JPH08326262A - Ground treatment method for interior finishing of alc panel - Google Patents
Ground treatment method for interior finishing of alc panelInfo
- Publication number
- JPH08326262A JPH08326262A JP7160013A JP16001395A JPH08326262A JP H08326262 A JPH08326262 A JP H08326262A JP 7160013 A JP7160013 A JP 7160013A JP 16001395 A JP16001395 A JP 16001395A JP H08326262 A JPH08326262 A JP H08326262A
- Authority
- JP
- Japan
- Prior art keywords
- alc panel
- paper
- alc
- thickness
- treatment method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、ALCパネルの内装仕
上げの下地処理方法に関し、特にALCパネル表面にク
ロス張り仕上げあるいは塗装仕上げする際に、ALCパ
ネル表面が平滑に仕上げられるALCパネルの内装仕上
げの下地処理方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a surface treatment method for finishing the interior of an ALC panel, and in particular, when the surface of the ALC panel is cross-tensioned or painted, the surface of the ALC panel is finished smoothly. The present invention relates to a surface treatment method.
【0002】[0002]
【従来の技術】ALCパネルを壁体として使用し、それ
を内装仕上げする場合は、ALCパネル自体の表面に直
接にクロス張り、化粧壁紙あるいは塗装を施しても、A
LCパネルの表面は他の素材の壁体表面に比してかなり
粗いため、化粧層もその凹凸に追従してしまって平滑な
面が得られ難い。そのため、団子状にした樹脂モルタル
あるいは石膏系接着材を介してALCパネルに表面の平
滑性の優れた石膏ボードを接着させ、その石膏ボード表
面を仕上げ下地面と成し、その面に塗装、クロス張りな
どの通常の種々の内装仕上げ処理が行われている。2. Description of the Related Art When an ALC panel is used as a wall and the interior is finished, even if a cloth is directly attached to the surface of the ALC panel and a decorative wallpaper or painting is applied,
Since the surface of the LC panel is considerably rougher than the wall surface of other materials, it is difficult to obtain a smooth surface because the decorative layer also follows the irregularities. Therefore, a plaster board with excellent surface smoothness is adhered to the ALC panel through a dumpling-shaped resin mortar or a plaster-based adhesive, and the surface of the plaster board is used as a finishing base surface, and the surface is painted or clothed. Various normal interior finishing processes such as upholstery are performed.
【0003】[0003]
【発明が解決しようとする課題】この従来のALCパネ
ルの内装仕上げの下地処理方法でも、平滑な下地面が得
られるが次のような種々の問題点があった。 ALCパネルと石膏ボードとを接着させるための樹脂
モルタルあるいは接着材の硬化に時間がかかるため、下
地処理および内装仕上げ工程に時間がかかる。 樹脂モルタル等を介し、また厚い石膏ボードを接着さ
せるため、壁厚が厚くなるとともに壁重量も重くなる。 地震等による壁体の変形によってモルタルあるいは接
着材とALCパネルとが剥離して石膏ボードが剥離し易
い。 壁が重くて大きいため施工作業が大変であり、コスト
もかかる。This conventional ALC panel interior finishing method can also provide a smooth underlayer, but has various problems as described below. Since it takes time to cure the resin mortar or the adhesive for adhering the ALC panel and the gypsum board, it takes time to perform the base treatment and the interior finishing process. Since thick gypsum board is adhered through resin mortar or the like, the wall thickness becomes thick and the wall weight becomes heavy. Due to the deformation of the wall body due to an earthquake or the like, the mortar or adhesive material and the ALC panel are easily peeled off, and the gypsum board is easily peeled off. Since the walls are heavy and large, construction work is difficult and costly.
