JPH091751A - Packaging multilayer film - Google Patents
Packaging multilayer filmInfo
- Publication number
- JPH091751A JPH091751A JP15370995A JP15370995A JPH091751A JP H091751 A JPH091751 A JP H091751A JP 15370995 A JP15370995 A JP 15370995A JP 15370995 A JP15370995 A JP 15370995A JP H091751 A JPH091751 A JP H091751A
- Authority
- JP
- Japan
- Prior art keywords
- random copolymer
- ethylene
- density
- mfr
- butene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の技術分野】本発明は、包装用多層フィルムに関
し、さらに詳しくは、特に自動包装機による物品の包装
適性に優れ、かつ、低温ヒートシール性に優れた包装用
多層フィルムに関する。TECHNICAL FIELD The present invention relates to a multi-layer film for packaging, and more particularly to a multi-layer film for packaging which has excellent suitability for packaging articles by an automatic packaging machine and excellent low-temperature heat-sealing property.
【０００２】[0002]
【発明の技術的背景】近年、食品等の物品をフィルムで
包装することが盛んに行なわれており、使用されるフィ
ルムの種類も内容物によって多種類に亘っている。その
中でも、ポリエチレン系のフィルムは、強度や透明性に
優れ、また廃棄する際の問題点も少ないことから益々重
要な位置を占めてきている。また、フィルムも単層だけ
でなく複層構造のフィルムも多種類使用され、益々機能
が高められている。実際の包装作業では、多くの場合自
動包装機が採用され、作業効率を高める工夫がなされて
いる。BACKGROUND OF THE INVENTION In recent years, articles such as foods have been actively packaged with films, and the types of films used vary widely depending on the contents. Among them, polyethylene-based films are occupying an increasingly important position because they are excellent in strength and transparency and have few problems when discarded. Further, not only a single layer but also a multi-layered film is used in various kinds, and the function is further enhanced. In actual packaging work, automatic packaging machines are often used to improve work efficiency.
【０００３】しかしながら、包装用途の高度化に伴い、
フィルムそれ自体の性能をさらに高め、かつ包装時の作
業効率をさらに一層高めることが強く求められている。
特に自動包装機を使用した場合において、フィルムのカ
ット性の良さおよび高いヒートシール強度は、ユーザー
からの最も多い要望点である。However, with the sophistication of packaging applications,
There is a strong demand to further improve the performance of the film itself and further improve the work efficiency during packaging.
Particularly when an automatic packaging machine is used, good cuttability of the film and high heat seal strength are the most desired points from users.
【０００４】したがって、自動包装機によるカット性に
優れ、しかも、機械強度特性、透明性およびヒートシー
ル性、特に低温ヒートシール性に優れた包装用多層フィ
ルムの出現が望まれている。Therefore, it has been desired to develop a multilayer film for packaging which is excellent in cuttability by an automatic wrapping machine and is also excellent in mechanical strength properties, transparency and heat sealability, especially low temperature heat sealability.
【０００５】[0005]
【発明の目的】本発明は、自動包装機によるカット性に
優れ、しかも、機械強度特性、透明性および低温ヒート
シール性に優れた包装用多層フィルムを提供することを
目的としている。SUMMARY OF THE INVENTION It is an object of the present invention to provide a multi-layer film for packaging which is excellent in cuttability by an automatic packaging machine and is excellent in mechanical strength characteristics, transparency and low temperature heat sealability.
【０００６】[0006]
【発明の概要】本発明に係る包装用多層フィルムは、外
層、１または２以上の中間層、および内層の少なくとも
３層からなる多層フィルムであって、外層および内層
は、それぞれ独立して、（Ａ）溶融指数（ＭＦＲ）が
０．１〜１０ｇ／１０分であり、密度が０．８８０〜
０．９２５ｇ／ｃｍ3 であり、平均分子量分布（Ｍｗ／
Ｍｎ）が２以上３未満である、エチレンと炭素原子数４
〜１０のα- オレフィンとのランダム共重合体；４０〜
９０重量％と、（Ｂ）溶融指数（ＭＦＲ）が０．１〜５
ｇ／１０分であり、密度が０．９００〜０．９２５ｇ／
ｃｍ3 であり、平均分子量分布（Ｍｗ／Ｍｎ）が３〜６
である、エチレンと炭素原子数４〜１０のα- オレフィ
ンとのランダム共重合体；０〜４０重量％と、（Ｃ）溶
融指数（ＭＦＲ）が０．１〜２０ｇ／１０分であり、密
度が０．８５０〜０．９００ｇ／ｃｍ3 である、エチレ
ンと炭素原子数３〜１０のα- オレフィンとのランダム
共重合体；５〜３０重量％と、（Ｄ）密度が０．９１５
〜０．９３０ｇ／ｃｍ3 である高圧法ポリエチレン；５
〜２０重量％とからなる樹脂組成物で形成されており、
中間層は、（Ｅ）溶融指数（ＭＦＲ）が０．１〜５ｇ／
１０分であり、密度が０．８９０〜０．９２５ｇ／ｃｍ
3 である1-ブテン系（共）重合体；４０〜１００重量％
と、（Ｆ）溶融指数（ＭＦＲ）が０．１〜１００ｇ／１
０分であり、プロピレン含量が５０〜９８モル％である
エチレン・プロピレン・1-ブテンランダム共重合体；０
〜６０重量％とからなる樹脂または樹脂組成物で形成さ
れていることを特徴としている。SUMMARY OF THE INVENTION The packaging multilayer film according to the present invention is a multilayer film comprising at least three layers of an outer layer, one or more intermediate layers, and an inner layer, and the outer layer and the inner layer are each independently ( A) Melt index (MFR) is 0.1 to 10 g / 10 minutes, and density is 0.880 to
0.925 g / cm 3, which is the average molecular weight distribution (Mw /
Mn) is 2 or more and less than 3, ethylene and 4 carbon atoms
Random copolymer with 10-α-olefin; 40-
90% by weight and (B) melting index (MFR) of 0.1 to 5
g / 10 minutes and the density is 0.900 to 0.925 g /
cm 3 , and the average molecular weight distribution (Mw / Mn) is 3 to 6
A random copolymer of ethylene and an α-olefin having 4 to 10 carbon atoms; 0 to 40% by weight, (C) a melt index (MFR) of 0.1 to 20 g / 10 minutes, and a density Is 0.850 to 0.900 g / cm 3 , a random copolymer of ethylene and an α-olefin having 3 to 10 carbon atoms; 5 to 30% by weight, and (D) density is 0.915.
-0.930 g / cm 3 high pressure polyethylene; 5
Formed of a resin composition consisting of
The intermediate layer (E) has a melting index (MFR) of 0.1 to 5 g /
10 minutes, density 0.890-0.925 g / cm
1-butene (co) polymer which is 3 ; 40 to 100% by weight
And (F) melting index (MFR) is 0.1 to 100 g / 1
0 minutes, ethylene-propylene / 1-butene random copolymer having a propylene content of 50 to 98 mol%; 0
It is characterized in that it is formed of a resin or a resin composition consisting of ˜60% by weight.
【０００７】特に、縦方向と横方向のエルメンドルフ引
裂強度の比［横方向／縦方向］が９．１以下である包装
用多層フィルムが、自動包装機によるカット性に優れて
いる。In particular, a multi-layer film for packaging having a ratio of the Elmendorf tear strengths in the longitudinal direction and the transverse direction [transverse direction / longitudinal direction] of 9.1 or less is excellent in cuttability by an automatic packaging machine.
