化樹脂製のプリプレグ(素材)を先細り棒状
のマンドレルに巻回し焼成して得られた先細り筒状の部
材である。各竿11 〜13は、図2に示すように、たと
えば、20〜40トン/mm 2 の引張弾性率を有するプ
リプレグにより成形された竿本体17を有している。竿
本体17の釣り糸ガイド14〜16装着位置には、炭素
繊維強化樹脂製の肉盛り部18が設けられている。肉盛
り部18は、釣り糸ガイド14〜16の内径に各竿11
〜13の外径を合わせるために設けられている。肉盛り
部18に用いられる炭素繊維強化樹脂の引張弾性率は、
たとえば20〜40トン/mm2 の範囲である。The hand rod 1 and each of the rods 11 to 13 are mainly
Pre-preg (material) made of carbon fiber reinforced resin is tapered and rod-shaped
Tapered cylindrical part obtained by winding around a mandrel and firing
Material. Each of the rods 11 to 13 is, as shown in FIG.
For example, 20 to 40 tons / mm TwoWith a tensile modulus of
It has a rod body 17 formed by repreg. rod
The fishing line guides 14 to 16 of the body 17
A built-up portion 18 made of fiber reinforced resin is provided. Build-up
Each rod 11 is provided with an inner diameter of the fishing line guides 14 to 16.
It is provided for adjusting the outer diameters of 1313. Overlay
The tensile modulus of the carbon fiber reinforced resin used for the part 18 is
For example, 20-40 tons / mmTwoRange.
【0013】肉盛り部18の端部には、ガラス繊維強化
樹脂製のつなぎ部19が設けられている。つなぎ部19
は、肉盛り部18による肉厚の大きな変化による剛性の
急激な変動を抑えるために設けられている。ここでつな
ぎ部19に用いられるガラス繊維強化樹脂のプリプレグ
の引張弾性率は、5〜10トン/mm2 であり、他の部
分(竿本体17及び肉盛り部18)より低い引張弾性率
となっており、剛性が肉盛り部18より低くなってい
る。つなぎ部19は、肉盛り部18の端部から離れるに
従い徐々に薄肉になるように形成されている。このた
め、つなぎ部19での剛性は徐々に低くなる。A connecting portion 19 made of glass fiber reinforced resin is provided at an end of the built-up portion 18. Joint 19
Is provided in order to suppress a rapid change in rigidity due to a large change in thickness due to the build-up portion 18. Here, the tensile elastic modulus of the prepreg of the glass fiber reinforced resin used for the connecting portion 19 is 5 to 10 ton / mm 2, which is lower than the other portions (the rod body 17 and the build-up portion 18). The rigidity is lower than that of the build-up portion 18. The connecting portion 19 is formed so as to gradually become thinner as the distance from the end of the build-up portion 18 increases. For this reason, the rigidity at the connecting portion 19 gradually decreases.