【0004】そこで、本発明の目的は、仕上げ工程時間
が短く、壁厚が薄くかつ軽く、壁体の変形による下地層
および化粧層の剥離がなく、さらに施工作業も容易でか
つ低コストで平滑な下地面が得られるALCパネル面の
内装仕上げの下地処理方法を提供することにある。Therefore, an object of the present invention is to shorten the finishing process time, thin and light the wall thickness, and prevent the base layer and the decorative layer from being peeled off due to the deformation of the wall body. Further, the construction work is easy and the cost is smooth. An object of the present invention is to provide a method for treating the surface of an ALC panel surface for finishing the interior of the ALC panel surface.
【0005】[0005]
【課題を解決するための手段】このような目的を達成さ
せる本発明の第1発明は、ALCパネル表面を内装仕上
げする前の下地処理方法において、該ALCパネル表面
に下地材として300g/m2 以上でかつ0.4mm以
上の厚さの紙(以下、下紙と言う)を接着させる方法で
ある。The first invention of the present invention for attaining the above object is to provide a substrate treatment method before the interior finishing of the surface of an ALC panel, wherein the surface of the ALC panel is treated with 300 g / m 2 as a substrate material. This is a method of adhering a paper having a thickness of 0.4 mm or more (hereinafter referred to as a lower paper).
【0006】また、第2の発明はALCパネル表面を内
装仕上げする前の下地処理方法において、該ALC表面
の凹凸を0.3mm以下と成し、その面に200g/m
2 以上でかつ0.3mm以上の厚さの下紙を接着させる
方法である。なお、本発明において、下紙の厚さの測定
方法はダイヤルゲージを用いる。A second aspect of the present invention is a method for treating a surface of a surface of an ALC panel before the surface of the ALC panel is internally finished.
This is a method of adhering a lower paper having a thickness of 2 or more and a thickness of 0.3 mm or more. In the present invention, a dial gauge is used as the method for measuring the thickness of the lower paper.
【0007】第1発明において、下紙としては、単位面
積当たりの重量が300g/m2 以上でかつ0.4mm
以上の厚さが必要である。より好ましくは400g/m
2 以上でかつ0.5mm以上の厚さである。300g/
m2 より少ないものおよび厚さが0.4mmより薄い下
紙を使用すると、その下紙表面に内装仕上げのためのク
ロス張り、塗装、化粧壁紙等を施しても、表面の平滑性
が得られない。また、本発明における紙の単位面積当た
りの重量および厚みの上限は、紙の接着作業性の面から
1000g/m2 以下でかつ1.2mm以下の厚さとす
ることが好ましい。下紙の素材は特に限定されず、上
質、中質あるいはざら紙のボール紙であっても良く、ま
た、撥水紙や不燃紙でも良い。In the first invention, the lower paper has a weight per unit area of 300 g / m 2 or more and 0.4 mm.
The above thickness is required. More preferably 400 g / m
The thickness is 2 or more and 0.5 mm or more. 300 g /
If the lower paper having a thickness of less than m 2 and a thickness of less than 0.4 mm is used, the smoothness of the surface can be obtained even if the surface of the lower paper is covered with cloth for interior finishing, painting, decorative wallpaper, etc. Absent. In addition, the upper limits of the weight per unit area and the thickness of the paper in the present invention are preferably 1000 g / m 2 or less and 1.2 mm or less from the viewpoint of the workability of adhering the paper. The material of the lower paper is not particularly limited, and may be high-quality, medium-quality or rough cardboard, water-repellent paper or non-combustible paper.
【0008】第2発明においては、ALCパネル表面の
凹凸を0.3mm以下と成し、このALCパネル表面に
200g/m2 以上でかつ0.25mm以上の厚さの下
紙を接着する方法である。なお、本発明におけるALC
パネル表面の凹凸の測定は、レーザー光の反射光を利用
した走査型の表面形状測定器を用いて測定し、単位はm
mで表示する。この第2発明において、ALCパネル表
面の凹凸や接着する下紙の重量、厚みが上記条件を外れ
ると、その下紙表面に内装仕上げした場合、平滑性の優
れた仕上げ面が得られないとともに、下紙とALCパネ
ル表面の接着性が低下し、さらには使用する接着剤の使
用量も多くなる。In the second aspect of the present invention, the unevenness of the surface of the ALC panel is set to 0.3 mm or less, and the lower paper having a thickness of 200 g / m 2 or more and 0.25 mm or more is adhered to the surface of the ALC panel. is there. The ALC in the present invention
The unevenness of the panel surface is measured by using a scanning surface shape measuring instrument using reflected light of laser light, and the unit is m.
