JPH1059421A - Composite container - Google Patents
Composite containerInfo
- Publication number
- JPH1059421A JPH1059421A JP8221300A JP22130096A JPH1059421A JP H1059421 A JPH1059421 A JP H1059421A JP 8221300 A JP8221300 A JP 8221300A JP 22130096 A JP22130096 A JP 22130096A JP H1059421 A JPH1059421 A JP H1059421A
- Authority
- JP
- Japan
- Prior art keywords
- container
- exterior material
- resin
- adhesive
- composite container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、紙を主体とする外
装材と樹脂製内装容器とを組み合わせた角型複合容器に
おいて、少なくとも胴部を除いて、外装材内面に部分的
に接着剤層を設けることにより、複合容器外装材のしわ
を防止したことを特徴とする複合容器に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rectangular composite container in which an exterior material mainly composed of paper and a resin interior container are combined, and an adhesive layer is partially formed on the inner surface of the exterior material except at least the body. The present invention relates to a composite container characterized by preventing wrinkles of a composite container exterior material by providing the composite container.
【０００２】[0002]
【従来の技術】近年、環境問題への関心が高まる中で、
プラスチックの使用量を減らし紙と組み合わせた複合容
器が開発され、市場に出回っている。その一例として、
我々は紙を主体とする外装材とプラスチックから成る内
装容器を組み合わせた複合容器を提案した（特願平６−
２１２５３７号等）。このような複合容器を製造する方
法としては予め、紙を主体とする外装容器をブロー金型
内に載置し、その中に成形温度に加熱されたプリフォー
ムを導入し、ブロー成形することによって、外装容器と
一体で且つ無継ぎ目に成形されたプラスチック製の内装
容器とを組み合わせた複合容器を製造する方法がある。2. Description of the Related Art In recent years, interest in environmental issues has increased,
Composite containers that use less plastic and are combined with paper have been developed and are on the market. As an example,
We have proposed a composite container that combines a paper-based exterior material and a plastic interior container.
No. 212537). As a method of manufacturing such a composite container, in advance, an outer container mainly composed of paper is placed in a blow mold, a preform heated to a molding temperature is introduced therein, and blow molding is performed. There is also a method of manufacturing a composite container in which an outer container is combined with a plastic inner container formed integrally and seamlessly.
【０００３】上記方法においては、外装材と内装容器と
を成形時に一体化することが望まれ、種々の工夫がなさ
れてきた。例えば、外装材内面に感熱性接着剤層を設
け、内装容器ブロー成形時の熱で、外装材と内装容器と
を一体化する方法等である。しかし、上記方法において
は外装材と内装容器樹脂の組合せによっては、複合容器
の外装材にしわが生じ、外観を損ねて商品価値を低下さ
せることがあることがわかった。これは、収縮しやすい
樹脂を内装容器に用いた場合、内装容器と接着剤で一体
化された外装材が、内装容器の収縮に伴って引っ張られ
ることにより生ずるものであり、接着剤の塗布パターン
によってもしわを防止することが可能とであるが、その
場合も外装材内面と内装容器とが部分的にではあっても
胴部において接着されているために内装容器の収縮に伴
って引っ張られることによるしわの発生を完全に防止す
ることはできない。In the above method, it is desired to integrate the exterior material and the interior container at the time of molding, and various measures have been taken. For example, there is a method in which a heat-sensitive adhesive layer is provided on the inner surface of the exterior material, and the exterior material and the interior container are integrated by heat during blow molding of the interior container. However, it has been found that in the above method, depending on the combination of the exterior material and the resin of the interior container, the exterior material of the composite container may be wrinkled, impairing the appearance and reducing the commercial value. This is because when an easily shrinkable resin is used for the inner container, the outer material integrated with the inner container and the adhesive is pulled by the shrinkage of the inner container, which is caused by the adhesive application pattern. It is also possible to prevent wrinkles, but also in this case, the inner surface of the outer material and the inner container are partially adhered to the trunk even though they are partially pulled because of the shrinkage of the inner container It is not possible to completely prevent wrinkles from occurring.
【０００４】[0004]
【本発明が解決しようとする課題】本発明は、以上の課
題を鑑み、紙を主体とする外装材と樹脂製内装容器とを
組み合わせた角型複合容器において、少なくとも胴部を
除いて、外装材内面に部分的に接着剤層を設けることに
より、複合容器外装材のしわを防止した複合容器を提供
することを目的とする。SUMMARY OF THE INVENTION In view of the above problems, the present invention has been made in consideration of the above problems, and has been made in consideration of the above problems in a rectangular composite container in which an exterior material mainly composed of paper and a resin interior container are combined, except for at least a trunk portion. An object of the present invention is to provide a composite container in which an adhesive layer is partially provided on the inner surface of the material to prevent wrinkles of the external material of the composite container.
【０００５】[0005]
【課題を解決するための手段】本発明は上記課題を解決
すべく考えられたものであり、請求項１の発明は、紙を
主体とする外装材と、胴部、肩部、底部から成る樹脂製
内装容器とを組み合わせた複合容器において、少なくと
も胴部を除いて、外装材内面に接着剤層を設けたことを
特徴とする複合容器である。請求項２の発明は、紙を主
体とする外装材と、胴部、肩部、底部から成る樹脂製内
装容器とを組み合わせた複合容器において、該複合容器
の少なくとも胴部においては、外装材内面と樹脂製内装
容器とが非接着であり、肩部および底部においては外装
材内面と樹脂製内装容器とが接着されていることを特徴
とする請求項１記載の複合容器である。請求項３の発明
は、外装材が胴フラップとその上端に連設された肩フラ
ップ、下端に連設された底フラップから成ることを特徴
とする請求項１又は請求項２記載の複合容器である。請
求項４の発明は、外装材内面と樹脂製内装容器とが、樹
脂製内装容器の少なくとも胴部を除いた部分において全
面接着されていることを特徴とする請求項１又は請求項
３記載の複合容器である。請求項５の発明は、外装材内
面と樹脂製内装容器とが、樹脂製内装容器の少なくとも
胴部を除いた部分において部分的に接着されていること
を特徴とする請求項１又は請求項３記載の複合容器であ
る。請求項６の発明は、外装材内面と樹脂製内装容器と
が、樹脂製内装容器の肩部および底部において全面接着
されていることを特徴とする請求項２又は請求項３記載
の複合容器である。請求項７の発明は、外装材内面と樹
脂製内装容器とが、樹脂製内装容器の肩部および底部に
おいて部分的に接着されていることを特徴とする請求項
２又は請求項３記載の複合容器である。請求項８の発明
は、ドット状パターンの接着剤層により外装材内面と樹
脂製内装容器とが接着されていることを特徴とする請求
項１乃至請求項７記載の何れかの複合容器である。請求
項９の発明は、紙を主体とする外装材の内面全面に接着
性樹脂層、部分的に施されたニス層を順次、設けたこと
を特徴とする請求項１又は請求項２記載の複合容器であ
る。請求項１０の発明は、外装材の水平断面形状が四角
形以上の多角形であることを特徴とする請求項１乃至請
