JPH10298869A - Moisture-permeable and waterproof cloth - Google Patents

Moisture-permeable and waterproof cloth

Info

Publication number
JPH10298869A
JPH10298869A JP9109761A JP10976197A JPH10298869A JP H10298869 A JPH10298869 A JP H10298869A JP 9109761 A JP9109761 A JP 9109761A JP 10976197 A JP10976197 A JP 10976197A JP H10298869 A JPH10298869 A JP H10298869A
Authority
JP
Japan
Prior art keywords
moisture
cloth
permeable waterproof
density
permeable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP9109761A
Other languages
Japanese (ja)
Inventor
Tetsuya Tonmiya
哲也 頓宮
Takashi Ando
孝志 安藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Japan Gore Tex Inc
Original Assignee
Japan Gore Tex Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Japan Gore Tex Inc filed Critical Japan Gore Tex Inc
Priority to JP9109761A priority Critical patent/JPH10298869A/en
Publication of JPH10298869A publication Critical patent/JPH10298869A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a moisture-permeable and waterproof cloth having a smaller thickness than that of a conventional cloth and better in needle resistance than that of the conventional one. SOLUTION: This moisture-permeable and waterproof fabric is obtained by laminating high-density fabrics 2a and 2b having a fiber density in which the total count of warp and weft yarns per inch corresponds to >=240 yarns expressed in terms of yarns having 70 denier onto both sides of a moisture- permeable and waterproof membrane 1 or laminating the plural fabrics 2a and 2b onto at least one side of the moisture-permeable and-waterproof membrane 1 and laminating the resultant plural laminates composed of the high-density fabrics 2a and 2b and the moisture-permeable and waterproof membrane 1 so as to alternate the moisture-permeable and waterproof membrane 1 and the high-density fabrics 2a and 2b. A protecting fabric may be laminated onto the outermost moisture-permeable and waterproof membrane 1 of the moisture-permeable and waterproof cloth.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、有刺植物や蜂等の
昆虫の毒針などの針状体に対する耐性(以下、「耐針
性」という)を向上させて、有刺植物などに当接しても
針状体の貫通を防止し、さらには透湿防水性を保持でき
る透湿防水布に関し、衣料素材又はテント等のアウトド
ア製品用素材に用いられる。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention improves the resistance to needle-like bodies such as stinging needles of insects such as barbed plants and bees (hereinafter referred to as "needle resistance"), and is applicable to barbed plants and the like. The present invention relates to a moisture-permeable waterproof cloth that can prevent penetration of a needle-like body even when it comes into contact with it and can maintain moisture-permeable and waterproof properties.

【0002】[0002]

【従来の技術及び発明が解決しようとする課題】雨天時
や発汗時にも快適に着用できるような衣服素材として、
防水性を有するが水蒸気は透過させるという機能を有す
る透湿防水膜を布に貼付した透湿防水布がある。ここ
で、透湿防水膜としては、特公昭51―18991号公
報や特開昭60−39014号公報に開示されている多
孔質の延伸ポリテトラフルオロエチレン膜(以下、「e
PTFE膜」と略記する)が代表的である。これは、延
伸により多孔質化しているポリテトラフルオロエチレン
の微細気孔組織により透湿性を有するとともに、空孔の
微細さ及びポリテトラフルオロエチレンの撥水性ゆえに
防水性を示す。
BACKGROUND OF THE INVENTION As a garment material that can be worn comfortably even in rainy weather or sweating,
2. Description of the Related Art There is a moisture-permeable waterproof cloth in which a moisture-permeable waterproof membrane having a waterproof property but having a function of transmitting water vapor is attached to a cloth. Here, as the moisture permeable waterproof membrane, a porous stretched polytetrafluoroethylene membrane (hereinafter referred to as "e") disclosed in Japanese Patent Publication No. 51-18991 or Japanese Patent Application Laid-Open No. Sho 60-39014.
Abbreviated as “PTFE film”). This has moisture permeability due to the microporous structure of polytetrafluoroethylene which has been made porous by stretching, and exhibits waterproofness due to the fineness of pores and the water repellency of polytetrafluoroethylene.

【0003】しかし、ePTFE膜自体は十分な耐針性
を有していないため、衣服が有刺植物等に引っかかっ
て、ePTFE膜が刺に当たると、ePTFE膜に穴が
あいたり、破れてしまい、折角の防水機能が損なわれて
しまうという問題があった。また、テントなどのアウト
ドア製品においても、針状体が貫通すると同様に防水機
能が損なわれる。このため、茨などの有刺植物にひっか
かっても破れにくい耐針性を有する透湿防水布が検討さ
れている。
[0003] However, since the ePTFE membrane itself does not have sufficient needle resistance, if the clothes are caught by a stabbed plant or the like and the ePTFE membrane hits the sting, the ePTFE membrane is perforated or torn. There is a problem that the waterproof function of the corner is impaired. Also, in outdoor products such as tents, the waterproof function is similarly impaired when the needle-shaped body penetrates. For this reason, a moisture-permeable waterproof cloth having needle resistance that does not easily break even when it is caught on a thorny plant such as thorn is being studied.

【0004】耐針性を有する透湿防水性布としては、特
開平4−41778号公報に、図5に示す構造を有する
透湿防水布が開示されている。すなわち、透湿防水膜た
るePTFE膜10に、1.5デニール以下の単繊維か
ら構成される糸を用いた高密度布帛11を、接着により
積層した透湿防水布である。しかし、その耐針性は実用
において未だ不十分であった。
As a moisture-permeable waterproof cloth having needle resistance, Japanese Patent Application Laid-Open No. 4-41778 discloses a moisture-permeable waterproof cloth having a structure shown in FIG. That is, it is a moisture-permeable waterproof cloth in which a high-density cloth 11 using a yarn composed of a single fiber of 1.5 denier or less is laminated on an ePTFE membrane 10 as a moisture-permeable waterproof film by bonding. However, its needle resistance was still insufficient for practical use.

【0005】本発明は、このような事情にかんがみてな
されたものであり、その目的とするところは、十分な耐
針性を有する透湿防水布を提供することにある。
The present invention has been made in view of such circumstances, and an object of the present invention is to provide a moisture permeable waterproof cloth having sufficient needle resistance.

【0006】[0006]

【課題を解決するための手段】すなわち、第1の発明に
かかる透湿防水布は、1インチあたりの縦糸及び横糸の
打ち込み合計本数が、70デニールの糸で240本以上
に相当する繊維密度を有している高密度布帛を、透湿防
水膜の両側に積層してなることを特徴とする。
That is, the moisture-permeable waterproof cloth according to the first aspect of the present invention has a fiber density equivalent to 240 or more warp yarns and weft yarns per inch, which is 70 denier yarns. The high-density cloth is laminated on both sides of a moisture-permeable waterproof membrane.

【0007】第2発明にかかる透湿防水布は、1インチ
あたりの縦糸及び横糸の打ち込み合計本数が、70デニ
ールの糸で240本以上に相当する繊維密度を有してい
る高密度布帛を、透湿防水膜の少なくとも一側に複数積
層してなることを特徴とする。
[0007] The moisture-permeable waterproof cloth according to the second invention is a high-density cloth having a fiber density equivalent to 240 or more yarns of 70-denier yarn in a total number of warp yarns and weft yarns per inch. It is characterized in that a plurality of layers are laminated on at least one side of the moisture-permeable waterproof membrane.