Display in m. In the second invention, when the unevenness of the ALC panel surface or the weight and thickness of the lower paper to be adhered deviates from the above-mentioned conditions, when the lower paper surface is internally finished, a finished surface having excellent smoothness cannot be obtained, and The adhesiveness between the lower paper and the surface of the ALC panel decreases, and the amount of adhesive used increases.
【0009】ALCパネル表面の凹凸を0.3mm以下
と成す方法として、ALCの製造工程における切断方式
や、成形体の表面研磨や、パテ埋めなどで平滑にするこ
とができるが、平滑性処理工程の省力のためには、製造
工程における切断方式で平滑にすることが望ましい。こ
の製造工程における切断方式としては、ALCパネル用
のグリーンケーキをオートクレーブ養生前にピアノ線に
て切断するが、その際、ピアノ線を振動させながら移動
させる方法、あるいはピアノ線によって切断した直後に
グリーンケーキをローラー又はブレード等で押しつけて
凹凸を小さくする方法がある。As a method of forming irregularities on the surface of the ALC panel to 0.3 mm or less, the cutting method in the ALC manufacturing process, the surface polishing of the molded body, the filling with putty, etc. can be used to smooth the surface. In order to save labor, it is desirable that the cutting method in the manufacturing process be smooth. As a cutting method in this manufacturing process, a green cake for ALC panel is cut with a piano wire before curing in an autoclave. At that time, a method of moving the piano wire while vibrating the piano wire or a green wire immediately after cutting with the piano wire is used. There is a method of reducing unevenness by pressing the cake with a roller or a blade.
【0010】ALCパネルと下紙との接着に使用する接
着剤としては、6〜20重量%の澱粉糊固形分と20重
量%の酢酸ビニル系樹脂との混合物の水溶液であること
が、接着性や紙の収縮防止等の点で望ましく、また同様
な理由から酢酸ビニル系樹脂含有量の下限は5重量%以
上とすることが望ましい。なお、本発明ではALCパネ
ル表面をシーラー等で表面処理した場合は、酢酸ビニル
系樹脂を含まない6〜20重量%の澱粉糊固形分のみの
接着剤でも適用可能である。また接着剤剤には、防菌・
防カビ剤が含有していてもよい。The adhesive used for adhering the ALC panel and the lower paper is an aqueous solution of a mixture of 6 to 20% by weight of starch paste solid content and 20% by weight of vinyl acetate resin. It is desirable from the standpoint of preventing shrinkage of paper and paper, and for the same reason, the lower limit of the vinyl acetate resin content is desirably 5% by weight or more. In the present invention, when the surface of the ALC panel is surface-treated with a sealer or the like, an adhesive containing only a starch paste solid content of 6 to 20% by weight, which does not contain a vinyl acetate resin, can be applied. In addition, anti-bacterial
A fungicide may be contained.
【0011】また、本発明においては、下紙を接着させ
る際にALCパネル間の目地上部に下紙同士の接合部が
位置しないように接着させることが望ましい。すなわ
ち、このようにすることにより、ALCパネル間の相対
的な変位を直接化粧層のクロス壁紙、塗装面に伝えない
ため、化粧層がALCパネル間の目地に沿ってキレツが
生じたりするのを防止することができる。Further, in the present invention, it is desirable that the lower papers are bonded so that the joints between the lower papers are not located at the joints between the ALC panels. That is, by doing so, the relative displacement between the ALC panels is not directly transmitted to the cross wallpaper of the decorative layer or the painted surface, so that the decorative layer may be cracked along the joints between the ALC panels. Can be prevented.
