JPH10236094A - Method and apparatus for manufacturing fancy veneer decorative material - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a method and apparatus for manufacturing a fancy veneer decorative material having high quality and excellent design properties without introducing decrease in productivity and adhesive fault and without generating a part observed with pattern omission. SOLUTION: A transfer sheet 1 obtained by releasably laminating a transfer layer 6 having a decorative layer made of ink containing thermoplastic resin binder solid at the ambient temperature on a support sheet 2 of thermoplastic resin is adhered on a strip-like or sheet-like fancy veneer 10 having air permeability, and laminated. The support sheet 2 among transfer sheet constituting members is peeled from the transfer layer 6. The transfer layer 6 is heated and softened. Further, the air retained in conduit grooves is sucked and vacuumized from a surface of the veneer 10 opposite to the transfer sheet having the conduit grooves via the veneer 10.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for bonding a transfer sheet having a decorative layer such as a grain pattern or a pattern on a support sheet in a releasable manner onto a strip-shaped or sheet-shaped veneer. The present invention relates to a method and an apparatus for obtaining a veneer decorative material having a transfer layer transferred to the surface by peeling only the support sheet after lamination.

[0002]

2. Description of the Related Art A transfer sheet used for producing a veneer decorative material of this kind is usually provided on a support sheet 2 made of a thermoplastic resin, as shown in FIG. The transfer layer 6 is laminated so as to be peelable.
As shown in the figure, the transfer layer 6 is often formed by sequentially laminating a release layer 3, a decorative layer 4 such as a grain pattern, and an adhesive layer 5 from the support sheet 2 side by gravure printing or the like.

[0005] Further, a veneer serving as a base portion of the veneer decorative material is formed in a strip shape or a sheet shape that can be wound up in a roll shape as shown in FIG. The surface has a number of conduit grooves 12, 1
2,... Are formed.

In order to obtain a veneer decorative material in which the transfer sheet 1 is transferred to the surface of the veneer 10 by bonding the transfer sheet 1 to the veneer 10, conventionally, the following (1) to (4) have been described. The method has been adopted.

[0005] (1) As shown in FIG. 6 (A), a filling agent 14 or an adhesive is filled so as to fill the conduit grooves 12, 12,... Are smoothed so that the upper surfaces of the grooves 12, 12,... And the surface of the veneer plate 10 are flush with each other, and then, as shown in FIG. 6B, the transfer sheet 6 is bonded and laminated on the veneer plate 10. rear,
Only the support sheet 2 of the components of the transfer sheet 2 is peeled off from the transfer layer 6.

(2) As shown in FIG.
After the transfer sheet 6 is bonded and laminated on the veneer 10 while the conduit grooves 12, 12,...
Only the support sheet 2 of the components of the transfer sheet 2 is peeled off from the transfer layer 6.

(3) Similarly to the above (2), the transfer sheet 6 is adhered and laminated on the veneer 10 while the conduit grooves 12, 12,... Sheet 2
7A, only the support sheet 2 is peeled off from the transfer layer 6, and then, as shown in FIG.
The portions (2, 12,...) (Non-adhered portions) are dissolved with an organic solvent 18 so that the transfer layer 6 follows the inner peripheral surfaces of the conduit grooves 12, 12,.

(4) The transfer sheet 6 is bonded and laminated on the veneer 10 in the same manner as in (3) above, and only the support sheet 2 is peeled off from the transfer layer 6. Are swelled with an organic solvent so that the transfer layer 6 follows the inner peripheral surfaces of the conduit grooves 12, 12,.

[0009]

SUMMARY OF THE INVENTION
As shown in (1), in the case where the filler grooves 14 or the adhesive or the like are filled in the conduit grooves 12, 12,... Of the veneer 10, the conduit groove shape is not sharp, so that a finished finish is obtained. There is a problem that the design property is reduced, and a process and time for drying the filler 14 or the adhesive or the like filled in the conduit grooves 12, 12,... Are required, and the productivity is reduced.

Also, as described in the above (2), the conduit grooves 12, 1
In the case where the transfer sheet 1 is bonded and laminated to the veneer 10 with the blanks 2,..., The transfer layer 6 is not bonded in the conduit grooves 12, 12,. Conduit groove 1
Since air is contained in the portions 2, 12,..., There is a problem that these conduit grooves 12, 12,. In this case, the luminous conduit grooves 12, 12,... Are not so conspicuous in the light color type, but are conspicuous as a pattern missing in the dark color type, and the quality is greatly reduced.