【0008】第3発明にかかる透湿防水布は、1インチ
あたりの縦糸及び横糸の打ち込み合計本数が、70デニ
ールの糸で240本以上に相当する繊維密度を有してい
る高密度布帛と、透湿防水膜とからなる積層体が、該透
湿防水膜と該高密度布帛とが交互になるように、複数積
層されていることを特徴とする。
[0008] The moisture-permeable waterproof fabric according to the third invention is a high-density fabric having a fiber density equivalent to 240 or more warp yarns and weft yarns per inch of 70 denier yarns. A plurality of laminates composed of a moisture-permeable waterproof membrane are laminated so that the moisture-permeable waterproof membrane and the high-density fabric are alternately arranged.

【0009】上記第2発明又は第3発明にかかる透湿防
水布において、透湿防水膜が最外層となっている場合、
該透湿防水膜上に、保護用布帛を積層することが好まし
い。
In the moisture-permeable waterproof cloth according to the second or third invention, when the moisture-permeable waterproof membrane is the outermost layer,
It is preferable that a protective fabric be laminated on the moisture-permeable waterproof membrane.

【0010】[0010]

【発明の実施の形態】以下に、本発明にかかる透湿防水
布の実施の形態を、図面に基づいて説明する。
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of a moisture-permeable waterproof cloth according to the present invention will be described below with reference to the drawings.

【0011】はじめに、第1発明にかかる透湿防水布の
一実施形態を、図1に基いて説明する。
First, an embodiment of the moisture-permeable waterproof cloth according to the first invention will be described with reference to FIG.

【0012】この透湿防水布は、透湿防水膜1を挟むよ
うにして、高密度布帛2a、2bを積層したものであ
る。透湿防水膜の両側に高密度布帛が積層されているの
で、針状体が一側の高密度布帛を貫通したり、刺がひっ
かかったりして、透湿防水膜に針状体の先端が当たるこ
とがあっても、着衣者と透湿防水膜の間には、他側に積
層された高密度布帛が介在しているので、着衣者に刺や
昆虫の毒針が直接当たったり、針先のチクチクする感じ
を防止できる。また、アウトドア製品としても、本来の
機能を維持できる。
This moisture-permeable waterproof cloth is obtained by laminating high-density cloths 2a and 2b with the moisture-permeable waterproof membrane 1 interposed therebetween. Since the high-density fabric is laminated on both sides of the moisture-permeable waterproof membrane, the needle-like body penetrates the high-density fabric on one side or a sting catches, and the tip of the needle-like body is attached to the moisture-permeable waterproof membrane. Even if it hits, the high-density fabric laminated on the other side is interposed between the wearer and the moisture-permeable waterproof membrane. The tingling sensation at the tip can be prevented. Also, the original function can be maintained as an outdoor product.

【0013】本発明に用いられる透湿性防水膜とは、防
水性及び透湿性を兼ね備えたシートで、3kg/cm2
以上の防水性、2000g/m2・24h以上、好まし
くは3000g/m2・24h以上、より好ましくは5
000g/m2・24h以上、さらに好ましくは800
0g/m2・24h以上の透湿性を有するシートであれ
ば、公知の種々の材料を使用できる。なかでも、特公昭
51−18991号公報に開示されている多孔性の延伸
PTFE膜(ePTFE膜)が好ましく用いられる。
[0013] moisture and is permeable waterproof film to be used in the present invention, a sheet having both waterproof and breathable, 3 kg / cm 2
Water resistance of 2000 g / m 2 · 24 h or more, preferably 3000 g / m 2 · 24 h or more, more preferably 5 g / m 2 · 24 h or more
000 g / m 2 · 24 h or more, more preferably 800
As long as the sheet has a moisture permeability of 0 g / m 2 · 24 h or more, various known materials can be used. Above all, a porous expanded PTFE membrane (ePTFE membrane) disclosed in JP-B-51-18991 is preferably used.

【0014】ここでePTFE膜とは、PTFEのファ
インパウダーを成形助剤と混合することにより得られる
ペーストの成形体から、成形助剤を除去した後、高温高
速度で平面状に延伸することにより得られるもので、多
孔質構造を有している。すなわち、ePTFEは、微小
な結晶リボンで相互に連結されたPTFEの1次粒子の
凝集体であるノードと、これら一次粒子から引きだされ
た伸び切った結晶リボンの束であるフィブリルとからな
り、そして、フィブリルと該フィブリルを繋ぐノードと
で画される空間が空孔となっっている。
Here, the ePTFE membrane is formed by removing a molding aid from a molded product of a paste obtained by mixing a fine powder of PTFE with a molding aid, and then stretching it in a plane at high temperature and high speed. It is obtained and has a porous structure. That is, ePTFE is composed of nodes, which are aggregates of PTFE primary particles interconnected by fine crystal ribbons, and fibrils, which are bundles of crystal ribbons extended from these primary particles, The space defined by the fibrils and the nodes connecting the fibrils is a hole.

【0015】ePTFEの平均孔径は、延伸倍率により
調整され、所望の透湿性及び防水性を有するためには、
コールターエレクトロニクス社のコールターポロメータ
ーで測定した値で、0.05〜3μmが好ましく、特に
0.1〜0.5μm程度が好ましい。また、空孔率も延
伸倍率により調整されるが、所望の透湿性及び防水性を
有するためには、60〜95%程度が好ましく、特に7
0〜85%が好ましい。
The average pore diameter of ePTFE is adjusted by the draw ratio, and in order to have desired moisture permeability and waterproofness,
It is preferably from 0.05 to 3 μm, particularly preferably from about 0.1 to 0.5 μm, as measured by a Coulter Porometer manufactured by Coulter Electronics Co., Ltd. The porosity is also adjusted by the draw ratio, but is preferably about 60 to 95%, particularly preferably 7 to 95%, in order to have desired moisture permeability and waterproofness.
0-85% is preferred.

【0016】上記構成を有するePTFE膜をそのまま
透湿防水膜として用いてもよいし、ePTFE膜に透湿
性樹脂を含浸又はコーティングして多孔質構造が消失し
た膜を用いてもよいし、多孔質構造を残したままで、e
PTFE膜の表面に撥水性又は撥油性を有するポリマー
をコーティングして用いてもよい。
The ePTFE membrane having the above structure may be used as a moisture permeable waterproof membrane as it is, or a membrane in which the porous structure has disappeared by impregnating or coating the ePTFE membrane with a moisture permeable resin may be used. While retaining the structure, e
The surface of the PTFE film may be coated with a water-repellent or oil-repellent polymer.

【0017】ここで、透湿性樹脂としては、親水性のポ
リウレタン系樹脂が例示される。ePTFE膜の多孔質
構造は消失しても、含浸又はコーティングされる透湿性
樹脂自体が透湿性を有しているので、ePTFE膜の透
湿防水性を保持するとともに、体脂肪や洗剤に含まれる
界面活性剤からの汚染に対するePTFE膜の耐性(耐
汚染性)を向上させることができる。
Here, as the moisture permeable resin, a hydrophilic polyurethane resin is exemplified. Even if the porous structure of the ePTFE membrane disappears, the impregnated or coated moisture-permeable resin itself has moisture permeability, so that the ePTFE membrane retains moisture permeability and waterproofness and is contained in body fat and detergent. The resistance (stain resistance) of the ePTFE membrane to the contamination from the surfactant can be improved.