【0012】さらに、接着する下紙はその幅が一枚のA
LCパネルの幅より大きいもの、特にALCパネル幅よ
り1.2倍以上のものを用いることが望ましい。すなわ
ち、このような下紙を用いれば、自ずと下紙同士の接合
部がALCパネル間の目地部に位置しにくくなり、施工
時に特別注意を払う必要がなくなる。しかも、下紙張り
の工期を短縮することができるようになる。ただし、接
着の作業性の面から下紙の幅としては1500mmまで
が望ましい。なお、本発明においては平滑性をより向上
させるために、隣合う下紙同士の接合部のすき間をでき
るだけ小さく(望ましくは3mm以下)し、またALC
パネル間の目地間隔も10mm以下にすることが望まし
い。Further, the bottom paper to be adhered has a width A of one sheet.
It is desirable to use one having a width larger than that of the LC panel, particularly 1.2 times or more the width of the ALC panel. That is, when such a bottom paper is used, the joint portion between the bottom papers is not easily located at the joint between the ALC panels, and it is not necessary to pay special attention during construction. In addition, it is possible to shorten the construction period for the underlay. However, the width of the lower sheet is preferably 1500 mm from the viewpoint of workability of adhesion. In the present invention, in order to further improve smoothness, the gap between the joints between adjacent lower sheets is made as small as possible (desirably 3 mm or less), and the ALC
It is desirable that the joint spacing between the panels is also 10 mm or less.
【0013】以下、本発明を実施例をもって説明する。The present invention will be described below with reference to examples.
【実施例1】固定したピアノ線によって切断されたAL
Cパネル(表面粗さ:0.5mm)を使用して、その表
面に200g/m2 ( 厚さ0.25mm) 、220g/
m2( 厚さ0.28mm) 、250g/m2 ( 厚さ0.
33mm) 、300g/m2( 厚さ0.41mm) 、4
00g/m2 ( 厚さ0.56mm) のボール紙を張っ
た。接着剤は、12重量%の澱粉糊固形分と10重量%
の酢酸ビニル系樹脂との混合物の水溶液を用いた。その
際、接着剤を下紙裏面に塗り、それをALCパネル表面
に張った後、スポンジローラーで空気抜きをした。1週
間後、ボール紙表面の平滑性を調べた。Example 1 AL cut by a fixed piano wire
Using a C panel (surface roughness: 0.5 mm), its surface is 200 g / m 2 (thickness 0.25 mm), 220 g /
m 2 (thickness 0.28 mm), 250 g / m 2 (thickness 0.
33 mm), 300 g / m 2 (thickness 0.41 mm), 4
A cardboard of 00 g / m 2 (thickness 0.56 mm) was stretched. The adhesive consists of 12 wt% starch paste solids and 10 wt%
An aqueous solution of a mixture of the above with a vinyl acetate resin was used. At that time, an adhesive was applied to the back surface of the lower paper, and the surface of the ALC panel was stretched, and then air was removed with a sponge roller. After one week, the smoothness of the cardboard surface was examined.
【0014】その結果、250g/m2 ( 厚さ0.33
mm) 以上のボール紙では、カッティング面の凹凸が目
立たなくなった。そしてこのボール紙の表面に内装仕上
げ用化粧層として再湿壁紙を設けた結果、凹凸が全く目
立たない平滑性の優れた化粧層が得られた。一方、25
0g/m2 ( 厚さ0.33mm) よりも軽くて薄いボー
ル紙では、カッティング面の凹凸が目立たち、かつこの
ボール紙の表面に内装仕上げ用化粧層として再湿壁紙を
設けたものは、表面の凹凸が目立ち商品価値の低いもの
であった。As a result, 250 g / m 2 (thickness 0.33
With the above cardboard, the irregularities on the cutting surface became inconspicuous. Then, a rewet wallpaper was provided on the surface of this cardboard as a decorative layer for interior finishing, and as a result, a decorative layer having excellent smoothness with no conspicuous unevenness was obtained. On the other hand, 25
For cardboard that is lighter and thinner than 0 g / m 2 (thickness 0.33 mm), the unevenness of the cutting surface is conspicuous, and this cardboard has a rewet wallpaper as a decorative layer for interior finishing, Surface irregularities were conspicuous and had low commercial value.