As described in the above (3), in the case where the conduit grooves 12, 12,... Of the transfer layer 6 are dissolved by the organic solvent 18, when the transfer layer 6 is a thin film, the pattern is formed by dissolution. There is a problem that it looks like it has disappeared, the appearance is poor, and the design is deteriorated. Also, as described in (4) above, the conduit grooves 12, 12,... In the case of the transfer layer 6, the thickness of the transfer layer 6, the mixing ratio of the solvent and the applied amount thereof, the drying mode, the atmosphere (humidity,
Temperature, etc., the air in the conduit grooves 12, 12,... May not completely escape, and the conduit grooves 12, 12,.
If air remains in the conduit grooves 12, 1
2. There is a problem that the part looks shiny, the appearance is poor, the design is reduced, and the quality varies.

SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and an object of the present invention is to provide a device which does not cause a decrease in productivity or poor adhesion, and a portion which looks like a missing pattern. It is an object of the present invention to provide a manufacturing method and an apparatus capable of obtaining a veneer decorative material having high quality and excellent designability without causing the generation of the veneer.

[0013]

In order to achieve the above-mentioned object, a method for producing a veneer decorative material according to the present invention comprises an ink containing a thermoplastic resin binder solid at room temperature on a thermoplastic resin support sheet. An adhesive laminating step of bonding and laminating a transfer sheet having a transfer layer having a decorative layer made of a releasable laminate on a strip-like or sheet-like veneer having air permeability and then laminating the transfer sheet, After performing a peeling step of peeling the support sheet of the constituent members from the transfer layer, a heating softening step of heating and softening the transfer layer,
A suction step of vacuum-suctioning air remaining inside the conduit groove or the like from the surface opposite to the transfer sheet laminating surface on which the conduit groove or the like is formed in the veneer through the veneer plate,
It is characterized by performing.

Further, the apparatus for producing a veneer decorative material according to the present invention can peel off a transfer layer having a decorative layer made of an ink containing a binder of a thermoplastic resin which is solid at room temperature on a thermoplastic resin support sheet. Adhesive laminating means for bonding and laminating the transfer sheet on a breathable band-like or sheet-like veneer using a laminated transfer sheet on the upstream side in the feed direction of the veneer is arranged. Further, on the downstream side of the adhesive laminating unit, a separating unit for separating the support sheet of the transfer sheet constituting member from the transfer layer is arranged, and on the downstream side of the separating unit, the transfer layer is heated. Means for softening by heating, and air remaining inside the conduit groove or the like from the surface opposite to the transfer sheet laminating surface on which the conduit groove or the like is formed in the veneer is vacuum suctioned through the veneer. And suction means, is characterized in that is arranged.

In a preferred embodiment of the method and apparatus for manufacturing a veneer decorative material according to the present invention having the above-described structure, after the transfer sheet is adhered and laminated on the veneer, the transfer layer portion of the transfer sheet constituting member is removed. The support sheet is peeled off from the transfer layer so as to remain on the veneer side.

After the peeling step is performed in this manner, the transfer layer is heated and softened, and air remaining inside the concave portion such as the conduit groove (the portion between the veneer and the transfer sheet) is removed by the veneer. Vacuum through. As a result, the air in the conduit groove is removed to the back side of the veneer, and floats from the veneer of the heat-softened transfer sheet (not adhered).
The conduit groove portion is extended along the inner peripheral surface of the conduit groove from which air has been removed, and adheres to the conduit groove portion.

By doing so, the air in the conduit groove or the like is removed by suction by the heating softening step and the vacuum suction step and does not remain there, and the transfer layer is formed along the inner surface of the veneer in the conduit groove. Because of the close contact, in the obtained veneer decorative material, a surface shape including irregularities such as a conduit groove shape of the veneer appears, and the sense of realism increases. Therefore, it is possible to obtain a high-quality veneer decorative material excellent in design without causing a decrease in productivity, poor adhesion, or the like, and without generating a portion that looks like a pattern.

The transfer sheet used in the method and apparatus for producing a veneer decorative material of the present invention transfers a transfer layer composed of a decorative layer or the like laminated on a support sheet having releasability to the veneer. A release layer may be provided on the sheet as needed. The transfer layer generally includes a release layer, a decoration layer, an adhesive layer, and the like, but layers other than the decoration layer are not necessarily required, and may be provided as necessary.