求項９記載の何れかの複合容器である。SUMMARY OF THE INVENTION The present invention has been conceived to solve the above-mentioned problems, and the invention of claim 1 comprises an exterior material mainly composed of paper, and a body, a shoulder, and a bottom. A composite container in which an adhesive layer is provided on an inner surface of an exterior material except for at least a body portion in a composite container in which a resin inner container is combined. The invention according to claim 2 is a composite container in which an exterior material mainly composed of paper and a resin interior container comprising a body, a shoulder, and a bottom are combined, and at least the body of the composite container has an exterior material inner surface. 2. The composite container according to claim 1, wherein the resin and the resin interior container are not adhered, and the inner surface of the exterior material and the resin interior container are adhered at the shoulder and the bottom. The invention according to claim 3 is the composite container according to claim 1 or 2, wherein the exterior material comprises a body flap, a shoulder flap connected to an upper end thereof, and a bottom flap connected to a lower end thereof. is there. The invention according to claim 4 is characterized in that the inner surface of the exterior material and the resin-made inner container are entirely adhered to each other at least in a portion of the resin-made inner container except for the body. It is a composite container. The invention according to claim 5 is characterized in that the inner surface of the exterior material and the resin-made interior container are partially bonded at least in a portion of the resin-made interior container excluding the body. It is a composite container of the description. The invention according to claim 6 is the composite container according to claim 2 or 3, wherein the inner surface of the exterior material and the resin-made inner container are entirely bonded at a shoulder portion and a bottom portion of the resin-made inner container. is there. The invention according to claim 7 is the composite according to claim 2 or 3, wherein the inner surface of the exterior material and the resin interior container are partially adhered to each other at a shoulder portion and a bottom portion of the resin interior container. Container. The invention according to claim 8 is the composite container according to any one of claims 1 to 7, wherein the inner surface of the exterior material and the interior container made of resin are adhered by an adhesive layer having a dot pattern. . The invention according to claim 9 is characterized in that an adhesive resin layer and a partially applied varnish layer are sequentially provided on the entire inner surface of the exterior material mainly composed of paper. It is a composite container. The invention according to claim 10 is the composite container according to any one of claims 1 to 9, wherein a horizontal cross-sectional shape of the exterior material is a polygon of a quadrangle or more.
【０００６】[0006]
【発明の実施の形態】以下、本発明を詳細に説明する。
本発明の複合容器の一例を示す図１において、複合容器
Ａは紙を主体とする外装材１、外装材１に収容された樹
脂から成る内装容器２により構成されている。内装容器
２は口部３、肩部４、胴部５、底部６が延伸ブロー成形
により一体に成形されている。複合容器の形状は図１の
四角形形状以外に多角形形状も可能である。また、各面
角度は同一である必要はなく、多面体であればよい。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail.
In FIG. 1 showing an example of the composite container of the present invention, a composite container A is composed of an exterior material 1 mainly composed of paper and an interior container 2 made of a resin accommodated in the exterior material 1. The inner container 2 has a mouth 3, a shoulder 4, a body 5, and a bottom 6 integrally formed by stretch blow molding. The shape of the composite container may be a polygonal shape other than the square shape in FIG. Also, the surface angles need not be the same, but may be polyhedrons.
【０００７】また、図２にその一例を示すように外装材
１は矩形状のフラップを罫線を介して連設した胴フラッ
プ、この胴フラップの上端に罫線を介して連設した台形
状の肩フラップおよび胴フラップの下端に罫線を介して
連設した底フラップから構成される。なお、底フラップ
下端の円弧部分は外装材を組み立てた時に円孔を形成
し、内装容器の底部を受入れて内装容器の底部がそこか
ら露出するような形状に打ち抜かれている（図４、５、
６、７、９、１０、１１、１２、１３、１４においても
同様）。接着剤塗工部分は図３あるいは図４に斜線部で
示される部分でも構わない。図５に示すドット状パター
ンも、使用後の外装材と内装容器との易分離性付与のた
め、好ましく用いられる。また、ドットの大きさや間隔
を調整することにより分離性をコントロールすることが
可能である。図２中に示されるように、外装材と内装容
器とは複合容器としての形状を保つため、各面とも肩部
の全部あるいは一部ａ、底部の全部あるいは一部ｂで接
着されていることが好ましい。本発明においては外装材
のしわを防止するため、胴部には接着剤を塗布しないこ
とが重要である。また、外装材と内装容器とを接着させ
る手段としては、上記の接着剤を接着性が必要な部分に
塗工する方法の他にも、紙層の内側全面に接着性樹脂層
を設けた後、接着性の不要部分には内装容器材質とは接
着性を示さないニス層を部分的に設けることもできる。As shown in FIG. 2, the exterior material 1 is composed of a body flap in which rectangular flaps are connected via a ruled line, and a trapezoidal shoulder which is connected to the upper end of the body flap through a ruled line. It is composed of a bottom flap connected to the lower end of the flap and the trunk flap via a ruled line. The arc portion at the lower end of the bottom flap forms a circular hole when the exterior material is assembled, and is punched into a shape such that the bottom of the inner container is received and the bottom of the inner container is exposed therefrom (FIGS. 4 and 5). ,
6, 7, 9, 10, 11, 12, 13, and 14). The adhesive-coated portion may be a portion indicated by hatching in FIG. 3 or FIG. The dot pattern shown in FIG. 5 is also preferably used for imparting easy separation between the exterior material and the interior container after use. In addition, it is possible to control the separability by adjusting the size and interval of the dots. As shown in FIG. 2, the exterior material and the interior container are bonded to each other at all or a part of the shoulder and at all or a part of the bottom in order to maintain the shape as a composite container. Is preferred. In the present invention, it is important not to apply an adhesive to the body in order to prevent wrinkles of the exterior material. Further, as a means for bonding the exterior material and the interior container, in addition to the method of applying the above-described adhesive to a portion requiring adhesiveness, after providing an adhesive resin layer on the entire inner surface of the paper layer, Alternatively, a varnish layer not exhibiting adhesiveness to the material of the interior container may be partially provided on the unnecessary adhesive portion.