【０００８】[0008]
【発明の具体的な説明】以下、本発明に係る包装用多層
フィルムについて具体的に説明する。本発明に係る包装
用多層フィルムは、外層、１または２以上の中間層およ
び内層の少なくとも３層構造のフィルムで構成されてい
る。外層および内層に使用する樹脂組成と中間層を構成
する樹脂組成とは異なっている。DETAILED DESCRIPTION OF THE INVENTION The multilayer film for packaging according to the present invention will be specifically described below. The multilayer film for packaging according to the present invention is composed of a film having at least a three-layer structure of an outer layer, one or more intermediate layers and an inner layer. The resin composition used for the outer layer and the inner layer is different from the resin composition constituting the intermediate layer.
【０００９】各層を構成する樹脂ないし樹脂組成物、お
よびフィルムの構成について説明する。外層および内層 外層および内層は、それぞれ独立して、［Ｉ］エチレン
と炭素原子数４〜１０のα- オレフィンとからなるラン
ダム共重合体（Ａ）、［II］成分（Ａ）および（Ｂ）と
は異なるエチレンと炭素原子数３〜１０のα-オレフィ
ンとからなるランダム共重合体（Ｃ）、［III］ 高圧法
ポリエチレン（Ｄ）、および必要に応じて、［IV］成分
（Ａ）および（Ｃ）とは異なるエチレンと炭素原子数４
〜１０のα-オレフィンとからなるランダム共重合体
（Ｂ）を所定の割合で混合した樹脂組成物から構成され
ている。外層と内層との樹脂組成は、同一であってもよ
く、また互いに異なっていてもよい。The constitution of the resin or resin composition constituting each layer and the film will be described. Outer layer and inner layer The outer layer and the inner layer are each independently a random copolymer (A) consisting of [I] ethylene and an α-olefin having 4 to 10 carbon atoms, [II] components (A) and (B). A random copolymer (C) consisting of ethylene and an α-olefin having 3 to 10 carbon atoms different from that of [III] high-pressure polyethylene (D), and, if necessary, [IV] component (A) and Different from (C) ethylene and 4 carbon atoms
It is composed of a resin composition in which a random copolymer (B) consisting of 10 to 10 α-olefins is mixed at a predetermined ratio. The resin compositions of the outer layer and the inner layer may be the same or different from each other.
【００１０】［ランダム共重合体（Ａ）］本発明で用い
られるランダム共重合体（Ａ）は、エチレンと炭素原子
数４〜１０のα- オレフィンとからなるエチレン・α-
オレフィンランダム共重合体である。[Random Copolymer (A)] The random copolymer (A) used in the present invention is ethylene / α-containing ethylene and α-olefin having 4 to 10 carbon atoms.
It is an olefin random copolymer.
【００１１】エチレンとランダム共重合される炭素原子
数４〜１０のα- オレフィンとしては、具体的には、1-
ブテン、1-ペンテン、4-メチル-1- ペンテン、1-ヘキセ
ン、1-ヘプテン、1-オクテン、1-ノネン、1-デセンなど
が挙げられる。本発明においては、これらのα- オレフ
ィンは、単独で用いてもよく、また混合物として用いて
もよい。これらのα- オレフィンの中でも、特に炭素原
子数６〜８のα- オレフィンが好ましい。The α-olefin having 4 to 10 carbon atoms which is randomly copolymerized with ethylene is, specifically, 1-
Examples include butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene. In the present invention, these α-olefins may be used alone or as a mixture. Among these α-olefins, α-olefins having 6 to 8 carbon atoms are particularly preferable.
【００１２】ランダム共重合体（Ａ）中のα- オレフィ
ン含量は、通常０．５〜１５モル％、好ましくは１．０
〜１０モル％、さらに好ましくは３〜７モル％である。
本発明で用いられるランダム共重合体（Ａ）は、溶融指
数（ＭＦＲ）が０．１〜１０ｇ／１０分、好ましくは
０．５〜８ｇ／１０分、さらに好ましくは１．０〜６．
０ｇ／１０分であり、密度が０．８８０〜０．９２５ｇ
／ｃｍ3 、好ましくは０．８８０〜０．９１５ｇ／ｃｍ
3 、さらに好ましくは０．８８０〜０．９１０ｇ／ｃｍ
3 であり、平均分子量分布（Ｍｗ／Ｍｎ）が２以上３未
満、好ましくは２〜２．５である。The content of α-olefin in the random copolymer (A) is usually 0.5 to 15 mol%, preferably 1.0.
It is from 10 to 10 mol%, more preferably from 3 to 7 mol%.
The random copolymer (A) used in the present invention has a melting index (MFR) of 0.1 to 10 g / 10 minutes, preferably 0.5 to 8 g / 10 minutes, and more preferably 1.0 to 6.
It is 0 g / 10 minutes, and the density is 0.880 to 0.925 g.
/ Cm 3 , preferably 0.880 to 0.915 g / cm
3 , more preferably 0.880 to 0.910 g / cm
3 , and the average molecular weight distribution (Mw / Mn) is 2 or more and less than 3, preferably 2 to 2.5.
【００１３】上記溶融指数（ＭＦＲ）は、ＡＳＴＭ Ｄ-
１２３８に準拠して、測定温度１９０℃、荷重２１６０
ｇの条件下で測定された値であり、密度は、ＡＳＴＭ
Ｄ-１５０５に準拠して測定された値であり、平均分子
量分布（Ｍｗ／Ｍｎ）は、ゲルパーミエーションクロマ
トグラフィーによってｏ- ジクロロベンゼン溶媒を用
い、１３５℃で測定された重量平均分子量（Ｍｗ）と数
平均分子量（Ｍｎ）との比で表わされる値である。The melt index (MFR) is ASTM D-
According to 1238, measurement temperature 190 ℃, load 2160
It is a value measured under the condition of g, and the density is ASTM
The average molecular weight distribution (Mw / Mn) is a value measured according to D-1505, and the weight average molecular weight (Mw) is measured by gel permeation chromatography at 135 ° C. using an o-dichlorobenzene solvent. And the number average molecular weight (Mn).
【００１４】ランダム共重合体のα- オレフィン含量、
溶融指数、密度および分子量分布が各々上記のような範
囲にあるランダム共重合体を用いると、透明性、ヒート
シール強度特性等に優れるとともに、押出加工性に優
れ、またベタツキおよびブロッキングが生じにくい樹脂
組成物を得ることができる。ランダム共重合体（Ａ）の
みでは自動包装機によるカット性が悪いが、このランダ
ム共重合体（Ａ）に、次に述べるランダム共重合体
（Ｃ）、高圧法ポリエチレン（Ｄ）、および必要に応じ
てランダム共重合体（Ｂ）を配合することによって自動
包装機によるカット性を向上させることができる。Α-olefin content of the random copolymer,
When using a random copolymer having a melt index, a density and a molecular weight distribution in the above ranges, respectively, the resin is excellent in transparency, heat seal strength properties, etc., and is also excellent in extrusion processability, and is less likely to cause stickiness and blocking. A composition can be obtained. Although the random copolymer (A) alone has poor cuttability by an automatic packaging machine, this random copolymer (A) has the following random copolymer (C), high-pressure polyethylene (D), and if necessary. By blending the random copolymer (B) accordingly, the cuttability by an automatic packaging machine can be improved.
【００１５】また、本発明で用いられるランダム共重合
体（Ａ）の示差走査熱量計（ＤＳＣ）により測定される
融点は、６０〜１３０℃、好ましくは７５〜１２０℃、
さらに好ましくは８０〜１２０℃であることが、低温で
のヒートシール性を高める上で望ましい。この融点は、
昇温速度１０℃／分で測定されるランダム共重合体
（Ａ）の吸熱曲線において、１個ないし複数個の鋭いピ
ークのうち、極大ピーク値として求められる。The melting point of the random copolymer (A) used in the present invention measured by a differential scanning calorimeter (DSC) is 60 to 130 ° C, preferably 75 to 120 ° C.