【0015】[0015]
【実施例2】オートクレーブ養生前の半硬化状のグリー
ンケーキを振動させたピアノ線によって切断して得られ
たALCパネル(表面粗さ:0.2mm)をパネルを使
用して、その表面に150g/m2 ( 厚さ0.18m
m) 、270g/m2 ( 厚さ0.20mm) 、200g
/m2 ( 厚さ0.25mm) 、250g/m2 ( 厚さ
0.33mm) 、350g/m2 ( 厚さ0.48mm)
のボール紙を張った。接着剤は、12重量%の澱粉糊固
形分と10重量%の酢酸ビニル系樹脂との混合物の水溶
液を用いた。その際、接着剤をボール紙に塗り、それを
ALCパネル表面に張った後、スポンジローラーで空気
抜きをした。1週間後、ボール紙表面の平滑性を調べ
た。[Example 2] An ALC panel (surface roughness: 0.2 mm) obtained by cutting a semi-cured green cake before curing in an autoclave with a vibrating piano wire was used. / M 2 (0.18m thick
m), 270 g / m 2 (thickness 0.20 mm), 200 g
/ M 2 (thickness 0.25mm), 250g / m 2 (thickness 0.33mm), 350g / m 2 (thickness 0.48 mm)
Put cardboard on. As the adhesive, an aqueous solution of a mixture of a starch paste solid content of 12% by weight and a vinyl acetate resin of 10% by weight was used. At that time, the adhesive was applied to the cardboard, and the cardboard was stretched on the surface of the ALC panel, and then air was removed with a sponge roller. After one week, the smoothness of the cardboard surface was examined.
【0016】その結果、200g/m2 ( 厚さ0.25
mm) 以上のボール紙では、カッティング面の凹凸が目
立たなくなった。そしてこのボール紙の表面に内装仕上
げ用化粧層として再湿壁紙を設けた結果、凹凸が全く目
立たない平滑性の優れた化粧層が得られた。As a result, 200 g / m 2 (thickness 0.25
With the above cardboard, the irregularities on the cutting surface became inconspicuous. Then, a rewet wallpaper was provided on the surface of this cardboard as a decorative layer for interior finishing, and as a result, a decorative layer having excellent smoothness with no conspicuous unevenness was obtained.
【0017】[0017]
【実施例3】実施例2と同一ALCパネルを使用して、
350g/m2 ( 厚さ0.48mm) のボール紙を張っ
た。その際、表1に示す接着剤を各々ボール紙に塗り、
それをALCパネル表面に張り、スポンジローラーで空
気抜きをした。接着剤の接着性について、1週間後にA
LCパネル表面からボール紙を手で剥がし、その際の紙
の剥離状態及び紙の収縮状態を調べた。また同条件でボ
ール紙張りしたALCパネルを、5℃、相対湿度95%で
4時間、40℃、相対湿度50%で4時間の温冷繰り返し試
験を50サイクル行なった。その後、ボール紙を剥がすこ
とで紙の剥離状態及び紙の収縮状態を調べた。Example 3 Using the same ALC panel as in Example 2,
A cardboard of 350 g / m 2 (thickness 0.48 mm) was stretched. At that time, apply each of the adhesives shown in Table 1 to the cardboard,
It was attached to the surface of the ALC panel, and air was removed with a sponge roller. About the adhesiveness of the adhesive, A after 1 week
The cardboard was peeled off from the LC panel surface by hand, and the peeled state of the paper and the contracted state of the paper at that time were examined. The cardboard-clad ALC panel under the same conditions was subjected to 50 cycles of a hot and cold repeated test at 5 ° C. and 95% relative humidity for 4 hours and 40 ° C. and 50% relative humidity for 4 hours. Then, the cardboard was peeled off to examine the peeled state of the paper and the contracted state of the paper.