【０００８】本発明の外装材は、紙または紙を主体とす
る材料から成る。紙としては一般的な紙器用板紙、例え
ば、加工板紙のコートボール等が用いられる。また、牛
乳パック、紙カップ用のバージンパルプ加工紙を用いる
ことも好ましく行なわれる。合成紙の使用も可能であ
る。容器強度の面から、坪量、厚みを考慮して外装材用
材料を選択することが好ましい。本発明の複合容器にお
いては、接着剤の塗工パターンを工夫することにより、
坪量の低い紙を外装材に用いても、複合容器外装材のし
わを生じにくくなっている。[0008] The exterior material of the present invention is made of paper or a material mainly composed of paper. As the paper, a general paperboard for paper containers, for example, a coated ball of processed paperboard is used. It is also preferable to use virgin pulp paper for milk packs and paper cups. The use of synthetic paper is also possible. From the viewpoint of container strength, it is preferable to select the material for the exterior material in consideration of the basis weight and the thickness. In the composite container of the present invention, by devising a coating pattern of the adhesive,
Even if paper having a low basis weight is used as the exterior material, the composite container exterior material is less likely to wrinkle.
【０００９】外装材に耐水性を付与する場合、バリアー
性フィルムを外側に貼り合わせることも有効であるが、
端面処理あるいは樹脂を含浸することも行なわれる。バ
リアー性フィルムを外側に貼り合わせた場合、外装材の
強度が向上するため、しわが生じにくくなる。When imparting water resistance to the exterior material, it is effective to attach a barrier film to the outside,
End face treatment or impregnation with resin is also performed. When the barrier film is bonded to the outside, the strength of the exterior material is improved, so that wrinkles are less likely to occur.
【００１０】本発明の接着剤としては内装容器の成形温
度で接着性を発現する接着剤なら構わないが、ホットメ
ルトタイプあるいはホットラッカーと呼ばれる溶媒希釈
タイプのホットメルトが好ましく用いられる。そのよう
な接着剤としてはエチレン−酢酸ビニル共重合体、エチ
レン−アクリル酸エチル、オレフィンを主成分とするも
の等を用いることができる。The adhesive of the present invention may be any adhesive that exhibits adhesiveness at the molding temperature of the inner container, but a hot-melt type or a hot-melt of a solvent dilution type called a hot lacquer is preferably used. As such an adhesive, an ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate, an adhesive mainly containing an olefin, or the like can be used.
【００１１】上記ホットラッカーは紙に直接、塗工する
としみ込んでしまい、接着力を発現できないことがある
ため、ポリエチレン貼り、あるいは目止め剤を塗工した
後に、ホットラッカーを重ね塗りするのが好ましい。そ
の他、感圧接着剤等も用いることができる。さらに、外
装材が紙のみから成る場合にはエマルジョンタイプの接
着剤、例えば、エチレン−酢酸ビニル共重合体エマルジ
ョンを用いることができる。接着剤の塗工方法としては
グラビアコーター、ロールコーター、グラビア印刷機等
が適宜、選択される。The above-mentioned hot lacquer may penetrate directly into paper and impair the adhesive strength. Therefore, it is preferable to apply the hot lacquer again after applying polyethylene or applying a filler. . In addition, a pressure-sensitive adhesive or the like can be used. Further, when the exterior material is made of only paper, an emulsion-type adhesive, for example, an ethylene-vinyl acetate copolymer emulsion can be used. As a method of applying the adhesive, a gravure coater, a roll coater, a gravure printing machine, or the like is appropriately selected.
【００１２】一方、接着性樹脂を紙基材に全面的に施し
た後、接着不要部分には非接着性ニスを部分塗工し、マ
スキングする構成においては、接着性樹脂としては熱可
塑性樹脂を用いるのが好ましく、そのような接着性樹脂
としてはエチレンαオレフィン共重合体、エチレンαオ
レフィン共重合体の有機酸変性物、エチレンアクリル酸
コポリマー、マレイン酸グラフトポリプロピレン、エチ
レン−酢酸ビニル共重合体（ＥＶＡ）、アイオノマー、
エチレン・メタクリル酸・エステル共重合物、等が挙げ
られ、用いる内装延伸ブロー容器を構成する樹脂により
好ましいものを選ぶことができる。On the other hand, after the adhesive resin is applied to the entire surface of the paper base material, a non-adhesive varnish is partially applied to portions that do not need to be adhered, and in a configuration in which masking is performed, thermoplastic resin is used as the adhesive resin. It is preferable to use such an adhesive resin as an ethylene α-olefin copolymer, an organic acid-modified ethylene α-olefin copolymer, ethylene acrylic acid copolymer, maleic acid-grafted polypropylene, ethylene-vinyl acetate copolymer ( EVA), ionomers,
Ethylene / methacrylic acid / ester copolymers and the like can be mentioned, and a preferable resin can be selected depending on the resin constituting the interior stretch blow container to be used.
【００１３】接着性樹脂の内装延伸ブロー容器との接着
性を向上させるために、接着性樹脂層を外装材の紙基材
上に設けた後にコロナ放電処理、プラズマ処理、紫外線
処理等を施すこともできる。外装材内面に部分的に塗工
する非接着性ニスとしては、内装容器を構成する延伸ブ
ロー容器との接着性がないものであればよく、剥離ニス
と呼ばれるシリコーン樹脂系ワニス、ニトロセルロース
系樹脂を主体とするワニス、アクリル樹脂系ワニス等か
ら選ぶことができる。In order to improve the adhesion of the adhesive resin to the interior stretch blow container, a corona discharge treatment, a plasma treatment, an ultraviolet treatment, etc. are performed after providing the adhesive resin layer on the paper base material of the exterior material. Can also. As the non-adhesive varnish to be partially applied to the inner surface of the exterior material, any non-adhesive varnish may be used as long as it does not have an adhesive property with the stretch blow container constituting the interior container. And acrylic resin-based varnishes.
【００１４】本発明の内装容器を構成する樹脂は、好ま
しくはポリプロピレンあるいはポリエチレンテレフタレ
ートであるが、ブロー成形、延伸ブロー成形可能な熱可
塑性プラスチックであれば良く、例えば、ポリエチレ
ン、ポリエチレン−２，６−ナフタレート、ポリアクリ
ロニトリル、またはこれらの樹脂のブレンドでもよい。
要求品質に応じて、酸素バリアー性、水蒸気バリアー性
等のガスバリアー性材料を選択するのが好ましい。The resin constituting the interior container of the present invention is preferably polypropylene or polyethylene terephthalate, but may be a thermoplastic plastic which can be blow-molded or stretch-blow-molded, such as polyethylene, polyethylene-2,6- Naphthalate, polyacrylonitrile, or a blend of these resins may be used.
It is preferable to select a gas barrier material such as an oxygen barrier property and a water vapor barrier property according to required quality.
【００１５】本発明の複合容器においては使用樹脂量を
減らすため、要求品質を満たす範囲内で、内装容器の胴
部肉厚を薄くするのが好ましい。内装容器の胴部肉厚が
薄くとも、延伸ブロー成形により、内装容器のガスバリ
アー性は向上し、また、接着剤塗工部分を工夫した外装
材で落下強度等の強度を付与することが可能である。In the composite container of the present invention, in order to reduce the amount of resin used, it is preferable to reduce the thickness of the body of the interior container within a range satisfying the required quality. Stretch blow molding improves the gas barrier properties of the interior container even if the thickness of the body of the interior container is thin, and it is possible to impart strength such as drop strength by using an exterior material with a modified adhesive-coated part. It is.
