JPH10225533A - Golf ball - Google Patents
Golf ballInfo
- Publication number
- JPH10225533A JPH10225533A JP9029371A JP2937197A JPH10225533A JP H10225533 A JPH10225533 A JP H10225533A JP 9029371 A JP9029371 A JP 9029371A JP 2937197 A JP2937197 A JP 2937197A JP H10225533 A JPH10225533 A JP H10225533A
- Authority
- JP
- Japan
- Prior art keywords
- cover
- hardness
- golf ball
- core
- layer cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、コアを被覆するカ
バーが、内層カバーと外層カバーの２層構造に構成され
るゴルフボールに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf ball in which a cover for covering a core has a two-layer structure of an inner cover and an outer cover.
【０００２】[0002]
【従来の技術】従来、ゴルフボールのカバーとしては、
その高反発性により十分な飛距離が得られることから、
硬質のアイオノマー樹脂からなるカバーが広く使用され
ている。ところが、硬質のアイオノマー樹脂をカバー材
料とするゴルフボールは、カバーが硬いために、打球
感、コントロール性が悪いことが指摘されている。この
欠点を改善するものとして、軟質樹脂を使用することに
よりカバーを柔軟化したゴルフボールが開発されてき
た。2. Description of the Related Art Conventionally, as a cover of a golf ball,
Because a sufficient flight distance is obtained by its high resilience,
A cover made of a hard ionomer resin is widely used. However, it has been pointed out that a golf ball using a hard ionomer resin as a cover material has poor hit feeling and controllability because the cover is hard. As a solution to this drawback, golf balls have been developed in which the cover is softened by using a soft resin.
【０００３】しかしながら、このようなゴルフボール
は、打球感およびコントロール性は良くなるものの、カ
バーの柔軟化に伴って反発性の低下を招き、飛距離が出
なくなる傾向がある。そこで、飛距離不足を補うため
に、例えば、ツーピースソリッドゴルフボールでは、コ
アを従来よりもかなり硬くしている。この場合、硬いコ
アが要因となって、打球感が損なわれ、また、スピン量
が多くなり、飛距離不足がそれほど解消されないという
問題がある。[0003] However, although such golf balls have improved shot feeling and controllability, the softness of the cover tends to reduce resilience and reduce the flight distance. Therefore, in order to compensate for the shortage of the flight distance, for example, in a two-piece solid golf ball, the core is considerably harder than before. In this case, there is a problem that, due to the hard core, the shot feeling is impaired, the spin rate is increased, and the shortage of the flight distance is not so solved.
【０００４】そこで、飛距離の低下を回避しながら、打
球感およびコントロール性が良いゴルフボールを得るた
めに、カバーを内層カバーと外層カバーの２層構造とす
ることが提案されている。例えば、特公平７−８３０１
号公報には、内層カバーを比較的軟質の熱可塑性樹脂に
より厚さ０．１〜２ｍｍに形成し、外層カバーを硬質の
熱可塑性樹脂により厚さ０．１〜１．５ｍｍに形成し、
かつ、カバーの全体の厚さを０．４〜２．２ｍｍとした
ものが開示されている。[0004] Therefore, in order to obtain a golf ball with good shot feeling and controllability while avoiding a decrease in flight distance, it has been proposed that the cover has a two-layer structure of an inner cover and an outer cover. For example, Japanese Patent Publication 7-8301
In the gazette, the inner cover is formed to a thickness of 0.1 to 2 mm by a relatively soft thermoplastic resin, and the outer cover is formed to a thickness of 0.1 to 1.5 mm by a hard thermoplastic resin.
Further, a cover having an overall thickness of 0.4 to 2.2 mm is disclosed.
【０００５】しかしながら、このソリッドゴルフボール
では、ショートアイアン、ウェッジ等のクラブによるシ
ョットにおいて、硬質の外層カバーが影響するため、必
ずしも打球感およびコントロール性が良くなるとは限ら
ない。However, in this solid golf ball, a shot with a club such as a short iron or a wedge is affected by the hard outer layer cover, so that the shot feeling and controllability are not always improved.
【０００６】また、特公平４−４８４７３号公報には、
カバーを軟質の内層カバーと硬質の外層カバーとの２層
構造としたソリッドゴルフボールにおいて、内層カバー
を高比重とすることにより、慣性モーメントを大きくし
て飛距離を伸ばしたものが開示されている。Further, Japanese Patent Publication No. 4-48473 discloses that
A solid golf ball in which the cover has a two-layer structure of a soft inner cover and a hard outer cover, in which the inner cover has a high specific gravity to increase the moment of inertia and extend the flight distance, is disclosed. .
