JPH09122657A - Mineral additive for water purifier and its preparation - Google Patents
Mineral additive for water purifier and its preparationInfo
- Publication number
- JPH09122657A JPH09122657A JP28158395A JP28158395A JPH09122657A JP H09122657 A JPH09122657 A JP H09122657A JP 28158395 A JP28158395 A JP 28158395A JP 28158395 A JP28158395 A JP 28158395A JP H09122657 A JPH09122657 A JP H09122657A
- Authority
- JP
- Japan
- Prior art keywords
- calcium
- magnesium
- water
- carbonate
- mineral additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は浄水器用ミネラル添
加剤、特に、浄水器や整水器等で水を浄化する際、水に
CaやMgのミネラル分を添加するための浄水器用ミネ
ラル添加剤及びその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a mineral additive for a water purifier, and more particularly, a mineral additive for a water purifier for adding Ca or Mg minerals to water when purifying the water with a water purifier or a water conditioner. And a manufacturing method thereof.
【0002】[0002]
【従来の技術】従来より、水道水をおいしい水にした
り、健康や美容に良い水に変えることを目的として、浄
水器や整水器等を用いて、遊離塩素の除去だけでなくカ
ルシウムやマグネシウムなどのミネラルを添加すること
が行われている。この種のミネラル添加剤としては、通
常、サンゴ石、貝化石、麦飯石等の天然石を粉砕して粒
子化したものが採用されている。2. Description of the Related Art Conventionally, in order to make tap water delicious water or change it into water that is good for health and beauty, water purifiers and water conditioners are used to remove not only free chlorine but also calcium and magnesium. Minerals such as are being added. As mineral additives of this type, those obtained by crushing natural stones such as coral stones, fossil shells and barley stones into particles are usually employed.
【0003】[0003]
【発明が解決しようとする課題】しかしながら、従来の
ミネラル添加剤では、これらの天然石の水に対する溶解
度が非常に低いため、通水によってカルシウムやマグネ
シウムなどのミネラルイオンが、ほとんど溶出しないと
いう根本的な問題があった。このことは、例えば、国民
生活センターの「ミネラルや制菌をうたった浄水器・整
水器の商品テスト結果」(平成6年11月)でも指摘さ
れている。従って、本発明の主目的は、浄水器及び整水
器にセットし通水するだけで水にカルシウムやマグネシ
ウムなどのミネラル分を添加できるようにすることにあ
る。However, with conventional mineral additives, since the solubility of these natural stones in water is extremely low, it is a fundamental problem that mineral ions such as calcium and magnesium hardly elute due to water flow. There was a problem. This has been pointed out, for example, in the “Results of product tests of water purifiers / water purifiers that claim minerals and bacteriostatics” (November 1994) of the National Living Center. Therefore, a main object of the present invention is to enable addition of minerals such as calcium and magnesium to water simply by setting them in a water purifier and a water conditioner and passing water.
【0004】[0004]
【課題を解決するための手段】本発明は、前記課題を解
決するための手段として、カルシウムイオン及びマグネ
シウムイオンなどミネラルイオンの供給源として、水に
対し適度の溶解度を示すカルシウム化合物とマグネシウ
ム化合物を用い、これらを所定の割合で配合して造粒及
び/又は成形し、その造粒成形体をミネラル添加剤とし
て用いるようにしたものである。As a means for solving the above problems, the present invention provides a calcium compound and a magnesium compound having a suitable solubility in water as a source of mineral ions such as calcium ions and magnesium ions. It is used by mixing these at a predetermined ratio, granulating and / or molding, and using the granulated molded product as a mineral additive.
【0005】[0005]
【発明の実施の形態】即ち、本発明に係る浄水器用ミネ
ラル添加剤は、25℃における溶解度が0.05〜1.0
0g/100ml の範囲内にあるカルシウム化合物及び
マグネシウム化合物を主成分とする造粒成形体で構成さ
れる。BEST MODE FOR CARRYING OUT THE INVENTION That is, the mineral additive for a water purifier according to the present invention has a solubility of 0.05 to 1.0 at 25 ° C.