【0018】なお、紙の剥離状態を示す紙層剥離および
界面剥離とは次の状態をいう。 紙層剥離:ALCパネル表面に接着させた紙を手で剥離
した際に、紙層の一部がALCパネル表面に接着して残
り、他の残りの紙層のみが剥離すること。 界面剥離:ALCパネル表面に接着させた紙を手で剥離
した際に、紙層の全てが剥離すること。 実施例3では、表1に示すようにいずれの条件でも紙の
剥離状態が紙層剥離し良好な接着性を示した。The paper layer peeling and the interface peeling, which represent the peeled state of the paper, are as follows. Paper layer peeling: When the paper adhered to the surface of the ALC panel is peeled by hand, a part of the paper layer remains adhered to the surface of the ALC panel, and the other remaining paper layers are separated. Interfacial peeling: When the paper adhered to the ALC panel surface is peeled by hand, the entire paper layer is peeled off. In Example 3, as shown in Table 1, the peeled state of the paper was peeled by the paper layer under all conditions, and good adhesiveness was exhibited.
【0019】[0019]
【比較例】表1の比較例に示す接着剤を使用した以外
は、実施例3と同一ALCパネルおよび同一条件で接着
剤の接着性を調べた。その結果、表1に示すように界面
剥離や紙層剥離でも紙が収縮して、後の仕上げ処理に支
障がきたすものであった。 表 1 実施例 接着剤 接着性 備考 静置 温冷繰り返し (1) 澱粉糊12%+酢酸ビニル系糊6 % 紙層剥離 紙層剥離 (2) 澱粉糊12%+酢酸ビニル系糊10% 紙層剥離 紙層剥離 (3) 澱粉糊12%+酢酸ビニル系糊15% 紙層剥離 紙層剥離 (4) 澱粉糊 8%+酢酸ビニル系糊15% 紙層剥離 紙層剥離 (5) 澱粉糊20%+酢酸ビニル系糊10% 紙層剥離 紙層剥離 比較例 (1) 澱粉糊(固形分12%) 紙層剥離 界面剥離 (2) 合成ゴム糊 紙層剥離 紙層剥離 紙が収縮 (3) 酢酸ビニル系糊 紙層剥離 一部界面剥離 紙が収縮 (4) 澱粉糊12%+合成ゴム糊 5% 紙層剥離 一部界面剥離 (5) 澱粉糊12%+合成ゴム糊15% 紙層剥離 紙層剥離 紙が収縮 (6) 澱粉糊12%+酢酸ビニル系糊10% 一部界面剥離 界面剥離 (7) 澱粉糊12%+酢酸ビニル系糊25% 紙層剥離 一部界面剥離 Comparative Example The adhesiveness of the adhesive was examined under the same ALC panel and conditions as in Example 3 except that the adhesive shown in the comparative example in Table 1 was used. As a result, as shown in Table 1, the paper shrinks even at the interface peeling and the paper layer peeling, which hinders the subsequent finishing treatment. Table 1 Example glue adhesion Remarks standing warm cold repeat (1) starch paste 12% + vinyl acetate adhesive 6% paper layer release paper layer peeling (2) starch paste 12% + vinyl acetate adhesive 10% paper layer Peeling Paper layer peeling (3) Starch glue 12% + Vinyl acetate glue 15% Paper layer peeling Paper layer peeling (4) Starch glue 8% + Vinyl acetate glue 15% Paper layer peeling Paper layer peeling (5) Starch glue 20 % + Vinyl acetate glue 10% Paper layer peeling Paper layer peeling comparative example (1) Starch glue (solid content 12%) Paper layer peeling Interface peeling (2) Synthetic rubber glue Paper layer peeling Paper layer peeling Paper shrinks (3) Vinyl acetate glue Peeling off paper layer Partial interface peeling Paper shrinks (4) Starch glue 12% + synthetic rubber glue 5% Paper layer peeling Partial interface peeling (5) Starch glue 12% + synthetic rubber glue 15% Paper layer peeling Paper layer peeling Paper shrinks (6) Starch glue 12% + Vinyl acetate glue 10% Partial interface peeling Interface peeling (7) Starch glue 12% + Vinyl acetate glue 25% Paper layer peeling Partial interface peeling