【０００７】しかしながら、このソリッドゴルフボール
においても、十分な打球感およびコントロール性の改善
の効果が得られるものではない。However, even with this solid golf ball, it is not possible to obtain sufficient effects of improving shot feeling and controllability.
【０００８】[0008]
【発明が解決しようとする課題】本発明は、十分な飛距
離が出て、しかも打球感およびコントロール性が良好で
あるゴルフボールを提供することを目的とする。SUMMARY OF THE INVENTION It is an object of the present invention to provide a golf ball having a sufficient flight distance and good hit feeling and controllability.
【０００９】[0009]
【課題を解決するための手段】本発明のゴルフボール
は、図１に断面構造を示すように、コア１と２層からな
るカバー２とから構成される。カバー２は、ショアＤ硬
度６０以上を有する内層カバー２ａと、内層カバー２ａ
よりも硬度が低く、ショアＤ硬度４５〜６５を有する外
層カバー２ｂとの２層構造に形成される。硬度が比較的
高い内層カバー２ａが反発性を低下させず、また、ドラ
イバー等のクラブによるショットにおけるスピン量を適
正にするので、十分な飛距離を得ることができる。ま
た、内層カバー２ａよりも硬度が低い外層カバー２ｂが
打球感をソフトにし、ショートアイアン等のクラブによ
るショットにおけるスピン量を適正にするので、良好な
打球感およびコントロール性を得ることができる。The golf ball of the present invention comprises a core 1 and a two-layer cover 2 as shown in FIG. The cover 2 includes an inner cover 2a having a Shore D hardness of 60 or more, and an inner cover 2a.
The outer cover 2b has a lower hardness than the outer cover 2b and has a Shore D hardness of 45 to 65. The inner cover 2a having a relatively high hardness does not reduce the resilience and makes the spin amount appropriate for a shot by a club such as a driver, so that a sufficient flight distance can be obtained. Also, the outer cover 2b having a lower hardness than the inner cover 2a softens the shot feeling and makes the spin amount appropriate for the shot by a club such as a short iron, so that a good shot feeling and controllability can be obtained.
【００１０】より良好な効果を得るためには、内層カバ
ー２ａは、ショアＤ硬度６３〜７３で、外層カバー２ｂ
は、ショアＤ硬度５０〜６２であるのが好ましい。In order to obtain a better effect, the inner cover 2a should have a Shore D hardness of 63 to 73 and an outer cover 2b.
Preferably has a Shore D hardness of 50 to 62.
【００１１】内層カバー２ａは、従来のカバー材料、例
えば、アイオノマー樹脂、熱可塑性エラストマー等の熱
可塑性樹脂を成分とする組成物を用いて形成することが
でき、エチレン・（メタ）アクリル酸共重合体のリチウ
ム塩のアイオノマー樹脂を、基材樹脂の総重量に対して
５０重量％以上含有する樹脂組成物から形成するのが好
ましい。エチレン・（メタ）アクリル酸共重合体のリチ
ウム塩のアイオノマー樹脂は、公知のエチレン・（メ
タ）アクリル酸共重合体のナトリウム塩または亜鉛塩の
アイオノマー樹脂と比べて反発性が高く、また、耐久性
が良いことから、本発明において好ましく使用すること
ができ、特に基材樹脂の総重量に対して８０重量％以上
含有させて使用するとより良好な効果が得られる。エチ
レン・（メタ）アクリル酸共重合体のリチウム塩のアイ
オノマー樹脂の市販品としては、例えば、米国デュポン
社製のサーリン７９３０、サーリン７９４０等があり、
これらは、（メタ）アクリル酸含有量が１２〜１８重量
％、イオン中和度が２０モル％以上のものである。The inner cover 2a can be formed by using a conventional cover material, for example, a composition containing a thermoplastic resin such as an ionomer resin and a thermoplastic elastomer as a component, and a copolymer of ethylene and (meth) acrylic acid. It is preferable to form the ionomer resin of the combined lithium salt from a resin composition containing 50% by weight or more based on the total weight of the base resin. The ionomer resin of a lithium salt of an ethylene / (meth) acrylic acid copolymer has higher resilience than a known ionomer resin of a sodium salt or a zinc salt of an ethylene / (meth) acrylic acid copolymer, and has a high durability. Since it has good properties, it can be preferably used in the present invention. Particularly, when used in an amount of 80% by weight or more based on the total weight of the base resin, a better effect can be obtained. Commercially available ionomer resins of lithium salt of ethylene / (meth) acrylic acid copolymer include, for example, Surlyn 7930 and Surlyn 7940 manufactured by DuPont, USA.