It is composed of a granulated product containing calcium compounds and magnesium compounds as main components in the range of 0 g / 100 ml.
【0006】前記カルシウム化合物及びマグネシウム化
合物の25℃における溶解度が0.05〜1.00g/1
00ml としたのは、それらの溶解度が0.05g/10
0ml未満では、通水時にほとんど溶解しないためミネラ
ル添加剤としての使用効果がなく、また、1.00g/
100mlを超えると、通水初期に短時間で溶解してしま
うためミネラル添加剤としての使用効果が持続しないか
らでる。The solubility of the calcium compound and the magnesium compound at 25 ° C. is 0.05 to 1.00 g / 1.
00 ml means that their solubility is 0.05 g / 10
If it is less than 0 ml, it hardly dissolves when passing water, so there is no effect as a mineral additive, and 1.00 g /
If it exceeds 100 ml, it will dissolve in a short time at the beginning of water flow and the effect of use as a mineral additive will not last.
【0007】前記カルシウム化合物としては、炭酸カル
シウム、硫酸カルシウム、酸化カルシウム、水酸化カル
シウムなどが好適であり、前記マグネシウム化合物とし
ては、炭酸マグネシウム、塩基性炭酸マグネシウム及び
亜硫酸マグネシウムなどが好適であるが、これらに限定
されるものではなく、要は、前記範囲内の溶解度を持つ
ものであれば良い。また、カルシウムイオン供給源とし
て、必ずしも前記カルシウム化合物を単独で使用する必
要は無く、2種以上を組み合わせて使用しても良い。こ
のことは、マグネシウムイオン供給源としてのマグネシ
ウム化合物についても適用される。The calcium compound is preferably calcium carbonate, calcium sulfate, calcium oxide, calcium hydroxide or the like, and the magnesium compound is preferably magnesium carbonate, basic magnesium carbonate or magnesium sulfite. It is not limited to these, and the essential point is that it has a solubility within the above range. Further, as the calcium ion supply source, it is not always necessary to use the calcium compound alone, and two or more kinds may be used in combination. This also applies to magnesium compounds as a source of magnesium ions.
【0008】前記カルシウム化合物とマグネシウム化合
物の配合比は、カルシウムがマグネシウムの2倍〜5倍
程度溶出するように配合するのが望ましい。好ましい実
施態様においては、ミネラル添加剤は、炭酸カルシウム
25%〜40%、硫酸カルシウム25%〜40%、塩基
性炭酸マグネシウム15%〜30%の重量比で配合され
る。The mixing ratio of the calcium compound and the magnesium compound is preferably such that calcium elutes about 2 to 5 times that of magnesium. In a preferred embodiment, the mineral additive is blended in a weight ratio of 25% to 40% calcium carbonate, 25% to 40% calcium sulfate, and 15% to 30% basic magnesium carbonate.
【0009】また、前記浄水器用ミネラル添加剤は、必
要に応じて、バインダを添加しても良い。このバインダ
ーとしては、通常造粒に使用される一般的なもので良
い。A binder may be added to the water purifier mineral additive, if necessary. As this binder, a general binder usually used for granulation may be used.
【0010】前記バインダの添加量は、通常、主成分の
全重量に対して1〜10%にあたる量が好適である。こ
れは、バインダの量が1%以下では長期にわたって形状
を維持させることが困難であり、10%を越えると製造
コストが高くなるだけでなく、主成分の溶解速度が低下
し過ぎてミネラル添加効果が低下するからである。The amount of the binder added is preferably 1 to 10% with respect to the total weight of the main components. This is because if the amount of the binder is 1% or less, it is difficult to maintain the shape for a long period of time, and if it exceeds 10%, not only the manufacturing cost becomes high, but also the dissolution rate of the main component is lowered too much and the effect of mineral addition is reduced. Is reduced.