【００１６】本発明の複合容器の製造方法としては、予
備成形体を射出成形によって得、その後、延伸ブロー成
形を行なう。本発明の製造方法の一例として延伸ブロー
成形について説明する。まず、樹脂から成る予備成形体
を予め、射出成形により得る。その後、所定形状に成形
した外装材を金型内に載置し、この外装材内で、成形温
度に加熱した内装容器の予備成形体を延伸ブロー成形す
ることによって本発明の容器を得ることができる。外装
材を金型に載置し、本発明の複合容器を得る場合、外装
材内面に内装容器の予備成形体の成形温度で接着効果を
発揮する接着剤層を設けることにより、外装材と内装容
器を一体化することが可能である。In the method for producing the composite container of the present invention, a preform is obtained by injection molding, and thereafter, stretch blow molding is performed. Stretch blow molding will be described as an example of the production method of the present invention. First, a preform made of resin is obtained in advance by injection molding. Thereafter, the exterior material molded into a predetermined shape is placed in a mold, and in this exterior material, the preform of the interior container heated to the molding temperature is subjected to stretch blow molding to obtain the container of the present invention. it can. When the exterior material is placed on a mold to obtain the composite container of the present invention, the exterior material and the interior material are provided by providing an adhesive layer that exhibits an adhesive effect at the molding temperature of the preform of the interior container on the interior surface of the exterior material. It is possible to integrate the container.
【００１７】本発明の複合容器は使用後、外装材と内装
容器とをさらに容易に分離し易くするため、外装材にミ
シン目、ジッパー等を設けて分離のきっかけを作るのが
好ましい。In the composite container of the present invention, in order to make it easier to separate the exterior material and the interior container after use, it is preferable to provide a perforation, a zipper or the like on the exterior material to create a trigger for separation.
【００１８】＜作用＞本発明の複合容器は内装容器の胴
部肉厚を薄くすることが可能であるので、内装容器の樹
脂使用量が、同容量のプラスチック容器と比較して減少
し、しかも延伸ブロー成形により内装容器のガスバリア
ー性および強度は向上し、紙から成る外装材が一体化さ
れているので内装容器だけよりも強度的に有利な構造と
なっている。また、外装材内面に少なくとも胴部を除い
て、部分的に接着剤層を設けてあるので成形時に外装材
と内装容器とを一体化することが可能となり、使用後、
廃棄する際には容易に外装材と内装容器を分離すること
も可能となる。<Function> The composite container of the present invention can reduce the wall thickness of the inner container, so that the amount of resin used in the inner container is reduced as compared with a plastic container having the same capacity. Stretch blow molding improves the gas barrier properties and strength of the inner container, and has a structure more advantageous in strength than the inner container alone because the outer material made of paper is integrated. Also, except for at least the trunk on the inner surface of the exterior material, it is possible to integrate the exterior material and the interior container during molding because the adhesive layer is partially provided, and after use,
At the time of disposal, the exterior material and the interior container can be easily separated.
【００１９】さらに本発明の複合容器は少なくとも胴部
を除いて、外装材内面に接着剤層を設けてあるため、内
装容器の収縮により外装材が引っ張られないのでしわを
防止することができる。また、製造に当たっても、成形
された外装材を内装容器の成形金型内に載置し、内装容
器の成形と同時に、一体化した複合容器を製造すること
ができるため、工程が簡単でコストダウンに繋がる。Further, since the composite container of the present invention has an adhesive layer on the inner surface of the exterior material except for at least the body, the exterior material is not pulled by the shrinkage of the interior container, so that wrinkles can be prevented. In addition, even in manufacturing, the molded exterior material is placed in the molding die of the interior container, and at the same time as the interior container is molded, an integrated composite container can be manufactured. Leads to.
【００２０】[0020]
【実施例】以下、実施例に基づき具体的に説明を行なう
が、本発明は以下の例に限定されるものではない。The present invention will be specifically described below with reference to examples, but the present invention is not limited to the following examples.
【００２１】（実施例１）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出コートしたコートボール
（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより図２の斜線部に塗工した後、抜き、背貼り
を行なって外装材とした。内装容器構成樹脂としてポリ
プロピレン（ＭＩ＝７）を用い、予備成形体を得た後、
予め作成した外装材を金型内に載置し、その中で延伸ブ
ロー成形して、図１に示す形状の、胴部平均肉厚１７０
μｍ、内容量１０００ｍｌの、内装容器と外装材とから
成る複合容器を成形した。Example 1 As an exterior material, a coated ball (basis weight 270 g / m 2 ) having an inner surface extruded with polyethylene (thickness 25 μm) was used, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the shaded portion in FIG. 2 with a gravure coater, punching and back-pasting were performed to obtain an exterior material. After using polypropylene (MI = 7) as the resin for the inner container and obtaining a pre-formed body,
The exterior material prepared in advance is placed in a mold and stretch blow-molded in the mold, and the body average thickness 170 of the shape shown in FIG.
A composite container composed of an inner container and an outer material having a size of 1000 μm and an inner volume of 1000 ml was formed.
【００２２】（実施例２）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出コートしたコートボール
（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより、図３の斜線部に塗工した後、抜き、背貼
りを行なって外装材とした。内装容器構成樹脂としてポ
リプロピレン（ＭＩ＝７）を用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図１に示す形状の、胴部平均肉厚１
７０μｍ、内容量１０００ｍｌの、内装容器と外装材と
から成る複合容器を成形した。(Example 2) As an exterior material, a coated ball (weight basis: 270 g / m 2 ) having an inner surface extruded with polyethylene (thickness: 25 μm) was used, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the shaded portion in FIG. 3 with a gravure coater, the coating was removed and back-adhered to obtain an exterior material. After using a polypropylene (MI = 7) as the resin for the interior container and obtaining a pre-molded body, the exterior material prepared in advance is placed in a mold and stretch blow-molded therein to obtain a shape shown in FIG. Of the body average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 1000 ml was formed.
【００２３】（実施例３）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出コートしたコートボール
（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより、図４の斜線部に塗工した後、抜き、背貼
りを行なって外装材とした。内装容器構成樹脂としてポ
リプロピレン（ＭＩ＝７）を用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図１に示す形状の、胴部平均肉厚１
７０μｍ、内容量１０００ｍｌの、内装容器と外装材と
から成る複合容器を成形した。(Example 3) As an exterior material, a coated ball (basis weight 270 g / m 2 ) having an inner surface extruded with polyethylene (thickness 25 μm) was used, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating was applied to the hatched portion in FIG. 4 by a gravure coater, punching and backing were performed to obtain an exterior material. After using a polypropylene (MI = 7) as the resin for the interior container and obtaining a pre-molded body, the exterior material prepared in advance is placed in a mold and stretch blow-molded therein to obtain a shape shown in FIG. Of the body average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 1000 ml was formed.