【0018】また、撥水性又は撥油性を有するポリマー
でコーティングした膜の場合、多孔質構造により、透湿
性を有するとともに、撥水性又は撥油性のコーティング
ポリマーにより耐汚染性を向上させることができる。こ
こで、撥水性又は撥油性を有するポリマーとしては、W
O/94/22928号公報に開示されているフッ素化
されたアクリレート又はメタクリレートをマイクロエマ
ルジョン重合して得られるポリマーや、PCT/US9
4/10074号に記載されているフッ素化されたアク
リレート又はメタクリレートと、テトラフルオロエチレ
ン又はテトラフルオロエチレン/ヘキサフルオロプロピ
レン混合物とから得られるコポリマーの水性エマルジョ
ン(平均粒径0.001〜0.1ミクロン)などが挙げ
られる。この水性エマルジョンは、コポリマー粒子が小
さいために、含浸法、スプレー法等により容易に上記e
PTFE膜の空孔内に侵入する。そして、上記水性エマ
ルジョンの含浸又はスプレー後、加熱すると、水性エマ
ルジョンに含まれていた水及び界面活性剤が除去される
とともに、コポリマーが溶融してePTFE膜の空孔内
に撥水性含フッ素高分子が付着する。
In the case of a film coated with a water-repellent or oil-repellent polymer, the porous structure has moisture permeability and the water-repellent or oil-repellent coating polymer can improve the stain resistance. Here, the polymer having water repellency or oil repellency is W
O / 94/22928, a polymer obtained by microemulsion polymerization of a fluorinated acrylate or methacrylate, PCT / US9
Aqueous emulsions of copolymers obtained from fluorinated acrylates or methacrylates described in U.S. Pat. No. 4,107,074 and tetrafluoroethylene or a mixture of tetrafluoroethylene / hexafluoropropylene (mean particle size 0.001 to 0.1 micron ). Since this aqueous emulsion has small copolymer particles, the above-mentioned e is easily prepared by impregnation, spraying, or the like.
It penetrates into the holes of the PTFE film. Then, when heated after impregnation or spraying of the aqueous emulsion, the water and surfactant contained in the aqueous emulsion are removed, and the copolymer is melted and the water-repellent fluoropolymer is formed in the pores of the ePTFE membrane. Adheres.

【0019】透湿防水膜の厚みは、一般に10〜150
μmであり、好ましくは20〜120μm、より好まし
くは35〜100μmである。
The thickness of the moisture-permeable waterproof membrane is generally from 10 to 150
μm, preferably 20 to 120 μm, more preferably 35 to 100 μm.

【0020】本発明に用いられる高密度布帛とは、製
織、編成等により布状としたもので、具体的には織物又
は編み物である。織物の場合、平織り、綾織、朱子織り
という原組織のほか、変化組織や重ね織り組織の織物で
あってもよい。編み物の場合、縦編み、横編み、丸編み
のいずれでもよい。
The high-density cloth used in the present invention is a cloth made by weaving, knitting or the like, and is specifically a woven or knitted fabric. In the case of a woven fabric, the woven fabric may be a plain weave, a twill weave, or a satin weave, as well as a change weave or a weave. In the case of knitting, any of vertical knitting, horizontal knitting, and circular knitting may be used.

【0021】高密度布帛に用いられる繊維の化学的種類
は、適用される製品の素材として要求される特性(引張
強さ等の機械的特性;防しわ性等の形態保持性;洗濯堅
牢度等の染色堅牢度など)に応じて適宜選択される。
The chemical type of the fiber used in the high-density fabric is determined by the properties required for the material of the product to be applied (mechanical properties such as tensile strength; form retention such as wrinkle resistance; washing fastness etc.). Is selected as appropriate depending on the color fastness of the dye.

【0022】高密度布帛を構成する糸は、マルチフィラ
メント糸又は紡績糸が好ましい。糸を構成する繊維は、
繊度が0.01〜1.5デニール程度、好ましくは0.
05〜1.0デニール程度の単繊維である。0.01デ
ニール未満では、糸の強度が弱くなって布帛の実用耐久
性が劣り、1.5デニールを上回ると、糸状体にしたと
きの平滑性、さらには布帛としての平滑性が低下して耐
針性にばらつきが生じるからである。
The yarn constituting the high-density fabric is preferably a multifilament yarn or a spun yarn. The fibers that make up the yarn are
Fineness is about 0.01 to 1.5 denier, preferably 0.1 to 1.5 denier.
It is a single fiber of about 05 to 1.0 denier. If it is less than 0.01 denier, the strength of the yarn becomes weak and the practical durability of the fabric is inferior.If it exceeds 1.5 denier, the smoothness when formed into a thread-like body, and further, the smoothness as a fabric is reduced. This is because the needle resistance varies.

【0023】布帛に用いる糸の太さは、好ましくは30
〜420デニール、より好ましくは40〜140デニー
ル、さらに好ましくは50〜80デニールである。繊維
密度が同程度の布帛であっても、糸が細すぎると布帛の
引き裂き強度が低下し、また布帛の厚みが薄くなるため
耐久性が劣るからである。一方、糸が太すぎると、刺等
が引っかかりやすいからである。
The thickness of the yarn used for the fabric is preferably 30
It is from 420 denier, more preferably from 40 to 140 denier, even more preferably from 50 to 80 denier. This is because, even if the fabric has the same fiber density, if the yarn is too thin, the tear strength of the fabric is reduced, and the thickness of the fabric is reduced, resulting in poor durability. On the other hand, if the thread is too thick, a sting or the like is likely to be caught.

【0024】高密度布帛の繊維密度、すなわち布帛1イ
ンチあたりの縦糸及び横糸の本数は、70デニールの糸
で打ち込み合計本数が240本以上となる程度であり、
さらに20本程度多い260本程度以上であることが好
ましい。本発明に用いる高密度布帛に用いられる糸の太
さは、上述のように70デニールに限定しないので、糸
の太さに応じて打ち込み本数を適宜選択することによ
り、同程度の繊維密度とすればよい。本発明で一般に用
いる30〜420デニールの糸と、所定の糸密度を得る
ための打ち込み本数の下限との関係を表1に示す。参考
のために、通常の布帛の場合の各繊度の糸の打ち込み本
数も、併せて表1に示す。
The fiber density of the high-density fabric, that is, the number of warp yarns and weft yarns per inch of the fabric is such that the total number of yarns driven by 70-denier yarn is 240 or more.
Further, the number is preferably about 260 or more, which is about 20 more. Since the thickness of the yarn used for the high-density fabric used in the present invention is not limited to 70 denier as described above, by appropriately selecting the number of fibers to be driven according to the thickness of the yarn, it is possible to achieve the same fiber density. I just need. Table 1 shows the relationship between the 30 to 420 denier yarn generally used in the present invention and the lower limit of the number of yarns for obtaining a predetermined yarn density. For reference, Table 1 also shows the number of yarns of each fineness in the case of a normal fabric.