【0020】[0020]
【発明の効果】本発明の方法によれば、ALCパネルの
内壁や間仕切り壁の内装仕上げに先立って、ALCパネ
ル表面に下紙を接着させることによって、 仕上げ面の平滑性を向上させることができ、綺麗な内
装仕上げができること 仕上げ作業が容易であること、 仕上げ工程を短縮できること、 壁厚を軽くかつ薄くすることができること、 仕上げの化粧層の剥離を防止できること、 コストの低減化が可能であること、 等の種々の多大な効果を奏するようになる。According to the method of the present invention, the smoothness of the finished surface can be improved by adhering the lower paper to the surface of the ALC panel prior to the interior finishing of the inner wall and the partition wall of the ALC panel. It is possible to make a clean interior finish, easy finishing work, shorten the finishing process, make the wall thickness lighter and thinner, prevent peeling of the decorative layer of the finish, and reduce costs. And various other great effects.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 中川 清之 愛知県尾張旭市下井町下井2035 小野田エ ー・エル・シー株式会社材料研究所内 (72)発明者 松尾 憲樹 愛知県尾張旭市下井町下井2035 小野田エ ー・エル・シー株式会社材料研究所内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Kiyoyuki Nakagawa 2035 Shimoi, Shimoi-cho, Owariasahi-shi, Aichi Prefecture Inoda Materials Research Co., Ltd. Onoda ALC Co., Ltd. Materials Research Laboratory
Claims (4)
地処理方法において、該ALCパネル表面に下地材とし
て300g/m2 以上でかつ0.4mm以上の厚さの紙
を接着させることを特徴とするALCパネルの内装仕上
げの下地処理方法。1. A surface treatment method before the surface of an ALC panel is internally finished, wherein a paper having a thickness of 300 g / m 2 or more and 0.4 mm or more is adhered to the surface of the ALC panel as a base material. ALC panel interior finishing surface treatment method.
地処理方法において、該ALC表面の凹凸を0.3mm
以下と成し、その表面に200g/m2 以上でかつ0.
25mm以上の厚さの紙を接着させることを特徴とする
ALCパネルの内装仕上げの下地処理方法。2. A surface treatment method before the interior finishing of an ALC panel surface, wherein the unevenness of the ALC surface is 0.3 mm.
The following was satisfied, and the surface was 200 g / m 2 or more and 0.
A method for treating the surface of an ALC panel as an interior finish, which comprises bonding a paper having a thickness of 25 mm or more.
の澱粉糊固形分と20重量%以下の酢酸ビニル系樹脂と
の混合物の水溶液であることを特徴とする請求項1また
は2記載のALCパネルの内装仕上げの下地処理方法。3. The adhesive for adhering paper is 6 to 20% by weight.
3. The method for treating the interior finish of an ALC panel according to claim 1 or 2, which is an aqueous solution of a mixture of said starch paste solid content and 20% by weight or less of a vinyl acetate resin.
部に位置しないように紙を接着させる請求項1、2また
は3記載のALCパネルの内装仕上げの下地処理方法。4. The method for treating the interior finish of an ALC panel according to claim 1, 2 or 3, wherein the paper is adhered so that the joint between the papers is not located at the joint between the ALC panels.