【００２４】（実施例４）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出コートしたコートボール
（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより、図５のドット部分に塗工した後、抜き、
背貼りを行なって外装材とした。内装容器構成樹脂とし
てポリプロピレン（ＭＩ＝７）を用い、予備成形体を得
た後、予め作成した外装材を金型内に載置し、その中で
延伸ブロー成形して、図１に示す形状の、胴部平均肉厚
１７０μｍ、内容量１０００ｍｌの、内装容器と外装材
とから成る複合容器を成形した。(Example 4) As an exterior material, a coated ball (weight basis: 270 g / m 2 ) having an inner surface extruded with polyethylene (thickness: 25 μm) was used, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. Using a gravure coater, apply the dots in FIG.
A backing was performed to obtain an exterior material. After using a polypropylene (MI = 7) as the resin for the interior container and obtaining a pre-molded body, the exterior material prepared in advance is placed in a mold and stretch blow-molded therein to obtain a shape shown in FIG. A composite container composed of an inner container and an outer material having an average body thickness of 170 μm and an inner volume of 1000 ml was molded.
【００２５】（実施例５）外装材として、内面にポリプ
ロピレン（厚み２５μｍ）を押出コートしたカップ原紙
（サイズ剤を充填したバージンパルプ、坪量３００ｇ／
ｍ2 ）を用い、接着剤としてエチレン−酢酸ビニル共重
合体系ホットラッカーを、グラビアコーターにより、図
２の斜線部に塗工した後、抜き、背貼りを行なって外装
材とした。内装容器構成樹脂としてポリプロピレン（Ｍ
Ｉ＝７）を用い、予備成形体を得た後、予め作成した外
装材を金型内に載置し、その中で延伸ブロー成形して、
図１に示す形状の、胴部平均肉厚１７０μｍ、内容量１
０００ｍｌの、内装容器と外装材とから成る複合容器を
成形した。(Example 5) As an exterior material, a cup base paper (virgin pulp filled with a sizing agent, basis weight 300 g /
Using m 2 ), an ethylene-vinyl acetate copolymer hot lacquer was applied as an adhesive to the hatched portion in FIG. 2 by a gravure coater, and then punched out and back-adhered to obtain an exterior material. Polypropylene (M
I = 7), and after obtaining a preform, the exterior material prepared in advance is placed in a mold and stretch blow-molded therein,
The shape shown in FIG.
000 ml of a composite container composed of an inner container and an outer material was molded.
【００２６】（実施例６）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出コートしたカップ原紙
（坪量３００ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターで図３の斜線部に塗工した後、抜き、背貼りを行
なって外装材とした。内装容器構成樹脂としてポリプロ
ピレン（ＭＩ＝７）を用い、予備成形体を得た後、予め
作成した外装材を金型内に載置し、その中で延伸ブロー
成形して、図１に示す形状の、胴部平均肉厚１７０μ
ｍ、内容量１０００ｍｌの、内装容器と外装材とから成
る複合容器を成形した。(Example 6) A cup base paper (basis weight 300 g / m 2 ) having an inner surface extruded with polyethylene (25 μm) was used as an exterior material, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the hatched portion in FIG. 3 with a gravure coater, punching and back-pasting were performed to obtain an exterior material. After using a polypropylene (MI = 7) as the resin for the interior container and obtaining a pre-molded body, the exterior material prepared in advance is placed in a mold and stretch blow-molded therein to obtain a shape shown in FIG. Of the body average thickness 170μ
m, a composite container having an inner volume of 1000 ml and comprising an inner container and an outer material was molded.
【００２７】（実施例７）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出コートしたカップ原紙
（坪量３００ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより、図４の斜線部に塗工した後、抜き、背貼
りを行なって外装材とした。内装容器構成樹脂としてポ
リプロピレン（ＭＩ＝７）を用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図１に示す形状の、胴部平均肉厚１
７０μｍ、内容量１０００ｍｌの、内装容器と外装材と
から成る複合容器を成形した。(Example 7) A cup base paper (basis weight 300 g / m 2 ) having an inner surface extruded with polyethylene (thickness 25 μm) was used as an exterior material, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating was applied to the hatched portion in FIG. 4 by a gravure coater, punching and backing were performed to obtain an exterior material. After using a polypropylene (MI = 7) as the resin for the interior container and obtaining a pre-molded body, the exterior material prepared in advance is placed in a mold and stretch blow-molded therein to obtain a shape shown in FIG. Of the body average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 1000 ml was formed.
【００２８】（実施例８）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出コートしたカップ原紙
（坪量３００ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより図５のドット部分に塗工した後、抜き、背
貼りを行なって外装材とした。内装容器構成樹脂として
ポリプロピレン（ＭＩ＝７）を用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図１に示す形状の、胴部平均肉厚１
７０μｍ、内容量１０００ｍｌの、内装容器と外装材と
から成る複合容器を成形した。(Example 8) A cup base paper (basis weight 300 g / m 2 ) having an inner surface extruded with polyethylene (thickness 25 μm) was used as an exterior material, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the dot portion in FIG. 5 with a gravure coater, punching and back bonding were performed to obtain an exterior material. After using a polypropylene (MI = 7) as the resin for the interior container and obtaining a pre-molded body, the exterior material prepared in advance is placed in a mold and stretch blow-molded therein to obtain a shape shown in FIG. Of the body average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 1000 ml was formed.
【００２９】（実施例９）外装材として、内面にポリエ
チレン（厚み２５μｍ）を押出しコートしたコートボー
ル（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレ
ン−酢酸ビニル共重合体系ホットラッカーを、グラビア
コーターにより図９の斜線部に塗工した後、抜き、背貼
りを行なって外装材とした。内装容器構成樹脂としてポ
リエチレンテレフタレートを用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図８に示す形状の、胴部平均肉厚１
７０μｍ、内容量８００ｍｌの、内装容器と外装材とか
ら成る複合容器を成形した。Example 9 As an exterior material, a coated ball (basis weight 270 g / m 2 ) having an inner surface extruded with polyethylene (thickness 25 μm) was used, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the shaded area in FIG. 9 with a gravure coater, the sheet was removed and back-adhered to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. Average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 800 ml was formed.
【００３０】（実施例１０）外装材として、内面にポリ
エチレン（厚み２５μｍ）を押出コートしたコートボー
ル（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレ
ン−酢酸ビニル共重合体系ホットラッカーを、グラビア
コーターにより図１０の斜線部に塗工した後、抜き、背
貼りを行なって外装材とした。内装容器構成樹脂として
ポリエチレンテレフタレートを用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図８に示す形状の、胴部平均肉厚１
７０μｍ、内容量８００ｍｌの、内装容器と外装材とか
ら成る複合容器を成形した。(Example 10) As an exterior material, a coat ball (basis weight 270 g / m 2 ) having an inner surface extruded with polyethylene (thickness 25 μm) was used, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the shaded portion in FIG. 10 with a gravure coater, the coating was removed and the back was applied to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. Average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 800 ml was formed.