【0014】このような構造の肉盛り部18及びつなぎ
部19は、以下のようにして製造する。図3に示すよう
に、竿本体17となるプリプレグ30を離型テープが巻
回された所定の形状のマンドレルに巻回した後、釣り糸
ガイド14〜16の装着位置の外周面に肉盛り部18と
なるシート状のプリプレグ31を巻回する。これらのプ
リプレグ30,31は、いずれも炭素繊維強化樹脂製で
ある。そして、図4に示すように、プリプレグ31を巻
回した後に、プリプレグ31の両端部に一部が重なるよ
うにつなぎ部19となる台形状のプリプレグ32を巻回
する。このプリプレグ32は、肉盛り部18の端部から
竿本体17にかけて徐々に薄肉になるように肉盛り部か
ら離れた側の幅が肉盛り部側の幅よりやや小さく形成さ
れたガラス繊維強化樹脂製の台形状のシート部材であ
る。これらのプリプレグ30〜32を巻回後、保護用テ
ープをプリプレグ30〜32の外周面に巻回して竿素材
を得て、この竿素材を焼成する。その後、離型用テー
プ,保護テープ等を剥離し、表面を研削加工して各竿体
11〜13を製造する。このようにして形成された肉盛
り部18は、両端部に剛性が低いつなぎ部19が形成さ
れるため、竿本体17との間での剛性の急激な変動が少
なくなり、繊維が剥離しにくくなる。The built-up portion 18 and the connecting portion 19 having such a structure are manufactured as follows. As shown in FIG. 3, after the prepreg 30 serving as the rod body 17 is wound on a mandrel having a predetermined shape on which a release tape is wound, the padding portion 18 is provided on the outer peripheral surface of the mounting position of the fishing line guides 14 to 16. The prepreg 31 is wound. These prepregs 30, 31 are both made of carbon fiber reinforced resin. Then, as shown in FIG. 4, after the prepreg 31 is wound, a trapezoidal prepreg 32 serving as the connecting portion 19 is wound so as to partially overlap both ends of the prepreg 31. The prepreg 32 is a glass fiber reinforced resin formed such that the width on the side away from the build-up portion is slightly smaller than the width on the build-up portion so that the thickness gradually decreases from the end of the build-up portion 18 to the rod body 17. It is a trapezoidal sheet member made of. After winding the prepregs 30 to 32, a protective tape is wound around the outer peripheral surfaces of the prepregs 30 to 32 to obtain a rod material, and the rod material is fired. Thereafter, the release tape, the protective tape, and the like are peeled off, and the surfaces are ground to manufacture the rod bodies 11 to 13. Since the connecting portion 19 having low rigidity is formed at both ends of the built-up portion 18 formed in this manner, a sudden change in rigidity between the cladding portion 18 and the rod body 17 is reduced, and the fiber is hardly peeled. Become.
【0015】釣り糸ガイド14〜16は、図2に示すよ
うに、ガイドフレーム20と、ガイドフレーム20の下
部に回転不能に嵌め込まれた筒状の装着部21と、上部
に嵌め込まれ釣り糸が通過可能な硬質セラミック製のガ
イドリング22とを有している。ガイドフレーム20
は、図3に示すように、ガイドリング22が嵌め込まれ
る上部リング部20aと、装着部21が嵌め込まれる1
対の下部リング部20bと、上下のリング部20a,2
0bを連結するアーム部20cとを有している。また、
下部リング部20bの上部内周部には回り止め用の凹部
20dが形成されている。The fishing line guides 14 to 16 are, as shown in FIG. 2, a guide frame 20, a cylindrical mounting portion 21 which is non-rotatably fitted into a lower portion of the guide frame 20, and a fishing line which is fitted into an upper portion so that the fishing line can pass therethrough. And a guide ring 22 made of a hard ceramic. Guide frame 20
As shown in FIG. 3, the upper ring portion 20a in which the guide ring 22 is fitted and the mounting portion 21 in which the mounting portion 21 is fitted.
A pair of lower ring portions 20b and upper and lower ring portions 20a, 2
0b to connect the arm portion 20c. Also,
A recess 20d for preventing rotation is formed in an upper inner peripheral portion of the lower ring portion 20b.
【0016】装着部21は、図2に示すように、下部リ
ング20bに嵌め込まれる硬質樹脂製の円筒部材25
と、円筒部材25の内部に回転不能に装着された弾性部
材26とを有している。円筒部材25の外周面の一部に
は、ガイドフレーム20を装着部21に対して回り止め
するための突起25aが軸方向に間隔を隔てて形成され
ている。この突起25aはガイドフレーム20の凹部2
0dにより係止される。この装着部21の内径に合わせ
るために肉盛り部18が竿本体17に形成されている。As shown in FIG. 2, the mounting portion 21 has a cylindrical member 25 made of a hard resin fitted into the lower ring 20b.