These have a (meth) acrylic acid content of 12 to 18% by weight and a degree of ion neutralization of 20 mol% or more.
【００１２】そして、内層カバー２ａは、形成するのに
用いる組成物にタングステン、鉛、銅等の金属粉、二酸
化チタン、酸化亜鉛、硫酸バリウム等の金属化合物等を
配合し、比重を１．０以上、好ましくは１．１以上とす
ることができる。内層カバー２ａを比重１．０以上とす
ると、慣性モーメントが大きくなるので、飛距離の低下
を避けることができる。なお、内層カバー２ａを形成す
るのに用いる組成物には、必要に応じて顔料、老化防止
剤、分散剤等を配合することもできる。The inner layer cover 2a is prepared by mixing a metal powder such as tungsten, lead, and copper, a metal compound such as titanium dioxide, zinc oxide, and barium sulfate into the composition used to form the inner cover 2a. Above, preferably 1.1 or more. When the specific gravity of the inner layer cover 2a is 1.0 or more, the moment of inertia increases, so that a decrease in flight distance can be avoided. The composition used to form the inner layer cover 2a may optionally contain a pigment, an antioxidant, a dispersant, and the like.
【００１３】内層カバー２ａの厚さは、１．０〜３．０
ｍｍ程度に形成することができ、薄くし過ぎると、反発
性が悪くなり、逆に、厚くし過ぎると、打球感が悪くな
る。The thickness of the inner cover 2a is 1.0 to 3.0.
When the thickness is too small, the resilience deteriorates. On the other hand, when the thickness is too large, the shot feeling deteriorates.
【００１４】外層カバー２ｂは、内層カバー２ａよりも
硬度を低くするために、軟質の熱可塑性樹脂、例えば軟
質のアイオノマー樹脂、軟質の熱可塑性ポリウレタン等
を用いた樹脂組成物から形成することができ、軟質の熱
可塑性樹脂と硬質のアイオノマー樹脂との混合物を基材
樹脂とすることもできる。外層カバー２ｂは、内層カバ
ー２ａと同様に高比重カバーとすることができるが、低
硬度の材料に充填剤を多く配合した場合には、耐久性が
悪くなる傾向があるので、外層カバー２ｂの比重は、
１．０以下に抑えるのが好ましい。The outer cover 2b can be formed from a resin composition using a soft thermoplastic resin, for example, a soft ionomer resin, a soft thermoplastic polyurethane, or the like, in order to make the hardness lower than that of the inner cover 2a. Alternatively, a mixture of a soft thermoplastic resin and a hard ionomer resin can be used as the base resin. The outer layer cover 2b can be a high specific gravity cover similarly to the inner layer cover 2a. However, if a low filler material is mixed with a large amount of filler, the durability tends to be deteriorated. The specific gravity is
It is preferred to keep it at 1.0 or less.
【００１５】外層カバー２ｂの厚さは、１．０〜３．０
ｍｍ程度に形成することができ、薄くし過ぎると耐久性
が悪くなり、逆に、厚くし過ぎると反発性が悪くなる。The thickness of the outer layer cover 2b is 1.0 to 3.0.
mm, the durability becomes poor when the thickness is too small, and the resilience becomes poor when the thickness is too large.