The support sheet has a thickness of 9 to 200.
A thermoplastic resin of μm, preferably 16-100 μm, is used. In this case, the thickness is excessively thin (less than 9 μm)
If it is too thin, the strength will be insufficient and it will be too thick (20
0 μm) increases the cost and
In a normal roll transfer method, heat transfer is deteriorated, so that the transfer speed has to be reduced, and productivity is reduced.

Specific materials for the support sheet include linear polyesters such as polyethylene terephthalate and polybutylene terephthalate, linear polyamides such as nylon 6 and nylon 66, polyolefins such as polyethylene, polypropylene and olefin-based thermoplastic elastomers;
A thermoplastic resin film having flexibility such as polyvinyl chloride or a laminate thereof is preferable. In addition, as the polyethylene terephthalate, it is preferable to use molding PET (biaxially stretched PET) having a small stretching ratio. In particular, in consideration of cost, printability, and moldability, it is preferable to use a sheet of a polyolefin resin or a polyvinyl chloride resin.

The release layer provided on the support sheet as required uses melamine, silicone, aminoalkyd, urethane, urea, epoxy resin or the like. The thickness is 0.01 ~
About 5 μm is preferable. It is also possible to adjust the peel strength by adding an additive. In order to adjust the gloss of the surface after transfer, a known matting agent such as microsilica may be added to the release layer.

Here, the release layer means a layer which remains on the support sheet side even after the transfer and facilitates the separation from the transfer layer. On the other hand, the release layer means the coating after the transfer. A layer which is transferred to the transfer body (veneer) side and becomes a surface protective layer of the transfer layer. The release is performed between the release layer (support sheet) and the release layer.

It is preferable to use an acrylic resin, a urethane resin, a vinyl chloride-vinyl acetate copolymer, a butyral resin, a cellulose resin or the like as a release layer provided on the transfer layer as required. In this case, an acrylic resin is preferable in consideration of abrasion and transparency.

In order to make the release layer have surface lubricity after transfer (after release of the support sheet), it is preferable to add polyethylene wax, Teflon wax, carnauba wax, paraffin wax or the like as an additive. Add benzotriazole, benzophenone, salicylic acid UV absorbers, hinderdomian stabilizers, phenolic antioxidants and heat stabilizers when used for exterior applications or in areas exposed to sunlight. Is preferred. The release layer is laminated by a known method such as gravure printing, roll coating, screen printing, and offset printing.

The decorative layer is not limited to one in which a pattern such as a wood pattern is formed partially or entirely, but may be a simple solid color, transparent or colored opaque resin layer. In order to form a picture, a binder composed of an ink layer colored with a pigment or a dye is selected from an acrylic resin, a vinyl chloride-vinyl acetate copolymer, a polyester resin, a cellulose resin, a urethane resin and the like. In addition, a vapor deposition, antistatic, infrared blocking layer, ultraviolet absorbing layer, or the like may be provided as a decoration layer or a functional layer. When only the decorative layer is the transfer layer, it is formed with an ink using a thermoplastic resin which is solid at normal temperature as a binder. When a release layer and / or a transfer layer of a thermoplastic resin (solid at ordinary temperature) is provided, the release layer may be a metal thin film or an uneven pattern formed by embossing the release layer.

The adhesive layer is a layer for transferring the transfer layer to an object to be transferred (a veneer) and bonding and laminating the same. Here, it is preferable to use a heat-sensitive adhesive. When the transfer layer constituting layers other than the adhesive layer such as the decorative layer and the release layer have sufficient adhesiveness, the adhesive layer can be omitted.

Examples of the heat-sensitive adhesive include thermoplastic resins such as acrylic resins, vinyl chloride-vinyl acetate copolymers, polyester resins, styrene resins, chlorinated polypropylene resins, polyamide resins, and the like, and thermoplastic resins such as urethane resins and epoxy resins. Curable resins and the like are particularly preferable, and one or more resins selected from these are laminated by a known method such as gravure printing, roll coating, screen printing, and offset printing. The adhesive may be applied to at least one of the transfer sheet side and the veneer side.