【0025】[0025]

【表1】 [Table 1]

【0026】高密度布帛2a及び高密度布帛2bは、上
記範囲を満たすものであればよく、両者の繊維の種類、
繊度、繊維密度などは同じであっても、異なっていても
よい。繊維密度が異なる場合、繊維密度が高い方の布帛
を、使用したときの外側すなわち針状体が直接当接する
側に使用することが好ましい。一般に、繊維密度が高い
程、耐針性に優れているといえるからである。
The high-density cloth 2a and the high-density cloth 2b only need to satisfy the above range.
The fineness and fiber density may be the same or different. When the fiber densities are different, it is preferable to use the fabric with the higher fiber density on the outer side when used, that is, on the side where the needle-shaped body directly contacts. In general, the higher the fiber density, the better the needle resistance.

【0027】各高密度布帛2a、2bの厚みとしては、
一般に0.05〜0.8mm、好ましくは0.2〜0.
4mmである。高密度布帛2aと高密度布帛2bとは、
同じ厚みであっても、異なる厚みであってもよい。厚み
が異なる場合、ぶ厚い方の布帛を、使用時の外側となる
ように使用することが好ましい。一般に、ぶ厚い程、耐
針性に優れているといえるからである。
The thickness of each high-density cloth 2a, 2b
Generally 0.05-0.8 mm, preferably 0.2-0.
4 mm. The high-density cloth 2a and the high-density cloth 2b
The thickness may be the same or different. When the thickness is different, it is preferable to use the thicker fabric so as to be outside when used. In general, it can be said that the thicker the film, the better the needle resistance.

【0028】高密度布帛と透湿防水膜との積層方法は、
接着剤による接着法、接着剤を使用しない圧着や融着な
どによる固着方法などがあり、高密度布帛及び透湿防水
膜の種類、親和性などにより適宜選択される。接着法と
しては、例えば、高密度布帛又は透湿防水膜の少なくと
もいずれか一方に、ウレタン系等の接着剤を、グラビア
ロール等を用いて点状、線状、格子状等に、接着面積の
20〜80%程度塗布した後、圧着により積層する方
法;多孔質構造を有する透湿防水性膜にポリウレタン樹
脂をコーティングした後、コーティング層を高密度布帛
と熱融着させて積層する方法;などが挙げられる。
The method of laminating the high-density cloth and the moisture-permeable waterproof membrane is as follows.
There are a bonding method using an adhesive, a fixing method using pressure bonding or fusion without using an adhesive, and the like, which is appropriately selected depending on the type and affinity of the high-density cloth and the moisture-permeable waterproof membrane. As the bonding method, for example, at least one of a high-density cloth and a moisture-permeable waterproof membrane, an urethane-based adhesive, using a gravure roll or the like, in the form of dots, lines, grids, etc. A method of applying by about 20 to 80% and then laminating by pressure bonding; a method of coating a polyurethane resin on a moisture-permeable waterproof membrane having a porous structure and then laminating the coating layer by heat fusion with a high-density cloth; Is mentioned.

【0029】尚、図1は、高密度布帛を1枚づつ積層し
た場合を示しているが、第1発明にかかる透湿防水布は
これに限定されず、少なくともいずれか一方に、複数枚
の高密度布帛を積層してもよい。
FIG. 1 shows a case in which high-density fabrics are laminated one by one. However, the moisture-permeable waterproof fabric according to the first invention is not limited to this, and at least one of the moisture-permeable waterproof fabrics has a plurality of fabrics. High density fabrics may be laminated.

【0030】次に、第2発明にかかる透湿防水布の一実
施形態を、図2に基いて説明する。
Next, an embodiment of the moisture-permeable waterproof cloth according to the second invention will be described with reference to FIG.

【0031】この透湿防水布は、透湿防水膜1の一側
に、第1高密度布帛3aと第2高密度布帛3bとを順次
積層したものである。
This moisture-permeable waterproof cloth is obtained by sequentially laminating a first high-density cloth 3a and a second high-density cloth 3b on one side of the moisture-permeable waterproof membrane 1.

【0032】透湿防水膜は、第1発明で用いた透湿防水
膜を用いることができる。
As the moisture permeable waterproof membrane, the moisture permeable waterproof membrane used in the first invention can be used.

【0033】また、高密度布帛3a、3bは、いずれも
第1発明で用いた高密度布帛を用いることができる。第
1高密度布帛3aと第2高密度布帛3bとは、布帛の種
類(織物又は編み物であるか、織り方又は編み方な
ど)、繊維の種類、繊維密度などが同じであっても、異
なっていてもよい。繊維密度が異なる場合には、いずれ
の繊維密度が大きくてもよい。また、布帛の種類が異な
る組み合わせの場合、第1高密度布帛3a又は第2高密
度布帛3bのいずれが織物又は編物であるかは不問であ
る。
As the high-density cloths 3a and 3b, the high-density cloth used in the first invention can be used. The first high-density cloth 3a and the second high-density cloth 3b are different even if the type of fabric (woven or knitted, weaving or knitting, etc.), fiber type, fiber density, etc. are the same. May be. When the fiber densities are different, any fiber density may be large. In addition, in the case of a combination of different types of fabric, it does not matter which of the first high-density fabric 3a and the second high-density fabric 3b is a woven or knitted fabric.

【0034】第1高密度布帛3aと第2高密度布帛3b
との積層方法は、前記の布帛と透湿防水膜との積層方法
を採用することができ、これらのうち、布帛の種類に応
じて適宜選択することができる。
The first high-density cloth 3a and the second high-density cloth 3b
Can be adopted as the lamination method of the above-mentioned cloth and the moisture-permeable waterproof membrane, and among them, it can be appropriately selected according to the type of the cloth.

【0035】かかる構成を有する透湿防水布は、高密度
布帛側が使用時の外側すなわち針状体が当接する側(以
下、単に「外側」という)となり、ePTFE膜側が内
側例えば衣服の場合は身体側(以下、単に「内側」とい
う)となる。ePTFE膜の外側には2枚の高密度布帛
が積層されていることから、1枚の布帛を積層する場合
と比べて、刺等の針状体がePTFE膜に到達しにくく
なる。特に、繊維密度が異なる布帛または織り方等の異
なる布帛を2枚重ねて積層した透湿防水布では、一方の
布帛が他方の布帛の織り目間隙又は編み目間隙等の空間
を閉塞するようになるため、1枚の布帛を積層しただけ
の従来の透湿防水布で総厚みが同じものよりも耐針性に
優れている。
In the moisture-permeable waterproof cloth having such a structure, the high-density cloth side is the outer side in use, that is, the side in contact with the needle-like body (hereinafter, simply referred to as “outer side”), and the ePTFE membrane side is the inner side. Side (hereinafter simply referred to as “inside”). Since two high-density cloths are laminated on the outside of the ePTFE membrane, needle-like bodies such as pricks do not easily reach the ePTFE membrane as compared with a case where one cloth is laminated. In particular, in a moisture-permeable waterproof cloth obtained by laminating and laminating two different fabrics having different fiber densities or different weaving methods, one of the fabrics blocks a space such as a weave gap or a weave gap of the other fabric. 1. A conventional moisture-permeable waterproof cloth in which only one piece of fabric is laminated is superior in needle resistance to that of the same total thickness.