【００３１】（実施例１１）外装材として、内面にポリ
エチレン（厚み２５μｍ）を押出コートしたコートボー
ル（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレ
ン−酢酸ビニル共重合体系ホットラッカーを、グラビア
コーターにより図１１の斜線部に塗工した後、抜き、背
貼りを行なって外装材とした。内装容器構成樹脂として
ポリエチレンテレフタレートを用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図８に示す形状の、胴部平均肉厚１
７０μｍ、内容量８００ｍｌの、内装容器と外装材とか
ら成る複合容器を成形した。(Example 11) As an exterior material, a coated ball (weight basis: 270 g / m 2 ) having an inner surface extruded with polyethylene (thickness: 25 μm) was used, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the hatched portion in FIG. 11 with a gravure coater, the coating was removed and back-adhered to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. Average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 800 ml was formed.
【００３２】（実施例１２）外装材として、内面にポリ
エチレン（厚み２５μｍ）を押出コートしたコートボー
ル（坪量２７０ｇ／ｍ2 ）を用い、接着剤としてエチレ
ン−酢酸ビニル共重合体系ホットラッカーを、グラビア
コーターにより図１２のドット部分に塗工した後、抜
き、背貼りを行なって外装材とした。内装容器構成樹脂
としてポリエチレンテレフタレートを用い、予備成形体
を得た後、予め作成した外装材を金型内に載置し、その
中で延伸ブロー成形して、図８に示す形状の、胴部平均
肉厚１７０μｍ、内容量８００ｍｌの、内装容器と外装
材とから成る複合容器を成形した。Example 12 A coated ball (weight basis: 270 g / m 2 ) having an inner surface extruded with polyethylene (25 μm) was used as an exterior material, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the dot portion in FIG. 12 with a gravure coater, punching and back bonding were performed to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. A composite container having an average thickness of 170 μm and an internal capacity of 800 ml and comprising an interior container and an exterior material was molded.
【００３３】（実施例１３）外装材として、内面にポリ
エチレン（厚み２５μｍ）を押出コートしたカップ原紙
（サイズ剤を充填したバージンパルプ、坪量３００ｇ／
ｍ2 ）を用い、接着剤としてエチレン−酢酸ビニル共重
合体系ホットラッカーを、グラビアコーターにより図９
の斜線部に塗工した後、抜き、背貼りを行なって外装材
とした。内装容器構成樹脂としてポリエチレンテレフタ
レートを用い、予備成形体を得た後、予め作成した外装
材を金型内に載置し、その中で延伸ブロー成形して、図
８に示す形状の、胴部平均肉厚１７０μｍ、内容量８０
０ｍｌの、内装容器と外装材とから成る複合容器を成形
した。Example 13 As an exterior material, a cup base paper (virgin pulp filled with a sizing agent, basis weight 300 g /
m 2 ), an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive, and a gravure coater was used as the adhesive in FIG.
After coating on the shaded portion of No. 4, the sheet was punched and back-adhered to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. Average thickness 170μm, content 80
A 0 ml composite container consisting of an interior container and an exterior material was molded.
【００３４】（実施例１４）外装材として、内面にポリ
エチレン（厚み２５μｍ）を押出コートしたカップ原紙
（坪量３００ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより図１０の斜線部に塗工した後、抜き、背貼
りを行なって外装材とした。内装容器構成樹脂としてポ
リエチレンテレフタレートを用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図８に示す形状の、胴部平均肉厚１
７０μｍ、内容量８００ｍｌの、内装容器と外装材とか
ら成る複合容器を成形した。(Example 14) A cup base paper (basis weight 300 g / m 2 ) having an inner surface extruded with polyethylene (25 μm) was used as an exterior material, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the shaded portion in FIG. 10 with a gravure coater, the coating was removed and the back was applied to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. Average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 800 ml was formed.
【００３５】（実施例１５）外装材として、内面にポリ
エチレン（厚み２５μｍ）を押出コートしたカップ原紙
（坪量３００ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより図１１の斜線部に塗工した後、抜き、背貼
りを行なって外装材とした。内装容器構成樹脂としてポ
リエチレンテレフタレートを用い、予備成形体を得た
後、予め作成した外装材を金型内に載置し、その中で延
伸ブロー成形して、図８に示す形状の、胴部平均肉厚１
７０μｍ、内容量８００ｍｌの、内装容器と外装材とか
ら成る複合容器を成形した。Example 15 A cup base paper (basis weight: 300 g / m 2 ) having an inner surface extruded with polyethylene (thickness: 25 μm) was used as an exterior material, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the hatched portion in FIG. 11 with a gravure coater, the coating was removed and back-adhered to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. Average thickness 1
A composite container composed of an inner container and an outer material having a size of 70 μm and an inner volume of 800 ml was formed.
【００３６】（実施例１６）外装材として、内面にポリ
エチレン（厚み２５μｍ）を押出コートしたカップ原紙
（坪量３００ｇ／ｍ2 ）を用い、接着剤としてエチレン
−酢酸ビニル共重合体系ホットラッカーを、グラビアコ
ーターにより図１２のドット部分に塗工した後、抜き、
背貼りを行なって外装材とした。内装容器構成樹脂とし
てポリエチレンテレフタレートを用い、予備成形体を得
た後、予め作成した外装材を金型内に載置し、その中で
延伸ブロー成形して、図８に示す形状の、胴部平均肉厚
１７０μｍ、内容量８００ｍｌの、内装容器と外装材と
から成る複合容器を成形した。(Example 16) A cup base paper (basis weight 300 g / m 2 ) having an inner surface extruded with polyethylene (25 μm) was used as an exterior material, and an ethylene-vinyl acetate copolymer hot lacquer was used as an adhesive. After coating the dots in Fig. 12 with a gravure coater,
A backing was performed to obtain an exterior material. After using polyethylene terephthalate as the resin for the interior container and obtaining a preform, the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a body portion having a shape shown in FIG. A composite container having an average thickness of 170 μm and an internal capacity of 800 ml and comprising an interior container and an exterior material was molded.