More preferably, the temperature is 80 to 120 ° C. in order to enhance the heat sealability at low temperatures. This melting point is
In the endothermic curve of the random copolymer (A) measured at a temperature rising rate of 10 ° C./min, it is determined as the maximum peak value among one or a plurality of sharp peaks.
【００１６】上記のようなエチレンと炭素原子数４〜１
０のα- オレフィンとのランダム共重合体（Ａ）は、遷
移金属のメタロセン化合物と、有機アルミニウムオキシ
化合物と、必要に応じて有機アルミニウム化合物および
／または有機ホウ素化合物とからなる、いわゆるメタロ
セン触媒を用いて製造することができる。Ethylene and carbon atoms of 4 to 1 as described above
The random copolymer (A) with an α-olefin of 0 is a so-called metallocene catalyst composed of a metallocene compound of a transition metal, an organoaluminum oxy compound, and optionally an organoaluminum compound and / or an organoboron compound. Can be manufactured using.
【００１７】このような製造方法の一例を挙げると、ビ
ス（n-プロピルシクロペンタジエニル）ジルコニウムジ
クロリドとアルミノオキサンとの存在下で、エチレンと
炭素原子数４〜１０のα- オレフィンとを、気相または
スラリー状態で重合させることによって上記のようなラ
ンダム共重合体（Ａ）を得ることができる。As an example of such a production method, ethylene and α-olefin having 4 to 10 carbon atoms are combined with ethylene in the presence of bis (n-propylcyclopentadienyl) zirconium dichloride and aluminoxane. The random copolymer (A) as described above can be obtained by polymerizing in the gas phase or slurry state.
【００１８】上記のようにして得られたランダム重合体
（Ａ）は、直鎖状の分子構造を有し、狭い分子量分布と
組成分布を有することが特徴である。本発明において
は、ランダム共重合体（Ａ）は、ランダム共重合体
（Ａ）、ランダム共重合体（Ｂ）、ランダム共重合体
（Ｃ）および高圧法ポリエチレンの合計量１００重量％
に対して、４０〜９０重量％、好ましくは４５〜８０重
量％、さらに好ましくは５０〜８０重量％の割合で用い
られる。The random polymer (A) obtained as described above is characterized by having a linear molecular structure and having a narrow molecular weight distribution and composition distribution. In the present invention, the random copolymer (A) is 100% by weight of the total amount of the random copolymer (A), the random copolymer (B), the random copolymer (C) and the high-pressure polyethylene.
On the other hand, it is used in a proportion of 40 to 90% by weight, preferably 45 to 80% by weight, more preferably 50 to 80% by weight.
【００１９】［ランダム共重合体（Ｂ）］本発明で必要
に応じて用いられるランダム共重合体（Ｂ）は、エチレ
ンと炭素原子数４〜１０、好ましくは６〜８のα- オレ
フィンとからなるエチレン・α-オレフィンランダム共
重合体である。[Random Copolymer (B)] The random copolymer (B) optionally used in the present invention comprises ethylene and an α-olefin having 4 to 10 carbon atoms, preferably 6 to 8 carbon atoms. Is an ethylene / α-olefin random copolymer.
【００２０】エチレンとランダム共重合される炭素原子
数４〜１０のα- オレフィンとしては、具体的には、1-
ブテン、1-ペンテン、4-メチル-1- ペンテン、1-ヘキセ
ン、1-ヘプテン、1-オクテン、1-ノネン、1-デセンなど
が挙げられる。本発明においては、これらのα- オレフ
ィンは、単独で用いてもよく、また混合物として用いて
もよい。これらの中でも、炭素原子数６〜８のα- オレ
フィン、特に4-メチル-1- ペンテンが好ましい。The α-olefin having 4 to 10 carbon atoms which is randomly copolymerized with ethylene is, specifically, 1-
Examples include butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene. In the present invention, these α-olefins may be used alone or as a mixture. Of these, α-olefins having 6 to 8 carbon atoms, especially 4-methyl-1-pentene are preferable.
【００２１】本発明で用いられるランダム共重合体
（Ｂ）は、溶融指数（ＭＦＲ）が０．１〜５ｇ／１０
分、好ましくは０．５〜４ｇ／１０分、さらに好ましく
は０．５〜３ｇ／１０分であり、密度が０．９００〜
０．９２５ｇ／ｃｍ3 、好ましくは０．９０５〜０．９
２０ｇ／ｃｍ3 、さらに好ましくは０．９０５〜０．９
１８ｇ／ｃｍ3 であり、平均分子量分布（Ｍｗ／Ｍｎ）
が３〜６、好ましくは３〜５である。The random copolymer (B) used in the present invention has a melting index (MFR) of 0.1 to 5 g / 10.
Min, preferably 0.5 to 4 g / 10 min, more preferably 0.5 to 3 g / 10 min, and a density of 0.900 to
0.925 g / cm 3 , preferably 0.905-0.9
20 g / cm 3 , more preferably 0.905 to 0.9
18 g / cm 3 , average molecular weight distribution (Mw / Mn)
Is 3 to 6, preferably 3 to 5.
【００２２】ここにおける溶融指数、密度および平均分
子量分布は、上述したランダム共重合体（Ａ）と同様の
方法で測定された値である。溶融指数、密度および平均
分子量分布が上記のような範囲にあるランダム共重合体
を得るためには、ランダム共重合体中のα- オレフィン
含量を１〜８モル％、好ましくは２〜７モル％にするこ
とが必要である。The melting index, density and average molecular weight distribution herein are values measured by the same method as for the above-mentioned random copolymer (A). In order to obtain a random copolymer having a melting index, density and average molecular weight distribution in the above ranges, the α-olefin content in the random copolymer is 1 to 8 mol%, preferably 2 to 7 mol%. It is necessary to
【００２３】上記のようなエチレンと炭素原子数４〜１
０のα- オレフィンとのランダム共重合体（Ｂ）は、通
常のチーグラー触媒を用いて製造することができ、特に
マグネシウム化合物に担持されたチタン系固体触媒と有
機アルミニウム化合物との組み合わせからなる高活性触
媒によって得ることができる。Ethylene and carbon atoms of 4 to 1 as described above
The random copolymer (B) with an α-olefin of 0 can be produced by using an ordinary Ziegler catalyst, and in particular, it can be produced by combining a titanium solid catalyst supported on a magnesium compound with an organoaluminum compound. It can be obtained with an active catalyst.
【００２４】このような重合方法で製造されたランダム
共重合体（Ｂ）は、直鎖状の分子構造を有してはいる
が、上述したランダム共重合体（Ａ）と比べて、広い分
子量分布と広い組成分布とを有している。したがって、
樹脂組成物中に占めるランダム共重合体（Ｂ）の配合量
を、ランダム共重合体（Ａ）の配合量よりも少なくする
ことによって、フィルムの透明性を増すことができる。The random copolymer (B) produced by such a polymerization method has a linear molecular structure, but has a broader molecular weight than the above-mentioned random copolymer (A). It has a distribution and a broad composition distribution. Therefore,
By making the blending amount of the random copolymer (B) in the resin composition smaller than the blending amount of the random copolymer (A), the transparency of the film can be increased.