On the other hand, the veneer to be transferred is a wood-based veneer having air permeability and has a thickness of 0.05 to 0.2 m.
m is desirable. The veneer can be efficiently produced if it is in the form of a strip (continuous sheet), but a sheet-like sheet can also be used. The back of the veneer (anti-transfer side) is used as a support to prevent cracking of the veneer and not impair the air permeability during the suction process.
Alternatively, a backing made of a non-woven fabric may be used. Further, a plywood or a glue may be used for the veneer, and the veneer may be used as it is in a flat plate shape (sheet shape), or may be used in a curved surface or a three-dimensional shape. If the veneer has irregularities such as conduit grooves or annual rings on the surface, it is an object of the present invention. As the tree species, zelkova, oak, lauan, teak, merapy,
Japanese cedar, cypress, pine, cherry blossoms and the like can be mentioned.

In the method apparatus of the present invention, a heating softening step and a suction step are performed after the support sheet peeling step is completed. In other words, the transfer layer is directly heated and softened in the absence of the support sheet, and the air in the conduit groove is evacuated.

Further, in the heating softening step, it is required to heat the support sheet and the transfer layer so that the surface temperatures of the support sheet and the transfer layer are higher than the softening temperature and lower than the melting temperature. This heating temperature is
When the support sheet and the transfer layer are formed of the ordinary resin material as described above, the temperature may be about 50 to 200 ° C. As the heat softening means, those using techniques such as infrared radiation, hot air blowing, dielectric heating, and pressing with a heating roller (rubber, metal, etc.) can be used.

In the suction step, air remaining in the conduit groove of the projecting plate closed by the transfer layer is removed by a suction means such as a vacuum pump or the like on the surface opposite to the transfer sheet lamination surface (back surface). Through the protruding plate to remove by vacuum suction.
In this case, as described above, since the transfer layer is heated and softened, the transfer layer adheres along the inner surface of the concave portion such as the conduit groove of the veneer plate by vacuum suction.

After the suction step, the surface of the transfer layer may be coated, if necessary. It is desirable to use a paint or a colorless and transparent paint that allows the transfer layer to be seen through. As the resin (binder) type, a fibrous resin (nitrified cotton, cellulose acetate, or the like), a two-component cured polyurethane resin, an amino alkyd resin, an acrylic resin, a fluorine resin, or the like can be used. The coating thickness is usually about 1 to 100 μm.

[0033]

Embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 schematically shows an embodiment of a veneer decorative material manufacturing apparatus for implementing the veneer decorative material manufacturing method according to the present invention.

The veneer decorative material manufacturing apparatus A of the present embodiment basically has a structure in which the transfer sheet 1 is adhered and laminated on the surface of the veneer 10 which is a strip-shaped continuous sheet, Only the body sheet 2 is peeled off, and the transfer layer 6
Is transferred to obtain a veneer decorative material 10 '.

In this embodiment, the transfer sheet 1
As shown in FIG. 2, a transfer layer 6 is releasably laminated on a support sheet 2 made of a thermoplastic resin. As the transfer layer 6, a known transfer layer is used. From the side of the support sheet 2, a release layer 3, a wood-grain decorative layer 4 made of ink containing a resin binder, and an adhesive layer 5 are sequentially provided.
Are sequentially laminated by gravure printing or the like, and each of these transfer layers is made of a solid resin binder at a temperature lower than room temperature (room temperature or use environment temperature, usually set to a maximum of about 80 ° C.). Its thickness is about 3 to 50 μm.

As shown in FIG. 5, a large number of conduit grooves 12, 12,... Are formed on the surface of the projecting plate 10, and its thickness is about 150 μm. A non-woven fabric 15 (see FIG. 3) is lined on the back surface (opposite to the transfer side) of the projecting plate 10.

Here, the projecting plate 10 unwound from the state of the take-up roll BR is conveyed substantially horizontally while being guided by rollers 26, 23 (which also serve as impression cylinders), 28, 34, 29. Finally, it is wound up as a veneer decorative material 10 'on which the transfer layer 6 is bonded and laminated (winding roll CR).

That is, the projecting plate 10 unwound from the state of the take-up roll BR is first passed between a pair of upper and lower feed guide rollers 26, 26 arranged at the uppermost stream. The transfer sheet 1 unwound from the state of the take-up roll DR is also passed between the feed guide rollers 26, 26, and the transfer sheet 1 faces the surface of the protruding plate 10 between the feed guide rollers 26, 26. In this state, the surface with the heater 21 constituting the adhesive laminating means is passed between the laminating roller 20 made of silicon rubber and the backup roller 23, heated and pressed at the same time. Thereby, the transfer sheet 1 is bonded and fixed on the surface of the protruding plate 10 (bonding and laminating step).