【0036】尚、図2は高密度布帛を2枚積層した場合
を示しているが、第2発明はこれに限らず、高密度布帛
が3枚以上積層したものであってもよい。衣服素材とし
て問題がなければ、高密度布帛の積層枚数が増加するほ
ど、耐針性が増加するからである。
Although FIG. 2 shows a case where two high-density fabrics are laminated, the second invention is not limited to this, and three or more high-density fabrics may be laminated. If there is no problem as a garment material, the needle resistance increases as the number of laminated high-density fabrics increases.

【0037】次に、第3発明にかかる透湿防水布の一実
施形態を、図3に基いて説明する。
Next, an embodiment of the moisture-permeable waterproof cloth according to the third invention will be described with reference to FIG.

【0038】この透湿防水布は、透湿防水膜1と高密度
布帛4とからなる積層体5と、透湿防水膜1′と高密度
布帛4′とからなる積層体5′とを積層したものであ
る。かかる構成を有する透湿防水布では、高密度布帛側
の面を外側、ePTFE膜側を内側として使用する。
This moisture-permeable waterproof cloth is formed by laminating a laminate 5 composed of the moisture-permeable waterproof membrane 1 and the high-density cloth 4 and a laminate 5 'composed of the moisture-permeable waterproof membrane 1' and the high-density cloth 4 '. It was done. In the moisture-permeable waterproof cloth having such a configuration, the surface on the high-density fabric side is used as the outside, and the ePTFE membrane side is used as the inside.

【0039】透湿防水膜の種類、高密度布帛の種類、高
密度布帛と透湿防水膜との積層方法は、いずれも第1発
明と同様である。透湿防水膜1と透湿防水膜1′とは同
じものであってもよいし、異なっているものであっても
よい。また、高密度布帛4と高密度布帛4′とは同じも
のであってもよいし、異なっているものでもよい。従っ
て、積層体5と積層体5′とは、同じであっても異なっ
ていてもよい。
The type of the moisture-permeable waterproof membrane, the type of the high-density fabric, and the method of laminating the high-density fabric and the moisture-permeable waterproof membrane are all the same as those of the first invention. The moisture-permeable waterproof membrane 1 and the moisture-permeable waterproof membrane 1 'may be the same or different. Further, the high-density cloth 4 and the high-density cloth 4 'may be the same or different. Therefore, the laminate 5 and the laminate 5 'may be the same or different.

【0040】第3発明の構成では、複数のePTFE膜
を有しているので、外側のePTFE膜が針により損傷
して透湿防水機能を損なっても、内側のePTFE膜が
透湿防水機能を発揮できる。
In the structure of the third aspect of the present invention, since a plurality of ePTFE membranes are provided, even if the outer ePTFE membrane is damaged by a needle and impairs the moisture-permeable and waterproof function, the inner ePTFE membrane has the moisture-permeable and waterproof function. Can demonstrate.

【0041】尚、図3では、積層体を2組重ねた場合で
あったが、第3発明はこれに限らず、積層体を3つ以上
重ねたものであってもよい。
Although FIG. 3 shows a case where two sets of stacked bodies are stacked, the third invention is not limited to this, and three or more stacked bodies may be stacked.

【0042】第1発明、第2発明、第3発明いずれの構
成の透湿防水布であっても、従来の透湿防水膜の一側に
高密度布帛を1枚だけ積層した透湿防水布と比べて、耐
針性が優れている。すなわち、従来の構成で、単に高密
度布帛の厚みや繊維密度を調整するよりも、本発明の構
造をとることの方が耐針性の向上は著しい。
The moisture-permeable waterproof cloth of any of the first, second and third inventions has a structure in which only one high-density cloth is laminated on one side of the conventional moisture-permeable waterproof membrane. Compared with, the needle resistance is excellent. That is, in the conventional configuration, the improvement of the needle resistance is more remarkable by adopting the structure of the present invention than simply adjusting the thickness and the fiber density of the high-density cloth.

【0043】さらに本発明の透湿防水布は、透湿防水膜
が最外面を形成している場合には、最外面の透湿防水膜
上に、さらに保護用布帛を積層してもよい。図4は、図
2に示した第2発明の一実施態様(透湿防水膜1の一側
に高密度布帛3a,3bを順次積層したもの)である透
湿防水布7に、保護用布帛6を積層した透湿防水布を示
している。保護用布帛6を積層した透湿防水布では、保
護用布帛6が内側となるように使用する。従って、衣服
素材の場合、身体又は身体側の着衣と透湿防水膜1との
間には保護用布帛6が介在することになるので、針状体
ほど鋭利でない突出物(内側からの刺激)などから透湿
防水膜を保護する働きを有するとともに、保護用布帛6
として身体に快適な素材を選択することにより着心地を
快適にした衣服素材を得ることができる。
Further, in the moisture permeable waterproof fabric of the present invention, when the moisture permeable waterproof film forms the outermost surface, a protective cloth may be further laminated on the outermost moisture permeable waterproof film. FIG. 4 shows a protective fabric on a moisture-permeable waterproof cloth 7 which is an embodiment of the second invention shown in FIG. 2 (a high-density cloth 3a, 3b is sequentially laminated on one side of the moisture-permeable waterproof membrane 1). 6 shows a moisture-permeable waterproof cloth in which No. 6 is laminated. In the moisture-permeable waterproof cloth on which the protective cloth 6 is laminated, the protective cloth 6 is used such that the protective cloth 6 is located inside. Therefore, in the case of the clothing material, since the protective cloth 6 is interposed between the clothing on the body or the body side and the moisture-permeable waterproof membrane 1, the projection is not as sharp as the needle-shaped body (stimulation from the inside). And has the function of protecting the moisture-permeable waterproof membrane from
By selecting a material that is comfortable for the body, it is possible to obtain a garment material that is comfortable to wear.

【0044】保護用布帛に用いる布帛の種類は限定せ
ず、織物、編物、不織布のいずれを用いることもできる
が、丸編みニット(例えば天竺編みニット)、縦編みニ
ット(例えばトリコットニット、トリコットハーフニッ
ト)等の編み物が好ましく用いられる。編み物は、透湿
防水布を用いて衣料製品とする際の縫製加工において、
シームテープ(目止めテープ)を用いる防水処理を施し
易いからである。
The type of the cloth used for the protective cloth is not limited, and any of a woven cloth, a knitted cloth and a non-woven cloth can be used, and a circular knit knit (for example, a sheet knit), a vertical knit (for example, a tricot knit, a tricot half) Knits) are preferably used. Knitting is a sewing process when making a clothing product using a moisture-permeable waterproof cloth.
This is because a waterproof treatment using a seam tape (sealing tape) can be easily performed.

【0045】また、保護用布帛の繊維密度は、特に限定
はしない。従って、本発明で用いる高密度布帛にまで達
しない繊維密度の布帛を用いてもよいし、高密度布帛に
該当する繊維密度を有する布帛を用いてもよい。
The fiber density of the protective cloth is not particularly limited. Therefore, a cloth having a fiber density that does not reach the high-density cloth used in the present invention may be used, or a cloth having a fiber density corresponding to the high-density cloth may be used.