【００２５】本発明においては、ランダム共重合体
（Ｂ）は、ランダム共重合体（Ａ）、ランダム共重合体
（Ｂ）、ランダム共重合体（Ｃ）および高圧法ポリエチ
レン（Ｄ）の合計量１００重量％に対して、０〜４０重
量％、好ましくは０〜３０重量％の割合で用いられる。In the present invention, the random copolymer (B) is the total amount of the random copolymer (A), the random copolymer (B), the random copolymer (C) and the high-pressure polyethylene (D). It is used in a proportion of 0 to 40% by weight, preferably 0 to 30% by weight, based on 100% by weight.
【００２６】［ランダム共重合体（Ｃ）］本発明で用い
られるランダム共重合体（Ａ）は、エチレンと炭素原子
数３〜１０のα- オレフィンとからなるエチレン・α-
オレフィンランダム共重合体である。[Random Copolymer (C)] The random copolymer (A) used in the present invention is ethylene / α-containing ethylene and an α-olefin having 3 to 10 carbon atoms.
It is an olefin random copolymer.
【００２７】エチレンとランダム共重合される炭素原子
数３〜１０のα- オレフィンとしては、具体的には、プ
ロピレン、1-ブテン、1-ペンテン、4-メチル-1- ペンテ
ン、1-ヘキセン、1-ヘプテン、1-オクテン、1-ノネン、
1-デセンなどが挙げられる。本発明においては、これら
のα- オレフィンは、単独で用いてもよく、また混合物
として用いてもよい。これらのα- オレフィンの中で
も、炭素原子数３〜５のα- オレフィン、特に1-ブテン
が好ましい。Specific examples of the α-olefin having 3 to 10 carbon atoms which is randomly copolymerized with ethylene include propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene,
1-decene and the like. In the present invention, these α-olefins may be used alone or as a mixture. Among these α-olefins, α-olefins having 3 to 5 carbon atoms, particularly 1-butene are preferable.
【００２８】本発明で用いられるランダム共重合体
（Ｃ）は、溶融指数（ＭＦＲ）が０．１〜２０ｇ／１０
分、好ましくは０．３〜１０ｇ／１０分、さらに好まし
くは０．５〜７ｇ／１０分であり、密度が０．８５０〜
０．９００ｇ／ｃｍ3 、好ましくは０．８６０〜０．８
９０ｇ／ｃｍ3 、さらに好ましくは０．８６５〜０．８
９０ｇ／ｃｍ3 である。The random copolymer (C) used in the present invention has a melting index (MFR) of 0.1 to 20 g / 10.
Min, preferably 0.3 to 10 g / 10 min, more preferably 0.5 to 7 g / 10 min, and a density of 0.850 to
0.900 g / cm 3 , preferably 0.860 to 0.8
90 g / cm 3 , more preferably 0.865 to 0.8
90 g / cm 3 .
【００２９】ここにおける溶融指数、密度および平均分
子量分布は、上述したランダム共重合体（Ａ）と同様の
方法で測定された値である。溶融指数、密度および平均
分子量分布が上記のような範囲にあるランダム共重合体
を得るためには、ランダム共重合体中のα- オレフィン
含量を５〜２５モル％、好ましくは７〜２０モル％にす
ることが必要である。The melting index, density and average molecular weight distribution herein are values measured by the same method as for the above-mentioned random copolymer (A). In order to obtain a random copolymer having a melting index, density and average molecular weight distribution in the above ranges, the α-olefin content in the random copolymer is 5 to 25 mol%, preferably 7 to 20 mol%. It is necessary to
【００３０】本発明で用いられるランダム共重合体
（Ｃ）は、Ｘ線回折法で測定された結晶化度が低く、４
０％以下、好ましくは３０以下％、さらに２０％以下で
あることが望ましい。結晶化度が上記のような範囲にあ
るランダム共重合体（Ｃ）を用いると、優れた低温ヒー
トシール性を得ることができる。The random copolymer (C) used in the present invention has a low crystallinity measured by an X-ray diffraction method.
It is 0% or less, preferably 30% or less, and more preferably 20% or less. By using the random copolymer (C) having a crystallinity in the above range, excellent low temperature heat sealability can be obtained.
【００３１】上記のようなエチレンと炭素原子数３〜１
０のα- オレフィンとのランダム共重合体（Ｃ）は、通
常のチーグラーナッタ触媒を用いて製造することができ
る。たとえば、バナジウム化合物と有機アルミニウム化
合物とを組み合わせた触媒系の下で、エチレンと炭素原
子数３〜１０のα- オレフィンとを共重合することによ
り、ランダム共重合体（Ｃ）を得ることができる。Ethylene as above and C 3 -C 1
The random copolymer (C) with 0-α-olefin can be produced using a conventional Ziegler-Natta catalyst. For example, a random copolymer (C) can be obtained by copolymerizing ethylene and an α-olefin having 3 to 10 carbon atoms under a catalyst system in which a vanadium compound and an organoaluminum compound are combined. .
【００３２】本発明においては、ランダム共重合体
（Ｃ）は、ランダム共重合体（Ａ）、ランダム共重合体
（Ｂ）、ランダム共重合体（Ｃ）および高圧法ポリエチ
レン（Ｄ）の合計量１００重量％に対して、５〜３０重
量％、好ましくは５〜２５重量％、さらに好ましくは５
〜２０重量％の割合で用いられる。In the present invention, the random copolymer (C) is the total amount of the random copolymer (A), the random copolymer (B), the random copolymer (C) and the high-pressure polyethylene (D). 5 to 30% by weight, preferably 5 to 25% by weight, more preferably 5 to 100% by weight
It is used in a proportion of up to 20% by weight.
【００３３】［高圧法ポリエチレン（Ｄ）］本発明で用
いられる高圧法ポリエチレン（Ｄ）は、密度が０．９１
５〜０．９３０ｇ／ｃｍ3 、好ましくは０．９１８〜
０．９２４ｇ／ｃｍ3 の範囲にある。[High-pressure polyethylene (D)] The high-pressure polyethylene (D) used in the present invention has a density of 0.91.
5 to 0.930 g / cm 3 , preferably 0.918 to
It is in the range of 0.924 g / cm 3 .
【００３４】本発明で用いられる高圧法ポリエチレンと
しては、具体的には、エチレン単独重合体、またはエチ
レンと２０重量％以下の量の酢酸ビニル、アクリル酸エ
ステル等のビニルモノマーとの共重合体などが挙げられ
る。Specific examples of the high-pressure polyethylene used in the present invention include ethylene homopolymers and copolymers of ethylene with vinyl monomers such as vinyl acetate and acrylate in an amount of 20% by weight or less. Is mentioned.
【００３５】本発明で用いられる高圧法ポリエチレン
（Ｄ）の溶融指数（ＭＦＲ）が、０．１〜１０ｇ／１０
分、好ましくは０．３〜５ｇ／１０分である場合に、優
れた成形性、特にインフレーション成形におけるバブル
の安定性を示す。The high-pressure polyethylene (D) used in the present invention has a melting index (MFR) of 0.1 to 10 g / 10.
Min, preferably 0.3 to 5 g / 10 min, shows excellent moldability, especially bubble stability in inflation molding.
【００３６】本発明においては、高圧法ポリエチレン
（Ｄ）は、ランダム共重合体（Ａ）、ランダム共重合体
（Ｂ）、ランダム共重合体（Ｃ）および高圧法ポリエチ
レン（Ｄ）の合計量１００重量％に対して、５〜２０重
量％、好ましくは５〜１０重量％、さらに好ましくは７
〜１０重量％の割合で用いられる。In the present invention, the high-pressure polyethylene (D) is 100 in total of the random copolymer (A), the random copolymer (B), the random copolymer (C) and the high-pressure polyethylene (D). 5 to 20% by weight, preferably 5 to 10% by weight, more preferably 7
It is used in a proportion of 10 to 10% by weight.