【００３７】（実施例１７）外装材として、内面にエチ
レン・メタクリル酸・エステル共重合物（厚み２０μ
ｍ）を押出コートしたカップ原紙（坪量３００ｇ／
ｍ2 ）を用い、非接着性ニスとしてニトロセルロース系
ワニスを図１２のドット部分を除く全面にグラビア塗工
した後、図１２に示す展開形状に打ち抜き、背貼りを行
なって筒状の外装材を作成した。内装容器を構成する樹
脂としてポリエチレンテレフタレートを用い、予備成形
体を射出成形した後、予め作成した外装材を金型内に載
置し、その中で延伸ブロー成形して図８に示す形状の胴
部平均肉厚１７０μｍ、内容量８００ｍｌの、内装容器
と外装材とから成る複合容器を成形した。Example 17 As an exterior material, an ethylene / methacrylic acid / ester copolymer (thickness: 20 μm)
m) extrusion-coated cup base paper (basis weight 300g /
m 2 ), a nitrocellulose-based varnish is applied as a non-adhesive varnish to the entire surface except for the dot portion in FIG. 12 and then punched into a developed shape shown in FIG. It was created. Using polyethylene terephthalate as a resin constituting the interior container, injection molding of a preform is carried out, and the exterior material prepared in advance is placed in a mold, stretch-blow molded therein, and a cylinder having a shape shown in FIG. A composite container composed of an interior container and an exterior material having a partial average thickness of 170 μm and an internal capacity of 800 ml was formed.
【００３８】（比較例１）接着剤を図６の斜線部に塗工
した以外は、実施例１と同様にして、比較例１の複合容
器を得た。(Comparative Example 1) A composite container of Comparative Example 1 was obtained in the same manner as in Example 1 except that the adhesive was applied to the hatched portions in FIG.
【００３９】（比較例２）接着剤を図７の斜線部に塗工
した以外は、実施例１と同様にして、比較例２の複合容
器を得た。(Comparative Example 2) A composite container of Comparative Example 2 was obtained in the same manner as in Example 1 except that the adhesive was applied to the hatched portion in FIG.
【００４０】（比較例３）接着剤を図６の斜線部に塗工
した以外は、実施例５と同様にして、比較例３の複合容
器を得た。Comparative Example 3 A composite container of Comparative Example 3 was obtained in the same manner as in Example 5, except that the adhesive was applied to the hatched portions in FIG.
【００４１】（比較例４）接着剤を図７の斜線部に塗工
した以外は、実施例５と同様にして、比較例４の複合容
器を得た。(Comparative Example 4) A composite container of Comparative Example 4 was obtained in the same manner as in Example 5, except that the adhesive was applied to the hatched portions in FIG.
【００４２】（比較例５）接着剤を図１３の斜線部に塗
工した以外は、実施例９と同様にして、比較例５の複合
容器を得た。(Comparative Example 5) A composite container of Comparative Example 5 was obtained in the same manner as in Example 9, except that the adhesive was applied to the hatched portion in FIG.
【００４３】（比較例６）接着剤を図１４の斜線部に塗
工した以外は、実施例９と同様にして、比較例６の複合
容器を得た。(Comparative Example 6) A composite container of Comparative Example 6 was obtained in the same manner as in Example 9 except that the adhesive was applied to the hatched portion in FIG.
【００４４】（比較例７）接着剤を図１３の斜線部に塗
工した以外は、実施例１３と同様にして、比較例７の複
合容器を得た。(Comparative Example 7) A composite container of Comparative Example 7 was obtained in the same manner as in Example 13 except that the adhesive was applied to the hatched portion in FIG.
【００４５】（比較例８）接着剤を図１４の斜線部に塗
工した以外は、実施例１３と同様にして、比較例８の複
合容器を得た。Comparative Example 8 A composite container of Comparative Example 8 was obtained in the same manner as in Example 13 except that the adhesive was applied to the hatched portion in FIG.
【００４６】実施例１乃至実施例１７、比較例１乃至比
較例８の複合容器を、温度２５℃、湿度６５％の条件下
で２４時間保存してから、しわの有無を確認した。その
結果を表１に示す。The composite containers of Examples 1 to 17 and Comparative Examples 1 to 8 were stored for 24 hours at a temperature of 25 ° C. and a humidity of 65%, and then checked for wrinkles. Table 1 shows the results.
【００４７】[0047]
【表１】 [Table 1]
【００４８】実施例１〜１７の複合容器ではしわは観察
されなかったが、比較例１〜８の複合容器では胴部のし
わが生じた。Although no wrinkles were observed in the composite containers of Examples 1 to 17, wrinkles of the body portion occurred in the composite containers of Comparative Examples 1 to 8.
【００４９】[0049]
【発明の効果】以上詳細に説明したように本発明によれ
ば、紙を主体とする外装材にしわがなく、外観の優れ
た、商品価値の高い複合容器が得られる。特に外装材と
内装容器とを肩部と底部において接着し、胴部において
は非接着とすることによりしわの発生防止だけでなく、
外装材と内装容器との一体性が保持され、複合容器とし
ての剛性も保持される。さらに外装材と内装容器とを肩
部と底部においてドット状等のパターンで部分的に接着
することよりしわの発生防止、複合容器としての剛性の
保持に加えて使用後の廃棄時の外装材と内装容器との分
離性も向上する。As described in detail above, according to the present invention, a composite container having excellent appearance and high commercial value can be obtained without wrinkles in an exterior material mainly composed of paper. In particular, the exterior material and the interior container are bonded at the shoulder and the bottom, and the body is not bonded.
The integrity of the exterior material and the interior container is maintained, and the rigidity of the composite container is also maintained. Furthermore, the exterior material and the interior container are partially adhered to each other in a dot-like pattern on the shoulder and the bottom to prevent wrinkles, maintain the rigidity of the composite container, and use the exterior material at the time of disposal after use. Separability from the interior container is also improved.
【００５０】[0050]
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明の複合容器の一例を示す斜視図である。FIG. 1 is a perspective view showing an example of a composite container of the present invention.
【図２】本発明の複合容器の第一例の外装材の第一の接
着剤塗工パターンを示す展開説明図である（斜線部が接
着剤塗工部）。FIG. 2 is a development explanatory view showing a first adhesive application pattern of an exterior material of the first example of the composite container of the present invention (hatched portions are adhesive applied portions).
【図３】本発明の複合容器の第一例の外装材の第二の接
着剤塗工パターンを示す展開説明図である（斜線部が接
着剤塗工部）。FIG. 3 is a development explanatory view showing a second adhesive coating pattern of the exterior material of the first example of the composite container of the present invention (hatched portions are adhesive coated portions).
【図４】本発明の複合容器の第一例の外装材の第三の接
着剤塗工パターンを示す展開説明図である（斜線部が接
着剤塗工部）。FIG. 4 is a development explanatory view showing a third adhesive application pattern of the exterior material of the first example of the composite container of the present invention (the hatched portion is an adhesive application portion).
【図５】本発明の複合容器の第一例の外装材の第四の接
着剤塗工パターンを示す展開説明図である（小さい丸で
囲まれた部分が接着剤塗工部）。FIG. 5 is a development explanatory view showing a fourth adhesive coating pattern of the exterior material of the first example of the composite container of the present invention (a portion surrounded by a small circle is an adhesive coating portion).