The veneer 10 on which the transfer sheet 1 is adhered and laminated in this manner is sufficiently cooled, and the adhesive strength between the veneer / transfer layer is greater than the adhesive strength between the transfer layer / support sheet.
Subsequently, the support sheet 2 of the transfer sheet constituent members
Is peeled off from the transfer layer 6 by a peeling roller 28 and a transfer sheet winding roll ER constituting a peeling means (peeling step).

Next, the veneer 10 from which the support sheet 2 is peeled off and only the transfer layer 6 remains in an adhesively laminated state is the infrared radiation heaters 32, 32, which constitute the heating and softening means 30.
Are sent into the chamber 31 in which is stored. The chamber 31 is formed with a slit-shaped inlet 31a and outlet 31b provided with appropriate airtight means (not shown) so as to be able to pass through the projecting plate 10 on which the transfer layer 6 is bonded and laminated. A vacuum suction passage 35 connected to a vacuum pump 40 constituting a suction means is opened at the bottom of the veneer plate 10 located on the back surface side (the side opposite to the transfer sheet lamination surface side).

During the passage through the chamber 31, the transfer layer 6 includes the infrared radiation heaters 32, 32,.
Is usually heated to about 100 to 150 ° C. to be softened so that the surface temperature becomes equal to or higher than the softening temperature and equal to or lower than the melting temperature (heating softening step).

At the same time, the vacuum pump 40
Are formed in the conduit grooves 12, 12,... From the surface (rear surface) opposite to the transfer sheet laminating surface in which the conduit grooves 12, 12,. Vacuum suction is performed through 10 (suction step).

Thus, the air in the conduit grooves 12, 12,...
, The conduit grooves 12, 12,... Floating (not bonded) from the veneer plate 10 of the transfer sheet 1, which has been softened by heating, are the conduit grooves 12 from which air is removed. 12, are stretched along the inner peripheral surface and closely adhered thereto (see FIG. 3).

After leaving the chamber 31,
It is cooled by a cooling device (not shown) if necessary, and the surface of the transfer layer 6 is coated by a coating roller 50 as necessary.

In this manner, the air in the conduit grooves 12, 12,... Is removed by suction by the heating softening step and the vacuum suction step and does not remain there.
As shown in FIG. 3, the transfer layer 6 is
2, 12,... So as to adhere along the inner surface, in the obtained veneer decorative material 10 ', the conduit groove shape of the veneer 10 appears, and the sense of realism increases. Therefore, it is possible to obtain a high-quality veneer decorative material excellent in design without causing a decrease in productivity, poor adhesion, or the like, and without generating a portion that looks like a pattern. In order to confirm such an effect, a comparative experiment was performed using the apparatus of FIG. 1 under the following conditions.

(1) Method device of the present invention Transfer sheet 1... Support sheet 2 has a thickness of 25
μm polyester film [manufactured by Diafile Corporation]. The transfer layer 6 is formed by sequentially forming an acrylic resin-based release layer 3 [manufactured by Showa Ink Industry Co., Ltd.
μm], an oak-patterned decorative layer 4 made of an ink obtained by adding a pigment to an acrylic resin and a vinyl chloride-vinyl acetate copolymer resin in a weight ratio of 1: 1 as a binder.
[2 μm thick, manufactured by Showa Ink Industry Co., Ltd.], and an adhesive layer of vinyl chloride-vinyl acetate copolymer resin [10 μm thick, manufactured by Showa Ink Co., Ltd.] gravure printed on the entire surface.

Veneer 10: A backing of a Lauan veneer having a 200 μm-thick conduit groove coated with a urethane resin-based base layer (manufactured by Hamani Paint Co., Ltd.) at a surface of 2 g / m ² and lined with a vinylon nonwoven fabric.

Adhesive lamination process: Transfer at 130 ° C. × 5 m / min. Peeling-off step: performed immediately after the bonding and laminating step. Heat softening step: infrared radiation heaters 32, 32,
, The surface temperature of the support sheet 2 and the transfer layer 6 is set to 120
Heat to ° C.