【００１６】このような２層構造のカバーで被覆される
コアは、単層構造のソリッドコア、２層以上の構造のソ
リッドコア、糸巻きコアのいずれでも構わないが、例え
ば、図２に示すように、内層コア２１ａと外層コア２１
ｂの２層構造のソリッドコア２１とする場合において、
内層コア２１ａおよび外層コア２１ｂは、従来のソリッ
ドコアに用いられているシス１，４−ポリブタジエンを
基材とするゴム組成物から形成するのが好ましく、内層
コア２１ａは、ＪＩＳ−Ｃ硬度４０〜９５、外層コア２
１ｂは、ＪＩＳ−Ｃ硬度５０〜９５とし、内層コア２１
ａと外層コア２１ｂとの硬度差をＪＩＳ−Ｃ硬度１０以
上とするのが好ましい。また、内層コア２１ａは、直径
３６ｍｍ以下、ソリッドコア２１は、直径３９ｍｍ以下
とするのが好ましい。The core covered with such a two-layered cover may be a solid core having a single-layered structure, a solid core having a structure of two or more layers, or a wound core. For example, as shown in FIG. The inner core 21a and the outer core 21
In the case where the solid core 21 has a two-layer structure b,
The inner layer core 21a and the outer layer core 21b are preferably formed from a rubber composition based on cis 1,4-polybutadiene used for a conventional solid core, and the inner layer core 21a has a JIS-C hardness of 40 to 95, outer layer core 2
1b is a JIS-C hardness of 50 to 95, and the inner core 21
It is preferable that the hardness difference between the outer layer core 21a and the outer layer core 21b be JIS-C hardness 10 or more. The inner core 21a preferably has a diameter of 36 mm or less, and the solid core 21 preferably has a diameter of 39 mm or less.
【００１７】コアを被覆して２層構造のカバーを形成す
るには、従来のカバーの被覆方法を繰り返し用いて行う
ことができる。例えば、熱可塑性樹脂用の射出成型機を
用いて、コアを被覆して内層カバー、外層カバーを射出
成型により形成することができる。In order to form a two-layer cover by coating the core, a conventional cover coating method can be repeatedly used. For example, the inner layer cover and the outer layer cover can be formed by injection molding by covering the core using an injection molding machine for a thermoplastic resin.
【００１８】[0018]
【実施例および比較例】表１の配合による内層コア用、
外層コア用のゴム組成物を使用して、表２の実施例１〜
３および比較例１〜２に示した直径、硬度、重量からな
る２層構造のソリッドコアを作製した。次いで、表１の
配合による内層カバー用、外層カバー用の樹脂組成物を
使用して、ソリッドコアを被覆して２層構造のカバーを
射出成型により形成し、研磨、塗装を施して実施例１〜
３および比較例１〜２のソリッドゴルフボールを作製し
た。EXAMPLES AND COMPARATIVE EXAMPLES For the inner layer core having the composition shown in Table 1,
Using the rubber composition for the outer layer core, Examples 1 to
3 and a solid core having a two-layer structure consisting of the diameter, hardness and weight shown in Comparative Examples 1 and 2. Next, using a resin composition for the inner layer cover and the outer layer cover according to the composition shown in Table 1, a solid core was coated to form a two-layered cover by injection molding, and polished and painted. ~
3 and Comparative Golf Balls 1 and 2 were produced.
【００１９】実施例１〜３および比較例１〜２につき、
キャリー、打球感、コントロール性を表２に示した。For Examples 1-3 and Comparative Examples 1-2,
Table 2 shows the carry, feel at impact, and controllability.
【００２０】この場合、比較例１〜２に対して、実施例
１〜３において打球感が向上していることが了解され
る。これは、カバーの外層が内層よりも柔らかく設定さ
れていることによる。しかも、キャリーには殆ど差異が
生じていない。また、コントロール性も向上している。In this case, it is understood that the shot feeling is improved in Examples 1 to 3 as compared with Comparative Examples 1 and 2. This is because the outer layer of the cover is set softer than the inner layer. Moreover, there is almost no difference in the carry. Also, controllability has been improved.
【００２１】[0021]
【表１】 [Table 1]
【００２２】[0022]
【表２】 [Table 2]
【００２３】＊１（サーリン７９３０）：商品名、米国
デュポン社製のエチレン・メタクリル酸共重合体（メタ
クリル酸含有量１５重量％）のリチウム塩のアイオノマ
ー樹脂、ショアＤ硬度６５。* 1 (Surlyn 7930): trade name, ionomer resin of lithium salt of ethylene-methacrylic acid copolymer (methacrylic acid content: 15% by weight) manufactured by DuPont, USA, Shore D hardness 65.
【００２４】＊２（ＥＥＡ部分ケン化樹脂）：三井デュ
ポンポリケミカル株式会社製のエチレン・アクリル酸エ
チル共重合体のナトリウムイオン部分ケン化樹脂、ショ
アＤ硬度２８。* 2 (EEA partially saponified resin): Partially saponified resin of sodium ion of ethylene / ethyl acrylate copolymer manufactured by Du Pont-Mitsui Polychemicals Co., Ltd., Shore D hardness 28.