And an elastic member 26 non-rotatably mounted inside the cylindrical member 25. On a part of the outer peripheral surface of the cylindrical member 25, projections 25a for preventing the guide frame 20 from rotating with respect to the mounting portion 21 are formed at intervals in the axial direction. The projection 25a is provided in the recess 2 of the guide frame 20.
Locked by 0d. A padding portion 18 is formed on the rod body 17 to match the inner diameter of the mounting portion 21.
【0017】弾性部材26は、両端に円筒部材25とほ
ぼ同径のフランジ部26aを有する弾性体製の筒状の部
材である。弾性部材26の内径は、各竿11〜13の釣
り糸ガイド14〜16の装着位置における肉盛り部18
の外径よりやや小さく、各竿11〜13の外周面を軸方
向に移動可能であるとともに、装着位置において摩擦に
より回転しにくくなっている。The elastic member 26 is a cylindrical member made of an elastic material and has a flange 26a having substantially the same diameter as the cylindrical member 25 at both ends. The inner diameter of the elastic member 26 depends on the thickness of the padding portion 18 at the position where the fishing line guides 14 to 16 of the rods 11 to 13 are mounted.
Is slightly smaller than the outer diameter of each of the rods 11 to 13, and can move axially on the outer peripheral surface of each of the rods 11 to 13, and is less likely to rotate at the mounting position due to friction.
【0018】この弾性体としては、ウレタンゴム等のゴ
ム系弾性体やアクティマー(商標),レオストマー(商
標)等のスチレンブロック共重合体系熱可塑弾性体やサ
ントプレーン(商標),ラバロン(商標)等の弾性体を
用いることができる。弾性体として、スチレン系弾性体
であるレオストマーに高温でのゴム弾性,耐油性を付与
して一層の高機能化を実現した動的架橋熱可塑性弾性体
であるアクティマーを用いると、弾性部材26の厚みを
薄くしても適度な弾力が得られ弾性部材26の耐久性が
とくに良好である。Examples of the elastic body include a rubber-based elastic body such as urethane rubber, a styrene block copolymer-based thermoplastic elastic body such as Actimer (trademark) and Rheostomer (trademark), Santoprene (trademark) and Lavalon (trademark). And the like. When actimer, which is a dynamically crosslinked thermoplastic elastic body that provides rubber elasticity and oil resistance at a high temperature to the rheostomer, which is a styrene-based elastic body, and achieves higher functionality, is used as the elastic body, the elastic member 26 Even when the thickness of the elastic member 26 is reduced, an appropriate elasticity is obtained, and the durability of the elastic member 26 is particularly good.
【0019】このように構成された振出竿では、各竿1
1〜13を伸ばして使用状態にする際には、1番竿11
から順に伸ばす。このとき、各釣り糸ガイド14〜16
は、装着部分よりやや穂先側に配置されており、各竿1
1〜13の竿本体17の装着位置から離れた位置に緩く
嵌め込まれている。そして、各釣り糸ガイド14〜16
を所定の装着位置に形成された肉盛り部18に移動させ
る。このとき、釣り糸ガイド14〜16は、弾性部材2
6が弾性により凹むので軸方向への移動が容易である。
そして、肉盛り部18に釣り糸ガイド14〜16が配置
されると、弾性部材26が凹んで各竿11〜13の外周
面との摩擦により、釣り糸ガイド14〜16が回りにく
くなる。In the thus constructed swing rod, each rod 1
When extending 1 to 13 to use the first rod 11
Stretch in order. At this time, each fishing line guide 14-16
Is located slightly ahead of the mounting part, and each rod 1
The rod bodies 17 are loosely fitted at positions away from the mounting positions of the rod bodies 17. And each fishing line guide 14-16
Is moved to the built-up portion 18 formed at a predetermined mounting position. At this time, the fishing line guides 14 to 16
6 is recessed by elasticity, so that it is easy to move in the axial direction.
When the fishing line guides 14 to 16 are disposed on the overlay portion 18, the elastic members 26 are depressed and the fishing line guides 14 to 16 are difficult to rotate due to friction with the outer peripheral surfaces of the rods 11 to 13.