【0046】[0046]

【実施例】 実施例1:透湿防水膜として、気孔率80%、最大孔径
0.2μmで、厚み40μmのePTFE膜を用いた。
ePTFE膜の一側に、0.38デニールのポリエステ
ル製単繊維を246本束ねて用いて75デニールの1本
の糸(以下、「0.38デニールの単繊維、75d/2
46フィラメントの糸」と表す)とし、この糸を用い
て、1インチあたり縦糸250本、横糸140本の織り
密度(以下、「250×140本/インチ」と表す)の
1/3ツイル布(縦糸3本毎に横糸を交叉させて織った
綾織布)を積層した。他側に、0.35デニール単繊
維、50d/144フィラメントの糸を用いた174×
94本/インチの平織り布を積層して、図1に示す構成
(タイプI)の透湿防水布を作製した。作成した透湿防
水布の厚みは、0.57mmであった。尚、ePTFE
膜と高密度布帛との積層は、グラビアロールを用いてウ
レタン系接着剤塗を布した後、圧着することにより行な
った。
EXAMPLES Example 1 An ePTFE membrane having a porosity of 80%, a maximum pore diameter of 0.2 μm, and a thickness of 40 μm was used as a moisture-permeable waterproof membrane.
On one side of the ePTFE membrane, 246 0.38 denier polyester single fibers are bundled and used to form a single thread of 75 denier (hereinafter referred to as “0.38 denier single fiber, 75d / 2”).
Using this yarn, a 1/3 twill cloth (hereinafter referred to as "250 × 140 yarns / inch") having a weaving density of 250 warp yarns and 140 weft yarns per inch is used. A twill woven fabric in which weft yarns are crossed every three warp yarns). On the other side, 174 × using 0.35 denier monofilament, 50d / 144 filament yarn
94 / inch plain woven fabrics were laminated to produce a moisture permeable waterproof fabric having the configuration (type I) shown in FIG. The thickness of the created moisture-permeable waterproof cloth was 0.57 mm. In addition, ePTFE
The lamination of the film and the high-density fabric was performed by applying a urethane-based adhesive coating using a gravure roll and then pressing the coating.

【0047】実施例2:実施例1で用いたePTFE膜
の一側に、0.35デニールの単繊維、50d/144
フィラメントの糸を用いた174×94本/インチの平
織り布を積層し、さらに0.38デニールの単繊維、7
5d/246フィラメントの糸を用いた250×140
本/インチの1/3ツイル布を積層して、図2に示す構
成(タイプII)の透湿防水布を作製した。透湿防水布の
厚みは0.57mmであった。ePTFE膜と布帛との
積層は実施例1と同様にして行い、ツイル布と平織り布
との積層は、ウレタン系接着剤で接着することにより行
った。
Example 2: One side of the ePTFE membrane used in Example 1, 0.35 denier single fiber, 50d / 144
174 x 94 yarns / inch plain woven fabric using filament yarn is laminated, and 0.38 denier single fiber, 7
250 × 140 using 5d / 246 filament yarn
2 / inch 1/3 twill cloths were laminated to produce a moisture-permeable waterproof cloth having the configuration (type II) shown in FIG. The thickness of the moisture-permeable waterproof cloth was 0.57 mm. Lamination of the ePTFE membrane and the fabric was performed in the same manner as in Example 1, and lamination of the twill cloth and the plain woven cloth was performed by bonding with a urethane-based adhesive.

【0048】実施例3:実施例1で用いたePTFE膜
の一側に、0.38デニールの単繊維、75d/246
フィラメントの糸を用いた250×140本/インチの
1/3ツイル布を2枚重ねて積層し、図2に示す構成
(タイプII)の透湿防水布を作製した。ePTFE膜と
ツイル布との積層、ツイル布同士の積層は、いずれも実
施例2と同様に行なった。
Example 3 On one side of the ePTFE membrane used in Example 1, 0.38 denier single fiber, 75d / 246
Two 250 × 140 / inch 1/3 twill cloths each using a filament yarn were laminated and laminated to produce a moisture-permeable waterproof cloth having a configuration (type II) shown in FIG. Lamination of the ePTFE membrane and the twill cloth and lamination of the twill cloths were performed in the same manner as in Example 2.

【0049】実施例4:実施例1で用いたePTFE膜
の一側に、0.38デニールの単繊維、75d/246
フィラメントの糸を用いた250×140本/インチの
1/3ツイル布を積層した第1積層体、及び実施例1で
用いたePTFE膜の一側に0.35デニールの単繊
維、50d/144フィラメントの糸を用いた174×
94本/インチの平織り布を積層した第2積層体を作成
し、ePTFE膜と布帛とを接着することにより、前記
第1積層体と第2積層体とを積層して、図3に示す構成
(タイプIII)の透湿防水布を作成した。次いで、最外
面を形成しているePTFE膜上に、保護用布帛とし
て、3デニールの単繊維、22d/7フィラメントの糸
を用いた36×50本/インチのトリコットハーフニッ
トを積層した。なお、ePTFE膜と保護用布帛との積
層方法は、ePTFE膜と高密度布帛との積層方法を採
用した。
Example 4: On one side of the ePTFE membrane used in Example 1, 0.38 denier single fiber, 75d / 246
A first laminate obtained by laminating 250 × 140 filaments / inch 1/3 twill cloth using filament yarn, and 0.35 denier single fiber on one side of the ePTFE membrane used in Example 1, 50d / 144 174 × using filament yarn
A second laminate in which 94 / inch plain woven fabrics are laminated is prepared, and the first laminate and the second laminate are laminated by bonding an ePTFE membrane and a fabric, and the configuration shown in FIG. (Type III) moisture permeable waterproof cloth was prepared. Next, a tricot half knit of 36 × 50 / inch using 3 denier single fiber and 22d / 7 filament yarn was laminated as a protective fabric on the ePTFE membrane forming the outermost surface. In addition, the lamination method of the ePTFE membrane and the high-density cloth was adopted as the lamination method of the ePTFE membrane and the protective cloth.

【0050】実施例5:透湿防水膜として、ePTFE
膜の一側面に、親水性ポリウレタン樹脂ハイポールFH
P3000(HAMPSHIRE CHEMICAL
CORPORATION社の商品名)をコーティングし
たものを用いた。透湿防水膜のコーティングしていない
側の面に、0.38デニールの単繊維、75d/246
フィラメントの糸を用いた250×140本/インチの
1/3ツイル布を積層した第1積層体、及び透湿防水膜
のコーティングしていない側の面に、50デニール/1
44フィラメントの糸を用いた174×94本/インチ
の平織り布を積層した第2積層体を作成した。第1積層
体の透湿防水膜と第2積層体の平織り布とを接着して、
タイプIIIの透湿防水布を作成した。さらに、最外面を
形成している第2積層体のePTFE膜のコーティング
面に、実施例4で用いた保護用布帛を積層した。
Example 5: ePTFE as a moisture-permeable waterproof membrane
On one side of the membrane, hydrophilic polyurethane resin Hypol FH
P3000 (HAMPSHIRE CHEMICAL
CORPORATION (trade name of CORPORATION) was used. On the uncoated side of the moisture-permeable waterproof membrane, a single fiber of 0.38 denier, 75d / 246
50 denier / 1 on the uncoated side of the first laminate in which a 250 × 140 / inch 1/3 twill cloth using filament yarn is laminated, and on the uncoated side of the moisture-permeable waterproof membrane.
A second laminate was prepared by laminating 174 × 94 plain woven fabrics using 44 filament yarns. Bonding the moisture-permeable waterproof membrane of the first laminate and the plain woven fabric of the second laminate,
A type III moisture permeable waterproof cloth was created. Further, the protective fabric used in Example 4 was laminated on the coating surface of the ePTFE membrane of the second laminate forming the outermost surface.