【００３７】［外層および内層を形成する樹脂組成物］
本発明に係る包装用多層フィルムの外層および内層は、
上述したランダム共重合体（Ａ）、ランダム共重合体
（Ｃ）、高圧法ポリエチレン（Ｄ）および必要に応じて
ランダム共重合体（Ｂ）から、上述したような配合割合
で構成されている。[Resin Composition Forming Outer Layer and Inner Layer]
The outer layer and the inner layer of the packaging multilayer film according to the present invention,
The random copolymer (A), the random copolymer (C), the high-pressure polyethylene (D), and, if necessary, the random copolymer (B) are contained in the above-described mixing ratio.
【００３８】外層を形成する樹脂組成物と内層を形成す
る樹脂組成物は、上述した配合割合の範囲内であれば、
包装目的に応じて各々独立してその樹脂組成を任意に変
えることができる。If the resin composition forming the outer layer and the resin composition forming the inner layer are within the ranges of the above-mentioned mixing ratios,
The resin composition can be arbitrarily changed depending on the purpose of packaging.
【００３９】本発明において、上記の成分（Ａ）〜
（Ｄ）の各成分の割合が上述した配合割合の範囲内であ
る場合に、包装用多層フィルムとして必要な優れた透明
性、高いヒートシール強度、および自動包装機による優
れたカット性が得られる。また、このような多層フィル
ムで実際に物品を包装した後、仮に指で内方向に押し込
んでも容易に元の形状に復元することができる。In the present invention, the above components (A) to
When the ratio of each component of (D) is within the range of the above-mentioned mixing ratio, excellent transparency, high heat-sealing strength, and excellent cuttability by an automatic wrapping machine required for a packaging multilayer film can be obtained. . In addition, even if an article is actually wrapped with such a multilayer film and then pushed inward with a finger, the article can be easily restored to its original shape.
【００４０】本発明においては、外層および内層を構成
する樹脂組成物中に、上記成分（Ａ）、（Ｂ）、（Ｃ）
および（Ｄ）に加えて、各種の安定剤、配合剤、充填剤
等を、本発明の目的を損なわない範囲で添加することが
できる。特に、内容物の見栄えを良くするために防曇
剤、帯電防止剤等を添加したり、また内容物を保護する
ために紫外線防止剤等を添加することができ、酸化防止
剤、滑剤を添加することもできる。In the present invention, the above components (A), (B) and (C) are contained in the resin composition constituting the outer layer and the inner layer.
In addition to (D) and (D), various stabilizers, compounding agents, fillers and the like can be added within a range that does not impair the object of the present invention. In particular, an antifogging agent, an antistatic agent, etc. can be added to improve the appearance of the contents, and an ultraviolet ray inhibitor, etc. can be added to protect the contents, and an antioxidant and a lubricant are added. You can also do it.
【００４１】防曇剤としては、N-アシルアミノ酸または
その塩、アルキルエーテルカルボン酸塩等の陰イオン界
面活性剤、脂肪族アミン塩、カルボキシベタイン、イミ
ダゾリニウムベタイン、アミノカルボン酸塩等の両性界
面活性剤、非イオン界面活性剤、およびフッソ系の界面
活性剤などが挙げられる。Examples of the antifogging agent include N-acyl amino acids or salts thereof, anionic surfactants such as alkyl ether carboxylates, amphoteric amphoteric salts such as aliphatic amine salts, carboxybetaine, imidazolinium betaine and aminocarboxylates. Examples thereof include surfactants, nonionic surfactants, and fluorine-based surfactants.
【００４２】これらの中でも、非イオン系の界面活性剤
が好ましい。好ましく用いられる防曇剤としては、たと
えばグリセリン脂肪酸エステル、ソルビトール脂肪酸エ
ステル類が挙げられる。Of these, nonionic surfactants are preferable. Examples of preferably used antifogging agents include glycerin fatty acid ester and sorbitol fatty acid ester.
【００４３】防曇剤は、ランダム共重合体（Ａ）、ラン
ダム共重合体（Ｂ）、ランダム共重合体（Ｃ）および高
圧法ポリエチレン（Ｄ）の合計量１００重量部に対し
て、通常０．１〜１．５重量部の割合で用いられる。防
曇剤を上記のような割合で用いると、その優れた防曇効
果を発揮する。The antifogging agent is usually 0 per 100 parts by weight of the total amount of the random copolymer (A), the random copolymer (B), the random copolymer (C) and the high-pressure polyethylene (D). It is used in a ratio of 1 to 1.5 parts by weight. When the antifogging agent is used in the above proportion, its excellent antifogging effect is exhibited.
【００４４】中間層 中間層は、1-ブテン系（共）重合体（Ｅ）、および必要
に応じて、エチレン・プロピレン・1-ブテンランダム共
重合体（Ｆ）からなる樹脂または樹脂組成物から構成さ
れている。 Intermediate Layer The intermediate layer is made of a resin or resin composition comprising a 1-butene type (co) polymer (E) and, if necessary, an ethylene / propylene / 1-butene random copolymer (F). It is configured.
【００４５】［1-ブテン系（共）重合体（Ｅ）］本発明
で好ましく用いられる1-ブテン系（共）重合体（Ｅ）
は、1-ブテン単独重合体、または1-ブテン７５〜８５モ
ル％とプロピレン１５〜２５モル％とからなる1-ブテン
・プロピレン共重合体である。[1-Butene (co) polymer (E)] 1-butene (co) polymer (E) preferably used in the present invention
Is a 1-butene homopolymer or a 1-butene / propylene copolymer composed of 75 to 85 mol% of 1-butene and 15 to 25 mol% of propylene.
【００４６】本発明で用いられる1-ブテン系（共）重合
体（Ｅ）は、溶融指数（ＭＦＲ）が０．１〜５ｇ／１０
分、好ましくは０．５〜２ｇ／１０分であり、密度が
０．８９０〜０．９２５ｇ／ｃｍ3 、好ましくは０．８
９５〜０．９２０ｇ／ｃｍ3 である。この溶融指数は、
上述したランダム共重合体（Ａ）と同様の方法で測定し
た値である。The 1-butene type (co) polymer (E) used in the present invention has a melting index (MFR) of 0.1 to 5 g / 10.
Min, preferably 0.5 to 2 g / 10 min and a density of 0.890 to 0.925 g / cm 3 , preferably 0.8.
It is 95 to 0.920 g / cm 3 . This melting index is
It is a value measured by the same method as the above-mentioned random copolymer (A).
【００４７】上記のような1-ブテン系（共）重合体
（Ｅ）は、通常のチーグラーナッタ触媒を用いて製造す
ることができる。本発明においては、1-ブテン系（共）
重合体（Ｅ）は、1-ブテン系（共）重合体（Ｅ）および
エチレン・プロピレン・1-ブテンランダム共重合体
（Ｆ）の合計量１００重量％に対して、４０〜１００重
量％、好ましくは５０〜９０重量％、さらに好ましくは
５５〜９５重量％の割合で用いられる。The 1-butene type (co) polymer (E) as described above can be produced by using an ordinary Ziegler-Natta catalyst. In the present invention, 1-butene (co)
The polymer (E) is 40 to 100% by weight based on 100% by weight of the total amount of the 1-butene (co) polymer (E) and the ethylene / propylene / 1-butene random copolymer (F), It is preferably used in an amount of 50 to 90% by weight, more preferably 55 to 95% by weight.