【0020】この状態で竿を使用すると、キャスティン
グ時や魚がかかった時に手元竿1及び各竿体11〜13
に繰り返して応力が発生する。しかし、肉盛り部18に
隣接して剛性の低いつなぎ部19が設けられているの
で、肉盛り部18の端部において剛性の急激な変動が生
じにくくなり、肉盛り部18の端部で繊維が剥離しにく
くなる。一方、振出竿を収納するときに、各釣り糸ガイ
ド14〜16を肉盛り部18から穂先側に移動させる。
そして、3番竿13から順次竿元側の竿に収納する。When the rod is used in this state, the rod 1 and the rods 11 to 13 can be used when casting or catching fish.
The stress is generated repeatedly. However, since the connecting portion 19 having low rigidity is provided adjacent to the built-up portion 18, a rapid change in rigidity is unlikely to occur at the end of the built-up portion 18, and the fiber is formed at the end of the built-up portion 18. Are difficult to peel off. On the other hand, when storing the swing rod, each of the fishing line guides 14 to 16 is moved from the padding portion 18 to the tip side.
Then, the third rod 13 is sequentially stored in the rod on the rod base side.
【0021】〔他の実施形態〕 (a) 図6及び図7に示すように、肉盛り部18に軸
方向に延びるローレット溝18aを形成してもよい。こ
のようなローレット溝18aを形成すると、釣り糸ガイ
ド14〜16がより回りにくくなる。 (b) 本発明は、釣り糸ガイドの装着位置に形成され
る外径調整用の肉盛り部に限定されるものではなく、リ
ールシート、グリップ、中通し竿の糸導入部等の竿に装
着される部品の装着位置に形成される肉盛り部や補強の
ために形成される肉盛り部等の釣り竿に形成される全て
の肉盛り部に適用可能である。[Other Embodiments] (a) As shown in FIGS. 6 and 7, a knurl groove 18 a extending in the axial direction may be formed in the built-up portion 18. When such a knurl groove 18a is formed, the fishing line guides 14 to 16 become more difficult to rotate. (B) The present invention is not limited to the outer diameter adjusting pad formed at the mounting position of the fishing line guide, but is mounted on a rod such as a reel sheet, a grip, and a line introduction part of a through-hole rod. The present invention can be applied to all the overlaid portions formed on the fishing rod, such as the overlaid portion formed at the mounting position of the component to be mounted and the overlaid portion formed for reinforcement.
【0022】(c) 竿本体及び肉盛り部の材質は、炭
素繊維強化樹脂に限定されるものではなく、ガラス繊維
強化樹脂等の他の高強度繊維強化樹脂でもよい。特に、
強度が不要な肉盛り部の場合には、高強度繊維強化樹脂
ではなく、ナイロン糸等の繊維や布で強化された通常の
繊維強化樹脂でもよい。 (d) つなぎ部の材質はガラス繊維強化樹脂に限定さ
れるものではなく、肉盛り部より剛性が低い繊維強化樹
脂であればどのようなものでもよい。したがって炭素繊
維強化樹脂等の他の高強度繊維強化樹脂でもよく、ナイ
ロン糸等の繊維や布で強化された通常の繊維強化樹脂で
もよい。(C) The material of the rod body and the overlaid portion is not limited to carbon fiber reinforced resin, but may be other high strength fiber reinforced resin such as glass fiber reinforced resin. Especially,
In the case of a build-up portion that does not require strength, not a high-strength fiber-reinforced resin but a normal fiber-reinforced resin reinforced with a fiber such as a nylon thread or a cloth may be used. (D) The material of the connecting portion is not limited to the glass fiber reinforced resin, but may be any fiber reinforced resin having lower rigidity than the build-up portion. Therefore, another high-strength fiber-reinforced resin such as a carbon fiber-reinforced resin may be used, or an ordinary fiber-reinforced resin reinforced with a fiber such as a nylon thread or a cloth may be used.