【0051】比較例1:実施例1で用いたePTFEの
一側に、0.38デニールの単繊維、75d/246フ
ィラメントの糸を用いて、250×140本/インチの
1/3ツイル布を積層して、図5に示す構成(タイプI
V)の透湿防水布を作成し、さらにePTFE膜の他側
に実施例4で用いた保護用布帛を積層した。保護用布帛
を含めた透湿防水布の厚みは0.51mmであった。
Comparative Example 1: One side of ePTFE used in Example 1 was a 250 × 140 / inch 1/3 twill cloth using 0.38 denier single fiber and 75d / 246 filament yarn. Laminated, the configuration shown in FIG. 5 (Type I
V) A moisture-permeable waterproof cloth was prepared, and the protective cloth used in Example 4 was laminated on the other side of the ePTFE membrane. The thickness of the moisture-permeable waterproof cloth including the protective cloth was 0.51 mm.

【0052】比較例2:実施例1で用いたePTFEの
一側に、0.38デニールの単繊維、75d/246フ
ィラメントの糸を用いた260×150本/インチの1
/3ツイル布を積層して、図5に示す構成(タイプIV)
の透湿防水布を作成し、さらにePTFE膜の他側に実
施例4で用いた保護用布帛を積層した。保護用布帛を含
めた透湿防水布の厚みは0.52mmであった。
Comparative Example 2: On one side of ePTFE used in Example 1, 0.38 denier single fiber and 260 × 150 yarns / inch using 75d / 246 filament yarn were used.
/ 3 twill cloths are laminated, and the configuration shown in Fig. 5 (Type IV)
And a protective cloth used in Example 4 was laminated on the other side of the ePTFE membrane. The thickness of the moisture-permeable waterproof cloth including the protective cloth was 0.52 mm.

【0053】比較例3:ePTFEの一側に、0.38
デニールの単繊維、150d/492フィラメントの糸
を用いた130×80本/インチの1/3ツイル布を積
層して、図5に示す構成(タイプIV)の透湿防水布を作
成し、さらにePTFE膜の他側に実施例4で用いた保
護用布帛を積層した。保護用布帛を含めた透湿防水布の
厚みは0.8mmであった。
Comparative Example 3: 0.38 on one side of ePTFE
A 130 × 80 yarn / inch 1/3 twill cloth using denier monofilament and 150d / 492 filament yarn is laminated to form a moisture-permeable waterproof cloth having a configuration (type IV) shown in FIG. The protective fabric used in Example 4 was laminated on the other side of the ePTFE membrane. The thickness of the moisture-permeable waterproof cloth including the protective cloth was 0.8 mm.

【0054】参考例:0.6デニールの単繊維、100
d/160フィラメント、180×77本/インチの平
織り布表面に、透湿性樹脂である親水性ポリウレタン樹
脂をコーティングして、非多孔質で透湿性を有する樹脂
層を形成した。
Reference Example: 0.6 denier single fiber, 100
A non-porous, moisture-permeable resin layer was formed by coating a hydrophilic polyurethane resin, which is a moisture-permeable resin, on the surface of a plain woven fabric of d / 160 filaments, 180 × 77 filaments / inch.

【0055】〔評価〕 耐水圧 JIS L−1092(繊維製品の防水性試験方法)に
基づいて耐水圧を測定した。すなわち、耐水度試験装置
に上記で作成した透湿防水布を取付け、透湿防水布の外
側となる側から、3.0kgf/cm2の水圧を加えた
ときの漏水を調べた。
[Evaluation] Water pressure The water pressure was measured in accordance with JIS L-1092 (test method for waterproofness of textiles). That is, the moisture permeable waterproof cloth prepared above was attached to a water resistance test apparatus, and water leakage when a water pressure of 3.0 kgf / cm 2 was applied from the outer side of the moisture permeable waterproof cloth was examined.

【0056】ピンホール 20本の針を立設した試験台の針の上方に、上記で作製
した透湿防水布を、高密度布帛側と針先とが対向するよ
うにセットした。かかる状態で、透湿防水布に1.5k
gの荷重を30秒間かけた。その後、透湿防水布を試験
台から取りはずし、透湿防水布の針が当っていた側に
0.2kg/cm2の水圧をかけ、漏水の有無を調べ
た。漏水した場合には、漏水の原因となったピンホール
数を調べた。
Pinhole The moisture permeable waterproof cloth prepared above was set above the needles of a test stand having 20 needles standing so that the high-density cloth side and the needle tip faced each other. In this state, 1.5k
g of load was applied for 30 seconds. Thereafter, the moisture-permeable waterproof cloth was removed from the test stand, and a pressure of 0.2 kg / cm 2 was applied to the side of the moisture-permeable waterproof cloth on which the needle was in contact, to check for water leakage. When water leaked, the number of pinholes that caused the water leak was examined.

【0057】次に、荷重を3kgに上げ、水圧を0.2
kg/cm2として同様の実験を行ない、漏水の有無、
およびピンホール数を調べた。ピンホールが生じていた
場合には、針が当っていた側に3.0kgの荷重をかけ
て針を押し当てたときに、内側(針が押し当てられてい
ない側)での針を感じる度合いを、○(ほとんど針先を
感じない)、△(針先は肉眼では認められなかったが、
チクチクする感じ)、×(肉眼でも針先が貫通している
ことが認められる)の3段階で評価した。
Next, the load was increased to 3 kg, and the water pressure was increased to 0.2 kg.
kg / cm 2 , the same experiment was carried out,
And the number of pinholes were examined. If a pinhole has occurred, the degree to which the needle is felt inside (the side where the needle is not pressed) when the needle is pressed against the side where the needle has hit with a load of 3.0 kg. , ○ (almost no needle point is felt), △ (needle point was not recognized with the naked eye,
Evaluation was made on a three-point scale, i.e., a tingling sensation) and x (it is recognized that the needle tip penetrates with the naked eye).

【0058】耐針荷重 JIS L−1096のB法に準拠する方法で測定し
た。すなわち、定速伸長破裂試験機に、しわ及びたるみ
が生じないように均一な張力を加えて、透湿防水布の試
験片をクランプに取り付けた。試験片は、いずれも外側
となる高密度布帛側が上面となるように、取り付けた。
押棒の先端に針を取付け、1分間あたり10cmの加圧
速度で押し棒を押し当て、針が試験片を貫通するときの
荷重を測定した。
Needle load was measured by a method based on the method B of JIS L-1096. That is, uniform tension was applied to the constant-speed elongation burst tester so as not to cause wrinkling and sagging, and a test piece of a moisture-permeable waterproof cloth was attached to the clamp. The test pieces were attached such that the high-density fabric side, which is the outside, was the top side.
A needle was attached to the tip of the push rod, and the push rod was pressed at a pressure rate of 10 cm per minute, and the load when the needle penetrated the test piece was measured.

【0059】評価結果を、透湿防水布の要件とともに表
2に示す。
The evaluation results are shown in Table 2 together with the requirements for the moisture-permeable waterproof cloth.