【図６】本発明の複合容器の比較例１及び比較例３の外
装材の接着剤塗工パターンを示す展開説明図である（斜
線部が接着剤塗工部）。FIG. 6 is a development explanatory view showing an adhesive application pattern of the exterior material of Comparative Example 1 and Comparative Example 3 of the composite container of the present invention (hatched portions are adhesive applied portions).
【図７】本発明の複合容器の比較例２及び比較例４の外
装材の接着剤塗工パターンを示す展開説明図である（斜
線部が接着剤塗工部）。FIG. 7 is a development explanatory view showing an adhesive coating pattern of the packaging material of Comparative Example 2 and Comparative Example 4 of the composite container of the present invention (hatched portions are adhesive coated portions).
【図８】本発明の複合容器の別の例を示す斜視図であ
る。FIG. 8 is a perspective view showing another example of the composite container of the present invention.
【図９】本発明の複合容器の第二例の外装材の第一の接
着剤塗工パターンを示す展開説明図である（斜線部が接
着剤塗工部）。FIG. 9 is a development explanatory view showing a first adhesive application pattern of an exterior material of a second example of the composite container of the present invention (a hatched portion is an adhesive application portion).
【図１０】本発明の複合容器の第二例の外装材の第二の
接着剤塗工パターンを示す展開説明図である（斜線部が
接着剤塗工部）。FIG. 10 is a development explanatory view showing a second adhesive coating pattern of the exterior material of the second example of the composite container of the present invention (the hatched portion is an adhesive coated portion).
【図１１】本発明の複合容器の第二例の外装材の第三の
接着剤塗工パターンを示す展開説明図である（斜線部が
接着剤塗工部）。FIG. 11 is a development explanatory view showing a third adhesive coating pattern of the exterior material of the second example of the composite container of the present invention (the hatched portion is an adhesive coated portion).
【図１２】本発明の複合容器の第二例の外装材の第四の
接着剤塗工パターンを示す展開説明図である（小さい丸
で囲まれた部分が接着剤塗工部）。FIG. 12 is a development explanatory view showing a fourth adhesive application pattern of the exterior material of the second example of the composite container of the present invention (a portion surrounded by a small circle is an adhesive application section).
【図１３】本発明の複合容器の比較例５及び比較例７の
外装材の接着剤塗工パターンを示す展開説明図である
（斜線部が接着剤塗工部）。FIG. 13 is a development explanatory view showing an adhesive coating pattern of the exterior material of Comparative Example 5 and Comparative Example 7 of the composite container of the present invention (hatched portions are adhesive coated portions).
【図１４】本発明の複合容器の比較例６及び比較例８の
外装材の接着剤塗工パターンを示す展開説明図である
（斜線部が接着剤塗工部）。FIG. 14 is a development explanatory view showing an adhesive application pattern of the exterior material of Comparative Example 6 and Comparative Example 8 of the composite container of the present invention (hatched portions are adhesive applied portions).
Ａ・・・複合容器 １・・・外装材 ２・・・内装容器 ３・・・口部 ４・・・肩部 ５・・・胴部 ６・・・
底部 ａ・・・肩部接着剤塗工部分 ｂ・・・底部接着剤塗工
部分A: Composite container 1 ... Exterior material 2 ... Interior container 3 ... Mouth 4 ... Shoulder 5 ... Body 6 ...
Bottom part a: Shoulder adhesive coated part b: Bottom adhesive coated part
フロントページの続き (72)発明者 鈴田 昌由 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内Continued on the front page (72) Inventor Masayoshi Suzuda 1-5-1, Taito, Taito-ku, Tokyo Letterpress Printing Co., Ltd.
Claims (10)
部から成る樹脂製内装容器とを組み合わせた複合容器に
おいて、少なくとも胴部を除いて、外装材内面に接着剤
層を設けたことを特徴とする複合容器。1. A composite container in which an exterior material mainly composed of paper and a resin interior container comprising a body, a shoulder, and a bottom are combined, and an adhesive layer is provided on the inner surface of the exterior material except for at least the body. A composite container characterized by being provided.
部から成る樹脂製内装容器とを組み合わせた複合容器に
おいて、該複合容器の少なくとも胴部においては、外装
材内面と樹脂製内装容器とが非接着であり、肩部および
底部においては外装材内面と樹脂製内装容器とが接着さ
れていることを特徴とする請求項１記載の複合容器。2. A composite container in which an exterior material mainly composed of paper is combined with a resin interior container having a body, a shoulder, and a bottom, wherein at least the body of the composite container has an inner surface of the exterior material and a resin. The composite container according to claim 1, wherein the inner container made of resin is non-adhesive, and the inner surface of the exterior material and the inner container made of resin are adhered at the shoulder and the bottom.
た肩フラップ、下端に連設された底フラップから成るこ
とを特徴とする請求項１又は請求項２記載の複合容器。3. The composite container according to claim 1, wherein the exterior material comprises a body flap, a shoulder flap connected to an upper end thereof, and a bottom flap connected to a lower end thereof.
内装容器の少なくとも胴部を除いた部分において全面接
着されていることを特徴とする請求項１又は請求項３記
載の複合容器。4. The composite container according to claim 1, wherein the inner surface of the exterior material and the resin inner container are entirely bonded at least in a portion of the resin inner container except for a body portion. .
内装容器の少なくとも胴部を除いた部分において部分的
に接着されていることを特徴とする請求項１又は請求項
３記載の複合容器。5. The resin inner container according to claim 1, wherein the inner surface of the exterior material and the resin inner container are partially adhered to each other at least in a portion of the resin inner container except for a body portion. Composite container.
内装容器の肩部および底部において全面接着されている
ことを特徴とする請求項２又は請求項３記載の複合容
器。6. The composite container according to claim 2, wherein the inner surface of the exterior material and the inner container made of resin are entirely adhered at the shoulder and the bottom of the inner container made of resin.
内装容器の肩部および底部において部分的に接着されて
いることを特徴とする請求項２又は請求項３記載の複合
容器。7. The composite container according to claim 2, wherein the inner surface of the exterior material and the resin inner container are partially adhered at the shoulder and the bottom of the resin inner container.
内面と樹脂製内装容器とが接着されていることを特徴と
する請求項１乃至請求項７記載の何れかの複合容器。8. The composite container according to claim 1, wherein the inner surface of the exterior material and the inner container made of resin are adhered to each other by an adhesive layer having a dot pattern.
樹脂層、部分的に施されたニス層を順次、設けたことを
特徴とする請求項１又は請求項２記載の複合容器。9. The composite container according to claim 1, wherein an adhesive resin layer and a partially applied varnish layer are sequentially provided on the entire inner surface of the exterior material mainly composed of paper. .
角形であることを特徴とする請求項１乃至請求項９記載
の何れかの複合容器。10. The composite container according to claim 1, wherein a horizontal cross-sectional shape of the exterior material is a quadrangle or more polygon.