Suction step: by the vacuum pump 40
Vacuum suction is performed from the surface (back surface) opposite to the transfer sheet laminating surface on which the conduit grooves 12, 12,...

(2) Comparative Example The same as the above embodiment, except that the same transfer sheet 1 and veneer plate 10 as those described above were used and the suction step was not performed.

(3) Results of Comparative Experiment In the embodiment of the method apparatus of the present invention, as shown in FIG. 3, the transfer layer 6 is in close contact with the inner surfaces of the conduit grooves 12, 12,. , Obtained veneer decorative material 10 '
In the comparative example, as shown in FIG. 4, air remained in the conduit grooves 12, 12,... , The transfer layer 6 floats in the conduit grooves 12, 12,... And has poor adhesion, and the obtained veneer decorative material is in the conduit grooves 12, 12,.
Are shining, and the design was inferior to that of the present invention.

[0052]

As will be understood from the above description, according to the method and apparatus for producing a veneer decorative material according to the present invention, air in the conduit groove or the like is sucked out by the heating softening step and the vacuum suction step. Since the transfer layer does not remain there and the transfer layer adheres along the inner surface of the conduit groove of the veneer, in the obtained veneer decorative material, the conduit groove shape of the veneer appears, and the sense of realism increases. Therefore, it is possible to obtain a high-quality veneer decorative material having high quality and excellent designability without causing a decrease in productivity, poor adhesion, and the like, and without causing a portion that looks like a missing pattern. Is obtained.

[Brief description of the drawings]

FIG. 1 is a view schematically showing one embodiment of a veneer decorative material manufacturing apparatus for carrying out a method for manufacturing a veneer decorative material according to the present invention.

FIG. 2 is a partial cross-sectional view showing an example of a transfer sheet used in the method for producing a veneer decorative material of the present invention.

FIG. 3 is a partial sectional view showing a veneer decorative material obtained by the veneer decorative material manufacturing method according to the present invention.

FIG. 4 is a partial cross-sectional view showing a veneer decorative material obtained by a veneer decorative material manufacturing method of a comparative example.

FIG. 5 is a partially enlarged perspective view showing a veneer plate.

FIG. 6 is a diagram which is used for describing a conventional method for manufacturing a veneer decorative material.

FIG. 7 is a diagram which is used for describing a conventional method for manufacturing a veneer decorative material.

[Explanation of symbols]

 DESCRIPTION OF SYMBOLS 1 Transfer sheet 2 Support sheet 3 Release layer 4 Decorative layer 5 Adhesive layer 6 Transfer layer 10 Veneer board 12 Conduit groove 20 Laminating roller 32 Infrared radiation heater 40 Vacuum pump BR, CR Veneer board take-up roll DR, ER Transfer sheet take-up roll

Claims (2)

[Claims] 1. A transfer sheet comprising a transfer layer having a decorative layer made of an ink containing a binder of a thermoplastic resin solid at room temperature on a support sheet of a thermoplastic resin in a releasable manner. Alternatively, an adhesive laminating step of bonding and laminating on a sheet-like sheet-like veneer is performed, and then, after performing a peeling step of peeling a support sheet of the transfer sheet constituent member from the transfer layer, the transfer is performed. A heating and softening step of heating and softening the layer, and passing air remaining inside the conduit groove or the like from the surface opposite to the transfer sheet laminating surface where the conduit groove or the like in the veneer is formed through the veneer. And performing a vacuum step of vacuum suction. 2. A veneer decorative material using a transfer sheet in which a transfer layer having a decorative layer made of an ink containing a binder of a thermoplastic resin solid at room temperature is peelably laminated on a support sheet of a thermoplastic resin. An adhesive laminating means for adhering and laminating the transfer sheet on a gas-permeable band-shaped or sheet-shaped sheet-shaped veneer, which is arranged on the upstream side in the feed direction of the veneer, and On the downstream side of the adhesive laminating means, a peeling means for peeling the support sheet of the transfer sheet constituting member from the transfer layer is arranged, and on the downstream side of the peeling means, the transfer layer is heated and softened. Heating and softening means, and suction means for vacuum-suctioning the air remaining inside the conduit groove and the like from the surface of the veneer plate opposite to the transfer sheet laminated surface where the conduit groove and the like are formed via the veneer plate. Apparatus for producing veneer decorative material, wherein a is located.