【0060】[0060]

【表2】 [Table 2]

【0061】[評価]表2から、実施例の透湿防水布
は、いずれも比較例の透湿防水布よりも耐針荷重が高い
ことがわかる。すなわち、タイプIVの構成(1枚の高密
度布帛)において、繊維密度を上げたり(比較例2)、
糸を太くする(比較例3)よりも、高密度布帛を2枚重
ねる方が優れていることがわかる。従って、荷重3kg
で行なったピンホール実験でも、実施例2〜5の透湿防
水布は漏水しなかったが、比較例の透湿防水布は漏水し
た。尚、実施例1では、漏水したものの、針感性におい
て、比較例より優れていたことから、たとえ透湿防水膜
に穴があいた場合であっても、内側特に衣服の場合には
着衣者を守ることができる。
[Evaluation] From Table 2, it can be seen that the moisture-permeable waterproof cloths of the examples have higher needle load than the moisture-permeable waterproof cloths of the comparative examples. That is, in the type IV configuration (one high-density cloth), the fiber density was increased (Comparative Example 2),
It can be seen that it is better to stack two high-density fabrics than to make the yarn thicker (Comparative Example 3). Therefore, load 3kg
In the pinhole experiment performed in the above, the moisture-permeable waterproof cloths of Examples 2 to 5 did not leak, but the moisture-permeable waterproof cloth of the comparative example did. In Example 1, although water leaked, the needle sensitivity was superior to that of the comparative example. Therefore, even if the moisture-permeable waterproof membrane had a hole, it protected the wearer especially in the case of clothes. be able to.

【0062】また、実施例1〜4と比較例3との比較か
ら、総厚みの大小よりも、高密度布帛を複数枚重ねた透
湿防水布(タイプI、II)や透湿防水膜と高密度布帛と
が交互に積層された透湿防水布(タイプIII)の方が耐
針性に優れていることがわかる。
Further, from the comparison between Examples 1 to 4 and Comparative Example 3, it was found that the moisture-permeable waterproof cloth (types I and II) or the moisture-permeable waterproof membrane in which a plurality of high-density cloths were stacked was smaller than the total thickness. It can be seen that the moisture-permeable waterproof cloth (type III) in which high-density cloths are alternately laminated has better needle resistance.

【0063】[0063]

【発明の効果】第1発明の透湿防水布では透湿防水膜の
両側に高密度布帛が積層され、第2発明の透湿防水布で
は透湿防水膜の一側に高密度布帛が複数枚積層され、第
3発明の透湿防水布では透湿防水膜と高密度布帛とから
なる積層体が複数積層されているので、従来よりも耐針
性に優れている。このことは、従来よりも薄くて、しか
も耐針性は従来と同程度以上である透湿防水布を提供で
きることを意味する。
According to the moisture-permeable waterproof cloth of the first invention, a high-density cloth is laminated on both sides of the moisture-permeable waterproof membrane, and in the moisture-permeable waterproof cloth of the second invention, a plurality of high-density cloths are provided on one side of the moisture-permeable waterproof membrane. The moisture-permeable waterproof cloth according to the third aspect of the present invention is more excellent in needle resistance than the conventional one because a plurality of laminates composed of the moisture-permeable waterproof membrane and the high-density cloth are laminated. This means that it is possible to provide a moisture-permeable waterproof cloth which is thinner than the conventional one and has the same or higher needle resistance as the conventional one.

【0064】また、保護用布帛を積層することにより、
透湿防水布の最外面が透湿防水膜となることを防止でき
るので、針状体からだけでなく、他の刺激からも透湿防
水膜を保護して、透湿防水布の取り扱いを容易にすると
ともに、保護布の種類に応じて、透湿防水布に種々の機
能を付与することもできる。
Further, by laminating the protective cloth,
Since the outermost surface of the moisture-permeable waterproof cloth can be prevented from becoming a moisture-permeable waterproof membrane, it protects not only the needle-shaped body but also other stimuli from the moisture-permeable waterproof membrane, making it easy to handle the moisture-permeable waterproof cloth. In addition, various functions can be provided to the moisture-permeable waterproof cloth according to the type of the protective cloth.

【図面の簡単な説明】[Brief description of the drawings]

【図1】 第1発明の一実施形態を示す図である。FIG. 1 is a diagram showing an embodiment of the first invention.

【図2】 第2発明の一実施形態を示す図である。FIG. 2 is a diagram showing an embodiment of the second invention.

【図3】 第3発明の一実施形態を示す図である。FIG. 3 is a diagram showing an embodiment of the third invention.

【図4】 保護布が積層された実施形態例を示す図であ
る。
FIG. 4 is a view showing an embodiment in which protective cloths are laminated.

【図5】 従来の透湿防水布の構成を示す図である。FIG. 5 is a diagram showing a configuration of a conventional moisture-permeable waterproof cloth.

【符号の説明】[Explanation of symbols]

1 透湿防水膜 2、3、4、 高密度布帛 6 保護用布帛 DESCRIPTION OF SYMBOLS 1 Moisture-permeable waterproof membrane 2, 3, 4, High density cloth 6 Protective cloth

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 FI D06M 17/00 D06M 17/00 Z ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI D06M 17/00 D06M 17/00 Z

Claims (4)

【特許請求の範囲】[Claims] 【請求項1】 1インチあたりの縦糸及び横糸の打ち込
み合計本数が、70デニールの糸で240本以上に相当
する繊維密度を有している高密度布帛を、透湿防水膜の
両側に積層してなることを特徴とする透湿防水布。
1. A high-density fabric having a fiber density equivalent to 240 or more of 70 denier yarns per one inch in the total number of warp yarns and weft yarns per inch is laminated on both sides of a moisture-permeable waterproof membrane. A breathable waterproof cloth characterized by being made of:
【請求項2】 1インチあたりの縦糸及び横糸の打ち込
み合計本数が、70デニールの糸で240本以上に相当
する繊維密度を有している高密度布帛を、透湿防水膜の
少なくとも一側に複数積層してなることを特徴とする透
湿防水布。
2. A high-density fabric having a fiber density equivalent to 240 or more of 70 denier yarns and a total number of warp yarns and weft yarns per inch is attached to at least one side of the moisture-permeable waterproof membrane. A moisture-permeable waterproof cloth characterized by being laminated.
【請求項3】 1インチあたりの縦糸及び横糸の打ち込
み合計本数が、70デニールの糸で240本以上に相当
する繊維密度を有している高密度布帛と、透湿防水膜と
からなる積層体が、 該透湿防水膜と該高密度布帛とが交互になるように、複
数積層されていることを特徴とする透湿防水布。
3. A laminate comprising a high-density fabric having a fiber density equivalent to 240 or more of 70 denier yarns and a warp yarn and a weft yarn per inch, and a moisture-permeable waterproof membrane. Wherein a plurality of the moisture-permeable waterproof membranes and the high-density fabrics are alternately laminated.
【請求項4】 請求項2または3に記載の透湿防水布の
最外の透湿防水膜上に、保護用布帛が積層されている透
湿防水布。
4. A moisture-permeable waterproof cloth in which a protective cloth is laminated on the outermost moisture-permeable waterproof membrane of the moisture-permeable waterproof cloth according to claim 2 or 3.
JP9109761A 1997-04-25 1997-04-25 Moisture-permeable and waterproof cloth Pending JPH10298869A (en)