【0011】前記浄水器用ミネラル添加剤の造粒成形方
法としては、押出造粒、撹拌造粒等の造粒方法、並びに
一軸プレス成形、CIP成形等の成形方法を採用するこ
とができる。As the granulation molding method of the mineral additive for water purifier, granulation methods such as extrusion granulation, stirring granulation and the like, and molding methods such as uniaxial press molding and CIP molding can be adopted.
【0012】この発明を用いれば、浄水器、整水器等に
利用するための高ミネラル添加能力をもった造粒体及び
成形体を容易に製造することができ、浄水された水にC
aやMgのミネラル分を添加し、水道水をおいしい水あ
るいは健康美容に良い水とすることができる。By using the present invention, it is possible to easily produce granules and compacts having a high mineral addition ability for use in water purifiers, water conditioners, etc.
By adding minerals such as a and Mg, tap water can be made delicious water or water good for health and beauty.
【0013】[0013]
【実施例1】原料として市販の高純度の塩基性炭酸マグ
ネシウム、炭酸カルシウム及び硫酸カルシウムを用い、
これらを塩基性炭酸マグネシウム25%、炭酸カルシウ
ム37.5%、硫酸カルシウム37.5%の重量比で配合
し、これにバインダとしてアクリル酸エステルを用い、
そのエマルジョン液をその固形分が配合粉に対して2%
になるように添加した後、撹拌造粒機で造粒して直径1
〜10mmの造粒成形体を得、これをミネラル添加剤の試
料Aとした。Example 1 Using commercially available high-purity basic magnesium carbonate, calcium carbonate and calcium sulfate as raw materials,
These are blended in a weight ratio of 25% basic magnesium carbonate, 37.5% calcium carbonate, and 37.5% calcium sulfate, and an acrylic ester is used as a binder in the mixture.
The emulsion liquid has a solid content of 2% based on the blended powder.
And then add granules with a stirring granulator to give a diameter of 1
A granulated molded body of 10 mm was obtained, and this was designated as sample A of the mineral additive.
【0014】[0014]
【実施例2】塩基性炭酸マグネシウム25%、炭酸カル
シウム37.5%、硫酸カルシウム37.5%の重量比で
配合し、これにバインダとしてメチルセルロース水溶液
をその固形分が配合粉に対して2%になるように添加
し、混合した後、押出成形して直径2mm,長さ3〜8mm
の造粒成形体を得、これをミネラル添加剤の試料Bとし
た。Example 2 Basic magnesium carbonate 25%, calcium carbonate 37.5%, and calcium sulfate 37.5% were mixed in a weight ratio, and a methylcellulose aqueous solution as a binder was added to the mixed powder in a solid content of 2%. So that it is added, mixed and extruded to a diameter of 2 mm and a length of 3 to 8 mm.
The granulated molded product of was obtained, and this was used as sample B of the mineral additive.
【0015】[0015]
【比較例】比較のため、小粒のサンゴ石(2〜5mm、試
料C)と小粒の貝化石(2〜5mm、試料D)をそれぞれ
ミネラル添加剤として用意した。Comparative Example For comparison, small coral stones (2 to 5 mm, sample C) and small shell fossils (2 to 5 mm, sample D) were prepared as mineral additives.
【0016】前記各試料50gをそれぞれ塩化ビニール
製カートリッジに投入し、水道水を5L/minで通水さ
せ、通水後の水中のCa濃度(ppm)及びMg濃度
(ppm)を測定した。カルシウムについての結果を表
1に、マグネシウムについての結果を表2にそれぞれ示
す。50 g of each sample was placed in a vinyl chloride cartridge, tap water was passed at 5 L / min, and Ca concentration (ppm) and Mg concentration (ppm) in the water after passing water were measured. The results for calcium are shown in Table 1 and the results for magnesium are shown in Table 2.