【００２５】＊３（ハイミラン１６０５）：商品名、三
井デュポンポリケミカル株式会社製のエチレン・メタク
リル酸共重合体のナトリウム塩のアイオノマー樹脂、シ
ョアＤ硬度６５。* 3 (Himilan 1605): trade name, ionomer resin of sodium salt of ethylene / methacrylic acid copolymer manufactured by Du Pont-Mitsui Polychemicals Co., Ltd., Shore D hardness 65.
【００２６】＊４（ハイミラン１７０６）：商品名、三
井デュポンポリケミカル株式会社製のエチレン・メタク
リル酸共重合体の亜鉛塩のアイオノマー樹脂、ショアＤ
硬度６４。* 4 (Himilan 1706): trade name, ionomer resin of zinc salt of ethylene / methacrylic acid copolymer manufactured by DuPont-Mitsui Polychemicals, Shore D
Hardness 64.
【００２７】＊５（ハイミランＡＭ７３１６）：商品
名、三井デュポンポリケミカル株式会社製のエチレン・
アクリル酸イソブチル・メタクリル酸三元共重合体の亜
鉛塩のアイオノマー樹脂、ショアＤ硬度２８。* 5 (Himilan AM7316): trade name, ethylene / polyethylene manufactured by DuPont-Mitsui Polychemicals, Inc.
An ionomer resin of zinc salt of isobutyl acrylate / methacrylic acid terpolymer, Shore D hardness 28.
【００２８】＊６（キャリー）：スイングロボット装置
を使用して、ウッド１番クラブによりクラブヘッド速度
４０ｍ／ｓｅｃで打って測定。* 6 (Carry): Measured by hitting with a No. 1 wood club at a club head speed of 40 m / sec using a swing robot device.
【００２９】＊７（打球感）および＊８（コントロール
性）：男子上級ゴルファーによる実打での評価。◎→極
めて良い、○→良い、×→悪い、とした。* 7 (hit feeling) and * 8 (controllability): Evaluation by actual hitting by a senior male golfer. ◎ → very good, ○ → good, × → bad.
【００３０】[0030]
【発明の効果】本発明のゴルフボールによれば、カバー
を２層構造とし、内層カバーを外層カバーよりも高硬度
に設定することにより、十分な飛距離が出て、しかも打
球感およびコントロール性が良好となるゴルフボールを
得ることができる。According to the golf ball of the present invention, the cover has a two-layer structure, and the inner layer cover is set to have a higher hardness than the outer layer cover, so that a sufficient flight distance can be obtained, and the shot feeling and controllability can be improved. Can be obtained.
【図１】単層構造のコアからなる本発明に係るゴルフボ
ールの断面構造図である。FIG. 1 is a sectional structural view of a golf ball according to the present invention comprising a single-layer core.
【図２】２層構造のコアからなる本発明に係るゴルフボ
ールの断面構造図である。FIG. 2 is a sectional structural view of a golf ball according to the present invention comprising a two-layer core.
１…コア ２…カバー ２ａ…内層カバー ２ｂ…外層カバー ２１…ソリッドコア ２１ａ…内層コア ２１ｂ…外層コア DESCRIPTION OF SYMBOLS 1 ... Core 2 ... Cover 2a ... Inner layer cover 2b ... Outer layer cover 21 ... Solid core 21a ... Inner layer core 21b ... Outer layer core
Claims (4)
層カバーの２層構造に構成されるゴルフボールにおい
て、 前記内層カバーは、ショアＤ硬度６０以上とし、前記外
層カバーは、内層カバーよりも硬度を低く設定し、ショ
アＤ硬度４５〜６５とすることを特徴とするゴルフボー
ル。1. A golf ball in which a cover for covering a core has a two-layer structure of an inner cover and an outer cover, wherein the inner cover has a Shore D hardness of 60 or more, and the outer cover is more than the inner cover. A golf ball having a low hardness and a Shore D hardness of 45 to 65.
合体のリチウム塩のアイオノマー樹脂を、基材樹脂の総
重量に対して５０重量％以上含有する樹脂組成物から形
成したことを特徴とするゴルフボール。2. The golf ball according to claim 1, wherein the inner layer cover comprises an ionomer resin of a lithium salt of an ethylene / (meth) acrylic acid copolymer in an amount of 50% by weight or more based on the total weight of the base resin. A golf ball formed from a resin composition containing the same.
とするゴルフボール。3. The golf ball according to claim 1, wherein the inner cover has a specific gravity of 1.0 or more.
ル。4. The golf ball according to claim 1, wherein said core has two layers.