【００４８】［エチレン・プロピレン・1-ブテンランダ
ム共重合体（Ｆ）］本発明で必要に応じて用いられるエ
チレン・プロピレン・1-ブテンランダム共重合体（Ｆ）
は、プロピレン含量が５０〜９８モル％、好ましくは７
０〜９７モル％であることが望ましい。[Ethylene / Propylene / 1-Butene Random Copolymer (F)] An ethylene / propylene / 1-butene random copolymer (F) optionally used in the present invention.
Has a propylene content of 50 to 98 mol%, preferably 7
It is preferably 0 to 97 mol%.
【００４９】本発明で用いられるエチレン・プロピレン
・1-ブテンランダム共重合体（Ｆ）は、溶融指数（ＭＦ
Ｒ）が０．１〜１００ｇ／１０分、好ましくは１〜３０
ｇ／１０分であり、密度が０．８９０〜０．９１０ｇ／
ｃｍ3 である。The ethylene / propylene / 1-butene random copolymer (F) used in the present invention has a melting index (MF).
R) is 0.1 to 100 g / 10 minutes, preferably 1 to 30
g / 10 minutes and the density is 0.890 to 0.910 g /
cm 3 .
【００５０】ここにおける溶融指数（ＭＦＲ）は、ＡＳ
ＴＭ Ｄ-１２３８に準拠して、測定温度２３０℃、荷重
２１６０ｇの条件下で測定された値であり、密度は、Ａ
ＳＴＭ Ｄ-１５０５に準拠して測定された値である。The melting index (MFR) here is AS
According to TM D-1238, it is a value measured under the conditions of a measurement temperature of 230 ° C. and a load of 2160 g, and the density is A
It is a value measured according to STM D-1505.
【００５１】上記のようなエチレン・プロピレン・1-ブ
テン共重合体（Ｆ）は、通常のチーグラーナッタ触媒を
用いて製造することができる。本発明においては、エチ
レン・プロピレン・1-ブテン共重合体（Ｆ）は、1-ブテ
ン系（共）重合体（Ｅ）およびエチレン・プロピレン・
1-ブテンランダム共重合体（Ｆ）の合計量１００重量％
に対して、０〜６０重量％、好ましくは１０〜５０重量
％、さらに好ましくは５〜４５重量％の割合で用いられ
る。The ethylene / propylene / 1-butene copolymer (F) as described above can be produced by using an ordinary Ziegler-Natta catalyst. In the present invention, the ethylene / propylene / 1-butene copolymer (F) is a 1-butene (co) polymer (E) or ethylene / propylene /
Total amount of 1-butene random copolymer (F) 100% by weight
On the other hand, it is used in a proportion of 0 to 60% by weight, preferably 10 to 50% by weight, more preferably 5 to 45% by weight.
【００５２】本発明において、上記の成分（Ｅ）および
（Ｆ）の各成分の割合が上述した配合割合の範囲に入る
場合に、自動包装機によるカット性に優れた多層フィル
ムが得られる。In the present invention, when the ratio of each of the above-mentioned components (E) and (F) falls within the range of the above-mentioned mixing ratio, a multilayer film excellent in cuttability by an automatic packaging machine can be obtained.
【００５３】本発明においては、上述した外層および内
層を構成する樹脂組成物と同様に、中間層を構成する樹
脂または樹脂組成物中に、上記成分（Ｅ）および（Ｆ）
に加えて、各種の安定剤、配合剤、充填剤等を、本発明
の目的を損なわない範囲で添加することができる。特
に、内容物の見栄えを良くするために防曇剤、帯電防止
剤等を添加したり、また内容物を保護するために紫外線
防止剤等を添加することができ、酸化防止剤、滑剤を添
加することもできる。In the present invention, the components (E) and (F) described above are added to the resin or resin composition constituting the intermediate layer in the same manner as the resin composition constituting the outer and inner layers described above.
In addition to the above, various stabilizers, compounding agents, fillers and the like can be added within a range not impairing the object of the present invention. In particular, an antifogging agent, an antistatic agent, etc. can be added to improve the appearance of the contents, and an ultraviolet ray inhibitor, etc. can be added to protect the contents, and an antioxidant and a lubricant are added. You can also do it.
【００５４】防曇剤については、上述した通りである。
中間層は、上述した1-ブテン系（共）重合体（Ｅ）およ
びエチレン・プロピレン・1-ブテンランダム共重合体
（Ｆ）が上記範囲内の量で配合された一層ないし二層以
上から構成されていてもよい。The antifogging agent is as described above.
The intermediate layer is composed of one or more layers in which the above-mentioned 1-butene-based (co) polymer (E) and ethylene / propylene / 1-butene random copolymer (F) are blended in an amount within the above range. It may have been done.
【００５５】包装用多層フィルム 本発明に係る包装用多層フィルムは、通常１０〜２０μ
ｍの厚さに成形され、その中間層は１〜５μｍ、外層お
よび内層は各々２〜８μｍの厚さに調整される。なお、
用途によっては、内層および／または外層のさらに外側
に別の樹脂層を形成することも可能である。 Multilayer Film for Packaging The multilayer film for packaging according to the present invention is usually 10 to 20 μm.
The thickness of the intermediate layer is adjusted to 1 to 5 μm, and the thickness of the outer layer and the inner layer is adjusted to 2 to 8 μm. In addition,
Depending on the application, it is possible to form another resin layer further outside the inner layer and / or the outer layer.
【００５６】このような多層フィルムは、各々の層を構
成する各成分を各種のブレンダーを用いて混合した後、
通常の成形法、すなわち押出機に複数のダイリップを備
えたインフレーションフィルム成形機、あるいはＴダイ
成形機等へ供給して製造される。Such a multilayer film is prepared by mixing the components constituting each layer using various blenders,
It is manufactured by supplying it to a usual molding method, that is, an inflation film molding machine having an extruder equipped with a plurality of die lips, a T-die molding machine, or the like.
【００５７】上記のようにして得られた多層フィルム
は、縦方向と横方向のエルメンドルフ引裂強度の比［横
方向／縦方向］が９．１以下である場合に、優れた包装
フィルムとして使用することができる。特にフィルムを
自動包装機に適用した場合、フィルムの横方向に走るナ
イフによってカットされることから、カット性の良しあ
しは縦方向と横方向のエルメンドルフ引裂強度の比によ
って評価することができる。このエルメンドルフ引裂強
度の比が９．１以下であれば、自動包装機によるカット
性は良好であると判断できる。The multilayer film obtained as described above is used as an excellent packaging film when the ratio of the Elmendorf tear strength in the machine direction to the transverse direction [machine direction / machine direction] is 9.1 or less. be able to. In particular, when the film is applied to an automatic wrapping machine, it is cut by a knife running in the lateral direction of the film, and thus the goodness of cut property can be evaluated by the ratio of the Elmendorf tear strength in the longitudinal direction and the transverse direction. When the ratio of the Elmendorf tear strength is 9.1 or less, it can be judged that the cutting property by the automatic packaging machine is good.
【００５８】本発明に係る包装用多層フィルムは、この
エルメンドルフ引裂強度の比［横方向／縦方向］が９．
１以下で、自動包装機によるカットが容易であり、しか
も、ハイスピードでの連続包装作業が可能である。In the packaging multilayer film according to the present invention, the Elmendorf tear strength ratio [transverse direction / longitudinal direction] is 9.
When it is 1 or less, it is easy to cut by an automatic packaging machine, and moreover, continuous packaging work at high speed is possible.
【００５９】なお、エルメンドルフ引裂強度は、ＪＩＳ
Ｚ-１７０２に準拠した方法て測定する。また、本発明
に係る包装用多層フィルムは、透明性に優れ、ヘイズ値
が通常２．０％以下である。The Elmendorf tear strength is JIS
It is measured by a method according to Z-1702. Moreover, the packaging multilayer film according to the present invention has excellent transparency and a haze value of usually 2.0% or less.