【0017】[0017]
【表1】 A B C D 通水量 実施例1 実施例2 サンゴ石 貝化石 0L 14ppm 14ppm 14ppm 14ppm 10L 30ppm 32ppm 14ppm 14ppm 50L 26ppm 26ppm 14ppm 14ppm 100L 20ppm 21ppm 14ppm 14ppm 500L 15ppm 21ppm 14ppm 14ppm[Table 1] ABCD Water flow rate Example 1 Example 2 Coral stone Shell fossil 0L 14ppm 14ppm 14ppm 14ppm 10L 30ppm 32ppm 14ppm 14ppm 50L 26ppm 26ppm 14ppm 14ppm 100L 20ppm 21ppm 14ppm 14ppm 14ppm 500L 15ppm
【0018】[0018]
【表2】 A B C D 通水量 実施例1 実施例2 サンゴ石 貝化石 0L 3ppm 3ppm 3ppm 3ppm 10L 7ppm 7ppm 3ppm 3ppm 50L 8ppm 6ppm 3ppm 3ppm 100L 12ppm 5ppm 3ppm 3ppm 500L 4ppm 10ppm 3ppm 3ppm[Table 2] ABCD Water flow rate Example 1 Example 2 Coral stone Shell fossil 0L 3ppm 3ppm 3ppm 3ppm 3ppm 10L 7ppm 7ppm 3ppm 3ppm 50L 8ppm 6ppm 3ppm 3ppm 100L 12ppm 5ppm 3ppm 3ppm 500L 4ppm
【0019】表1及び2に示す結果から、本発明に係る
ミネラル添加剤は、浄水器及び整水器にセットして通水
するだけで、カルシウムとマグネシウムイオンを容易に
添加できることが判る。From the results shown in Tables 1 and 2, it is understood that the mineral additive according to the present invention can easily add calcium and magnesium ions only by setting it in a water purifier and a water conditioner and passing water.
【0020】[0020]
【発明の効果】以上の説明から明らかなように、本発明
は、溶解度が0.05〜1.00(g/100ml,25
℃)のカルシウム及びマグネシウム化合物を組み合わせ
て造粒及び/又は成形したものをミネラル添加剤として
使用するようにしたので、浄水器及び整水器にセットす
ることで、水道水にミネラル分を添加することができ
る。As is apparent from the above description, the present invention has a solubility of 0.05 to 1.00 (g / 100 ml, 25
(° C) A mixture of calcium and magnesium compounds and granulated and / or molded product is used as a mineral additive. By setting it in a water purifier and a water conditioner, minerals are added to tap water. be able to.
Claims (5)
0g/100ml の範囲内にあるカルシウム化合物及び
マグネシウム化合物を主成分とする混合物からなる浄水
器用ミネラル添加剤。1. The solubility at 25 ° C. is 0.05 to 1.0.
Mineral additive for water purifiers, consisting of a mixture containing calcium compounds and magnesium compounds in the range of 0 g / 100 ml.
ム、硫酸カルシウム、酸化カルシウム及び水酸化カルシ
ウムからなる群から選ばれた少なくとも一種である請求
項1に記載のミネラル添加剤。2. The mineral additive according to claim 1, wherein the calcium compound is at least one selected from the group consisting of calcium carbonate, calcium sulfate, calcium oxide and calcium hydroxide.
シウム、塩基性炭酸マグネシウム及び亜硫酸マグネシウ
ムからなる群から選ばれた少なくとも一種である請求項
1に記載のミネラル添加剤。3. The mineral additive according to claim 1, wherein the magnesium compound is at least one selected from the group consisting of magnesium carbonate, basic magnesium carbonate and magnesium sulfite.
酸カルシウム25%〜40%及び塩基性炭酸マグネシウ
ム15%〜30%である請求項1〜3のいずれかに記載
のミネラル添加剤。4. The mineral additive according to claim 1, wherein the calcium carbonate is 25% to 40%, the calcium sulfate is 25% to 40%, and the basic magnesium carbonate is 15% to 30%.
度が0.05〜1.00gの範囲内のカルシウム化合物及
びマグネシウム化合物を配合し、造粒又は成形すること
を特徴とするミネラル添加剤の製造方法。5. A method for producing a mineral additive, which comprises mixing a calcium compound and a magnesium compound having a solubility in 100 ml of water at 25 ° C. in the range of 0.05 to 1.00 g, and granulating or molding.