【0023】[0023]
【発明の効果】本発明に係る釣り竿では、肉盛り部の端
部に設けられたつなぎ部の剛性が肉盛り部より低いの
で、つなぎ部での剛性は肉厚が厚い分だけ竿本体よりは
高くなるが肉盛り部よりは低くなる。このため肉盛り部
から竿本体にかけての剛性の変動が少なくなり、繊維が
剥離しにくくなる。In the fishing rod according to the present invention, the rigidity of the joint provided at the end of the cladding is lower than that of the cladding. Higher, but lower than the overlay. For this reason, the variation in rigidity from the built-up portion to the rod body is reduced, and the fibers are less likely to peel.
【図1】本発明の一実施形態による振出竿の側面図。FIG. 1 is a side view of a swing rod according to an embodiment of the present invention.
【図2】釣り糸ガイド装着位置での側面断面図。FIG. 2 is a side sectional view at a fishing line guide mounting position.
【図3】肉盛り部の製造手順を示す側面図。FIG. 3 is a side view showing the procedure for manufacturing the overlay.
【図4】肉盛り部の製造手順を示す側面図。FIG. 4 is a side view showing the procedure for manufacturing the overlay.
【図5】釣り糸ガイドの正面図。FIG. 5 is a front view of a fishing line guide.
【図6】他の実施形態の釣り糸ガイド装着位置での側面
図。FIG. 6 is a side view of another embodiment at a fishing line guide mounting position.
【図7】図6のVII −VII 断面図。FIG. 7 is a sectional view taken along line VII-VII of FIG. 6;
11 1番竿 12 2番竿 13 3番竿 14〜16 釣り糸ガイド 17 竿本体 18 肉盛り部 19 つなぎ部 11 No. 1 pole 12 No. 2 pole 13 No. 3 pole 14-16 Fishing line guide 17 Rod body 18 Overlay 19 Joint
Claims (6)
体と、 前記竿本体の少なくとも一部に形成された繊維強化樹脂
製の肉盛り部と、 前記肉盛り部の端部に設けられ、前記肉盛り部より剛性
が低い繊維強化樹脂製のつなぎ部と、を備えた釣り竿。1. A tapered cylindrical rod body made of a high-strength fiber-reinforced resin, a fiber-reinforced resin build-up portion formed on at least a part of the rod body, and an end provided at the end of the build-up portion. And a connecting portion made of fiber reinforced resin having a lower rigidity than the build-up portion.
離れるに従い徐々に薄肉になるように形成されている、
請求項1に記載の釣り竿。2. The connecting portion is formed so as to gradually become thinner as the distance from an end of the built-up portion increases.
The fishing rod according to claim 1.
ある、請求項1又は2に記載の釣り竿。3. The fishing rod according to claim 1, wherein the build-up portion is made of a high-strength fiber-reinforced resin.
ある、請求項3に記載の釣り竿。4. The fishing rod according to claim 3, wherein said connecting portion is made of a high-strength fiber-reinforced resin.
維は炭素繊維であり、前記つなぎ部の高強度繊維はガラ
ス繊維である、請求項4に記載の釣り竿。5. The fishing rod according to claim 4, wherein the main high-strength fibers of the rod main body and the build-up portion are carbon fibers, and the high-strength fibers of the connecting portion are glass fibers.
強化樹脂の引張弾性率は20トン/mm2 から40トン
/mm2 であり、前記つなぎ部に用いるガラス繊維強化
樹脂の引張弾性率は5トン/mm2 から10トン/mm
2 である、請求項5に記載の釣り竿。Wherein a said rod body and the tensile modulus was 20 t / mm 2 from 40 t / mm 2 of the carbon fiber-reinforced resins used in building up section, the tensile modulus of the glass fiber-reinforced resins used in the connecting portion Is 5 ton / mm 2 to 10 ton / mm
The fishing rod according to claim 5, which is 2 .