【００６０】さらに、本発明に係る包装用多層フィルム
は、実施例において後述する指押し復元性に優れ、初期
復元率が７０％以上であり、残留歪が５．５ｍｍ以下で
ある。Further, the multilayer film for packaging according to the present invention is excellent in the finger-pushing restoration property described later in Examples, the initial restoration rate is 70% or more, and the residual strain is 5.5 mm or less.
【００６１】さらにまた、本発明に係る包装用多層フィ
ルムは、低温シール性に優れ、９０℃でヒートシールし
たフィルムのシール強度が１００ｋｇ／ｃｍ2 以上であ
る。Furthermore, the multilayer film for packaging according to the present invention is excellent in low-temperature sealing property, and the sealing strength of the film heat-sealed at 90 ° C. is 100 kg / cm 2 or more.
【００６２】[0062]
【発明の効果】本発明によれば、自動包装機によるカッ
ト性に優れ、しかも、機械強度特性、透明性および低温
ヒートシール性に優れた包装用多層フィルムを提供する
ことができる。According to the present invention, it is possible to provide a multilayer film for packaging which is excellent in cuttability by an automatic wrapping machine and is excellent in mechanical strength characteristics, transparency and low temperature heat sealability.
【００６３】また、本発明に係る包装用多層フィルム
は、包装後に、たとえば指で内容物側へ押し込んでもそ
の後のフィルムの復元性がよく、後述する初期復元率が
７０％以上を示し、このフィルムで包装された製品を展
示しても見栄えをフィルムにより損なうことはない。In addition, the packaging multilayer film according to the present invention has good restorability of the film even after being pushed to the contents side with a finger after packaging, and has an initial restoration rate of 70% or more, which will be described later. Even if the product packaged with is displayed, the appearance will not be spoiled by the film.
【００６４】さらにまた、本発明に係る包装用多層フィ
ルムは、上述したように、自動包装機にかけたとき、優
れたカット性を示すことから、包装効率が高い。したが
って、上記のような効果を有する、本発明に係る包装用
多層フィルムは、食料品、日用品等の包装に適してい
る。たとえば、食品を入れたトレーを自動包装機に連続
して供給し、本発明に係る多層フィルムで包装した場合
には、上記のような優れた効果が得られる。Furthermore, the packaging multi-layer film according to the present invention, as described above, exhibits excellent cutting properties when applied to an automatic packaging machine, and therefore has high packaging efficiency. Therefore, the multilayer film for packaging according to the present invention, which has the above effects, is suitable for packaging food products, daily necessities and the like. For example, when a tray containing food is continuously supplied to an automatic packaging machine and is packaged with the multilayer film according to the present invention, the above excellent effects can be obtained.
【００６５】以下、本発明を実施例により説明するが、
本発明は、これらの実施例に限定されるものではない。The present invention will be described below with reference to examples.
The present invention is not limited to these examples.
【００６６】[0066]
【実施例１〜５】まず、次の７種類の樹脂を準備した。（Ａ）成分 （Ａ−１）メタロセン触媒を用いて調製したエチレン・
1-ヘキセンランダム共重合体 エチレン／1-ヘキセン（モル比）：９４．９／５．１ ＭＦＲ ： ４．０ｇ／１０分 密 度 ： ０．９０５ｇ／ｃｍ3 Ｍｗ／Ｍｎ ： ２．１（Ｂ）成分 （Ｂ−１）エチレン・1-ブテン・4-メチル-1- ペンテン
ランダム共重合体エチレン／1-ブテン／4-メチル-1- ペ
ンテン（モル比）：９４．８／４．０／１．２ ＭＦＲ ： ２．０ｇ／１０分 密 度 ： ０．９０５ｇ／ｃｍ3 Ｍｗ／Ｍｎ ： ３．５（Ｃ）成分 （Ｃ−１）エチレン・1-ブテンランダム共重合体 エチレン／1-ブテン（モル比）：８８／１２ ＭＦＲ ： ０．５ｇ／１０分 密 度 ： ０．８８５ｇ／ｃｍ3 結晶化度 ： ８％ （Ｃ−２）エチレン・1-ブテンランダム共重合体 エチレン／1-ブテン（モル比）：８２／１８ ＭＦＲ ： ０．５ｇ／１０分 密 度 ： ０．８６５ｇ／ｃｍ3 結晶化度 ： ０％（Ｄ）成分 （Ｄ−１）高圧法で製造したエチレン単独重合体 ＭＦＲ ： ０．６ｇ／１０分 密 度 ： ０．９２２ｇ／ｃｍ3 （Ｅ）成分 （Ｅ−１）1-ブテン・プロピレンランダム共重合体 1-ブテン／プロピレン（モル比）：７８／２２ ＭＦＲ ： １．０ｇ／１０分 密 度 ： ０．９００ｇ／ｃｍ3 （Ｆ）成分 （Ｆ−１）エチレン・プロピレン・1-ブテンランダム共
重合体 エチレン／プロピレン／1-ブテン（モル比）： ３．２／９５．３／１．５ ＭＦＲ ： ７．０ｇ／１０分 密 度 ： ０．９１０ｇ／ｃｍ3 次に、上記の樹脂を用いて、第１表に記載した組成の樹
脂組成物を調製し、５種類の３層構造のインフレーショ
ンフィルムを製造した。フィルム全体の厚さは１５μ
ｍ、内層と中間層と外層との厚み比は、２：１：２とし
た。Examples 1 to 5 First, the following seven kinds of resins were prepared. (A) Component (A-1) Ethylene prepared using a metallocene catalyst
1-hexene random copolymer ethylene / 1-hexene (molar ratio): 94.9 / 5.1 MFR: 4.0 g / 10 min Density: 0.905 g / cm 3 Mw / Mn: 2.1 (B ) Component (B-1) ethylene / 1-butene-4-methyl-1-pentene random copolymer ethylene / 1-butene / 4-methyl-1-pentene (molar ratio): 94.8 / 4.0 / 1.2 MFR: 2.0 g / 10 minutes Density: 0.905 g / cm 3 Mw / Mn: 3.5 (C) Component (C-1) ethylene / 1-butene random copolymer ethylene / 1-butene (Molar ratio): 88/12 MFR: 0.5 g / 10 min Density: 0.885 g / cm 3 Crystallinity: 8% (C-2) Ethylene / 1-butene random copolymer Ethylene / 1-butene (Molar ratio): 82/18 MFR: 0.5 g / 10 minutes Density: 0.865 g / c m 3 Crystallinity: 0% (D) Component (D-1) Ethylene homopolymer produced by high pressure method MFR: 0.6 g / 10 min Density: 0.922 g / cm 3 (E) Component (E- 1) 1-butene / propylene random copolymer 1-butene / propylene (molar ratio): 78/22 MFR: 1.0 g / 10 minutes Density: 0.900 g / cm 3 (F) component (F-1) Ethylene / propylene / 1-butene random copolymer Ethylene / propylene / 1-butene (molar ratio): 3.2 / 95.3 / 1.5 MFR: 7.0 g / 10 min Density: 0.910 g / cm 3 Next, using the above resin, a resin composition having the composition shown in Table 1 was prepared to produce five types of blown films having a three-layer structure. The total film thickness is 15μ
m, and the thickness ratio of the inner layer, the intermediate layer, and the outer layer was 2: 1: 2.
【００６７】上記のようにして得られたフィルムのヘイ
ズ、エルメンドルフ引裂強度、指押し復元性およびヒー
トシール強度を下記の方法に従って測定した。結果を第
１表に示す。 （１）ヘイズ：ＡＳＴＭ Ｄ-１００３に準拠した方法で
測定した。 （２）エルメンドルフ引裂強度：ＪＩＳ Ｚ-１７０２に
準拠した方法で縦方向および横方向の強度を測定した。 （３）指押し復元性：図１に示すように、フィルムの固
定が可能な内径１００ｍｍの筒状装置１にフィルム２を
展張し、そのフィルム２中心部に先端が半球状になった
棒状の治具（Ｒ＝１／２インチ）３を速度１００ｍｍ／
分で押し当て、２０ｍｍの距離だけ変形させた。この操
作を１０回繰り返した。The haze, Elmendorf tear strength, finger-pushing resilience and heat seal strength of the film obtained as described above were measured according to the following methods. The results are shown in Table 1. (1) Haze: Measured by a method according to ASTM D-1003. (2) Elmendorf tear strength: longitudinal and transverse strengths were measured by a method based on JIS Z-1702. (3) Finger-push restoration property: As shown in FIG. 1, a film 2 is spread on a tubular device 1 having an inner diameter of 100 mm capable of fixing the film, and a hemispherical rod-shaped tip is formed at the center of the film 2. Jig (R = 1/2 inch) 3 speed 100mm /
It was pressed in minutes and deformed by a distance of 20 mm. This operation was repeated 10 times.
【００６８】最初の応力−歪曲線より初期復元率を求
め、１０回目の応力−歪曲線より残留歪量を求め、復元
性の評価値とした。この応力−歪曲線の例を図２に示
す。 （４）ヒートシール強度（低温ヒートシール性の指
標）：ＪＩＳ Ｚ-１７０７に準拠した方法に従い、９０
℃にてヒートシールを行ない、その剥離強度を測定し、
ヒートシール強度とした。The initial recovery rate was calculated from the first stress-strain curve, and the residual strain amount was calculated from the tenth stress-strain curve, which was used as the evaluation value of the recoverability. An example of this stress-strain curve is shown in FIG. (4) Heat seal strength (index of low temperature heat sealability): 90 according to the method based on JIS Z-1707
Heat seal at ℃, measure the peel strength,
The heat seal strength was used.
【００６９】[0069]
【比較例１〜３】前記の各樹脂を用い、第１表に示す組
成の樹脂組成物を調製し、実施例１と同様の方法で単層
インフレーションフィルムおよび２種類の３層構造のイ
ンフレーションフィルムを製造した。得られたフィルム
の物性を実施例１と同様にして測定した。その結果を第
１表に示す。[Comparative Examples 1 to 3] A resin composition having the composition shown in Table 1 was prepared using each of the above resins, and a single layer inflation film and two types of three layer inflation film were prepared in the same manner as in Example 1. Was manufactured. The physical properties of the obtained film were measured in the same manner as in Example 1. Table 1 shows the results.
【００７０】[0070]
【表１】 [Table 1]
【図１】図１は、本発明に係るフィルムの指押し復元性
を評価するために行なった実験方法の模式図である。FIG. 1 is a schematic diagram of an experimental method performed for evaluating the finger-pressing restoring property of the film according to the present invention.
【図２】指押し復元性を評価するために行なった実験に
おける応力−歪曲線の一例を示す図である。FIG. 2 is a diagram showing an example of a stress-strain curve in an experiment conducted to evaluate the finger-pushing restoring property.
１ ・・・・・ フィルムの固定が可能な筒状装置 ２ ・・・・・ フィルム ３ ・・・・・ 棒状の治具 1 ・ ・ ・ Cylindrical device capable of fixing film 2 ・ ・ ・ Film 3 ・ ・ ・ ・ ・ Rod jig
Claims (2)
層の少なくとも３層からなる多層フィルムであって、 外層および内層は、それぞれ独立して、（Ａ）溶融指数
（ＭＦＲ）が０．１〜１０ｇ／１０分であり、 密度が０．８８０〜０．９２５ｇ／ｃｍ3 であり、 平均分子量分布（Ｍｗ／Ｍｎ）が２以上３未満である、 エチレンと炭素原子数４〜１０のα- オレフィンとのラ
ンダム共重合体；４０〜９０重量％と、（Ｂ）溶融指数
（ＭＦＲ）が０．１〜５ｇ／１０分であり、 密度が０．９００〜０．９２５ｇ／ｃｍ3 であり、 平均分子量分布（Ｍｗ／Ｍｎ）が３〜６である、 エチレンと炭素原子数４〜１０のα- オレフィンとのラ
ンダム共重合体；０〜４０重量％と、（Ｃ）溶融指数
（ＭＦＲ）が０．１〜２０ｇ／１０分であり、 密度が０．８５０〜０．９００ｇ／ｃｍ3 である、 エチレンと炭素原子数３〜１０のα- オレフィンとのラ
ンダム共重合体；５〜３０重量％と、（Ｄ）密度が０．
９１５〜０．９３０ｇ／ｃｍ3 である高圧法ポリエチレ
ン；５〜２０重量％とからなる樹脂組成物で形成されて
おり、 中間層は、（Ｅ）溶融指数（ＭＦＲ）が０．１〜５ｇ／
１０分であり、 密度が０．８９０〜０．９２５ｇ／ｃｍ3 である1-ブテ
ン系（共）重合体；４０〜１００重量％と、（Ｆ）溶融
指数（ＭＦＲ）が０．１〜１００ｇ／１０分であり、 プロピレン含量が５０〜９８モル％であるエチレン・プ
ロピレン・1-ブテンランダム共重合体；０〜６０重量％
とからなる樹脂または樹脂組成物で形成されていること
を特徴とする包装用多層フィルム。1. A multilayer film comprising at least three layers of an outer layer, one or more intermediate layers, and an inner layer, wherein the outer layer and the inner layer each independently have (A) a melting index (MFR) of 0. 1 to 10 g / 10 minutes, the density is 0.880 to 0.925 g / cm 3 , and the average molecular weight distribution (Mw / Mn) is 2 or more and less than 3, ethylene and α having 4 to 10 carbon atoms -Random copolymer with olefin; 40 to 90% by weight, (B) Melt index (MFR) is 0.1 to 5 g / 10 min, and density is 0.900 to 0.925 g / cm 3 . , An average molecular weight distribution (Mw / Mn) of 3 to 6, a random copolymer of ethylene and an α-olefin having 4 to 10 carbon atoms; 0 to 40% by weight, and (C) a melting index (MFR). Is 0.1 to 20 g / 10 minutes, and the density is 0. A 850~0.900g / cm 3, a random copolymer of ethylene and having 3 to 10 carbon atoms α- olefin; and 5 to 30% by weight, (D) Density 0.
915 to 0.930 g / cm 3 of high-pressure process polyethylene; formed from a resin composition of 5 to 20% by weight, and the intermediate layer has (E) a melting index (MFR) of 0.1 to 5 g /
10-minute, 1-butene (co) polymer having a density of 0.890 to 0.925 g / cm 3 ; 40 to 100% by weight, and (F) melting index (MFR) of 0.1 to 100 g. / 10 minutes, the propylene content is 50-98 mol% ethylene propylene 1-butene random copolymer; 0-60 wt%
A multilayer film for packaging, which is formed of a resin or a resin composition comprising
の比［横方向／縦方向］が、９．１以下であることを特
徴とする請求項１に記載の包装用多層フィルム。2. The multilayer film for packaging according to claim 1, wherein the ratio of the Elmendorf tear strength in the machine direction to the transverse direction [machine direction / machine direction] is 9.1 or less.